Enhancement of initial permeability due to Mn substitution in polycrystalline Ni0.50−xMnxZn0.50Fe2O4

The structural and magnetic properties of Mn substituted Ni_0.50−xMn_xZn_0.50Fe₂O₄ (where x=0.00, 0.10 and 0.20) sintered at various temperatures have been investigated thoroughly. The lattice parameter, average grain size and initial permeability increase with Mn substitution. Both bulk density and initial permeability increase with increasing sintering temperature from 1250 to 1300 °C and above 1300 °C they decrease. The Ni_0.30Mn_0.20Zn_0.50Fe₂O₄ sintered at 1300 °C shows the highest relative quality factor and highest initial permeability among the studied samples. The initial permeability strongly depends on average grain size and intragranular porosity. From the magnetization as a function of applied magnetic field, M(H), it is clear that at room temperature all samples are in ferrimagnetic state. The number of Bohr magneton, n(μ_B), and Neel temperature, T_N, decrease with increasing Mn substitution. It is found that Mn substitution in Ni_0.50−xMn_xZn_0.50Fe₂O₄ (where x=0.20) decreases the Neel temperature by 25% but increases the initial permeability by 76%. Possible explanation for the observed characteristics of microstructure, initial permeability, DC magnetization and Neel temperature of the studied samples are discussed.     

Structural and magnetic properties of MnxCo1−xFe2O4 ferrite nanoparticles

We report on the structural and magnetic properties of nanoparticles of Mn_xCo_1−xFe₂O₄ (x=0.1, 0.5) ferrites produced by the glycothermal reaction. From the analysis of XRD spectra and TEM micrographs, particle sizes of the samples have been found to be about 8 nm (for x=0.1) and 13 nm (for x=0.5). The samples were characterized by DC magnetization in the temperature range 5-380 K and in magnetic fields of up to 40 kOe using a SQUID magnetometer. Mössbauer spectroscopy results show that the sample with higher Mn content has enhanced hyperfine fields after thermal annealing at 700 °C. There is a corresponding small reduction in hyperfine fields for the sample with lower Mn content. The variations of saturation magnetization, remnant magnetization and coercive fields as functions of temperature are also presented. Our results show evidence of superparamagnetic behaviour associated with the nanosized particles. Particle sizes appear to be critical in explaining the observed properties.     

Li0.5Fe2.5−xMnxO4 ferrite sintered from microwave-induced combustion

Li_0.5Fe_2.5−xMn_xO₄ (0≦x≦1.0) powders with small and uniformly sized particles were successfully synthesized by microwave-induced combustion, using lithium nitrate, ferric nitrate, manganese nitrate and carbohydrazide as the starting materials. The process takes only a few minutes to obtain as-received Mn-substituted lithium ferrite powders. The resultant powders annealed at 650 ^°C for 2 h and were investigated by thermogravimeter/differential thermal analyzer (TG/DTA), X-ray diffractometer (XRD), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM), and thermomagnetic analysis (TMA). The results revealed that the Mn content were strongly influenced the magnetic properties and Curie temperature of Mn-substituted lithium ferrite powder. As for sintered Li_0.5Fe_2.5−xMn_xO₄ specimens, substituting an appropriate amount of Mn for Fe in the Li_0.5Fe_2.5−xMn_xO₄ specimens markedly improved the complex permeability and loss tangent.     

Structural and magnetic properties of sol-gel Co2xNi0.5−x Zn0.5−xFe2O4 thin films

Nanocrystalline Co_2xNi_0.5−xZn_0.5−xFe₂O₄ (x=0−0.5) thin films have been synthesized with various grain sizes by a sol-gel method on polycrystalline silicon substrates. The morphology as well as magnetic and microwave absorption properties of the films calcined at 1073 K were studied using X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, and vibrating sample magnetometry. All films were uniform without microcracks. The Co content in the Co-Ni-Zn films resulted in a grain size ranging from 15 to 32 nm while it ranged from 33 to 49 nm in the corresponding powders. Saturation and remnant magnetization increased with increase in grain size, while coercivity demonstrated a drop due to multidomain behavior of crystallites for a given value of x. Saturation magnetization increased and remnant magnetization had a maximum as a function of grain size independent of x. In turn, coercivity increased with x independent of grain size. Complex permittivity of the Co-Ni-Zn ferrite films was measured in the frequency range 2-15 GHz. The highest hysteretic heating rate in the temperature range 315-355 K was observed in CoFe₂O₄. The maximum absorption band shifted from 13 to 11 GHz as cobalt content increased from x=0.1 to 0.2.     

Synthesis of (Mg0.476Mn0.448Zn0.007)(Fe1.997Ti0.002)O4 powder and sintered ferrites by high energy ball-milling process

(Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder prepared by high energy ball-milling process were consolidated by microwave and conventional sintering processes. Phases, microstructure and magnetic properties of the ferrites prepared by different processes were investigated. The (Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder could be prepared by high energy ball-milling process of raw Fe₃O₄, MnO₂, ZnO, TiO₂ and MgO powders. Prefired and microwave sintered ferrites could achieve the maximum density (4.86 g/cm⁻³), the average grain size (15 μm) was larger than that (10 μm) prepared by prefired and conventionally sintered ferrites with pure ferrite phase, and the saturation magnetization (66.77 emu/g) was lower than that of prefired and conventionally sintered ferrites (88.25 emu/g), the remanent magnetization (0.7367 emu/g) was higher than that of prefired and conventionally sintered ferrites (0.0731 emu/g). Although the microwave sintering process could increase the density of ferrites, the saturation magnetization of ferrites was decreased and the remanent magnetization of ferrites was also increased.     

Enhancement of microstructure and initial permeability due to Cu substitution in Ni0.50−xCuxZn0.50Fe2O4 ferrites

Structural and magnetic properties of Cu substituted Ni_0.50−xCu_xZn_0.50Fe₂O₄ ferrites (where x=0.0-0.25) prepared by an auto combustion method have been investigated. The X-ray diffraction patterns of these compositions confirmed the formation of the single phase spinel structure. The lattice parameter increases with the increase in Cu²⁺ content obeying Vegard's law. The particle size of the starting powder compositions varied from 22 to 72 nm. The theoretical density increases with increase in copper content whereas the Néel temperature decreases. The bulk density, grain size and permeability increases up to a certain level of Cu²⁺ substitution, beyond that all these properties decrease with increase in Cu²⁺ content. The bulk density increases with increase in sintering temperatures up to 1250 °C for the parent composition, while for substituted compositions it increases up to 1200 °C. Due to substitution of Cu²⁺, the real part of the initial permeability increases from 97 to ∼390 for the sample sintered at 1100 °C and from 450 to 920 for the sample sintered at 1300 °C. The ferrites with higher initial permeability have a relatively lower resonance frequency, which obey Snoek's law. The initial permeability strongly depends on average grain size and intragranular porosity. The saturation magnetization, M_s, and the number of Bohr magneton, n(μ_B)_, decreases up to x=0.15 due to the reduction of the A-B interaction in the AB₂O₄ spinel type ferrites. Beyond that value of x, the M_s and the n(μ_B) values are enhanced. The substitution of Cu²⁺ influences the magnetic parameters due to modification of the cation distribution.     

Monodispersed nanocrystalline Co1–xZnxFe2O4 particles by forced hydrolysis: Synthesis and characterization

Zinc-substituted cobalt ferrites, Co_1–xZn_xFe₂O₄, were for the first time successfully prepared by forced hydrolysis method. The obtained materials are single phase, monodispersed nanocrystalline with an average grain size of about 3 nm. These materials are superparamagnetic at room temperature and ferrimagnetic at temperature lower than the blocking temperature. When the zinc substitution increases from x=0 to 0.4, at 4.2 K, the saturation magnetization increases from 72.1 to 99.7 emu/g. The high saturation magnetization of these samples suggests that this method is suitable for preparing high-quality nanocrystalline magnetic ferrites for practical applications.     

Structural, AC, and DC magnetic properties of Zn1−xCoxFe2O4

Structural, AC and DC magnetic properties of polycrystalline Zn_1−xCo_xFe₂O₄ (x=0.2, 0.4) samples sintered at various temperatures (1100-1300 °C), and various dwell times (0.2-15 h) have been investigated thoroughly. The bulk density of the Zn_0.60Co_0.40Fe₂O₄ samples increases as the sintering temperature (T_s) increases from 1100 to 1250 °C, and above 1250 °C the bulk density decreases slightly. The Zn_0.80Co_0.20Fe₂O₄ samples show similar behavior of changes to that of Zn_0.60Co_0.40Fe₂O₄ samples except that the bulk density is found to be highest at 1200 °C. The DC magnetization as a function of temperature curves show that the Zn_0.60Co_0.40Fe₂O₄ sample is ferrimagnetic at room temperature while the Zn_0.80Co_0.20Fe₂O₄ sample is paramagnetic at room temperature. The T_c of Zn_0.80Co_0.20Fe₂O₄ sample is found to be 170 K from DC magnetization measurement. Separate measurement (AC magnetization), initial permeability as a function of temperature shows that the T_c of the Zn_0.60Co_0.40Fe₂O₄ sample is 353 K. Slight variation of T_c is observed depending on sintering condition. The initial permeability for the Zn_0.60Co_0.40Fe₂O₄ composition sintered at 1250 °C is found to be maximum.     

Nanostructural,magnetic and Mössbauer studies of nanosized Co1−xZnxFe2O4 synthesized by co-precipitation

This work presents a systematic investigation on the structural and magnetic properties of Co_1−xZn_xFe₂O₄ (0.5<x<0.75) nanoparticles synthesized by the chemical co-precipitation method. The X-ray diffraction analysis, the Fourier Transform Infrared (FTIR) and the Vibrating Sample Magnetometer were carried out at room temperature to study the micro-structural and magnetic properties. The X-ray measurements revealed the production of a broad single cubic phase with the crystallite size within the range of 6–10 nm. The FTIR measurements between 400 and 4000 cm⁻¹ confirmed the intrinsic cation vibrations of the spinel structure. The magnetic measurements show that the saturation magnetization and coercivity decrease by increasing the zinc content. Furthermore, the results reveal that the sample with a chemical composition of Co_0.3Zn_0.7Fe₂O₄ exhibits the super-paramagnetic behavior and the Curie point of 97 °C.     

Magnetoresistive properties of Zn1−xCoxFe2O4 ferrites

The magnetic and magnetoresistive properties of spinel-type Zn_1−xCo_xFe₂O₄ (x=0, 0.2 and 0.4) ferrites are extensively investigated in this study. A large negative magnetoresistance (MR) effect is observed in Zn_1−xCo_xFe₂O₄ ferrites of spinel structure. These materials are either ferrimagnetic or paramagnetic at room temperature, and show a spin-(cluster) glass transition at low temperatures, depending on the chemical compositions. The MR curves as a function of magnetic fields, MR(H), are parabolic at all temperatures for paramagnetic polycrystalline ZnFe₂O₄. The MR for ZnFe₂O₄ at 110 K in the presence of 9 T applied magnetic field is 30%. On the other hand, MR(H) are linear for x=0.2 and 0.4 ferrimagnetic Zn_1−xCo_xFe₂O₄ samples up to 9 T. The MR effect is independent of the sintering temperatures, and can be explained with the help of the spin-dependent scattering and the Yafet–Kittel angle of Zn_1−xCo_xFe₂O₄ mixed ferrites.     

Effects of sintering temperature on grain growth and the complex permeability of Co0.2Ni0.3Zn0.5Fe2O4 material prepared using mechanically alloyed nanoparticles

Nanoparticle-sized Co_0.2Ni_0.3Zn_0.5Fe₂O₄ was prepared using mechanical alloying and sintering. The starting raw materials were milled in air and subsequently sintered at various temperatures from 600 to 1300 °C. The effects of sintering temperature on physical, magnetic and electrical characteristics were studied. The complex permittivity and permeability were investigated in the frequency range 10 MHz to 1.0 GHz. The results show that single phase Co_0.2Ni_0.3Zn_0.5Fe₂O₄ could not be formed during milling alone and therefore requires sintering. The crystallization of the ferrite sample increases with increasing sintering temperature; which decrease the porosity and increase the density, crystallite size and the shrinkage of the material. The maximum magnetization value of 83.1 emu/g was obtained for a sample sintered at 1200 °C, while both the retentivity and the coercivity decrease with increasing the sintering temperature. The permeability values vary with both the sintering temperature and the frequency and the absolute value of the permeability decreased after the natural resonance frequency. The real part of the permittivity was constant within the measured frequency, while the loss tangent values decreased gradually with increasing frequency.     

No room temperature ferromagnetism in Mn over-doped Zn1−xMnxO (x>0.02)

Mn-doped ZnO samples having composition Zn_1−xMn_xO (x=0.02, 0.04 and 0.05) were synthesized by solid state reaction technique with varying concentration of Mn from 0.02 to 0.05. Evidence of room temperature ferromagnetism was observed only in the composition Zn_0.98Mn_0.02O sintered at 500 °C. Our XRD pattern confirms the presence of Mn₃O₄ impurity phase in all the Zn_1−xMn_xO samples with the exception of Zn_0.98Mn_0.02O. We emphasize that the appearance of Mn₃O₄ phase in the system forbids the exchange type of interaction between the Mn ions and suppresses the ferromagnetism in all the Mn over-doped Zn_1−xMn_xO (x>0.02) system. SEM microstructure study also supports the interruption of exchange type of interaction inside the system with the increase in Mn concentration in the sample. Interestingly, for this particular composition, Zn_0.98Mn_0.02O sintered at 500 °C, glassy ferromagnetism type of transition is observed at low temperature. This type of transition is attributed to the formation of the oxides of Mn clusters at low temperature.     

Sintering temperature dependence of room temperature magnetic and dielectric properties of Co0.5Zn0.5Fe2O4 prepared using mechanically alloyed nanoparticles

Co_0.5Zn_0.5Fe₂O₄ nanoparticles were prepared using mechanical alloying (MA) and sintering. The crystallite size, coercivity, retentivity and saturation magnetization were also measured. The frequency dependence of dielectric and the magnetic parameters, namely, real permittivity ε′, loss tanget tan δ, real permeability μ′ and loss factor μ″ were measured at room temperature for samples sintered from 600 to 1000 °C, in the frequency range 10 MHz to 1.0 GHz. The results show that the crystallite size of the resulting products ranges between 16 and 67 nm for as-milled sample and the sample sintered at 1000 °C, respectively. The sample sintered at 1000 °C, measured at room temperature exhibited a saturation magnetization of 37 emu g⁻¹. The values of permittivity remain constant within the measured frequency, but vary with sintering temperature. The permeability values, on the other hand however vary with both the sintering temperature and the frequency, thus, the absolute value of the permeability decreased after the natural resonance frequency.     

Influence of frequency, temperature and composition on electrical properties of polycrystalline Co0.5CdxFe2.5−xO4 ferrites

Polycrystalline ferrites with general formula Co_0.5Cd_xFe_2.5−xO₄ (0.0?x?0.5) were prepared by sol-gel method. The dielectric properties ε′, ε″, loss tangent tan δ and ac conductivity σ_ac have been studied as a function of frequency, temperature and composition. The experimental results indicate that ε′, ε″, tan δ and σ_ac decrease as the frequency increases; whereas they increase as the temperature increases. These parameters are found to increase by increasing the concentration of Cd content up to x=0.2, after which they start to decrease with further increase in concentration of Cd ion. The dielectric properties and ac conductivity in studied samples have been explained on the basis of space charge polarization according to Maxwell and Wagner's two-layer model and the hoping between adjacent Fe²⁺ and Fe³⁺ as well as the hole hopping between Co³⁺and Co²⁺ ions at B-sites. The values of activation energies E_f for conduction process are determined from Arrhenius plots, and the variations in these activation energies as a function of Cd content are discussed. The complex impedance analysis is used to separate the grain and grain boundary of the system Co_0.5Cd_xFe_2.5−xO₄. The variations of both grain boundary and grain resistances with temperature and composition are evaluated in the frequency range 42 Hz-5 MHz.     

Room temperature ferromagnetism behavior of Sn1−xMnxO2 powders

In this paper, we have investigated Mn-doped SnO₂ powder samples prepared by solid-state reaction method. X-ray diffraction showed a single phase polycrystalline rutile structure. The atomic content of Mn ranged from ∼0.8 to 5 at%. Room temperature M-H loops showed a ferromagnetic behavior for all samples. The ferromagnetic Sn_0.987Mn_0.013O₂ showed a coercivity H_c=545 Oe, which is among the highest reported for dilute magnetic semiconductors. The magnetic moment per Mn atom was estimated to be about 2.54 μ_B of the Sn_0.9921Mn_0.0079O₂ sample. The average magnetic moment per Mn atom sharply decreases with increasing Mn content, while the effective fraction of the Mn ions contributing to the magnetization decreases. The magnetic properties of the Sn_1−xMn_xO₂ are discussed based on the competition between the antiferromagnetic superexchange coupling and the F-center exchange coupling mechanism, in which both oxygen vacancies and magnetic ions are involved.     

Electromagnetic properties of manganese-zinc ferrite with lithium substitution

Polycrystalline manganese-zinc ferrite with lithium substitution of composition Li_0.5xMn_0.4Zn_0.6−xFe_2+0.5xO₄ (0.0≤x≤0.4) was prepared by the usual ceramic method. X-ray diffraction analysis confirmed that the samples have a spinel structure and are of single phase for some values of Li content. Lithium doping considerably modifies saturation magnetization since its value increases from 57.5 emu/g for x=0.0 to 82.9 emu/g for x=0.4. Lithium inclusion increases the real permeability (over 1 MHz) while the natural resonance frequency shifts to lower values as the fraction of Li increases. These ferrites show good electromagnetic properties as absorbers in the microwave range of 1 MHz - 1 GHz.     

Observation of mixed-phase behavior in the Mn-doped cobaltite La0.7Sr0.3Co1−xMnxO3 (x=0-0.5)

Studies on La_0.7Sr_0.3Co_1−xMn_xO₃ (x=0-0.5) compounds evidence that the interaction between Mn and Co ions in this system is antiferromagnetic super-exchange and not ferromagnetic (FM) double-exchange (DE). As a result, antiferromagnetism and magnetic glassiness develop steadily with increasing Mn content and the system becomes a spin glass at x∼0.1. Analyses of high-field magnetization data indicate that the system consists of two major phases: a metallic FM phase which magnetically saturates in rather low field, and an insulating non-FM phase which has a linear dependence of magnetization on magnetic field. In the low doping regime, the fraction of the non-FM component expands with temperature at the expense of the FM phase and becomes maximal at T_C. Ferromagnetism reappears in highly doped (x≥0.2) compounds due to the presence of DE interaction between the Mn ions. The small volume fraction of the FM phase derived from the M(H) data in high-field region supports the coexistence of insulating and FM behaviors in the highly doped samples.     

Structural, thermal and magnetic properties of Ni1−xMnxFe2O4 nanoferrites

In this paper, the structural, thermal and magnetic properties of Ni_1−xMn_xFe₂O₄ are presented. It is observed that high concentration of Mn²⁺ ions into NiFe₂O₄ tends to reduce the particle size. Calcination at 500 °C has resulted in the growth of Ni_1−xMn_xFe₂O₄ nanoparticles, but the calcination at 900 °C has led to the evaporation of the majorities of the polyvinyl alcohol. After calcination at 900 °C, crystallographically oriented NiMnFe₂O₄ nanoparticles are formed. These Ni_1−xMn_xFe₂O₄ nanoparticles show hysteresis behaviour upon magnetization. On the other hand, saturation magnetization (Ms) values decreases with increasing Mn content in ferrite due to the influence of Mn²⁺ ion in the sub lattice.     

The structure and magnetic properties of Zn1−xNixFe2O4 ferrite nanoparticles prepared by sol–gel auto-combustion

Zn_1−xNi_xFe₂O₄ ferrite nanoparticles were prepared by sol–gel auto-combustion and then annealed at 700 °C for 4 h. The results of differential thermal analysis indicate that the thermal decomposition temperature is about 210 °C and Ni–Zn ferrite nanoparticles could be synthesized in the self-propagating combustion process. The microstructure and magnetic properties were investigated by means of X-ray diffraction, scanning electron microscope, and Vibrating sample magnetometer. It is observed that all the spherical nanoparticles with an average grain size of about 35 nm are of pure spinel cubic structure. The crystal lattice constant declines gradually with increasing x from 0.8435 nm (x=0.20) to 0.8352 nm (x=1.00). Different from the composition of Zn_0.5Ni_0.5Fe₂O₄ for the bulk, the maximum M_s is found in the composition of Zn_0.3Ni_0.7Fe₂O₄ for nanoparticles. The H_c of samples is much larger than the bulk ferrites and increases with the enlarging x. The results of Zn_0.3Ni_0.7Fe₂O₄ annealed at different temperatures indicate that the maximum M_s (83.2 emu/g) appears in the sample annealed at 900 °C. The H_c of Zn_0.3Ni_0.7Fe₂O₄ firstly increases slightly as the grain size increases, and presents a maximum value of 115 Oe when the grains grow up to about 30 nm, and then declines rapidly with the grains further growing. The critical diameter (under the critical diameter, the grain is of single domain) of Zn_0.3Ni_0.7Fe₂O₄ nanoparticles is found to be about 30 nm.     

Influence of manganese substitution and annealing temperature on the formation,microstructure and magnetic properties of Mn–Zn ferrites

The effects of annealing temperature and manganese substitution on the formation, microstructure and magnetic properties of Mn_xZn_1−xFe₂O₄ (with x varying from 0.3 to 0.9) through a solid-state method have been investigated. The correlation of the microstructure and the grain size with the magnetic properties of Mn–Zn ferrite powders was also reported. X-ray diffraction (XRD), a scanning electron microscope (SEM) and a vibrating sample magnetometer (VSM) were utilized in order to study the effect of variation of manganese substitution and its impact on crystal structure, crystalline size, microstructure and magnetic properties of the ferrite powders formed. The XRD analysis showed that pure single phases of Mn–Zn ferrites were obtained by increasing the annealing temperature to 1200–1300 °C. Increasing the annealing temperature to ?1300 °C led to abnormal grain growth with inter-granular pores and this led to a decrease in the saturation magnetization. Moreover, an increase in the Mn²⁺ ion substitution up to x=0.8 increased the lattice parameter of the formed powders due to the high ionic radii of the Mn²⁺ ion. Mn–Zn ferrites phases were formed and the positions of peaks were shifted by substituting manganese. The average crystalline size was increased by increasing the annealing temperature and decreased by increasing the substitution by manganese up to 0.8. The average crystalline size was in the range 95–137.3 nm. The saturation magnetization of the Mn–Zn-substituted ferrite powders increased continuously with an increase in the Mn concentration up to 0.8 at annealing temperatures of 1200–1300 °C. Further increase of Mn substitution up to 0.9 led to a decrease of saturation magnetization. The saturation magnetization increased from 17.3 emu/g for the Mn_0.3Zn_0.7Fe₂O₄ phase particles produced to 59.08 emu/g for Mn_0.8Mn_0.2Fe₂O₄ particles.