Quenching of thermo-stimulated photo-ionization by energy transfer in CaAl4O7: Tb, Ce

Crystal fibers of Ce³⁺ and Tb³⁺ singly doped and co-doped CaAl₄O₇ were grown by the LHPG method. Photoluminescence, excitation spectra and photoconduction were measured. Thermo-stimulated photo-ionization (delocalization) of electrons from the lowest field component of the 5d excited state of Ce³⁺ was observed in the Ce³⁺ singly doped sample under excitation at 355 nm. The 5d sublevel was found to locate at 0.3 eV below the conduction band of the host. However, the thermo-stimulated photo-ionization was greatly quenched due to the fast energy transfer from the 5d sublevel to Tb³⁺ ions in the Ce³⁺/Tb³⁺ double doped sample.     

Luminescence and energy transfer processes in Lu2SiO5:Ce scintillator

The energy transfer processes in Lu₂SiO₅:Ce³⁺ luminescence was investigated through the temperature dependent luminescence under excitation with VUV-UV. Ce1 center emission peaking at 393 and 422 nm and Ce2 center emission peaking at 462 nm were observed. Ce2 center emission is enhanced with the temperature, which can be explained by the rate of energy transfer from Ce1 center increases when the temperature rises. The Ce1 emission shows the thermal quenching effect under the direct excitation of Ce³⁺ at 262 nm. However, under the interband excitation of 183 nm, the Ce1 center emission exhibits undulating temperature dependence. This is because the emission is governed by thermal quenching and possible thermal enhancement of the transport of free carriers with the rising temperature.     

Spectroscopic investigations of Nd-, Er-, Er/Yb-, and Tm-ions doped SiO2-Al2O3-CaF2-GdF3 glasses

This paper reports on the absorption, visible and near-infrared luminescence properties of Nd³⁺, Er³⁺, Er³⁺/2Yb³⁺, and Tm³⁺ doped oxyfluoride aluminosilicate glasses. From the measured absorption spectra, Judd-Ofelt (J-O) intensity parameters (Ω₂, Ω₄ and Ω₆) have been calculated for all the studied ions. Decay lifetime curves were measured for the visible emissions of Er³⁺ (558 nm, green), and Tm³⁺ (650 and 795 nm), respectively. The near infrared emission spectrum of Nd³⁺ doped glass has shown full width at half maximum (FWHM) around 45 nm (for the ⁴F_3/2→⁴I_9/2 transition), 45 nm (for the ⁴F_3/2→⁴I_11/2 transition), and 60 nm (for the ⁴F_3/2→⁴I_13/2 transition), respectively, with 800 nm laser diode (LD) excitation. For Er³⁺, and Er³⁺/2Yb³⁺ co-doped glasses, the characteristic near infrared emission bands were spectrally centered at 1532 and 1544 nm, respectively, with 980 nm laser diode excitation, exhibiting full width at half maximum around 50 and 90 nm for the erbium ⁴I_13/2→⁴I_15/2 transition. The measured maximum decay times of ⁴I_13/2→⁴I_15/2 transition (at wavelength 1532 and 1544 nm) are about 5.280 and 5.719 ms for 1Er³⁺ and 1Er³⁺/2Yb³⁺ (mol%) co-doped glasses, respectively. The maximum stimulated emission cross sections for ⁴I_13/2→⁴I_15/2 transition of Er³⁺ and Er³⁺/Yb³⁺ are 10.81×10⁻²¹ and 5.723×10^-21 cm². These glasses with better thermal stability, bright visible emissions and broad near-infrared emissions should have potential applications in broadly tunable laser sources, interesting optical luminescent materials and broadband optical amplification at low-loss telecommunication windows.     

New red phosphors BaZr(BO3)2 and SrAl2B2O7 doped with Eu for PDP applications

Vacuum ultraviolet (VUV) excitation and photoluminescence (PL) characteristics of Eu³⁺ ion doped borate phosphors; BaZr(BO₃)₂:Eu³⁺ and SrAl₂B₂O₇:Eu³⁺ are studied. The excitation spectra show strong absorption in the VUV region with the absorption band edge at ca. 200 nm for BaZr(BO₃)₂:Eu³⁺ and 183 nm for SrAl₂B₂O₇:Eu³⁺, respectively, which ensures the efficient absorption of the Xe plasma emission lines. In BaZr(BO₃)₂:Eu³⁺, the charge transfer band of Eu³⁺ does not appear strongly in the excitation spectrum, which can be enhanced by co-doping Al³⁺ ion into the BaZr(BO₃)₂ lattices. The luminescence intensity of BaZr(BO₃)₂:Eu³⁺ is also increased by Al³⁺ incorporation into the lattices. The PL spectra show the strongest emission at 615 nm corresponding to the electric dipole ⁵D₀→⁷F₂ transition of Eu³⁺ in both BaZr(BO₃)₂ and SrAl₂B₂O₇, similar to that in YAl₃(BO₃)₄, which results in a good color purity for display applications.     

Highly enhanced photoluminescence and X-ray excited luminescence of Li doped Gd2O3:Eu thin films

Transparent Li-doped Gd₂O₃:Eu³⁺ thin-film phosphors were prepared by a modified sol-gel method. The effect of the Li⁺ ions on luminescent properties of the thin film was investigated. The results indicated that incorporation of Li⁺ ions into Gd₂O₃ lattice could result in a remarkable increase on photoluminescence or X-ray excited luminescence, and the strongest emission was observed from Gd_1.84Li_0.08Eu_0.08O_3−δ film, in which the intensity was increased by a factor of 1.9 or 2.3 in comparison with that of Gd_1.92Eu_0.08O₃ film. And it could be achieved the highest intensity for sintering the Gd_1.84Li_0.08Eu_0.08O_3−δ film at 700 °C. Such a temperature is much lower than the typical solid-state reaction temperature for its powder phosphors. This kind of transparent thin-film phosphors may promise for application to micro X-ray imaging system.     

Emission analysis of Dy and Pr:Bi2O3-ZnF2-B2O3-Li2O-Na2O glasses

In this paper, we present the spectral results of Dy³⁺ and Pr³⁺ (1.0 mol%) ions doped Bi₂O₃-ZnF₂-B₂O₃-Li₂O-Na₂O glasses. Measurements of X-ray diffraction (XRD), differential scanning calorimetry (DSC) profiles of these rare-earth ions doped glasses have been carried out. From the DSC thermograms, glass transition (T_g), crystallization (T_c) and melting (T_m) temperatures have been evaluated. The direct and indirect optical band gaps have been calculated based on the glasses UV absorption spectra. The emission spectrum of Dy³⁺:glass has shown two emission transitions ⁴F_7/2→⁶H_15/2 (482 nm) and ⁴F_7/2→⁶H_13/2 (576 nm) with an excitation at 390 nm wavelength and Pr³⁺:glass has shown a strong emission transition ¹D₂→³H₄ (610 nm) with an excitation at 445 nm. Upon exposure to UV radiation, Dy³⁺ and Pr³⁺ glasses have shown bright yellow and reddish colors, respectively, from their surfaces.     

Emission characteristics of Er in vapor-transport-equilibrated Er/Zn-codoped LiNbO3 crystals

Polarized visible and infrared emission characteristics of Er³⁺ ions in vapor-transport-equilibration (VTE)-treated LiNbO₃ crystals codoped with different concentrations of Zn and Er were investigated in comparison with corresponding as-grown crystals. The results show that the VTE treatment leads to substantial spectral changes of Er³⁺ emissions at 0.65, 0.98 and 1.5 μm regions, and the spectral changes in the 0.98 and 1.5 μm regions appear to be Zn-concentration-dependent. It is concluded in combination with X-ray powder diffraction results and optical absorption characteristics reported previously that the VTE treatment resulted in crystalline phase transformation with respect to Er³⁺ ions from original LiNbO₃ to ErNbO₄ phase in all crystals studied. The formation of the ErNbO₄ phase and the Zn²⁺ codopants are responsible for the VTE-induced substantial spectral changes. The emission characteristics of the ErNbO₄ precipitates in the Zn/Er-codoped crystals are found to be very different from those of the ErNbO₄ precipitates in the only Er-doped crystal in the infrared region, and the difference is attributed to the influence of the Zn²⁺ codopant on the Er³⁺ ion environment. The mechanism of the crystalline phase transformation is qualitatively explained from the viewpoint of the declined solubility of Er³⁺ ion in a Li-rich LiNbO₃ crystal and from the phase diagram of Li₂O-Nb₂O₅ system.     

Photoluminescence studies of red-emitting NaEu(WO4)2 as a near-UV or blue convertible phosphor

Sodium europium double tungstate [NaEu(WO₄)₂] phosphor was prepared by the solid-state reaction method. Its crystal structure, photoluminescence properties and thermal quenching characteristics were investigated aiming at the potential application in the field of white light-emitting diodes (LEDs). The influences of Sm doping on the photoluminescence properties of this phosphor were also studied. It is found that this phosphor can be effectively excited by 394 or 464 nm light, which nicely match the output wavelengths of near-ultraviolet (UV) or blue LED chips. Under 394 or 464 nm light excitation, this phosphor exhibits stronger emission intensity than the Y₂O₂S:Eu³⁺ or Eu²⁺-activated sulfide phosphor. The introduction of Sm³⁺ ions can broaden the excitation peaks at 394 and 464 nm of the NaEu(WO₄)₂ phosphor and significantly enhance its relative luminance under 400 and 460 nm LEDs excitation. Furthermore, the relative luminance of NaEu(WO₄)₂ phosphor shows a superior thermal stability compared with the commercially used sulfide or oxysulfide phosphor, and make it a promising red phosphor for solid-state lighting devices based on near-UV or blue LED chips.     

Enhanced emission of Er from alternately Er doped Si-rich Al2O3 multilayer film with Si nanocrystals as broadband sensitizers

Alternately Er doped Si-rich Al₂O₃ (Er:SRA) multilayer film, consisting of alternate Er-Si-codoped Al₂O₃ (Er:Si:Al₂O₃) and Si-doped Al₂O₃ (Si:Al₂O₃) sublayers, has been synthesized by co-sputtering from separated Er, Si, and Al₂O₃ targets. The dependence of Er³⁺ related photoluminescence (PL) properties on annealing temperatures over 700-1100 °C was studied. The maximum intensity of Er³⁺ PL, about 10 times higher than that of the monolayer film, was obtained from the multilayer film annealed at 950 °C. The enhancement of Er³⁺ PL intensity is attributed to the energy transfer from the silicon nanocrystals in the Si:Al₂O₃ sublayers to the neighboring Er³⁺ ions in the Er:Si:Al₂O₃ sublayers. The PL intensity exhibits a nonmonotonic temperature dependence: with increasing temperature, the integrated intensity almost remains constant from 14 to 50 K, then reaches maximum at 225 K, and slightly increases again at higher temperatures. Meanwhile, the PL integrated intensity at room temperature is about 30% higher than that at 14 K.     

Upconversion from the I13/2 and I11/2 levels in Er:YAG

The efficiency of erbium three-micron laser (laser transition ⁴I_11/2→⁴I_13/2) depends essentially on the ratio of the parameters of active energy transfer upconversion (ETU) from the laser levels. The parameters of both ETU processes can be obtained from the analysis of the shape of the kinetics of the ⁴I_11/2 level in concentrated Er:YAG crystals, under short pulse pumping. Mathematical modeling is used to evaluate the sensitivity of the method and to estimate the errors which can be introduced by the inhomogeneous pumping and accidental impurities. It was found that the ratio of the parameters corresponding to the ETU from the laser levels is less sensitive to the pumping inhomogeneities than that corresponding to the lower laser level. A reduction of this ratio with increasing erbium concentration is observed.     

Eu red long afterglow in Y2O2S:Ti, Eu phosphor through afterglow energy transfer

Eu,Ti co-doped Y₂O₂S:0.03Ti,0.03Eu phosphors and single Eu or Ti doped Y₂O₂S phosphors were prepared and their luminescent properties were investigated in detail by photoluminescence (PL) spectra, long afterglow spectra and thermoluminescence spectra measurements. The results showed that Y₂O₂S:Ti,Eu phosphors possess orange-red afterglow color with afterglow time above 5 h. The reddish afterglow color, which corresponds to a set of linear Eu³⁺ emissions at low-energy range (540-630 nm), was demonstrated to come from the energy transfer process from yellow Ti afterglow emissions, the proposed energy transfer mechanism may well explain the Eu³⁺ afterglow emission.     

Potential PDP phosphors with strong absorption around 172 nm: Rare earth doped NaLaP2O7 and NaGdP2O7

NaLaP₂O₇ and NaGdP₂O₇ powder samples are prepared by solid-state reactions at 750 and 600 °C, respectively, and the VUV-excited luminescence properties of Ln³⁺ (Ln=Ce, Pr, Tb, Tm, Eu) in both diphosphates are studied. Ln³⁺ ions in both hosts show analogous luminescence. For Ce³⁺-doped samples, the five Ce³⁺ 5d levels can be clearly identified. As for Pr³⁺ and Tb³⁺-doped samples, strong 4f-5d absorption band around 172 nm is observed, which matches well with Xe-He excimer in plasma display panel (PDP) devices. As a result, Pr³⁺ can be utilized as sensitizer to absorb 172 nm VUV photon and transfer energy to appropriate activators, and Tb³⁺-doped NaREP₂O₇(RE=La, Gd) are potential 172 nm excited green PDP phosphors. For Tm³⁺ and Eu³⁺-doped samples, the Tm³⁺-O²⁻ charge transfer band (CTB) is observed to be at 177 nm, but the CTB of Eu³⁺ is observed at abnormally low energy position, which might originate from multi-position of Eu³⁺ ions. The similarity in luminescence properties of Ln³⁺ in both hosts indicates certain structural resemblance of coordination environment of Ln³⁺ in the two sodium rare earth diphosphates.     

Preparation and spectroscopic properties of Nb2O5 nanorods

Nb₂O₅ nanorods have been prepared using water/ethanol media. The samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV-visible absorption and photoluminescence spectroscopy. The as-prepared Nb₂O₅ nanorods appeared to be single pseudohexagonal (TT-Nb₂O₅) phase. From the photoluminescence spectrum, two emission bands at 407 and 496 nm, respectively, were observed. The origin of the luminescence was discussed in detail.     

Origin of PL intensity increase of CaMgSi2O6:Eu phosphor after baking process for PDPs application

We have synthesized blue-emitting CaMgSi₂O₆:Eu²⁺ (CMS) and evaluated its thermal stability after baking process. To evaluate its thermal stability, CMS was baked in air at 500 and 600 °C for 20 min, respectively, and compared with BaMgAl₁₀O₁₇:Eu²⁺ (BAM) treated in the same condition. After baking process, CMS showed somewhat increased photoluminescence (PL) intensity with baking temperature. To investigate the reasons behind the increase of PL intensity after baking process, vacuum ultraviolet (VUV)/PL, electron spin resonance (ESR), X-ray photoelectron spectroscopy (XPS) techniques were applied. From the ESR and the XPS analyses, it is noted that spectral intensity of Eu²⁺ ion somewhat increased. It was believed that due to charge balance Eu³⁺ ions reduced to Eu²⁺ ions during the baking process in air. It is clear that the concentration of Eu²⁺ increased after the baking process in air and it leads to slight increase of the VUV/PL intensity of CMS phosphor.     

Temperature-dependent photoluminescence in La2/3Ca1/3MnO3

Visible photoluminescence and its temperature dependence of La_2/3Ca_1/3MnO₃ in the temperature range 138-293 K were measured. It was observed that the main broad band centered at ∼1.77 eV with the shoulders at ∼1.57 and ∼1.90 eV existed in the entire temperature range. It can be well fitted by three Gaussian curves B₁, B₂ and B₃ centered at ∼1.52, ∼1.75 and ∼1.92 eV, respectively. The intensities of the peak B₁ and B₂ vary as temperature increases. In the entire temperature range, the intensity of B₁ increases with increasing temperature, whereas that of B₂ decreases. The photoluminescence mechanisms for La_2/3Ca_1/3MnO₃ are presented based on the electronic structures formed by the interactions among spin, charge and lattice, in which B₁ was identified with the charge transfer excitation of an electron from the lower Jahn-Teller split e_g level of a Mn³⁺ ion to the e_g level of an adjacent Mn⁴⁺ ion, B₂ is assigned to the transition between the spin up and spin down e_g bands separated by Hund's coupling energy E_J and B₃ is attributed to the transition, determined by the crystal field energy E_C, between a t_2g core electron of Mn³⁺ to the spin up e_g bands of Mn⁴⁺ by a dipole allowed charge transfer process.     

Temperature-dependent photoluminescence spectra of Er-Tm-codoped Al2O3 thin film

Er-Tm-codoped Al₂O₃ thin films with different Tm to Er concentration ratios were synthesized by cosputtering from separated Er, Tm, Si, and Al₂O₃ targets. The temperature dependence of photoluminescence (PL) spectra was studied. A flat and broad emission band was achieved in the 1.4-1.7 μm and the observed 1470, 1533 and 1800 nm emission bands were attributed to the transitions of Tm³⁺: ³H₄ → ³F₄, Er³⁺: ⁴I_13/2 → ⁴I_15/2 and Tm³⁺: ³F₄ → ³H₆, respectively. The temperature dependence is rather complicated. With increasing measuring temperature, the peak intensity related to Er³⁺ ions increases by a factor of five, while the Tm³⁺ PL intensity at 1800 nm decreases by one order of magnitude. This phenomenon is attributed to a complicated energy transfer (ET) processes involving both Er³⁺ and Tm³⁺ and increase of phonon-assisted ET rate with temperature as well. It should be helpful to fully understand ET processes between Er and Tm and achieve flat and broad emission band at different operating temperatures.     

Laser-excited spectra of Lu2SiO5:Ce scintillator

The emission spectra of Lu₂SiO₅:Ce single crystal under the excitation of 266 nm laser were investigated. The emission spectra of LSO single crystal show no temperature quenching from 20 to 300 K, under the excitation of 266 nm laser with 2 mJ pulse energy. With rising temperature, the Ce1 emission is slightly decreased, while the Ce2 emission is slightly increased. These results show the emissions of Ce1 and Ce2 is not only dependent on the concentration ratio but also influenced by the possible energy transfer processes, including Ce1 to Ce2, intrinsic STHs to Ce2 and the phonon-assisted transfer processes. The spectral thermal broadening and the spectral overlap become evident at high temperature, leading to the enhancement of energy transfer. When the excitation power lowers, the ratio of Ce1 and Ce2 emission increases, and is close to the Xe lamp ultraviolet (UV) excitation, suggesting that the energy transfer from Ce1 center to Ce2 center may be also dependent on the excitation power.     

Spectral performance and intensive green upconversion luminescence in Er/Yb-codoped NaY(WO4)2 crystal

Using Czochralski (CZ) pulling method, an Er³⁺/Yb³⁺-codoped NaY(WO₄)₂ crystal was prepared. Absorption spectra, emission spectra and excitation spectra of this crystal were measured at room temperature. Some optical parameters, such as intensity parameters, spontaneous emission probabilities and lifetimes, were calculated from absorption spectra with Judd-Ofelt (J-O) theory. Upconversion luminescence excited by a 970 nm diode laser was studied. In this crystal, green upconversion luminescence is particularly intensive. Energy transfer mechanisms that play an important role in upconversion processes were analyzed. Two cross-relaxation processes: ⁴G_11/2 + ⁴I_9/2 → ²H_11/2 (or ⁴S_3/2) + ²H_11/2 (or ⁴S_3/2), and ⁴G_11/2 + ⁴I_15/2 → ²H_11/2 (or ⁴S_3/2) + ²I_13/2, which contribute to the intensive green luminescence under 378 nm excitation, were put forward. Background energy transfer ⁴G_11/2(Er³⁺) + ²F_7/2(Yb³⁺) → ⁴F_9/2(Er³⁺) + ²F_5/2(Yb³⁺) was also demonstrated.     

Enhancement of red spectral emission intensity of Y3Al5O12:Ce phosphor via Pr co-doping and Tb substitution for the application to white LEDs

We have enhanced color-rendering property of a blue light emitting diode (LED) pumped white LED with yellow emitting Y₃Al₅O₁₂:Ce³⁺ (YAG:Ce) phosphor using addition of Pr and Tb as a co-activator and host lattice element, respectively. Pr³⁺ addition to YAG:Ce phosphor resulted in sharp emission peak at about 610 nm through ¹D₂→³H₄ transition. And when Tb³⁺ substituted Y³⁺ sites, Ce³⁺ emission band shifted to a longer wavelength due to larger crystal field splitting. Y₃Al₅O₁₂:Ce³⁺, Pr³⁺ and (Y_1−xTb_x)₃Al₅O₁₂:Ce³⁺ phosphors were coated on blue LEDs to fabricate white LEDs, respectively, and their color-rendering indices (CRIs, R_a) were measured. As a consequence of the addition of Pr³⁺ or Tb³⁺, CRI of the white LEDs improved to be R_a=83 and 80, respectively. Especially, blue LED pumped (Y_0.2Tb_0.8)₃Al₅O₁₂:Ce³⁺ white LED showed both strong luminescence and high color-rendering property.     

Nanocrystal and interface defects related photoluminescence in silicon-rich Al2O3 films

In this study, silicon nanocrystal-rich Al₂O₃ film has been prepared by co-sputtering a silicon and alumina composite target and subsequent annealing in N₂ atmosphere. The microstructure of the film has been characterized by infrared (IR) absorption, Raman spectra and UV-absorption spectra. Typical nanocrystal and interface defects related photoluminescence with the photon energy of 1.54 (IR band) and 1.69 eV (R band) has been observed by PL spectrum analysis. A post-annealing process in oxygen atmosphere has been carried out to clarify the emission mechanism. Despite the red shift of the spectra, enhanced emission of the 1.69 eV band together with the weak emission phenomenon of the 1.54 eV band has been found after the post-annealing. The R band is discussed to originate from silicon nanocrystal interface defects. The IR band is concluded to be a coupling effect between electronic and vibrational emissions.