Excision of uranium oxide chains and ribbons in the novel one-dimensional uranyl iodates K(2)[(UO(2))3(IO(3))(4)O(2)] and Ba[(UO(2)2(IO(3))(2)O(2)](H(2)O)

The alkali metal and alkaline-earth metal uranyl iodates K(2)[(UO(2))(3)(IO(3))(4)O(2)] and Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O) have been prepared from the hydrothermal reactions of KCl or BaCl(2) with UO(3) and I(2)O(5) at 425 and 180 degrees C, respectively. While K(2)[(UO(2))(3)(IO(3))(4)O(2)] can be synthesized under both mild and supercritical conditions, the yield increases from <5% to 73% as the temperature is raised from 180 to 425 degrees C. Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O), however, has only been isolated from reactions performed in the mild temperature regime. Thermal measurements (DSC) indicate that K(2)[(UO(2))(3)(IO(3))(4)O(2)] is more stable than Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O) and that both compounds decompose through thermal disproportionation at 579 and 575 degrees C, respectively. The difference in the thermal behavior of these compounds provides a basis for the divergence of their preparation temperatures. The structure of K(2)[(UO(2))(3)(IO(3))(4)O(2)] is composed of [(UO(2))(3)(IO(3))(4)O(2)](2)(-) chains built from the edge-sharing UO(7) pentagonal bipyramids and UO(6) octahedra. Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O) consists of one-dimensional [(UO(2))(2)(IO(3))(2)O(2)](2)(-) ribbons formed from the edge sharing of distorted UO(7) pentagonal bipyramids. In both compounds the iodate groups occur in both bridging and monodentate binding modes and further serve to terminate the edges of the uranium oxide chains. The K(+) or Ba(2+) cations separate the chains or ribbons in these compounds forming bonds with terminal oxygen atoms from the iodate ligands. Crystallographic data: K(2)[(UO(2))(3)(IO(3))(4)O(2)], triclinic, space group P_1, a = 7.0372(5) A, b = 7.7727(5) A, c = 8.9851(6) A, alpha = 93.386(1) degrees, beta = 105.668(1) degrees, gamma = 91.339(1) degrees, Z = 1; Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O), monoclinic, space group P2(1)/c, a = 8.062(4) A, b = 6.940(3) A, c = 21.67(1), beta= 98.05(1) degrees, Z = 4.     

Further evidence for the tetraoxoiodate(V) anion,IO(4)(3-): hydrothermal syntheses and structures of Ba[(MoO(2))(6)(IO(4))(2)O(4)] x H(2)O and Ba(3)[(MoO(2))(2)(IO(6))(2)] x 2H(2)O

The hydrothermal reaction of MoO(3) with BaH(3)IO(6) at 180 degrees C for 3 days results in the formation of Ba[(MoO(2))(6)(IO(4))(2)O(4)] x H(2)O (1). Under similar conditions, the reaction of Ba(OH)(2) x 8H(2)O with MoO(3) and Ba(IO(4))(2) x 6H(2)O yields Ba(3)[(MoO(2))(2)(IO(6))(2)] x 2H(2)O (2). The structure of 1, determined by single-crystal X-ray diffraction, consists of corner- and edge-sharing distorted MoO(6) octahedra that create two-dimensional slabs. Contained within this molybdenum oxide framework are approximately C(2v) tetraoxoiodate(V) anions, IO(4)(3-), that are involved in bonding with five Mo(VI) centers. The two equatorial oxygen atoms of the IO(4)(3-) anion chelate a single Mo(VI) center, whereas the axial atoms are mu(3)-oxo groups and complete the octahedra of four MoO(6) units. The coordination of the tetraoxoiodate(V) anion to these five highly electropositive centers is probably responsible for stabilizing the substantial anionic charge of this anion. The Ba(2+) cations separate the layers from one another and form long ionic contacts with neighboring oxygen atoms and a water molecule. Compound 2 also contains distorted MoO(6) octahedra. However, these solely edge-share with octahedral hexaoxoiodate(VII), IO(6)(5-), anions to form zigzagging one-dimensional, (1)(infinity)[(MoO(2))(IO(6))](3-), chains that are polar. These chains are separated from one another by Ba(2+) cations that are coordinated by additional water molecules. Bond valence sums for the iodine atoms in 1 and 2 are 5.01 and 7.03, respectively. Crystallographic data: 1, monoclinic, space group C2/c, a = 13.584(1) A, b = 7.3977(7) A, c = 20.736(2) A, beta = 108.244(2) degrees, Z = 4; 2, orthorhombic, space group Fdd2, a = 13.356(7) A, b = 45.54(2) A, c = 4.867(3) A, Z = 8.     

Explorations of new second-order nonlinear optical materials in the potassium vanadyl iodate system

Four new potassium vanadyl iodates based on lone-pair-containing IO(3) and second-order Jahn-Teller distorted VO(5) or VO(6) asymmetric units, namely, α-KVO(2)(IO(3))(2)(H(2)O) (Pbca), β-KVO(2)(IO(3))(2)(H(2)O) (P2(1)2(1)2(1)), K(4)[(VO)(IO(3))(5)](2)(HIO(3))(H(2)O)(2)·H(2)O (P1), and K(VO)(2)O(2)(IO(3))(3) (Ima2) have been successfully synthesized by hydrothermal reactions. α-KVO(2)(IO(3))(2)(H(2)O) and β-KVO(2)(IO(3))(2)(H(2)O) exhibit two different types of 1D [VO(2)(IO(3))(2)](-) anionic chains. Neighboring VO(6) octahedra in the α-phase are corner-sharing into a 1D chain with the IO(3) groups attached on both sides of the chain in a uni- or bidentate bridging fashion, whereas those of VO(5) polyhedra in the β-phase are bridged by IO(3) groups into a right-handed helical chain with remaining IO(3) groups being grafted unidentately on both sides of the helical chain. The structure of K(4)[(VO)(IO(3))(5)](2)(HIO(3))(H(2)O)(2)·H(2)O contains novel isolated [(VO)(IO(3))(5)](2-) units composed of one VO(6) octahedron linked to five IO(3) groups and one terminal O(2-) anion. The structure of K(VO)(2)O(2)(IO(3))(3) exhibits a 1D [(VO)(2)O(2)(IO(3))(3)](-) chain in which neighboring VO(6) octahedra are interconnected by both oxo and bridging iodate anions. Most interestingly, three of four compounds are noncentrosymmetric (NCS), and K(VO)(2)O(2)(IO(3))(3) displays a very strong second-harmonic generation response of about 3.6 × KTP, which is phase matchable. It also has high thermal stability, a wide transparent region and moderate hardness as well as an excellent growth habit. Thermal analyses and optical and ferroelectric properties as well as theoretical calculations have also been performed.     

Expanding the remarkable structural diversity of uranyl tellurites: hydrothermal preparation and structures of K[UO(2)Te(2)O(5)(OH)], Tl(3)[(UO(2))(2)[Te(2)O(5)(OH)](Te(2)O(6))].2H(2)O,beta-Tl(2)[UO(2)(TeO(3))(2)], and Sr(3)[UO(2)(TeO(3))(2)](TeO(3))(2)

The reactions of UO(2)(C(2)H(3)O(2))(2).2H(2)O with K(2)TeO(3).H(2)O, Na(2)TeO(3) and TlCl, or Na(2)TeO(3) and Sr(OH)(2).8H(2)O under mild hydrothermal conditions yield K[UO(2)Te(2)O(5)(OH)] (1), Tl(3)[(UO(2))(2)[Te(2)O(5)(OH)](Te(2)O(6))].2H(2)O (2) and beta-Tl(2)[UO(2)(TeO(3))(2)] (3), or Sr(3)[UO(2)(TeO(3))(2)](TeO(3))(2) (4), respectively. The structure of 1 consists of tetragonal bipyramidal U(VI) centers that are bound by terminal oxo groups and tellurite anions. These UO(6) units span between one-dimensional chains of corner-sharing, square pyramidal TeO(4) polyhedra to create two-dimensional layers. Alternating corner-shared oxygen atoms in the tellurium oxide chains are protonated to create short/long bonding patterns. The one-dimensional chains of corner-sharing TeO(4) units found in 1 are also present in 2. However, in 2 there are two distinct chains present, one where alternating corner-shared oxygen atoms are protonated, and one where the chains are unprotonated. The uranyl moieties in 2 are bound by five oxygen atoms from the tellurite chains to create seven-coordinate pentagonal bipyramidal U(VI). The structures of 3 and 4 both contain one-dimensional [UO(2)(TeO(3))(2)](2-) chains constructed from tetragonal bipyramidal U(VI) centers that are bridged by tellurite anions. The chains differ between 3 and 4 in that all of the pyramidal tellurite anions in 3 have the same orientation, whereas the tellurite anions in 4 have opposite orientations on each side of the chain. In 4, there are also additional isolated TeO(3)(2-) anions present. Crystallographic data: 1, orthorhombic, space group Cmcm, a = 7.9993(5) A, b = 8.7416(6) A, c = 11.4413(8) A, Z = 4; 2, orthorhombic, space group Pbam, a = 10.0623(8) A, b = 23.024(2) A, c = 7.9389(6) A, Z = 4; 3, monoclinic, space group P2(1)/n, a = 5.4766(4) A, b = 8.2348(6) A, c = 20.849(3) A, beta = 92.329(1) degrees, Z = 4; 4, monoclinic, space group C2/c, a = 20.546(1) A, b = 5.6571(3) A, c = 13.0979(8) A, beta = 94.416(1) degrees, Z = 4.     

Aqueous reactions of U(VI) at high chloride concentrations: syntheses and structures of new uranyl chloride polymers

The reactions of UO(3) with acidic aqueous chloride solutions resulted in the formation of two new polymeric U(VI) compounds. Single crystals of Cs(2)[(UO(2))(3)Cl(2)(IO(3))(OH)O(2)].2H(2)O (1) were formed under hydrothermal conditions with HIO(3) and CsCl, and Li(H(2)O)(2)[(UO(2))(2)Cl(3)(O)(H(2)O)] (2) was obtained from acidic LiCl solutions under ambient temperature and pressure. Both compounds contain pentagonal bipyramidal coordination of the uranyl dication, UO(2)(2+). The structure of 1 consists of infinite [(UO(2))(3)Cl(2)(IO(3))(mu(3)-OH)(mu(3)-O)(2)](2-) ribbons that run down the b axis that are formed from edge-sharing pentagonal bipyramidal [UO(6)Cl] and [UO(5)Cl(2)] units. The Cs(+) cations separate the chains from one another and form long ionic contacts with terminal oxygen atoms from iodate ligands, uranyl oxygen atoms, water molecules, and chloride anions. In 2, edge-sharing [UO(3)Cl(4)] and [UO(5)Cl(2)] units build up tetranuclear [(UO(2))(4)(mu-Cl)(6)(mu(3)-O)(2)(H(2)O)(2)](2-) anions that are bridged by chloride to form one-dimensional chains. These chains are connected in a complex network of hydrogen bonds and interactions of uranyl oxygen atoms with Li(+) cations. Crystal data: 1, orthorhombic, space group Pnma, a = 8.2762(4) A, b = 12.4809(6) A, c = 17.1297(8) A, Z = 4; 2, triclinic, space group P1, a = 8.110(1) A, b = 8.621(1) A, c = 8.740(1) A, Z = 2.     

Mixed-metal uranium(VI) iodates: hydrothermal syntheses,structures, and reactivity of Rb[UO(2)(CrO(4))(IO(3))(H(2)O)], A(2)[UO(2)(CrO(4))(IO(3))(2)] (A = K,Rb, Cs), and K(2)[UO(2)(MoO(4))(IO(3))(2)

The reactions of the molecular transition metal iodates A[CrO(3)(IO(3))] (A = K, Rb, Cs) with UO(3) under mild hydrothermal conditions provide access to four new, one-dimensional, uranyl chromatoiodates, Rb[UO(2)(CrO(4))(IO(3))(H(2)O)] (1) and A(2)[UO(2)(CrO(4))(IO(3))(2)] (A = K (2), Rb (3), Cs (4)). Under basic conditions, MoO(3), UO(3), and KIO(4) can be reacted to form K(2)[UO(2)(MoO(4))(IO(3))(2)] (5), which is isostructural with 2 and 3. The structure of 1 consists of one-dimensional[UO(2)(CrO(4))(IO(3))(H(2)O)](-) ribbons that contain uranyl moieties bound by bridging chromate and iodate anions as well as a terminal water molecule to create [UO(7)] pentagonal bipyramidal environments around the U(VI) centers. These ribbons are separated from one another by Rb(+) cations. When the iodate content is increased in the hydrothermal reactions, the terminal water molecule is replaced by a monodentate iodate anion to yield 2-4. These ribbons can be further modified by replacing tetrahedral chromate anions with MoO(4)(2)(-) anions to yield isostructural, one-dimensional [UO(2)(MoO(4))(IO(3))(2)](2)(-) ribbons. Crystallographic data: 1, triclinic, space group P(-)1, a = 7.3133(5) A, b = 8.0561(6) A, c = 8.4870(6) A, alpha = 88.740(1) degrees, beta = 87.075(1) degrees, gamma = 71.672(1) degrees, Z = 2; 2, monoclinic, space group P2(1)/c, a = 11.1337(5) A, b = 7.2884(4) A, c = 15.5661(7) A, beta = 107.977(1) degrees, Z = 4; 3, monoclinic, space group P2(1)/c, a = 11.3463(6) A, b = 7.3263(4) A, c = 15.9332(8) A, beta = 108.173(1) degrees, Z = 4; 4, monoclinic, space group P2(1)/n, a = 7.3929(5) A, b = 8.1346(6) A, c = 22.126(2) A, beta = 90.647(1) degrees, Z = 4; 5, monoclinic, space group P2(1)/c, a = 11.3717(6) A, b = 7.2903(4) A, c = 15.7122(8) A, beta = 108.167(1) degrees, Z = 4.     

Syntheses, structures, and ion-exchange properties of the three-dimensional framework uranyl gallium phosphates, Cs4[(UO2)2(GaOH)2(PO4)4].H2O and Cs[UO2Ga(PO4)2

The reaction of UO(2)(NO(3))(2).6H(2)O with Cs(2)CO(3) or CsCl, H(3)PO(4), and Ga(2)O(3) under mild hydrothermal conditions results in the formation of Cs(4)[(UO(2))(2)(GaOH)(2)(PO(4))(4)].H(2)O (UGaP-1) or Cs[UO(2)Ga(PO(4))(2)] (UGaP-2). The structure of UGaP-1 was solved from a twinned crystal revealing a three-dimensional framework structure consisting of one-dimensional (1)(infinity)[Ga(OH)(PO(4))(2)](4-) chains composed of corner-sharing GaO(6) octahedra and bridging PO(4) tetrahedra that extend along the c axis. The phosphate anions bind the UO(2)(2+) cations to form UO(7) pentagonal bipyramids. The UO(7) moieties edge-share to create dimers that link the gallium phosphate substructure into a three-dimensional (3)(infinity)[(UO(2))(2)(GaOH)(2)(PO(4))(4)](4-) anionic lattice that has intersecting channels running down the b and c axes. Cs(+) cations and water molecules occupy these channels. The structure of UGaP-2 is also three-dimensional and contains one-dimensional (1)(infinity)[Ga(PO(4))(2)](3-) gallium phosphate chains that extend down the a axis. These chains are formed from fused eight-membered rings of corner-sharing GaO(4) and PO(4) tetrahedra. The chains are in turn linked together into a three-dimensional (3)(infinity)[UO(2)Ga(PO(4))(2)](1-) framework by edge-sharing UO(7) dimers as occurs in UGaP-1. There are channels that run down the a and b axes through the framework. These channels contain the Cs(+) cations. Ion-exchange studies indicate that the Cs(+) cations in UGaP-1 and UGaP-2 can be exchanged for Ca(2+) and Ba(2+). Crystallographic data: UGaP-1, monoclinic, space group P2(1)/c, a = 18.872(1), b = 9.5105(7), c = 14.007(1) A, beta = 109.65(3)(o) , Z = 4 (T = 295 K); UGaP-2, triclinic, space group P, a = 7.7765(6), b = 8.5043(7), c = 8.9115(7) A, alpha = 66.642(1)(o), beta = 70.563(1)(o), gamma = 84.003(2)(o), Z = 2 (T = 193 K).     

New mercury vanadium phosphate hydrate Hg(4)(-)(x)()O(1-)(y)()((VO)(PO(4))(2).H(2)O with unprecedented tetrahedral oxo-cluster [Hg( approximately )(4)O( approximately )(5)

The new mercury vanadium phosphate hydrate Hg(4)(-)(x)()O(1)(-)(y)()(VO)(PO(4))(2).H(2)O has been synthesized under hydrothermal conditions. X-ray investigations led to orthorhombic symmetry, space group P2(1)2(1)2(1) (No. 19), a = 6.3632(2) A, b = 12.4155(5) A, c = 14.2292(6) A, Z = 4. The crystal structure was solved and refined from single-crystal diffractometer data to residuals R[F(2) > 2sigmaF(2)] = 0.039, R(w)(F(2)) = 0.055. The VPO framework consists of infinite one-dimensional [VO(PO(4))(2)]( infinity ) chains with corner-connected VO(6) octahedra and PO(4) tetrahedra. The chains run along the [100] direction and are held together by the unprecedented tetrahedral cationic units [Hg(4)(-)(x)()O(1)(-)(y)()](4+). Presence of Hg-Hg bonding contacts is proved from theoretical calculations.     

A new oxoanion: [IO]3- containing I(V) with a stereochemically active lone-pair in the silver uranyl iodate tetraoxoiodate(V), Ag4(UO2)4(IO3)2(IO4)2O2

The hydrothermal reaction of elemental Ag, or water-soluble silver sources, with UO3 and I2O5 at 200 degrees C for 5 days yields Ag4(UO2)4(IO3)2(IO4)2O2 in the form of orange fibrous needles. Single-crystal X-ray diffraction studies on this compound reveal a highly complex network structure consisting of three interconnected low-dimensional substructures. The first of these substructures are ribbons of UO8 hexagonal bipyramids that edge-share to form one-dimensional chains. These units further edge-share with pentagonal bipyramidal UO7 units to create ribbons. The edges of the ribbons are partially terminated by tetraoxoiodate(V), [IO4]3-, anions. The uranium oxide ribbons are joined by bridging iodate ligands to yield two-dimensional undulating sheets. These sheets help to form, and are linked together by, one-dimensional chains of edge-sharing AgO7 capped octahedral units and ribbons formed by corner-sharing capped trigonal planar AgO4 polyhedra, AgO6 capped square pyramids, and AgO6 octahedra. The [IO4]3- anions in Ag4(UO2)4(IO3)2)(IO4)2O2 are tetraoxoiodate(V), not metaperiodate, and contain I(V) with a stereochemically active lone-pair. Bond valence sum calculations are consistent with this formulation. Differential scanning calorimetry measurements show distinctly different thermal behavior of Ag4(UO2)4(IO3)2(IO4)2O2 versus other uranyl iodate compounds with endotherms at 479 and 494 degrees C. Density functional theory (DFT) calculations demonstrate that the approximate C2v geometry of the [IO4]3- anion can be attributed to a second-order Jahn-Teller distortion. DFT optimized geometry for the [IO4]3- anion is in good agreement with those measured from single-crystal X-ray diffraction studies on Ag4(UO2)4(IO3)2(IO4)2O2.     

Structure and properties of the thorium vanadyl tellurate, Th(VO2)2(TeO6)(H2O)2

The hydrothermal reaction of Th(NO3)4.xH2O with V2O5 and H6TeO6 at 200 degrees C under autogenously generated pressure results in the formation of Th(VO2)2(TeO6)(H2O)2 as a pure phase. The single-crystal X-ray data indicate that Th(VO2)2(TeO6)(H2O)2 possesses a three-dimensional structure constructed from ThO9 tricapped trigonal prisms, VO5 distorted square pyramids, VO4 distorted tetrahedra, and TeO6 distorted octahedra. Both of the vanadium polyhedra contain VO2+ vanadyl units with two short V=O bond distances. The tellurate octahedron is tetragonally distorted and utilizes all of its oxygen atoms to bond to adjacent metal centers, sharing edges with ThO9 and VO5 units, and corners with two ThO9, one VO5, and two VO4 polyhedra. Crystallographic data: Th(VO2)2(TeO6)(H2O)2, orthorhombic, space group Pbca, a = 12.6921(7), b = 11.5593(7), c = 13.0950(8) A, Z = 8 (T = 193 K). The UV-vis diffuse reflectance spectrum of Th(VO2)2(TeO6)(H2O)2 shows vanadyl-based charge-transfer absorption features. Th(VO2)2(TeO6)(H2O)2 decomposes primarily to Th(VO3)4 when heated at 600 degrees C in air.     

Hydrothermal synthesis and structure of a new one-dimensional, mixed-metal U(VI) iodate, Cs(2)[(UO(2))(CrO(4))(IO(3))(2)

The reaction of the molecular transition metal iodate, Cs[CrO(3)(IO(3))], with UO(3) under mild hydrothermal conditions provides access to a new low-dimensional, mixed-metal U(VI) compound, Cs(2)[(UO(2))(CrO(4))(IO(3))(2)] (1). The structure of 1 is quite unusual and consists of one-dimensional (1)(infinity)[(UO(2))(CrO(4))(IO(3))(2)](2-) ribbons separated by Cs(+) cations. These ribbons are formed from [UO(7)] pentagonal bipyramids that contain a uranyl core, [CrO(4)] tetrahedra, and both monodentate and bridging iodate anions. Crystallographic data: 1, monoclinic, space group P2(1)/n, a = 7.3929(5) A, b = 8.1346(6) A, c = 22.126(2) A, beta = 90.647(1) degrees, Z = 4 (T = 193 K).     

A novel open framework uranyl molybdate: synthesis and structure of (NH4)4[(UO2)5(MoO4)7](H2O)5

Single crystals of (NH(4))(4)[(UO(2))(5)(MoO(4))(7)](H(2)O)(5) have been synthesized hydrothermally using (NH(4))(6)Mo(7)O(24), (UO(2))(CH(3)COO)(2).2H(2)O, and H(2)O at 180 degrees C. The phase has been characterized by single-crystal X-ray diffraction using a merohedrally twinned single crystal: it is hexagonal, P6(1), a = 11.4067(5) A, c = 70.659(5) A, V = 7961.9(7) A(3), and Z = 6. The structure is based upon an open framework with composition [(UO(2))(5)(MoO(4))(7)](4-) that is composed of UO(7) pentagonal bipyramids that share vertexes with MoO(4) tetrahedra. The framework has large channels (effective pore size: 4.8 x 4.8 A(2)) parallel to the c axis and a system of smaller channels (effective pore size: 2.5 x 3.6 A(2)) parallel to [100], [110], [010], [110], [110], and [110]. The channels are occupied by NH(4)(+) cations and H(2)O molecules. The topological structure of the uranyl molybdate framework can be described either in terms of fundamental chains of UO(7) pentagonal bipyramids and MoO(4) tetrahedra or in terms of tubular building units parallel to the c axis.     

Methanesulfonates of high-valent metals: syntheses and structural features of MoO2(CH3SO3)2, UO2(CH3SO3)2, ReO3(CH3SO3), VO(CH3SO3)2, and V2O3(CH3SO3)4 and their thermal decomposition under N2 and O2 atmosphere

Oxide methanesulfonates of Mo, U, Re, and V have been prepared by reaction of MoO(3), UO(2)(CH(3)COO)(2)·2H(2)O, Re(2)O(7)(H(2)O)(2), and V(2)O(5) with CH(3)SO(3)H or mixtures thereof with its anhydride. These compounds are the first examples of solvent-free oxide methanesulfonates of these elements. MoO(2)(CH(3)SO(3))(2) (Pbca, a=1487.05(4), b=752.55(2), c=1549.61(5) pm, V=1.73414(9) nm(3), Z=8) contains [MoO(2)] moieties connected by [CH(3)SO(3)] ions to form layers parallel to (100). UO(2)(CH(3)SO(3))(2) (P2(1)/c, a=1320.4(1), b=1014.41(6), c=1533.7(1) pm, β=112.80(1)°, V=1.8937(3) nm(3), Z=8) consists of linear UO(2)(2+) ions coordinated by five [CH(3)SO(3)] ions, forming a layer structure. VO(CH(3)SO(3))(2) (P2(1)/c, a=1136.5(1), b=869.87(7), c=915.5(1) pm, β=113.66(1)°, V=0.8290(2) nm(3), Z=4) contains [VO] units connected by methanesulfonate anions to form corrugated layers parallel to (100). In ReO(3)(CH(3)SO(3)) (P1, a=574.0(1), b=1279.6(3), c=1641.9(3) pm, α=102.08(2), β=96.11(2), γ=99.04(2)°, V=1.1523(4) nm(3), Z=8) a chain structure exhibiting infinite O-[ReO(2)]-O-[ReO(2)]-O chains is formed. Each [ReO(2)]-O-[ReO(2)] unit is coordinated by two bidentate [CH(3)SO(3)] ions. V(2)O(3)(CH(3)SO(3))(4) (I2/a, a=1645.2(3), b=583.1(1), c=1670.2(3) pm, β=102.58(3), V=1.5637(5) pm(3), Z=4) adopts a chain structure, too, but contains discrete [VO]-O-[VO] moieties, each coordinated by two bidentate [CH(3)SO(3)] ligands. Additional methanesulfonate ions connect the [V(2)O(3)] groups along [001]. Thermal decomposition of the compounds was monitored under N(2) and O(2) atmosphere by thermogravimetric/differential thermal analysis and XRD measurements. Under N(2) the decomposition proceeds with reduction of the metal leading to the oxides MoO(2), U(3)O(7), V(4)O(7), and VO(2); for MoO(2)(CH(3)SO(3))(2), a small amount of MoS(2) is formed. If the thermal decomposition is carried out in a atmosphere of O(2) the oxides MoO(3) and V(2)O(5) are formed.     

Syntheses and Properties of New Layered Alkali-Metal/Ammonium Vanadium(V) Methylphosphonates: M(VO(2))(3)(PO(3)CH(3))(2) (M = NH(4), K, Rb, Tl). Single-Crystal Structures of K(VO(2))(3)(PO(3)CH(3))(2) and NH(4)(VO(2))(3)(PO(3)CH(3))(2)

The hydrothermal syntheses of a family of new alkali-metal/ammonium vanadium(V) methylphosphonates, M(VO(2))(3)(PO(3)CH(3))(2) (M = K, NH(4), Rb, Tl), are described. The crystal structures of K(VO(2))(3)(PO(3)CH(3))(2) and NH(4)(VO(2))(3)(PO(3)CH(3))(2) have been determined from single-crystal X-ray data. Crystal data: K(VO(2))(3)(PO(3)CH(3))(2), M(r) = 475.93, trigonal, R32 (No. 155), a = 7.139(3) ?, c = 19.109(5) ?, Z = 3; NH(4)(VO(2))(3)(PO(3)CH(3))(2), M(r) = 454.87, trigonal, R32 (No. 155), a = 7.150(3) ?, c = 19.459(5) ?, Z = 3. These isostructural, noncentrosymmetric phases are built up from hexagonal tungsten oxide (HTO) like sheets of vertex-sharing VO(6) octahedra, capped on both sides of the V/O sheets by PCH(3) entities (as [PO(3)CH(3)](2-) methylphosphonate groups). In both phases, the vanadium octahedra display a distinctive two short + two intermediate + two long V-O bond distance distribution within the VO(6) unit. Interlayer potassium or ammonium cations provide charge balance for the anionic (VO(2))(3)(PO(3)CH(3))(2) sheets. Powder X-ray, TGA, IR, and Raman data for these phases are reported and discussed. The structures of K(VO(2))(3)(PO(3)CH(3))(2) and NH(4)(VO(2))(3)(PO(3)CH(3))(2) are compared and contrasted with related layered phases based on the HTO motif.     

Topological evolution in uranyl dicarboxylates: synthesis and structures of one-dimensional UO2(C6H8O4)(H2O)2 and three-dimensional UO2(C6H8O4)

Two novel uranyl adipates are reported as synthesized via hydrothermal treatment of uranium oxynitrate and adipic acid. One-dimensional UO(2)(C(6)H(8)O(4))(H(2)O)(2) (1) [a = 9.6306(6) A, c = 11.8125(10) A, tetragonal, P4(3)2(1)2 (No. 96), Z = 4] consists of chains of (UO(2))O(4)(H(2)O)(2) hexagonal bipyramids tethered through a linear adipic acid backbone. Three-dimensional UO(2)(C(6)H(8)O(4)) (2) [a = 5.5835(12) A, b = 8.791(2) A, c = 9.2976(17) A, alpha = 87.769(9) degrees, beta = 78.957(8) degrees, gamma = 81.365(11) degrees, triclinic, P1 (No. 2), Z = 2] is produced by decreasing the hydration level of the reaction conditions. This structure contains a previously unreported [(UO(2))(2)O(8)] building unit cross-linked into a neutral metal-organic framework topology with vacant channels.     

Cation-cation interactions between uranyl cations in a polar open-framework uranyl periodate

Novel open-framework alkali metal uranyl periodates, having the formula A[(UO2)3(HIO6)(OH)(O)(H2O)].1.5H2O (A = Li, Na, K, Rb, Cs), have been prepared through mild hydrothermal synthesis. These isostructural compounds contain distorted UO7 pentagonal bipyramids that are linked through a uranyl (UO22+) to uranyl cation-cation interaction. This interaction arises from a single axial uranyl oxygen coordinating at an equatorial site of an adjacent uranyl unit. These uranium oxide polyhedra are further bound by IO6 distorted octahedra creating an open-framework structure whose channels contain the alkali metal cations.     

Crystal structure and spectroscopic characterization of K8(VO)2O(SO4)6

Red and yellow dichroistic crystals of a vanadium(V) compound, potassium (mu-oxo, di-mu-sulfato)bis(oxodisulfatovanadate), K(8)(VO)(2)O(SO(4))(6), have been obtained from the ternary catalytic model melt system K(2)S(2)O(7)[bond]K(2)SO(4)[bond]V(2)O(5). By slow cooling of the melt from 420 to 355 degrees C, crystal growth occurred, using solid V(2)O(5) crystals present in the melt as nucleation promoter. The compound crystallizes in the monoclinic space group P2(l) with a = 13.60(9) A, b = 13.93(9) A, c = 14.05(9) A, beta = 90.286(10) degrees, and Z = 2. It contains two VO(6) octahedra linked together by a mu-oxo and two mu-sulfato bridges. Furthermore, each octahedron has two monodentate sulfate ligands, making the dimeric entity coordinatively saturated. IR spectroscopy shows bands arising from V[bond]O[bond]V and V[double bond]O stretches as well as splitting of sulfate bands due to the different degrees of freedom present for different conformations of sulfate ligands. The coordination of vanadium in K(8)(VO)(2)O(SO(4))(6) is discussed in relation to the reaction mechanism of SO(2) oxidation catalysis.     

Hydrothermal preparation of nickel(II)/uranium(IV) fluorides with one-, two-, and three-dimensional topologies

A modified compositional diagram for the reactions of Ni(C(2)H(3)O(2))(2).4H(2)O with UO(2)(C(2)H(3)O(2))(2).2H(2)O and HF in aqueous media under mild hydrothermal conditions (200 degrees C) has been completed to yield three Ni(II)/U(IV) fluorides, Ni(H(2)O)(4)UF(6).1.5H(2)O (1), Ni(2)(H(2)O)(6)U(3)F(16).3H(2)O (2), and Ni(H(2)O)(2)UF(6)(H(2)O) (3). The structure of 1 consists of one-dimensional columns constructed from two parallel chains of edge-sharing dodecahedral [UF(8)] units. The sides of the columns are terminated by octahedral Ni(II) units that occur as cis-[Ni(H(2)O)(4)F(2)] polyhedra. In contrast, the crystal structure of 2 reveals a two-dimensional Ni(II)/U(IV) architecture built from edge-sharing tricapped trigonal prismatic [UF(9)] units. The top and bottom of the sheets are capped by fac-[Ni(H(2)O)(3)F(3)] octahedra. The structure of 3 is formed from [UF(8)(H(2)O)] tricapped trigonal prisms that edge share with one another to form one-dimensional chains. These chains are then joined together into a three-dimensional network by corner sharing with trans-[Ni(H(2)O)(2)F(4)] octahedra. Crystallographic data: 1, orthorhombic, space group Cmcm, a = 14.3383(8) A, b = 15.6867(8) A, c = 8.0282(4) A, Z = 8; 2, hexagonal, space group P6(3)/mmc, a = 7.9863(5) A, c = 16.566(1) A, Z = 2; 3, monoclinic, space group C2/c, a = 12.059(1) A, b = 6.8895(6) A, c = 7.9351(7) A, beta = 92.833(2) degrees, Z = 4.     

New vanadium selenites: centrosymmetric Ca2(VO2)2(SeO3)3(H2O)2, Sr2(VO2)2(SeO3)3, and Ba(V2O5)(SeO3), and noncentrosymmetric and polar A4(VO2)2(SeO3)4(Se2O5) (A = Sr2+ or Pb2+)

Five new vanadium selenites, Ca(2)(VO(2))(2)(SeO(3))(3)(H(2)O)(2), Sr(2)(VO(2))(2)(SeO(3))(3), Ba(V(2)O(5))(SeO(3)), Sr(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)), and Pb(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)), have been synthesized and characterized. Their crystal structures were determined by single crystal X-ray diffraction. The compounds exhibit one- or two-dimensional structures consisting of corner- and edge-shared VO(4), VO(5), VO(6), and SeO(3) polyhedra. Of the reported materials, A(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)) (A = Sr(2+) or Pb(2+)) are noncentrosymmetric (NCS) and polar. Powder second-harmonic generation (SHG) measurements revealed SHG efficiencies of approximately 130 and 150 × α-SiO(2) for Sr(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)) and Pb(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)), respectively. Piezoelectric charge constants of 43 and 53 pm/V, and pyroelectric coefficients of -27 and -42 μC/m(2)·K at 70 °C were obtained for Sr(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)) and Pb(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)), respectively. Frequency dependent polarization measurements confirmed that the materials are not ferroelectric, that is, the observed polarization cannot be reversed. In addition, the lone-pair on the Se(4+) cation may be considered as stereo-active consistent with calculations. For all of the reported materials, infrared, UV-vis, thermogravimetric, and differential thermal analysis measurements were performed. Crystal data: Ca(2)(VO(2))(2)(SeO(3))(3)(H(2)O)(2), orthorhombic, space group Pnma (No. 62), a = 7.827(4) ?, b = 16.764(5) ?, c = 9.679(5) ?, V = 1270.1(9) ?(3), and Z = 4; Sr(2)(VO(2))(2)(SeO(3))(3), monoclinic, space group P2(1)/c (No. 12), a = 14.739(13) ?, b = 9.788(8) ?, c = 8.440(7) ?, β = 96.881(11)°, V = 1208.8(18) ?(3), and Z = 4; Ba(V(2)O(5))(SeO(3)), orthorhombic, space group Pnma (No. 62), a = 13.9287(7) ?, b = 5.3787(3) ?, c = 8.9853(5) ?, V = 673.16(6) ?(3), and Z = 4; Sr(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)), orthorhombic, space group Fdd2 (No. 43), a = 25.161(3) ?, b = 12.1579(15) ?, c = 12.8592(16) ?, V = 3933.7(8) ?(3), and Z = 8; Pb(4)(VO(2))(2)(SeO(3))(4)(Se(2)O(5)), orthorhombic, space group Fdd2 (No. 43), a = 25.029(2) ?, b = 12.2147(10) ?, c = 13.0154(10) ?, V = 3979.1(6) ?(3), and Z = 8.     

Explorations of new quaternary phases in the Ln(III)-V(V)(d0)-Se(IV)-O (Ln = Nd, Eu, Gd, Tb) systems

Systematic explorations of new phases in the Ln(III)-V(V)-Se(IV)-O systems by hydrothermal syntheses led to four new quaternary compounds, namely, Nd(2)(V(V)(2)O(4))(SeO(3))(4)·H(2)O (1), Ln(V(V)O(2))(SeO(3))(2) (Ln = Eu 2, Gd 3, Tb 4). The structure of Nd(2)(V(V)(2)O(4))(SeO(3))(4)·H(2)O features a 3D framework composed of the 2D layers of [N d(SeO(3))](+) bridged by the infinite [VO(2)(SeO(3))](-) chains with the lattice water molecules located at the 6-membered ring tunnels formed. The structure of Ln(V(V)O(2))(SeO(3))(2) (Ln = Eu, Gd, Tb) also features a 3D framework composed of 2D layers of [Ln(SeO(3))](+) bridged by the infinite [(VO(2))(SeO(3))](-) double chains. The 1D vanadium oxide selenite chain of 1 differs significantly from those in compounds 2-4 in terms of the coordination modes of the selenite groups and the connectivities between neighbouring VO(6) octahedra. Luminescent and magnetic properties of these compounds were also measured.