以陶瓷厚膜为绝缘层的橙色电致发光器件的研究

报道了采用陶瓷厚膜作为绝缘层、ZnS:Mn作为发光层的橙色电致发光器件(TDEL).介绍了器件的制造工艺,测量了器件的电致发光光谱、阈值电压、亮度与电压、亮度与频率关系.结果显示厚膜电致发光器件比薄膜电致发光器件有更低的阈值电压.     

无机厚膜电致发光显示器件的研究

采用丝网印刷技术,在Al2O3陶瓷基板上印刷、高温烧结内电极及绝缘层,制备出陶瓷厚膜基板,进而制备了新型厚膜电致发光显示器(TDEL).整个器件结构为陶瓷基板/内电极/厚膜绝缘层/发光层/薄膜绝缘层/ITO透明电极.测试了器件的阈值电压、亮度与电压、亮度与频率关系,并对器件衰减特性进行了分析.结果显示厚膜电致发光器件比薄膜电致发光器件有更低的阈值电压和较小的介电损耗,有效地防止了串扰现象.     

可溶性聚合物薄膜发光器件的电致发光

采用脱氯化氢反应合成出氯仿可溶性的ＭＥＨ－ＰＰＶ聚合物,用ＭＥＨ－ＰＰＶ作为发光材料制备了单层结构ＩＴＯ／ＭＥＨ－ＰＰＶ／Ａｌ和双层结构ＩＴＯ／ＭＥＨ－ＰＰＶ／Ａｌｑ３／Ａｌ电致发光器件,测量了器件的电致发光谱、Ｉ－Ｖ特性和Ｂ－Ｖ特性,利用能级理论分析了器件的发光特性了随器件结构的不同所具有的规律,实验表明,单层结构器件和双层结构器件的发光出现在ＭＥＨ－ＰＰＶ层,当加入Ａｌｑ３电子传输层／空穴阻挡     

双层阴极结构BaO/Al聚合物电致发光器件电子注入的研究

介绍了用双层阴极BaO/Al和发光层MEH-PPV制成的聚合物电致发光器件(PLEDs),研究了绝缘层BaO对电子注入所起的作用.实验发现,BaO对电子的注入起到显著的促进作用,与直接用Al做阴极的器件对比,其发光亮度和效率分别提高了20倍和10倍,达到了1 250 cd/m2和0.4%.同时也研究了不同厚度的绝缘层BaO对电子注入的影响,随着厚度的增加,外部量子效率和亮度先增加后减少,存在一个约为1 nm的最佳厚度.另外,国外用绝缘层LiF和CsF做成器件,与他们的实验结果对比,发现是绝缘层BaO增强了电子的注入,而不是BaO分解得到的金属Ba.     

有机电致发光器件及其发光机理

有机电致发光器件是近年来国际上研究的一个热点,发展非常迅速.文章概述了有机电致发光(EL)器件的材料与结构,特别对其发光机理进行了详细介绍,展望了器件未来的发展趋势.     

有机电致发光器件的研制及其性能测试

有机电致发光器件是当前国际上的一个研究热点。文中分别利用８－羟基喹啉铝和聚乙烯咔唑作为电子传输层和空穴传输层，通过染料掺杂制得发绿光的双层有机电致发光器件。器件的最大发射峰位于４９１ｎｍ；驱动电压为２２Ｖ时，发光亮度超过２００ｃｄｍ－２。另外，还讨论了器件发光光谱的电压效应，并测定了器件的电流－电压、亮度－电压曲线。通过对比器件在室温条件下保存一周前后的发射光谱，发现器件的发光强度在保存一段时间后有较大的衰减，但其发光光谱的形状则保持不变。     

有机薄膜电致发光器件的研究进展（综述）

对近几年来有机薄膜电致发光（ＥＬ）器件的研究进展进行了综合评停和分析,有机薄膜ＥＬ器件是近年来国际上研究的一个热点,该器件具有可与集成电路相匹配,直流电压低,发光亮度高,以及它与无机薄膜相比较易实现多色显示等优点。     

有机电致发光器件的热传导特性研究

采用简化热阻模型和一维稳态有内热源的热传导方程,对有机电致发光(OLED)器件的热传导特性进行了研究.为了改善OLED器件的性能,设计并实现了一种新型结构的OLED器件.在给定OLED器件的结构、输入功率、对流换热和热物性参数等因素情况下,推导得出OLED器件运行时温度升高与输入功率,基片及各功能层薄膜的热导系数、厚度、面积等之间的关系式,建立了OLED器件内部的温度分布关系.研究结果表明,器件内的有机层和基底的传热性能是影响器件温度分布的重要因素,在功率密度为1.167×104W/m2、外界温度为300 K时,OLED器件在发光层AlQ3中可获得最高温度,其温度值比环境温度高29 K.在研发OLED器件过程中,要提高OLED器件的热稳定性,改善焦耳热效应对OLED器件性能的影响,则需要选用热物性较好的OLED有机材料,使有机层与导热性能良好的电极保持良好接触.通过实验研究,验证了理论分析的正确性.在相同的输入功率情况下,对自制备的若干Al阴极厚度不同的OLED器件进行了比较分析,验证了理论模型的有效性.研究结果对于OLED研发具有重要的价值.     

具有异质结的聚合物有机薄膜电致发光器件

本文报道了由一层电子传输材料ＰＰＱ和一层空穴传输材料ＰＤＤＯＰＶ构成的有机聚合物异常结发光二极管的实验结果。虽然双层器件的点亮电压高于由纯ＰＤＤＯＰＶ构成的单层器件,但是它在一定电压下,电流密度降低了一个数量级,而亮度却提高了近两个数量级。     

The ultraviolet and blue luminescence properties of ZnO:Zn thin film

The ultraviolet (UV) and blue luminescence of Zn-rich zinc oxide thin film deposited by electron-beam evaporation have been investigated at room temperature (RT). We observed that the UV and blue electroluminescence (EL) emission band centered around 480 nm which is blue shifted in comparison with that of the ZnO thin film prepared by low pressure metal organic chemical vapor deposition (LP MOCVD). The UV emission is much stronger than blue emission in the photoluminescence (PL) spectra. The field-induced ionization of excited luminescent centers of ZnO:Zn thin film at high electric field and the difference between PL and EL are discussed. The experiments show that the ZnO:Zn thin film provides a hopeful new mechanism to obtain UV and blue emission.     

Analysis on mechanism of thin film lubrication

It is an important concern to explore the properties and principles of lubrication at nano or molecular scale. For a long time, measurement apparatus for film thickness of thin film lubrication （TFL） at nano scale have been devised on the basis of superthin interferometry technique. Many experiments were carried out to study the lubrication principles of TFL by taking advantages of aforementioned techniques, in an attempt to unveil the mechanism of TFL. Comprehensive experiments were conducted to explore the distinctive characteristics of TFL. Results show that TFL is a distinctive lubrication state other than any known lubrication ones, and serves as a bridge between elastohydrodynamic lubrication （EHL） and boundary lubrication （BL）. Two main influence factors of TFL are the solid surface effects and the molecular properties of the lubricant, whose combination effects result in alignment of liquid molecules near the solid surfaces and subsequently lubrication with ordered film emerged. Results of theoretical analysis considering microstructure are consistent with experimental outcomes, thus validating the proposed mechanism.     

单异质结有机薄膜电致器件发光过程的理论模型

在Fowler—Nordheim方程的基础上，利用高斯定理对单异质结有机薄膜电致发光器件的发光过程进行理论分析和计算。计算结果表明在单异质结电致发光器件中，可降低器件的电流水平，提高器件的发光效率。     

铝诱导晶化非晶硅薄膜研究

应用晶化非晶硅（a—Si）薄膜铝诱导方法，采用X射线衍射（X-ray diffraction，XRD）、光学显微镜（Optical Microscopy，OM）和原子力显微镜（Atomic Force Microscopy，AFM）等测试手段，研究了退火条件对样品晶化的影响．结果表明，样品在300℃下退火后仍为非晶态；退火温度为400℃时，样品开始晶化．随着退火时间的增加，薄膜晶化程度越来越高，晶粒越来越大，同时薄膜表面粗糙度增加．     

以铜酞菁为过渡层的有机电致发光器件特性

研究过渡层结构对有机薄膜电致发光器件性能的影响。分别以铟、锡的氧化物 ( indium- tin- oxide,ITO)为阳极 ,以镁银合金 ( Mg:Ag)为阴极 ,用真空热蒸发法制备了结构为 ITO/ Cu Pc/ TPD/ Alq3/ Mg:Ag和 ITO/ TPD/ Alq3/ Mg:Ag的两类器件 ,并测定了器件的衰减曲线、发光光谱以及亮度—电压特性曲线。结果显示 :铜酞菁过渡层的使用虽然改善了器件的稳定性 ,但是却增大了器件的启亮电压 ,而且器件最大发光强度和最大光视效能也降低了。结果表明 :在高稳定性和高亮度、高光视效能不可兼得的时候 ,需要通过选择过渡层材料 ,优化制备工艺 ,获得一个最佳平衡值     

三层一维非金属薄膜材料热传导效应的研究

从声子散射模型出发,用拉普拉斯变换法得到三层一维非金属薄膜在简谐温度边界条件下温度响应的解。通过算例分析,讨论了在微尺度条件下非金属薄膜的热响应特征。计算表明,热响应温度和热传播速度随特征参数E的变化而变化。在薄膜中不同位置处,当E<0.1时,波动特性明显,最高响应温度在波的传播方向上先减小后增大;当E>0.1时,最高响应温度持续减小。当E取较大值时,热传播速度也较大,达到最大响应温度的热响应时间几乎相同。而在薄膜后表面,热传播速度随E的增大而增大。另外,当E<0.25,最大热扰动响应温度随E的增大而减小;当E>0.25时,最大热扰动响应温度随E的增大而增大。     

掺杂氧化锌薄膜的结构与刻蚀性能研究

本文利用中频反应磁控溅射方法,以Zn/Al (98 : 2) (wt. %)合金靶为靶材,制备了综合性能优良的铝掺杂氧化锌（ZnO:Al, AZO）透明导电薄膜. 研究了沉积工艺对薄膜结构、电学及光学性能的影响,分析了AZO薄膜的刻蚀性能以及所制备的绒面结构特性. 结果表明：基体温度对薄膜生长有较大的影响,当温度为150℃时,薄膜具有较好的晶化率,晶粒呈明显的柱状生长,晶界间结合紧密,薄膜的电阻率为4.6×10-4Ωcm. 镀膜时基体的移动速度会影响薄膜的晶体生长方式,但对其沉积速率影响不大. 具有择优生长特性、形成柱状晶组织的薄膜经稀盐酸腐蚀后,其表面呈规则的粗糙形貌;此结构有利于充分捕集太阳光,从而提高薄膜太阳电池的效率.