The comparative structure, properties, and ionic conductivity of LiI + Li2S + GeS2 glasses doped with Ga2S3 and La2S3

The well known and characterized fast ion conducting (FIC) LiI + Li₂S + GeS₂ glass-forming system has been further optimized for higher ionic conductivity and improved thermal and chemical stability required for next generation solid electrolyte applications by doping with Ga₂S₃ and La₂S₃. These trivalent dopants are expected to eliminate terminal and non-bridging sulfur (NBS) anions thereby increasing the network connectivity while at the same time increasing the Li⁺ ion conductivity by creating lower basicity [(Ga or La)S_4/2]⁻ anion sites. Consistent with the finding that the glass-forming range for the Ga₂S₃ doped compositions is larger than that for the La₂S₃ compositions, the addition of Ga₂S₃ is found to eliminate NBS units to create bridging sulfur (BS) units that not only gives an improvement to the thermal stability, but also maintains and in some cases increases the ionic conductivity. The compositions with the highest Ga₂S₃ content showed the highest T_gs of ∼325 °C. The addition of La₂S₃ to the base glasses, by comparison, is found to create NBS by forming high coordination octahedral LaS₆³⁻ sites, but yet still improved the chemical stability of the glass in dry air and retained its high ionic conductivity and thermal stability. Significantly, at comparable concentrations of Li₂S and Ga₂S₃ or La₂S₃, the La₂S₃-doped glasses showed the higher conductivities. The addition of the LiI to the glass compositions not only improved the glass-forming ability of the compositions, but also increased the ionic conductivity glasses. LiI concentrations from 0 to 40 mol% improved the conductivities of the Ga₂S₃ glasses from ∼10⁻⁵ to ∼10⁻³ (Ω cm)⁻¹ and of the La₂S₃ glasses from ∼10⁻⁴ to ∼10⁻³ (Ω cm)⁻¹ at room temperature. A maximum conductivity of ∼10⁻³ (Ω cm)⁻¹ at room temperature was observed for all of the glasses and this value is comparable to some of the best Li ion conductors in a sulfide glass system. Yet these new compositions are markedly more thermally and chemically stable than most Li⁺ ion conducting sulfide glasses. LiI additions decreased the T_gs and T_cs of the glasses, but increased the stability towards crystallization (T_c − T_g).     

Thermo-optic properties of B2O3 doped Li2O-Al2O3-SiO2 glass-ceramics

Reduction in the temperature coefficient of the optical path length, dS/dT of Li₂O-Al₂O₃-SiO₂ glass-ceramics with near-zero thermal expansion coefficient was attempted using control of the temperature coefficient of electronic polarizability, ?, and the thermal expansion coefficient, α. The dS/dT value of 2.6 mol% B₂O₃-doped glass-ceramic was 12.5  × 10⁻⁶/°C, which was 0.9 ×  10⁻⁶/°C smaller than that of B₂O₃-free glass-ceramic. On the other hand, reduction in dS/dT through B₂O₃ doping was not confirmed in precursor glasses. Results showed that reduction in dS/dT of the glass-ceramic through B₂O₃ doping is caused by the reduction in ?. The reduction in ? from B₂O₃ doping was probably attributable to numerical reduction in non-bridging oxide ions with larger ? value by the concentration of boron ions in the residual glass phase. In addition, application of hydrostatic pressure during crystallization was effective to inhibit precipitation of β-spodumene solid solution, which thereby decreases dS/dT. The dS/dT value of B₂O₃-doped glass-ceramic crystallized under 196 MPa was 11.7 ×  10⁻⁶/°C. That value was slightly larger than that of silica glass. The α value of this glass-ceramic was smaller than that of silica glass.     

Effect of heat-treatment condition on crystallization behavior and thermal expansion coefficient of Li2O-ZnO-Al2O3-SiO2-P2O5 glass-ceramics

Utilizing P₂O₅ as nucleation agent, a Li₂O-ZnO-Al₂O₃-SiO₂ glass was prepared by conventional melt quenching technique and subsequently converted to glass-ceramics with different crystal phases. During the processing, two-step heat-treatments including nucleation and crystallization were adopted. The effects of heat-treatment on the crystal type, the microstructure and the thermal expansion behavior of the glass-ceramics were studied by means of differential scanning calorimetry, X-ray powder diffraction analysis, scanning electron microscopy and thermal expansion coefficient tests. It was shown that the crystallization of occurred after the glass was treated at 580 °C. As the temperature increased from 580 °C to 630 °C, cristobalite and were identified as main and second crystal phases, respectively, in the glass-ceramic. An increase in the temperature to 700 °C, the β-quartz solid solution in the glass-ceramic accompanied by a decrease in cristobalite content. The transformation from to γ₀-Li₂ZnSiO₄ took place from 700 °C to 750 °C. The resulting crystallization phases in the glass-ceramics obtained at the temperature higher than 750 °C were β-quartz solid solution and γ₀-Li₂ZnSiO₄. The glass-ceramics containing or β-quartz solid solution crystal phase possessed a microstructure formed by the development of dendritic crystals. The thermal expansion coefficient of the glass-ceramics varied from 36.7 to 123.8 × 10⁻⁷ °C⁻¹ in the temperature range of 20-400 °C, this precise value is dependent on the type and the proportion of the crystalline phases presented.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Optical properties of Cr ion in lithium metasilicate Li2O · SiO2 transparent glass-ceramics

The optical properties of Cr³⁺ ions in lithium metasilicate (Li₂O · SiO₂) transparent glass-ceramics were investigated. The main crystalline phase precipitated was the lithium metasilicate (Li₂O · SiO₂) crystal. The percent crystallinity and crystalline size were ranging 65-75% and 20-35 nm, respectively. The color changes drastically to deep pink from emerald green upon crystallization. New and strong absorption bands appeared and the absorption intensity increases by about 10 times that in glass. These new absorption bands are found to be derived from Cr³⁺ ions in octahedral sites in the lithium metasilicate crystal lattice. Cr³⁺ ions substitute for three Li⁺ ions and occupy the distorted octahedral site between single [SiO₄]_n chains of lithium metasilicate crystal. The ligand field parameters can be estimated: 10Dq = 13 088 cm⁻¹, B = 453 cm⁻¹, Dq/B = 2.89 and C = 2036 cm⁻¹. The near-infrared luminescence centered at 1250 nm was not detected in the deep pink glass-ceramics unlike emerald green glass.     

Spectroscopic properties of Er-doped Na2O-Sb2O3-B2O3-SiO2 glasses

Spectroscopic properties of Er³⁺-doped Na₂O-Sb₂O₃-B₂O₃-SiO₂ glasses have been investigated for developing 1.5-μm broadband fiber amplifiers. An intense 1.5-μm near infrared emission with a broad full width at half maximum (FWHM) of 88 nm has been obtained for Er³⁺-doped 5Na₂O-20Sb₂O₃-35B₂O₃-40SiO₂ glass upon excitation with a 980 nm laser diode. The obtained emission cross-section of the ⁴I_13/2 → ⁴I_15/2 transition and the lifetime of the ⁴I_13/2 level of Er³⁺ ions are 6.8 × 10⁻²¹ cm² and 0.36 ms, respectively. It is noted that the product of the emission cross-section and the FWHM of the glass, σ_e × FWHM, is as great as 598.4 × 10⁻²¹ cm² nm, which is comparable or higher than that of Er³⁺-doped bismuth-based and tellurite-based glasses. These special optical properties encourage in identifying them as important materials for potential applications in high performance optics and optical communication networks.     

Electric conductivity of glasses in the system Na2O/CaO/SiO2/Fe2O3

The addition of polyvalent transition metal ions to the usually insulating traditional soda-lime-silica glasses can lead to semiconducting properties. We report on synthesis of glasses and glass-ceramics in a soda-lime-silicate based system containing Fe₂O₃ in the concentration range from 5 to 30 mol%. Two sub-systems were considered, in one of them the ratio [Na₂O]/[Fe₂O₃] was varied while in the other one, the ratio [SiO₂]/[Fe₂O₃] was changed. The phase composition of the synthesized products was characterized by X-ray diffraction and energy dispersive X-ray analysis, while the electrical properties were studied by impedance spectroscopy. Partially crystallized non-reduced samples are semiconducting even at room temperature while the glassy samples (both reduced and non-reduced) exhibit semiconducting properties at temperatures equal or larger than 100 °C. An attempt is done to predict the physical approximation explaining the conduction process in the glasses.     

Optical Properties of Bi2O3-TeO2-B2O3 Glasses

Glasses of the Bi₂O₃-TeO₂-B₂O₃ ternary system were developed and their linear and nonlinear optical properties were investigated. The absorption edges of these glasses were found to be 367-384 nm with a good transmittance in visible wavelength, although they exhibit the refractive indices as high as 1.98-2.12 at 633 nm. The absorption edges are quite steep and they are analyzed by the Urbach theory. The obtained Urbach energies of these glasses are 73-79 meV which are comparable to silica glasses. The high refractive index and its glass composition dependency are discussed according to the basics of the electronic polarizability and optical basicity. The high third order nonlinear susceptibility χ⁽³⁾ = 2.0 × 10^− 12 esu at 800 nm was also obtained in the 36Bi₂O₃-18TeO₂-46B₂O₃ glass.     

Thermal and some physical properties of glasses in the La2O3−CaO−B2O3 ternary system

Glasses in the La₂O₃−CaO−B₂O₃ ternary system were studied. The glass forming range as determined by the appearance of the annealed cast was found to match previously published findings. Clear glasses were formed in the composition range of 5.7−19.1 mol% La₂O₃ with constant B₂O₃ content of 71.4 mol%, and in glasses of constant La₂O₃:CaO ratio of 1:4 with B₂O₃ content in the range of 71.4-55.0 mol%. The non-linear optical crystalline phase La₂Ca₂B₁₀O₁₉ was crystallized from the clear glasses after heat treatments, as determined by powder XRD. Two types of the LaBO₃ crystalline phases were detected in the partially and the fully crystallized glass compositions outside the glass forming range. Data are reported for the glass transition temperature (T_g), dilatometric softening point (T_d), linear coefficient of expansion (α), onset crystallization temperature (T_x), exothermal peak temperature (T_P), density (ρ) and index of refraction (n_D) in the clear glasses.     

Crystallization of monoclinic WO3 in tungstate fluorophosphate glasses

Tungstate fluorophosphate glass compositions with high WO₃ concentration were prepared in the ternary system (80−0.8x)NaPO₃-(20−0.2x)BaF₂-xWO₃ with x = 40,50 and 60 mol%. Transparency decreases as WO₃ concentration increases but can be improved by addition of oxidizing systems such as CeO₂ or Sb₂O₃/NaNO₃. Characterizations by thermal analysis (DSC) point out that an increase in the amount of WO₃ results in a higher glass transition temperature. In addition, such compositions are very stable against devitrification since samples containing 40% and 50% of WO₃ donot even exhibit the expected crystallization event. In these samples, the stability against crystallization decreases with the WO₃ content and vitreous sample containing 60% of WO₃ exhibits an endothermic event around 620 °C due to crystallization of monoclinic WO₃ phase. In these glasses, it was shown that the nucleation stage can be induced by thermal-treatment when external nucleating agents such as Ti or Sb are used. Finally, gold-doped samples exhibit a higher crystallization tendency and monoclinic WO₃ phase can be grown in such glasses.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Sodium tracer diffusion in glasses of the type (CaO·Al2O3)x(2 SiO2)1−x

Tracer diffusion coefficients of the radioactive isotope Na-22 were measured in glasses of the type (CaO·Al₂O₃)_x(2 SiO₂)_1−x to study the diffusion of sodium as a function of glass composition, x, temperature and initial water content. The diffusion of Na-22 in glasses diffusion-annealed in dry air can always be well described by a single tracer diffusion coefficient, but sometimes not in samples annealed in common air. It was found that the sodium tracer diffusion coefficient decreases by about six orders of magnitude when the glass composition x changes from 0 to 0.75 at 800 °C. The temperature dependence of the diffusion of sodium seems to decrease as the silica content increases. Variations of the initial water content in some of the glasses investigated did not very significantly influence the rate of the tracer diffusion of sodium.     

Spectroscopic properties of Er-doped xGeO2-(80 − x)TeO2-10ZnO-10BaO glasses

Erbium-doped glasses with composition xGeO₂-(80 − x)TeO₂-10ZnO-10BaO were prepared by melt-quenching technique. The phonon sideband spectra and the optical absorption band edges for the host matrix were confirmed by means of the spectral measurements. Standard Judd-Ofelt calculations have been completed to these glasses. The dependence of up-conversion and infrared emission under 980 nm excitation on the glass composition was studied. The quantum efficiencies for the ⁴I_13/2 → ⁴I_15/2 transition of trivalent erbium in the glasses were estimated.     

Structural changes during the crystallization of the Bi4Ge3O12 glasses

Bismuth-germanate glass ceramics with the composition 40% Bi₂O₃-60% GeO₂ (in molar percents) were prepared through controlled crystallization of melt-quenched glass. The Raman and FTIR spectra recorded in the as-made glasses show broad bands at 240, 400, 780 cm^− 1 and 400, 745 cm^− 1 have been assigned Ge-O bonds which appear right after preparation. X-ray diffraction has shown that the as-made glasses are amorphous, but after annealing above the crystallization temperature at 558 °C, BGO nano-crystallites with a size of about 50 nm precipitate in the glass matrix. The Raman and FTIR spectra reveal sharp peaks associated to the “internal” and “external vibrations” of GeO₄ tetrahedral groups inside the BGO nano-crystallites. In the glass ceramic sample the transparency region is shifted at longer wavelengths compared to as-made glass, due to the Rayleigh scattering on the BGO nano-crystallites.     

Synthesis and physical properties of glasses in the Sb2O3-PbCl2-MoO3 system

Lead chloroantimonite glasses form stable binary glasses that may accommodate numerous oxides or halides as a third component. Molybdenum trioxide is a glass progenitor leading to molybdate glasses. Ternary glasses have been synthesized and studied in the Sb₂O₃-PbCl₂-MoO₃ system. Compositional limits of glass formation are reported and two series of glass samples have been prepared corresponding to the general formulas: (90 − x)Sb₂O₃-xPbCl₂-10MoO₃ and (90 − x)Sb₂O₃-xMoO₃-10PbCl₂. Glass transition temperature is close to 290 °C at high Sb₂O₃ content and decreases as antimony oxide is substituted by MoO₃ or PbCl₂. Position, width and intensity of crystallization peak suggest that devitrification rate is small in some composition ranges. The evolution of density, thermal expansion, refractive index and microhardness has been studied as a function of composition parameter x. Deviations from linearity are observed. They suggest structural changes in the case of the MoO₃/Sb₂O₃ substitution while it appears that molar volume increases linearly versus lead content in the other series of glasses. Refractive index is close to 2.04. Optical transmission ranges from 550 nm in the visible spectrum to 5.5 μm in the infrared. It is limited by extrinsic absorption bands arising from hydroxyls and silicon impurities. Young's, bulk and shear moduli have been measured for the two series of samples.     

The effect of PbF2 content on the microstructure and upconversion luminescence of Er-doped SiO2-PbF2-PbO glass ceramics

The Er³⁺ doped transparent oxyfluoride glass ceramics were obtained by appropriate heat treatment of the precursor glasses with composition (mol%) 50SiO₂-xPbF₂-(50 − x)PbO-0.5ErF₃. The microstructure and optical properties of the glasses and glass ceramics were determined by differential scanning calorimetry (DSC), X-ray diffraction (XRD), absorption spectra and luminescence spectra. The intensity of upconversion luminescence significantly increased in glass ceramics compared to that in precursor glass. The emission bands centered around 660 nm (⁴F_9/2 → ⁴I_15/2) and 410 nm (²H_9/2 → ⁴I_15/2) were simultaneously observed in glass ceramics but cannot be seen in the corresponding precursor glass. The influence of different PbF₂ content on the microstructure and upconversion luminescence of the samples was analyzed in detail. The results indicated that with the increase of PbF₂ content, the Ω₂ was almost the same and the ratios of red to green upconversion luminescence decreased in glass ceramics.     

Structure and non-linear optical performance of TeO2-Nb2O5-ZnO glasses

The non-linear optical performance and structure of TeO₂-Nb₂O₅-ZnO glasses was investigated as a function of ZnO content. The third-order non-linear optical susceptibility (χ⁽³⁾) as measured by a Degenerate Four Wave Mixing (DFWM) method, initially increased with increasing ZnO content to about 8.2 × 10⁻¹³ esu for a glass containing 2.5 wt% ZnO, and then decreased to 5.9 × 10⁻¹³ esu as the ZnO content increased to 10 wt%. There was no noticeable change as the ZnO content increased from 10 to 15 wt%. The non-linear optical response time, which caused electron cloud deformation, was from 450 to 500 fs. The structure of these glasses as analyzed by Raman spectroscopy and FT-IR spectra, was affected by the addition of ZnO up to 5 wt%, when, it is believed, the Zn²⁺ ions occupied the interstitial positions in the glass network by replacing the Nb⁵⁺ ions. The replaced Nb⁵⁺ ions occupied the network forming positions as the Te⁴⁺ ions. Increasing ZnO > 5 wt% did not have any further effect on the glass structure.     

Structural study of PbO-MoO3-P2O5 glasses by Raman and NMR spectroscopy

Glasses in the ternary system PbO-MoO₃-P₂O₅ were prepared in three compositional series (100 − x)[0.5PbO-0.5P₂O₅]-xMoO₃ (A), 50PbO-yMoO₃-(50 − y)P₂O₅ (B) and (50 − z)PbO-xMoO₃-50P₂O₅ (C) and their structure was studied by Raman and ³¹P NMR spectroscopies. In the compositional series (100 − x)[0.5PbO-0.5P₂O₅]-xMoO₃ homogeneous glasses were prepared in the concentration region of 0-70 mol% MoO₃. Their glass transition temperature increases with increasing MoO₃ content having a maximum at x = 50 mol% MoO₃. ³¹P MAS NMR spectra reveal that in the glass series (A) the incorporation of MoO₃ results in the shortening of phosphate chains and gradual transformation Q² units into Q² and Q⁰ units, prevailing in glasses with a high MoO₃ content. Octahedral structural units MoO₆ dominate in most glass compositions and they are present also in the structure of Pb(MoO₂)₂(PO₄)₂ compound corresponding to the glass composition 50Pb(PO₃)₂-50MoO₃. The analysis of Raman spectra of glasses of the (B) series with a high MoO₃ content showed the transformation of octahedral MoO₆ units into tetrahedral MoO₄ units.     

Electron spin resonance and magnetic studies on CaO-SiO2-P2O5-Na2O-Fe2O3 glasses

Room temperature electron spin resonance (ESR) spectra and temperature dependent magnetic susceptibility measurements have been performed to investigate the effect of iron ions in 41CaO · (52 − x)SiO₂ · 4P₂O₅ · xFe₂O₃ · 3Na₂O (2 ? x ? 10 mol%) glasses. The ESR spectra of the glass exhibited the absorptions centered at g ≈ 2.1 and g ≈ 4.3. The variation of the intensity and linewidth of these absorption lines with composition has been interpreted in terms of variation in the concentration of the Fe²⁺ and Fe³⁺ in the glass and the interaction between the iron ions. The magnetic susceptibility data were used to obtain information on the relative concentration and interaction between the iron ions in the glass.     

Crystallization processes of Li2O-Ga2O3-SiO2-NiO system glasses

Crystallization processes of Li₂O-Ga₂O₃-SiO₂-NiO system glasses have been studied by X-ray diffraction, differential calorimetry and optical absorption. Transparent glass-ceramic containing LiGa₅O₈:Ni²⁺ as the sole crystalline phase has been obtained from glass with the composition of 13Li₂O-23Ga₂O₃-64SiO₂-0.1NiO (in mol%) by the heat treatment in the temperature range from 923 to 953 K. It was revealed that the specific surface area of samples enhances crystallization of LiGaSi₂O₆ but obstructed that of LiGa₅O₈. LiGa₅O₈ grew to nano-sized crystallites dispersed in the glass matrices and did not affect the transparency seriously. In contrast, LiGaSi₂O₆ grew to crystallites with diameters more than 100 nm on the surface and made the glasses opaque. Optical absorption measurements revealed that doped Ni²⁺ occupied five-folded trigonal bipyramidal sites in the as-quenched glass matrices but six-folded octahedral sites of precipitated LiGa₅O₈ in the glass-ceramics. It was confirmed that transparent glass-ceramic containing Ni²⁺:LiGa₅O₈ was effectively obtained by the heat treatment at a temperature of 953 K for 10 h.