含硅芳炔树脂/苯并噁嗪/氰酸酯三元聚合体系研究

以双酚A型氰酸酯(BADCy)和含炔丙氧基苯并噁嗪(P-appe)为改性剂,通过与含硅芳炔树脂(PSA)的溶液混合与浓缩制备了含硅芳炔树脂/氰酸酯/苯并噁嗪三元共混体系(PPB),研究了该共混体系的热固化过程、共混树脂的热稳定性和动态力学性能、弯曲性能和冲击性能.结果表明,开环后的苯并噁嗪能催化氰酸酯的环三聚反应,可降低氰酸酯的固化温度;PPB热固化中三嗪环可与噁嗪环反应形成氰酸酯与苯并噁嗪共聚;当PPB树脂中PSA树脂的质量分数为70%时,三元共混树脂浇铸体在氮气中质量损失5%的温度(Td5)高于500oC,玻璃化转变温度高于450oC;BADCy/P-appe改性PSA树脂的三元共混体系相容性好,共混树脂浇铸体PPB-5的弯曲强度较PSA树脂提高了115%,冲击强度提升了104%,断裂面出现明显的韧性断裂特征.     

对炔丙氧基苯基噁唑啉的合成及改性苯并噁嗪树脂的研究

通过四步法合成了对炔丙氧基苯基噁唑啉(p-propynyloxyphenyl-2-oxazoline简称POPO),采用核磁共振氢谱(1H-NMR)、傅立叶红外光谱(FTIR)、气相色谱质谱联用仪(GC-MS)和元素分析证实了其分子结构,以示差扫描量热仪(DSC)和热重分析(TGA)揭示了其固化行为和热分解性质,该化合物熔点为120℃,起始固化温度为200℃,固化峰值温度为280℃,自固化产物5 wt%热失重温度为321℃.在此基础上,通过溶液共混法制备了双酚A型苯并噁嗪(BZ)/对炔丙氧基苯基噁唑啉(POPO)共聚树脂,且对其固化机理、固化产物的热分解性质和动态力学性能进行考察.结果表明,该噁唑啉作为交联剂,与苯并噁嗪发生开环聚合和自身炔基发生三聚成环反应,使固化产物的交联密度增加,DSC、TG和动态热机械分析(DMA)表明噁唑啉的引入提高了固化树脂的热性能和动态力学性能.且在噁唑啉含量为10 wt%时,固化树脂的综合性能较优,较之纯的双酚A型苯并噁嗪树脂,起始固化温度从215℃降低至180℃,残碳率从28%提高至44%,玻璃化转变温度从166℃提高至186℃.     

双官能度手性和消旋苯并噁嗪的合成及热性能研究

采用无溶剂法合成了新型双酚A和双酚AF(六氟双酚A)基手性和消旋苯并噁嗪单体,利用红外光谱(FTIR)、核磁共振氢谱(1H-NMR)、旋光仪和高效液相色谱(HPLC)对单体结构和性质进行了表征,通过差式扫描量热仪(DSC)和热重分析仪(TGA)对苯并噁嗪的固化行为及聚合物的热性能进行了研究.结果表明,无溶剂法合成苯并噁嗪单体具有反应速度快、产率高、对环境友好等特点;双官能度消旋苯并噁嗪单体由内消旋和外消旋异构体组成,且内消旋苯并噁嗪单体含量高于外消旋;手性和消旋苯并噁嗪单体具有相同的开环聚合行为;由于消旋苯并噁嗪分子的立体构型不同,使得聚苯并噁嗪的自由体积减小,分子链的堆积更加致密,因而消旋聚苯并噁嗪的玻璃化转变温度(Tg)和热稳定性均高于手性聚苯并噁嗪和传统的双酚A-苯胺型聚苯并噁嗪;此外,C—F键具有高的解离能,因而双酚AF基聚苯并噁嗪的热性能显著提高.     

3-甲基邻苯二酚/糠胺型聚苯并噁嗪的制备与性能

通过分子设计合成了含有酚羟基的3-甲基邻苯二酚/糠胺型苯并噁嗪(M-f). 通过差示扫描量热法(DSC)测得M-f的放热峰值温度(T_p)为172 ℃, 而间甲酚/糠胺型苯并噁嗪(MC-f)的T_p为244 ℃, 表明酚羟基的引入有利于降低苯并噁嗪的开环固化温度. 通过非等温DSC法研究2种苯并噁嗪单体的固化动力学, Kissinger法和Ozawa法的计算结果均表明M-f的表观活化能低于MC-f. 此外, 通过拉伸剪切强度测试考察了聚苯并噁嗪对于金属基材的黏附性能, M-f聚合物对于铝和低碳钢基材的拉伸剪切强度分别为2.53 MPa和3.09 MPa, 均高于MC-f聚合物.     

含烯丙基的三元酚型苯并噁嗪的合成及性能

以合成的1,3,5-三(p-羟基苯基)苯(TP)、烯丙基胺和甲醛为原料,合成了一种新型的含烯丙基的三元酚型苯并噁嗪单体——1,3,5-三(3-烯丙基-3,4-二氢-2H-1,3-苯并噁嗪基)苯(tp-ala).采用核磁共振谱、傅里叶变换红外光谱、紫外-可见吸收光谱和差示扫描量热表征了tp-ala的结构和固化行为,用热失重分析、动态热机械分析和荧光光谱测试了固化物P-tp-ala的热性能及光学性能.结果表明,烯丙基的引入使P-tp-ala玻璃化转变温度高达322℃,5%的热失重温度为351℃,800℃残炭率达到61.4%,与不含烯丙基的三元酚型苯并噁嗪相比具有较好的耐热性.在233 nm激发波长下,P-tp-ala的荧光发射波长为350 nm,具有荧光性能.由于P-tp-ala中的芳香含量高,使其折射率高达1.6325,在防折射涂层方面有很好的应用潜力.     

基于乙炔基-苯并噁嗪单元双重交联反应的聚酰亚胺树脂的制备与性能

为开发可低温固化的聚酰亚胺树脂, 通过分子结构设计将苯并噁嗪单元引入聚酰亚胺树脂中, 合成了含苯并噁嗪单元及乙炔基封端的双官能化新型聚酰亚胺预聚体(PIBzA). 经高温处理, 苯并噁嗪单元发生开环交联, 同时, 乙炔基端基发生三聚成环反应, 从而在固化树脂中形成双重交联网络结构. 苯并噁嗪单元的引入使聚酰亚胺树脂最快固化反应温度降低约32 ℃, 有效降低了固化温度. 同时, 苯并噁嗪单元的引入未大幅度降低树脂的耐热稳定性, 其玻璃化转变温度(T_g)介于266~290 ℃之间, 5%热失重温度(T_d,5%)接近500 ℃, 依然可以满足耐高温复合材料的应用需求. 此外, PIBzA固化树脂具有低介电特性, 其介电常数k介于2.3~3.0, 介电损耗介于0.002~0.008, 可满足透波复合材料及先进微电子封装材料的应用需求.     

聚苯并噁嗪高性能化:分子设计、合金与纳米复合物

聚苯并噁嗪通过环状苯并噁嗪单体热诱导开环聚合得到,作为一种新型的酚醛树脂,不仅具有传统酚醛树脂的耐热、低吸水性等性质,还具有传统酚醛树脂不具备的性能,如分子设计的灵活性、固化反应没有小分子副产物产生、优异的尺寸稳定性以及良好的阻燃性能,在微电子、印刷电路板、电子封装以及航空航天等高技术领域具有广阔的应用前景.然而,聚苯并噁嗪缺点是固化温度高、固化材料脆性大.本文介绍了聚苯并噁嗪性能增强的各种方法,包括新型单体分子设计、引入可交联单元、高相对分子质量聚合物前体制备、聚合物合金化、纳米复合等.最近,石墨烯和笼型聚倍半硅氧烷(POSS)与聚苯并噁嗪复合材料因具有优异的热性能和电学性能,成为先进电子材料的潜力材料.     

芴基苯并噁嗪单体的合成、固化动力学及热性能

以芴、苯酚、对甲氧基苯酚和多聚甲醛为原料,采用溶液法合成了直接在芴的苯环结构上进行修饰的2个新型芴基苯并噁嗪单体3-芴基-3,4-二氢-1,3-苯并噁嗪(FBZ-1)和3-芴基-6-甲氧基-3,4-二氢-1,3-苯并噁嗪(FBZ-2)。利用FT-IR,~1H NMR和~(13)C NMR对其结构进行了表征。采用示差扫描量热法(DSC)研究了2个单体的固化动力学,计算了固化反应活化能,确定了最佳固化温度。通过DSC和热重(TGA)分析了单体及其聚合物的热性能。结果表明,FBZ-1和FBZ-2呈现出典型的热开环固化特征,放热峰顶温度(5℃·min~(-1)的升温速率)分别为231.2℃,228.7℃,其聚合物初始热分解温度(热失重5%时)达290℃、299℃;850℃时的残炭率(Yc)达到40.9%和36.9%,极限氧指数(LOI)分别是33.86、32.26。     

含双螺环三聚磷腈单元的苯并噁嗪树脂的结构和热稳定性

以双螺环取代三聚磷腈基双苯甲酰氯和4-氨基(N-苯基)苯并噁嗪单体为原料合成了一种含双螺环取代三聚磷腈结构单元的苯并噁嗪树脂单体(HCP-5);采用傅立叶变换红外光谱仪(FT-IR)和核磁共振谱仪(1 H NMR,13 C NMR,31P NMR)表征了苯并噁嗪树脂单体的结构,基于FT-IR和示差扫描量热法研究了其固化行为,并利用热重分析和示差热重分析研究了HCP-5树脂单体、均聚物及其与双酚A型苯并噁嗪树脂(Bz)共聚物的热稳定性.结果表明,HCP-5均聚物具有很好的热稳定性和成炭性,其在317℃下的热失重为5%,在800℃下的残炭率为50%,可用于普通苯并噁嗪树脂改性.此外,HCP-5/Bz(1∶1;质量分数)共聚物在332℃下的热失重为5%,在800℃下的残炭率为48%.     

含氟苯并噁嗪-含硅芳炔改性树脂的制备与性能

采用溶剂法合成了一系列带有活性基团的含氟苯并噁嗪(烯丙基含氟苯并噁嗪(BOZF-1)、苯乙炔基含氟苯并噁嗪(BOZF-2)和炔丙基含氟苯并噁嗪(BOZF-3)),并将其与含硅芳炔树脂(PSA)进行共混改性,研究不同氟苯并噁嗪(BOZF)的结构与质量分数对改性树脂性能的影响.采用差示扫描量热法(DSC)研究BOZF/PS...     

Ab-initio study of electronic,optical, thermal,and transport properties of Cr4AlB6

Theoretical investigation of different physical parameters of Cr₄AlB₆ have been done within the framework of density functional theory. Cr₄AlB₆ is a no band gap material. Its Cr-3d states contributes the most at the Fermi level. Thermal properties are investigated using quasi-harmonic Debye model as implemented in Gibbs code for different values of pressure and temperature. Study of transport property suggests that its electrical conductivity increases nonlinearly with increase in temperature but the relative change in its value is very low whereas its thermal conductivity increases linearly with the increase in temperature and relative increase in thermal conductivity is very high. The behavior of Cr₄AlB₆ is anisotropic and property is ceramic. It has potential applications in making ceramic capacitors. Its reflectivity is high in low energy region. It suggests that material can be used as coating material for far-infrared radiation. Study of the transport property suggests that because of very high value of thermal conductivity, it can be used for heat sink applications.     

Thermal,structural and electrical properties

The chloro compound of 3-hydroxy-2-quinoxalinecarboxylic acid with nickel(II) has been prepared in ethanolic solution from which a solid compound was isolated. Spectral and magnetic measurements show that the nickel ions are in an octahedral environment. Thermogravimetry, differential thermal analysis and electrical conductivity data are reported for 3-hydroxy-2-quinoxalinecarboxylic acid and its nickel complex. The conductivity measurements indicate that electron/hole traps are emptied during heating of the complex but repopulation occurs in about 24 h at room temperature.     

Reliability of flexible electrically conductive adhesives

Based on our previous work about electrically conductive adhesives (ECAs), a flexibilizer named 1,3‐propanediol bis (4‐aminobenzoate) was used to fabricate flexible ECAs (FECAs). ECAs, FECAs, and electronic devices connected by them were carried out the hot and humid aging test under constant humidity level of 85% relative humidity at 85 °C for 600 h. After aging, the bulk resistance change of ECAs was about 26%, that of FECAs was a little higher, about 29%. The contact resistance change of devices connected by ECAs and FECAs was very great, about 450% and 410%, respectively. The bonding area at connection interface between colloids and devices had delamination, even cracks. The delamination of ECAs was calculated about 60%, the average shear strength of ECAs was reduced about 45%, and those of FECAs were about 50% and 30%, respectively, so FECAs had a higher bonding stability in hot and humid environment. Copyright © 2012 John Wiley & Sons, Ltd.     

Assimilation of manganese metal ion doped hydroxyapatite by Co-Precipitation technique

Calcium phosphate mineral [HAp] is a vital ingredient in orthopaedics, dental and hard tissue applications in mammals. Since it can absorb a large number of impurities, the doped HAp has the potential for biomedical applications using its physical and structural properties. In this research, the Mn-doped HAp in which x calcium atoms are replaced by Mn (Ca_10-x Mn_x (PO₄)₆(OH)₂ where x = 0.2, 0.4, 0.6, 0.8 mol) is obtained by the co-precipitation method. The physical properties of Mn-doped HAp, such as average crystallite size and degree of crystalline, are determined through XRD studies. The peaks corresponding to the functional groups PO4^3?, CO, and OH of the samples are identified by FTIR studies. The impedance spectroscopy method helps in the investigation of electrical conductivity, and dielectric loss in the impedance spectra for various doping concentrations. The average molar ratio of HApMn is determined with the help of EDX. It was found that there is a decrease in the degrees of crystallization with the doping element concentration (Mn) in all the samples. The diffraction (hkl) indices are confirmed from the selected area electron diffraction (SAED) rings, and the morphological study of the samples using TEM confirms the shape as a rod-like structure. To conclude, the variation in the characteristics of HAp relies on the doping concentration of Mn.     

Typical superparamagnetism with improved electrical properties of nano modified bismuth ferrite multiferroic composites

Multiferroic composites with the chemical formula, (0.5) BiFeO₃ + (0.5) Ni_0.5Zn_0.5Fe₂O₄, in bulk and nano forms were synthesized by preparing bismuth ferrite (BiFeO₃ or BFO) in bulk (B) and nano (N) forms and nickel zinc ferrite (Ni_0.5Zn_0.5Fe₂O₄or NZFO) in nano form. Single phase BFO was synthesized using conventional solid-state reaction as well as sol-gel autocombustion methods and NZFO powders were prepared by using sol-gel autocombustion method, respectively. X-ray diffraction (XRD) studies reveal the existence of rhombohedrally distorted perovskite structure for BFO and cubic spinel phase for NZFO in single phase as well as composite samples. Microstructural studies and energy dispersive spectroscopy (EDS) data reveal the formation of grains, intergranular porosities and chemical purity of the synthesized samples. Dielectric and AC conductivity measurements confirm the existence of space charge polarization along with the small polaron model in these composites. Ferroelectric and magnetic studies show that there was a considerable enhancement in the ferroelectric and magnetic orders for the nano form of the BFO (N) + NZFO composite. The observed remnant polarization values 2.80388 & 7.75901 μC/cm², saturation magnetization values 37.96072 & 40.47491emu/gm for bulk BFO (B) + NZFO and nano BFO (N) + NZFO composites, respectively. Interestingly, both the samples exhibit superparamagnetic behaviour at room temperature with coercivities close to zero. This typical behaviour is attributed to the corresponding anisotropic contributions originated from the individual constituents. The observed variations in BFO (N) + NZFO sample attributed to the corresponding structural modifications brought about by the variations due to its size effect in the present work.     

Tetrametallic macrocyclic frameworks constructed from ferrocenedicarboxylato and 2,2-bipyridine: synthesis, molecular structures and characteristics

Four novel tetranuclear macrocyclic compounds [Cd₂(η²-O₂CFcCO₂)₂(2,2^′-bpy)₂(H₂O)₂] · 2H₂O (1), [Zn₂(η²-O₂CFcCO₂)₂(2,2^′-bpy)₂(H₂O)₂] · CH₃OH · H₂O (2), [Co₂(O₂CFcCO₂)₂(2,2^′-bpy)₂(μ₂-OH₂)₂] · CH₃OH · 2H₂O (3), and [Ni₂(O₂CFcCO₂)₂(2,2^′-bpy)₂(μ₂-OH₂)₂] · CH₃OH · 2H₂O (Fc=(η⁵-C₅H₄)Fe(η⁵-C₅H₄) (4) have been synthesized and structurally characterized by single crystal diffraction. The magnetic behaviors for compounds (3) and (4) are studied in the temperature range of 5.0-300 K. The results show that the antiferromagnetic coupling of Co^II-Co^II pairs occurs in (3), and unusual global ferromagnetic coupling between nickel (II) ions exists in (4). The solution-state differential pulse voltammetries of compounds (1)-(4) all show two peaks with large separations (ΔE) that indicate strong interactions between two ferrocene moieties. Their fluorescent and thermal properties were also investigated.