Opposite effect of Li<Superscript>+</Superscript> codoping on the upconversion emissions of Er<Superscript>3+</Superscript>-doped TiO<Subscript>2</Subscript> powders

The Er³⁺-Li⁺ codoped TiO₂ powders have been prepared by the non-aqueous sol–gel method. The green and red upconversion emissions centered at about 526, 550 and 663 nm were observed by the ²H_11/2, ⁴S_3/2 → ⁴I_15/2 and ⁴F_9/2 → ⁴I_15/2 transitions of Er³⁺, respectively. Li⁺ codoping has opposite effect on the upconversion emissions intensities for Er³⁺-doped TiO₂ at sintering temperatures of 1,073 and 1,273 K. At 1,073 K, the Er³⁺-doped TiO₂ phase transition from anatase to rutile was accelerated with increasing Li⁺ codoping concentration, leading to the increase of crystal field symmetry of Er³⁺, thus the upconversion emissions intensities decreased. At 1,273 K, Li⁺ codoping had no effect on the phase structure of Er³⁺-doped TiO₂ and only increased the Er–O bond length, it indicated that the upconversion emissions intensities greatly enhanced because of the decrease of crystal field symmetry of Er³⁺.     

Two color up-conversion emissions of Er<Superscript>3+</Superscript>-doped Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanopowders prepared by non-aqueous sol-gel method

Er³⁺-doped Al₂O₃ nanopowders have been prepared by the non-aqueous sol-gel method using the aluminum isopropoxide as precursor, acetylacetone as a chelating agent, nitric acid as a catalyzer, and hydrated erbium nitrate as a dopant under isopropanol environment. The different phase structure, including three crystalline types of (Al, Er)₂O₃ phases, α, γ, θ, and an Er–Al–O stoichiometric compound phase, Al₁₀Er₆O₂₄, was observed for the 0.01–0.5 mol% Er³⁺-doped Al₂O₃ nanopowders at the sintering temperature of 1,000 °C. The green and red up-conversion emissions centered at about 523, 545 and 660 nm, corresponding respectively to the ²H_11/2, ⁴S_3/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 transitions of Er³⁺, were detected by a 978 nm semiconductor laser diodes excitation. With increasing Er³⁺ doping concentration from 0.01 to 0.1 mol%, the intensity of the green and red emissions increased with a decrease of the intensity ratio of the green to red emission. When the Er³⁺ doping concentration rose to 5 mol%, the intensity of the green and red emissions decreased with an increase of their intensity ratio. The maximum intensity of both the green and red emissions with the minimum of intensity ratio was obtained, respectively, for the 0.1 mol% Er³⁺-doped Al₂O₃ nanopowders composed of a single α-(Al,Er)₂O₃ phase. The intensity ratio of the green emission at 523 and 545 nm increased monotonously for all Er³⁺ doping concentrations. The two-photon absorption up-conversion process was involved in the green and red up-conversion emissions of the Er³⁺-doped Al₂O₃ nanopowders.     

Blue,green,red upconversion luminescence and optical characteristics of rare earth doped rare earth oxide and oxysulfide

The cold isostatic press pretreatment process was adopted to prepare fine rare earth oxysulfide up-conversion phosphors with spherical shape, narrow size distribution and high luminescence efficiency. The upconversion optical characteristics and brightness of the blue (Y2O2SYb,Tm), green (Y2O2S: Yb,Er), red (Y2O3Yb,Er) emitter were also investigated, and a novel method was successfully developed for the brightness measurement of upconversion luminescence (UPL). It is shown that a white color can be obtained by the appropriate mixture of these primary blue, green and red emissions components. The Er3 ions exhibit different upconversion mechanism in Y2O2S and Y2O3 host materials. The rare earth oxysulfide is an efficient upconversion matrix. The UPL brightness of Y2O2S: Yb,Er is 6.5 times higher than that of Y2O3: Yb,Er, and Y2O2S: Yb,Er shows UPL brightness of 1100 cd/m2 under 5.56 W/cm2 power density using a 980 nm laser diode.     

Upconversion properties of Er3+, Yb3+ and Tm3+ codoped fluorophosphate glasses

Er3+, Yb3+ and Tm3+ codoped fluorophosphate glasses emitting blue, green and red upconversion luminescence at 970 nm laser diode excitation were studied. It was shown that Tm3+ behaves as the sensitizer to Er3+ for the green upconversion luminescence through the energy transfer process: Tm3+:3H4+Er3+:4I 15/2-->Er3+:4I 9/2+Tm3+:3H6, and for the red upconversion luminescence through the energy transfer process: Tm3+:3F4+Er3+:4I 11/2-->Tm3+:3H6+Er3+:4F 9/2. Moreover, Er3+ acts as quenching center for the blue upconversion luminescence of Tm3+. The sensitization of Tm3+ to Er3+ depends on the concentration of Yb3+. The intensity of blue, green and red emissions can be changed by adjusting the concentrations of the three kinds of rare earth ions. This research may provide useful information for the development of high color and spatial resolution devices and white light simulation.     

Investigation of Er3+, Yb3+, Nd3+ doped yttrium calcium oxyborate for photon upconversion applications

In this work, investigation have been done on polycrystalline yttrium calcium oxyborate (YCa₄O(BO₃)₃) for the realization of existence of second harmonic generation and other photon upconversion processes as concurrent effect with the aid of Er, Yb, Nd trivalent lanthanide ions. Pure, Er:Yb co-doped and Er:Yb:Nd triply-doped YCa₄O(BO₃)₃ samples were prepared through solid state reaction and the phase identification has been done using powder X-ray diffraction spectral analysis. FTIR spectra show that the dopants increases the absorption of functional groups and modifies the lattice vibrational modes of YCa₄O(BO₃)₃. The spectral overlap of optical absorption bands of Er³⁺, Yb³⁺, Nd³⁺ ions in 840 nm–1070 nm region indicates the prospect of energy transfer between these ions. The photoluminescence spectrum of Er:Yb:Nd triply doped sample show good enhancement compared to pure and Er:Yb co-doped YCa₄O(BO₃)₃ samples. In the photon upconversion test carried out using 1064 nm Nd:YAG laser YCa₄O(BO₃)₃:Er:Yb:Nd sample produced green light with efficiency higher than the other two samples. Surface morphology of the samples was recorded using field emission scanning electron microscope and analysed. The elemental composition of the samples has been confirmed by energy dispersive X-ray spectral analysis.     

A general approach for selective enhancement of green upconversion emissions in Er3+ doped oxides by Yb3+–MoO4 2− dimer sensitizing

In this paper, we report a general approach to enhance the upconversion (UC) luminescence of Er³⁺ doped oxides phosphors by Yb³⁺–MoO₄ ^2? dimer sensitizing, which induced strong green UC emissions under the 976 nm laser diode excitation. By codoping of Yb³⁺ and Mo⁶⁺ in the Er³⁺ doped TiO₂ and ZnO, the green UC emissions intensity can be selectively increased about 10 and 500 times than those of Er³⁺–Yb³⁺ codoped TiO₂ and ZnO, respectively. The high excited state energy transfer between |²F_7/2, ³T₂> state of Yb³⁺–MoO₄ ^2? dimer and ⁴F_7/2 level of Er³⁺ significantly avoids the nonradiative decay processes happened at lower energy levels of Er³⁺, and then increases the green UC emissions efficiently. The proposed Yb³⁺–MoO₄ ^2? dimer sensitizing has been realized as an efficient way to enhance the green UC emissions in other Er³⁺ doped oxides phosphors. It is expected that the selective enhanced green UC emissions sensitized by Yb³⁺–MoO₄ ^2? dimer in Er³⁺ doped oxides phosphors can greatly extend their scope of applications.     

Study of luminescence properties of novel Er3+ single-doped and Er3+/Yb3+ co-doped tellurite glasses

The novel Er(3+) single-doped and Er(3+)/Yb(3+) co-doped tellurite glasses were prepared. The effect of Yb(2)O(3) concentration on absorption spectra, emission spectra and upconversion spectra of glasses were measured and investigated. The emission intensity, fluorescence full width at half maximum (FWHM) and upconversion luminescence of Er(3+) go up with the increasing concentration of Yb(3+) ions. The maximum FWHM of (4)I(13/2) --> (4)I(15/2) transition of Er(3+) is approximate 77 nm for 1.41 x 10(21)ions/cm(3) concentration of Yb(3+)-doped glass. The visible upconversion emissions at about 532, 546 and 659 nm, corresponding to the (2)H(11/2) --> (4)I(15/2), (4)S(3/2) --> (4)I(15/2) and (4)F(9/2) --> (4)I(15/2) transitions of Er(3+), respectively, were simultaneously observed under the excitation at 970 nm. Subsequently, the possible upconversion mechanisms and important role of Yb(3+) on the green and red emissions were discussed and compared. The results demonstrate that this kind of tellurite glass may be a potentially useful material for developing potential amplifiers and upconversion optical devices.     

Composition dependent frequency upconversion of Er/Yb-codoped lead chloride tellurite glasses

The green and red upconversion luminescence of Er³⁺ in lead chloride tellurite glasses excited at 980 nm is investigated. Three intense emission bands centered at 530, 545, and 658 nm corresponding to the transitions ⁴S_3/2→⁴I_15/2, ²H_11/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2, respectively, were simultaneously observed at room temperature. With increasing PbCl₂ content, the intensity of green (530 nm) emissions increase slightly, while the green (545 nm) and red (658 nm) emissions increase significantly. The results indicate that PbCl₂ has more influence on the green (545 nm) and red (658 nm) emissions than the green (530 nm) emission. The dependence of upconversion intensities on excitation power and possible upconversion mechanisms are discussed and evaluated.     

白光LED用Eu掺杂红色荧光粉

白光LED因亮度高、体积小、寿命长、高效节能、绿色环保等优点而引起人们的广泛关注,但是目前大部分白光LED用荧光粉的不足之处在于其发光效率较低,显色指数较差,色温较高,成本较高等等。红色荧光粉可明显改善白光LED的色温和显色指数,因此红色荧光粉在调制白光LED和改善其显色指数方面具有至关重要的作用。近年来红色荧光粉得到了深入研究,并有不少文献报道了新型的红色荧光粉。本文介绍了Eu~(3+)掺杂的线状红光发射荧光粉、Eu~(2+)掺杂的带状红光发射荧光粉并着重介绍了Eu~(2+)掺杂的新型窄带红光发射荧光粉,以及目前Eu掺杂红色荧光粉发展的不足及其改善方法。     

相位可控的氟钪纳米晶的合成及其上转换发光性能

控制反应条件如表面活性剂的组成、加入量或反应时间,可以制得不同形态、相结构且具有上转换发光(UCL)的氟钪纳米晶(NCs)。改变表面活性剂油酸(OA)/油胺(OM)的比例有利于晶体结构从立方相ScF_3∶Yb,Er转变为具有上转换发光性能增强的正交相KSc_2F_7∶Yb,Er纳米晶,而纳米晶的形态会发生从小到大的转变。改变掺杂元素的种类及含量,在980 nm光激发下,KSc_2F_7纳米晶的上转换发光可以从蓝色变到白色,再到主要发射紫色光。     

Host dependent frequency upconversion of Er3+/Yb3+-codoped bismuth-germanate glasses

The absorption and upconversion fluorescence spectra of a series of Er3+/Yb3+-codoped xBi(2)O(3)-(90-x)GeO2-10Na(2)O (BGN x, x=31, 36, 41, 46 and 51 mol%) glasses have been studied. Intense green and red emission bands at around 533, 548 and 659 nm, corresponding to the 2H(11/2)-->4I(15/2), 4S(3/2)-->4I(15/2) and 4F(9/2)-->4I(15/2) transitions of Er3+, respectively, were simultaneously observed at room temperature. The dependence of intensities of upconversion emission on excitation power and possible upconversion mechanisms were evaluated and analyzed. The important role of Bi(2)O(3) in upconversion intensity is observed and its influence on the green (533 and 548 nm) and red (659 nm) emissions is compared and discussed. The influence of Bi(2)O(3) on the upconversion emissions has been investigated based on the IR spectra.     

Controllable synthesis of β-NaYF4:Yb,Er nanorods by potassium oleate as ligand

By using potassium oleate (KOL) as a part of ligand, nanorods of β-NaYF₄:Yb,Er were synthesized. The aspect ratio of β-NaYF₄:Yb,Er nanocrystals was tuned by changing the amount of KOL. We found that potassium from KOL is not only absorbed on the surface of nanocrystals, but also partially substitutes Na element in nanocrystals lattice. Different from the classical shape control mechanism that oleate ions are absorbed on different facets of nanocrystals, the anisotropic growth of β-NaYF₄:Yb,Er in current work is caused by the doping of K⁺. The incorporation of K⁺ would not lead to obvious decrease of the upconversion fluorescence intensity. Meanwhile, oleate ions promote the phase transition of nanocrystals from cubic to hexagonal phase, resulting in the simultaneous controllability of the nanocrystals size.     

Green and red upconversion luminescence in CeO2:Er powders produced by 785 nm laser

CeO₂:Er³⁺ powders were prepared by Pechini type sol-gel method. The structural properties of CeO₂:Er³⁺ were studied by X-ray diffraction (XRD) and Fourier transform infrared (FT-IR) spectra. The results show that CeO₂:Er³⁺ has low phonon cutoff energy, which indicate that CeO₂:Er³⁺ may have high luminescent efficiency. The green and red upconverted luminescence spectra of Er³⁺ were investigated under excitation into the ⁴I_9/2 level by 785 nm laser. The upconversion mechanisms were studied in detail through laser power dependence and Er³⁺ ions concentration dependence of upconverted emissions, and results show that excited state absorption and energy transfer process are the possible mechanisms for the upconversion. The upconversion properties indicate that CeO₂:Er³⁺ may be used in upconversion phosphors.     

SrMoO4:Er3+-Yb3+ upconverting phosphor for photonic and forensic applications

The Er³⁺-Yb³⁺ codoped strontium molybdate (SrMoO₄) phosphors have been synthesized via chemical co-precipitation method by adding ammonium hydroxide as a base reagent. The phase, crystal structure and formation of spindle-like particles present in the prepared phosphors have been recognized by using the X-ray powder diffraction (XRPD) and Field emission scanning electron microscopy (FE-SEM) techniques. The Fourier transform infrared (FTIR) spectroscopy of the developed phosphors has been analyzed to mark the different functional groups present in synthesized phosphors. The multicolour upconversion emissions observed upon excitation with 980 nm and 808 nm laser diode have been explained on the basis of dopants ions concentration, pump power dependence, energy level structure and decay curve analysis. The colour co-ordinate study confirmed that the codoped phosphor emits non-tunable green colour when excited with the 980 nm laser diode, whereas it shows the colour tunability from yellow to green region upon excitation with the 808 nm laser diode. The applicability of non-tunable green colour emission has been demonstrated in the security ink and latent finger print detection. This shows the utility of the developed phosphors in the photonic and forensic applications.     

Microwave synthesis and photoluminescent properties of Sr2CeO4/Ln3+ (Ln = Er, Ho, Tm)

Sr₂CeO₄/Ln³⁺ (Ln = Er, Ho, Tm) phosphors were synthesized with the microwave radiation method for the first time. The luminescent properties of the samples were investigated and the up-conversion luminescence of Er³⁺, Ho³⁺ and Tm³⁺ doped Sr₂CeO₄ phosphors was observed. The spectra indicate that the energy transfer takes place from the triplet excited state of MLCT (metal-to-ligand charge transfer) state for Sr₂CeO₄ (sensitizer) to the rare earth ions (activator). __________ Translated from Journal of Hebei Normal University (Natural Science Edition), 2007, 31(2): 212–216 [译自: 河北师范大学学报 (自然科学版)]     

Strong up-conversion emissions in ZnO:Er3+, ZnO:Er(3+)-Yb3+ nanoparticles and their surface modified counterparts

ZnO:Er(3+) and ZnO:Er(3+)-Yb(3+) nanoparticles (NPs) are fabricated by a sol-gel method, afterwards parts of which are separated and surface modified in Mo(NO(3))(3) solution. Analyses on phase and structure based on X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) techniques indicate that Er(3+) and Yb(3+) are incorporated into the ZnO lattice successfully and after Mo treatment, a thin layer of MoO(3) forms on the NPs surface, forming core/shell structures. Raman scattering spectra reveal the existence of ZnMoO(4) in the shell part. Visible up-conversion (UC) is observed in all the samples, with Mo treated and untreated ZnO:Er(3+) emitting dominant but relatively weak red light, corresponding to (4)F(9/2)-(4)I(15/2) transition of Er(3+). In Yb(3+)-codoping systems, the integral UC intensity is enhanced obviously though red emission still dominates the UC spectra before surface modification. In the Mo treated system, ZnO:Er(3+)-Yb(3+)/MoO(3), green emission is increased while the red is suppressed in comparison to ZnO:Er(3+)-Yb(3+), with the intensity of green to red ratio (GRR) changing from 0.25 to 8. A novel phenomenon is discovered that the green emissions in our samples involve three-photon processes.     

Nanocrystalline Ce0.8EuyR0.2 ? yO2 ? δ (R = Yb, Er) solid solutions: Synthesis by homogeneous hydrolysis method

Nanocrystalline (<5 nm) quasi-ternary ceria-based solid solutions doped with REE (Er, Eu, Y) in various concentrations (5–20 mol %) were prepared by homogeneous hydrolysis in the presence of hexamethylenetetramine (HMTA). Physicochemical characteristics of Ce_0.8Eu _y R_{0.2 − y} O_{2 - δ} (R = Er, Yb) solid solutions were analyzed.     

Comparative investigation on structure and luminescence properties of fluoride phosphors codoped with Er/Yb

This paper reports on comparative investigation of structure and luminescence properties of tetragonal LiYF₄ and BaYF₅, and hexagonal NaYF₄ phosphors codoped with Er³⁺/Yb³⁺ by a facile hydrothermal synthesis. The products were characterized by X-ray diffractometer, scanning electron microscope, and photoluminescence spectroscopy. Intense visible emissions centered at around 525, 550 and 650 nm, originated from the transitions of ²H_11/2 → ⁴I_15/2, ⁴S_3/2 → ⁴I_15/2, and ⁴F_9/2 → ⁴I_15/2 of Er³⁺, respectively, have been observed in all the samples upon excitation with a 980 nm laser diode, and the involved mechanisms have been explained. Based on the green up-conversion emission performance, the Yb³⁺ concentrations of Er³⁺/Yb³⁺-codoped LiYF₄, BaYF₅, and NaYF₄ phosphors have been optimized to be 10, 20, and 20 mol.%, respectively. The quadratic dependence of fluorescence on excitation laser power has confirmed that two-photon contribute to up-conversion of the green–red emissions.     

Investigation on the upconversion luminescence of Sr3AlO4F:Yb3+, Er3+, Ho3+ phosphors

To develop new emission-tunable upconversion (UC) phosphors, the Sr₃AlO₄F:5%Yb³⁺, xEr³⁺, yHo³⁺ (0 ≤ x ≤ 1%, 0 ≤ y ≤ 1%) samples were prepared by conversional solid-state reaction method, and their luminescence properties upon 980 nm excitation were studied. Upon 980 nm excitation, Yb³⁺-Er³⁺ codoped Sr₃AlO₄F shows a predominant emission peak between 645 and 700 nm which is attributed to the ⁴F_9/2-⁴I_15/2 transition of Er³⁺, and the Er³⁺ green emissions have been almost quenched. In this case, the yellowish green emitting light is obtained. The possible reason was interpreted by the energy level diagram and the proposed UC mechanism. For Yb³⁺-Ho³⁺ codoped Sr₃AlO₄F, three emissions are observed obviously which are all derived from the Ho³⁺ ion. The corresponding chromaticity coordinates indicate a red emission has been gained. To realize the tunable emission, the typical Sr₃AlO₄F:5%Yb³⁺, 0.2%Er³⁺, 1%Ho³⁺ phosphor was developed, and its emission spectrum includes the emission peaks of both Er³⁺ and Ho³⁺. Correspondingly, the sample gives a yellow emission.     

Strong up conversion photoluminescence in Er3+ doped Bi4Ti3O12 ferroelectric materials prepared by sol–gel method

Bi₄Ti₃O₁₂ (BTO) doped with different concentrations of Er³⁺ was prepared using sol–gel method. Their structures and surface morphology were examined by X-ray diffraction, Raman spectroscopy and scanning electron microscopy, respectively. All XRD peaks can be indexed according to orthorhombic BTO phase, which is consistent with Raman measurement results. Strong upconversion green luminescence is observed in the Er³⁺ doped BTO powders pumped by 980 nm at room temperature. Three upconversion emission bands centered at about 525, 550 and 662 nm are due to the radiative relaxation of Er³⁺ from ²H_11/2, ⁴S_3/2 and ⁴F_9/2 to the ground level ⁴I_15/2, respectively. The upconversion emission mechanism of the samples were identified and analyzed. In addition, the doped BTO ceramics show obvious hysteresis loops, demonstrating the ferroelectric properties of the samples. These results illustrate the potential of this class of materials for photonic applications in optoelectronics devices.