Solubility in the Na2Cr2O7-(NH4)2Cr2O7-K2Cr2O7-H2O system

Solubility in the Na₂Cr₂O₇-(NH₄)₂Cr₂O₇-K₂Cr₂O₇-H₂O four-component water-salt system at 25, 50, and 75°C was studied for the first time. Phase field boundaries for individual salts and potassium and ammonium dichromate solid solutions, monovariant lines, and invariant points were determined. Experimental data were used to optimize the looped isohydric process of potassium dichromate preparation involving additional salts.     

Polymorphism in the Sc2Si2O7-Y2Si2O7 system

This paper examines the structural changes with temperature and composition in the Sc₂Si₂O₇-Y₂Si₂O₇ system; members of this system are expected to form in the intergranular region of Si₃N₄ and SiC structural ceramics when sintered with the aid of Y₂O₃ and Sc₂O₃ mixtures. A set of different compositions have been synthesized using the sol-gel method to obtain a xerogel, which has been calcined at temperatures between 1300 and 1750 °C during different times. The temperature-composition diagram of the system, obtained from powder XRD data, is dominated by the β-RE₂Si₂O₇ polymorph, with γ-RE₂Si₂O₇ and δ-RE₂Si₂O₇ showing very reduced stability fields. Isotherms at 1300 and 1600 °C have been analysed in detail to evaluate the solid solubility of the components. Although, the XRD data show a complete solid solubility of β-Sc₂Si₂O₇ in β-Y₂Si₂O₇ at 1300 °C, the ²⁹Si MAS-NMR spectra indicate a local structural change at x ca. 1.15 (Sc_2−xY_xSi₂O₇) related to the configuration of the Si tetrahedron, which does not affect the long-range order of the β-RE₂Si₂O₇ structure. Finally, it is interesting to note that, although Sc₂Si₂O₇ shows a unique stable polymorph (β), Sc³⁺ is able to replace Y³⁺ in γ-Y₂Si₂O₇ in the compositional range 1.86?x?2 (where x is Sc_2−xY_xSi₂O₇) as well as in δ-Y₂Si₂O₇ for compositions much closer to the pure Y₂Si₂O₇.     

KCl-KBO2-K2CO3, K2MoO4-KBO2-K2CO3, and K2WO4-KBO2-K2CO3 ternary systems

phase diagrams of KCl-KBO₂-K₂CO₃, K₂MoO₄-KBO₂-K₂CO₃, and K₂WO₄-KBO₂-K₂CO₃ ternary systems were studied by a calculation-experimental method and differential thermal analysis (DTA). The coordinates of ternary eutectics were determined to be E ₁: 622°C, 8.5 mol % KBO₂, 56.5 mol % KCl, and 35 mol % K₂CO₃; E ₂: 710°C, 23 mol % KBO₂, 43 mol % K₂CO₃, and 34 mol % K₂MoO₄; E ₃: 710°C, 23 mol % KBO₂, 43 mol % K₂CO₃, and 34 mol % K₂WO₄. The specific heats of melting of the eutectics were determined.     

Interaction in the Ga2S3-Y2O2S system

The phase diagram of the Ga₂S₃-Y₂O₂S system has been investigated by differential thermal, X-ray powder diffraction, microstructural, and thermodynamic analyses. It has been established that the system is eutectic, and solubility at 295 K from the Ga₂S₃ side reaches 3 mol % Y₂O₂S. The coordinates of the eutectic point are 14 mol % Y₂O₂S and 1320 K.     

Some studies on the solid solutions in the systems Sr2Nb2O7Eu2Nb2O7 and Sr2Ta2O7Eu2Ta2O7

Preparation of new solid solutions containing divalent europium have been tried in the systems Eu₂Nb₂O₇Sr₂Nb₂O₇ and Eu₂Ta₂O₇Sr₂Ta₂O₇. These solid solutions described as Eu_2xSr_2(1?x)M₂O₇ (M = Nb and Ta) exist in a pure orthorhombic phase in a limited region of x from 0 to about 0.5. The compounds with compositions close to Eu₂M₂O₇ exist but techniques have not been found to prepare them in pure form.     

The preparation of NbH5(Me2PCH2CH2Me2)2 and NbHL2(Me2PCH2CH2PMe2)2 (L = CO or C2H4)

MMe₅(dmpe) (M = Nb or Ta, dmpe = Me₂PCH₂CH₂PMe₂) reacts with H₂ (500 atm) and dmpe in THF at 60°C to give MH₅(dmpe)_2? NbH₅(dmpe)₂ readily reacts with two mol of CO or ethylene (L) to give NbHL₂(dmpe)₂. The exchange of the hydride ligand with the ethylene protons in NbH(C₂H₄)₂(dmpe)₂ is not rapid on the ¹H NMR time scale (60 MHz) at 95°C.     

Phase equilibria and glass formation in the As2S3-TlAs2S2Se2 section of the As2S3-As2Se3-TlS system

Alloys in the As₂S₃-TlAs₂S₂Se₂ section of the As₂S₃-As₂Se₃-TlS ternary system were studied and a phase diagram was constructed using physicochemical methods (differential thermal analysis, microstructural analysis, X-ray powder diffraction, also microhardness and density measurements). The diagram in the As₂S₃-TlAs₂S₂Se₂ section is a non-quasi-binary diagonal section of the As₂S₃-As₂Se₃-TlSe quasi-ternary system. It was found that all the alloys in the section under ordinary conditions are obtained in the vitreous state. At low As₂S₃ concentrations in the section, solid solutions form up to 2.5 mol %, and at low TlAs₂S₂Se₂ concentrations, their extent is 3 mol %.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

High-temperature equilibria and critical phenomena in the Na2CO3-NaCl-H2O and Na2CO3-Na2WO4-H2O systems

Phase equilibria in the Na₂CO₃-NaCl-H₂O and Na₂CO₃-Na₂WO₄-H₂O ternary systems formed by type 1 salts (NaCl, Na₂WO₄) and a type 2 salt (Na₂CO₃) were experimentally studied at temperatures from 425 to 500°C and pressures from 30 to 160 MPa with the contents of type 1 salts from 10 to 30 wt %. Transition from supercritical homogeneous fluid equilibria of the Na₂CO₃-H₂O system to heterogeneous equilibria of the title ternary systems was studied in the presence or absence of liquid phase immiscibility in the type 1 subsystems.     

NaBO2-NaCl-Na2CO3, NaBO2- Na2CO3-NaMoO4, NaBO2- Na2CO3-NaWO4, and NaBO2-NaCl-Na2WO4 ternary systems

The phase diagrams of the NaBO₂-NaCl-Na₂CO₃, NaBO₂-Na₂CO₃-Na₂MoO₄, NaBO₂- Na₂CO₃-Na₂WO₄, and NaBO₂-NaCl-Na₂WO₄ ternary systems were studied by a calculation-experimental method and differential thermal analysis. The coordinates of ternary eutectics were determined: E ₁: 612°C, 16 mol % NaBO₂, 42 mol % NaCl, and 42 mol % Na₂CO₃; E ₂: 568°C, 12 mol % NaBO₂, 28 mol % Na₂CO₃, and 60 mol % Na₂MoO₄; E ₃: 575°C, 12 mol % NaBO₂, 32 mol % Na₂CO₃, and 56 mol % Na₂WO₄; E ₄: 628°C, 8 mol % NaBO₂, 20 mol % NaCl, and 72 mol % Na₂WO₄; and E ₅: 655°C, 9 mol % NaBO₂, 53 mol % NaCl, and 38 mol % Na₂WO₄.     

Li2SO4-Na2SO4-H2O和Li2SO4- K2SO4-H2O溶液的体积性质

本文用高精度数字式振荡管密度计测定了288K至318K温度范围内Li₂SO₄ + Na₂SO₄ + H₂O和 Li₂SO₄ + K₂SO₄ + H₂O三元体系的密度。混合溶液的离子强度范围从0.1到4.5 mol.kg_–1,混合溶液中Na₂SO₄和K₂SO₄的离子强度分数为0.2,0.4,0.6和0.8。用密度实验值拟合得到了不同温度下Pitzer离子相互作用模型混合参数θ_V和 ψ_V,模型的计算值与实验值的偏差在±0.002 g.cm_–3以内。用Pitzer模型计算了不同离子强度下三元体系的混合体积。     

(H2NC4H8NCH2CH2NH2)(HNCH2CH2NH2)3Zn2Ge2Se8: A new,templated one-dimensional ternary semiconductor stabilized by mixed organic cations

The novel, 1D semiconductor (H₂NC₄H₈NCH₂CH₂NH₂)(HNCH₂CH₂NH₂)₃Zn₂Ge₂Se₈ has been synthesized under solvothermal conditions using N-(2-aminoethyl)piperazine as solvent and templating agent at 200 °C. The material was characterized by single crystal and powder X-ray diffraction, IR and Raman spectroscopy and thermogravimetric analysis. The compound consists of 1D anionic [Zn₂Ge₂Se₈]⁴⁻ chains made of alternating edge-shared [ZnSe₄] and [GeSe₄] tetrahedra that charged balanced by one N-(2-aminoethyl)piperazinium and three piperazinium cations. The optical properties were investigated with solid state UV–Vis/near IR spectroscopy and the results show that the solid is a medium gap semiconductor with an absorption edge at 1.8 eV.     

CaF2对CaO-CaF2-B2O3-SiO2：Sm2O3玻璃的光致发光增强效应

用高温熔融法制备了掺杂Sm₂O₃的CaO-CaF₂-B₂O₃-SiO₂(CFBS:Sm)发光玻璃材料, 并借助X射线衍射(XRD)谱、傅里叶变换红外(FTIR)光谱以及光致发光(PL)光谱等分析手段研究了玻璃基体中CaF₂的摩尔分数及其结构、红外透过性能以及荧光性能的关系. XRD和FTIR测试表明, 玻璃基体中引入CaF₂并未引起非晶结构的变化但其红外透过峰发生移动. 光谱学测试表明, CFBS:Sm发光玻璃在404 nm波长激发下出现对应于Sm³⁺离子位于566、603和650 nm的特征荧光峰, 其发光颜色为橙红色(x=0.531, y=0.371). 此外, 随着玻璃基体中CaF₂摩尔分数的增加, CFBS:Sm发光玻璃的荧光发射强度、荧光寿命(Sm³⁺的⁴G_5/2能级)和荧光量子效率也表现出增大的趋势. 这种CFBS:Sm发光玻璃中荧光发射强度和荧光寿命的提高主要是由于玻璃基体中的CaF₂替代CaO引起基体相互作用和声子能量降低、无辐射跃迁减弱造成的.     

Synthesis and characterization of inorganic solid electrolytes of Li2O-SiO2-P2O5 and Li2O-TiO2-SiO2-P2O5 systems

The lithium-ion-conducting inorganic solid electrolytes in the oxide systems Li₂O-SiO₂-P₂O₅ and Li₂O-TiO₂-SiO₂-P₂O₅ were prepared by the solid-state reaction, and the electrolyte pellet made by cold-pressing method had diameter of 13 mm and was about 1 mm thick. Phase identification and surface morphology of the products were carried out by X-ray diffraction and scanning electron microscopy. Ionic conductivity of the pellets was investigated through ac impedance. The results show that the adding of other cations can improve the ionic conductivity of the solid electrolyte, and the sintering temperature and duration can influence the ionic conductivity. The maximum ionic conductivity in the samples is 9.9 × 10⁻⁴ S/cm in the Li₂O-TiO₂-SiO₂-P₂O₅ system. Original Russian Text ? W. Li, M. Wang, Z.H. Li, X.F. Shang, H. Wang, Y.W. Wang, Y.B. Xu, 2007, published in Elektrokhimiya, 2007, Vol. 43, No. 11, pp. 1341–1345.     

Ag2Se-Tl2Se-Bi2Se3 quasi-ternary system

The Ag₂Se-Tl₂Se-Bi₂Se₃ quasi-ternary system (system A) was studied using DTA, X-ray powder diffraction, microstructure examination, and microhardness measurements. TlBiSe₂-AgBiSe₂, AgTlSe-AgBiSe₂, AgTlSe-Bi₂Se₃, and Tl₂Se-AgBiSe₂ polytherms, isothermal sections at 500 and 800 K, and liquidus surface projection of system A were constructed. System A is congruently triangulated into the following subordinate triangles: Tl₂Se-AgTlSe-Tl₉BiSe₆ (I), AgTlSe-Tl₉BiSe₆-TlBiSe₂ (II), Ag₂Se-AgTlSe-TlBiSe₂ (III), Ag₂Se-AgBiSe₂-TlBiSe₂ (IV), and AgBiSe₂-TlBiSe₂-Bi₂Se₃ (V). Subsystems I, III, and V are ternary systems with three-phase eutectic equilibrium; system II has a three-phase eutectic, and system IV is characterized by several invariant and monovariant peritectic and eutectic equilibria. Primary crystallization and homogeneity fields were outlined, and the types and coordinates of invariant and monovariant equilibria in system A were determined. A characteristic feature of the title system is an extensive field of solid solutions between high-temperature cubic AgBiSe₂ and TlBiSe₂ phases; this field lies as a continuous belt along the AgBiSe₂-TlBiSe₂ quasibinary section and covers about one-fourth of the surface area of the triangular diagram of system A.     

Tl2S-Sb2S3-Bi2S3 quasi-ternary system

The Tl₂S-Sb₂S₃-Bi₂S₃ quasi-ternary system (system A) was studied using DTA, X- ray powder diffraction, microstructure examination, and microhardness measurements. TlSbS₂-Tl₄Bi₂S₅(TlBiS₂, Bi₂S₃), Sb₂S₃-TlBiS₂, Tl₃SbS₃-TlBiS₂(Bi₂S₃), and [TlSb_0.5Bi_0.5S₂]-Tl₂S isopleths; isothermal sections at 500 K; and liquidus surface projection of system A were constructed. Characteristic features of the title system are extensive fields of solid solutions extended along the TlSbS₂-TlBiS₂ quasi-binary section and a continuous solubility belt 1–2 mol % wide extended along the Sb₂S₃-Bi₂S₃ binary subsystem. Primary separation fields of phases and the types and coordinates of invariant and monovariant equilibria in system A were determined.     

In vitro bioactivity and crystallization behavior of bioactive glass in the system SiO2-CaO-Al2O3-P2O5-Na2O-MgO-CaF2

In this study, bioactivity of glass in the system SiO₂-CaO-Al₂O₃-P₂O₅-Na₂O-MgO-CaF₂ was investigated. For this purpose, a glass sample was prepared by the traditional melting method. Crystallization behavior of bioactive glass was also investigated using differential thermal analyses. The Avrami constant of bioactive glass sample calculated according to the Ozawa equation was 3.72 ± 0.4, which indicates bulk crystallization. Using the Matusita-Sakka and the Kissinger equations, activation energy of crystal growth was determined as (394 ± 17) kJ mol⁻¹ and (373 ± 12) kJ mol⁻¹, respectively. These results indicate that the crystallization activation energy data of bioactive glass obtained in this study are accurate and reliable. Bioactivity of the resultant glass sample was analyzed by immersion in simulated body fluid. Scanning electron microscopy, thin film X-ray diffraction, ultraviolet spectroscopy and inductively coupled plasma techniques were used to monitor changes in the glass surface and the simulated body fluid composition. The results revealed that a hydroxyapatite layer was formed on the glass surface after 21 days of immersion in SBF. Formation of the hydroxyapatite layer confirmed the bioactivity of the glass in the system SiO₂-CaO-Al₂O₃-P₂O₅-Na₂O-MgO-CaF₂. In addition, physical and mechanical properties of the sample were measured to determine changes in the properties with the immersion time. The results show that bioactive glass maintained its strength during the immersion in a simulated body fluid solution.     

Formation of [Cp2TiSbMe2]2, [Cp2TiSb(SiMe3)2]2 and [Cp2TiCl]2·2Mes4Sb2

Reactions of [Cp₂Ti(btmsa)] (btmsa = bis(trimethylsilyl)acetylene) with R₄Sb₂ (R = Me, Me₃Si) give [Cp₂TiSbMe₂]₂ (1) or [Cp₂TiSb(SiMe₃)₂]₂ (2) respectively. [Cp₂TiCl]₂·2Mes₄Sb₂ (3) is serendipitously formed from [Cp₂Ti(btmsa)] and Mes₂SbH containing NH₄Cl traces.     

Evolution and characterization of fluorite-like nano-SrBi2Nb2O9 phase in the SrO-Bi2O3-Nb2O5-Li2B4O7 glass system

Transparent glasses of various compositions in the system (100−x)Li₂B₄O₇−x(SrO-Bi₂O₃-Nb₂O₅) (where x=10, 20, 30, 40, 50 and 60, in molar ratio) were fabricated via splat quenching technique. The glassy nature of the as-quenched samples was established by differential thermal analyses. X-ray powder diffraction (XRD) and transmission electron microscopic studies confirmed the amorphous nature of the as-quenched and crystallinity in the heat-treated samples. Fluorite phase formation prior to the perovskite SrBi₂Nb₂O₉ phase was analyzed by both the XRD and high-resolution transmission electron microscopy. Dielectric and the optical properties (transmission, optical band gap and Urbach energy) of these samples have been found to be compositional dependent. Refractive index was measured and compared with the values predicted by Wemple-Didomemenico and Gladstone-Dale relations. The glass nanocomposites comprising nanometer-sized crystallites of fluorite phase were found to be nonlinear optic active.     

Fluorine sites in glasses and transparent glass-ceramics of the system Na2O/K2O/Al2O3/SiO2/BaF2

The transparent glass-ceramics obtained in the silicate system Na₂O/K₂O/SiO₂/BaF₂ show homogeneously dispersed BaF₂ nano crystals with a narrow size distribution. The X-ray diffraction and the nuclear magnetic resonance spectroscopy were applied to glasses and the respective glass-ceramics in order to clarify the crystallization mechanism and the role of fluorine during crystallization. With an increasing annealing time, the concentration and also the number of crystals remain approximately constant. With an increasing annealing temperature, the crystalline fraction increases until a saturation limit is reached, while the number of crystals decreases and the size of the crystals increases. Fluoride in the glassy network occurs as Al-F-Ba, Al-F-Na and also as Ba-F structures. The latter are transformed into crystalline BaF₂ and fluoride is removed from the Al-F-Ba/Na bonds. However, some fluorine is still present in the glassy phase after the crystallization.