Synthesis and luminescence investigation of RE (Eu, Tb and Ce)-doped lithium silicate (Li2SiO3)

Synthesis and photoluminescence (PL) investigations of lithium metasilicate doped with Eu³⁺, Tb³⁺ and Ce³⁺ were carried out. PL spectra of Eu-doped sample showed peaks corresponding to the ⁵D₀→⁷F_j (j=1, 2, 3 and 4) transitions under ultraviolet excitation. Strong red emission coming from the hypersensitive ⁵D₀→⁷F₂ transition of Eu³⁺ ion suggested the presence of the dopant ion in structurally disordered environment. Tb³⁺-doped silicate sample showed blue-green emission corresponding to the ⁵D₄→⁷F_j (j=6, 5 and 4) transitions. Ce-doped sample under excitation from UV, showed a broad emission band in the region 350-370 nm with shoulders around 410 nm. The fluorescence lifetimes of Eu³⁺ and Tb³⁺ ions were found out to be 790 and 600 μs, respectively. For Ce³⁺, the lifetime was of the order of 45 ns. PL spectra of the europium- and terbium-doped samples were compared with commercial red (Y₂O₃:Eu³⁺) and green (LaPO₄:Tb³⁺) phosphors, respectively. It was found that the emission from the doped silicate sample was 37% of the commercial phosphor in case of the Tb-doped sample and 8% of the commercial phosphor in case of the Eu-doped sample.     

Control of luminescence and conductivity of delafossite-type CuYO2 by substitution of rare earth cation (Eu, Tb) and/or Ca cation for Y cation

Delafossite-type oxides of CuTb_yY_1−yO₂, CuEu_yY_1−yO₂, CuCa_xTb_yY_1−x−yO₂ and CuCa_xEu_yY_1−x−yO₂ have been prepared by solid state reactions. The lattice-parameter dependence on the composition implies substitution of the Tb³⁺, Eu³⁺ and Ca²⁺ cations for the Y³⁺ site. Noticeable sharp emission lines due to the f-f transitions (⁵D₄→⁷F_J, J=3-6) of Tb³⁺ or due to the f-f transitions (⁵D₀→⁷F_J, J=0-4) of Eu³⁺ are observed at room temperature. Electrical conductivities of CuCa_xTb_yY_1−x−yO₂ and CuCa_xEu_yY_1−x−yO₂ are larger than those of CuTb_yY_1−yO₂ and CuEu_yY_1−yO₂, indicating the increase of the hole concentration caused by the substitution of Ca²⁺ for the Y³⁺ site. These results indicate the controllability of the luminescence and conductivity in CuCa_xTb_yY_1−x−yO₂ and CuCa_xEu_yY_1−x−yO₂ delafossite-type oxides by simultaneous substitution of the rare earth Tb³⁺ or Eu³⁺ cation and the Ca²⁺ cation for the Y³⁺ site.     

Sol-gel synthesis and photoluminescence of CaSiO3:Eu nanophosphors using novel silicate sources

In this paper, seven kinds of silane coupling reagents were employed as silicate sources to prepare CaSiO₃:Eu³⁺ phosphors by the sol-gel method. The different silicate precursors were used to adjust the microstructure and size of the resulting phosphors. The crystallite size of phosphors is in the range of 30-35 nm and some of them show regular microstructure after high-temperature thermolysis. The photoluminescence properties show that all of them exhibit the characteristic fluorescence ⁵D₀→⁷F_J (J=0, 1, 2, 3, 4) of the Eu³⁺ ion and the strongest one is the red emission at 610 nm. Furthermore, the emission quantum efficiency (η) of the ⁵D₀ Eu³⁺ excited state has been calculated to be around 33% from the emission spectrum and the lifetime of the Eu³⁺ first excited level (τ, ⁵D₀).     

A white light emitting phosphor Sr1.5Ca0.5SiO4:Eu, Tb, Eu for LED-based near-UV chip: Preparation, characterization and luminescent mechanism

In this work, we report preparation, characterization and luminescent mechanism of a phosphor Sr_1.5Ca_0.5SiO₄:Eu³⁺,Tb³⁺,Eu²⁺ (SCS:ETE) for white-light emitting diode (W-LED)-based near-UV chip. Co-doped rare earth cations Eu³⁺, Tb³⁺ and Eu²⁺ as aggregated luminescent centers within the orthosilicate host in a controlled manner resulted in the white-light phosphors with tunable emission properties. Under the excitation of near-UV light (394 nm), the emission spectra of these phosphors exhibited three emission bands: one broad band in the blue area, a second band with sharp lines peaked in green (about 548 nm) and the third band in the orange-red region (588-720 nm). These bands originated from Eu²⁺ 5d→4f, Tb³⁺⁵D₄→⁷F_J and Eu³⁺⁵D₀→⁷F_J transitions, respectively, with comparable intensities, which in return resulted in white light emission. With anincrease of Tb³⁺ content, both broad Eu²⁺ emission and sharp Eu³⁺ emission increase. The former may be understood by the reduction mechanism due to the charge transfer process from Eu³⁺ to Tb³⁺, whereas the latter is attributed to the energy transfer process from Eu²⁺ to Tb³⁺. Tunable white-light emission resulted from the system of SCS:ETE as a result of the competition between these two processes when the Tb³⁺ concentration varies. It was found that the nominal composition Sr_1.5Ca_0.5SiO₄:1.0%Eu³⁺, 0.07%Tb³⁺ is the optimal composition for single-phased white-light phosphor. The CIE chromaticity calculation demonstrated its potential as white LED-based near-UV chip.     

Photoluminescence investigations of Zn2SiO4 co-doped with Eu and Tb ions

Zinc silicate phosphors co-doped with Eu³⁺ ions and also with both Eu³⁺ and Tb³⁺ ions were prepared by high temperature solid state reaction in air or reducing atmosphere. The luminescence characteristics of the prepared phosphors were investigated. While in the samples prepared in air, Eu³⁺ emission was found to be dominant over Tb³⁺ emission, in the samples prepared in reducing atmosphere, intense Eu²⁺ emission at 448 nm was found to be predominant over narrow Tb³⁺ emission. Luminescence studies showed that Eu³⁺ ions occupy asymmetric sites in Zn₂SiO₄ lattice. The intense f-f absorption peak of Eu³⁺ at 395 nm observed in these phosphors suggests their potential as red emitting phosphors for near ultra-violet light emitting diodes.     

In situ sol-gel composition of multicomponent hybrid precursors to luminescent novel unexpected microrod of Y2SiO5:Eu employing different silicate sources

Y₂SiO₅ doped with Eu³⁺ were in situ synthesized by a hybrid precursor assembly sol-gel technology employing four different silicate sources, 3-aminopropyl-trimethoxysilane (APMS), 3-aminopropyl-triethoxysilane (APES), 3-aminopropyl-methyl-diethoxysilane (APMES) and tetraethoxysilane (TEOS), respectively. The SEM result shows that there exist some novel unexpected morphological microrod structures owing to using the crosslinking reagents other than TEOS as silicate source. The photoluminescent properties of Y₂SiO₅:Eu³⁺ have been studied as a function of Eu³⁺ doping concentration. A cross-relaxation process between identical Eu³⁺ ions results in the quenching of the ⁵D₁ emission for high concentration sample.     

Emission analysis of Tb:MgAl2O4 powder phosphor

This paper reports the emission analysis of green-emitting Tb³⁺-doped MgAl₂O₄ phosphors. Uniformity of the phase of the Tb³⁺-doped MgAl₂O₄ phosphor has been checked by X-ray diffraction (XRD) technique and show common bands existing in the results of Fourier transform infrared (FT-IR). This phosphor exhibits weak blue, orange emissions and a strong emission at λ_exci=350 nm. The blue and green-orange emissions are ascribed to ⁵D₃→⁷F_J and ⁵D₄→⁷F_J (where J=3-6) transitions of Tb³⁺ ions, respectively. These phosphors have shown a strong, more prominent green emission from ⁵D₄→⁷F₅ at 543 nm. The results have indicated that MgAl₂O₄:Tb³⁺ could be a potential candidate as agreen-emitting powder phosphor.     

Luminescence properties of Y2WO6:Eu incorporated with Mo or Bi ions as red phosphors for light-emitting diode applications

In this study, the red phosphors, Y₂W_1−xMo_xO₆:Eu³⁺ and Y₂WO₆:Eu³⁺,Bi³⁺, have been investigated for light-emitting diode (LED) applications. In Y₂WO₆:Eu³⁺, the excitation band edge shifts to longer wavelength with the incorporation of Mo⁶⁺ or Bi³⁺ ions. The emission spectra exhibit ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transition of Eu³⁺ ion at 588, 593, and 610 nm, respectively. Moreover, the bluish-green luminescence of the WO₆⁶⁻ at about 460 nm is observed to decrease with the incorporation of Mo⁶⁺, which results in pure red color. Thus, this study shows that the red phosphor, Y₂WO₆:Eu³⁺, incorporated with Mo⁶⁺ or Bi³⁺ ions is advantageous for LEDs applications.     

Synthesis and luminescent properties of a new red-emitting phosphor for solid-state lighting: Eu0.1GdxLa1.9−xTeO6 (0.02?x?0.1)

The photoluminescence (PL) emission and excitation behavior of red-emitting Eu_0.1Gd_xLa_1.9−xTeO₆ (0.02?x?0.1) powder phosphors is reported. Three dominant bands centered at 395, 466 and 534 nm characterized the excitation spectrum. Under the excitation of 395 nm UV light, the emission spectrum exhibits an intense peak centered at 616 nm corresponding to the ⁵D₀→⁷F₂ transition of Eu³⁺. Because the f→f transitions are located in the wavelength range of blue or near-UV range, optimized phosphor, Eu_0.10Gd_0.08La_1.82TeO₆, is a promising material for solid-state lighting based on GaN LEDs applications.     

The luminescent properties of CaYBO4:Ln(Ln=Eu, Tb) under UV-VUV range

The luminescent properties of CaYBO₄:Ln(Ln=Eu³⁺, Tb³⁺) were investigated under ultraviolet (UV) and vacuum ultraviolet (VUV) region. The CT band of Eu³⁺ at about 245 nm blue-shifted to 230 nm in VUV excitation spectrum; the band with the maximum at 183 nm was considered as the host lattice absorption. For the sample of CaYBO₄:0.08Tb³⁺, the bands at about 235 and 263 nm were assigned to the f-d transitions of Tb³⁺ and the CT band of Tb³⁺ was calculated according to Jφrgensen's theory. Under UV and VUV excitation, the main emission of Eu³⁺ corresponding to the ⁵D₀-⁷F₂ transition located at about 610 nm and two intense emission of Tb³⁺ from the ⁵D₄-⁷F₅ transition had been observed at about 542 and 552 nm, respectively. With the incorporation of Gd³⁺ into the host lattice of CaYBO₄, the luminescence of Tb³⁺ was enhanced while that of Eu³⁺ was decreased because of their different excitation mechanism.     

Synthesis and luminescence properties of red-emitting phosphors NaY0.87Eu0.13(WO4)1.2(MoO4)0.8

A series of NaY_1−yEu_y(WO₄)_2−x(MoO₄)_x (x=0−2 and y=0.06−0.15) phosphors have been prepared by a combustion route. X-ray powder diffraction, photoluminescence excitation and emission spectra were used to characterize the resulting samples. The excitation spectra of these phosphors show the strongest absorption at about 396 nm, which matches well with the commercially available n-UV-emitting GaN-based LED chip. Their emission spectra show an intense red emission at 616 nm due to the ⁵D₀→⁷F₂ electric dipole transition of Eu³⁺. As the Mo content increases, the intensity of the ⁵D₀→⁷F₂ emission of Eu³⁺ activated at wavelength of 396 nm increases and reaches a maximum when the relative ratio of Mo/W is 2:3. The intense red-emission of the tungstomolybdate phosphors at near-UV excitation suggests that the material is a potential candidate for white light emitting diode (WLEDs).     

Synthesis and luminescence behavior of Eu-doped CaF2 nanoparticles

Luminescent Ca_1−xF_2+x:Eu_x nanoparticles were synthesized by a chemical co-precipitation method in an ethanol solution. The Ca_1−xF_2+x:Eu_x nanoparticles exhibit a sphere-like morphology with particle diameter of about 15-20 nm. With increasing concentration of Eu³⁺ ion the intensity of XRD diffraction peaks decreased significantly and full width at half-maximum of the peaks increased gradually, which indicated that more Eu³⁺ ions resulted in the increase of structural defects. The emission spectrum of Ca_1−xF_2+x:Eu_x nanoparticles consisted of a few narrow, sharp lines corresponding to Eu³⁺ ions. The luminescence intensity of Ca_1−xF_2+x:Eu_x nanoparticles increased with increasing concentration of Eu³⁺ ion and reached a maximum at approximately 15 mol%.     

Enhancement of red spectral emission intensity of Y3Al5O12:Ce phosphor via Pr co-doping and Tb substitution for the application to white LEDs

We have enhanced color-rendering property of a blue light emitting diode (LED) pumped white LED with yellow emitting Y₃Al₅O₁₂:Ce³⁺ (YAG:Ce) phosphor using addition of Pr and Tb as a co-activator and host lattice element, respectively. Pr³⁺ addition to YAG:Ce phosphor resulted in sharp emission peak at about 610 nm through ¹D₂→³H₄ transition. And when Tb³⁺ substituted Y³⁺ sites, Ce³⁺ emission band shifted to a longer wavelength due to larger crystal field splitting. Y₃Al₅O₁₂:Ce³⁺, Pr³⁺ and (Y_1−xTb_x)₃Al₅O₁₂:Ce³⁺ phosphors were coated on blue LEDs to fabricate white LEDs, respectively, and their color-rendering indices (CRIs, R_a) were measured. As a consequence of the addition of Pr³⁺ or Tb³⁺, CRI of the white LEDs improved to be R_a=83 and 80, respectively. Especially, blue LED pumped (Y_0.2Tb_0.8)₃Al₅O₁₂:Ce³⁺ white LED showed both strong luminescence and high color-rendering property.     

In situ sol-gel composition of multicomponent hybrid precursor to hexagon-like Zn2SiO4:Tb microcrystalline phosphors with different silicate sources

Zn₂SiO₄ doped with Tb³⁺ were in situ synthesized by a modified sol-gel technology with the assembly hybrid precursor employed four different silicate sources, i.e. 3-aminopropyl-trimethoxysilane (APMS), 3-aminopropyl-triethoxysilane (APES), 3-aminopropyl-methyl-diethoxysilane (APMES) and tetraethoxysilane (TEOS), respectively. The SEM result shows that there exist some novel unexpected micromorphological structures of hexagon-like with the dimension of 0.5-1.0 μm. The photoluminescent properties of Zn₂SiO₄:Tb³⁺ phosphors have been studied as a function of Tb³⁺ doping concentration. Cross-relaxation process between identical Tb³⁺ ions results in the quenching of the ⁵D₃ emission for high concentration sample.     

White-light long-lasting phosphorescence from Tb-activated Y2O2S phosphor

The white-light long-lasting phosphors Y₂O₂S:Tb³⁺, Sr²⁺ or/and Zr⁴⁺ were prepared and studied. The white-light afterglow emission after the irradiation with 254 nm UV are composed of the blue light emission and the yellowish-green light emission, originating from the transitions of ⁵D₃→⁷F₅, ⁵D₄→⁷F₅ in Tb³⁺ when the Tb³⁺ concentration is not higher than 0.3 at%. The codoped Sr²⁺ and Zr⁴⁺ ions act as trap-creating ions. The afterglow can last over 21 min in the dark for Y₂O₂S:Tb³⁺0.3%, Sr²⁺4%, Zr⁴⁺4% after irradiation by 254 nm ultraviolet light. Y₂O₂S:Tb³⁺ may be a promising material for the development of white-light long-lasting phosphor since the Tb³⁺ has a high luminescent efficiency and the dominant excitation band of 4f →5d is located at 220-300 nm.     

VUV-UV luminescence of magnetoplumbite: (Sr0.96−xBa0.04)Al12−yMgyO19:Tbx

The title compounds (Sr_0.96−xBa_0.04)Al_12−yMg_yO₁₉:Tb_x (0<x<0.4; 0<y<0.18) are single-phase magnetoplumbite determined by X-ray powder diffraction analysis. The characteristic emission lines of ⁵D₃→⁷F_j (j=2, 3, 4, 5) and ⁵D₄→⁷F_j (j=4, 5, 6) of Tb³⁺ are recorded under the VUV excitation. The intensive luminescence mainly comes from ⁵D₃→⁷F_j transition when the concentration of Tb³⁺ is low. However, when the concentration of Tb³⁺ starts to increase from very low concentration, ⁵D₄→⁷F_j transition is becoming dominant. Three broad excitation bands at 165, 193 and 233 nm have been observed. The band at 165 nm originates from the overlap between the host absorption and the charge transfer of Tb³⁺-O²⁻. The other two broad bands are the first spin-allowed and the spin-forbidden of 4f-5d transition, respectively. The experimental observation of the 4f-5d transition of Tb³⁺ is consistent well with the theoretical expectations.     

Sol-gel preparation and photoluminescence property of YBO3:Eu/Tb nanocrystalline thin films

YBO₃:Eu³⁺/Tb³⁺ nanocrystalline thin films were successfully deposited onto quartz glass substrates by Pechini sol-gel dip-coating method, using rare-earth nitrates and boric acid as starting materials. The crystal structure, morphology, chemical composition and photoluminescence property of the films were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared (FTIR) spectroscopy and fluorescence spectrophotometer. The results of XRD, AFM, XPS and FTIR revealed that the films were composed of spherical YBO₃:Eu³⁺/Tb³⁺ nanocrystals with average grain size of 80 nm. The YBO₃:Eu³⁺ film exhibited strong orange emission at 595 nm and red emission at 615 nm, which were, respectively ascribed to the (⁵D₀→⁷F₁) and (⁵D₀→⁷F₂) transitions of Eu³⁺. The YBO₃:Tb³⁺ film showed dominant green emission at 545 nm due to the ⁵D₄-⁷F₅ transition of Tb³⁺.     

Green emission from Tb-doped SrSi2O2N2 phosphors under ultraviolet light irradiation

Tb-doped SrSi₂O₂N₂ phosphors with promising luminescent properties were synthesized by the conventional solid-state reaction method, characterized by powder X-ray diffraction and studied by photoluminescence excitation and emission spectra. The synthesized materials exhibited a weak blue emission and a strong green emission in the region of 400-470 nm and 480-650 nm, which are attributed to ⁵D₃→⁷F_j (j=5, 4, 3) and ⁵D₄→⁷F_j (j=6, 5, 4, 3) transitions of Tb³⁺, respectively. The green emission from ⁵D₄→⁷F₅ at 543 nm showed the highest intensity under the optimized concentration of 0.1 mol, after which the quenching concentration became relevant. The quenching behavior of the emission of Tb³⁺ was explained by the cross-relaxation of its excited state.     

Comparative structural and photoluminescent study of Eu-doped La2O3 and La(OH)3 nanocrystalline powders

Eu³⁺-doped La₂O₃ nanocrystalline powder was prepared by polymer complex solution method and further used for preparation of Eu³⁺-doped La(OH)₃. Structural and optical characterization was carried out by powder X-ray diffraction and photoluminescent spectroscopy. XRD measurements confirmed the formation of hexagonal La₂O₃ and its recrystallization into La(OH)₃ in a humid atmosphere. Excitation spectra show redshift of host lattice and charge transfer emission bands in La(OH)₃ while bands that correspond to Eu³⁺f–f transitions are placed at same wavelengths in both samples. Photoluminescence spectra recorded over the temperature range from 10 K to 300 K show that intensities of emission lines in Eu³⁺-doped La₂O₃ do not depend on temperature as much as in La(OH)₃ sample. Observed dominant ⁵D₀→⁷F₂ and markedly visible ⁵D₀→⁷F₀ emissions in doped La₂O₃ indicate that Eu³⁺ ion is located in a structural site without an inversion center. On the other hand, in Eu³⁺-doped La(OH)₃⁵D₀→⁷F₀ transition is barely visible while ⁵D₀→⁷F₂ is not prominent, and with temperature drop three ⁵D₀→⁷F_J (J=1, 2, 4) transitions become almost of the same intensity. In both La₂O₃ and La(OH)₃ structures Eu³⁺ ion replaces La³⁺ in non-centrosymmetric C_3v and C_3h crystallographic sites, respectively, and difference in symmetry of the crystal field around europium ion is explained by comparing shape and volume of these sites. Decay times of the ⁵D₀- level recorded over the temperature range 10−300 K revealed that emission lifetime values in La₂O₃ (~0.7 ms) are almost two times higher than in La(OH)₃ (~0.4 ms), and unlike in La₂O₃, lifetime in La(OH)₃ is temperature dependent.     

A combinatorial approach to the discovery and optimization of YCa4O(BO3)3-based luminescent materials

Thin films of YCa₄O(BO₃)₃ (YCOB)-based new luminescent materials were explored by the combinatorial pulsed laser deposition (PLD) method which enabled us to fabricate continuous composition spread film libraries. Strong red and green luminescence were found in the Y_1−xEu_xCOB (0 ≤ x ≤ 1), (YEuCOB) and Y_1−yTb_yCOB (0 ≤ y ≤ 1) (YTbCOB) films, respectively. The film libraries were characterized by photoluminescence (PL), PL decay, an electron-probe microanalyzer and an electron diffraction analysis. The luminescent intensities in the amorphous film libraries strongly depended on the chemical composition of each rare-earth (RE) ion. The optimum concentration of rare-earth ions in YEuCOB and YTbCOB were experimentally determined to be Eu = 7.5% and Tb = 20-30%, respectively.