A Novel Boron-Rich Scandium Borocarbide; Sc4.5−xB57−y+zC3.5−z(x=0.27, y=1.1, z=0.2)

A novel ternary boron-rich scandium borocarbide Sc_4.5−xB_57−y+zC_3.5−z (x=0.27, y=1.1, z=0.2) was found. Single crystals were obtained by the floating zone method by adding a small amount of Si. Single-crystal structure analysis revealed that the compound has an orthorhombic structure with lattice constants of a=1.73040(6), b=1.60738(6) and c=1.44829(6) nm and space group Pbam (No. 55). The crystal composition ScB_13.3C_0.78Si_0.008 calculated from the structure analysis agreed with the measured composition of ScB_12.9C_0.72Si_0.004. The orthorhombic crystal structure is a new structure type of boron-rich borides and there are six structurally independent B₁₂ icosahedra I1—I6, one B₈/B₉ polyhedron and nine bridging sites all which interconnect each other to form a three-dimensional boron framework. The main structural feature of the boron framework structure can be understood as a layer structure where two kinds of boron icosahedron network layer L1 and L2 stack each other along the c-axis. There are seven structurally independent Sc sites in the open spaces between the boron icosahedron network layers.     

A novel boron-rich quaternary scandium borocarbosilicide Sc3.67−xB41.4−y−zC0.67+zSi0.33−w

A novel quaternary scandium borocarbosilicide Sc_3.67−xB_41.4−y−zC_0.67+zSi_0.33−w was found. Single crystallites were obtained as an intergrowth phase in the float-zoned single crystal of Sc_0.83−xB_10.0−yC_0.17+ySi_0.083−z that has a face-centered cubic crystal structure. Single crystal structure analysis revealed that the compound has a hexagonal structure with lattice constants a = b = 1.43055(8) nm and c = 2.37477(13) nm and space group (No. 187). The crystal composition calculated from the structure analysis for the crystal with x = 0.52, y = 1.42, z = 1.17, and w = 0.02 was ScB_12.3C_0.58Si_0.10 and that agreed rather well with the composition of ScB_11.5C_0.61Si_0.04 measured by EPMA. In the crystal structure that is a new structure type of boron-rich borides, there are 79 structurally independent atomic sites, 69 boron and/or carbon sites, two silicon sites and eight scandium sites. Boron and carbon form seven structurally independent B₁₂ icosahedra, one B₉ polyhedron, one B₁₀ polyhedron, one irregularly shaped B₁₆ polyhedron in which only 10.7 boron atoms are available because of partial occupancies and 10 bridging sites. All polyhedron units and bridging site atoms interconnect each other forming a three-dimensional boron framework structure. Sc atoms reside in the open spaces in the boron framework structure.     

X-ray structural study of intermetallic alloys RT2Si and RTSi2 (R=rare earth, T=noble metal)

Two series of intermetallic alloys, RT₂Si and RTSi₂, have been synthesized from stoichiometric compositions. The crystal structures of EuPt_1+xSi_2−x (CeNiSi₂-type), CeIr₂Si (new structure type), YbPd₂Si and YbPt₂Si (both YPd₂Si-type) have been elucidated from X-ray single crystal CCD data, which were confirmed by XPD experiments. The crystal structures of LaRh₂Si and LaIr₂Si (CeIr₂Si-type), {La,Ce,Pr,Nd}AgSi₂ (all TbFeSi₂-type), and EuPt₂Si (inverse CeNiSi₂-type) were characterized by XPD data. RT₂Si/RTSi₂ compounds were neither detected in as-cast alloys Sc₂₅Pt₅₀Si₂₅, Eu₂₅Os₂₅Si₅₀ and Eu₂₅Rh₂₅Si₅₀ nor after annealing at 900 °C. Instead, X-ray single crystal data prompted Eu₂Os₃Si₅ (Sc₂Fe₃Si₅-type) and EuRh_2+xSi_2−x (x=0.04, ThCr₂Si₂-type) as well as a new structure type for Sc₂Pt₃Si₂ (own type).     

X-ray and neutron powder diffraction studies of Ba(NdxY2−x)CuO5

Ba(R,R′)₂CuO₅ (R,R′=lanthanides and Y) plays an important role as a flux-pinning agent in enhancing the superconducting properties of the Ba₂(R,R′)Cu₃O_6+x (R,R′=lanthanides and Y) coated conductors. Using X-ray diffraction and neutron diffraction, we found that the Ba(Nd_xY_2−x)CuO₅ solid solution adopts two structure types. In the Nd-rich region (1.8?x?2.0), the materials are of brown color (commonly referred to as the ‘brown phase’), and the structure is tetragonal with space group I4/mbm (no. 127). In the Y-rich region (0.0?x?1.4), the materials are green (commonly referred to as the ‘green phase’) and the structure is orthorhombic with space group Pnma (no. 62). A two-phase region (1.4<x<1.8) exists between the orthorhombic and tetragonal phases. The crystal chemistry and crystallography of the orthorhombic ‘green phase’ series, Ba(Nd_xY_2−x)CuO₅ (isostructural to BaY₂CuO₅), are discussed in this paper.     

Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

Visible light-sensitive yellow TiO2−xNx and Fe-N co-doped Ti1−yFeyO2−xNx anatase photocatalysts

Nitrogen substituted yellow colored anatase TiO_2−xN_x and Fe-N co-doped Ti_1−yFe_yO_2−xN_x have been easily synthesized by novel hydrazine method. White anatase TiO_2−δ and N/Fe-N-doped samples are semiconducting and the presence of ESR signals at g ∼1.994-2.0025 supports the oxygen vacancy and g∼4.3 indicates Fe³⁺ in the lattice. TiO_2−xN_x has higher conductivity than TiO_2−x and Fe/Fe-N-doped anatase and the UV absorption edge of white TiO_2−x extends in the visible region in N, Fe and Fe-N co-doped TiO₂, which show, respectively, two band gaps at ∼3.25/2.63, ∼3.31/2.44 and 2.8/2.44 eV. An activation energy of ∼1.8 eV is observed in Arrhenius log resistivity vs. 1/T plots for all samples. All TiO₂ and Fe-doped TiO₂ show low 2-propanol photodegradation activity but have significant NO photodestruction capability, both in UV and visible regions, while standard Degussa P-25 is incapable in destroying NO in the visible region The mid-gap levels that these N and Fe-N-doped TiO₂ consist may cause this discrepancy in their photocatalytic activities.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.     

New synthesis of excellent visible-light TiO2−xNx photocatalyst using a very simple method

An excellent visible-light-responsive (from 400 to 550 nm) TiO_2−xN_x photocatalyst was prepared by a simple wet method. Hydrazine was used as a new nitrogen resource in this paper. Self-made amorphous titanium dioxide precursor powders were dipped into hydrazine hydrate, and calcined at low temperature (110 °C) in the air. The TiO_2−xN_x was successfully synthesized, following by spontaneous combustion. The photocatalyst was characterized by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), transmission electron microscope (TEM), UV-Vis diffuse reflectance spectrometer (DRS), and X-ray photoelectron spectroscopy (XPS). Analysis of XPS indicated that N atoms were incorporated into the lattice of the titania crystal during the combustion of hydrazine on the surface of TiO₂. Ethylene was selected as a target pollutant under visible-light excitation to evaluate the activity of this photocatalyst. The newly prepared TiO_2−xN_x photocatalyst with strong photocatalytic activity and high photochemical stability under visible-light irradiation was firstly demonstrated in the experiment.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

Charge compensation and oxidation in NaxCoO2−δ and LixCoO2−δ studied by XANES

A comparative study on the oxidation and charge compensation in the A_xCoO_2−δ systems, A=Na (x=0.75, 0.47, 0.36, 0.12) and Li (x=1, 0.49, 0.05), using X-ray absorption spectroscopy at O 1s and Co 2p edges is reported. Both the O 1s and Co 2p XANES results show that upon removal of alkali metal from A_xCoO_2−δ the valence of cobalt increases more in Li_xCoO_2−δ than in Na_xCoO_2−δ. In addition, the data of O 1s XANES indicate that charge compensation by oxygen is more pronounced in Na_xCoO_2−δ than in Li_xCoO_2−δ.     

The pyrochlore to ‘defect fluorite’ transition in the Y2(ZryTi1−y)2O7 system and its underlying crystal chemistry

A careful investigation of the previously reported single phase, pyrochlore structure type Y₂(Zr_yTi_1−y)₂O₇, 0?y?0.9, (YZT) solid solution has been carried out. Given the known slow rate of diffusion of cations in fluorite-related stabilized zirconia systems and the consequent difficulty in achieving equilibrium, careful attention was paid to synthesis procedures while Guinier XRD and electron diffraction were used to investigate the synthesized materials. As a consequence, a subtle but nonetheless clear two-phase region separating a pyrochlore-type solid solution field (from 0?y?∼0.54) from a “defect fluorite” type solid solution field (from ∼0.68?y?1) has been found. The underlying crystal chemistry of the system has been investigated using the bond valence sum approach. The dielectric properties have also been measured as a function of composition. The dielectric constant and dielectric loss of the lowest y compounds are potentially quite useful but deteriorate rapidly with increasing Zr content.     

Structure and phase composition of nanocrystalline Ce1−xLuxO2−y

The microstructure and phase stability of nanocrystalline mixed oxide Lu_xCe_1−xO_2−y (x=0-1) are described. Nano-sized (3-4 nm) oxide particles were prepared by the reverse microemulsion method. Morphological and structural changes upon heat treatment in an oxidizing atmosphere were studied by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman and Yb³⁺ emission spectroscopy, the latter ion being present as an impurity in the Lu₂O₃ starting material. Up to 950 °C, the samples were single phase, with structure changing smoothly with Lu content from fluorite type (F) to bixbyite type (C). For the samples heated at 1100 °C phase separation into coexisting F- and C-type structures was observed for 0.35<x<0.7. It was also found that addition of Lu strongly hinders the crystallite growth of ceria during heat treatment at 800 and 950 °C.     

Structural, spectroscopic and photoluminescence studies of LiEu(WO4)2−x(MoO4)x as a near-UV convertible phosphor

A series of lithium europium double tungsto-molybdate phosphors LiEu(WO₄)_2−x(MoO₄)_x (x=0, 0.4, 0.8, 1.2, 1.6, 2.0) have been synthesized by solid-state reactions and their crystal structure, optical and luminescent properties were studied. As the molybdate content increases, the intensity of the ⁵D₀→⁷F₂ emission of Eu³⁺ activated at wavelength of 396 nm was found to increase and reach a maximum when the relative ratio of Mo/W is 2:0. These changes were found to be accompanied with the changes in the spectral feature, which can be attributed to the crystal field splitting of the ⁵D₀→⁷F₂ transition. As the molybdate content increases the emission intensity of the 615 nm peak also increases. The intense red-emission of the tungstomolybdate phosphors under near-UV excitation suggests them to be potential candidate for white light generation by using near-UV LEDs. In this study the effect of chemical compositions and crystal structure on the photoluminescent properties of LiEu(WO₄)_2−x(MoO₄)_x is investigated and discussed.     

Thermochemistry of Li1+xMn2−xO4 (0?x?1/3) spinel

Lithium substituted Li_1+xMn_2−xO₄ spinel samples in the entire solid solution range (0?x?1/3) were synthesized by solid-state reaction. The samples with x<0.25 are stoichiometric and those with x?0.25 are oxygen deficient. High-temperature oxide melt solution calorimetry in molten 3Na₂O·4MoO₃ at 974 K was performed to determine their enthalpies of formation from constituent binary oxides at 298 K. The cubic lattice parameter was determined from least-squares fitting of powder XRD data. The variations of the enthalpy of formation from oxides and the lattice parameter with x follow similar trends. The enthalpy of formation from oxides becomes more exothermic with x for stoichiometric compounds (x<0.25) and deviates endothermically from this trend for oxygen-deficient samples (x?0.25). This energetic trend is related to two competing substitution mechanisms of lithium for manganese (oxidation of Mn³⁺ to Mn⁴⁺ versus formation of oxygen vacancies). For stoichiometric spinels, the oxidation of Mn³⁺ to Mn⁴⁺ is dominant, whereas for oxygen-deficient compounds both mechanisms are operative. The endothermic deviation is ascribed to the large endothermic enthalpy of reduction.     

Synthesis, optical properties and electronic structures of polyoxometalates K3P(Mo1−xWx)12O40 (0?x?1)

Various compositions of solid solutions K₃P(Mo_1−xW_x)₁₂O₄₀ (0?x?1) were prepared using two solid state synthetic routes. The crystallite size was determined by linewidth refinements of X-ray diffraction patterns using the Warren-Averbach method, and the grain size distribution by laser scattering experiments. Optical properties were determined by diffuse reflectance measurements in the UV-visible range. The optical gap E_g was found to increase exponentially from ∼2.5 to ∼3.30 eV with increasing x, and is systematically shifted to a higher energy when the grain size decreases. The relation between E_g and x was analyzed by calculating the HOMO-LUMO gaps of the [P(Mo_1−xW_x)₁₂O₄₀]³⁻ anions on the basis of tight-binding electronic structure calculations.     

Homoatomic Clustering in the Intermediate Valence Compounds Yb1−yAl3−xSix and Yb1−yAl3−xGex

Two new phases, Yb_1−xAl_3−xSi_x and Yb_1−yAl_3−xGe_x, were found by systematic investigations of the according ternary systems. The crystal structures of Yb_1−yAl_2.8Si_0.2 and Yb_1−yAl_2.8Ge_0.2 (defect HT-PuAl₃ type) were studied by X-ray powder methods (CuKα₁ radiation, λ=1.54056 Å, hexagonal system, space group P6₃/mmc (No. 194), a=6.009(1) and 6.015(1) Å, c=14.199(2) and 14.241(5) Å, V=444.0(2) and 446.2(3) ų, 93 and 92 reflections, and 8200 and 8000 profile points for silicide and germanide, respectively). Full profile refinements with 11 and 13 structural parameters resulted in R_I=0.049 and 0.054, and R_p=0.088 and 0.104, respectively. The ternary structures are distorted closest packings in comparison with the binary YbAl₃ compound with AuCu₃-type structure. They are characterized by the formation of Al₃-, Si₃-, and Ge₃-homoatomic clusters and aluminum networks. Magnetization measurements show that both the silicide and germanide are valence fluctuation compounds with enhanced electronic density of states at the Fermi level similar to the binary YbAl₃. The characteristic maximum of the magnetic susceptibility increases from ≈120 K for YbAl₃ to ≈140 K for Yb_1−yAl_2.8Si_0.2or Yb_1−yAl_2.8Ge_0.2 and further to ≈150 K for Yb_1−yAl_2.75Si_0.25. The S-shape of the electrical resistivity curves is also characteristic of valence fluctuations.     

Formation of crystalline TiO2−xNx and its photocatalytic activity

Amorphous precursors to nitrogen-doped TiO₂ (NTP) and pure TiO₂ (ATP) powders were synthesized by hydrolytic synthesis and sol-gel method (SGM), respectively. Corresponding crystalline phases were obtained by thermally induced transformation of these amorphous powders. From FT-IR and XPS data, it was concluded that a complex containing titanium and ammonia was formed in the precipitate stage while calcination drove weakly adsorbed ammonium species off the surface, decomposed ammonia bound on surface of precipitated powder and led to substitution of nitrogen atom into the lattice of TiO₂ during the crystallization. The activation energies required for grain growth in amorphous TiO_2−xN_x and TiO₂ samples were determined to be 1.6 and 1.7 kJ/mol, respectively. Those required for the phase transformation from amorphous to crystalline TiO_2−xN_x and TiO₂ were determined to be 129 and 142 kJ/mol, respectively. A relatively low temperature was required for the phase transformation in NTP sample than in ATP sample. The fabricated N-doped TiO₂ photocatalyst absorbed the visible light showing two absorption edges; one in UV range due to titanium oxide as the main edge and the other due to nitrogen doping as a small shoulder. TiO_2−xN_x photocatalyst demonstrated its photoactivity for photocurrent generation and decomposition of 2-propanol (IPA) under visible light irradiation ().     

CeAlO3 and Ce1−xRxAlO3 (R=La, Nd) solid solutions: Crystal structure, thermal expansion and phase transitions

The crystal structures of CeAlO₃ and the solid solutions Ce_1−xR_xAlO₃ (R=La, Nd), and their thermal behaviour in a wide temperature range of 12−1200 K have been precisely determined by means of in situ high-resolution X-ray powder diffraction technique applying synchrotron radiation, thermal analysis and magnetic measurements. The unique sequence of the reversible phase transitions I4/mcm↔Imma↔R3¯c↔Pm3¯m has been detected in CeAlO₃ and solid solutions formed in the pseudo-binary system CeAlO₃-LaAlO₃. In the Ce_1−xNd_xAlO₃ system, the samples with x=0.3 and 0.5 compositions undergo three phase transformations I2/m↔Imma↔R3¯c↔Pm3¯m, whereas for the Ce-rich sample Ce_0.9Nd_0.1AlO₃ four successive transitions are observed: I4/mcm↔I2/m↔Imma↔R3¯c↔Pm3¯m. Crystal structure parameters of all structural polymorphs of CeAlO₃ and solid solutions based on them as well as their thermal evolution are reported. Based on in situ powder diffraction and DTA/DSC data, the phase diagrams of the pseudo-binary systems CeAlO₃-LaAlO₃ and CeAlO₃-NdAlO₃ are constructed together with a combined phase diagram, where the transition temperatures are presented as a function of the average radius of rare-earth cations.