Effect of P2O5 content in two series of soda lime phosphosilicate glasses on structure and properties - Part I: NMR

The effect of the variation in phosphate (P₂O₅) content on the structure of two series of bioactive glasses in the quaternary system SiO₂-Na₂O-CaO-P₂O₅ was studied. The first series (I) was a simple substitution of P₂O₅ for SiO₂ keeping the Na₂O:CaO ratio fixed (1.00:0.87). The second series was designed to ensure charge neutrality in the orthophosphate , therefore as P₂O₅ was added the Na₂O and CaO content was varied to provide sufficient Na⁺ and Ca²⁺ cations to charge balance the orthophosphate present. The glass network connectivity (NC) was calculated for each glass and a modification for the presence of a separate P₂O₅ phase was included (NC′). ³¹P and ²⁹Si magic-angle-spinning nuclear magnetic resonance (MAS-NMR) spectroscopy was performed on glass series I and II to determine the structural units present and their relation to glass properties. ³¹P MAS-NMR spectra of series I resulted in a broad resonance around 9 ppm corresponding to orthophosphate in an amorphous environment. The 9.25 mol% P₂O₅ glass shown to be partially crystalline by X-ray diffraction was heat treated, and the ³¹P MAS-NMR spectrum showed a sharp peak around 3 ppm corresponding to calcium orthophosphate or sodium pyrophosphate and overlapping broader peaks at 8.5, 10.5 and 14 ppm possibly corresponding to two mixed calcium-sodium orthophosphate phases and amorphous sodium orthophosphate respectively. ³¹P MAS-NMR spectra of series II resulted in a broad resonance around 10.5 ppm corresponding to orthophosphate in an amorphous environment. ²⁹Si MAS-NMR spectra of glasses from series I showed a shift in the resonance peak from around −78 to −86 ppm indicating an increase in Q³ species in the glass and a reduction in Q² with phosphate addition confirming the presence of orthophosphate. The heat treated sample showed a sharp ²⁹Si-NMR resonance at −88 ppm, indicating a crystalline Q² six-membered combeite (Na₂O · 2CaO · 3SiO₂) silicate-type phase, which was confirmed by powder X-ray diffraction. ²⁹Si MAS-NMR spectra of glasses from series II showed no shift in the resonance at around −78 ppm across the series, confirming an orthophosphate environment.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Thermal and some physical properties of glasses in the La2O3−CaO−B2O3 ternary system

Glasses in the La₂O₃−CaO−B₂O₃ ternary system were studied. The glass forming range as determined by the appearance of the annealed cast was found to match previously published findings. Clear glasses were formed in the composition range of 5.7−19.1 mol% La₂O₃ with constant B₂O₃ content of 71.4 mol%, and in glasses of constant La₂O₃:CaO ratio of 1:4 with B₂O₃ content in the range of 71.4-55.0 mol%. The non-linear optical crystalline phase La₂Ca₂B₁₀O₁₉ was crystallized from the clear glasses after heat treatments, as determined by powder XRD. Two types of the LaBO₃ crystalline phases were detected in the partially and the fully crystallized glass compositions outside the glass forming range. Data are reported for the glass transition temperature (T_g), dilatometric softening point (T_d), linear coefficient of expansion (α), onset crystallization temperature (T_x), exothermal peak temperature (T_P), density (ρ) and index of refraction (n_D) in the clear glasses.     

Thermal properties and crystallization of iron phosphate glasses containing up to 25 wt% additions of Si-, Al-, Na- and U-oxides

The thermal properties (expansion, T_g and T_SOFT.) of glasses, having 56-66% P₂O₅, 14.8-34.2% Fe₂O₃ and 2-25 wt% additions of SiO₂, Al₂O₃, Na₂O and UO₂, were comparatively estimated from dilatometric measurements in similar conditions. The T_g reversibility was clearly verified by varying the heating rates between 1 and 5 °C min⁻¹. From linear equations fits of the various glass properties as functions of the six components it is suggested the iron, sodium and uranium oxides decrease the thermal expansion (for 50 < T ? 300 °C), T_g and T_SOFT. From DTA/XRD analysis of three glasses it was confirmed the crystallization tendency decreased with increasing the UO₂ level in the glasses. Leaching test data for two compositions containing Na₂O suggest addition of UO₂ increases the chemical durability of the related glass. The roles of UO₂, Na₂O and Fe-oxide species as structural components of the glass network are discussed.     

Electron spin resonance and magnetic studies on CaO-SiO2-P2O5-Na2O-Fe2O3 glasses

Room temperature electron spin resonance (ESR) spectra and temperature dependent magnetic susceptibility measurements have been performed to investigate the effect of iron ions in 41CaO · (52 − x)SiO₂ · 4P₂O₅ · xFe₂O₃ · 3Na₂O (2 ? x ? 10 mol%) glasses. The ESR spectra of the glass exhibited the absorptions centered at g ≈ 2.1 and g ≈ 4.3. The variation of the intensity and linewidth of these absorption lines with composition has been interpreted in terms of variation in the concentration of the Fe²⁺ and Fe³⁺ in the glass and the interaction between the iron ions. The magnetic susceptibility data were used to obtain information on the relative concentration and interaction between the iron ions in the glass.     

Electrical properties of phosphate glasses

The electrical properties of glasses in the Na₂OP₂O₅, Ag₂OP₂O₅ and (1?x)Na₂OxAg₂OP₂O₅ systems have been measured over a range of temperature and composition.The properties of the Na₂OP₂O₅ and Ag₂OP₂O₅ glasses have been compared within the phosphate system as well as with silicate glasses. The silver-containing glasses show higher conductivity and lower temperature coefficients when compared with the sodium-containing glasses. A maximum in the room temperature resistivity of the (1?x)Na₂O?xAg₂O?P₂O₅ system was found around the mole ratio of 0.16:0.84 Ag₂O:Na₂O, indicating a mixed-alkali effect. A similar effect was seen in the tan δ, but not in the T_g-against-composition plots. A linear relationship was noted for the tan δ-versus-log₁₀ (resistivity) plot, as has been seen in other glass-forming systems.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Bioactive glasses in the system CaO-B2O3-P2O5: Preparation, structural study and in vitro evaluation

Glasses in the system x B₂O₃(1 − x) [y CaO P₂O₅], (x = 0, 0.1, 0.2, 0.3, y = 2, 2.6, 3, 4, 5) have been prepared by fast quenching of high temperature melts. The presence of B₂O₃ affected the glass forming ability, allowing the preparation of calcium phosphate glasses with y ? 2.6. The structure of glasses was analyzed by μ-Raman and infrared spectroscopy. The analysis indicated that the glass network is dominated by highly charged species from phosphate tetrahedra with 3 (pyro) or 4 (ortho) NBOs, while the boron atoms are incorporated mainly in 3 coordinated sites in the form of B∅₃ or B∅₂O⁻ units. A small fraction of units was also evident from the spectra analysis of glasses with high CaO content. All calcium borophosphate glasses exhibited bioactivity after soaking in SBF solution within a few days. This was observed by μ-Raman and SEM microscopy, while XRD patterns clearly revealed growth of hydroxyapatite phase. The presence of boron in the glass network has a catalytic effect at favoring bioactivity of the otherwise bioinert calcium phosphate glasses.     

Influence of alkali and alkali-earth metal oxide substitutions on the properties of lithium-iron-phosphate glasses

The influences of different alkali and alkali-earth oxide substitutions on the properties of lithium-iron-phosphate (LIP) glasses have been studied. Na₂O, K₂O, MgO, CaO and BaO were used to substitute Li₂O to prepare LIP glasses with molar compositions of (20 − x)Li₂O − xR₂O(RO) − 30Fe₂O₃ − 50P₂O₅ (x = 2.4, 4, 5.6 and 7.2). The glass transition temperature (T_g) was determined by the differential thermal analysis technique. The density and chemical durability of the prepared glasses were measured based on the Archimedes principle and the weight losses after the glasses were boiled in water. The results show that T_g decreases with the initial substitutions, whereas the density and chemical durability increase. The diminution of the aggregation effect of Li⁺ ions on the glass structure due to the decrease in Li⁺ concentration, the larger molecule weights of the substitutes, the mixed-alkali and depressing effects as well the slower mobility of substitute ions mainly contribute to the initial changes in T_g, density and chemical durability of the LIP glasses, respectively. Further increasing the amounts of substitutes brings about increasing diminution of the aggregation effect of Li⁺ ions and breakage of the glass network on the one hand and increasing amounts of substitutes with larger molecule weights and ion radii on the other hand. Both aspects influence the glass properties oppositely and consequently non-monotonic variations in the properties of LIP glasses with the substitutions are observed.     

Structure and properties of Ni60(Nb100−xTax)34Sn6 bulk metallic glass alloys

Refractory bulk metallic glasses and bulk metallic glass composites are formed in quaternary Ni-Nb-Ta-Sn alloy system. Alloys of composition Ni₆₀(Nb_100−xTa_x)₃₄Sn₆ (x = 20, 40, 60, 80) alloys were prepared by injection-casting the molten alloys into copper molds. Glassy alloys are formed in the thickness of half mm strips. With thicker strips (e.g., 1 mm), Nb₂O₅ and Ni₃Sn phases and the amorphous phase form an in situ composite. Glass transition temperatures, crystallization temperatures, and ΔT_x, defined as T_x1 − T_g (T_x1: first crystallization temperature, T_g: glass transition temperature) of the alloys increase dramatically with increasing Ta contents. These refractory bulk amorphous alloys exhibit high Young’s modulus (155-170 GPa), shear modulus (56-63 GPa), and estimated yield strength (3-3.6 GPa).     

Structure-property correlation in (50 − x)Na2O–50P2O5–xCoCl2 glassy systems

Ternary sodium–cobalt–phosphate glasses of the composition (50 − x)Na₂O–50P₂O₅–xCoCl₂ with x varying between 0 and 15 mol% prepared by melt quenching have been characterized by Fourier transform infrared (FT-IR) spectroscopy and X-ray diffraction (XRD) techniques. Thermal (T_g, T_c) and electrical properties have been investigated. Infrared spectra reveal the formation of metaphosphate glasses (Q² tetrahedral units) with symmetric bridging oxygen (P–O–P) and non-bridging oxygen (P–O⁻). The spectra also indicate the formation of P–O–Co bonds in the metaphosphate glasses that replace P–O⁻–Na⁺ bonds. The results of thermal studies correlate with these FT-IR findings and support the formation of P–O–Co bonds and an increased cross-link density with increasing CoCl₂. This results in enhanced chemical durability and increased T_g and T_c of the glasses. The electrical conductivity parameters upon changing the composition have been correlated with structural changes in the glass matrix.     

Bond character and properties of the mixed alkali system Na2OK2OAl2O3SiO2

The mixed alkali glass system Na₂OK₂OAl₂O₃SiO₂ was investigated. Density, transformation temperature, refractive index, and chemical durability were studied. Optical absorption and ESR spectra of the CuO-doped glasses were determined.Calculations of the polarizability of O^2?, bonding parameters of the Cu²⁺ complex, and the packing density are presented. It was found that for the mixed alkali glasses, the oxygen- alkali bond has a more ionic character than expected from additivity. This fact enables the non-linear changes of the refractive index, of the shift of the Cu²⁺ absorption band, and of the covalency to be interpreted as the Na mole fraction is varied. It is also possible to explain qualitatively the density, T_g and chemical durability non-linear variations with change of the Na content by the ionicity deviations of the bond character and the postulated pairs of Na⁺ and K⁺ ions in the mixed alkali glasses.     

O nuclear magnetic resonance study of Na2O-P2O5 glasses

The preparation and structural investigation of ¹⁷O-enriched xNa₂O-(100−x)P₂O₅ glasses (46.5?x?62.8) by nuclear magnetic resonance (NMR) is described. Enriched phosphoric acid was prepared by hydrolysis of PCl₅ with ¹⁷O-enriched water and neutralized with sodium carbonate. The sodium metaphosphate was then melted at 800 °C for 15 h and quenched. Polyphosphate and ultraphosphate glass compositions were prepared by remelting the metaphosphate with sodium carbonate and phosphorus pentoxide, respectively. ³¹P magic angle sample spinning (MAS) NMR was used to determine the Na₂O/P₂O₅ content in the glasses. ¹⁷O NMR spectra (quadrupole echo for non-rotating samples and multiple-quantum excitation for rotating samples (MQMAS)) show two oxygen sites in the samples with large quadrupolar coupling constants (4.7 and 7.7 MHz), in accordance with the high phosphorus electronegativity. According to the correlation of ¹⁷O quadrupolar constants with bond ionicity, these two components are attributed to bridging P-O-P and non-bridging P-O?Na oxygens. The average P-O-P bond angle is estimated with the quadrupolar asymmetry derived from the fit of the static echo spectra. The MQMAS spectrum shows a distribution of non-bridging oxygen chemical shifts, attributed to a variation of bond length and angle.     

Glass transition and fragility of Na2O-TeO2 glasses

The heat capacity (C_p) change in the glass transition region for the xNa₂O ·(100−x)TeO₂, mol%, glass forming melts with x=7.5, 11.1, 15.0, 20.0 and 25.0 was measured as a function of heating rate (2, 4, 6, 10 and 15 °C/min) using differential scanning calorimetry. The glass transition properties that have been measured and reported in this paper include the glass transition temperature (T_g), glass transition width (ΔT_g), heat capacities in the glassy and liquid state (C_pg and C_pl) and the activation enthalpy for glass transition (). T_g for these sodium tellurite melts decreased and increased with increasing Na₂O. Values of the ratio C_pl/C_pg ranged between 1.28 and 2.47, and the fragility parameter ranged between 100 and 130, suggesting that these glass forming melts may be classified as intermediate between typical strong and fragile liquids. The viscosity, η, calculated at a few selected temperatures near the glass transition region decreased with increasing Na₂O at any given temperature, which is also expected.     

Thermal and electrical properties of BaO-B2O3-ZnO glasses

Glasses in the BaO-ZnO-B₂O₃ system were examined as potential replacement for PbO glass frits with low firing temperature (500-600 °C) for the dielectric layer of a plasma display panel (PDP). The glasses were evaluated for glass transition temperature (T_g), thermal expansion coefficient (α) and dielectric constant ε. The electrical and the thermal properties were also compared with theoretical data calculated by a known empirical equation. T_g of the glasses varied between 480 and 560 °C, and α was in the range of 7-9×10⁻⁶ K⁻¹. The dielectric constant ranges from 14 to 19 and the theoretical data showed lower α and ε than the experimental data. The results suggest that BaO-ZnO-B₂O₃ glasses would be suitable as an alternative to Pb-based dielectric layer in PDPs.     

Thermal stability, spectra and laser properties of Yb: lead-zinc-telluride oxide glasses

A series of new glasses of 70TeO₂-(20 − x) ZnO-xPbO − 5La₂O₃-2.5K₂O-2.5Na₂O (mol%) doped with Yb³⁺ is presented. Thermal stability, spectra and laser properties of Yb³⁺ ions have been measured. It found that 70TeO₂-15PbO-5ZnO-5La₂O₃-2.5K₂O-2.5Na₂O composition glass had fine stability ((T_x−T_g)>190 °C), high-stimulated emission cross-section of 1.25 pm² for the ²F_5/2 → ²F_7/2 transition and existed measured fluorescence lifetime of 0.94 ms and the broad fluorescence effective linewidth of 72 nm. Evaluated from the good potential laser parameters, this system glass is excellent for short pulse generation in diode pumped lasers, short pulse generation tunable lasers, high-peak power and high-average power lasers.     

Non-random cation distribution in sodium-strontium-phosphate glasses

Vitreous compositions in the (0.55−x)Na₂O:xSrO:0.45P₂O₅ (0?x?0.55) system were characterized by differential scanning calorimetry and ³¹P solid state NMR. High strontium containing glasses were found to be partly crystallized. In the pure glass samples a general increase in T_g and a decrease in isotropic chemical shift with increasing x were observed. Two distinct linear ranges were observed in plots of these parameters against composition, with a transition point at x≈0.20. This composition corresponds to the point at which all Na⁺ ions associated with charge balance of the terminal Q¹ phosphate tetrahedra are substituted for Sr²⁺. In the mixed cation glasses, this suggests a non-random distribution of cations, with preferential location of Sr²⁺ ions near the chain ends. Crystalline models have been used to discuss trends in the variation of chemical shift anisotropy and propose possible coordination environments for the metal cations in the glasses.     

Glass-forming ability and crystallization of bulk metallic glass (HfxZr1−x)52.5Cu17.9Ni14.6Al10Ti5

We have produced a series of bulk metallic glasses of composition (Hf_xZr_1−x)_52.5Cu_17.9Ni_14.6Al₁₀Ti₅ (with x=0-1) by an arc melting/suction casting method. The density of these alloys increases by nearly 67% with increasing Hf content from 6.65 g/cm³ (x=0) to 11.09 g/cm³ (x=1). Over the same composition range the glass-forming ability decreases, as demonstrated by the size of the largest amorphous ingots that can be cast without crystallization. Although both the glass transition temperature and the melting temperature increase linearly with increasing Hf content, the reduced glass transition temperature (T_g/T_m) decreases, from 0.64 (x=0) to 0.62 (x=1), which suggests that the `confusion principle' correlating increased glass-forming ability with increased number of components, does not apply in this case due to the chemical similarity between Zr and Hf. A different crystallization behavior is observed for Zr-based and Hf-based glasses. The final crystalline phases are CuZr₂ and Zr₂Ni for Zr-based alloys, and Al₁₆Hf₆Ni₇ and CuHf₂ for Hf-based alloys.     

Synthesis and characterization of calcium phosphate based bioactive quaternary P2O5-CaO-Na2O-K2O glasses

Calcium phosphate based bioactive quaternary glass systems P₂O₅-CaO-Na₂O-K₂O were prepared by melt growth technique. Glasses were prepared in five different compositions by fixing P₂O₅ at 47 mol% and CaO at 30.5 mol% and by varying the K₂O and Na₂O concentrations. The structural properties of the glasses are analyzed using X-ray diffraction (XRD) studies and scanning electron microscopy (SEM) studies; and the composition of the glasses are studied using energy dispersive X-ray spectrum (EDS). The microhardness of the glass systems are studied by Vickers hardness measurements and the bioactivity of the glasses are studied using in vitro study. The thermal properties have been examined by means of thermogravimetric analysis (TGA) and differential thermal analysis (DTA). The ultrasonic velocity measurements show that the addition of K₂O contents produces non-bridging oxygen ion and hence weaken of the glass structure. The weakening of the glass structure reduces the ultrasonic velocity and hence an increase in attenuation.     

Influence of Nd2O3 on the thermal and dielectric properties of Pb-based lead borosilicate glasses

Neodymium has been employed in various Pb-based glass compositions containing ZnO, MgO, CaO, and BaO, to obtain low melting glasses for use as dielectric materials. Thermal analysis (DTA, TMA) was applied for both qualitative and quantitative thermal properties (T_g, CTE) of the glasses, and impedance analysis of the dielectric properties (ε_r, tanδ) was performed. It was found that with increasing Nd₂O₃, the glass transition temperature (T_g), the dilatometer softening point (T_d) and dielectric constant (ε_r) became higher. Also, a peak shift suggesting neodymium oxide introduced structural changes was found with IR spectra and XPS. These seem to support the conclusion that the addition of increased amounts of Nd₂O₃ can lead to a more rigid glass structure.