Magnetic characterization of dual phase FeZrB soft magnetic alloy

The magnetic properties and the annealing process of Fe₇₈Zr₇B₁₅ amorphous ribbons are investigated by X-ray diffraction (XRD), differential scanning calorimetry, and vibrating sample magnetometer. The fully amorphous structure of the as-quenched ribbons is confirmed by the XRD pattern. The Curie temperature and the saturation magnetization M_s of the ribbons are 305 °C and 124.3 emu/g, respectively. Annealing at 550 °C can result in an increase in M_s with annealing time due to the increasing crystallized volume fraction of α-Fe phase. The optimized annealing process is established at 550 °C for 20-30 min with maximum M_s of 146.6 emu/g. The morphology of the ribbons annealed at 550 °C is observed by scanning electron microscopy, showing that nanocrystalline α-Fe grains are dispersed in an amorphous matrix.     

The effect of different chemical compositions caused by the variation of deposition potential on properties of Ni-Co films

The magnetic and microstructural properties of Ni-Co films electrodeposited at different cathode potentials were investigated. The compositional analysis revealed that the Ni content increases from 13 at.% to 44 at.% in the films with increasing deposition potential. Magnetic measurements showed that the saturation magnetization, M_s of the films decreased with increase of Ni content as the deposition potential increased. M_s values changed between 1160 emu/cm³ and 841 emu/cm³. The X-ray diffraction revealed that the crystalline structure of the films is a mixture of the predominant face-centered cubic (fcc) and hexagonal closed packed. However, the mixture phase turns to the fcc because of increasing Ni content up to 44 at.% at the highest (−1.9 V) potential by enhancing the intensity of reflections from the fcc phase. The changes observed in the magnetic and microstructural properties were ascribed to the changes observed in the chemical composition caused by the applied different deposition potentials.     

Effect of pH value on the structural and magnetic properties of nanocrystalline strontium hexaferrite thin films

Strontium hexaferrite SrFe₁₂O₁₉ thin films have been synthesized at different pH, adjusted by NH₄OH, on the Si (1 0 0) substrate using a spin coating sol-gel process. Fourier transform infrared spectroscopy analysis and theoretical calculations were conducted for determination and controlling metal citrates in solution precursors. X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer were applied to evaluate the composition, microstructure, crystallite size and magnetic properties of the SrFe₁₂O₁₉ thin films. Using the solution with pH 7, the approximately single phase strontium hexaferrite thin films with optimum physical properties can be obtained at calcination temperature of 800 °C. The SrFe₁₂O₁₉ thin films derived from the solution with pH 7 after calcination at 800 °C exhibited crystallite size of 42 nm and magnetic properties of M_s=267 emu/cm³ (at 10 kOe), M_r=134 emu/cm³ and H_c=4290 Oe.     

Study of the magnetic and structural properties of Mn-, Fe-, and Co-doped ZnO powder

A study of the magnetic and structural properties of Zn_1−xM_xO powder (where x=0 or 0.01, and M=Mn, Fe or Co) produced by the proteic sol–gel process was undertaken. The sample crystal structure was analyzed by XRD and magnetic measurements were carried out in a SQUID magnetometer. Of the XRD analysis, all samples had hexagonal wurtzite crystal structure with P63mc space group, and no secondary phase was observed. It is observed of the M(H) measures at 2 K, that the Co- and Mn-doped ZnO displayed saturation magnetizations (M_s) of approximately 2 and 3.2 emu/g, respectively, and no remanence (M_r) was observed, indicating a superparamagnetic behavior in these samples. However, the Fe-doped sample showed a ferromagnetic behavior with M_s∼0.34 emu/g, M_r∼0.05 emu/g, and coercivity (H_c)∼1090 Oe. Already at room temperature, the M(H) measurements reveal a purely paramagnetic behavior for Mn- and Fe-doped ZnO, indicating that the Curie temperature (T_c) is below 300 K. However, a weak superparamagnetic behavior was observed in the Co-doped sample, indicating that T_c>300 K.     

Synthesis and surface modified hard magnetic properties in Co0.5Pt0.5 nanocrystallites from a rheological liquid precursor

Small crystallites of a metastable phase Co_0.5Pt_0.5 are precipitated by heating a rheological liquid precursor of cobalt–hydrazine complex and platinum chloride H₂PtCl₆·xH₂O in polymer molecules of poly(vinylpyrrolidone) (PVP) in ethylene glycol. The hydrazine co-reduces nascent atoms from the Co²⁺ and Pt⁴⁺ that recombine and grow as Co_0.5Pt_0.5. The PVP molecules cap a growing Co_0.5Pt_0.5 as it achieves a critical size so that it stops growing further in given conditions. X-ray diffraction pattern of a recovered powder reveals a crystalline Co_0.5Pt_0.5 phase (average crystallite size D∼8 nm) of a well-known Fm3m-fcc crystal structure with the lattice parameter a=0.3916 nm (density ρ=14.09 g/cm³). A more ordered L1₀ phase (ρ=15.91 g/cm³) transforms (D≥25 nm) upon annealing the powder at temperature lesser than 700 °C (in vacuum). At room temperature, the virgin crystallites bear only a small saturation magnetization M_s=5.54 emu/g (D=8 nm) of a soft magnet and it hardly grows on bigger sizes (D≤31 nm) in a canted ferromagnetic structure. A rectangular hysteresis loop is markedly expanded on an optimally annealed L1₀ phase at 800 °C for 60 min, showing a surface modified coercivity H_c=7.781 kOe with remnant ratio M_r/M_s=0.5564, and M_s=39.75 emu/g. Crystallites self-assembled in an acicular shape tailor large H_c from ideal single domains and high magnetocrystalline anisotropy of a hard magnet L1₀ phase.     

Solid-state synthesis and magnetic properties of epitaxial FePd3(0 0 1) films

The solid-state synthesis of magnetically soft phase FePd₃ in epitaxial Pd(0 0 1)/Fe(0 0 1)/MgO(0 0 1) film systems was studied experimentally. The system had a Fe to Pd ratio of 1:3. An increase to 450 °C leads to the formation of three variants of ordered L1₀-FePd crystallites. At 500 °C, the solid-state reaction of unreacted Pd with L1₀-FePd crystallites initiates the growth of an ordered epitaxial L1₂-FePd₃(0 0 1) layer. When annealing at 650 °С, a gradual disordering is observed. The magnetic anisotropy (K₁=−2.0×10³ erg/cm³) and the saturation magnetization (M_S=650 emu/cm³) of the disordered FePd₃ phase were determined.     

Magnetic properties and static-dynamic magnetostrictive characteristics for SmFe2/Fe exchange-coupled multilayers

Giant magnetostrictive SmFe₂/Fe exchange-coupled multilayers were fabricated by ion beam sputtering deposition on glass substrates. The effects of SmFe₂/Fe exchange coupling action and vacuum annealing on soft-magnetic property and static-dynamic magnetostrictive characteristics of SmFe₂/Fe multilayers were investigated. The results showed that the soft-magnetic, static-dynamic magnetostrictive characteristics were greatly improved by SmFe₂/Fe exchange coupling action and proper vacuum annealing treatment temperature. Compared with that of SmFe₂ single film, the coercivity in the direction of easy magnetization axis for SmFe₂/Fe exchange-coupled multilayers exhibited a greater decrease. Better soft-magnetic properties were achieved (H_c=2.54 kA/m, M_s=120.38 emu/g, and M_r/M_s=0.21) after vacuum annealing at certain temperature. The magnetostrictive coefficient for SmFe₂/Fe exchange-coupled multilayers was about 135 ppm at 16 kA/m magnetic field. At first order resonant frequency (99.2 Hz), the amplitude peak-peak value for the as-deposited SmFe₂/Fe exchange-coupled multilayers was 46 μm. After the vacuum annealing treatment at 250 °C, the amplitude peak-peak value increased to 650 μm.     

Synthesis,characterization and magnetic properties of MFe2O4 (M=Co,Mg, Mn,Ni) nanoparticles using ricin oil as capping agent

We focused on obtaining MFe₂O₄ nanoparticles using ricin oil solution as surfactant and on their structural characterization and magnetic properties. The annealed samples at 500 °C in air for 6 h were analyzed for the crystal phase identification by powder X-ray diffraction using CuKα radiation. The particle size, the chemical composition and the morphology of the calcinated powders were characterized by scanning electron microscopy. All sintered samples contain only one phase, which has a cubic structure with crystallite sizes of 12–21 nm. From the infrared spectra of all samples were observed two strong bands around 600 and 400 cm⁻¹, which correspond to the intrinsic lattice vibrations of octahedral and tetrahedral sites of the spinel structure, respectively, and characteristic vibration for capping agent. The magnetic properties of fine powders were investigated at room temperature by using a vibrating sample magnetometer. The room temperature M–H hysteresis loops show ferromagnetic behavior of the calcined samples, with specific saturation magnetization (M_s) values ranging between 11 and 53 emu/g.     

Effects of rapid thermal annealing on structural, magnetic and optical properties of Ni-doped ZnO thin films

XPS depth profiles were used to investigate the effects of rapid thermal annealing under varying conditions on the structural, magnetic and optical properties of Ni-doped ZnO thin films. Oxidization of metallic Ni from its metallic state to two-valence oxidation state occurred in the film annealed in air at 600 °C, while reduction of Ni²⁺ from its two-valence oxidation state to metallic state occurred in the film annealed in Ar at 600 and 800 °C. In addition, there appeared to be significant diffusion of Ni from the bottom to the top surface of the film during annealing in Ar at 800 °C. Both as-deposited and annealed thin films displayed obvious room temperature ferromagnetism (RTFM) which was from metallic Ni, Ni²⁺ or both with two distinct mechanisms. Furthermore, a significant improvement in saturation magnetization (M_s) in the films was observed after annealing in air (M_s = 0.036 μ_B/Ni) or Ar (M_s = 0.033 μ_B/Ni) at 600 °C compared to that in as-deposited film (M_s = 0.017 μ_B/Ni). An even higher M_s value was observed in the film annealed in Ar at 800 °C (M_s = 0.055 μ_B/Ni) compared to that at 600 °C mainly due to the diffusion of Ni. The ultraviolet emission of the Ni-doped ZnO thin film was restored during annealing in Ar at 800 °C, which was also attributed to the diffusion of Ni.     

Magnetic properties of cobalt substituted M-type barium hexaferrite prepared by co-precipitation

The co-precipitation and solid state methods were used in the synthesis of barium hexaferrite (BaM). Phase pure BaM was obtained with 1, 2, 3, 5, 10, 15, 20 and 30 wt% cobalt oxide (Co₃O₄). The addition of Co^2+/3+ ions to the BaM increased the permeability and magnetic loss tangent to a value of 3.5 at 5% and reduced to 1 at 30% doping. With increased Co doping, M_s was reduced from 87-58 emu/g, M_r increased from 11 to 40 emu/g with 3–5 wt% Co and 9 emu/g for 30% doping. H_c sharply increased from 540 to 2200 Oe with a reduction to 280 Oe at 10 K with increasing temperature to 300 K. T_c increased from 740 to 750 K for 30% Co doping. DTA–TGA studies of green body showed decarboxilation to occur at around 825 °C and the transformation of residual Co₃O₄ to Co₂O₃ at around 577 °C. The XRD data confirmed the Co ions substituting into Fe sites until a 10–15% doping level where the structure altered to W-type hexaferrite. The densities of the compounds varied with doping to a maximum of 4.45 g/cm³.     

Magnetic properties of strontium hexaferrite films prepared by pulsed laser deposition

The magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films fabricated by pulsed laser deposition on the Si(100) substrate with Pt(111) underlayer have been studied as a function of film thickness (50–700 nm). X-ray diffraction patterns confirm that the films have c-axis perpendicular orientation. The coercivities in perpendicular direction are higher than those for in-plane direction which indicates the films have perpendicular magnetic anisotropy. The coercivity was found to decrease with increasing of thickness, due to the increasing of the grain size and relaxation in lattice strain. The 200 nm thick film exhibits hexagonal shape grains of 150 nm and optimum magnetic properties of M_s=298 emu/cm³ and H_c=2540 Oe.     

Synthesis of α-Fe2O3 nanobelts and nanoflakes by thermal oxidation and study to their magnetic properties

α-Fe₂O₃ nanobelts and nanoflakes have been successfully synthesized by oxidation of iron-coated ITO glass in air. The X-ray diffraction, Raman spectrum and scanning electron microscopy are carried out to characterize the nanobelts and nanoflakes. The formation mechanism has been presented. Significantly, the magnetic investigations show that the magnetic properties are strongly shape-dependent. The magnetization measurements of belt-like and flake-like α-Fe₂O₃ in perpendicular exhibit ferromagnetic feature with the coercivity (H_c) and saturation magnetization (M_s) of 334.5 Oe and 1.35 emu/g, 239.5 Oe and 0.12 emu/g, respectively. For the parallel, belt-like and flake-like α-Fe₂O₃ also exhibit ferromagnetic feature with the H_c and M_s of 205.5 Oe and 1.44 emu/g, 159.6 Oe and 0.15 emu/g, respectively.     

Microstructure and magnetic properties of Ni-rich Ni54Mn25.7Ga20.3 ferromagnetic shape memory alloy thin film

A Ni₅₄Mn_25.7Ga_20.3 ferromagnetic shape memory alloy thin film has been fabricated by using the RF magnetron-sputtering technique. The structure and magnetic properties of the film were systematically investigated. The results show that the film is in ferromagnetic martensite state at room temperature with the Curie temperature (T_c) of about 370 K. The saturation magnetization (M_s) of the film reaches 45 emu/g at 300 K, which is about 80% as large as that of Ni–Mn–Ga bulk material. The magnetization hysteresis loops significantly depend on temperatures. The residual magnetization (M_r) and the coercive force (H_c) increase with decreasing temperatures. The grains homogeneously distribute in the film. The microstructure of the film consists of martensite plates. The interface between the martensite variants is clear and straight, indicating a good mobility.     

Effect of magnetic field annealing on microstructure and magnetic properties of FePt films

FePt (20 nm) films were annealed in a magnetic field (along the normal direction of the films) at a temperature around the Curie temperature of L1₀ FePt. The influence of magnetic filed annealing on texture and magnetic properties of FePt films were investigated. The results indicate that preferential (0 0 1) orientation and perpendicular anisotropy can be obtained in L1₀ FePt films by using magnetic field annealing around the Curie temperature of L1₀ FePt. This is one of the potential methods to obtain (0 0 1) orientation and thus to improve the perpendicular anisotropy in FePt films.     

Ultraviolet electroluminescence from ZnO-based light-emitting diode with p-ZnO:N/n-GaN:Si heterojunction structure

A p-ZnO:N/n-GaN:Si structure heterojunction light-emitting diode (LED) is fabricated on c-plane sapphire by full metal organic chemical vapor deposition (MOCVD) technique. The p-type layer with hole concentration of 8.94×10¹⁶ cm⁻³ is composed of nitrogen-doped ZnO using NH₃ as the doping source with subsequent annealing in N₂O plasma ambient. Silicon-doped GaN film with electron concentration of 1.15×10¹⁸ cm⁻³ is used as the n-type layer. Desirable rectifying behavior is observed from the current-voltage (I-V) curve of the device. The forward turn on voltage is about 4 V and the reverse breakdown voltage is more than 7 V. A distinct ultraviolet (UV) electroluminescence (EL) with a dominant emission peak centered at 390 nm is detected at room temperature from the heterojunction structure under forward bias conditions. The origins of the EL emissions are discussed in comparison with the photoluminescence (PL) spectra.     

Synthesis and the magnetic characterization of iridium–cobalt substituted calcium hexaferrites

M-type hexagonal ferrite powder with partial substitution lr⁴⁺+Co²⁺ has been synthesized by chemical-coprecipitation technique. The saturation magnetization M_s decreases linearly from 69.8 to 40.3 emu/g with increasing doping content from 0.5 to 1. The Coerecivity sharply drops for x=0.5, which can be explained by the decrease of the anisotropy constant K₁ Curie temperature T_c decreases linearly with increasing ‘x’. Crystallographic studies were explained on the cation distribution consistent with Gorter spin model of parallel alignment.     

Structural and magnetic properties of self-assembled Sm-Co spherical aggregates

Self-assembled Sm-Co nanoparticles in the form of spherical aggregates (referred as nanospheres) with diameter ranging from 50 to 180 nm were achieved by means of polyol technique. The size distribution of the Sm-Co nanospheres can be regulated close to ∼100 nm by controlling the molar ratio of Sm:Co precursor. The spherical aggregates exhibited Sm₂Co₇ phase as a major constituent; while the aggregates obtained at higher Co concentration showed co-existence of Co-phase with Sm₂Co₇ phase. Upon annealing, the biphasic nature of nanospheres (Sm₂Co₇/Co) transformed into Sm₂Co₁₇ structure. By varying the Sm:Co precursor ratio from 1:5 to 1:9, the coercivity (H_c) and magnetization (M_s) values of the as-synthesized nanospheres can be tuned from 336 to 140 Oe and from 63.7 to 108 emu/g, respectively, and these values significantly improved after annealing. Maximum values of H_c (1050 Oe) at the Sm:Co molar ratio of 1:5 and M_s of 184.6 emu/g at the Sm:Co molar ratio of 1:9 were achieved in the annealed samples.     

Heat treatment effects on microstructure and magnetic properties of Mn-Zn ferrite powders

Mn-Zn ferrite powders (Mn_0.5Zn_0.5Fe₂O₄) were prepared by the nitrate-citrate auto-combustion method and subsequently annealed in air or argon. The effects of heat treatment temperature on crystalline phases formation, microstructure and magnetic properties of Mn-Zn ferrite were investigated by X-ray diffraction, thermogravimetric and differential thermal analysis, scanning electron microscopy and vibrating sample magnetometer. Ferrites decomposed to Fe₂O₃ and Mn₂O₃ after annealing above 550 °C in air, and had poor magnetic properties. However, Fe₂O₃ and Mn₂O₃ were dissolved after ferrites annealing above 1100 °C. Moreover, the 1200 °C annealed sample showed pure ferrite phase, larger saturation magnetization (M_s=48.15 emu g⁻¹) and lower coercivity (H_c=51 Oe) compared with the auto-combusted ferrite powder (M_s=44.32 emu g⁻¹, H_c=70 Oe). The 600 °C air annealed sample had the largest saturation magnetization (M_s=56.37 emu g⁻¹) and the lowest coercivity (H_c=32 Oe) due to the presence of pure ferrite spinel phase, its microstructure and crystalline size.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

Study of Zn1−xCoxO (0.02≤x≤0.08) dilute magnetic semiconductor prepared by mechanosynthesis route

Single-phase Zn_1−xCo_xO (0.02≤x≤0.08) dilute magnetic semiconductor is prepared by mechanical milling process. The shift of XRD peaks towards the higher angle and a redshift in the band gap compared to the undoped ZnO ensure the incorporation of Co²⁺ ions in the semiconductor host lattice. Pure Zn_xCo_1−xO phases show the paramagnetic behavior in the temperature range 80 K≤T≤300 K. The room temperature volume magnetic susceptibility (χ_v) estimated in case of Zn_0.96Co_0.04O is ∼10⁻⁵ emu/Oe cm³. The temperature dependence of susceptibility χ_v can be fitted well with Curie law confirming the paramagnetic interaction. The observed crystal-field splitting of 3d levels of Co²⁺ ions inside Zn_1−xCo_xO has been successfully interpreted using Curie law.