Fe_3O_4/SiO_2/PMMA磁性纳米粒子的制备及其磁性能

通过沉淀氧化法制得Fe3O4磁性粒子(1);通过Stber法用Si O2对Fe3O4进行表面改性制得Fe3O4/Si O2磁性纳米粒子(2);通过原子转移自由基聚合法将聚甲基丙烯酸甲酯(PMMA)接枝到2上,制得Fe3O4/Si O2/PMMA磁性高分子纳米粒子(3),其结构和磁性能经IR,扫描电镜(SEM),透射电镜(TEM),磁性分析(VSM)和热重分析(TGA)表征。结果表明,3的粒径小且磁性强,平均粒径约为220 nm,饱和磁化强度为44.3 emu·g-1,室温下具有超顺磁性。     

Preparation for Magnetic Nanoparticles Fe3O4 and Fe3O4@SiO2 and Heterogeneous Fenton Catalytic Degradation of Methylene Blue

Dyestuff textile wastewater treatment has become a research hotspot due to its high chroma, poor biodegradability, and low toxicity characteristics. In this paper, we have synthesized magnetic Fe₃O₄ and core‐shell Fe₃O₄@SiO₂ materials by hydrothermal methods. These materials were characterized by XRD, TEM, N₂ adsorption‐desorption and so on. These materials’ heterogeneous Fenton has been applied to dye wastewater treatment. Methylene blue was used as a typical target of dye wastewater. Decolorization ratios of methylene blue were determined by different nanostructure composites catalysts. A serious of results of study showed that decolorization ratios of magnetic nanoparticles and core‐shell composites arrived at above 90 % under the weakly acidic or neutral conditions and room temperature. When these catalysts were reused, the results show that Fe₃O₄@SiO₂ materials were possessed with good cycle performance.     

A comparative study of TiO2, Al2O3, and Fe3O4 nanoparticles as reusable heterogeneous catalysts in the synthesis of tetrahydrobenzo[a]xanthene-11-ones

Russian Journal of General Chemistry - Catalytic effect of three nanosized metal oxides TiO2, Al2O3 and Fe3O4 nanoparticles in the onepot synthesis of tetrahydrobenzo[a]xanthene-11-ones by...     

纳米Fe3O4/PVDF磁性复合膜的原位制备及表征

通过膜相渗透原位化学沉积法制备了聚合物基Fe3O4/聚偏氟乙烯（PVDF）磁性纳米复合膜，研究了复合膜制备的适宜条件，采用红外光谱（FT-IR）、差热分析（DSC）、X射线衍射、扫描电镜（SEM）等手段对复合膜的组成、结构进行了表征和分析，通过气体渗透法测定了复合膜的孔径随制备条件的变化情况. FT-IR和XRD图谱结果表明，在基膜中原位生成Fe3O4后不影响基膜PVDF的分子结构；复合膜中的Fe3O4粒子尺寸为68 nm左右，复合膜的磁化率达0.044 cm3•g－1；复合膜的磁化率、平均孔径、最大孔径及孔径分布范围随反应条件的改变而有明显变化.     

单分散Fe3O4纳米颗粒的控制合成和表征

以十八烯为溶剂、乙酰丙酮铁为铁源,并在油酸、油胺的辅助作用下,通过热分解法成功合成了单分散Fe3O4纳米颗粒。讨论了实验参数如反应温度、表面活性剂的量和种类、溶剂、油酸、油胺对单分散Fe3O4纳米颗粒的尺寸及形貌的影响。利用X射线衍射（XRD）、透射电子显微镜（TEM）、选区电子衍射（SAED）和高分辨透射电子显微镜（HRTEM）对所得产物的物相、结构、尺寸和形貌进行了表征分析。通过振动样品磁强计（VSM）表征产物磁性能,表明在室温下,Fe3O4纳米颗粒的饱和磁化强度（Ms）和矫顽力（Hc）分别为74.0 emu/g,72.6 Oe。     

导电聚苯胺与Fe3O4磁性纳米颗粒复合物的合成与表征

对十二烷基苯磺酸(DBSA)掺杂的导电聚苯胺(PAn-DBSA)的氯仿溶液,在pH为中性的条件下,采用“修饰-再掺杂(Modification-re-doped)法”合成了含有Fe₃O₄磁性纳米颗粒的导电聚苯胺复合物的有机溶液.用FTIR,XRD,TEM,UV-Vis和SQUID等对所得复合物进行了表征,结果表明,该复合物呈现超顺磁性和半导体的导电性,并具有较好的透明性.     

新型磁性Fe3O4/EDTA复合纳米粒子的制备及性能研究

采用氨羧络合剂EDTA对纳米磁性Fe3O4粒子进行表面改性,制备出能够螯合金属离子和放射性核素离子的磁性Fe3O4/EDTA复合纳米粒子.用X射线衍射、红外光谱、透射电子显微镜、光电子能谱、振动样品磁强计和原子吸收光谱对复合粒子进行了表观形貌、结构、磁学及螯合性能表征.结果表明,纳米磁性Fe3O4和EDTA之间能够有效地以化学键合方式进行复合.改性后,Fe3O4/EDTA纳米复合粒子可以对包括放射性金属离子在内的多种金属离子具有良好的络合效果.     

A Novel Synthesis and Antioxidant Evaluation of Functionalized [1,3]‐Oxazoles Using Fe3O4‐Magnetic Nanoparticles

In this research, green procedure was employed for biosynthesis of magnetic nanoparticles of iron oxide (Fe₃O₄‐MNPs) by reduction of ferric chloride solution with Orange peel water extract. Also, dihydro‐2H‐cyclopenta[d][1,3]oxazole was generated through multicomponent reaction of 1,3‐oxazole‐2(3H)‐thione, dialkyl acetylenedicarboxylates, α‐haloketones, and Fe₃O₄‐MNPs as catalyst at ambient temperature in good yield. Initially, 1,3‐oxazole‐2(3H)‐thione derivatives as one of the precursors are produced through the reaction of alkyl bromides, isothiocyanate, sodium hydride, and Fe₃O₄‐MNPs as catalyst water at ambient temperature in 83–95% yields. Also, diphenyl‐picrylhydrazine radical trapping and ferric reduction activity potential assays are used for evaluation of antioxidant activity of some synthesized compounds. Among investigated compounds, 4b has good power for radical trapping activity and 4d has good reduction power to butylated hydroxytoluene and 2‐tert‐butylhydroquinone.     

磁性Fe3O4纳米晶制备及应用

磁性Fe₃O₄纳米晶由于其独特的磁性能,已在许多领域得到了广泛的应用,并且在不同的应用领域其制备方法也不尽相同。本文综述了近年来磁性Fe₃O₄纳米晶的液相制备方法,如沉淀法、溶剂热法、溶胶-凝胶法、微乳液法、微波超声法等研究进展,对这些制备方法的特点进行了归纳概括,并详细分析了制备工艺中不同影响因素对Fe₃O₄纳米晶结构与性能的影响。同时,对磁性Fe₃O₄纳米晶在磁流体、微波吸收、污水处理、催化、药物载体、生物酶固定、生物传感器等方面的应用及发展趋势进行了评述,以期对Fe₃O₄纳米晶的制备及应用有较全面的认识。     

羧甲基纤维素/Fe3O4复合纳米磁性材料的制备、表征及吸附性能的研究

采用改进的氧化沉淀法在羧甲基纤维素(CMC)体系中制备了以磁性纳米Fe₃O₄为核心, 外层包覆羧甲基纤维素的复合磁性纳米材料. 用透射电镜、X射线衍射、红外光谱、Zeta电位和震动样品磁强计对复合纳米Fe₃O₄进行了表面形貌、结构和磁学的表征. 在此基础上研究了复合纳米Fe₃O₄对Cu^2＋的吸附性能, 探讨了溶液pH、反应时间和 Cu^2＋的初始浓度对其吸附性能的影响. 实验结果表明, 复合Fe₃O₄粒子为反尖晶石型, 平均粒径在40 nm左右, 羧甲基纤维素在Fe₃O₄粒子表面是化学吸附, 复合Fe₃O₄粒子的饱和磁化强度为36.74 emu/g, 在中性溶液中Cu^2＋的吸附量最高, 吸附平衡时间为1.5 h, 二级动力学模型能够很好地拟合吸附动力学数据, 吸附等温数据符合Langmuir模型. 复合纳米Fe₃O₄对Cu^2＋的吸附机理主要为表面配位反应.     

Characterization and application of Fe3O4/SiO2 nanocomposites

A sol-gel procedure was used to cover Fe₃O₄ nanoparticles with SiO₂ shell, forming a core/shell structure. The core/shell nanocomposites were synthesized by a two-step process. First, Fe₃O₄ nanoparticles were obtained through co-precipitation and dispersed in aqueous solution through electrostatic interactions in the presence of tetramethylammonium hydroxide (TMAOH). In the second step, Fe₃O₄ was capped with SiO₂ generated from the hydrolyzation of tetraethyl orthosilicate (TEOS). The structure and properties of the formed Fe₃O₄/SiO₂ nanocomposites were characterized and the results indicate that the Fe₃O₄/SiO₂ nanocomposites are superparamagnetic and are about 30 nm in size. Bioconjugation to IgG was also studied. Finally, the mechanism of depositing SiO₂ on magnetic nanoparticles was discussed.     

双官能Fe3O4/CdSe/CdS荧光磁性复合物的制备和表征

采用化学共沉淀法, 以FeCl₂•4H₂O和FeC1₃•6H₂O为原料制备磁性Fe₃O₄纳米颗粒(MNPs), 采用氨基酸对其进行修饰使其表面连上氨基. 用巯基乙酸作为稳定剂合成了水溶性的CdSe/CdS量子点, 并利用偶联剂1-乙基-3-(3-二氨丙基)碳二亚胺盐酸盐(EDC)和N-羟基琥珀酰亚胺(NHS)连接氨基修饰的Fe₃O₄和带有羧基的CdSe/CdS, 成功制备了Fe₃O₄/CdSe/CdS荧光磁性纳米颗粒. 该荧光磁性纳米复合物保留了CdSe/CdS量子点优异的荧光特性, 平均粒径在40 nm左右; 磁化曲线表明此纳米复合物具有超顺磁性. 这种双官能复合纳米颗粒有望成为新型荧光磁性双标记复合微粒而广泛应用于免疫检测、荧光追踪、磁性分离等领域.     

共同装载吴茱萸碱和Fe3O4纳米粒子的磁性药物载体的制备

以单甲醚-聚乙二醇-聚（丙交酯-乙交酯）（mPEG-PLGA）作为载体,采用溶液透析的方法共同装载抗癌药物吴茱萸碱和Fe₃O₄ 磁性纳米粒子. 通过透射电子显微镜、红外光谱、紫外-可见光谱及体外释放实验、普鲁士蓝染色、体外毒性实验和磁靶向研究,综合评价了磁性纳米药物载体的性能. 结果表明,磁性药物载体胶束分散性良好,粒径均一,有较高的载药量和包封率,能够实现药物缓释,具有磁靶向特性.     

荧光磁性双功能Fe_3O_4/Alendronate@CdSe/CdS纳米复合物的制备与表征

采用化学共沉淀法制备了磁性Fe3O4纳米颗粒,并用四甲基氢氧化铵(TMAOH)、阿伦磷酸钠、丙烯酸丁酯和无水乙二胺对Fe3O4纳米颗粒表面进行修饰,制备出3代表面胺基化的Fe3O4树状分子.采用油相合成的方法制备CdSe/CdS量子点,再用巯基乙酸进行修饰,使其具有良好的水溶性和较好的稳定性.将制备的Fe3O4树状分子与修饰后的量子点进行连接,制备出双功能树状Fe3O4/Alendronate@CdSe/CdS微球.通过这种方法得到的材料的荧光性能明显增强,但材料的荧光性能并不随代数成线性变化的.     

超顺磁Fe_3O_4@PDA核-壳结构纳米粒子的制备及表征

利用多元醇高温热解法和溶液氧化法制备超顺磁四氧化三铁聚多巴胺核-壳结构纳米粒子(Fe_3O_4@PDA)。采用X射线衍射(XRD)、透射电子显微镜(TEM)、动态光散射(DLS)、傅里叶转换红外光谱(FT-IR)和热重分析(TG)等对Fe_3O_4@PDA的结构、形貌和组成进行表征。采用综合物性测试系统(PPMS)对样品的磁性能进行表征。结果表明:Fe_3O_4@PDA的尺寸可以通过氨水与多巴胺的物质的量之比和反应时间进行调控;当Fe_3O_4@PDA中Fe_3O_4的质量分数约为5%时,具有超顺磁性,磁饱和强度为3.8emu/g,比理论值高出36%。     

Fe_3O_4磁性纳米粒子的PEG修饰剂的合成与性能

采用共沉淀法制备了用柠檬酸包覆的Fe3O4磁性纳米粒子,为提高其生物环境适应性和生物应用,利用聚乙二醇二胺(NH2-PEG-NH2)通过碳二亚胺化学法进一步修饰,得到具有良好性能的磁性纳米粒子修饰剂,并分别用场发射扫描电子显微镜(SEM)、洛伦兹透射电子显微镜(TEM)、马尔文激光粒度仪、X-射线粉末衍射仪(XRD)、傅里叶变换红外光谱(FTIR)、综合热分析仪(TG/DTA)、振动样品磁强计(VSM)对磁性纳米粒子的表面形态、化学结构、晶体结构、热稳定性和磁性能进行了表征.在此基础上用合成的磁性纳米粒子修饰剂对盐酸阿霉素(DOX·HCl)进行了修饰,研究了修饰剂的载药和释药行为.结果表明,所制备的修饰剂近乎球形,尺寸相对均匀,粒径在15 nm左右,饱和磁化强度为68 A·m2/kg,在磁靶向药物运输中可以达到良好的磁响应性能.在水中的载药量达到83%,在p H=7.4和p H=5.0下,磁性纳米粒子载药盐酸阿霉素释放均是一个缓慢的过程,具有明显的缓释效果,此外,由于不同p H值下,DOX中的氨基质子化程度存在差异,在较低的p H值下质子化的氨基互相排斥,这更有利于DOX的释放,累计释药率在72 h后分别为65.8%(p H=7.4)与73.6%(p H=5.0).研究表明该磁性纳米粒子具有很好的载药能力及缓释效果.