3 MeV electron irradiation-induced defects in CuInSe2 thin films

3 MeV electron irradiation induced-defects in CuInSe₂ (CIS) thin films have been investigated. Both of the carrier concentration and Hall mobility were decreased as the electron fluence exceeded 1×10¹⁷ cm⁻². The carrier removal rate was estimated to be about 1 cm⁻¹. To evaluate electron irradiation-induced defect, the electrical properties of CIS thin films before and after irradiation were investigated between 80 and 300 K. From the temperature dependence of the carrier concentration in non-irradiated thin films, we obtained N_D=1.8×10¹⁷ cm⁻³, N_A=1.7×10¹⁶ cm⁻³ and E_D=18 meV from the SALS fitting to the experimental data on the basis of the charge balance equation. After irradiation, a new defect level was formed, and N_T0=1.4×10¹⁷ cm⁻³ and E_T=54 meV were also obtained from the same procedure. From the temperature dependence of Hall mobility, the ionized impurity density was discussed before and after the irradiation.     

Influence of Cu doping on the microstructure,optical properties and photoluminescence features of Cd0.9Zn0.1S nanoparticles

Cd_0.9−xZn_0.1Cu_xS (0≤x≤0.06) nanoparticles were successfully synthesized by a conventional chemical co-precipitation method at room temperature. Crystalline phases and optical absorption of the nanoparticles have been studied by X-ray diffraction (XRD) and UV–visible spectrophotometer. XRD confirms the phase singularity of the synthesized material, which also confirmed the formation of Cd–Zn–Cu–S alloy nanocrystals rather than separate nucleation or phase formation. Elemental composition was examined by the energy dispersive X-ray analysis and the microstructure was examined by scanning electron microscope. The blue shift of absorption edge below Cu=2% is responsible for dominance of Cu⁺ while at higher Cu concentration dominated Cu²⁺, d–d transition may exist. It is suggested that the addition of third metal ion (Cu²⁺/Cu⁺) is an effective way to improve the optical property and stability of the Cd_0.9Zn_0.1S solid solutions. When Cu is introduced, stretching of Cd–Zn–Cu–S bond is shifted lower wave number side from 678 cm⁻¹ (Cu=0%) to 671 cm⁻¹ (Cu=6%) due to the presence of Cu in Cd–Zn–S lattice and also the size effect. The variation in blue band emission peak from 456 nm (∼2.72 eV) to 482 nm (∼2.58 eV) by Cu-doping is corresponding to the inter-band radiation combination of photo-generated electrons and holes. Intensity of red band emission centered at 656 nm significantly increased up to Cu=4%; beyond 4% it is decreased due to the quenching of Cu concentration.     

Effect of Li2CO3 addition on the structural,optical, ferroelectric,and electric-field-induced strain of lead-free BNKT-based ceramics

In this work, we reported the effect of Li₂CO₃ addition on the structural, optical, ferroelectric properties and electric-field-induced strain of Bi_0.5(Na,K)_0.5TiO₃ (BNKT) solid solution with CaZrO₃ ceramics. Both rhombohedral and tetragonal structures were distorted after adding Lithium (Li). The band gap values decreased from 2.91 to 2.69 eV for 5 mol% Li-addition. The maximum polarization and remanent polarization decreased from 49.66 μC/cm² to 27.11 μC/cm² and from 22.93 μC/cm² to 5.35 μC/cm² for un-doped and 5 mol% Li- addition BNKT ceramics, respectively. The maximum S_max/E_max value was 567 pm/V at 2 mol% Li₂CO₃ access. We expected this work will help to understand the role of A-site dopant in lead-free ferroelectric BNKT materials.     

Anomalous high salt conductivity in primary diamines as solvents

It is shown that the conductivities of LiBF₄, LiPF₆, LiN(SO₂CF₃)₂ (LiTFSI), NaPF₆, KPF are abnormally high in two diamine solvents: ethylenediamine (EDA) and 1,3-diaminopropane (1,3 DAP). This is particularly evident for KPF₆, κ_MAX(EDA) = 35 mS cm^− 1 and κ_MAX(1,3 DAP) = 17.4 mS cm^− 1. Compared to three other organic solvents having the same viscosity, η ≅ 1.6 cP, but higher relative permittivity, NMF ε = 186.9, NMP ε = 32, γ-Bu ε = 39.1, the maxima of conductibility of EDA and 1,2 DAP, which have a low relative permittivity, ε ≅ 13–11, are largely superior or equal to those of NMF, NMP, γ-Bu. For KPF₆, κ_MAX(NMF) = 15.4mS cm^− 1, κ_MAX(NMP) = 7.8 mS cm^− 1 and κ_MAX(γ-BL) = 10.8 mS cm^− 1. We assume that this is due to a non-Stokesian conductivity mechanism.     

Bulk and surface properties of ionic salt CsH5(PO4)2

We report a comparative study of transport and thermodynamic properties of single-crystal and polycrystalline samples of the ionic salt CsH₅(PO₄)₂ possessing a peculiar three-dimensional hydrogen-bond network. The observed potential of electrolyte decomposition ≈ 1.3 V indicates that the main charge carriers in this salt are protons. However, in spite of the high proton concentration, the conductivity appears to be rather low with a high apparent activation energy E_a ≈ 2 eV, implying that protons are strongly bound. The transport anisotropy though is not large, correlates with the crystal structure: the highest conductivity is found in the [001] direction (σ_130 °C ∼ 5.6 × 10^− 6 S cm^− 1) while the minimal conductivity is in the [100] direction (σ_130 °C ∼ 10 ⁻⁶ S cm^− 1). The conductivity of polycrystalline samples appears to exceed the bulk one by 1–3 orders of magnitude with a concomitant decrease of the activation energy (E_a ≈ 1.05 eV), which indicates that a pseudo-liquid layer with a high proton mobility is formed at the surface of grains. Infrared and Raman spectroscopy used to study the dynamics of the hydrogen-bond system in single-crystal and polycrystalline samples have confirmed the formation of such a modified surface layer in the latter. However, no bulk phase transition into the superionic disordered phase is observed in CsH₅(PO₄)₂ up to the melting point T_melt ∼ 151.6 °C, in contrast to its closest relative compound CsH₂PO₄.     

Ionic and electronic conductivities,stability and thermal expansion of La10 − x(Si,Al)6O26 ± δ solid electrolytes

Apatite-type La_10 − xSi_6 − yAl_yO_{27 − 3x/2 − y/2} (x = 0–0.33; y = 0.5–1.5) exhibit predominant oxygen ionic conductivity in a wide range of oxygen partial pressures. The conductivity of silicates containing 26.50–26.75 oxygen atoms per formula unit is comparable to that of gadolinia-doped ceria at 770–870 K. The average thermal expansion coefficients are (8.7–10.8) × 10^− 6 K^− 1 at 373–1273 K. At temperatures above 1100 K, silicon oxide volatilization from the surface layers of apatite ceramics and a moderate degradation of the ionic transport with time are observed under reducing conditions, thus limiting the operation temperature of Si-containing solid electrolytes.     

High room-temperature pyroelectric response of MgO-modified Pb0.99(Zr0.95Ti0.05)0.98Nb0.02O3 ceramics

The dielectric and pyroelectric responses of MgO-modified Pb_0.99(Zr_0.95Ti_0.05)_0.98Nb_0.02O₃ ceramics were investigated near F_R(LT)–F_R(HT) phase transition. It was found that MgO additive reduced the F_R(LT)–F_R(HT) phase transition temperature from 41 °C to room temperature (24 °C). Superior room-temperature pyroelectric properties were obtained in the composition of 0.10 wt% MgO addition without DC bias. The largest pyroelectric coefficient, 65 × 10⁻⁸ C cm⁻² K⁻¹, was detected. Accordingly, the detectivity figures of merit F_d had maximum values of 20 × 10⁻⁵ Pa^−1/2, and especially the voltage responsivity F_v = 0.91 m²C⁻¹ is the highest value reported so far among all pyroelectric materials. It shows promising potential for application in uncooled pyroelectric infrared detector.     

Synthesis of ammonia at atmospheric pressure with Ce0.8M0.2O2−δ (M = La,Y, Gd,Sm) and their proton conduction at intermediate temperature

Ionic conduction in fluorite-type structure oxide ceramics Ce_0.8M_0.2O_2−δ (M = La, Y, Gd, Sm) at temperature 400–800 °C was systematically studied under wet hydrogen/dry nitrogen atmosphere. On the sintered complex oxides as solid electrolyte, ammonia was synthesized from nitrogen and hydrogen at atmospheric pressure in the solid states proton conducting cell reactor by electrochemical methods, which directly evidenced the protonic conduction in those oxides at intermediate temperature. The rate of evolution of ammonia in Ce_0.8M_0.2O_2−δ (M = La, Y, Gd, Sm) is up to 7.2 × 10^− 9, 7.5 × 10^− 9, 7.7 × 10^− 9, 8.2 × 10^− 9 mol s^− 1 cm^− 2, respectively.     

Oxygen diffusion and surface exchange studies on (La0.75Sr0.25)0.95Cr0.5Mn0.5O3−δ

Oxygen tracer diffusion coefficient (D^⁎) and surface exchange coefficient (k^⁎) have been measured for (La_0.75Sr_0.25)_0.95Cr_0.5Mn_0.5O_3−δ using isotopic exchange and depth profiling by secondary ion mass spectrometry technique as a function of temperature (700–1000 °C) in dry oxygen and in a water vapour-forming gas mixture. The typical values of D^⁎ under oxidising and reducing conditions at ∼ 1000 °C are 4 × 10^− 10 cm² s^− 1 and 3 × 10^− 8 cm² s^− 1 respectively, whereas the values of k^⁎ under oxidising and reducing conditions at ∼ 1000 °C are 5 × 10^− 8 cm s^− 1 and 4 × 10^− 8 cm s^− 1 respectively. The apparent activation energies for D^⁎ in oxidising and reducing conditions are 0.8 eV and 1.9 eV respectively.     

Spectroscopic properties of Co2+: ZnAl2O4 nanocrystals in sol–gel derived glass–ceramics

Transparent glass–ceramics containing zinc–aluminum spinel (ZnAl₂O₄) nanocrystals doped with tetrahedrally coordinated Co²⁺ ions were obtained by the sol–gel method for the first time. The gels of composition SiO₂–Al₂O₃–ZnO–CoO were prepared at room temperature and heat-treated at temperature ranging 800–950 °C. When the gel samples were heated up to 900 °C, ZnAl₂O₄ nanocrystals were precipitated. Co²⁺ ions were located in tetrahedral sites in ZnAl₂O₄ nanocrystals. X-ray diffraction analysis shows that the crystallite sizes of ZnAl₂O₄ crystal become large with the heat-treatment temperature and time, and the crystallite diameter is in the range of 10–15 nm. The dependence of the absorption and emission spectra of the samples on heat-treatment temperature were presented. The difference in the luminescence between Co²⁺ doped glass–ceramic and Co²⁺ doped bulk crystal was analysed. The crystal field parameter D_q of 423 cm⁻¹ and the Racah parameters B of 773 cm⁻¹ and C of 3478.5 cm⁻¹ were calculated for tetrahedral Co²⁺ ions.     

Transport and phase dynamics of poly(vinyl pyrrolidone) doped plastically crystalline N-methyl-N-propylpyrrolidinium tetrafluoroborate

The plastic crystal phase forming N-methyl-N-propylpyrrolidinium tetrafluoroborate organic salt (P₁₃BF₄) was combined with 2, 5 and 10 wt.% poly(vinyl pyrrolidone) (PVP). The ternary 2 wt.% PVP/2 wt.% LiBF₄/P₁₃BF₄ was also investigated. Thermal analysis, conductivity, optical thermomicroscopy, and Nuclear Magnetic Resonance (¹¹B, ¹⁹F, ¹H, ⁷Li) were used to probe the fundamental transport processes. Both the onset of phase I and the final melting temperature were reduced with increasing additions of PVP. Conductivity in phase I was 2.6 × 10^− 4 S cm^− 1 5.2 × 10^− 4 S cm^− 1 1.1 × 10^− 4 S cm^− 1 and 3.9 × 10^− 5 S cm^− 1 for 0, 2, 5 and 10 wt.%PVP/P₁₃BF₄, respectively. Doping with 2 wt.% LiBF₄ increased the conductivity by up to an order of magnitude in phase II. Further additions of 2 wt.% PVP slightly reduced the conductivity, although it remained higher than for pure P₁₃BF₄.     

Dielectric and piezoelectric properties of (Bi1−x−yNdxNa1−y)0.5BayTiO3 lead-free ceramics

New lead-free (Bi_1−x−yNd_xNa_1−y)_0.5Ba_yTiO₃ ceramics were prepared by a conventional ceramic technique and their dielectric and piezoelectric properties were studied. X-ray diffraction studies reveal that Nd³⁺ and Ba²⁺ diffuse into the Bi_0.5Na_0.5TiO₃ lattices to form a new solid solution with a pure perovskite structure, and a morphotropic phase boundary (MPB) of rhombohedral and tetragonal phases is formed at 0.04 < y < 0.10. The partial substitutions of Nd³⁺ and Ba²⁺ decrease effectively the coercive field E_c and increase significantly the remanent polarization P_r. Because of lower E_c, larger P_r and the formation of the MPB, the piezoelectric properties of the ceramics are significantly enhanced at x/y = 0.02/0.06: d₃₃ = 150 pC/N and k_p = 30.5%. The ceramics exhibit relaxor characteristic, which is probably resulted from the cation disordering in the 12-fold coordination sites. The depolarization temperature T_d shows a strong compositional dependence and reaches a minimum value at the MPB. The temperature dependences of the ferroelectric and dielectric properties suggest that the ceramics may contain both the polar and non-polar regions near the depolarization temperature T_d, which cause the polarization hysteresis loop become deformed near/above T_d.     

Kinetic studies of electronically conducting Yb3Al5O12 garnet

Upon reduction, originally fully transparent and insulating ytterbium alumina garnet single crystals, Yb₃Al₅O₁₂, become deeply colored and electrically conducting with a conductivity of the order of 10^− 3 Ω^− 1 cm^− 1 in the temperature range of 550 °C to 1000 °C. The redox kinetics of the material is studied by means of conductivity relaxation experiments performed at oxidising and reducing conditions. Good agreement is obtained with an optical study into the redox kinetics of Yb₃Al₅O₁₂.     

Thermal cis–trans isomerization of triazo-benzene

1,3,5-Hydroxy-triazo-benzene (H-TAB) was synthesized through a coupling-oxidation protocol. Temperature-controlled UV, IR, and ab initio calculation were carried out to investigate the cis–trans thermal isomerization of H-TAB. In temperature-controlled UV experiments, λ_max of the π–π¹ band and for the trans conformation at 335 nm and that for the cis form at 282 nm are shifted by increased temperature; band intensities of the π–π¹ transition decrease and λ_max of the π–π¹ band is shifted toward the high-energy region. The maximum peak at 2922 cm⁻¹ is shifted to 2926 cm⁻¹, and that at 2852 cm⁻¹ is shifted to 2856 cm⁻¹ at increased temperature in the temperature-controlled IR experiment. Ab initio calculation reveals that the cis conformation of H-TAB is more stable than the trans form because the cis form has less spatial repulsion. Therefore, the ground-state energy difference induced by steric repulsion of the benzene unit is the driving force of the blue shift in the thermal IR and UV spectra for the triazo-benzene.     

Synthesis and electrochemical properties of Li2S–B2S3–Li4SiO4

New Li⁺ ion-conductive glasses Li₂S–B₂S₃–Li₄SiO₄ were synthesized by rapid quenching, and they were transformed into glass ceramics by heat treatment. The heat treatment increased the ionic conductivities of the Li₄SiO₄-doped glasses, and the highest ionic conductivity observed in the system was 1.0 × 10^− 3 S cm^− 1 at room temperature. The glass ceramics were highly stable against electrochemical oxidation with a wide electrochemical window of 10 V.     

Oxygen nonstoichiometry and transport properties of strontium substituted lanthanum cobaltite

Oxygen nonstoichiometry, structure and transport properties of the two compositions (La_0.6Sr_0.4)_0.99CoO_3−δ (LSC40) and La_0.85Sr_0.15CoO_3−δ (LSC15) were measured. It was found that the oxygen nonstoichiometry as a function of the temperature and oxygen partial pressure could be described using the itinerant electron model. The electrical conductivity, σ, of the materials is high (σ > 500 S cm^− 1) in the measured temperature range (650–1000 °C) and oxygen partial pressure range (0.209–10^− 4 atm). At 900 °C the electrical conductivity is 1365 and 1491 S cm^− 1 in air for LSC40 and LSC15, respectively. A linear correlation between the electrical conductivity and the oxygen vacancy concentration was found for both samples. The mobility of the electron-holes was inversely proportional with the absolute temperature indicating a metallic type conductivity for LSC40. Using electrical conductivity relaxation the chemical diffusion coefficient of oxygen was determined. It was found that accurate values of the chemical diffusion coefficient could only be obtained using a sample with a porous surface coating. The porous surface coating increased the surface exchange reaction thereby unmasking the chemical diffusion coefficient. The ionic conductivity deduced from electrical conductivity relaxation was determined to be 0.45 S cm^− 1 and 0.01 S cm^− 1 at 1000 and 650 °C, respectively. The activation energy for the ionic conductivity at a constant vacancy concentration (δ = 0.125) was found to be 0.90 eV.     

Synthesis and characterization of (Pr0.75Sr0.25)1 − xCr0.5Mn0.5O3 − δ as anode for SOFCs

The complex perovskite (Pr_0.75Sr_0.25)_1 − xCr_0.5Mn_0.5O_3 − δ (PSCM) has been prepared and studied as possible anode material for high-temperature solid oxide fuel cells (SOFCs). PSCM exhibits GdFeO₃-type structure and is both physically and chemically compatible with the conventional YSZ electrolyte. The reduction of PSCM resulted in structural change from orthorhombic Pbnm to cubic Pm-3m. Selected area electron diffraction (SAED) analysis on the reduced phases indicated the presence of a √2 × √2 × 2 superlattice. The total conductivity values of ∼ 75% dense Pr_0.75Sr_0.25Cr_0.5Mn_0.5O_3 − δ at 900 °C in air and 5% H₂/Ar are 9.6 and 0.14 S cm^− 1 respectively. The conductivity of PSCM drops with decreasing Po₂ and is a p-type conductor at all studied Po₂. The average TEC of Pr_0.75Sr_0.25Cr_0.5Mn_0.5O_3 − δ is 9.3 × 10^− 6 K^− 1, in the temperature range of 100–900 °C and is close to that of YSZ electrolyte. The anode polarization resistance of PSCM in wet 5%H₂ is 1.31 Ω cm² at 910 °C and in wet CH₄ at 930 °C; the polarization resistance is 1.29 Ω cm². PSCM was unstable at 900 °C in unhumidified hydrogen. Cell performance measurements carried out using graded PSCM and La_0.8Sr_0.2MnO₃ as anode and cathode respectively yielded a maximum power density of 0.18 W cm^− 2 in wet 5%H₂/Ar at 910 °C and the corresponding current density was 0.44 A cm^− 2 at 0.4 V. The activation energy for the electrochemical cell operating in wet (3% H₂O) 5%H₂/Ar fuel is 85 kJ mol^− 1.     

Low-temperature preparation and properties of ceramics with composition (1−x)CaTiO3−xPbF2−xLiF

Fluorinated ceramics with initial composition (1−x)CaTiO₃+xPbF₂+xLiF were sintered at 950 °C. The X-ray diffraction (XRD) patterns of the samples showed the formation of a novel solid solution in the initial composition range 0⩽x⩽0.125. SEM observations were performed on fractured ceramics and DSC analyses were carried out from room temperature up to 600 °C. Three second-order phase transitions were detected for all the samples. Capacitors were prepared from the pre-sintered ceramics then dielectric measurements were performed as a function of temperature in the frequency range 10²–4×10⁷ Hz. The ε′_r−T curves exhibit the profile of dielectrics for class I capacitors, however the values of tan δ are too high (tan δ⩾1%).     

Synthesis and electrical properties of nanocrystalline Ca1 − xEuxMnO3 ± δ (0.1 ≤ x ≤ 0.4) powders prepared at low temperature using citrate gel method

Nanopowders of Ca_1 − xEu_xMnO₃ (0.1 ≤ x ≤ 0.4) manganites were synthesized as a single phase using the auto gel-combustion method. The citrate method shows to be simple and appropriate to obtain single phases avoiding segregation or contamination. The Ca_1 − xEu_xMnO₃ system has been synthesized at 800 °C during 18 h, against the conventional method of mixing oxides used to obtain these materials at higher temperatures of synthesis. The formation reaction was monitored by X-ray diffraction (XRD) analysis and an infrared absorption technique (FTIR). The polycrystalline powders are characterised by nanometric particle size, ∼ 48 nm as determined from X-ray line broadening analysis using the Scherrer equation. Morphological analysis of the powders, using the scanning electron microscope (SEM), revealed that all phases are homogeneous and the europium-substituted samples exhibit a significant decrease in the grain size when compared with the undoped samples. The structure refinement by using the Rietveld method indicates that the partial calcium substitution by europium (for x ≥ 0.3) modifies the orthorhombic structure of the CaMnO₃ perovskite towards a monoclinic phase. All manganites show two active IR vibrational modes around 400 and 600 cm^− 1. The high temperature dependence of electrical resistivity (between 25 and 600 °C) allows us to conclude that all the samples exhibit a semiconductor behaviour and the europium causes a decrease in the electrical resistivity by more than one order of magnitude. The results can be well attributed to the Mn⁴⁺/Mn³⁺ ratio.     

M/Li+(M = Mg2+, Zn2+, and Mn2+) ion-exchange on lithium ion-conducting perovskite-type oxides and their properties

Lithium ions of perovskite-type lithium ion conductor La_0.55Li_0.35TiO₃ were replaced by divalent Mg²⁺, Zn²⁺, and Mn²⁺ ions in an ion-exchange reaction using molten chlorides. The polycrystalline Mg-exchanged and Zn-exchanged samples are solid electrolytes for divalent Mg²⁺ and Zn²⁺ ions, whose dc ionic conductivities (σ = 2.0 × 10^− 6 S cm^− 1 at 558 K for the Mg-exchanged sample, La_0.56(2)Li_0.02(1)Mg_0.16(1)TiO_3.01(2) and σ = 1.7 × 10^− 6 S cm^− 1 at 708 K for the Zn-exchanged samples, La_0.55(1)Li_0.0037(2)Zn_0.15(1)TiO_2.98(2)) were compared to those of the known highest Mg²⁺ and Zn²⁺ inorganic solid electrolytes. The Mn-exchanged sample, then, showed paramagnetic behavior in the temperature range of 2 to 300 K. The Mn ions in the exchanged sample are divalent and the spin configuration is in high spin state (S = 5/2).