Structure and thermal stability of MOCVD ZrO2 films on Si (1 0 0)

The structure and thermal stability of ZrO₂ films grown on Si (1 0 0) substrates by metalorganic chemical vapor deposition have been studied by high-resolution transmission electron microscopy, selected area electron diffraction and X-ray energy dispersive spectroscopy. As-deposited films consist of tetragonal ZrO₂ nanocrystallites and an amorphous Zr silicate interfacial layer. After annealing at 850°C, some monoclinic phase is formed, and the grain size is increased. Annealing a 6 nm thick film at 850°C in O₂ revealed that the growth of the interfacial layer is at the expense of the ZrO₂ layer. In a 3.0 nm thick Zr silicate interfacial layer, there is a 0.9 nm Zr-free SiO₂ region right above the Si substrate. These observations suggest that oxygen reacted with the Si substrate to grow SiO₂, and SiO₂ reacted with ZrO₂ to form a Zr silicate interfacial layer during the deposition and annealing. Oxygen diffusion through the tetragonal ZrO₂ phase was found to be relatively easier than through the monoclinic phase.     

Correlation between interfacial structure and c-axis-orientation of LiNbO3 films grown on Si and SiO2 by electron cyclotron resonance plasma sputtering

Thin films of crystalline lithium niobate (LN) grown on Si(1 0 0) and SiO₂ substrates by electron cyclotron resonance plasma sputtering exhibit distinct interfacial structures that strongly affect the orientation of respective films. Growth at 460–600 °C on the Si(1 0 0) surface produced columnar domains of LiNbO₃ with well-oriented c-axes, i.e., normal to the surface. When the SiO₂ substrate was similarly exposed to plasma at temperatures above 500 °C, however, increased diffusion of Li and Nb atoms into the SiO₂ film was seen and this led to an LN–SiO₂ alloy interface in which crystal-axis orientations were randomized. This problem was solved by solid-phase crystallization of the deposited film of amorphous LN; the degree of c-axis orientation was then immune to the choice of substrate material.     

Epitaxial growth of ZnO thin films on Si substrates by PLD technique

Epitaxial ZnO thin films have been grown on Si(1 1 1) substrates at temperatures between 550 and 700 °C with an oxygen pressure of 60 Pa by pulsed laser deposition (PLD). A ZnO thin film deposited at 500 °C in no-oxygen ambient was used as a buffer layer for the ZnO growth. In situ reflection high-energy electron diffraction (RHEED) observations show that ZnO thin films directly deposited on Si are of a polycrystalline structure, and the crystallinity is deteriorated with an increase of substrate temperature as reflected by the evolution of RHEED patterns from the mixture of spots and rings to single rings. In contrast, the ZnO films grown on a homo-buffer layer exhibit aligned spotty patterns indicating an epitaxial growth. Among the ZnO thin films with a buffer layer, the film grown at 650 °C shows the best structural quality and the strongest ultraviolet (UV) emission with a full-width at half-maximum (FWHM) of 86 meV. It is found that the ZnO film with a buffer layer has better crystallinity than the film without the buffer layer at the same substrate temperature, while the film without the buffer layer shows a more intense UV emission. Possible reasons and preventive methods are suggested to obtain highly optical quality films.     

Effects of growth temperature on the properties of ZnO/GaAs prepared by metalorganic chemical vapor deposition

A series of ZnO films were grown on GaAs(0 0 1) substrates at different growth temperatures in the range 250–720°C by metalorganic chemical vapor depostion. Field emission scanning electron microscopy was utilized to investigate the surface morphology of ZnO films. The crystallinity of ZnO films was investigated by the double-crystal X-ray diffractometry. The optical and electrical properties of ZnO films were also investigated using room-temperature photoluminescence and Hall measurements. Arrhenius plots of the growth rate versus reciprocal temperature revealed the kinetically limited growth behavior depending on the growth temperature. It was found that the surface morphology, structural, optical and electrical properties of the films were improved with increasing growth temperature to 650°C. All the properties of the film grown at 720°C were degraded due to the decomposition of ZnO film.     

CrO2 (1 0 0) and TiO2 (1 0 0) film heteroepitaxy on a BaF2 (1 1 1)/Si (1 0 0) substrate

Multi-domained heteroepitaxial rutile-phase TiO₂ (1 0 0)-oriented films were grown on Si (1 0 0) substrates by using a 30-nm-thick BaF₂ (1 1 1) buffer layer at the TiO₂–Si interface. The 50 nm TiO₂ films were grown by electron cyclotron resonance oxygen plasma-assisted electron beam evaporation of a titanium source, and the growth temperature was varied from 300 to 600 °C. At an optimal temperature of 500 °C, X-ray diffraction measurements show that rutile phase TiO₂ films are produced. Pole figure analysis indicates that the TiO₂ layer follows the symmetry of the BaF₂ surface mesh, and consists of six (1 0 0)-oriented domains separated by 30° in-plane rotations about the TiO₂ [1 0 0] axis. The in-plane alignment between the TiO₂ and BaF₂ films is oriented as [0 0 1] TiO₂ || BaF₂ or [0 0 1] TiO₂ || BaF₂ . Rocking curve and STM analyses suggest that the TiO₂ films are more finely grained than the BaF₂ film. STM imaging also reveals that the TiO₂ surface has morphological features consistent with the BaF₂ surface mesh symmetry. One of the optimally grown TiO₂ (1 0 0) films was used to template a CrO₂ (1 0 0) film which was grown via chemical vapor deposition. Point contact Andreev reflection measurements indicate that the CrO₂ film was approximately 70% spin polarized.     

Properties of ZnO films grown on (0 0 0 1) sapphire substrate using H2O and N2O as O precursors by atmospheric pressure MOCVD

In this paper, we compare the properties of ZnO thin films (0 0 0 1) sapphire substrate using diethylzinc (DEZn) as the Zn precursor and deionized water (H₂O) and nitrous oxide (N₂O) as the O precursors, respectively in the main ZnO layer growth by atmospheric pressure metal–organic chemical vapor deposition (AP-MOCVD) technique. Surface morphology studied by atomic force microscopy (AFM) showed that the N₂O-grown ZnO film had a hexagonal columnar structure with about 8 μm grain diameter and the relatively rougher surface compared to that of H₂O-grown ZnO film. The full-widths at half-maximum (FWHMs) of the (0 0 0 2) and () ω-rocking curves of the N₂O-grown ZnO film by double-crystal X-ray diffractometry (DCXRD) measurement were 260 and 350 arcsec, respectively, indicating the smaller mosaicity and lower dislocation density of the film compared to H₂O-grown ZnO film. Compared to H₂O-grown ZnO film, the free exciton A (FX_A) and its three phonon replicas could be clearly observed, the donor-bound exciton A⁰X (I₁₀):3.353 eV dominated the 10 K photoluminescence (PL) spectrum of N₂O-grown ZnO film and the hydrogen-related donor-bound exciton D⁰X (I₄):3.363 eV was disappeared. The electron mobility (80 cm²/V s) of N₂O-grown ZnO film has been significantly improved by room temperature Hall measurement compared to that of H₂O-grown ZnO film.     

Epitaxial growth of the CoFe2O4 film on SrTiO3 and its characterization

Cobalt ferrite (CoFe₂O₄) thin film is epitaxially grown on (0 0 1) SrTiO₃ (STO) by laser molecular beam epitaxy (LMBE). The growth modes of CoFe₂O₄ (CFO) film are found to be sensitive to laser repetition, the transitions from layer-by-layer mode to Stranski–Krastanov (SK) mode and then to island mode occur at the laser repetition of 3 and 5 Hz at 700 °C, respectively. The X-ray diffraction (XRD) results show that the CFO film on (0 0 1) SrTiO₃ is compressively strained by the underlying substrate and exhibits high crystallinity with a full-width at half-maximum of 0.86°. Microstructural studies indicate that the as-deposited CFO film is c-oriented island structure with rough surface morphology and the magnetic measurements reveal that the compressive strained CoFe₂O₄ film exhibits an enhanced out-of-plane magnetization (190 emu/cm³) with a large coercivity (3.8 kOe).     

Low-temperature synthesis of C60 thin films by ionized cluster beam deposition technique

C₆₀ films on Si(1 1 1) have been grown at low substrate temperature of 100°C by ionized cluster beam deposition technique. Fourier transform infrared (FTIR) transmission spectroscopy, Raman measurements and X-ray diffraction are employed to investigate the structure of deposited films. The results show that the acceleration voltage plays an important role in the growth of the films. As the acceleration voltage is moderate (100 V), a pristine C₆₀ film with face-centered-cubic (fcc) crystal structure can be grown. Further increase of the acceleration voltage leads to the formation of amorphous carbon (a-C) in the grown films. When the acceleration voltage is increased to 600 V, the deposited film has a complete amorphous carbon (a-C) structure.     

MgO films grown on yttria-stabilized zirconia by molecular beam epitaxy

MgO films were grown on (0 0 1) yttria-stabilized zirconia (YSZ) substrates by molecular beam epitaxy (MBE). The crystalline structures of these films were investigated using X-ray diffraction and transmission electron microscopy. Growth temperature was varied from 350 to 550 °C, with crystalline quality being improved at higher temperatures. The MgO films had a domain structure: (1 1 1)[1 1 2¯]_MgO(0 0 1)[1 0 0]_YSZ with four twin variants related by a 90° in-plane rotation about the [1 1 1]_MgO axis. The observed epitaxial orientation was compared to previous reports of films grown by pulsed laser deposition and sputtering and explained as resulting in the lowest interface energy.     

Microstructure and ferroelectric properties of BaTiO3 films on LaNiO3 buffer layers by rf sputtering

We have fabricated LaNiO₃ and BaTiO₃ films using the rf sputtering method. The LaNiO₃ were deposited on Si substrates, demonstrating a (1 0 0) highly oriented structure and nanocrystalline characteristic with a grain size of 30 nm. The BaTiO₃ thin films were deposited on the LaNiO₃ buffer layers, and have exhibited a (1 0 0) texture with a thickness of 400 nm. A smooth interface is obtained between the LaNiO₃ bottom electrode and the BaTiO₃ film from cross-section observations by scanning electron microscopy. The bi-layer films show a dense and column microstructure with a grain size of 60 nm. Ferroelectric characterizations have been obtained for the BaTiO₃ films. The remnant polarization and coercive field are 2.1 μC/cm² and 45 kV/cm, respectively. The leak current measurements have shown a good insulating property.     

Characteristics of ZnO–B2O3–CaO–Na2O–P2O5 glass powders prepared by spray pyrolysis

Fine-sized ZnO–B₂O₃–CaO–Na₂O–P₂O₅ glass powders with spherical shape were directly prepared by high temperature spray pyrolysis. The ZnO–B₂O₃–CaO–Na₂O–P₂O₅ powders prepared by spray pyrolysis at temperatures above 1200 °C had broad peaks at around 30° in the XRD patterns. The glass transition temperatures (T_g) of the glass powders obtained by spray pyrolysis at preparation temperatures between 900 °C and 1400 °C were near 480 °C regardless of the preparation temperatures. The dielectric layers formed from the glass powders prepared by spray pyrolysis at preparation temperatures above 1300 °C had clean surface and dense inner structure at the firing temperature of 580 °C. The transmittance of the dielectric layer formed from the glass powders obtained by spray pyrolysis at preparation temperature of 1400 °C was 90% at the firing temperature of 580 °C, in which the thickness of the dielectric layer was 13 μm. The UV cutoff edges gradually shift towards longer wavelength with increasing the preparation temperature of glass powders and the firing temperature of dielectric layers.     

Influence of cooling rate on the liquid-phase epitaxial growth of Zn3P2

We report the liquid-phase epitaxial growth of Zn₃P₂ on InP (1 0 0) substrates by conventional horizontal sliding boat system using 100% In solvent. Different cooling rates of 0.2–1.0 °C/min have been adopted and the influence of supercooling on the properties of the grown epilayers is analyzed. The crystal structure and quality of the grown epilayers have been studied by X-ray diffraction and high-resolution X-ray rocking measurements, which revealed a good lattice matching between the epilayers and the substrate. The supercooling-induced morphologies and composition of the epilayers were studied by scanning electron microscopy and energy dispersive X-ray analysis. The growth rate has been calculated and found that there exists a linear dependence between the growth rate and the cooling rate. Hall measurements showed that the grown layers are unintentionally doped p-type with a carrier mobility as high as 450 cm²/V s and a carrier concentration of 2.81×10¹⁸ cm⁻³ for the layers grown from 6 °C supercooled melt from the cooling rate of 0.4 °C/min.     

Deep ultraviolet emission of ZnO films prepared by RF magnetron sputtering at changing substrate temperature

ZnO films with deep ultraviolet emission on (0 0 0 6) sapphire substrates were prepared by RF magnetron sputtering at periodically changing substrate temperature. It is found that the as-prepared ZnO films consist of the obvious multilayered structures from the SEM images of their cross-sections. Room temperature photoluminescence of ZnO films with multilayered structure shows two emissions centered at 332 and 388 nm with 260 nm excited wavelength. The strong deep ultraviolet emission at 332 nm is due to the O 2p dangling-bond state in the multilayered structure of ZnO films. Raman scattering spectrum of sample shows that such structured ZnO film possesses strong compressive stress.     

High-quality ZnO thin films prepared by two-step thermal oxidation of the metallic Zn

In this paper, we report the preparation of nanocrystalline ZnO thin films on Si (1 0 0) substrates using a simple method, in which a resistive thermal evaporation of Zn and a two-step annealing process were employed. The aim of the first annealing step in an oxygen ambient at 300°C for 2 h is to form ZnO layers on the surface of the Zn films to prevent the diffusion of the metallic Zn from the films during the high-temperature annealing process. To obtain high-quality ZnO films, a high-temperature annealing step was performed at temperature in the range of 600–900°C. The effects of the annealing temperature on the photoluminescence (PL) and orientation of ZnO nanocrystalline thin films were studied. A very strong near-band-edge emission around 375 nm with a full-width at half-maximum of 105 meV and a relatively weak emission around 510 nm related to deep-level defects were observed, which indicated that high-quality ZnO films have been obtained.     

Growth and optical absorption spectra of ZnO films grown by pulsed laser deposition

ZnO films on Al₂O₃ substrate were grown by using a pulsed laser deposition method. Through photoluminescence (PL) and X-ray diffraction (XRD) measurements, the optimum growth conditions for the ZnO growth were calculated. The results of the XRD measurement indicate that ZnO film was strongly oriented to the c-axis of hexagonal structure and epitaxially crystallized under constraints created by the substrate. The full-width half-maximum for a theta curve of the (0 0 0 2) peak was 0.201°. Also, from the PL measurement, the grown ZnO film was observed to be a free exciton, which indicates a high quality of epilayer. The Hall mobility and carrier density of the ZnO film at 293 K were estimated to be 299 cm²/V sec and , respectively. The absorption spectra revealed that the temperature dependence of the optical band gap on the ZnO films was − .     

Structural,electrical and optical properties of SnO2 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

SnO₂ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates at different substrate temperatures (500–800 °C) by metalorganic chemical vapor deposition (MOCVD). Structural, electrical and optical properties of the films have been investigated. The films deposited at 500 and 600 °C are epitaxial SnO₂ films with orthorhombic columbite structure, and the HRTEM analysis shows a clear epitaxial relationship of columbite SnO₂(1 0 0)||YSZ(1 0 0). The films deposited at 700 and 800 °C have mixed-phase structures of rutile and columbite SnO₂. The carrier concentration of the films is in the range from 1.15×10¹⁹ to 2.68×10¹⁹ cm⁻³, and the resistivity is from 2.48×10⁻² to 1.16×10⁻² Ω cm. The absolute average transmittance of the films in the visible range exceeds 90%. The band gap of the obtained SnO₂ films is about 3.75–3.87 eV.     

Fabrication of Zn/ZnO nanocables through thermal oxidation of Zn nanowires grown by RF magnetron sputtering

Fabrication of Zn/ZnO nanocables by thermal oxidation of Zn nanowires grown by RF magnetron sputtering is reported. Single crystalline Zn nanowires could be grown by controlling supersaturation of source material through the adjustment of temperature and Zn RF power. X-ray diffraction and high-resolution transmission electron microscopy showed that surfaces of these Zn nanowires, grown along the [0 1 0] direction, gradually oxidized inward the Zn core to form coaxial Zn/ZnO nanocables in the subsequent oxidation at 200 °C. In the Zn/ZnO nanocable, epitaxial relations of [1 0 0]_Zn//[1 0 0]_ZnO, and (0 0 1)_Zn//(0 0 1)_ZnO existed at the interface between the Zn core and ZnO shell. A number of dislocations were also observed in the interface region of the Zn/ZnO nanocable, which are attributed to large differences in the lattice constants of Zn and ZnO. With further increasing the oxidation temperature over 400 °C, Zn nanowires were completely oxidized to form polycrystalline ZnO nanowires. The results in this study suggest that coaxial Zn/ZnO nanocable can be fabricated through controlled thermal oxidation of Zn nanowires, yielding various cross-sectional areal fractions of Zn core and ZnO shell.     

Study on the Ce substitution effects of BiFeO3 films on ITO/glass substrates

Ce substituted Bi_1−xCe_xFeO₃ (BCFO) films with x=0–0.15 were deposited on indium tin oxide (ITO)/glass substrates by sol–gel process annealed at 500 °C. Rhombohedral phase was confirmed by XRD study and no impure phases were observed till x=0.15. Substantially enhanced ferroelectricity was observed at room temperature due to the substitution of Ce. In the films with x=0.05 and 0.10, the double remnant polarization are 75.5 and 57.7 μC/cm² at an applied field 860 kV/cm. Moreover, the breakdown field was enhanced in the films with Ce substitution.     

Solvothermal growth of ZnO

The growth of ZnO single crystals and crystalline films by solvothermal techniques is reviewed. Largest ZnO crystals of 3 inch in diameter are grown by a high-pressure medium-temperature hydrothermal process employing alkaline-metal mineralizer for solubility enhancement. Structural, thermal, optical and electrical properties, impurities and annealing effects as well as machining are discussed. Poly- and single-crystalline ZnO films are fabricated from aqueous and non-aqueous solutions on a variety of substrates like glass, (100) silicon, -Al₂O₃, Mg₂AlO₄, ScAlMgO₄, ZnO and even some plastics at temperatures as low as 50 °C and ambient air conditions. Film thickness from a few nanometers up to some tens of micrometers is achieved. Lateral epitaxial overgrowth of thick ZnO films on Mg₂AlO₄ from aqueous solution at 90 °C was recently developed. The best crystallinity with a full-width half-maximum from the (0002) reflection of 26 arcsec has been obtained by liquid phase epitaxy employing alkaline-metal chlorides as solvent. Doping behavior (Cu, Ga, In, Ge) and the formation of solid solutions with MgO and CdO are reported. Photoluminescence and radioluminescence are discussed.     

Growth and properties of (Pb0.90La0.10)TiO3 thick films prepared by RF magnetron sputtering with a PbO buffer layer

The (Pb_0.90La_0.10)TiO₃ [PLT] thick films (3.0 μm) with a PbO buffer layer were deposited on the Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates by RF magnetron sputtering method. The PLT thick films comprise five periodicities, the layer thicknesses of (Pb_0.90La_0.10)TiO₃ and PbO in one periodicity are fixed. The PbO buffer layer improves the phase purity and electrical properties of the PLT thick films. The microstructure and electrical properties of the PLT thick films with a PbO buffer layer were studied. The PLT thick films with a PbO buffer layer possess good electrical properties with the remnant polarization (P_r=2.40 μC cm⁻²), coercive field (E_c=18.2 kV cm⁻¹), dielectric constant (ε_r=139) and dielectric loss (tan δ=0.0206) at 1 kHz, and pyroelectric coefficient (9.20×10⁻⁹ C cm⁻² K⁻¹). The result shows the PLT thick film with a PbO buffer layer is a good candidate for pyroelectric detector.