基于FTO/VO2/FTO结构的VO2薄膜电压诱导相变光调制特性

采用直流磁控溅射和后退火工艺在掺氟的SnO₂(FTO)导电玻璃衬底上制备VO₂薄膜, 研究了不同退火时间和不同比例的氮氧气氛对VO₂薄膜性能的影响, 对VO₂薄膜的结晶取向、表面形貌、表面元素的相对含量和透过率随波长变化进行了测试分析, 结果表明在最佳工艺条件下制备得到了组分相对单一的VO₂薄膜. 基于FTO/VO₂/FTO结构在VO₂薄膜两侧的透明导电膜上施加电压并达到阈值电压时, 观察到了明显的电流突变. 当接触面积为3 mm×3 mm时, 阈值电压为1.7 V, 阈值电压随接触面积的增大而增大. 与不加电压的情况相比, FTO/VO₂/FTO结构在电压作用下高低温的红外透过率差值可达28%, 经反复施加电压, 该结构仍保持性能稳定, 具有较强的电致调控能力.     

O2流量对磁控溅射N掺杂TiO2薄膜成分及晶体结构的影响

利用直流脉冲磁控溅射方法在室温下通过改变O₂流量制备具有不同晶体结构的N掺杂TiO₂薄膜,利用台阶仪、X射线光电子能谱仪、X射线衍射仪、紫外-可见分光光度计等设备对薄膜沉积速率、化学成分、晶体结构、禁带宽度等进行分析.结果表明:所制备的薄膜元素配比约为TiO_1.68±0.06N_0.11±0.01,N为替位掺杂,所有样品退火前后均未形成Ti—N相结构,N掺杂TiO₂薄膜的沉积速率、晶体结构等主要依赖于O₂流量.在O₂流量为2 sccm时,N掺杂TiO₂薄膜沉积速率相对较高,薄膜为非晶态结构,但薄膜内含有锐钛矿(anatase)和金红石(rutile)相晶核,退火后薄膜呈anatase和rutile相混合结构,禁带宽度仅为2.86 eV.随着O₂流量的增加,薄膜沉积速率单调下降,退火后样品禁带宽度逐渐增加.当O₂流量为12 sccm时,薄膜为anatase相择优生长,退火后呈anatase相结构,禁带宽度为3.2 eV.综合本实验的分析结果,要在室温条件下制备晶态N掺杂TiO₂薄膜,需在高O₂流量(＞10 sccn)条件下制备. 关键词： 2薄膜')" href="#">N掺杂TiO₂薄膜 磁控溅射 化学配比 晶体结构     

Ga-Ti共掺杂ZnO薄膜的制备及其光电性能

采用ZnO:Ga2O3:TiO2为靶材,在玻璃衬底上射频磁控溅射制备了多晶Ga-Ti共掺杂ZnO(GTZO)薄膜,通过XRD、四探针、透射光谱测试研究了生长温度对薄膜结构和光电性能的影响.结果表明:所制备的薄膜具有c轴择优取向,光学带隙均大于本征ZnO的禁带宽度.当生长温度为620K时GTZO薄膜的结晶质量最佳、电阻率最低、透射率最大、品质因数最高.     

离子注入掺杂锐钛矿TiO2薄膜的光学性能

在玻璃基体上,采用射频磁控溅射方法在不同的基体温度下制备了TiO2薄膜,然后在薄膜中注入注量分别为5×1016, 1×1017和5×1017/cm2的N离子以制备N掺杂的TiO2薄膜。X射线衍射结果表明：制备出的TiO2薄膜为锐钛矿型。X射线光电子能谱研究结果表明：注入的N离子与TiO2晶粒相互作用,形成了含氮的TiOxN2-x化合物,从而改变了TiO2薄膜的吸收边;随N离子注量增加,吸收边移动更明显;同时,由于氮离子注入产生的辐照缺陷使TiO2薄膜在紫外和可见光区的吸收也明显增强。     

MBE法制备VO2薄膜及其中红外调制深度测量

为了给VO₂薄膜在定向红外对抗系统防护方面的应用提供理论依据,我们用透过率调制深度表征VO₂薄膜在中红外波段的相变特性。本实验利用分子束外延法（MBE）制备VO₂外延单晶薄膜,经XRD、AFM表征,发现其具有（020）择优取向、纯度较高,薄膜表面平整、均匀且致密。经VU-Vis-IR测量发现其近红外透过率相变特性显著,但在紫外和可见光范围内透过率相变特性较不明显。然后我们对制备时间为30 min、40 min的两组薄膜分别进行25~70℃的升温和降温实验,观察其对波长为3 459 nm、脉宽50 ns、重频50 kHz、功率密度0.14 W/cm²的中红外激光的透过率变化,并比较两组薄膜的温滞曲线特性。实验发现它们对中红外透过率的调制深度均可达60%以上,前者比后者对中红外的调制深度高出约4%。这说明利用分子束外延法制备的VO₂单晶薄膜具有良好的中红外调制特性,且调制深度和膜厚有关。进一步表明了利用VO₂薄膜实现中红外激光防护具有一定的可行性。     

衬底温度对反应磁控溅射W掺杂ZnO薄膜的微观结构及光电性能的影响

采用直流脉冲反应磁控溅射方法生长W掺杂ZnO（WZO）透明导电氧化物薄膜并研究了衬底温度对薄膜微观结构、组分、表面形貌以及光电性能的影响.实验结果表明,WZO薄膜具有良好的（002）晶面择优取向,且适当的衬底温度是制备优质WZO薄膜的关键因素.随着衬底温度升高,薄膜表面粗糙度先增大后减小;衬底温度较高时,薄膜的结构致密,结晶质量好,电子迁移率高.当衬底温度为325℃时,WZO薄膜获得最低电阻率9.25×10^-3Ω·cm,方块电阻为56.24Ω/□,迁移率为11.8 cm² V^-1·s^-1,其在可见光及近红外区域（400—1500 nm）范围的平均透过率达到85.7%.     

花状掺杂W-VO$lt;sub$gt;2$lt;/sub$gt;/ZnO热致变色纳米复合薄膜研究

为解决掺杂引起的二氧化钒薄膜的红外调制幅度下降以及二氧化钒复合薄膜相变温度需要进一步降低等问题, 采用纳米结构、掺杂改性和复合结构等多种机理协同作用的方案, 利用共溅射氧化法, 先在石英玻璃上制备高(002)取向的ZnO薄膜, 再在ZnO层上室温共溅射沉积钒钨金属薄膜, 最后经热氧化处理获得双层钨掺杂W-VO₂/ZnO纳米复合薄膜. 利用X射线衍射、X射线光电子能谱、扫描电镜和变温光谱分析等对薄膜的结构、组分、形貌和光学特性进行了分析. 结果显示, W-VO₂/ZnO 纳米复合薄膜呈花状结构, 取向性提高, 在保持掺杂薄膜相变温度(约39 ℃)和热滞回线宽度(约6 ℃)较低的情况下, 其相变前后的红外透过率差量增加近2倍, 热致变色性能得到协同增强. 关键词： 2')" href="#">VO₂ ZnO W掺杂 热致变色     

纳米VO2/ZnO复合薄膜的热致变色特性研究

为提高VO₂薄膜的热致变色性能,采用纳米结构和复合结构二者相结合的方法,通过磁控溅射技术先在玻璃衬底上制备高(002)取向ZnO薄膜,再在ZnO层上室温沉积钒金属薄膜,最后经热氧化处理获得纳米结构VO₂/ZnO复合薄膜.利用变温拉曼光谱观察分析了VO₂/ZnO薄膜相变前后的晶格畸变和键态的演变过程,讨论了薄膜的结构与热致红外开关特性和相变温度的内在关系.结果显示,与相同条件获得的同厚度的单层VO₂薄膜相比,纳米VO关键词： ZnO 2')" href="#">VO₂ 纳米复合薄膜 热致变色 拉曼光谱     

溶胶-凝胶VO2薄膜转换特性研究

利用溶胶凝胶法在SiO2Si衬底上沉积高取向的V2O5薄膜,在压强低于2Pa,温度高于400℃的条件下,对V2O5薄膜进行真空烘烤,获得了电阻率变化3个数量级以上、弛豫宽度为62℃的VO2多晶薄膜.以X射线衍射(XRD)、扫描电子显微镜(SEM)图和电阻率转换特性等实验结果为依据,详细分析了溶胶凝胶薄膜在真空烘烤时从V2O5向VO2的转化,它经历了从VnO2n+1(n=2,3,4,6)到VO2的过程.实验证明,根据选择合适的成膜热处理条件和真空烘烤条件是实现溶胶凝胶V2O5结构向VO2结构成功转换的关键 关键词： 溶胶-凝胶法 氧化钒薄膜 VO2膜转换特性     

CdTe太阳电池前电极SnO2:F/SnO2复合薄膜性能分析

减薄CdS窗口层是提高CdS/CdTe太阳电池转换效率的有效途径之一,减薄窗口层会对器件造成不利的影响,因此在减薄了的窗口层与前电极之间引入过渡层非常必要.利用反应磁控溅射法在前电极SnO₂:F薄膜衬底上制备未掺杂的SnO₂薄膜形成过渡层,并将其在N₂/O₂=4 ∶1,550 ℃环境进行了30 min热处理,利用原子力显微镜、X射线衍射仪、紫外分光光度计对复合薄膜热处理前后的形貌、结构、光学性能进行了表征,同时分析了复     

Study of nanocrystalline VO2 thin films prepared by magnetron sputtering and post-oxidation

Nanocrystalline VO2 thin films were deposited onto glass slides by direct current magnetron sputtering and postoxidation. These films undergo semiconductor-metal transition at 70°C, accompanied by a resistance drop of two magnitude orders. The crystal structures and surface morphologies of the VO2 films were characterized by x-ray diffraction (XRD) and atomic force microscope (AFM), respectively. Results reveal that the average grain size of VO2 nanograins measured by XRD is smaller than those measured by AFM. In addition, Raman characterization indicates that stoichiometric VO2 and oxygen-rich VO2 phases coexist in the films, which is supported by x-ray photoelectron spectroscopy (XPS) results. Finally, the optical properties of the VO2 films in UV-visible range were also evaluated. The optical band gap corresponding to 2p-3d inter-band transition was deduced according to the transmission and reflection spectra. And the deduced value, E opt2p-3d = 1.81 eV, is in good agreement with that previously obtained by theoretical calculation.     

Fabrication and characterization of Mn-doped Cu2O thin films grown by RF magnetron sputtering

Two series of Mn-doped Cu₂O diluted-magnetic-semiconductor thin films were prepared by radio-frequency (RF) magnetron sputtering. One is prepared at different deposition temperature with the same Mn doping concentration; the other is deposited at the same temperature but with varying Mn concentration. They were used to find out the ferromagnetic-order zone for the Mn-doped Cu₂O systems. Most of the samples show high (1 1 1) orientation, except low doping concentration (<6 at%). No impurities were found by X-ray diffraction and electron diffraction measurement. The doped Mn ions substituted Cu ions in the Cu₂O lattice and there were about 1.5% cation vacancies. The grains shown in the transmission electron microscopy (TEM) images for all the samples were tiny, i.e. just 5 nm in diameter. A rough phase diagram for the ferromagnetic order existing in the Mn-doped Cu₂O thin films was given with varying Mn doping concentration and deposition temperature.     

The structure and photocatalytic activity of TiO2 thin films deposited by dc magnetron sputtering

This paper seeks to determine the optimal settings for the deposition parameters, for TiO₂ thin film, prepared on non-alkali glass substrates, by direct current (dc) sputtering, using a ceramic TiO₂ target in an argon gas environment. An orthogonal array, the signal-to-noise ratio and analysis of variance are used to analyze the effect of the deposition parameters. Using the Taguchi method for design of a robust experiment, the interactions between factors are also investigated. The main deposition parameters, such as dc power (W), sputtering pressure (Pa), substrate temperature (°C) and deposition time (min), were optimized, with reference to the structure and photocatalytic characteristics of TiO₂. The results of this study show that substrate temperature and deposition time have the most significant effect on photocatalytic performance. For the optimal combination of deposition parameters, the (1 1 0) and (2 0 0) peaks of the rutile structure and the (2 0 0) peak of the anatase structure were observed, at 2θ ∼ 27.4°, 39.2° and 48°, respectively. The experimental results illustrate that the Taguchi method allowed a suitable solution to the problem, with the minimum number of trials, compared to a full factorial design. The adhesion of the coatings was also measured and evaluated, via a scratch test. Superior wear behavior was observed, for the TiO₂ film, because of the increased strength of the interface of micro-blasted tools.     

Thermochromic VO2 thin films synthesized by rf-inverted cylindrical magnetron sputtering

The novel physical vapor deposition called inverted cylindrical magnetron sputtering (also known as hollow cathode sputtering) is commonly used to coat wires, fibers, ribbons as well as all sides of three-dimensional substrates. It is a reproducible method for the production of nano-structured systems onto complex shapes substrates. This paper reports the first synthesis and feasibility of reliably reproduced stoichiometric pure textured VO₂ nano-structures by the rf-inverted cylindrical magnetron sputtering. Morphological, structural, elemental analysis and optical properties of synthesized VO₂ under optimized conditions are reported.     

AlNxOy thin films deposited by DC reactive magnetron sputtering

AlN_xO_y thin films were produced by DC reactive magnetron sputtering, using an atmosphere of argon and a reactive gas mixture of nitrogen and oxygen, for a wide range of partial pressures of reactive gas. During the deposition, the discharge current was kept constant and the discharge parameters were monitored. The deposition rate, chemical composition, morphology, structure and electrical resistivity of the coatings are strongly correlated with discharge parameters. Varying the reactive gas mixture partial pressure, the film properties change gradually from metallic-like films, for low reactive gas partial pressures, to stoichiometric amorphous Al₂O₃ insulator films, at high pressures. For intermediate reactive gas pressures, sub-stoichiometric AlN_xO_y films were obtained, with the electrical resistivity of the films increasing with the non-metallic/metallic ratio.     

直流磁控溅射Cr-Cr2O3复合金属陶瓷薄膜光学特性研究

采用直流反应磁控溅射技术在不同靶电流条件下制备了Cr-Cr₂O₃金属陶瓷薄膜,并利用椭偏仪测量了薄膜的光学常数。采用修正的 M-G (Maxwell-Gannett)理论对不同靶电流条件下沉积的Cr-Cr₂O₃金属陶瓷薄膜的光学常数进行了理论计算,并将理论计算结果与实验数据进行了比较。结果表明：随着靶电流的增加,膜层中金属微粒体积百分比增加,金属微粒的平均半径随之增加,且金属微粒逐渐趋于扁圆形,理论计算结果与实验结果吻合较好。     

Optical properties of p-type CuAlO2 thin film grown by rf magnetron sputtering

We report the structural and optical properties of copper aluminium oxide (CuAlO₂) thin films, which were prepared on c-plane sapphire substrates by the radio frequency magnetron sputtering method. X-ray photoelectron spectroscopy (XPS) along with X-ray diffraction (XRD) analysis confirms that the films consist of delafossite CuAlO₂ phase only. The optical absorption studies show the indirect and direct bandgap is 1.8 eV and 3.45 eV, respectively. Room temperature photoluminescence (PL) measurements show three emission peaks at 360 nm (3.45 eV), 470 nm (2.63 eV) and 590 nm (2.1 eV). The first one is near band edge emission while the other two are originated from defects.