Synthesis process and the luminescence properties of rare earth doped NaLa(WO4)2 nanoparticles

Rare earth doped NaLa(WO₄)₂ nanoparticles have been prepared by a simply hydrothermal synthesis procedure. The X-ray diffraction (XRD) pattern shows that the Eu³⁺-doped NaLa(WO₄)₂ nanoparticles with an average size of 10-30 nm can be obtained via hydrothermal treatment for different time at 180 °C. The luminescence intensity of Eu³⁺-doped NaLa(WO₄)₂ nanoparticles depended on the size of the nanoparticles. The bright upconversion luminescence of the 2 mol% Er³⁺ and 20 mol% Yb³⁺ codoped NaLa(WO₄)₂ nanoparticles under 980 nm excitation could also be observed. The Yb³⁺-Er³⁺ codoped NaLa(WO₄)₂ nanoparticles prepared by the hydrothermal treatment at 180 °C and then heated at 600 °C shows a 20 times stronger upconversion luminescence than those prepared by hydrothermal treatment at 180 °C or by hydrothermal treatment at 180 °C and then heated at 400 °C.     

Crystalline-structure-dependent green and red upconversion emissions of Er-Yb-Li codoped TiO2

Crystalline structures and infrared-to-visible upconversion luminescence spectra have been investigated in 1 mol% Er³⁺, 10 mol% Yb³⁺ and 0-20 mol% Li⁺ codoped TiO₂ [1Er10Yb(0-20)Li:TiO₂] nanocrystals. The crystalline structures of 1Er10Yb(0-20)Li:TiO₂ were divided into three parts by the addition of Yb³⁺ and Li⁺. Both green and red upconversion emissions were observed from the ²H_11/2/⁴S_3/2 → ⁴I_15/2 and ⁴F_9/2 → ⁴I_15/2 transitions of Er³⁺ in Er³⁺-Yb³⁺-Li⁺ codoped TiO₂, respectively. The green and red upconversion emissions of 1Er:TiO₂ were enhanced significantly by Yb³⁺ and Li⁺ codoping, in which the intensities of green and red emissions and the intensity ratio of green to red emissions (I_green/I_red) were highly dependent on the crystalline structures. The significant enhanced upconversion emissions resulted from the energy migration between Er³⁺ and Yb³⁺ as well as the distortion of crystal field symmetry of Er³⁺ caused by the dissolving of Li⁺ at lower Li⁺ codoping concentration and the phase transformation at higher Li⁺ concentration. It is concluded that codoping with ions of smaller ionic radius like Li⁺ can efficiently improve the upconversion emissions of Er³⁺ or other rare-earth ions doped luminsecence materials.     

Infrared-to-visible upconversion in Er and Er/Yb activated Sb2O4 nanopowders prepared by sol-gel route

We prepared Er³⁺ doped and Er³⁺/Yb³⁺ codoped Sb₂O₄ nanocrystals by the sol-gel method. The Raman, X-ray diffraction (XRD), transmission electron microscope (TEM), and photoluminescence spectra of the samples were studied. The phonon energy of the Sb₂O₄ nanocrystals is very low (the maximum value being 461 cm⁻¹). The upconversion (UC) red emission of the Er³⁺/Yb³⁺ codoped sample is very strong at 975 nm laser diode excitation. The Sb₂O₄ nanocrystals will be a promising luminous material.     

Luminescence spectroscopy of Er-doped and Er, Yb-codoped LaPO4 single crystals

LaPO₄ single crystals lightly doped with Er³⁺, and codoped with Er³⁺ and Yb³⁺ have been grown by spontaneous nucleation in a lead phosphate flux. Absorption and luminescence spectra have been measured in the visible and near-IR regions and the excited state dynamics has been studied upon pulsed laser excitation. The obtained results have allowed the evaluation of the effective emission cross-sections around 1.5 μm, that have been found to be similar to important oxide laser crystals doped with Er³⁺. Efficient visible upconversion has been observed upon excitation at 980 nm in the codoped crystals. This behaviour is attributed to Yb³⁺-Er³⁺ energy transfer processes.     

Upconversion properties of Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glasses

The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3＋/Er^3＋ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3＋/Er^3＋ is also studied, The luminescence intensity increases with the ratio of Yb^3＋/Er^3＋ increasing. The ratio of Yb^3＋/Er^3＋ plays a more important role than the concentration of Er^3＋ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3＋/Er^3＋ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.     

Optical spectroscopy of Yb/Er codoped NaY(WO4)2 crystal

Erbium and ytterbium codoped double tungstates NaY(WO₄)₂ crystals were prepared by using Czochralski (CZ) pulling method. The absorption spectra in the region 290-2000 nm have been recorded at room temperature. The Judd-Ofelt theory was applied to the measured values of absorption line strengths to evaluate the spontaneous emission probabilities and stimulated emission cross sections of Er³⁺ ions in NaY(WO₄)₂ crystals. Intensive green and red lights were measured when the sample were pumped by a 974 nm laser diode (LD), especially, the intensities of green upconversion luminescence are very strong. The mechanism of energy transfer from Yb³⁺ to Er³⁺ ions was analyzed. Energy transfer and nonradiative relaxation played an important role in the upconversion process. Photoexcited luminescence experiments are also fulfilled to help analyzing the transit processes of the energy levels.     

Influence of Yb doping concentration on upconversion luminescence of Er in Lu2O3 phosphor

Cubic phase Lu₂O₃:Er³⁺/Yb³⁺ nanocrystal phosphors were prepared by sol–gel method. Fourier transform infrared (FT-IR) spectra were measured to evaluate the vibrational feature of the samples. Green and red radiations were observed upon 980 nm diode laser excitation. Laser power and Er³⁺ or Yb³⁺ doping concentration dependence of upconversion luminescence were studied to understand upconversion mechanisms. Excited state absorption, cross relaxation and energy transfer processes are the possible mechanisms for the visible emissions.     

White upconversion emission and color tunability of Y2O3:R(R=Yb3+, Er3+, Tm3+) nanophosphors

The Y₂O₃:R(R = Yb³⁺, Er³⁺, Tm³⁺) nanophosphors were synthesized by a solvothermal method and the temperature dependence of the white upconversion emission was studied using a 975 nm LD. The upconversion emission spectra in 1 mol% Er³⁺/5 mol% Yb³⁺/xTm³⁺ tri-doped Y₂O₃ nanophosphors were sintered at 1000 ^°C with x from 0 to 0.5 mol%. The blue emission intensity increases increasing Tm³⁺ concentration from 0 to 0.5 mol%, because the Tm³⁺ state can be easily reached due to the ²F_7/2 → ²F_5/2 transition of Yb³⁺ near 10,000 cm⁻¹. The Y₂O₃: Er³⁺/Yb³⁺/Tm³⁺ nanophosphors exhibit upconversion emission from white to green with increasing sintering temperature. The calculated CIE coordinates are located in the white region at a pump power of 700 mW at 1000 °C, and the color coordinates were very similar to the standard white light emission. Their upconversion process was described through energy level diagrams and results of upconversion emission spectra and pump power dependence.     

Green and red up-conversion emissions of Er-Yb-codoped Al2O3 powders prepared by the nonaqueous sol-gel method

The 1 mol% Er³⁺- and 0-20 mol% Yb³⁺-codoped Al₂O₃ powders have been prepared by the nonaqueous sol-gel process using aluminum isopropoxide as precursor, acetylacetone as chelating agent, nitric acid as catalyzer, and hydrated erbium and ytterbium nitrate as dopant under isopropanol environment. The two crystalline types of doped Al₂O₃, γ and θ, and a stoichiometric compound, (Yb,Er)₃Al₅O₁₂, were obtained for all the Er³⁺-Yb³⁺-codoped Al₂O₃ powders at the sintering temperature of 1000 °C. The maximal intensity of both the green and red up-conversion emissions centered at about 523, 545, and 660 nm was observed for the 1 mol% Er³⁺- and 10 mol% Yb³⁺-codoped Al₂O₃ powders. The intensity ratio of the red to green up-conversion emission (I_red/I_green) increased with increasing the Yb³⁺ doping concentration for the Er³⁺-Yb³⁺-codoped Al₂O₃ powders. Furthermore, the intensity ratio of the green up-conversion emission at about 523 to 545 nm (I₅₂₃/I₅₄₅) was proportional to the Yb³⁺ doping concentration and pump electric current, which was associated with the elevated temperature of powders.     

Intense ultraviolet and blue upconversion emissions in Yb-Tm codoped stoichiometric Y7O6F9 powder

Stoichiometric Y₇O₆F₉ powder codoped with Yb³⁺-Tm³⁺ was synthesized via co-precipitation and subsequent calcining route. The results of X-ray diffraction and transmission electron microscopy reveal that when the calcining temperature is beyond 800 °C, orthorhombic YF₃ nanoparticles can be completely oxidized into orthorhombic Y₇O₆F₉ powder. Under the excitation of a 980 nm laser, Y₇O₆F₉ powder exhibits multicolor UC emission in regions spanning the UV to the NIR. In addition, the upconversion emission intensities of YF₃, Y₇O₆F₉ and Y₂O₃ powders were compared under the same dopant condition (Yb/Tm=5/0.5 mol%). The low phonon energy revealed by Raman spectra helped to understand the high efficient upconversion emission of Y₇O₆F₉ and the main phonon vibration of Y₇O₆F₉ lies at 472 cm⁻¹, which is far lower that of Y₂O₃ (at 708 cm⁻¹). Our results indicate that orthorhombic rare earth ions doped Y₇O₆F₉ is an efficient matrix for UV and blue UC emission, and has potential applications in color displays, anti-counterfeiting and multicolor fluorescent labels.     

Up-conversion luminescence of Er/Yb/Nd-codoped tellurite glasses

Up-conversion luminescence and energy transfer (ET) processes in Nd³⁺-Yb³⁺-Er³⁺ triply doped TeO₂-ZnO-Na₂O glasses have been studied under 800 nm excitation. Intense green up-conversion emissions around 549 nm, which can be attributed to the Er³⁺: ⁴S_3/2→⁴I_15/2 transition, are observed in triply doped samples. In contrast, the green emissions are hardly observed in Er³⁺ singly doped and Er³⁺-Yb³⁺ codoped samples under the same condition. Up-conversion luminescence intensity exhibits dependence of Yb₂O₃-concentration and Nd₂O₃-concentration. Up-conversion mechanism in the triply doped glasses under 800 nm pump is discussed by analyzing the ET among Nd³⁺, Yb³⁺ and Er³⁺. And a possible up-conversion mechanism based on sequential ET from Nd³⁺ to Er³⁺ through Yb³⁺ is proposed for green and red up-conversion emission processes.     

Enhanced optical activation of Er in Er-doped Al2O3 powders by Y codoping in a sol-gel method

Enhanced photoluminescence (PL) mechanism of Er³⁺-doped Al₂O₃ powders by Y³⁺ codoping at wavelength 1.53 μm has been investigated through PL measurements of 0.1 mol% Er³⁺- and 0-20 mol% Y³⁺-codoped Al₂O₃ powders prepared at a sintering temperature of 900 °C in a non-aqueous sol-gel method. PL intensity and lifetime of Er³⁺-Y³⁺-codoped Al₂O₃ powders composed of γ-(Al,Er,Y)₂O₃ and θ-(Al,Er,Y)₂O₃ phases increased with increasing Y³⁺-codoping concentration. The 10-20 mol% Y³⁺ codoping in 0.1 mol% Er³⁺-doped Al₂O₃ powders intensified the PL intensity by about 20 times, with a PL lifetime prolonged from 3.5 to 5.8 ms. A maximal increase of the optical activity of Er³⁺ in 0.1 mol% Er³⁺-Y³⁺-codoped Al₂O₃ powders about one order was achieved by 10-20 mol% Y³⁺ codoping. It is found that the improved PL properties for Er³⁺-Y³⁺-codoped Al₂O₃ powders are mainly attributed to enhanced optical activation of Er³⁺ in the Al₂O₃ by Y³⁺ codoping, and to the slightly increased radiative quantum efficiency of Er³⁺ in the Al₂O₃.     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Upconversion Properties of Er3+/Yb3+ Co-doped TeO2–TiO2–K2O Glasses

The Er³⁺/Yb³⁺ co-doped TeO₂–TiO₂–K₂O glasses were prepared by conventional melting procedures, and their upconversion spectra were performed. The dependence of luminescence intensity on the ratio of Yb³⁺/Er³⁺ was studied, and the relationship between green upconversion luminescence intensity and Er³⁺ concentration is discussed in detail. The 546 nm green upconversion luminescence intensity is optimised in the studied glasses either when the Yb³⁺/Er³⁺ ratio is 25/1 and Er³⁺ concentration is 0.1 mol%, or when the Yb³⁺/Er³⁺ ratio is 10/1 and Er³⁺ concentration is 0.15 mol%. These glasses could be one of the potential candidates for LD pumping microchip solid-state lasers.     

Upconversion luminescence of Er/Yb-codoped natrium-germanium-bismuth glasses

The absorption and upconversion fluorescence spectra of a series of Er³⁺/Yb³⁺-codoped natrium-germanium-bismuth glasses have been studied. The transition probabilities, excited state lifetimes, and the branching ratios have been predicted for Er³⁺ based on the Judd-Ofelt theory. At room temperature, an upconversion efficiency of 6.1×10⁻² has been obtained for the green emission from the glass with 0.5 wt% Er₂O₃ and 3.0 wt% Yb₂O₃ pumped by 980 nm radiation with an intensity of 270 W/cm². And the “standardized” efficiency for green upconversion light is higher than that reported in lead-germanate, lead-tellurite-germanate, and silicate glasses. The results indicate that the Er³⁺/Yb³⁺-codoped natrium-germanium-bismuth oxide glass may be a potential material for developing upconversion optic devices.     

Yb3+/Er3+共掺锗碲酸盐玻璃上转换发光增强机理的研究

玻璃的最大声子能量决定稀土离子的上转换发光强度，但本研究发现：Yb³⁺/Er ³⁺共掺锗碲酸盐玻璃在980nm LD抽运下，上转换荧光强度随着Bi₂O ₃对PbO的取代和碱 金属离子半径的增大而明显增强.而Raman光谱显示基质玻璃的最大声子能量并不随Bi ₂O₃对PbO的取代和碱金属离子半径的增大而变化，但玻璃的最大声子密 度随着Bi₂O₃对PbO 取代和碱金属离子半径的增大而降低.从玻璃无辐射跃迁概率的角度，通过分析表明，最大 声子密度的降低是玻璃上转换发光强度增强的主要原因.     

Upconversion luminescence and mechanisms in Yb-sensitized Tm-doped oxyhalide tellurite glasses

Effect of Yb₂O₃ content on upconversion luminescence and mechanisms in Yb³⁺-sensitized Tm³⁺-doped oxyhalide tellurite glasses were investigated under 980 nm excitation. Intense blue and relatively weak red upconversion emission centered at 476 and 649 nm corresponding to the transitions ¹G₄→³H₆ and ¹G₄→³H₄ of Tm³⁺, respectively, are simultaneously observed at room temperature. The results show that upconversion blue and red emission intensities of Tm³⁺ first increase, reach its maximum at Yb₂O₃%=3 mol%, and then decrease with increasing Yb₂O₃ content. The effect of Yb₂O₃ content on upconversion intensity is discussed, and possible effect mechanisms are evaluated. The investigated results were conducing to increase upconversion luminescence efficiency of Tm³⁺.     

Role of Al2O3 in upconversion and NIR emission in Tm and Er codoped calcium fluoro phosphorous silicate glass system

In this study, the principal role of Al₂O₃ on the features of the photoluminescence spectra of Tm³⁺ ion and upconversion phenomenon in Tm³⁺ and Er³⁺ codoped CaF₂−Al₂O₃−P₂O₅−SiO₂ glass system has been investigated. The concentration of Al₂O₃ is varied from 2 to 10 mol% while that of Er³⁺ and Tm³⁺ is fixed. IR and Raman spectral studies have indicated that there is a gradual increase in the degree of disorder in the glass network with increase in the concentration of Al₂O₃ up to 6.0 mol%. This is attributed to the presence of Al³⁺ ions in octahedral positions in larger proportions. When the glasses are doped with Tm³⁺ ions, the blue and red emissions were observed, whereas in Er³⁺ doped glasses blue, green and red emissions were observed. When the glasses are codoped with Tm³⁺ and Er³⁺ ions and excited at 790 nm, all the three emission lines were observed to be reinforced, especially in the glasses mixed with 6.0 mol% of Al₂O₃. The IR emission band detected at about 1.8 μm due to ³F₄→³H₆ transition of Tm³⁺ ions is also observed to be strengthened due to codoping. The reasons for enhancement in the intensity of various emission bands due to codoping have been identified and discussed with the help of rate equations for various emission transitions.     

Facile synthesis of well-dispersed SrF2:Yb/Er upconversion nanocrystals in oleate complex systems

Well oil-dispersible SrF₂:Yb³⁺/Er³⁺ upconversion (UC) nanocrystals (NCs) were easily synthesized in the water-ethanol-oleic acid-sodium oleate complex systems. The as-prepared NCs all show size-uniformity, and their sizes, morphologies can be controlled by varying the solvent and reaction time, and rectangular SrF₂:Yb³⁺/Er³⁺ nanosheets with the sizes of 5-25 nm can be obtained. The possible mechanism on the nucleation and growth of nanocrystals occurred at the oleic acid/sodium oleate interface was also discussed. The size and morphology dependent UC luminescence behaviors have been observed in SrF₂:Yb³⁺/Er³⁺ NCs, and their UC luminescence transitions were proposed. The as-prepared UC nanocrystals are expected to fulfill the demand for biological applications.     

Infrared-excited bright green and red luminescence in La3Ga5.5Ta0.5O14 doped with erbium and ytterbium

Bright green (at 525 and 550 nm) and red (at 660 nm) luminescence in Er:Yb:La₃Ga_5.5Ta_0.5O₁₄ (LGT) powder synthesized by solid state reaction was obtained by pumping at 936 nm. Yb³⁺-Er³⁺ energy transfer processes accounting for population of the ²H2_11/2, ⁴S_3/2 and ⁴F_9/2 Er³⁺ levels are discussed. The dependence of ratio between the intensities of the green and red luminescence on pump intensity is analyzed. The rather high quantum efficiency (58%) of the (⁴S_3/2, ²H2_11/2) Er³⁺ emitting level recommends LGT doped with erbium and ytterbium for upconversion applications.