层状纳米催化复合材料HNbWO6／Pt的合成及性质

用固相合成法合成出LiNbWO6,并用离子交换法制备出HNbWO6;通过PrNH2层间膨胀、Pt(NH3)4^2 层间插入和紫外光分解等反应,合成出一种新的层状光催化纳米复合材料HNbWO6／Pt,并比较了不同合成方法对样品性能的影响,X射线衍射、漫反射、ICP和比表面积测定等的表征结果表明：该样品的层间高度为0.3-0.5nm ,禁带能隙为2.25-3.10eV,用波长大于290nm和450W汞灯照射5h,1g样品可催化分解甲醇溶液（10％）产生氢气约40ml,表明所研制的层状纳米合材料具有较高的光催化活性。     

层状纳米光催化复合材料H0.8Fe0.8Ti1.2O4/TiO2的合成及性质

用固相合成法制备出K0.8Fe0.8Ti1.2O4,并用离子交换反应制备出H0.8Fe0.8Ti1.2O4;通过C3H7NH2层间膨胀,TiO2粒子的插入和紫外光分解等反应,合成出一种新的层状光催化纳米复合材料-H0.8Fe0.8Ti1.2O4/TiO2.X射线衍射和漫反射等表征结果表明 该样品的层间高度为0.47nm,禁带能隙为2.18和2.88eV.用(>400 nm的光照射30 min,0.4 g样品可使甲基橙溶液(20 mg/L)的降解率达到22.1%.而同样条件下标准TiO2(P-25)仅为6.2%,表明所研制的层状纳米复合材料具有较高的光催化活性.     

HNdNb2O7/(Pt,TiO2)的制备和光催化性能的研究

利用层间插入反应,合成HNdNb2O7/(Pt,TiO2 )层状光催化纳米复合材料.采用X射线衍射、紫外-可见光漫反射、比表面积测定分析等分析手段对所制备的材料进行了表征.通过光照分解水,考察了所制备的材料的光催化性能,结果表明所制备的HNdNb2O7 /(Pt ,TiO2 )纳米复合材料具有较高的光催化分解水效率并且其光催化活性稳定.     

层间距为1.44 nm层状氢氧化苯甲酸锌剥离重组行为研究

层间距为1.44 nm层状氢氧化苯甲酸锌在乙醇、正丙醇、正丁醇介质中可剥离成其基本组成单元纳米层. 用TG-DTA、XRD、SEM、TEM和元素分析等手段研究了剥离的纳米层重组得到样品的结构特征、形貌和化学组成. 结果表明: 水热合成样品和剥离的纳米层重组样品具有相同的层状结构, 它们的化学组成分别为Zn(OH)1.12(C6H5COO)0.88和Zn(OH)1.1(C6H5COO)0.9. 水热合成的纤维状粒子剥离重组后改变成为像纳米带和纳米花粒子形貌.     

Ni-CH_3CH_2NH_2/H_(1.78)Sr_(0.78)Bi_(0.22)Nb_2O_7复合层状钙钛矿的合成及光催化分解水产氢性能(英文)

自从分解水产氢被首次报道以来,许多光催化剂被开发出来并用于光催化分解水产氢.然而,由于光生电子和空穴的复合率普遍较高,大部分的光催化剂分解水产氢效率都很低.因此,开发新型高效的光催化材料至关重要.具有(Bi_2O_2)~(2+)(A_(m-1)M_mO_(3m+1))~(2-)通式的Aurivillius相层状钙钛矿材料因具有独特的层状结构、元素可调性以及优异的电荷传输和分离能力而广泛应用于光催化分解水和去除有机污染物.此外,当该类层状钙钛矿被剥离成超薄纳米片时,其光催化性能进一步提高.为了进一步提高层状钙钛矿的载流子分离能力,将客体(如贵金属,半导体等)通过化学反应的途径插入到层状钙钛矿的层间区域,从而合成出复合层状钙钛矿被广泛发展和应用.然而,引入的客体主要是贵金属和半导体,这类客体的高成本和不均匀分布制约了其进一步的应用.由于廉价、无毒和稳定等优点,镍基材料如Ni,NiO,Ni_2O_3,NiS,NiS_2,Ni(OH)2和Ni(OH)x等被广泛用作增强电极材料的光电性能和催化剂的光催化分解水产氢性能的助催化剂.本文采用简单的原位化学反应法制备出镍基配合物Ni-CH_3CH_2NH_2(Ni-EA)插层的Ni-CH_3CH_2NH_2/H_(1.78)Sr_(0.78)Bi_(0.22)Nb_2O_7(Ni-EA/HSNNs)复合层状钙钛矿;然后采用X-射线衍射(XRD)、傅立叶变换红外光谱(FTIR)、X-射线光电子能谱(XPS)、紫外-可见漫反射光谱等手段对Ni-EA/HSNNs光催化剂进行了系统的研究.XRD结果表明,引入Ni~(2+)后,HSNNs层间距减小并且平行于钙钛矿层的晶面结晶度增强,证明HSNNs沿垂直于钙钛矿层的方向出现了层层组装.FTIR和XPS结果表明,引入的Ni~(2+)与HSNNs层间和表面的乙胺分子之间存在较强的相互作用,结合高分辨透射电镜图可知,Ni的存在形态可能为配合物Ni-EA.由此可见,当向HSNNs中引入Ni~(2+)时,Ni~(2+)和HSNNs层间和表面的乙胺分子反应生成带正电的配合物Ni-EA,由于Ni-EA与HSNNs的钙钛矿层带有异种电荷,两者之间存在较强的静电相互作用力,从而引起钙钛矿纳米片HSNNs的层层组装,最后形成Ni-EA/HSNNs复合层状钙钛矿.光催化分解水产氢性能测试结果表明,当引入0.5 wt%Ni时,复合层状钙钛矿表现出最优的光催化性能.与HSNNs(241.58μmol/h)相比,0.5%Ni-EA/HSNNs的光催化分解水产氢速率(372.67μmol/h)提高了0.54倍,表现出与0.5%Pt/HSNNs可比拟的光催化活性,可见,非贵金属Ni具有替代贵金属Pt的能力.进一步的研究表明,镍基配合物Ni-EA显著增强了催化剂的光生载流子的传输和分离能力,从而提高了其光催化分解水产氢性能.该文为光催化分解水产氢提供了一种简便的合成非贵金属配合物助催化剂的方法.     

X射线光电子能谱法研究UV_(254nm)光催化、O_3强化UV_(254nm)光催化和真空紫外光催化降解甲醛中Pt-TiO_2薄膜的表面性质(英文)

以Pt-TiO2为光催化剂,研究了气相甲醛分别在35 h连续UV254 nm光催化、O3强化UV254 nm(O3+UV254 nm)光催化和真空紫外(UV254+185 nm)光催化中的降解效率,考察了副产物O3的去除率,采用X射线光电子能谱(XPS)法分析Pt-TiO2在不同光催化前后Pt的电子态和累积有机产物,研究纳米Pt对甲醛降解和O3去除的强化机理.连续光催化降解实验表明,以纳米Pt改性TiO2可以同时增强甲醛和O3的去除率,特别是O3的去除率可提高3.1–3.4倍.对催化剂C 1s和O 1s峰分别经分峰拟合处理后,发现Pt-TiO2上累积的含羰基和羟基的有机物含量按以下顺序减少:UV254 nm光催化O3强化UV254 nm光催化真空紫外光催化,而在连续35 h光催化降解过程中,催化剂的失活现象却按相反的方向变得越来越不明显.负载的金属Pt在O3+UV254 nm和UV254+185nm光催化过程中被氧化成PtOads和Pt4+物种,而在UV254 nm光催化过程中金属Pt未被氧化,所以推测是气相中的O3和羟基自由基参与金属Pt的氧化过程.Pt-TiO2表面高价态的Pt氧化物种可作为光生电子捕获中心,强化光生载流子的分离过程,增强Pt-TiO2的光催化活性.Pt氧化物种可作为O3分解的活化中心,使Pt-TiO2对O3的分解效率远高于纯TiO2.以XPS对比研究在三种不同光催化环境中Pt-TiO2表面性质,可以解释在UV254+185 nm光催化过程中纳米Pt对甲醛和O3同时去除的强化机理,并说明了催化剂不失活的内在原因.     

Ag3VO4纳米粒子的合成及其对可见光下降解罗丹明B的催化活性

利用一种简单共沉淀的方法,通过调变合成温度(0～80 ℃)成功地合成了一系列Ag3VO4样品,其粒子尺寸在100 nm～5 μm间. 通过在合成体系中添加聚乙二醇4000, Ag3VO4粒子尺寸可进一步降低至50～100 nm. 可见光下降解罗丹明B的实验结果表明, Ag3VO4样品特别是纳米尺寸的样品,显示出比当前广泛使用的P25更高的催化活性. Ag3VO4样品循环使用4次之后其光催化活性并没有明显降低,证明Ag3VO4是一种稳定有效的可见光催化剂.     

原位聚合法制备聚丙烯酸甲酯/ZnAl层状双氢氧化物插层纳米复合材料及其形貌特征

近 2 0年来 ,聚合物 /层状无机物纳米复合材料引起了广泛关注 ,与聚合物材料相比 ,该类纳米复合材料在力学、热稳定性、阻燃、气体阻隔等性能方面都有显著增强 .但所报道的绝大部分无机物均采用蒙脱土为代表的层状硅酸盐[1～ 3] ,而以层状双氢氧化物 (Layered double hydroxide,LDH)为基础制备的聚合物 /层状无机物纳米复合材料的报道极少 .LDH是由水镁石结构中的二价阳离子 (M2 + )被三价阳离子 (M3+ )取代而形成的 ,层上产生的剩余正电荷被吸附在层间的阴离子平衡 .与层状硅酸盐相比 ,L DH层间电荷密度高 ,层与层之间相互作用强 ,导…     

原位光还原法制备高分散铂沉积多孔氮化碳复合材料及其降解水中4-氟苯酚的高效可见光光催化活性（英文）

作为一种新型水中有机污染物,有机氟化物中C–F共价键的键能较大,因而很难通过传统的可见光光催化剂降解.因此,开发高效可见光光催化剂是实现在可见光照射下成功降解水中有机氟化物的关键.作为一种非金属半导体光催化剂,石墨相氮化碳(g-C_3N_4)因具有可见光响应、环境友好及低成本等优点而广泛应用于水中有机污染物去除.然而,体相层状结构严重限制了g-C_3N_4的可见光活性.这是由于体相层状结构不利于光生电子的表面迁移,同时增加了光催化反应过程的传质阻力.为了开发一种可重复使用且具有优异可见光活性的光催化剂,进而实现在可见光照射下水中有机氟化物的高效降解及矿化,本文以氯铂酸和多孔氮化碳(pg-C_3N_4)为前驱体,运用简单的原位光还原法成功制备出一系列高分散铂沉积多孔氮化碳复合材料(Pt/pg-C_3N_4),而pg-C_3N_4则是以三聚氰胺为原料采用前驱体预处理法制备.与传统铂沉积石墨相氮化碳(Pt/g-C_3N_4)复合材料相比,由于多孔氮化碳前驱体具有暴露的几何内外表面,铂纳米粒子可高度分散于其上.因此,铂纳米粒子的电子捕获效应显著增强.另外,与其他传统还原法相比,原位光还原技术还可有效抑制铂纳米粒子的自凝聚.我们对制备的Pt/pg-C_3N_4复合材料的形貌、孔隙率、相结构、化学组成及光电性质进行了详细表征.结果显示,与传统Pt/g-C_3N_4复合材料相比,由于多孔微观结构的构建以及高度分散铂纳米粒子的沉积,制备的Pt/pg-C_3N_4复合材料的BET比表面积显著增大,光吸收能力明显增强,光催化量子效率显著提高.在可见光条件下,初步评价了该复合材料光催化降解水中偶氮染料甲基橙的活性,然后将其进一步应用于水中4-氟苯酚的降解及矿化.结果表明,由于多孔微观结构的构建以及高度分散铂纳米粒子的沉积,所制备Pt/pg-C_3N_4复合材料具有相当高的可见光光催化活性.结果还显示,所制复合材料具有很高的稳定性,连续使用4次均保持相似的活性.作为一种可见光催化剂,所制Pt/pg-C_3N_4复合材料有望广泛应用于水中持久性有机污染物的降解以及光催化劈裂水产氢、NO分解和CO_2还原等领域.     

原位光还原法制备高分散铂沉积多孔氮化碳复合材料及其降解水中4-氟苯酚的高效可见光光催化活性

作为一种新型水中有机污染物,有机氟化物中C–F共价键的键能较大,因而很难通过传统的可见光光催化剂降解.因此,开发高效可见光光催化剂是实现在可见光照射下成功降解水中有机氟化物的关键.作为一种非金属半导体光催化剂,石墨相氮化碳(g-C3N4)因具有可见光响应、环境友好及低成本等优点而广泛应用于水中有机污染物去除.然而,体相层状结构严重限制了g-C3N4的可见光活性.这是由于体相层状结构不利于光生电子的表面迁移,同时增加了光催化反应过程的传质阻力.为了开发一种可重复使用且具有优异可见光活性的光催化剂,进而实现在可见光照射下水中有机氟化物的高效降解及矿化,本文以氯铂酸和多孔氮化碳(pg-C3N4)为前驱体,运用简单的原位光还原法成功制备出一系列高分散铂沉积多孔氮化碳复合材料(Pt/pg-C3N4),而pg-C3N4则是以三聚氰胺为原料采用前驱体预处理法制备.与传统铂沉积石墨相氮化碳(Pt/g-C3N4)复合材料相比,由于多孔氮化碳前驱体具有暴露的几何内外表面,铂纳米粒子可高度分散于其上.因此,铂纳米粒子的电子捕获效应显著增强.另外,与其他传统还原法相比,原位光还原技术还可有效抑制铂纳米粒子的自凝聚.我们对制备的Pt/pg-C3N4复合材料的形貌、孔隙率、相结构、化学组成及光电性质进行了详细表征.结果显示,与传统Pt/g-C3N4复合材料相比,由于多孔微观结构的构建以及高度分散铂纳米粒子的沉积,制备的Pt/pg-C3N4复合材料的BET比表面积显著增大,光吸收能力明显增强,光催化量子效率显著提高.在可见光条件下,初步评价了该复合材料光催化降解水中偶氮染料甲基橙的活性,然后将其进一步应用于水中4-氟苯酚的降解及矿化.结果表明,由于多孔微观结构的构建以及高度分散铂纳米粒子的沉积,所制备Pt/pg-C3N4复合材料具有相当高的可见光光催化活性.结果还显示,所制复合材料具有很高的稳定性,连续使用4次均保持相似的活性.作为一种可见光催化剂,所制Pt/pg-C3N4复合材料有望广泛应用于水中持久性有机污染物的降解以及光催化劈裂水产氢、NO分解和CO2还原等领域.     

Catalysis by Using TiO2 Nanoparticles and Nanotubes

TiO2 has attracted considerable attention due to its stability, non-toxicity, low cost, and great potential for use as a photocatalyst in environmental applications. Since strong metal-support interaction (SMSI) of titania-supported noble metals was first reported in 1978, titania supported catalyst has been intensively studied in heterogeneous catalysis. However, the effective catalytic activity was restricted due to the low surface area of TiO2. Recently, TiO2-based nanotubes were extensively investigated because of their potentials in many areas such as highly efficient photocatalysis and hydrogen sensor.In the present study, formation of titanium oxide (TiO2) nanotubes was carried out by hydrothermal method, with TiO2 nanoparticle-powders immersed in concentrated NaOH solution in an autoclave at 110 ℃. Preparation of nano-size Pt on TiO2-nanoparticles or TiO2-nanotubes was performed by photochemical deposition method with UV irradiation on an aqueous solution containing TiO2 and hexachloroplatinic acid or tetrachloroauric acid. The TEM micrographs show that TiO2-nanotubes exhibit ～300 nm in length with an inner diameter of ～ 6 nm and the wall thickness of ～ 2 nm, and homogeneous nanosize Pt particles (～ 2 nm) were well-dispersed on both nanoparticle- and nanotube- titania supports. It also shows the nanotube morphology was retained up2o n Pt-immobilization. Nitrogen adsorption isotherm at 77K resulted a high surface area (～ 200m/g) of TiO2-nanotubes, which is about 40 times greater than that of "mother" TiO2 nanoparticles (～5 m/g). All the spectroscopic results exhibited that the nanotube structure was not significantly affected by the immobilized Pt particles. Ti K-edge XANES spectra of TiO2 nanotube and Pt/TiO2-nanotube represent that most titanium are in a tetrahedral coordination with few retained in the octahedral structure.In the in-situ FT-IR experiments, an IR cell was evacuated to a pressure of 10-5 torr at room temperature as soon as the catalyst-pellet, Pt/TiO2 or Pt/TiO2-nanotube, was placed inside the cell.Then, 60 torr of hydrogen was introduced into the cell and subsequently the temperature was programmed to increase from room temperature to 300℃ at a constant heating rate of 5℃/min.For Pt/TiO2, an IR peak at 2083 em-1 started to appear at 200℃ with a maximum intensity at 250℃ and then decreasing as temperature increased. The 2083 em-1 IR peak corresponds to the linearly adsorption of CO on the well-dispersed Pt sites. Simultaneously, the IR bands of gaseous methane at 3016 em-1 started to appear at 225℃ and the peak intensity increased with temperature. The results reveal that Pt/TiO2 can adsorb gaseous CO2 and further catalyzes the reduction of CO2 by H2 through the intermediate CO, which further produces gaseous methane. While for the Pt/TiO2-nanotube catalyst, methane was produced at relatively low temperature, 100℃, and it catalyzed the direct conversion of CO2 to CH4. The absence of intermediate CO-adsorption signals durinng the temperature programmed process indicates that the prepared TiO2 nanotube-supported nanosize Pt possesses a potent capability for CO2 adsorption and highly catalytic activity in the hydrogenation of CO2, and was superior to the conventional Pt/TiO2 catalyst. The catalytic activity of Pt/TiO2-nanotube was indeed significantly enhanced by the high surface area of TiO2-nanotubes.Details will be discussed.     

Kinetic analysis of superoxide anion radical-scavenging and hydroxyl radical-scavenging activities of platinum nanoparticles

There are few reports on the physiological effects of metal nanoparticles (nps), especially with respect to their functions as scavengers for superoxide anion radical (O2(.-)) and hydroxyl radical (.OH). We tried to detect the scavenging activity of Pt nps using a hypoxanthine-xanthine oxidase system for O2(.-) and using a Fenton and a UV/H2O2 system for .OH. Electron spin resonance analysis revealed that 2 nm particle size Pt nps have the ability to scavenge O2(.-) and .OH. The calculated rate constant for the O2(.-)-scavenging reaction was 5.03 +/- 0.03 x 10(7) M (-1) s (-1). However, the analysis of the Fenton and UV/H 2O 2 system in the presence of Pt nps suggested that the .OH-scavenging reaction cannot be determined in both systems. Among particle sizes tested from 1 to 5 nm, 1 nm Pt nps showed the highest O2(.-)-scavenging ability. Almost no cytotoxicity was observed even after adherent cells (TIG-1, HeLa, HepG2, WI-38, and MRC-5) were exposed to Pt nps at concentrations as high as 50 mg/L. Pt nps scavenged intrinsically generated reactive oxygen species (ROS) in HeLa cells. Additionally, Pt nps significantly reduced the levels of intracellular O2(.-) generated by UVA irradiation and subsequently protected HeLa cells from ROS damage-induced cell death. These findings suggest that Pt nps may be a new type of antioxidant capable of circumventing the paradoxical effects of conventional antioxidants.     

有机钌螯合物/TiO_2杂化膜修饰电极上Pt纳米团簇的光电流增强效应

利用LB膜技术可控制备了纳米单层和多层的二氧化钛-有机钌螯合物杂化膜,并研究了上述无机-有机杂化膜修饰电极在Pt纳米团簇敏化后的光电流增强效应.实验结果表明:(1)纳米单层TiO2/[Ru(phen)2(dC18bpy)]2+(简称为TiO2-Ru)杂化膜的平均厚度为(3.6±0.5)nm;(2)在光照条件下TiO2-Ru杂化膜能有效催化还原[Pt(NH3)6]4+形成粒径位于20～160nm之间的Pt纳米团簇;(3)Pt纳米团簇的引入消除了金属钌螯合物中配体对电子传递的阻碍作用,改变了电子传递途径,从而有效减少了电子空穴对的复合,提高了Pt纳米团簇敏化的n层杂化膜修饰电极(ITO/(TiO2-Ru)n/Pt)在支持电解质中的光电流.与纳米单层TiO2-Ru杂化膜修饰的ITO电极(ITO/TiO2-Ru)相比,当工作电压为900mV时,ITO/TiO2-Ru/Pt在0.1mol·L-1的NaClO4电解质溶液中和光照(λ360nm)条件下,单位面积的光电流提高了约5倍;(4)ITO/(TiO2-Ru)n/Pt电极光电流的大小与杂化膜的层数密切相关,当TiO2-Ru杂化膜的层数从一层、二层增加到四层时,光电流呈现先升高后下降行为,这表明ITO/(TiO2-Ru)n/Pt电极的电子传递过程直接通过非电活性的二氧化钛纳米单层进行.     

含葑基的缩氨基硫脲、噻二唑的合成、表征与晶体结构

以(－)-葑酮为原料经中间体葑胺合成4-葑基氨基硫脲(4), 4与醛缩合得到11个未见文献报道的葑基缩氨基硫脲(5), 5用六氰合铁(III)酸钾氧化成环得到相应的2,5-二取代-1,3,4-噻二唑类化合物(6); 产物的结构经IR, NMR和元素分析确认, 并用X射线衍射法测定化合物6d的晶体结构. 化合物6d属单斜晶系, P2(1)空间群, 晶胞参数 a＝1.18719(10) nm, b＝1.48814(18) nm, c＝1.21629(12) nm, β＝118.113(2)°, Mr＝343.48, V＝1.8953(3) nm3, Dc＝1.204 Mg/m3, Z＝4, λ＝0.071073 nm, μ(Mo Kα)＝0.181 mm－1, F(000)＝736.     

A New Method for the HPLC Analysis of Pt(II) in Urine

Abstract

An analytical method has been developed to measure Pt(II) in urine via derivatization and UV or HPLC analysis. A measured quantity of urine is heated briefly with diethyl ammonium diethyl-dithiocarbamate, and the resulting Pt(Et₂NCS₂)₂ is extracted into a measured volume of chloroform. Concentrations of Pt(II) are determined by UV absorption at 346 nm or by reverse phase HPLC analysis. The detection limit for Pt(II) as its dithiocarbamate is ～ 1 ng by HPLC; the concentration limit for HPLC analysis by direct extraction was ～ 25 ng/ml. Chromatographic response was linearly related to Pt(II) concentration over the range 100-4, 000 ng/ml; dilution of more concentrated samples has extended this range to at least 30, 000 ng/ml. This method has been applied to the analysis of Pt(II) in the urine of patients who have received cis-dichlorodiamniineplatinum(II) (CDDP) chemotherapy.     

Synthesis and characterization of platinum catalysts on multiwalled carbon nanotubes by intermittent microwave irradiation for fuel cell applications

Pt electrocatalysts supported on multiwalled carbon nanotube (Pt/MWCNT) nanocomposites have been synthesized by a rapid intermittent microwave irradiation (IMI) technique for polymer electrolyte and direct methanol fuel cells (PEFCs and DMFCs), using H(2)PtCl(6) as Pt precursor. The Pt/MWCNT nanocomposites are characterized by XRD, XPS, and TEM. The results indicate that Pt particle size and distribution on the MWCNT support are affected significantly by the oxidation treatment of MWCNTs, the IMI procedure, and the MWCNT tube diameter or surface area. The PtO(x) (x = 1, 2) species was first deposited on the surface of MWCNTs by the IMI and subsequently reduced to Pt(0) with refluxing in the presence of HCOOH. Pt/MWCNT nanocomposites synthesized by this IMI method have achieved extremely uniform dispersed Pt nanoparticles with a particle size of approximately 3 nm. Electrochemical measurement indicates that Pt/MWCNT nanocomposites synthesized by the IMI method display a significantly higher electrochemically active area and higher catalytic activity for the methanol oxidation reaction in comparison to a commercial Pt/C catalyst.     

二氧化硫水溶液在修饰硫化镉粉末上的光催化反应

本文从应用意图出发,采用CdS、混Pt/CdS和镀Pt/CdS三种光催化剂,研究(1)反应温度,(2)催化剂表面含Pt量,(3)修饰方法和催化剂表面结构形貌对光催化SO₂水溶液生成H₂SO₄同时放H₂反应的活性和选择性的影响。结果表明:(1)本反应有明显温度效应,利用太阳能中约占50％的红外段辐射来提高反应温度到70℃可使活性增至7倍,但选择性下降,(2)估算了反应活化能为21kJ·mol^-1,(3)得出60℃为反应较佳温度,(4)表面含Pt量在5％左右活性最高,(5)混Pt/CdS体系形成高分散、细颗粒分布,其催化活性比镀Pt/CdS体系为高。根据实验结果对反应机理进行了一些讨论。     

固相反应制备的Pt/C催化剂对乙醇氧化的电催化活性

用固相反应法制备了Pt/C催化剂(Pt/C(s))，并研究了该催化剂对乙醇氧化的电催化活性. XRD和TEM测量表明， Pt/C(s)中Pt的平均粒径为3.8 nm，结晶度为2.38，远小于用传统的液相还原方法制得的Pt/C催化剂(Pt/C(l))的平均粒径(8.5 nm)和结晶度(5.56).因此, Pt/C(s)对乙醇的电催化氧化性能远好于液相还原法制得的Pt/C(l).     

Pt/CNT纳米催化剂的微波快速合成及其对甲醇电化学氧化的电催化性能

碳纳米管 (CNT)作为制备新型催化剂载体已有广泛的研究 [1～ 8] ,例如 ,在其表面负载 Pt,Ru和Pt Ru后则具有良好的催化性能[1,2 ,6～ 8] .但在 CNT表面负载金属微粒的方法难以获得尺寸和形状均匀的纳米粒子 .因此 ,如何制备超细和均匀的纳米粒子是一项具有重要的学术意义和技术价值的工作 .我们利用微波加热的多元醇工艺合成了 XC-72碳负载铂纳米粒子的催化剂 ,并发现它对甲醇的氧化具有较高的电催化活性 [9] .本文进一步以 CNT作为载体 ,利用微波加热法快速合成了 Pt/ CNT纳米催化剂 ,并对其对甲醇电化学氧化的性能进行了初步研究 …     

Pt纳米催化剂在质子交换膜燃料电池催化层中的尺寸效应研究

以XC-72碳黑为载体, H2[PtCl6]为前驱体, 采用浸渍还原法并结合后续高温处理, 制备出不同尺寸Pt颗粒(3～8 nm)的Pt/C催化剂. 在基于质子交换膜燃料电池(PEMFC)单电池的电化学电解池中, 对实际PEMFC催化层中燃料电池反应的Pt催化剂尺寸效应进行了研究. 结果表明, 在PEMFC催化层环境中, Pt/C纳米催化剂对氢氧化和氧还原反应均有显著的粒度尺寸效应. 随着Pt粒度减小, 氢氧化和氧还原反应的表面积活性均降低.