End‐group modification of poly(2,6‐dimethyl‐1,4‐phenylene ether) and in situ synthesis of poly(2,6‐dimethyl‐1,4‐phenylene ether)‐b‐poly(ethylene terephthalate) block copolymer

The preparation of poly(2,6‐dimethyl‐1,4‐phenylene ether)‐b‐poly(ethylene terephthalate) block copolymer was performed by the reaction of the 2‐hydroxyethyl modified poly(2,6‐dimethyl‐1,4‐phenylene ether) (PPE‐EtOH) with poly(ethylene terephthalate) (PET) by an in situ process, during the synthesis of the polyester. The yield of the reaction of the 2‐hydroxyethyl functionalized PPE‐EtOH with PET was close to 100%. A significant proportion of the PET‐b‐PPE‐EtOH block copolymer was found to have short PET block. Nevertheless, the copolymer structured in the shape of micelles (20 nm diameter) and very small domains with 50–200 nm diameter, whereas unmodified PPE formed much larger domains (1.5 μm) containing copolymer. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3985–3991, 2008     

A Novel Approach to the Preparation of Nanoblends of Poly(2,6‐dimethyl‐1,4‐phenylene oxide)/Polyamide 6

Summary: A novel approach of in situ polymerization and in situ compatibilization was adopted to prepare poly(2,6‐dimethyl‐1,4‐phenylene oxide) (PPO) and polyamide 6 (PA6) nanoblends. Anionic ring‐opening polymerization of ε‐caprolactam was carried out in the presence of PPO, the chain of which bore p‐methoxyphenylpropionate (MPAA), acting as macroactivator to initiate PA6 chain growth from the PPO chain and form a graft copolymer of PPO and PA6 and pure PA6 simultaneously. The nanostructured PA6 dispersed phase in the PPO matrix could be achieved.

A TEM image of poly(2,6‐dimethyl‐1,4‐phenylene oxide)/polyamide 6 nanoparticles obtained from in situ polymerization and in situ compatibilization.     

Synthesis of new thermosetting poly(2,6‐dimethyl‐1,4‐phenylene oxide)s containing epoxide pendant groups

A new class of thermosetting poly(2,6‐dimethyl‐1,4‐phenylene oxide)s containing pendant epoxide groups were synthesized and characterized. These new epoxy polymers were prepared through the bromination of poly(2,6‐dimethyl‐1,4‐phenylene oxide) in halogenated aromatic hydrocarbons followed by a Wittig reaction to yield vinyl‐substituted polymer derivatives. The treatment of the vinyl‐substituted polymers with m‐chloroperbenzoic acid led to the formation of epoxidized poly(2,6‐dimethyl‐1,4‐phenylene oxide) with variable pendant ratios, and the structures and properties were studied with nuclear magnetic resonance spectroscopy, Fourier transform infrared spectroscopy, differential scanning calorimetry, thermogravimetric analysis, and gel permeation chromatography. The ratios of pendant functional groups were tailored for the polymer properties, and the results showed that the glass‐transition temperatures increased as the benzylic protons were replaced by bromo‐, vinyl‐, or epoxide‐functional groups, whereas the thermal stability decreased in comparison with the original polymer. Within a molar fraction of 20–50%, the degree of functionalization had little effect on the glass‐transition temperature; however, it correlated inversely with the thermal stability of each functionalized polymer. The thermal curing behavior of the epoxide‐functionalized polymer was enhanced by the increment of the pendant functionality, which resulted in a significant increase in the glass‐transition temperature as well as the thermal stability after the curing reaction. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5875–5886, 2006     

Glass‐formation kinetics of miscible blends of atactic polystyrene and poly(2,6‐dimethyl‐1,4‐phenylene oxide)

We present a detailed investigation of the kinetics associated with the glass transitions of miscible blends composed of atactic polystyrene (a‐PS) and poly(2,6‐dimethyl‐1,4‐phenylene oxide) (PPO). According to both dynamic mechanical analysis and differential scanning calorimetry, relaxation times displayed an enhanced temperature dependence (i.e., more fragile or more cooperative behavior) for the blends compared with additive behavior based on the responses of neat a‐PS and PPO. This is consistent with the notion that specific interactions between the blend components heighten the intermolecular cooperativity. The compositional dependence of fragility provided insight into physical aging results for the properties of volume and enthalpy. The combination of our research and a previously reported pressure–volume–temperature study by Zoller and Hoehn (J Polym Sci Polym Phys Ed 1982, 20, 1385) provided evidence that the observation of increased glassy densities for the blends compared with those of the pure polymers was kinetic in origin and was not a feature of the thermodynamics of miscibility. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2118–2129, 2001     

Oxidative polymerization of 2,6‐dimethylphenol to form poly(2,6‐dimethyl‐1,4‐phenylene oxide) in water through one water‐soluble copper(II) complex of a zwitterionic calix[4]arene

In the presence of excess NaOH, reaction of Cu(OAc)₂·H₂O with equimolar ammonium calix[4]arene [H₄L]I₄ ( 1 , H₄L = [5,11,17,23‐tetrakis(trimethylammonium)‐25,26,27,28‐tetrahydroxycalix[4]arene]) resulted in the formation of a mononuclear cationic Cu(II) complex [Cu(II)L(H₂O)]I₂ ( 2 ) in 43% yield. Complex 2 was characterized by elemental analysis, infrared (IR), and single crystal X‐ray diffraction. The Cu(II) atom in 2 is coordinated by four oxygen atoms of one L^4? ligand and one O atom from one water molecule, forming a square pyramidal geometry. Complex 2 exhibited high catalytic activity in the oxidative polymerization of 2,6‐dimethylphenol using O₂ as oxidizing agent in water under mild conditions. The selective polymerization produced poly(2,6‐dimethyl‐1,4‐phenylene oxide) in high yields with almost no diphenoquinone. The influence of the polymerization temperature, the time interval, the molar ratio of 2,6‐dimethylphenol/ 2 , the concentrations of sodium hydroxide, and sodium n‐dodecyl sulfate were examined. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Poly(2,5‐dihydroxy‐1,4‐phenylene benzobisthiazole)/poly(1,4‐phenylene benzobisthiazole) copolymers: Chain packing and properties

Crystal‐packing, optical, and electrical properties of poly(2,5‐dihydroxy‐1,4‐phenylene benzobisthiazole) (DiOH‐PBZT) and copolymers of DiOH‐PBZT/poly(1,4‐phenylene‐benzobisthiazole) (PBZT) were examined. Intramolecular hydrogen bonds between the hydroxyl units and the neighboring nitrogen atoms, as evidenced by the IR spectra, led to the formation of a pseudoladder chain structure and changed the chain packing. The (200) and (010) planes were both affected by the copolymer composition, with the (200) plane spacing increasing from 5.895 to 6.482 Å and the (010) plane spacing decreasing from 3.539 to 3.404 Å with the transition from the unsubstituted PBZT homopolymer to the DiOH‐PBZT homopolymer. The cell dimensions of the copolymers were simple averages of those of the individual homopolymers, suggesting the isomorphic crystal structure formation of the two units. The c‐axis spacing, however, remained unchanged. The increase in the conjugation length of the copolymers as the dihydroxy content increased was confirmed by the bathochromic shift of the absorption band in the ultraviolet–visible spectra. The intrinsic conductivities of the copolymers were 3 orders of magnitude higher than that of the unsubstituted PBZT. © 2001 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 559–565, 2001     

Copolymerization of poly(vinyl alcohol)‐graft‐poly(1,4‐dioxan‐2‐one) with designed molecular structure by a solid‐state polymerization method

Poly(vinyl alcohol)‐graft‐poly(1,4‐dioxan‐2‐one) (PVA‐g‐PPDO) with designed molecular structure was synthesized by a solid‐state polymerization. The solid‐state copolymerization was preceded by a graft copolymerization of PDO initiated with PVA as a multifunctional initiator, and Sn (Oct)₂ as a coininitiator/catalyst in a homogeneous molten state. The polymerization temperature was then decreased and the copolymerization was carried out in a solid state. The products prepared by solid‐state polymerization were characterized by ¹H NMR and DSC, and were compared with those synthesized in the homogeneous molten state. The degree of polymerization (D_p), degree of substitution (D_s), yield and the average molecular weight of the graft copolymer with different molecular structure were calculated from the ¹H NMR spectra. The results show that the crystallization process during the solid‐state polymerization may suppress the undesirable inter‐ or intramolecular side reactions, then resulting in a controlled molecular structure of PVA‐g‐PPDO. The results of DSC measurement show that the molecular structures determine the thermal behavior of the PVA‐g‐PPDO. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3083–3091, 2006     

Structural Diversity in the Self‐assembly of Cd(II) Complexes Containing 2,6‐Dimethyl‐3,5‐dicyano‐4‐(4‐pyridyl)‐1,4‐dihydropyridine

The syntheses, structures and properties of the complexes [CdBr₂( L )₂·4H₂O]_n [ L = 2,6‐dimethyl‐3,5‐dicyano‐4‐(4‐pyridyl)‐1,4‐dihydropyridine], 1 and [Cd(SCN)₂( L )₂(H₂O)]_n, 2 , are reported. In polymeric complexes 1 — 2 , the L ligands bridge the metal centers through the pyrimidyl and cyano nitrogen atoms forming 1‐D double‐stranded chain and zigzag chain, respectively. The L ligands in complex 1 act as κ1, κ1‐bidentate bridging ligand, whereas the L ligands in complex 2 act as κ1‐monodentae and κ1, κ1‐bidentate bridging ligand. The molecules of these complexes are interlinked through various weak interactions that form the packed structure. All the complexes exhibit emissions which may be tentatively assigned as intraligand (IL) π→π* transitions.     

Cancer‐associated pH‐responsive tetracopolymeric micelles composed of poly(ethylene glycol)‐b‐poly(L‐histidine)‐b‐poly(L‐lactic acid)‐b‐poly(ethylene glycol)

To create a novel vector for specifically delivering anticancer therapy to solid tumors, we used diafiltration to synthesize pH‐sensitive polymeric micelles. The micelles, formed from a tetrablock copolymer [poly(ethylene glycol)‐b‐poly(L ‐histidine)‐b‐poly(L ‐lactic acid)‐b‐poly(ethylene glycol)] consisted of a hydrophobic poly(L ‐histidine) (polyHis) and poly(L ‐lactic acid) (PLA) core and a hydrophilic poly(ethylene glycol) (PEG) shell, in which we encapsulated the model anticancer drug doxorubicin (DOX). The robust micelles exhibited a critical micellar concentration (CMC) of 2.1–3.5 µg/ml and an average size of 65–80 nm pH 7.4. Importantly, they showed a pH‐dependent micellar destabilization, due to the concurrent ionization of the polyHis and the rigidity of the PLA in the micellar core. In particular, the molecular weight of PLA block affected the ionization of the micellar core. Depending on the molecular weight of the PLA block, the micelles triggering released DOX at pH 6.8 (i.e. cancer acidic pH) or pH 6.4 (i.e. endosomal pH), making this system a useful tool for specifically treating solid cancers or delivering cytoplasmic cargo in vivo. Copyright © 2008 John Wiley & Sons, Ltd.     

One‐Pot Synthesis of 1,4‐Oxathiino[2,3‐b]quinoxalines or ‐pyrazines from 2,3‐Dichloroquinoxaline or ‐pyrazine and 1‐Aryl‐2‐bromoalkan‐1‐ones

An efficient one‐pot synthesis of novel heterocyclic derivatives, 2‐aryl‐1,4‐oxathiino[2,3‐b]quinoxalines or ‐pyrazines 5 , via the reaction of 2,3‐dichloroquinoxaline or ‐pyrazine with Na₂S?9 H₂O, and subsequent treatment of the resulting 2‐chloro‐3‐sodiosulfanylquinoxaline or ‐pyrazine 2 with 1‐aryl‐2‐bromo‐1‐alkanones and then NaH under mild conditions is described.     

A Facile Method for the Synthesis of Hydrazine‐4‐oxothiazolidine and Imino‐5‐oxothiadiazine Derivatives from 1,4‐Disubstituted Thiosemicarbazides

1,4‐Disubstituted thiosemicarbazides reacted with dimethyl acetylenedicarboxylate with formation of (2‐hydrazono‐4‐oxothiazolidin‐5‐ylidene)acetates and, in one case, a (2‐imino‐1,3,4‐thiadiazin‐5‐on‐6‐ylidene)acetate. Several mechanistic options involving nucleophilic interaction are presented. The structures of all newly synthesized compounds were identified by ¹H NMR, ¹³C NMR, COSY, HMQC and HMBC spectral data.     

Isomerization polymerization and copolymerization of glycidyl alkanoates catalyzed by methylaluminum bis(2,6‐di‐t‐butyl‐4‐methylphenoxide)

The isomerization polymerizations of glycidyl propionate (1b), octanoate (1c), and stearate (1d) with methylaluminum bis(2,6‐di‐tert‐butyl‐4‐methylphenoxide) (3) were investigated. The polymerizations selectively gave poly(2‐alkyl‐1,3‐dioxolane‐4,2‐diyloxymethylene)s (2), although the polymer yield as well as the polymer molecular weight significantly decreased as the acyl chain of 1 was lengthened. These polymers readily hydrolyzed to glycerin and the corresponding fatty acids under mild conditions. The copolymerizations of glycidyl acetate (1a) with these monomers were also examined. In any combination, the composition of the obtained copolymer was essentially identical with the feed ratio, while both copolymer yield and molecular weight decreased as the feed of 1a was decreased. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 435–444, 1999 (See graphics.)     

Synthesis and properties of new polyarylates from 1,4‐bis(4‐carboxyphenoxy)naphthyl or 2,6‐bis(4‐carboxyphenoxy)naphthyl and various bisphenols

New 1,4‐naphthyl and 2,6‐naphthyl‐containing polyarylates having inherent viscosities up to 1.28 dL/g were synthesized by the high‐temperature solution polycondensation from the acid chloride of 1,4‐bis(4‐carboxyphenoxy)naphthyl or 2,6‐bis(4‐carboxyphenoxy)naphthyl and various bisphenols. Most of the resulting polyarylates showed amorphous characteristics and were readily soluble in common organic solvents such as N,N‐dimethylacetamide (DMAc), N‐methyl‐2‐pyrrolidone (NMP), o‐chlorophenol, and chloroform. Transparent, flexible, and colorless films of these polymers could be cast from the DMAc solutions. Their cast films had tensile strengths ranging from 54.9 to 84.2 MPa, elongations at break from 5.3% to 19.0%, and initial modulus from 2.0 to 2.8 GPa. These polymers had glass transition temperatures in the range of 172–280°C and began to lose weight around 400°C, with 10% weight loss being recorded at about 450°C in air. Dynamic mechanical analysis (DMA) reveals that the polyarylates containing isopropylidene linkages have three transitions on the temperature scale between −100 and 300°C. However, only two transitions were observed in the other polyarylates without isoproylidene linkage. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 645–652, 1999     

Rapid ring‐opening polymerization of 1,4‐dioxan‐2‐one initiated by titanium alkoxides

Ring‐opening polymerization of 1,4‐dioxan‐2‐one in bulk was initiated by three titanium alkoxides, titanium dichlorodiisopropoxide (TiCl₂(OiPr)₂), titanium chlorotriisopropoxide (TiCl(OiPr)₃), and titanium tetraisopropoxide (Ti(OiPr)₄). The results indicate that the polymerization rate increased with number of OiPr groups in the initiator. High conversion of monomer (90%) and high molecular weight (11.9 × 10⁴ g/mol) of resulting polymer can be achieved in only 5 min at 60 °C with Ti(OiPr)₄ as an initiator. Analysis on nuclear magnetic resonance (NMR) spectra suggests the initiating sites for TiCl₂(OiPr)₂, TiCl(OiPr)₃, and Ti(OiPr)₄ to be 1.9, 2.6, and 3.8, respectively. Coordination‐insertion mechanism for the polymerization via cleavage of the acyl–oxygen bonds of the monomer was proved by NMR investigation. Kinetic studies indicate that polymerization initiated by Ti(OiPr)₄ followed a first‐order kinetics, with an apparent activation energy of 33.7 kJ/mol. It is noteworthy that this value is significantly lower than earlier reported values with other catalysts, namely La(OiPr)₃ (50.5 kJ/mol) and Sn(Oct)₂ (71.8 kJ/mol), which makes it an attractive catalyst for reactive extrusion polymerization. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Thermoplastic elastomers based on poly(l‐Lysine)‐Poly(ε‐Caprolactone) multi‐block copolymers

Novel thermoplastic elastomers based on multi‐block copolymers of poly(l ‐lysine) (PLL), poly(N‐ε‐carbobenzyloxyl‐l ‐lysine) (PZLL), poly(ε‐caprolactone) (PCL), and poly(ethylene glycol) (PEG) were synthesized by combination of ring‐opening polymerization (ROP) and chain extension via l ‐lysine diisocyanate (LDI). SEC and ¹H NMR were used to characterize the multi‐block copolymers, with number‐average molecular weights between 38,900 and 73,400 g/mol. Multi‐block copolymers were proved to be good thermoplastic elastomers with Young's modulus between 5 and 60 MPa and tensile strain up to 1300%. The PLL‐containing multi‐block copolymers were electrospun into non‐woven mats that exhibited high surface hydrophilicity and wettability. The polypeptide–polyester materials were biocompatible, bio‐based and environment‐friendly for promising wide applications. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 3012–3018     

The synthesis,characterization, and crystal structures of poly(2,6‐naphthalenebenzobisoxazole) and poly(1,5‐naphthalenebenzobisoxazole)

The rigid‐rod polymers, poly(2,6‐naphthalenebenzobisoxazole) (Naph‐2,6‐PBO) and poly(1,5‐naphthalenebenzobisoxazole) (Naph‐1,5‐PBO) were synthesized by high temperature polycondensation of isomeric naphthalene dicarboxylic acids with 4,6‐diaminoresorcinol dihydrochloride in polyphosphoric acid. Expectedly, these polymers were found to have high thermal as well as thermooxidative stabilities, similar to what has been reported for other polymers of this class. The chain conformations of Naph‐2,6‐PBO and Naph‐1,5‐PBO were trans and the crystal structures of Naph‐2,6‐PBO and Naph‐1,5‐PBO had the three‐dimensional order, although the axial disorder existed for both Naph‐2,6‐PBO and Naph‐1,5‐PBO. Naph‐2,6‐PBO exhibited a more pronounced axial disorder than Naph‐1,5‐PBO because of its more linear shape. The repeat unit distance for Naph‐2,6‐PBO (14.15 Å) was found to be larger compared with that of Naph‐1,5‐PBO (12.45 Å) because of the more kinked structure of the latter. The extents of staggering between the adjacent chains in the ac projection of the crystal structure were 0.25c and 0.23c for Naph‐2,6‐PBO and Naph‐1,5‐PBO, respectively. Naph‐1,5‐PBO has a more kinked and twisted chain structure relative to Naph‐2,6‐PBO. The kinked and twisted chain structure of Naph‐1,5‐PBO in the crystal seems to prevent slippage between adjacent chains in the crystal structure. The more perfect crystal structure of Naph‐1,5‐PBO may be due to this difficulty in the occurrence of the slippage. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1948–1957, 2006     

Transesterification kinetics of poly(ethylene terephthalate) and poly(ethylene 2,6‐naphthalate) blends with the addition of 2,2′‐bis(1,3‐oxazoline)

The kinetics of the transesterification reaction between poly(ethylene terephthalate) (PET) and poly(ethylene 2,6‐naphthalate) (PEN) with and without the addition of a chain extender were studied with ¹H NMR. Different kinetic approaches were considered, and a second‐order, reversible reaction was accepted for the PET/PEN reactive blend system. The addition of 2,2′‐bis(1,3‐oxazoline) (BOZ) promoted the transesterification reaction between PET and PEN in the molten state. The activation energy of the transesterification reaction for the PET/PEN reactive blend with BOZ (94.0 kJ/mol) was lower than that without BOZ (168.9KJ/mol). The rate constant k took an almost constant value for blend samples with different compositions mixed at 275 °C. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2607–2614, 2001     

Synthesis and nuclear magnetic resonance analysis of starch‐g‐poly(1,4‐dioxan‐2‐one) copolymers

A new biodegradable starch graft copolymer, starch‐g‐poly(1,4‐dioxan‐2‐one), was synthesized through the ring‐opening graft polymerization of 1,4‐dioxan‐2‐one onto a starch backbone. The grafting reactions were conducted with various 1,4‐dioxan‐2‐one/starch feed ratios to obtain starch‐g‐poly(1,4‐dioxan‐2‐one) copolymers with various poly(1,4‐dioxan‐2‐one) graft structures. The microstructure of starch‐g‐poly(1,4‐dioxan‐2‐one) was characterized in detail with one‐ and two‐dimensional NMR spectroscopy. The effect of the feed composition on the resulting microstructure of starch‐g‐poly(1,4‐dioxan‐2‐one) was investigated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3417–3422, 2004     

Crystallinity and crystalline phase orientation of poly(1,4‐cis‐isoprene) from Hevea brasiliensis and Taraxacum kok‐saghyz

Crystallization is studied for poly(isoprene‐1,4‐cis) from Hevea brasiliensis (natural rubber [NR]) and from taraxacum kok‐saghyz, mainly by collecting wide‐angle X‐ray diffraction patterns after processing and stretching. Although rubber samples before stretching are generally fully amorphous, crystallization can be induced in NR samples by processing at room temperature under moderate pressure. This phenomenon is possibly associated with nucleation by saturated fatty acid components. For rubber samples being fully amorphous in the undeformed state, strain‐induced crystallization occurs only at high strain ratios (α > 4), leading to high degrees of crystalline phase orientation (f_c > 0.9 for α = 5). Rubber samples presenting some crystallinity already in the unstretched state, on the contrary, reach much lower degrees of axial orientation, even for high strain ratios (f_c < 0.7 for α = 5). These differences in crystallinity and in crystalline phase orientations produce large differences in stress–strain behavior of the rubber. By room temperature processing, the considered NR samples can also develop an unreported disordered crystalline modification, with low intensity of 120 and 121 reflections. This disordered crystalline modification, which is also maintained after axial stretching procedures, can rationalized by a structural disorder along the b axis, possibly associated with statistical sequences of A⁺TA^? or A^?T A⁺ conformations for poly(isoprene‐1,4‐cis) chains. Copyright © 2016 John Wiley & Sons, Ltd.     

Chain composition dependence of luminescence properties for copolymers of 2‐methoxy‐5‐2′‐ethyl‐hexyloxy‐1,4‐phenylenevinylene and 2,3‐diphenyl‐5‐octyl‐1,4‐phenylenevinylene

The copolymers of 2‐methoxy‐5‐2′‐ethyl‐hexyloxy‐1,4‐phenylenevinylene (MEH‐PV) and 2,3‐diphenyl‐5‐octyl‐1,4‐phenylenevinylene were prepared via the Gilch route with their chain compositions and the reactivity ratios of the monomers estimated by ¹H NMR spectroscopy. The results indicated that the copolymers tended to form an alternative copolymer as the feed ratio of the monomers closed to one‐half. When an individual copolymer solution in tetrahydrofuran was spun‐cast to form a film, the MEH‐PV units were able to attract the like units from the adjacent chains. As a result, the ultraviolet–visible absorption spectrum of the alternative copolymer in film form was broader than the spectra of those with different compositions. The photoluminescence spectra of the copolymers in film form exhibited the characteristic shoulder of poly(2‐methoxy‐5‐2′‐ethyl‐hexyloxy‐1,4‐phenylenevinylene), even though the content of MEH‐PV units was not great enough for the formation of repeat units in sequence. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2180–2186, 2003