Effect of Fe substitution on magnetocaloric effect in La0.7Sr0.3Mn1−xFexO3 (0.05≤x≤0.20)

We have studied the effect of Fe substitution on magnetic and magnetocaloric properties in La_0.7Sr_0.3Mn_1−xFe_xO₃ (x=0.05, 0.07, 0.10, 0.15, and 0.20) over a wide temperature range (T=10-400 K). It is shown that substitution by Fe gradually decreases the ferromagnetic Curie temperature (T_C) and saturation magnetization up to x=0.15 but a dramatic change occurs for x=0.2. The x=0.2 sample can be considered as a phase separated compound in which both short-range ordered ferromagnetic and antiferromagnetic phases coexist. The magnetic entropy change (−ΔS_m) was estimated from isothermal magnetization curves and it decreases with increase of Fe content from 4.4 J kg⁻¹ K⁻¹ at 343 K (x=0.05) to 1.3 J kg⁻¹ K⁻¹ at 105 K (x=0.2), under ΔH=5 T. The La_0.7Sr_0.3Mn_0.93Fe_0.07O₃ sample shows negligible hysteresis loss, operating temperature range over 60 K around room temperature with refrigerant capacity of 225 J kg⁻¹, and magnetic entropy of 4 J kg⁻¹ K⁻¹ which will be an interesting compound for application in room temperature refrigeration.     

A study on magnetoelastic properties of Tb3 (Fe28−xCox) V1.0 (x=0, 3, 6) compounds

In this work, The magnetoelastic properties of polycrystalline samples of Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) intermetallic compounds are investigated by means of linear thermal expansion and magnetostriction measurements in the temperature range of 77–515 K under applied magnetic fields up to 1.5 T. The linear thermal expansion increases with the Co content. The well-defined anomalies observed in the linear thermal expansion coefficients for Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) compounds are associated with the magnetic ordering temperature for x=0 and spin reorientation temperatures for x=3, 6. Below transition temperatures, the value of the longitudinal magnetostriction (λ_Pa) at 1.6 T increases with Co content.     

Magnetostriction, Curie temperature and microstructure of Tb0.29(Dy1−xPrx)0.71Fe1.97 oriented alloys

The Tb_0.29(Dy_1−xPr_x)_0.71Fe_1.97 (x=0, 0.1, 0.2 and 0.3) alloys were prepared by directional solidification method. The orientation, magnetostriction λ, Curie temperature T_c and microstructure of alloys were characterized by XRD, standard resistant strain gauge technique, VSM and SEM-EDS. The results reveal that the alloys have a preferred orientation of 〈1 1 0〉 and 〈1 1 3〉 direction when x>0. With the increase in Pr content, the T_c of alloys decreases gradually and the non-cubic phase appears, resulting in the decline of λ dramatically, from 1935.2×10⁻⁶ for x=0 to 695.9×10⁻⁶ for x=0.3 at a compressive stress of 6 MPa and a magnetic field of H=240 kA m⁻¹.     

Magnetic/structural diagram, chemical composition-dependent magnetocaloric effect in self-doped antipervoskite compounds Sn1−xCMn3+x (0≤x≤0.40)

The effects of Mn substitutions on the crystal structure, magnetic properties, and magnetocaloric effect (MCE) of antiperovskite Sn_1−xCMn_3+x (0≤x≤0.40) have been investigated detailedly. Both the Curie temperature (T_C) and the magnetizations at 40 kOe decrease with increasing x firstly for x≤0.10, and then increase with increasing x further. The type of magnetic transition changes from first-order to second-order around x=0.10 with increasing x. Chemical composition-dependent MCE is also studied around T_C. With increasing x, the maximal magnetic entropy changes decrease and the magnetic phase transitions broaden. Accordingly, the relative cooling power (RCP) increases with increasing x, reaching the largest values of ∼0.56 J/cm³ (∼75 J/kg) and ∼1.66 J/cm³ (∼221 J/kg) with the magnetic changes of 20 kOe and 48 kOe, respectively. Considering the large RCP, inexpensive, and innoxious raw materials, these serial samples Sn_1−xCMn_3+x are suggested to be potential room-temperature magnetic refrigerant materials.     

Near room temperature magnetocaloric properties of melt-spun Gd100−xBx (x=0, 5, 10, 15, and 20 at%) alloys

The magnetocaloric properties of melt-spun Gd-B alloys were examined with the aim to explore their potential application as magnetic refrigerants near room temperature. A series of Gd_100−xB_x (x=0, 5, 10, 15, and 20 at%) alloys were prepared by melt spinning. With the decrease in Gd/B ratio, Curie temperature (T_C) remains constant at ∼293 K, and saturation magnetization, at 275 K, decreases from ∼100 to ∼78 emu/g. Negligible magnetic hysteresis was observed in these alloys. The peak value of magnetic entropy change, (−ΔS_M)_max, decreased from ∼9.9 J/kg K (0-5 T) and ∼5.5 J/kg K (0-2 T) for melt-spun Gd to ∼7.7 J/kg K (0-5 T) and ∼4.0 J/kg K (0-2 T), respectively for melt-spun Gd₈₅B₁₅ and Gd₈₀B₂₀ alloys. Similarly, the refrigeration capacity (q) decreased monotonously from ∼430 J/kg (0-5 T) for melt-spun Gd to ∼330 J/kg (0-5 T) for melt-spun Gd₈₀B₂₀ alloy. The near room temperature magnetocaloric properties of melt-spun Gd_100−xB_x (0≤x≤20) alloys were found to be comparable to few first-order transition based magnetic refrigerants.     

Structural, magnetic properties and magnetostriction studies of Sm1−xNdxFe1.55 alloys

Structural, magnetic properties and magnetostriction studies of Sm_1−xNd_xFe_1.55 (0≤x≤0.56) alloys have been performed. X-ray diffraction analysis confirms the presence of single cubic Laves phase in Sm_1-xNd_xFe_1.55 alloys with 0≤x≤0.48. The lattice parameter of alloys increases linearly with increase in Nd content while the Curie temperature behaves in the opposite way. The alloy x=0.08 exhibits a giant magnetostriction value (λ_∥-λ_⊥) of −2187 ppm at a magnetic field of 12 kOe due to the anisotropy compensation between Sm³⁺ and Nd³⁺ ions.     

BiFeO3/Zn1−xMnxO bilayered thin films

BiFeO₃/Zn_1−xMn_xO (x = 0-0.08) bilayered thin films were deposited on the SrRuO₃/Pt/TiO₂/SiO₂/Si(1 0 0) substrates by radio frequency sputtering. A highly (1 1 0) orientation was induced for BiFeO₃/Zn_1−xMn_xO. BiFeO₃/Zn_1−xMn_xO thin films demonstrate diode-like and resistive hysteresis behavior. A remanent polarization in the range of 2P_r ∼ 121.0-130.6 μC/cm² was measured for BiFeO₃/Zn_1−xMn_xO. BiFeO₃/Zn_1−xMn_xO (x = 0.04) bilayer exhibits a highest M_s value of ∼15.2 emu/cm³, owing to the presence of the magnetic Zn_0.96Mn_0.04O layer with an enhanced M_s value.     

Structure, transport and magnetic properties in La2xSr2−2xCo2xRu2−2xO6

The perovskite solid solutions of the type La_2xSr_2−2xCo_2xRu_2−2xO₆ with 0.25≤x≤0.75 have been investigated for their structural, magnetic and transport properties. All the compounds crystallize in double perovskite structure. The magnetization measurements indicate a complex magnetic ground state with strong competition between ferromagnetic and antiferromagnetic interactions. Resistivity of the compounds is in confirmation with hopping conduction behaviour though differences are noted especially for x=0.4 and 0.6. Most importantly, low field (50 Oe) magnetization measurements display negative magnetization during the zero field cooled cycle. X-ray photoelectron spectroscopy measurements indicate the presence of Co²⁺/Co³⁺ and Ru⁴⁺/Ru⁵⁺ redox couples in all compositions except x=0.5. Presence of magnetic ions like Ru⁴⁺ and Co³⁺ gives rise to additional ferromagnetic (Ru-rich) and antiferromagnetic sublattices and also explains the observed negative magnetization.     

Magnetic/structural phase diagram and enhanced giant magnetoresistance in Zn-doped antiperovskite compound Ga1−xZnxCMn3

The structural, magnetic and electrical transport properties of Zn-doped antiperovskite compounds Ga_1−xZn_xCMn₃ (0≤x≤0.30) have been investigated. After partial substitution of Zn for Ga, the Curie temperature increases monotonously and the ground antiferromagnetic (AFM)-ferromagnetic intermediate (FI) phase transition is gradually suppressed. With increasing the doping level x, the saturated magnetizations decreases gradually firstly for x≤0.20, then increases with increasing x. The electrical transport properties of Ga_1−xZn_xCMn₃ are studied at different magnetic fields. Enhanced giant magnetoresistance (GMR) was observed around the AFM-FI transition. With increasing x, the maximal values and peak widths of GMR increase. Particularly, for x=0.20, GMR reaches a maximum value of 75%, spanning a temperature range of 80 K at 50 kOe and displays the behavior of strongly depending on the magnetization history. The possible origins are discussed.     

Synthesis and magnetic properties of Zn1−xMnxO films prepared by the sol-gel method

We report on the ferromagnetic characteristics of Zn_1−xMn_xO films (x=0.1-0.3) prepared by the sol-gel method on silicon substrates using transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), X-ray diffractometry (XRD) and superconducting quantum interference device (SQUID) magnetometry at various temperatures. Magnetic measurement show that the Curie temperature (T_C) and the coercive field (H_C) were ∼39 K and ∼2100 Oe for the film of x=0.2, respectively. EDS and TEM measurements indicate that Mn content at the interface is significantly higher than that at the center of the Zn_0.8Mn_0.2O film showing the ratio, Zn:Mn:O≅1:12:15. This experimental evidence suggests that ferromagnetic precipitates containing manganese oxide may be responsible for the observed ferromagnetic behavior of the film.     

Antiferromagnetism and spin-glass transition in the FeInxCr2−xSe4 series of selenides

The magnetic behavior of the FeIn_xCr_2−xSe₄ system (with x=0.0, 0.2 and 0.4) has been investigated by magnetic and Mössbauer spectroscopy. Hyperfine parameters indicate that iron is in the Fe²⁺ oxidation state, with a minor (∼9%) Fe³⁺ fraction, located at different layers in the structure. Low-field magnetization curves as a function of temperature showed that the antiferromagnetic (AFM) order temperature is T_N=208(2) K for FeCr₂Se₄ and decreases to 174(3) K for FeIn_0.4Cr_1.6Se₄. The effective magnetic moment μ_eff decreases with increasing In contents, and shows agreement with the expected values from the contribution of Fe²⁺ (⁵D) and Cr³⁺ (⁴F) electronic states. A second, low-temperature transition is observed at T_G∼13 K, which has been assigned to the onset of a glassy state.     

Structural and magnetic properties of sol-gel Co2xNi0.5−x Zn0.5−xFe2O4 thin films

Nanocrystalline Co_2xNi_0.5−xZn_0.5−xFe₂O₄ (x=0−0.5) thin films have been synthesized with various grain sizes by a sol-gel method on polycrystalline silicon substrates. The morphology as well as magnetic and microwave absorption properties of the films calcined at 1073 K were studied using X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, and vibrating sample magnetometry. All films were uniform without microcracks. The Co content in the Co-Ni-Zn films resulted in a grain size ranging from 15 to 32 nm while it ranged from 33 to 49 nm in the corresponding powders. Saturation and remnant magnetization increased with increase in grain size, while coercivity demonstrated a drop due to multidomain behavior of crystallites for a given value of x. Saturation magnetization increased and remnant magnetization had a maximum as a function of grain size independent of x. In turn, coercivity increased with x independent of grain size. Complex permittivity of the Co-Ni-Zn ferrite films was measured in the frequency range 2-15 GHz. The highest hysteretic heating rate in the temperature range 315-355 K was observed in CoFe₂O₄. The maximum absorption band shifted from 13 to 11 GHz as cobalt content increased from x=0.1 to 0.2.     

Structural,optical, FTIR and photoluminescence properties of Zn0.96−xCo0.04CuxO (x=0.03, 0.04 and 0.05) nanopowders

Un-hydrogenated and hydrogenated Cu, Co co-doped ZnO (Zn_0.96−xCo_0.04Cu_xO, x=0.03, 0.04 and 0.05) nanopowders have been synthesized by co-precipitation method. The synthesized samples have been characterized by powder X-ray diffraction, energy dispersive X-ray spectra, UV–Visible spectrophotometer and Fourier transform infrared spectroscopy. The calculated average crystalline size increases from 37.3 to 50.6 nm for un-hydrogenated samples from x=0.03 to 0.05 and it changes from 29.4 to 34.9 nm for hydrogenated samples. The change in lattice parameters, micro-strain, a small shift of X-ray diffraction peaks towards lower angles and reduction in energy gap reveal the substitution of Cu²⁺ ions into Zn–Co–O lattice. The hydrogenation effect reduces the particle size and induces the more uniform distribution of particles than the un-hydrogenated samples which is confirmed by SEM micrographs. Photoluminescence spectra of Zn_0.96−xCo_0.04Cu_xO system shows that red shift in near band edge ultraviolet emission from 393 to 403 nm with suppressing intensity and a blue shift in green band emission from 537 to 529 nm with enhancing intensity confirms the substitution of Cu into the Zn–Co–O lattice.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

Room temperature ferromagnetism behavior of Sn1−xMnxO2 powders

In this paper, we have investigated Mn-doped SnO₂ powder samples prepared by solid-state reaction method. X-ray diffraction showed a single phase polycrystalline rutile structure. The atomic content of Mn ranged from ∼0.8 to 5 at%. Room temperature M-H loops showed a ferromagnetic behavior for all samples. The ferromagnetic Sn_0.987Mn_0.013O₂ showed a coercivity H_c=545 Oe, which is among the highest reported for dilute magnetic semiconductors. The magnetic moment per Mn atom was estimated to be about 2.54 μ_B of the Sn_0.9921Mn_0.0079O₂ sample. The average magnetic moment per Mn atom sharply decreases with increasing Mn content, while the effective fraction of the Mn ions contributing to the magnetization decreases. The magnetic properties of the Sn_1−xMn_xO₂ are discussed based on the competition between the antiferromagnetic superexchange coupling and the F-center exchange coupling mechanism, in which both oxygen vacancies and magnetic ions are involved.     

High-temperature electrical properties of magnesiowustite Mg1 − xFexO and spinel Fe3 − x − yMgxCryO4 ceramics

Phase relationships, thermal expansion and electrical properties of Mg_1 − xFe_xO (x = 0.1-0.45) cubic solid solutions and Fe_{3 − x − y}Mg_xCr_yO_4 ± δ (x = 0.7-0.95; y = 0 or 0.5) spinels were studied at 300-1770 K in the oxygen partial pressure range from 10 Pa to 21 kPa. Increasing iron content enlarges the spinel phase stability domain at reduced oxygen pressures and elevated temperatures. The total conductivity of the spinel ceramics is predominantly n-type electronic and is essentially p(O₂)-independent within the stability domain. The computer simulations using molecular dynamics technique confirmed that overall level of ion diffusion remains low even at high temperatures close to the melting point. Temperature dependencies of the total conductivity in air exhibit a complex behavior associated with changing the dominant defect-chemistry mechanism from prevailing formation of the interstitial cations above 1370-1470 K to the generation of cation vacancies at lower temperatures, and with kinetically frozen cation redistribution in spinel lattice below 700-800 K. The average thermal expansion coefficients of the spinel ceramics calculated from dilatometric data in air vary in the range (9.6-10.0) × 10^− 6 K^− 1 at 300-500 K and (13.2-16.1) × 10^− 6 K^− 1 at 1050-1370 K. Mg_1 − xFe_xO solid solutions undergo partial decomposition on heating under oxidizing and mildly reducing conditions, resulting in the segregation of spinel phase and conductivity decrease.     

Effect of Cr on the magnetic properties of evaporated CoxCr1−x/Si(1 0 0) and CoxCr1−x/glass thin films

Series of Co_xCr_1−x thin films have been evaporated under vacuum onto Si(1 0 0) and glass substrates. Thickness ranges from 17 to 220 nm, and x from 0.80 to 0.88. Alternating gradient field magnetometer (AGFM) measurements provided saturation magnetization values ranging from 220 to 1200 emu/cm³. Values of squareness exceeding 0.8 have been measured. Coercive field may reach values up to 700 Oe, depending on the percentage of chromium, as well as the substrate nature and the direction of the applied magnetic field. The saturation magnetization value decreases as the Cr content increases. In order to study their dynamical magnetic properties, Brillouin Light Scattering (BLS) measurements have been performed on these samples. Stiffness constant value and anisotropy magnetic field were adjusted to fit the experimental BLS spectra. These results are analyzed and correlated.     

Phase stability,elastic, electronic,thermal and optical properties of Ti3Al1−xSixC2 (0≤x≤1): First principle study

The structural parameters with stability upon Si incorporation and elastic, electronic, thermodynamic and optical properties of Ti₃Al_1−xSi_xC₂ (0≤x≤1) are investigated systematically by the plane wave pseudopotential method based on the density functional theory (DFT). The increase of some elastic parameters with increasing Si-content renders the alloys to possess higher compressive and tensile strength. The Vickers hardness value obtained with the help of Mulliken population analysis increases as x is increased from 0 to 1. The solid solutions considered are all metallic with valence and conduction bands, which have a mainly Ti 3d character, crossing the Fermi level. The temperature and pressure dependences of bulk modulus, normalized volume, specific heats, thermal expansion coefficient, and Debye temperature are all obtained through the quasi-harmonic Debye model with phononic effects for T=0−1000 K and P=0−50 GPa. The obtained results are compared with other results available. Further an analysis of optical functions for two polarization vectors reveals that the reflectivity is high in the visible–ultraviolet region up to ∼10.5 eV region showing promise as a good coating material.     

Room-temperature ferromagnetism in Zn1−xMnxO

In view of recent controversies on above room-temperature ferromagnetism (RTFM) in transition-metal-doped ZnO, the present paper aims to shed some light on the origin of ferromagnetism by investigating annealing effects on structure and magnetism for polycrystalline Zn_1−xMn_xO powder samples prepared by solid-state reaction method and annealed in air at different temperatures. Magnetic measurements indicate that the samples are ferromagnetic at room temperature (RTFM). Room temperature ferromagnetism has been observed in the sample annealed at a low temperature of 500 °C with a saturated magnetization (M_s) of 0.159 emu/g and a coercive force of 89 Oe. A reduction in RTFM is clearly observed in the sample annealed at 600 °C. Furthermore, the saturation magnetic moment decreases with an increase in grain size, suggesting that ferromagnetism is due to defects and/or oxygen vacancy confined to the surface of the grains. The experimental results indicate that the ferromagnetism observed in Zn_1−xMn_xO samples is intrinsic rather than associated with secondary phases.     

Highly cation-deficient manganese perovskite, La1−xMn1−yO3 with x=y

Oxidative (δ>0) nonstoichiometry in the perovskite ‘LaMnO_3+δ’ has been known to be manifested not with O interstitials but rather with cation vacancies of equal amounts at the two cation sites, La and Mn, i.e. La_1−xMn_1−yO₃ with x=y. Here, we report the fabrication of samples with record-high cation-vacancy concentrations (x>0.12 or δ>0.4) by means of a variety of high-pressure oxygenation techniques. Linear (negative) dependence of the cell volume on x was observed within the whole x range investigated, down to 56.9 Å³ (per formula unit) for a sample oxygenated at 5 GPa and 1100 °C using Ag₂O₂ as an excess oxygen source. With increasing degree of cation deficiency in La_1−xMn_1−xO₃, the ferromagnetic transition temperature was found to follow a bell shape with respect to x exhibiting a maximum of ∼250 K about x≈0.1. For moderately oxygenated samples large magnetoresistance effect was evidenced.