A multinuclear NMR study of sodium-borovanadophosphate glasses

xNaVO₃ · yNaPO₃ · (1 − y)NaBO₂ glasses were prepared where x = 0.0, 0.05, 0.5 and 0 ? y ? 1. These glasses have been investigated with multinuclear MAS NMR. ⁵¹V NMR spectra show that two vanadate configurations are possible, assigned as four and five coordinated vanadium. The concentration of the latter group decreases upon addition of sodium-borate. The presence of four and three coordinated boron sites can be deduced from the ¹¹B NMR spectra. The latter boron sites appear only when borate groups are connected to each other. ³¹P NMR spectra of borophosphates and borovanadophosphates show that the ratio of pyro- and metaphosphates is greater in the glasses containing vanadate than in simple borophosphates. These results indicate phosphate to be the most acidic agent and therefore the best chain-terminating group in these glasses.     

Effects of Nb on the formation of icosahedral quasicrystalline phase in Ti-rich Ti-Zr-Ni-Cu-Be glassy forming alloys

As-cast (Ti₄₀Zr₂₅Ni₈Cu₉Be₁₈)_100−xNb_x (0 ? x ? 5) (Ф3) glassy forming alloys were investigated in order to clarify the role of Nb on the formation of icosahedral quasicrystalline phase (I-phase) in Ti-rich Ti-Zr-Ni-Cu-Be glassy system. It is found that an I-phase is formed in Ti-Zr-Ni-Cu-Be glassy alloy by addition of Nb element; however, the nucleation rate of I-phase increases, whereas the grain growth rate decreases with increasing Nb content. Moreover, with increasing Nb content, the thermal stability against crystallization increases, while the temperature range of stability of the I-phase decreases.     

The effect of composition on the structure of sodium borophosphate glasses

Glasses in the system 40(P₂O₅)-x(B₂O₃)-(60 − x)(Na₂O) (10 ? x ? 30 mol%) have been prepared by the melt-quenching technique. Thermal properties were studied using differential thermal analysis and the relationship between composition and thermal stability was obtained. Structural characterization was achieved by a combination of experimental data (infrared and Raman spectroscopy, ¹¹B and ³¹P solid state NMR). In particular, variations in the phosphate network structure upon addition of B₂O₃ and Na₂O were investigated. Analysis of the data indicates that with increasing B₂O₃ content and decreasing Na₂O, the glass network shows increasing levels of cross-linking between phosphate and borate units. Evidence of direct B-O-P bonds was observed. In the compositional range investigated, borate groups contain boron almost exclusively in four-fold coordination.     

Crystallisation of a simulated borosilicate high-level waste glass produced on a full-scale vitrification line

A simulated (inactive) borosilicate high-level waste (HLW) glass was produced on a full-scale vitrification line with composition simulating vitrified oxide fuel (UO₂) reprocessing waste. As-cast samples were compositionally homogeneous (Type I microstructure) and/or compositionally inhomogeneous displaying compositional ‘banding’ and frequently containing ‘reprecipitated calcine’ (Type II microstructure). Crystal phases identified in as-cast samples were: tetragonal RuO₂, cubic Pd-Te alloy, cubic (Cr,Fe,Ni,Ru)₃O₄, trigonal Na₃Li(MoO₄)₂·6H₂O, ostensibly cubic Zr_{1 − x − y}Ce_xGd_yO_2 − 0.5y and a lanthanoid (Nd,Gd,La,Ce) silicate. Zr_{1 − x − y}Ce_xGd_yO_2 − 0.5y and lanthanoid (Nd,Gd,La,Ce) silicate were found exclusively in the Type II microstructure as component crystal phases of ‘reprecipitated calcine’. Heat treated samples (simulating the retarded cooling experienced by actual (active) borosilicate HLW glasses after pouring) displayed extensive crystallisation and cracking (Type A microstructure) and/or ‘banded’ crystallisation (Type B microstructure) depending on their parent (as-cast) microstructure (Type I and/or Type II respectively). Crystal phases identified in heat treated samples were: tetragonal SiO₂ (α-cristobalite), tetragonal (Na,Sr,Nd,La)MoO₄, cubic Ce_{1 − x − y}Zr_xGd_yO_2 − 0.5y, a Ni-rich phase, a lanthanoid (Nd,Gd,La,Ce) silicate and orthorhombic LiNaZrSi₆O₁₅ (zektzerite). α-cristobalite was found exclusively in the Type A microstructure, while lanthanoid (Nd,Gd,La,Ce) silicate and zektzerite were only found in the Type B microstructure. Potential host phases for HLW radionuclides are: Pd-Te alloy (¹⁰⁷Pd and ⁷⁹Se), (Cr,Fe,Ni,Ru)₃O₄ (⁶³Ni), Zr_{1 − x − y}Ce_xGd_yO_2 − 0.5y (⁹³Zr, Pu and U), both lanthanoid (Nd,Gd,La,Ce) silicates (Am and Cm), (Na,Sr,Nd,La)MoO₄ (⁹⁰Sr, Am and Cm), Ce_{1 − x − y}Zr_xGd_yO_2 − 0.5y (⁹³Zr, Pu and U), the Ni-rich phase (⁶³Ni) and zektzerite (⁹³Zr, ¹²⁶Sn and U). Cracking in samples was attributed to thermal expansion mismatch between the borosilicate HLW glass matrix and RuO₂, cristobalite (both α and β), (Na,Sr,Nd,La)MoO₄ and zektzerite on cooling. There was also a contribution from the cristobalite α-β phase transition.     

Electron spin resonance and magnetic studies on CaO-SiO2-P2O5-Na2O-Fe2O3 glasses

Room temperature electron spin resonance (ESR) spectra and temperature dependent magnetic susceptibility measurements have been performed to investigate the effect of iron ions in 41CaO · (52 − x)SiO₂ · 4P₂O₅ · xFe₂O₃ · 3Na₂O (2 ? x ? 10 mol%) glasses. The ESR spectra of the glass exhibited the absorptions centered at g ≈ 2.1 and g ≈ 4.3. The variation of the intensity and linewidth of these absorption lines with composition has been interpreted in terms of variation in the concentration of the Fe²⁺ and Fe³⁺ in the glass and the interaction between the iron ions. The magnetic susceptibility data were used to obtain information on the relative concentration and interaction between the iron ions in the glass.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Bioactive glasses in the system CaO-B2O3-P2O5: Preparation, structural study and in vitro evaluation

Glasses in the system x B₂O₃(1 − x) [y CaO P₂O₅], (x = 0, 0.1, 0.2, 0.3, y = 2, 2.6, 3, 4, 5) have been prepared by fast quenching of high temperature melts. The presence of B₂O₃ affected the glass forming ability, allowing the preparation of calcium phosphate glasses with y ? 2.6. The structure of glasses was analyzed by μ-Raman and infrared spectroscopy. The analysis indicated that the glass network is dominated by highly charged species from phosphate tetrahedra with 3 (pyro) or 4 (ortho) NBOs, while the boron atoms are incorporated mainly in 3 coordinated sites in the form of B∅₃ or B∅₂O⁻ units. A small fraction of units was also evident from the spectra analysis of glasses with high CaO content. All calcium borophosphate glasses exhibited bioactivity after soaking in SBF solution within a few days. This was observed by μ-Raman and SEM microscopy, while XRD patterns clearly revealed growth of hydroxyapatite phase. The presence of boron in the glass network has a catalytic effect at favoring bioactivity of the otherwise bioinert calcium phosphate glasses.     

The effect of composition on UV-vis-NIR spectra of iron doped glasses in the systems Na2O/MgO/SiO2 and Na2O/MgO/Al2O3/SiO2

Glasses with the compositions xNa₂O · 10MgO · (90 − x)SiO₂, 10Na₂O · xMgO · (90 − x)SiO₂, 5Na₂O · 15MgO · xAl₂O₃ · (80 − x)SiO₂, xNa₂O · 10MgO · 10Al₂O₃ · (80 − x)SiO₂, 10Na₂O · 10MgO · xAl₂O₃ · (80 − x)SiO₂, 10Na₂O · 5MgO · 10Al₂O₃ · (80 − x)SiO₂ were melted and studied using UV-vis-NIR spectroscopy in the wavenumber range from 5000 to 30 000 cm⁻¹. At [Al₂O₃] > [Na₂O], the UV-cut off is strongly shifted to smaller wavenumbers and the NIR peak at around 10 000 cm⁻¹ attributed to Fe²⁺ in sixfold coordination gets narrower. Furthermore, the intensity of the NIR peak at 5500 cm⁻¹ increases. This is explained by the incorporation of iron in the respective glass structures.     

Synthesis of Nb2O5·nH2O nanoparticles by water-in-oil microemulsion

Hydrous niobium oxide (Nb₂O₅·nH₂O) nanoparticles had been successfully prepared by water-in-oil microemulsion. They were characterized by X-ray diffraction (XRD), thermal analysis (TG/DTG), Fourier transform infrared spectroscopy (FTIR), BET surface area measurement, transmission electron microscopy (TEM), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results showed that the nanoparticle was exactly Nb₂O₅·nH₂O with spherical shape. Their BET surface area was 60 m² g⁻¹. XRD results showed that Nb₂O₅·nH₂O nanoparticles with crystallite size in nanometer scale were formed. The crystallinity and crystallity size increased with increasing annealing temperature. TT-phase of Nb₂O₅ was obtained when the sample is annealed at 550 °C.     

Structural and optical properties of Zn(Mg,Cd)O alloy films grown by remote-plasma-enhanced MOCVD

We report the structural and optical properties of wurtzite-structure Zn(Mg,Cd)O ternary alloys. Wurtzite (0 0 0 1) Zn_1−xCd_xO and Mg_yZn_1−yO films were grown on (11–20) sapphire substrates using remote-plasma-enhanced metalorganic chemical vapor deposition. The large bowing parameters of Zn_1−xCd_xO and Mg_yZn_1−yO ternary alloys are 3.0 and 3.5, respectively, which reflects the large difference of each binary’s electronegativity. We have analyzed the broadening of photoluminescence (PL) in Zn(Mg,Cd)O alloys on alloy content by taking into account the statistical alloy fluctuation and the localization of the exciton, and have clarified that the localization of the exciton strongly affects to PL full-width at half-maximum (FWHM) in Zn(Mg,Cd)O alloys. The alloy broadenings in steady-state PL of Zn(Mg,Cd)O alloys are in good agreement with the calculated tendency by the theoretical model based on the statistical alloy fluctuation, while PL FWHM of Zn_1−xCd_xO is three times larger than the calculated results. Moreover, as another way to confirm alloy broadening, we also have done time-resolved PL measurements and derived the localized depth of the exciton in ZnO-based system, indicating a good agreement with the tendency of PL FWHM broadening.     

Structure and properties of potassium niobato-borophosphate glasses

Bulk glasses of the series (1 ? x)[0.5K₂O–0.1B₂O₃–0.4P₂O₅]–xNb₂O₅ with x = 0–45.7 mol% Nb₂O₅ were prepared by slow cooling in air and investigated by Raman, ³¹P, and ¹¹B MAS NMR spectroscopy. The incorporation of Nb₂O₅ into the parent borophosphate glass results in a substantial increase in the glass transition temperature and chemical durability of glasses. Raman spectra showed that Nb atoms form distorted NbO₆ octahedra, which are isolated at low Nb₂O₅ content, whereas at higher Nb₂O₅ content they form clusters. ¹¹B NMR spectra of the glasses revealed the interaction between Nb₂O₅ and BO₄ tetrahedral units, which results in a partial transformation of tetrahedral BO₄ units to trigonal BO₃ units and the formation of mixed B(OP)_4?n(ONb)_n units.     

FTIR and ultrasonic investigations on modified bismuth borate glasses

Studies on xRO · 30Bi₂O₃ · (70−x)B₂O₃ glasses have been carried out (0 ? x ? 30 mol%, R = Zn, Ba). Elastic properties and Debye temperature have been investigated using sound velocity measurements at 4 MHz. The ultrasonic parameters along with the IR spectroscopic studies have been employed to explore the role of divalent cations in the structure of the studied glasses. Analysis of infrared spectra indicates that RO is preferentially incorporated into the borate network, forming BO₄ units. It is assumed that Bi₂O₃ enters the structure in the form of BiO₆ only. The change of density and molar volume with RO content reveals that BO₄ units linked to R²⁺ cations are denser than those linked to positive sites in the Bi₂O₃ network. Predicted values of four co-ordinated boron put forward questions about the reliability of assignment of structural units that Bi₂O₃ may form.     

Preparation and characterization of new fluorotellurite glasses for photonics application

Glasses based on (85 − x)TeO₂-xZnF₂-12PbO-3Nb₂O₅ (x = 0-40) system have been studied for the first time for fabricating mid-infrared optical fiber lasers. The thermal and optical properties including UV-Vis, Raman as well as FTIR spectra are reported. It is demonstrated that increasing the ZnF₂ concentration to 30 mol% significantly increased the thermal stability of the glass. Adding ZnF₂ also reduced the hydroxyl (OH) content of the glass resulting in lower optical absorption in the mid-infrared region, which is crucial for infrared laser applications. The glass absorption cut-off edge near 400 nm blue-shifts with increasing ZnF₂ addition. Raman spectra show a depolymerization of the glass network with increasing transformation of TeO₃₊₁ to TeO₃ structures.     

Boron content dependance of magnetoimpedance in Fe91−xZr5BxNb4 alloys

A systematic investigation of the influence of B content on the magnetoimpedance (MI) effect in melt-spun Fe_91−xZr₅B_xNb₄ (FZBN, 0 ? x ? 30) ribbons has been performed within a frequency range, f ∼ 310-1110 kHz and under a varying dc magnetic field (H_dc) up to 70 Oe. The MI effect is not observed in the sample with x ? 5 but within the range 8 ? x ? 30. A distinct MI effect has been observed with a maximum change of 180% at around 1.1 MHz in the sample with x = 20, coincident with a saturation magnetic field of 66 Oe and a field sensitivity of about 7%/Oe. Magnetic measurements reveal that the MI effect and B content dependence of the effect are closely related to coercivity of the FZBN alloy series, except for the sample with 20 at.%. The drastic MI ratio observed in the sample with x = 20 is ascribed to its special microstructure. The mechanism of the MI effect in FZBN alloys and of the significant MI value appearing at a B content of x = 20 is discussed in this paper.     

Structure and properties of Ni60(Nb100−xTax)34Sn6 bulk metallic glass alloys

Refractory bulk metallic glasses and bulk metallic glass composites are formed in quaternary Ni-Nb-Ta-Sn alloy system. Alloys of composition Ni₆₀(Nb_100−xTa_x)₃₄Sn₆ (x = 20, 40, 60, 80) alloys were prepared by injection-casting the molten alloys into copper molds. Glassy alloys are formed in the thickness of half mm strips. With thicker strips (e.g., 1 mm), Nb₂O₅ and Ni₃Sn phases and the amorphous phase form an in situ composite. Glass transition temperatures, crystallization temperatures, and ΔT_x, defined as T_x1 − T_g (T_x1: first crystallization temperature, T_g: glass transition temperature) of the alloys increase dramatically with increasing Ta contents. These refractory bulk amorphous alloys exhibit high Young’s modulus (155-170 GPa), shear modulus (56-63 GPa), and estimated yield strength (3-3.6 GPa).     

Effect of microalloying of Nb on corrosion resistance and thermal stability of ZrCu-based bulk metallic glasses

Bulk metallic glasses (BMGs) of Zr_46−xNb_xCu_37.6Ag_8.4Al₈ with x = 0, 0.5, 1, 2 and 4 at.% were prepared by copper mould casting. The corrosion resistance of the ZrCu-based BMGs with different Nb contents was carefully examined by weight loss measurements and potentiodynamic polarization tests in 3 mass% NaCl, 1 N HCl and 1 N H₂SO₄ solutions, respectively. Nb addition improves the newly developed BMGs’ corrosion resistance in chloride-containing solutions and the alloys all exhibit excellent corrosion resistance in 1 N H₂SO₄. The corrosion behavior of the alloy containing 0 and 4 at.% Nb in phosphate-buffered solution was examined by electrochemical polarization tests. The influence of Nb addition on glass forming ability (GFA), thermal stability and mechanical property was investigated by X-ray diffraction, differential scanning calorimetry and compression tests, respectively. It is found that the addition of Nb can deteriorate the GFA and thermal stability of the base system, but little effect is observed on the mechanical properties, e.g., yielding strength and plasticity, of the ZrCu-based BMG alloys.     

The presence of a thermally reversing window in Al-Te-Si glasses revealed by alternating differential scanning calorimetry and electrical switching studies

Alternating differential scanning calorimetric (ADSC) studies and electrical switching experiments have been undertaken on Al₁₅Te_85−xSi_x (2 ? x ? 12) system of glasses. These glasses are found to exhibit two crystallization reactions (T_c1 and T_c2), for compositions with x < 8. Above x = 8, a single-stage crystallization is seen. Further, a trough is seen in the composition dependence of non-reversing enthalpy (ΔH^NR), based on which it is proposed that there is a thermally reversing window in Al₁₅Te_85−xSi_x glasses, in the composition range 4 ? x ? 8. Electrical switching studies indicate that Al₁₅Te_85−xSi_x glasses exhibit a threshold type electrical switching at ON state currents less than 2 mA. Further, the switching voltages are found to increase with the increase in silicon content. It is interesting to note that the start (x = 4) and the end (x = 8) of the thermally reversing window are exemplified by a kink and a saturation in the composition dependence of switching voltages, respectively.     

Structural analysis of Cd-Te-O films prepared by RF reactive sputtering

Crystalline and microcrystalline Cd-Te-O samples have been obtained by RF reactive sputtering from a CdTe target using N₂O as oxidant. The growth conditions were substrate temperatures of 323 K, 573 K and 773 K and cathode voltage of −400 V, corresponding to 30 W of forward power. The samples were studied by micro-Raman spectroscopy, X-ray diffraction and optical transmittance. The films are remarkably transparent in the visible range, with transmittances about 88% at 400 nm and band gap energies above the absorption edge of the glass substrates. Although only the samples prepared at 773 K present defined diffraction peaks, the analysis of the Raman spectra indicate that samples prepared at 323 K and 573 K have a defined microstructure indeed. The spectra fitting performed by comparison with pattern compounds demonstrate that Cd-Te-O films are formed of Te-O units similar to those present in metal oxide-doped tellurite glasses, such as TeO₃ and TeO_3 + 1 linked through Cd-O bonds. As the substrate temperature increases the microstructure evolves from a γ-TeO₂ richer state to Cd_xTe_yO_z. In the crystalline sample the main phase identified was CdTeO₃ even though evidence of other phases was observed.     

Nano- and micro-indentation studies on lithium borate-barium bismuth niobate glasses

The structure and mechanical properties of multifunctional lithium tetra-borate based glasses and glass-ceramics of the system (100 − x) Li₂B₄O₇₋x(BaO-Bi₂O₃-Nb₂O₅) with x = 10, 20 and 30 in molar ratio, have been characterized. Nano- and micro-indentation techniques were employed to evaluate the elastic modulus, hardness and toughness of the as-cast and annealed glasses. These were complemented with detailed structural investigations using X-ray diffraction, microscopy (optical, scanning electron and high resolution transmission electron microscopies) and nuclear magnetic resonance spectroscopy. These investigations reveal a smooth variation of the mechanical properties with composition except for the composition corresponding to x = 20. This deviation has been attributed to subtle changes in the glass-structure due to amorphous phase-separation and heat-treatment-assisted nano-crystallization.     

A study on structural formation and optical property of wide band-gap Be0.2Zn0.8O layers grown by RF magnetron co-sputtering system

Wide band-gap BeZnO layers were grown on Al₂O₃ (0 0 0 1) substrate using radio-frequency magnetron co-sputtering. The rate of Be_xZn_1−xO crystallized as a hexagonal structure was x=0.2. From the X-ray photoelectron spectroscopy measurement, the O–Zn bonds relating the crystal structure and the Be–O bonds related to the deviation of the stoichiometry in the BeZnO layer were caught at 530.4 and 531.7 eV in the O 1s spectrum, respectively. Thus, the observance on the Be 1s peak of 113.2 eV associated with the bonding Be–O indicates that the sputtered Be atoms are substituted for the host-lattice site in ZnO. This Be–O bonding shows a relatively low intense and broadening spectrum caused by large fluctuation of Be content in the BeZnO layer. From the photoluminescence and transmittance measurement, the free exciton and the neutral donor-bound exciton (D⁰, X) emissions were observed at 3.7692 and 3.7313 eV, respectively, and an average transmittance rate over 95% was achieved in a wide ultraviolet (UV)–visible region. Also, the binding energy for the (D⁰, X) emission was extracted to be 37.9 meV. Through the wide band-gap material BeZnO, we may open some possibilities for fabricating a ZnO-based UV light-emitting diode to be utilized as a barrier layer comprised of the ZnO/BeZnO quantum well structure and/or an UV light emitting material itself.