Spin-wave resonances in Eu<Subscript>0.8</Subscript>Ce<Subscript>0.2</Subscript>Mn<Subscript>2</Subscript>O<Subscript>5</Subscript> and EuMn<Subscript>2</Subscript>O<Subscript>5</Subscript> multiferroics

Spin-wave resonances have been observed in superlattices arising due to the phase separation and self-organization of charge carriers in Eu_0.8Ce_0.2Mn₂O₅ single crystals. The resonances are found within the 5–80 K temperature range at frequencies close to 30 GHz. Similar resonances with intensities about an order of magnitude lower are also observed in EuMn₂O₅. The latter suggests the existence of charge transfer processes between the manganese ions of different valences in EuMn₂O₅.     

Magnetic dynamics of phase separation domains in GdMn<Subscript>2</Subscript>O<Subscript>5</Subscript> and Gd<Subscript>0.8</Subscript>Ce<Subscript>0.2</Subscript>Mn<Subscript>2</Subscript>O<Subscript>5</Subscript> multiferroics

Specific features of the magnetic properties and magnetic dynamics of isolated phase separation domains in GdMn₂O₅ and Gd_0.8Ce_0.2Mn₂O₅ have been investigated. These domains represent 1D superlattices consisting of dielectric and conducting layers with the ferromagnetic orientation of their spins. A set of ferromagnetic resonances of separate superlattice layers has been studied. The properties of the 1D superlattices in GdMn₂O₅ and Gd_0.8Ce_0.2Mn₂O₅ are compared with the properties of the previously investigated RMn₂O₅ (R = Eu, Tb, Er, and Bi) series. The similarity of the properties for all the RMn₂O₅ compounds with different R ion types is established. Based on the concepts of the magnetic dynamics of ferromagnetic multilayers and properties of semiconductor superlattices, a 1D model of the superlattices in RMn₂O₅ is built.     

Large optical nonlinearity in CaCu<Subscript>3</Subscript>Ti<Subscript>4</Subscript>O<Subscript>12</Subscript> thin films

CaCu₃Ti₄O₁₂ (CCTO) thin films were successfully prepared on LaAlO₃ substrates by pulsed laser deposition technique. We measured the nonlinear optical susceptibility of the thin films using Z-scan method at a wavelength of 532 nm with pulse durations of 25 ps and 7 ns. The large values of the third-order nonlinear optical susceptibility, χ ⁽³⁾, of the CCTO film were obtained to be 2.79×10⁻⁸ esu and 3.30×10⁻⁶ esu in picosecond and nanosecond time regimes, respectively, which are among the best results of some representative nonlinear optical materials. The origin of optical nonlinearity of CCTO films was discussed. The results indicate that the CCTO films on LaAlO₃ substrates are promising candidate materials for applications in nonlinear optical devices.     

Soft X-ray resonant scattering study of single-crystal LaSr<Subscript>2</Subscript>Mn<Subscript>2</Subscript>O<Subscript>7</Subscript>

Soft X-ray resonant scattering studies at the Mn L_{II, III}- and the La M_{IV, V}- edges of single-crystal LaSr₂Mn₂O₇ are reported. At low temperatures, below T_N ≈ 160 K, energy scans with a fixed momentum transfer at the A-type antiferromagnetic (0 0 1) reflection around the Mn L_{II, III}-edges with incident linear σ and π polarizations show strong resonant enhancements. The splitting of the energy spectra around the Mn L_{II, III}-edges may indicate the presence of a mixed valence state, e.g., Mn³⁺/Mn⁴⁺. The relative intensities of the resonance and the clear shoulder-feature as well as the strong incident σ and π polarization dependences strongly indicate its complex electronic origin. Unexpected enhancement of the charge Bragg (0 0 2) reflection at the La M_{IV, V}-edges with σ polarization has been observed up to 300 K, with an anomaly appearing around the orbital-ordering transition temperature, T_OO ≈ 220 K, suggesting a strong coupling (competition) between them.     

Investigation on the electrochemical performances of Li<Subscript>4</Subscript>Mn<Subscript>5</Subscript>O<Subscript>12</Subscript> for battery applications

In this study, well-crystallized Li₄Mn₅O₁₂ powder was synthesized by a self-propagating combustion method using citric acid as a reducing agent. Various conditions were studied in order to find the optimal conditions for the synthesis of pure Li₄Mn₅O₁₂. The precursor obtained was then annealed at different temperatures for 24 h in a furnace. X-ray diffraction results showed that Li₄Mn₅O₁₂ crystallite is stable at relatively low temperature of 400 °C but decompose to spinel LiMn₂O₄ and monoclinic Li₂MnO₃ at temperatures higher than 500 °C. The prepared samples were also characterized by FESEM and charge-discharge tests. The result showed that the specific capacity of 70.7 mAh/g was obtained within potential range of 4.2 to 2.5 V at constant current of 1.0 mA. The electrochemical performances of Li₄Mn₅O₁₂ material was further discussed in this paper.     

Experimental study of antiferromagnetic resonance in noncollinear antiferromagnetic Mn<Subscript>3</Subscript>Al<Subscript>2</Subscript>Ge<Subscript>3</Subscript>O<Subscript>12</Subscript>

The structural and magnetic properties of the mesoporous systems based on silicon dioxide with a regular hexagonal arrangement of pores several microns in length and several nanometers in diameter, which are filled with iron compound nanofilaments in various chemical states, are studied in detail. The studies are performed using the following mutually complementary methods: transmission electron microscopy, SQUID magnetometry, electron spin resonance, Mössbauer spectroscopy, polarized neutron small-angle diffraction, and synchrotron radiation diffraction. It is shown that the iron nanoparticles in pores are mainly in the γ phase of Fe₂O₃ with a small addition of the α phase and atomic iron clusters. The effective magnetic field acting on a nanofilament from other nanofilaments is 11 mT and has a dipole nature, the ferromagnetic–paramagnetic transition temperature is in the range 76–94 K depending on the annealing temperature of the samples, and the temperature that corresponds to the change in the magnetic state of the iron oxide nanofilaments is T ≈ 50–60 K at H = 0 and T ≈ 80 K at H = 300 mT. It is also shown that the magnetization reversal of an array of nanofilaments is caused by the magnetostatic interaction between nanofilaments at the fields that are lower than the saturation field.     

Magnetoresistive effect in RCu<Subscript>3</Subscript>Mn<Subscript>4</Subscript>O<Subscript>12</Subscript> perovskite-like oxides

The electrical properties of and the magnetoresistive effect in RCu₃Mn₄O₁₂ (R=rare-earth ion or Th) are studied. In all compounds of this series, the magnetoresistive effect amounts to 20% at liquid nitrogen temperature in the presence of a field of 0.9 T. An increase in the magnetoresistance with decreasing temperature and a high sensitivity to weak magnetic fields at low temperatures point to the intergranular nature of the effect. The magnetoresistance shows a peak in the vicinity of the Curie temperature T_C. Based on the dependences of the magnetoresistance on an external magnetic field, it is assumed that the magnetoresistance peak near T_C is related to the charge carrier scattering by magnetic inhomogeneities as in substituted orthomanganites. We believe that the magnetoresistance value near the magnetic ordering temperature depends on the synthesis conditions and the effect of the intergranular spacer on the transport properties of these compounds.     

Elevated electrochemical property of LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> originated from nano-sized Mn<Subscript>3</Subscript>O<Subscript>4</Subscript>

By employment of nano-sized pre-prepared Mn₃O₄ as precursor, LiMn₂O₄ particles have been successfully prepared by facile solid state method and sol-gel route, respectively. And the reaction mechanism of the used precursors of Mn₃O₄ is studied. The structure, morphology, and element distribution of the as-synthesized LiMn₂O₄ samples are characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). Compared with LiMn₂O₄ synthesized by facile solid state method (SS-LMO), LiMn₂O₄ synthesized by modified sol-gel route (SG-LMO) possesses higher crystallinity, smaller average particle size (~175 nm), higher lithium chemical diffusion coefficient (1.17 × 10^?11 cm² s^?1), as well as superior electrochemical performance. For example, the cell based on SG-LMO can deliver a capacity of 85.5 mAh g^?1 at a high rate of 5 °C, and manifests 88.3% capacity retention after 100 cycles at 0.5 °C when cycling at 45 °C. The good electrochemical performance of the cell based on SG-LMO is ascribed mainly to its small particle size, high degree of dispersion, and uniform element distribution in bulk material. In addition, the lower polarization potential accelerates Li⁺ ion migration, and the lower atom location confused degree maintains integrity of crystal structure, both of which can effectively improve the rate capability and cyclability of SG-LMO.     

NMR spectrum in a Mn<Subscript>3</Subscript>Al<Subscript>2</Subscript>Ge<Subscript>3</Subscript>O<Subscript>12</Subscript> noncollinear antiferromagnet

The dependence of the NMR frequencies on the external magnetic field in a Mn₃Al₂Ge₃O₁₂ non-collinear 12-sublattice antiferromgnet is calculated using the exchange approximation for the spin dynamics.     

Synthesis,sintering, and conductivity of Mn<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript>

Studies on the sintering of manganese pyrovanadate depending on the temperature and the crystallite size show that we are prevented from obtaining a bulk ceramic sample by the anisotropic growth of grains. Investigation of the electrical properties of Mn₂V₂O₇ in the temperature range of 250–800°C reveals the activation energy at which bulk conductivity is 0.62 eV.     

Low-temperature formation of thermal and electrodynamic states in Bi<Subscript>2</Subscript>Sr<Subscript>2</Subscript>CaCu<Subscript>2</Subscript>O<Subscript>8</Subscript>

The formation of thermal and electrodynamic states in Bi₂Sr₂CaCu₂O₈ under the condition of current input is studied. The analysis is carried out for partial and complete current penetration under the assumption that the superconductor is cooled down to liquid helium temperature at the zero time. When the current input is continuous, the temperature dependence of the Bi₂Sr₂CaCu₂O₈ specific heat influences the form of the I-V and I-T characteristics of the superconductor. This effect is observed at high electric fields when both stable and unstable states form. As a result, the nonstationary I-V characteristic of Bi₂Sr₂CaCu₂O₈ has the only branch the slope of which is positive and decreases with increasing temperature. Therefore, the higher the rate of current input, the more pronounced the decrease in the slope. It is concluded that one cannot find the current above which instability develops from the Bi₂Sr₂CaCu₂O₈ I-V characteristic if the current input is continuous.     

Investigation of the phase diagram and superconductivity of Hg−Pb−Bi−Ba<Subscript>2</Subscript>CaCu<Subscript>2</Subscript>O<Subscript>6+δ</Subscript>

Compounds of the series Hg_(1?x?y) Bi_xPb_yBa₂CaCu₂O_6+δ (0≤x,y≤0.5) are synthesized directly from the metal oxides without using a precursor. Structural, and morphological investigations are made by x-ray diffraction, SEM and EDXA techniques. Bi and Pb substitution suppresses or enhances the simultaneous formation of Hg-1201 and Hg-1223 phase. Multiphase Hg_0.8Bi_0.2Ba₂CaCu₂O_6+δ has a maximum T_c of 134K. For Bi and Pb concentrations higher than 0.5 mole, non-superconducting phases are formed.     

Investigation of luminescence spectra of the Y<Subscript>3</Subscript>Al<Subscript>5</Subscript>O<Subscript>12</Subscript> and Y<Subscript>3</Subscript>Al<Subscript>5</Subscript>O<Subscript>12</Subscript>:Ce single-crystal films

The luminescence spectra of single-crystal films and bulk crystals of yttrium-aluminum garnet Y₃Al₅O₁₂ and Ce³⁺-activated Y₃Al₅O₁₂ were investigated. It was shown that the room-temperature luminescence intensity of the Ce³⁺-free single-crystal Y₃Al₅O₁₂ film was considerably lower than that of the bulk crystals, while the luminescence intensity of the Ce³⁺ ions in the Y₃Al₅O₁₂:Ce films was considerably higher than that one for the corresponding bulk crystal.     

Long-range magnetic order in quasi-one-dimensional NaCrSi<Subscript>2</Subscript>O<Subscript>6</Subscript> and NaCrGe<Subscript>2</Subscript>O<Subscript>6</Subscript> metal oxides

Formation of a long-range magnetic order is observed at low temperatures in NaCrSi₂O₆ and NaCrGe₂O₆ quasi-one-dimensional metal oxide compounds with a pyroxene structure. The first of these compounds, NaCrSi₂O₆, is an antiferromagnet with the Néel temperature T _N =3 K, while the second, NaCrGe₂O₆, is a ferromagnet with the Curie temperature T _C =6 K. From the measurements of magnetization and specific heat of these compounds, the main parameters of their magnetic subsystems are determined. In NaCrSi₂O₆, a spin-flip transition is observed. A change in the type of magnetic order that accompanies the replacement of Si by Ge can be attributed to a change in the parameters of the competing direct antiferromagnetic Cr-Cr and indirect ferromagnetic Cr-O-Cr interactions in isolated chains of CrO₆ octahedra.     

One-step synthesis of colloidal Mn<Subscript>3</Subscript>O<Subscript>4</Subscript> and γ-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> nanoparticles at room temperature

A facile room-temperature synthesis has been developed to prepare colloidal Mn₃O₄ and γ-Fe₂O₃ nanoparticles (5 to 25 nm) by an ultrasonic-assisted method in the absence of any additional nucleation and surfactant. The morphology of the as-prepared samples was observed by transmission electron microscopy. High-resolution transmission electron microscopy observations revealed that the as-synthesized nanoparticles were single crystals. The magnetic properties of the samples were investigated with a superconducting quantum interference device magnetometer. The possible formation process has been proposed.     

Dilute ferrimagnetism of ilmenites Mn<Subscript>3</Subscript>FeTiSbO<Subscript>9</Subscript> and Mn<Subscript>4</Subscript>FeTi<Subscript>2</Subscript>SbO<Subscript>12</Subscript>

Metastable solid solutions (SS) Mn₃FeTiSbO₉ and Mn₄FeTi₂SbO₁₂ with the ilmenite structure (space group R\(\bar 3\)) have been prepared by quenching at normal conditions. The compositions of the compounds have been justified using EDX spectroscopy and X-ray diffraction. The magnetic properties of SSs have been analyzed by comparison with ferrimagnetic ilmenite Mn₂FeSbO₆ (T_N = 269 K) as a natural mineral and ceramics obtained at high pressure and high temperature. The solid solutions have been characterized as dilute magnetic systems formed as a result of substitution of nonmagnetic cations Ti⁴⁺ for a part of Fe³⁺ and Sb⁵⁺ cations. Mn₃FeTiSbO₉ is considered as a ferromagnetic with T_N = 171 K and Mn₄FeTi₂SbO₁₂ as a magnetic with the concentration of magnetic clusters below the percolation threshold.     

Conductivity and spectroscopic studies of Li<Subscript>2</Subscript>O-V<Subscript>2</Subscript>O<Subscript>5</Subscript>-B<Subscript>2</Subscript>O<Subscript>3</Subscript> glasses

Lithium vanadium-borate glasses with the composition of 0.3Li₂O–(0.7-x)B₂O₃–xV₂O₅ (x?=?0.3, 0.325, 0.35, 0.375, 0.4, 0.425, 0.45, and 0.475) were prepared by melt-quenching method. According to differential scanning calorimetry data, vanadium oxide acts as both glass former and glass modifier, since the thermal stability of glasses decreases with an increase in V₂O₅ concentration. Fourier transform infrared spectroscopy data show that the vibrations of [VO₄] structural units occur at V₂O₅ concentration of 45 mol%. It is established that the concentration of V⁴⁺ ions increases exponentially with the growth of vanadium oxide concentration. Direct and alternative current measurements are carried out to estimate the contribution both electronic and ionic conductivities to the value of total conductivity. It is shown that the electronic conductivity is predominant in the total one. The glass having the composition of 0.3Li₂O-0.275B₂O₃-0.475V₂O₅ shows the highest electrical conductivity that has the value of 7.4?×?10^?5 S cm^?1 at room temperature.     

Laser performance of holmium-doped Lu<Subscript>3</Subscript>Al<Subscript>5</Subscript>O<Subscript>12</Subscript> and (Lu,Y)<Subscript>3</Subscript>Al<Subscript>5</Subscript>O<Subscript>12</Subscript> crystals pumped by Tm:fiber laser

Optical properties of Ho³⁺-doped Lu₃Al₅O₁₂ and (Lu,Y)₃Al₅O₁₂ crystals were investigated and compared. Substitution of Y for Lu in the host garnet Lu₃Al₅O₁₂ results in broad absorption and emission spectra, and improvements in the laser behavior of Ho³⁺. Pumped by Tm:fiber laser, a maximum output power of 5.02 and 5.73 W of Ho-doped Lu₃Al₅O₁₂ and (Lu,Y)₃Al₅O₁₂ have been obtained, respectively. The center lasing wavelength are 2124.5 and 2123.0 nm for Lu₃Al₅O₁₂ and (Lu,Y)₃Al₅O₁₂, respectively.