具有宽过冷液相区的Fe62Co8—x（Cr,Mo）xNb4Zr6B20非晶态合金的热稳定性与磁性

根据制备块状非晶态合金的三条经验准则,选择了成分为Fe62Co8-xCrxNb4Zr6B20和Fe62Co8-xMoxNb4Zr6B20(x=0,2,4)的合金系,利用单辊急冷法制备出厚为30μm宽为5mm左右的条带,并用差热分析,X射线衍射以及Faraday磁天平,静态磁性测量仪等研究了合金的热稳定性,非晶结构和磁性能,发现含2at%Cr的Fe62Co6Cr2Nb4Zr6B20非晶态合金的过冷液相区ΔTx最宽,达到85K,但是合金系的饱和磁比强度σs随Cr或Mo含量的增加而急剧下降,合金系经973K真空退火900s后,由于晶化相α-Fe等晶相析出,使得合金的σs和Hc都迅速升高。     

具有宽过冷液相区的Fe62Co8-x(Cr,Mo)xNb4Zr6B20非晶态合金的热稳定性与磁性

根据制备块状非晶态合金的三条经验准则,选择了成分为Fe₆₂Co_8-xCr_xNb₄Zr₆B₂₀和Fe₆₂Co_8-xMo_xNb₄Zr₆B₂₀(x=0,2,4)的合金系.利用单辊急冷法制备出厚为30μm宽为5mm左右的条带,并用差热分析、X射线衍射以及 关键词： 过冷液相区 铁磁性 非晶态合金     

a—Fe—(Co,Cr)—Zr系列合金的穆斯堡尔谱研究

本文研究了a-Fe_90-xCo_xZr₁₀(x=4,10,20,…,70)和Fe_90-yCr_yZr₁₀(y=0,4,7,16,20)系列合金的M?ssbaner谱。实验结果表明a-Fe_90-yCo_yZr₁₀和富Fe区(x<30)的a-Fe_90-xCo_xZr_{10 关键词：}     

非晶态RE—TM(RE=Nd,Pr,TM=Fe,Co,Ni)薄膜的磁性和Pr的变价行为

本文通过对非晶态轻稀土Pr,Nd和过渡族金属Fe,Co,Ni薄膜合金的低温磁性研究,分别得到了(Pr,Nd)_x-(Fe,Co,Ni)_1-x合金中Pr,Nd和Fe,Co,Ni金属磁矩随成份x的变化,并且通过对磁矩的研究得到Pr离子的4f电子可能有退局域化的结论。 关键词：     

辐照诱发中间相Zr(Cr,Fe)2非晶化的原位电子显微研究

 在美国Argonne国家实验室连接有IVEM-Tandem National Facility加速器的Hitatch3000电子显微镜上，通过能量600keV及注量率为2.5×10¹²cm^-2·s^-1的Ne离子原位辐照,研究了锆-4合金中沉淀相hcp Zr(Cr,Fe)₂的重离子辐照效应，结果表明：600keV的Ne离子在350℃原位辐照至0.2dpa时，hcp-Zr(Cr,Fe)₂沉淀相的层错条纹开始消失；0.8dpa时沉淀相的电子衍射斑点大部分消失，发生明显的化学无序；2.7dpa时明场像衬度完全消失，非晶环已非常明显，表明沉淀相已经非晶化。600keV的Ne离子在350℃辐照hcp-Zr(Cr,Fe)₂相非晶化的临界损伤离位率约为2.7dpa。     

辐照诱发中间相Zr(Cr,Fe)2非晶化的原位电子显微研究

在美国Argonne国家实验室连接有IVEM-Tandem National Facility加速器的Hitatch3000电子显微镜上,通过能量600keV及注量率为2.5×1012cm-2·s-1的Ne离子原位辐照,研究了锆-4合金中沉淀相hcp Zr(Cr,Fe)2的重离子辐照效应,结果表明：600keV的Ne离子在350℃原位辐照至0.2dpa时,hcp-Zr(Cr,Fe)2沉淀相的层错条纹开始消失;0.8dpa时沉淀相的电子衍射斑点大部分消失,发生明显的化学无序;2.7dpa时明场像衬度完全消失,非晶环已非常明显,表明沉淀相已经非晶化。600keV的Ne离子在350℃辐照hcp-Zr(Cr,Fe)2相非晶化的临界损伤离位率约为2.7dpa。     

Co2YSn(Y=Ti,Zr)电子结构和轨道磁性的第一性原理研究

基于密度泛函理论(DFT)采用第一性原理的全势能线性缀加平面波(FLAPW)的能带计算方法研究了强磁性Heusler合金Co2TiSn和Co2ZrSn的电子能带结构,在计算中考虑了自旋-轨道藕合(SOC)的修正.计算结果表明两种合金在费米面附近的能带结构是一个d-d电子杂化作用形成的能带.分析计算结果发现Co原子对磁矩有主要的贡献,两种Heusler合金的磁矩是由于Co原子3d eg的自旋劈裂形成的,3deg的自旋向下分量是合金的电子态密度(DOS)的主要来源.由能带计算得到Co2TiSn和Co2ZrSn的自旋磁矩分别为1.97μB和1.96μB,其中Co原子在上述两种合金中的自旋磁矩分别是1.01μB和1.02μB,轨道磁矩分别为0.041μB和0.051μB.     

Full-Heusler合金X2YGa(X=Co,Fe,Ni;Y=V,Cr,Mn)的电子结构、磁性及半金属特性的第一性原理研究

利用基于密度泛函理论的全势线性缀加平面波方法,结合广义梯度近似,对full-Heusler X₂YGa(X=Co,Fe,Ni;Y=V,Cr,Mn)合金的电子结构、磁性及半金属特性进行了研究,并讨论了自旋-轨道耦合作用对它们的影响.计算结果表明,自旋-轨道耦合作用对full-Heusler X₂YGa(X=Co,Fe,Ni;Y=V,Cr,Mn)合金的电子结构,磁性与半金属特性的影响很小. 当未考虑自旋-轨道耦合作用时,Co₂VGa,Co₂CrGa,和Fe₂CrGa合金为半金属或准半金属铁磁体,加入自旋-轨道耦合作用后体系的自旋极化率将降低1%左右, 它们依然保持很高的自旋极化率.Fe₂MnGa,Co₂MnGa,Ni₂CrGa和Ni₂MnGa合金为一般铁磁体,Fe₂VGa和Ni₂VGa合金为顺磁体. 关键词： 半金属特性 自旋-轨道耦合 Heusler合金 全势线性缀加平面波方法(FLAPW)     

Pr2Fe14(C,B)/α-(Fe,Co)型纳米晶复合磁体的结构与磁性

研究了Pr_xFe_82-x-yTi_yCo₁₀B₄C₄ (x=9—10.5;y=0, 2)纳米晶薄带的结构与磁性. 结果表明,所有薄带皆主要由2∶14∶1, 2∶17和α-(Fe, Co)三相组成. 对于y=0的合金,其内禀矫顽力随Pr含量x的增加而增加,剩磁随Pr含量x的增加而减小. 以Ti置换部分Fe (y=2),合金的磁性能得到显著提高,表现为:添加Ti后,合金的剩磁B_r基本不降低,x=10.5时合金的B_r值甚至有较明显的提高;同时添加Ti后,合金的内禀矫顽力及退磁曲线的方形度都明显改善. 当x=10.5,y=2时,合金薄带的磁性能达到最佳值为: B_r=9.6 kGs(1 Gs=10^-4 T),_iH_c =10.2 kOe(1 Oe=79.5775 A/m)和(BH)_max＝17.4 MGOe. 随着Pr含量的提高,合金中的硬磁相2 ∶14 ∶1的含量相对增加,内禀矫顽力提高;而Ti置换Fe抑制了软磁相α-(Fe, Co)在快淬和热处理过程中的优先长大,使合金中软磁相和硬磁相的晶粒尺寸及比例趋向最佳组合,交换耦合作用明显增强. 关键词： 纳米晶永磁材料 2Fe₁₄(C')" href="#">Pr₂Fe₁₄(C B) Ti添加 交换耦合     

Ga2基Heusler合金Ga2XCr(X = Mn,Fe, Co,Ni, Cu)的四方畸变、电子结构、磁性及声子谱的第一性原理计算

运用基于密度泛函理论的第一性原理的方法, 对Ga₂基Heusler合金Ga₂XCr (X = Mn, Fe, Co, Ni, Cu)的四方畸变、电子结构、磁性及声子谱特性进行了系统的研究. 结果表明, 在保持体积不变的四方畸变中, 五种合金的磁矩主要由Cr元素提供; Ga₂FeCr, Ga₂CoCr和Ga₂CuCr保持稳定的立方相, 而在Ga₂MnCr和Ga₂NiCr 中观察到能量更低的四方相, 且其能量最低点对应的c/a分别位于1.28和1.11处, 而对应的能量差ΔE 分别为-8.26 meV和-6.14 meV. 电子结构显示, Ga₂MnCr和Ga₂ NiCr的费米能级附近存在尖锐的电子态密度峰, 导致3d电子能级杂化向宽能量范围扩展, 以消除体系的高能量不稳态, 这个过程导致结构转变的发生. 基于适度的畸变度和能量差, 本文认为Ga₂MnCr有存在铁磁马氏体相变的可能, 其声学支虚频的出现, 也进一步表明体系有声子模软化的行为.     

2: 17型结构Gd-Fe-Co-Ga化合物的结构与磁性

用电弧熔炼的方法制备了Gd₂（Fe_1-xCo_x）₁₅Ga₂（0≤x≤1.0）和Gd₂（Fe_0.8Co_0.2）_17-yGa_y（0≤y≤8）化合物，通过Ｘ射线衍射和磁性测量手段研究了它们的结构和磁性．实验结果表明它们都是2∶17型结构的单相化合物．Gd₂（Fe_{1 关键词：}     

STRUCTURE AND MAGNETIC PROPERTIES OF NITRIDES R3Fe29-xCrxN4

A systematic investigation of nitrides R₃Fe_29-xCr_xN₄(R=Y, Ce, Nd, Sm, Gd, Tb, and Dy) has been performed. The nitrogen concentration in the nitride R₃Fe_29-xCr_xN_y was determined to be y=4. Nitrogenation leads to a relative volume expansion of about 5.3%. The lattice constants and unit cell volume decrease with in creasing rare earth atomic number from Nd to Dy, reflecting the lanthanide contraction. In average, the increase of Curie temperature upon nitrogenation is about 200 K, compared with its parent compound. The nitrogenation also results in a remarkable improvement in the saturation magnetization and anisotropy fields for R₃Fe_29-xCr_xN₄ at 4.2 K and room temperature, comp ared with their parent compounds. A spin reorientation of Nd₃Fe_24.5 Cr_4.5N₄ occurs at around 368 K, which is 138 K higher than that of Nd₃Fe_24.5Cr_4.5.Magnetohistory effects of R₃Fe_29-xCr_xN₄(R=Nd and Sm) are observed in a low field of 0.04 T. First order magneti zation process occurs in Sm₃Fe_24.0Cr_5.0N₄ in magnetic fields of around 3.0 T at 4.2 K. After nitrogenation the easy magnetization direction of Sm₃Fe_24.0Cr_5.0 is changed from the easy cone structure to the uniaxial. The excellent intrinsic magnetic properties of Sm₃Fe_24.0Cr_5.0N₄ make this compound a hopeful candidate for new high performance permanent magnets.     

Mn_(1-x)Zn_xCr_2O_4(0.0≤x≤1.0)晶体结构与磁性研究

通过固相反应法制备了尖晶石氧化物Mn1-xZnxCr2O4(0.0≤x≤1.0)多晶系列样品,并对其晶体结构和磁性进行了系统研究.研究结果表明,系列样品具有立方尖晶石结构,随Zn掺杂浓度x增大,晶格常数单调减小,体系的阻挫因子逐渐增大.低温下MnCr2O4表现为共线亚铁磁和螺旋亚铁磁的共存.当x≤0.4时,随着x增大,4.5T磁场下所测量的磁化强度逐渐减小,矫顽力逐渐增大,表明体系中的螺旋亚铁磁成分逐渐增多.随着x进一步增加,样品x=0.6和0.8表现为自旋玻璃态特征,最终在x=1.0时转变为强阻挫的反铁磁态.     

磁性隧道结Ni80Fe20/Al2O3/Co的制备和物性

用等离子体氧化形成绝缘层的方法,重复性地制备出了Ｎｉ８０Ｆｅ２０／Ａｌ２Ｏ３／Ｃｏ磁性隧道结。样品的隧道磁电阻（ＴＭＲ）比值在室温下最高可达６．０％,翻转场（ｓｗｉｔｃｈ ｆｉｅｌｄ）可低于８００Ａ／ｍ,平台宽度约２４００Ａ／ｍ。结电阻的变化范围从几百欧姆到几百千欧。     

Helium gas-bubble formation and blistering in metallic glass Ni45Fe5Co20Cr10Mo4Bl6

We report here the formation of helium gas bubbles in a nickel based metallic glass Ni₄₅Fe₅Co₂₀Cr₁₀Mo₄B_l6 after 50 keV helium ion irradiations at room temperature studied by transmission electron microscopy. At higher doses bubbles eventually grow and deform the material surface plastically leading to blister formation. Critical dose for blister formation is determined. Helium gas bubble formation is associated with partial crystallisation of the glass which can be observed from selected area diffraction from the region where bubbles are formed. Micro-hardness measurements are also performed on the irradiated samples as a function of dose. Increase in the microhardness has been observed after a dose at which helium bubbles are formed.     

NdFe10M2(M=Mo,Cr)渗C(N)化合物的结构和内禀磁性研究

本文采用气—固反应，将Ｃ、Ｎ原子渗入到ＮｄＦｅ₁₀Ｍ₂结构中的间隙位，不改变它们的ＴｈＭｎ₁₂型结构，进而研究了ＮｄＦｅ₁₀Ｍ_xZ_x（ｚ＝Ｃ，Ｎ）的内禀磁性，Ｃ，Ｎ原子对它们的磁性影响不尽相同，其中ＮｄＦｅ₁₀Ｍｏ₂Ｃ_0.8有单轴各向异性，磁晶各向异性场Ｈ_s＝１１６．０ｋＯｅ。最后对样品进行了穆斯堡尔谱测量，研究了它们的超精细场特性。 关键词：     

POWDER NEUTRON DIFFRACTION STUDIES OF THE CRYSTALLOGRAPHIC AND MAGNETIC STRUCTURE OF Ho2Fe9Ga8 and Ho2Fe9Ga6AI2

The crystallographic and magnetic structures of Ho₂Fe₉Ga₈ and Ho₂Fe₉Ga₆AI₂ were studied by powder neutron diffraction at room temperature. The atom fractional occupancies of Ga and Al and the magnetic moments of Ho and Fe were obtained by using Rietveld analysis program. The magnetic structures of the two samples show an easy-axis anisotropy, with the Fe magnetic moment being ferrimagneticlly coupled to those of Ho.     

Fe40—45Cr30—35Co20—25Mo0—4Zr0—2合金微观结构对矫顽力的影响

研究了高矫顽力型FeCrCo合金的磁性和微观结构.实验结果表明，适当的合金成分及热处理 条件可以明显提高FeCrCo合金的矫顽力.通过透射电镜、x射线衍射等手段得出结论：主体元 素含量的提高和微量元素的掺杂可以有效地控制相的组成，磁场热处理导致强磁性相和弱磁 性相的分离，回火后形成起磁硬化作用的调幅结构.该调幅结构中较大的两相成分差有利于 提高FeCrCo合金的矫顽力. 关键词： 矫顽力 调幅分解 磁场热处理 两相结构 成分差