利用溶胶-凝胶法制备了多孔晶体材料C12A7-Cl- (Ca12Al14O32Cl2), 制备凝胶的原料是四水合硝酸钙、九水合硝酸铝、氯化钙、尿素和乙二醇. 混合溶液经过搅拌2-3 h形成溶胶, 再经350 ℃热处理后形成凝胶体, 最终在流动氩气气氛中1000 ℃烧结后得到材料. 用X射线衍射, 场发射扫描电子显微镜, 热重分析, 电子顺磁共振和离子色谱等方法表征合成的C12A7-Cl-多孔晶体材料. 结果表明, 利用溶胶-凝胶法成功地生成了C12A7 结构, 氯负离子是材料中存储的主要负离子. 此外, 从C12A7-Cl-晶体材料表面发射的氯负离子也被飞行时间质谱观测到. 上述结果说明溶胶-凝胶法可被用于制备C12A7-Cl-晶体材料.     

溶胶-凝胶法制备氧化铝光学薄膜

氧化铝薄膜性能优异,具有较高的介电常数、高热导率、抗辐照能力强、抗碱离子渗透能力强以及在很宽的波长范围内透明等性能。因此,氧化铝薄膜广泛地应用于微电子器件、电致发光器件、光波导器件以及抗腐蚀涂层等众多领域[1]。特别是氧化铝光学薄膜具有高的抗激光损伤阈值[2],用     

溶胶-凝胶法制备光学杂化功能材料

在简述溶胶-凝胶法基本原理的基础上,介绍了设计杂化材料的原则及预掺杂法、后掺杂法和原位化学合成法三种溶胶-凝胶法制备光学杂化功能材料的途径;综述了稀土发光材料、波导材料和光致变色材料三种光学杂化功能材料,并结合国内外的研究提出开展光学杂化功能材料研究的重要方向.     

溶胶-凝胶法制备Bi-Pb-Sr-Ca-Cu-O微粉

以金属醋酸盐为原料,用溶胶-凝胶技术制备了Bi-Pb-Sr-Ca-Cu-O微粉,并用TG、DTA、IR、XRD和TEM等手段对Bi_1.85Pb_0.35Sr_1.9Ca₂Cu_3.1O_y粉末的热分解和晶化行为以及粉末粒度进行了分析测试,并用此微粉制备出以2223相为主要物相、零电阻为105K的高温陶瓷超导体。     

溶胶-凝胶法制备含偶氮生色团的三阶非线性材料

通过溶胶-凝胶法制备了含三阶非线性光学发色团DRl9硅氧烷染料的有机-无机复合材料(3),其结构经1H NMR和IR表征.研究了pH值对3微观形态及光学性能的影响.     

溶胶-凝胶法制备功能陶瓷超微粉末

陶瓷超微粉末的研究是目前高技术领域中的一项重要课题。溶胶-凝胶法是近几年来才开发的一种制备陶瓷超微粉末的新技术。应用该方法所合成的粉末纯度高、化学成份均匀、颗粒度小且分布范围窄,易烧结成致密的陶瓷体,尤其对于多元陶瓷粉末的制备这些优点更为突出。因而对该方法的研究及应用已引起人们的普遍重视。PbTiO_3、BaTiO_3和Pb(Zr,Ti)O_3作为陶瓷压电材料广泛应用于电子信息技术和光电技术领域;有关它们的研究报道甚多。     

溶胶-凝胶模板法制备钛酸钡纳米管

采用氢氧化钡和钛酸四丁酯为前驱体, 溶胶-凝胶结合模板法制备了钛酸钡纳米管, 通过SEM, TEM, XPS和XRD等表征分析, 钛酸钡纳米管直径100 nm, 钛酸钡为立方相结构, 晶胞参数a＝3.995 Å.     

溶胶-凝胶工艺制备发光薄膜研究进展

本文综述了通过深胶－凝胶工艺制备发光薄膜的基本过程、薄膜的表征方法、发光薄膜的当前发展及应用情况。依据组成特点,对溶胶－凝胶法制备的发光薄膜乾地了分类阐述,并预言了今后该法制备发光薄膜的发展趋势。     

金属离子水化学-溶胶凝胶法制备固体催化材料的化学基础

简要介绍了作为溶胶凝胶法制备固体催化材料的化学基础的金属离子水化学进展.     

溶胶-凝胶法制备疏水型超低折射率膜层材料

以正硅酸乙酯(TEOS)和甲基三乙氧基硅烷(MTES)为共同前驱体,羟丙基-β-环糊精(HPCD)为致孔剂,水和乙醇为溶剂,氨水为催化剂,采用溶胶-凝胶法制备了HPCD-Si O2溶胶.溶胶经过六甲基二硅氮烷(HMDS)改性后,制得疏水型超低折射率膜层,其最低折射率可达1.05,静态水接触角从66.4°上升至128.7°.以羟丙基-β-环糊精为致孔剂制得的膜层孔径约为4 nm,因而膜层不会因为孔径接近光波长的1/4而引起散射.与传统的致孔剂泊洛沙姆(F127)等相比,羟丙基-β-环糊精具有致孔效率高及折射率更低等优点,在模板剂领域具有广泛的应用前景.     

C12A7-O-纳米材料的制备及抗菌活性

利用溶胶-凝胶法制备了C12A7-O-{[Ca24Al28O64]4+·4(O-)}纳米材料. 采用X射线衍射、电子顺磁共振及透射电子显微镜等手段对制备的材料进行了表征. 结果表明, 在最佳焙烧条件(1150 ℃, 6 h)下制备的材料平均粒径为74 nm, 并具有晶胞参数为(1.199±0.004) nm的C12A7(Ca12Al14O33)笼状结构, 材料内包含浓度高达1.2×1020 cm-3的氧负离子(O-). 初步研究结果表明, 合成的C12A7-O-纳米材料具有良好的广谱抗菌作用.     

微孔晶体材料C12A7-Cl-的表面氯负离子发射性能和机理

利用飞行时间质谱(TOF-MS)观测到氯负离子从合成的微孔晶体材料C12A7-Cl-(11CaO·7Al2O3·CaCl2)表面发射出来, 详细研究了C12A7-Cl-的发射特性, 包括发射强度分支比、温度效应、电场效应和表观活化能. 在我们的检测范围内从C12A7-Cl-表面发射的离子中绝大部分是氯负离子(最大强度分支比为98%), 此外还有弱的氧负离子和电子发射. 各种离子的绝对发射电流强度都随着表面温度升高或引出电场强度的增加而显著增强, 随着引出电场强度从200增加到1200 V·cm-1, 氯负离子发射的表观活化能从180.9 kJ·mol-1减小到110.0 kJ·mol-1. 氯负离子和C12A7-Cl-表面之间的结合能大约是228 kJ·mol-1. 研究了氯负离子的发射稳定性, 并且应用一种电化学注入法, 以获得持续的氯负离子发射. 基于上述实验还讨论了氯负离子的形成和发射机理. 目前的方法可望被用于发展氯负离子储存/发生器.     

C12A7-Mg催化剂水蒸汽重整生物油、石脑油和CH4制氢

Hydrogen production by catalytic steam reforming of the bio-oil, naphtha, and CH4 was investigated over anovel metal-doped catalyst of (Ca24Al28O64)4+￠4O-/Mg (C12A7-Mg). The catalytic steam reforming wasinvestigated from 250 to 850 ±C in the ˉxed-bed continuous °ow reactor. For the reforming of bio-oil, theyield of hydrogen of 80% was obtained at 750 ±C, and the maximum carbon conversion is nearly close to95% under the optimum steam reforming condition. For the reforming of naphtha and CH4, the hydrogenyield and carbon conversion are lower than that of bio-oil at the same temperature. The characteristics ofcatalyst were also investigated by XPS. The catalyst deactivation was mainly caused by the deposition ofcarbon in the catalytic steam reforming process.     

C12A7-MgO催化剂上的生物油裂解制氢

Catalytic steam reforming of condensable vapors, i.e. bio-oil, derived from pyrolysis of biomass is an important process for hydrogen production, which is expected to form renewable and clean energy. The generation of hydrogen from bio-oil was investigated from 250 to 750 ℃ by a MgO mixed C12A7-O-(C12A7-MgO) catalyst in a fixed-bed micro-reactor. The hydrogen yield on C12A7-MgO was about 44% at 750 ℃. It is found that both the catalytic activity and catalysis life are improved by doping MgO. The XRD results show that the C12A7 structure of the positively charged lattice framework remains in the C12A7-MgO catalyst.     

Characterization of C12A7-O- Catalyst and Mechanism of Phenol Formation by Hydroxylation of Benzene

The benzene conversion and phenol selectivity from C6H6/O2/H2O over Ca24Al28O644+·4O-(C12A7-O-) catalyst were investigated using a flow reactor. The benzene conversion increases with the increase of temperature, and the phenol selectivity mainly depends on both reaction temperature and the composition of the mixtures. The changes of the catalyst structure before and after the reactions and the intermediates on the catalyst surface and in the bulk were investigated by XRD, EPR and FT-IR. The catalytic reactions do not cause any damage to the structure of the positively charged lattice framework C12A7-O-, but part of the O- and O2- species in the bulk of C12A7-O- translate to OH- after the reactions. The neutral species and anion intermediate were investigated by Q-MS and TOF-MS respectively. It is suggested that the active O- and OH- species played a key role in the process of phenol formation.     

Na2O掺杂C12A7材料的结构及其抗菌性能

本文利用溶胶-凝胶方法制备了Na2O掺杂的C12A7(12CaO.7Al2O3-Na2O)材料,通过X-射线衍射(XRD)、电子顺磁共振(EPR)、电感等离子体耦合-原子发射光谱(ICP-AES)和飞行时间质谱(TOF-MS)研究了材料结构与性能。选用金黄色葡萄球菌和大肠杆菌为受试菌种,研究了C12A7-Na2O的抗菌性能。结果表明,Na2O掺杂对C12A7的晶体结构以及材料中的氧负离子的浓度没有显著的影响,且C12A7-Na2O材料具有较高的抗菌性能。利用扫描电镜(SEM)对杀菌前后的金黄色葡萄球菌和大肠杆菌的菌体形态进行了观测,初步探讨了C12A7-Na2O的抗菌机理。     

掺杂Cs元素的微孔晶体材料C12A7的表征及负离子发射特性

利用浸渍CsI的方法在微孔晶体材料12CaO·7Al₂O₃ (C12A7)表面掺杂Cs元素并对其进行场发射扫描电镜、透射电子显微镜、X射线衍射以及电子顺磁共振的表征. 场发射扫描电镜以及透射电子显微镜的结果均证实CsI沉积在C12A7的表面; X射线衍射证明C12A7的结构并没有被破坏; 电子顺磁共振谱说明了浸渍后C12A7中的O^-和O₂^-浓度也无明显变化. 将浸渍后的同原始的C12A7进行比较发现, 掺杂样品在结构和存储特性上均无明显变化. 此外, 对该材料的发射性能与温度和引出场的关系也进行了研究与分析. 结果表明: 浸渍CsI至C12A7表面不仅降低了氧负离子的发射温度, 还大幅增强了发射强度; 氧负离子发射增强的主要原因归结于浸渍CsI后其表观活化能的降低.     

Darstellung und Charakterisierung der Fulleren-Kokristallisate C60 · 12 C6H12, C70 · 12 C6H12, C60 · 12 CCl4, C60 · 2 CHBr3, C60 · 2 CHCl3, C60 · 2 H2CCl2

Synthesis and Characterization of the Fullerene Co-Crystals C₆₀ · 12 C₆H₁₂, C₇₀ · 12 C₆H₁₂, C₆₀ · 12 CCl₄, C₆₀ · 2CHBr₃, C₆₀ · 2CHCl₃, C₆₀ · 2H₂CCl₂ By crystallization of fullerenes from non-polar solvents (C₆H₁₂, CCl₄, CHBr₃, CHCl₃, H₂CCl₂) compounds of the following compositions were obtained: C₆₀ · 12C₆H₁₂, C₇₀ · 12C₆H₁₂, C₆₀ · 12CCl₄, C₆₀ · 2CHCl₃, C₆₀ · 2CHBr₃ and C₆₀ · 2H₂CCl₂. Lattice parameters have been determined by X-ray diffraction of powder samples; according to single-crystal examinations on C₆₀ · 12C₆H₁₂, C₆₀ · 12CCl₄ and C₆₀ · 2CHBr₃ the fullerene is orientationally disordered. C₆₀ · 12C₆H₁₂, cubic, a = 28.167(1) Å; C₇₀ · 12C₆H₁₂, cubic, a = 28.608(2) Å; C₆₀ · 12CCl₄, cubic, a = 27.42(1) Å; C₆₀ · 2CHBr₃, hexagonal, a = 10.212(1), c = 10.209(1) Å; C₆₀ · 2CHCl₃, hexagonal, a = 10.08(1), c = 10.11(2) Å; C₆₀ · 2H₂CCl₂, tetragonal, a = 16.400(1) Å, c = 11.645(7) Å.     

C5~C7烃类组分在Al2O3毛细管色谱柱上的分离及应用

详细研究了54种常见的C₅~C₇烃类组分在S型、KCl型和M型3种类型Al₂O₃毛细管色谱柱上的分离和定性,结果显示大部分C₅~C₇烃类组分在3种类型Al₂O₃毛细管色谱柱上的分离效果良好,但也存在一些组分分离不完全或共流出的现象,3种类型Al₂O₃毛细管色谱柱上的分离效果也存在一定的差异。共测定了15个C₅烃类组分,25个C₆烃类组分及14个C₇烃类组分在这3种类型Al₂O₃毛细管色谱柱上的线性程序升温保留指数,为C₅~C₇烃类组分在Al₂O₃毛细管色谱柱上的定性提供了依据。同时定量分析了某石化企业的裂解气样品中C₅~C₇烃类组分的含量。本研究拓展了Al₂O₃毛细管色谱柱的应用范围,可以为石化企业轻烃的分析提供参考。