Effect of annealing temperature and annealing atmosphere on the structure and optical properties of ZnO thin films on sapphire (0 0 0 1) substrates by magnetron sputtering

ZnO thin films were epitaxially grown on sapphire (0 0 0 1) substrates by radio frequency magnetron sputtering. ZnO thin films were then annealed at different temperatures in air and in various atmospheres at 800 °C, respectively. The effect of the annealing temperature and annealing atmosphere on the structure and optical properties of ZnO thin films are investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), photoluminescence (PL). A strong (0 0 2) diffraction peak of all ZnO thin films shows a polycrystalline hexagonal wurtzite structure and high preferential c-axis orientation. XRD and AFM results reveal that the better structural quality, relatively smaller tensile stress, smooth, uniform of ZnO thin films were obtained when annealed at 800 °C in N₂. Room temperature PL spectrum can be divided into the UV emission and the Visible broad band emission. The UV emission can be attributed to the near band edge emission (NBE) and the Visible broad band emission can be ascribed to the deep level emissions (DLE). By analyzing our experimental results, we recommend that the deep-level emission correspond to oxygen vacancy (V_O) and interstitial oxygen (O_i). The biggest ratio of the PL intensity of UV emission to that of visible emission (I_NBE/I_DLE) is observed from ZnO thin films annealed at 800 °C in N₂. Therefore, we suggest that annealing temperature of 800 °C and annealing atmosphere of N₂ are the most suitable annealing conditions for obtaining high quality ZnO thin films with good luminescence performance.     

Physico-chemical, optical and electrochemical properties of iron oxide thin films prepared by spray pyrolysis

Iron oxide thin films were prepared by spray pyrolysis technique onto glass substrates from iron chloride solution. They were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and (UV-vis) spectroscopy. The films deposited at T_s ≤ 450 °C were amorphous; while those produced at T_sub = 500 °C were polycrystalline α-Fe₂O₃ with a preferential orientation along the (1 0 4) direction. By observing scanning electron microscopy (SEM), it was seen that iron oxide films were relatively homogeneous uniform and had a good adherence to the glass substrates. The grain size was found (by RX) between 19 and 25 nm. The composition of these films was examined by X-ray photoelectron spectroscopy and electron probe microanalysis (EPMA). These films exhibited also a transmittance value about 80% in the visible and infrared range. The cyclic voltammetry study showed that the films of Fe₂O₃ deposited on ITO pre-coated glass substrates were capable of charge insertion/extraction when immersed in an electrolyte of propylene carbonate (PC) with 0.5 M LiCLO₄.     

Growth of oxide thin films for optical gas sensor applications

Tungsten trioxide and titanium dioxide thin films were synthesised by pulsed laser deposition. We used for irradiations of oxide targets an UV KrF* (λ = 248 nm, τ_FWHM ≅ 20 ns, ν = 2 Hz) excimer laser source, at 2 J/cm² incident fluence value. The experiments were performed in low oxygen pressure. The (0 0 1) SiO₂ substrates were heated during the thin film deposition process at temperature values within the 300-500 °C range. The structure and crystalline status of the obtained oxide thin films were investigated by high resolution transmission electron microscopy. Our analyses show that the films are composed by nanoparticles with average diameters from a few to a few tens of nm. Moreover, the films deposited at substrate temperatures higher than 300 °C are crystalline. The tungsten trioxide films consist of a mixture of triclinic and monoclinic phases, while the titanium dioxide films structure corresponds to the tetragonal anatase phase. The oxide films average transmittance in the visible-infrared spectral range is higher than 80%, which makes them suitable for sensor applications.     

Modified thermal evaporation process using GeO2 for growing ZnO structures

In the current work, zinc oxide (ZnO) nano/microstructures are synthesized using a modified thermal-evaporation process by introducing germanium oxide (GeO₂) powder mixed with metallic Zn powder as the raw material. Without the use of any catalyst and oxygen flow in the furnace system, GeO₂ is utilized to provide an oxygen source for the growth of ZnO structure. The samples are treated by different temperatures ranging from 500 to 900 °C. Morphology, phase structure, and photoluminescence properties are investigated by scanning electron microscopy (SEM), X-ray diffractometer (XRD) and photoluminescence (PL) spectrometer. The structures and morphologies of the samples were found to vary with growth temperature. The XRD diffraction peaks show that the films grown at temperature from 600 to 800 °C consist of hexagonal wurtzite ZnO structures. Room-temperature PL measurement revealed ZnO spectra representing two bands: near-band-edge emission in the ultraviolet (UV) region and broad deep-level emission centered at about 500 nm. The strong UV emission in the PL spectra indicates that the GeO₂ supplies sufficient oxygen for formation of ZnO structures with few oxygen vacancies. The growth mechanism and the roles of GeO₂ for formation of ZnO structures are discussed in detail.     

Influence of annealing temperature on structural and optical properties of ZnO: In thin films prepared by ultrasonic spray technique

Transparent conducting indium doped zinc oxide was deposited on glass substrate by ultrasonic spray method. The In doped ZnO samples with indium concentration of 3 wt.% were deposited at 300, 350 and 400 °C with 2 min of deposition time. The effects of substrate temperature and annealing temperature on the structural, electrical and optical properties were examined. The DRX analyses indicated that In doped ZnO films have polycrystalline nature and hexagonal wurtzite structure with (0 0 2) preferential orientation and the maximum average crystallite size of ZnO: In before and annealed at 500 °C were 45.78 and 55.47 nm at a substrate temperature of 350 °C. The crystallinity of the thin films increased by increasing the substrate temperature up 350 °C, the crystallinity improved after annealing temperature at 500 °C. The film annealed at 500 °C and deposited at 350 °C show lower absorption within the visible wavelength region. The band gap energy increased from E_g = 3.25 to 3.36 eV for without annealing and annealed films at 500 °C, respectively, indicating that the increase in the transition tail width. This is due to the increase in the electrical conductivity of the films after annealing temperature.     

Effect of UV lamp irradiation during oxidation of Zr/Pt/Si structure on electrical properties of Pt/ZrO2/Pt/Si structure

Metal-insulator-metal (MIM) capacitors were fabricated using ZrO₂ films and the effects of structural and native defects of the ZrO₂ films on the electrical and dielectric properties were investigated. For preparing ZrO₂ films, Zr films were deposited on Pt/Si substrates by ion beam deposition (IBD) system with/without substrate bias voltages and oxidized at 200 °C for 60 min under 0.1 MPa O₂ atmosphere with/without UV light irradiation (λ = 193 nm, Deep UV lamp). The ZrO₂(∼12 nm) films on Pt(∼100 nm)/Si were characterized by X-ray diffraction pattern (XRD), field emission scanning electron microscopy (FE-SEM) and high-resolution transmission electron microscopy (HRTEM), capacitance-voltage (C-V) and current-voltage (I-V) measurements were carried out on MIM structures. ZrO₂ films, fabricated by oxidizing the Zr film deposited with substrate bias voltage under UV light irradiation, show the highest capacitance (784 pF) and the lowest leakage current density. The active oxygen species formed by UV irradiation are considered to play an important role in the reduction of the leakage current density, because they can reduce the density of oxygen vacancies.     

Effect of post-annealing on the properties of copper oxide thin films obtained from the oxidation of evaporated metallic copper

Thin films of copper oxide were obtained through thermal oxidation (100-450 °C) of evaporated metallic copper (Cu) films on glass substrates. The X-ray diffraction (XRD) studies confirmed the cubic Cu phase of the as-deposited films. The films annealed at 100 °C showed mixed Cu-Cu₂O phase, whereas those annealed between 200 and 300 °C showed a single cubic Cu₂O phase. A single monoclinic CuO phase was obtained from the films annealed between 350 and 450 °C. The positive sign of the Hall coefficient confirmed the p-type conductivity in the films with Cu₂O phase. However, a relatively poor crystallinity of these films limited the p-type characteristics. The films with Cu and CuO phases show n-type conductivity. The surface of the as-deposited is smooth (RMS roughness of 1.47 nm) and comprised of uniformly distributed grains (AFM and SEM analysis). The post-annealing is found to be effective on the distribution of grains and their sizes. The poor transmittance of the as-deposited films (<1%) is increased to a maximum of ∼80% (800 nm) on annealing at 200 °C. The direct allowed band gap is varied between 2.03 and 3.02 eV.     

Deposition of quasi-crystal Al-doped ZnO thin films for photovoltaic device applications

Quasi-crystal aluminum-doped zinc oxide (AZO) films were prepared by in situ radio frequency (RF) magnetron sputtering (sputtering without annealing) on glass substrates. The influence of deposition parameters on the optoelectronic and structural properties of the in situ deposited quasi-crystal AZO films was investigated in order to compare resulting samples. X-ray diffraction (XRD) patterns show that the quasi-crystal AZO thin films have excellent crystallization improved with increase of the RF power and substrate temperature, with an extremely preferential c-axis orientation exhibit sharp and narrow XRD pattern similar to that of single-crystal. Field emission scanning electron microscopy (FESEM) images show that quasi-crystal AZO thin films have uniform grains and the grain size increase with the increase of RF power and substrate temperature. Craters of irregular size with the columnar structure are observed in the quasi-crystal AZO thin films at a lower substrate temperature while many spherical shaped grains appeared at a higher substrate temperature. The average optical transmittance of all the quasi-crystal AZO films was over 85% in the 400-800 nm wavelength range. The resistivity of 4.176 × 10⁻⁴ Ω cm with the grain size of 76.4891 nm was obtained in the quasi-crystal AZO thin film deposited at 300 °C, under sputtering power of 140 W.     

Effects of post-thermal annealing temperature on the optical and structural properties of gold particles on silicon suboxide films

In this work, silicon suboxide (SiO_x) thin films were deposited using a RF magnetron sputtering system. A thin layer of gold (Au) with a thickness of about 10 nm was sputtered onto the surface of the deposited SiO_x films prior to the thermal annealing process at 400 °C, 600 °C, 800 °C and 1000 °C. The optical and structural properties of the samples were studied using scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), X-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR) and optical transmission and reflection spectroscopy. SEM analyses demonstrated that the samples annealed at different temperatures produced different Au particle sizes and shapes. SiO_x nanowires were found in the sample annealed at 1000 °C. Au particles induce the crystallinity of SiO_x thin films in the post-thermal annealing process at different temperatures. These annealed samples produced silicon nanocrystallites with sizes of less than 4 nm, and the Au nanocrystallite sizes were in the range of 7-23 nm. With increased annealing temperature, the bond angle of the Si-O bond increased and the optical energy gap of the thin films decreased. The appearance of broad surface plasmon resonance absorption peaks in the region of 590-740 nm was observed due to the inclusion of Au particles in the samples. The results show that the position and intensity of the surface plasmon resonance peaks can be greatly influenced by the size, shape and distribution of Au particles.     

Effect of annealing on the properties of N-doped ZnO films deposited by RF magnetron sputtering

N-doped ZnO films were deposited by RF magnetron sputtering in N₂/Ar gas mixture and were post-annealed at different temperatures (T_a) ranging from 400 to 800 °C in O₂ gas at atmospheric pressure. The as-deposited and post-annealed films were characterized by their structural (XRD), compositional (SIMS, XPS), optical (UV-vis-NIR spectrometry), electrical (Hall measurements), and optoelectronic properties (PL spectra). The XRD results authenticate the improvement of crystallinity following post-annealing. The weak intensity of the (0 0 2) reflection obtained for the as-deposited N-doped ZnO films was increased with the increasing T_a to become the preferred orientation at higher T_a (800 °C). The amount of N-concentration and the chemical states of N element in ZnO films were changed with the T_a, especially above 400 °C. The average visible transmittance (400-800 nm) of the as-deposited films (26%) was increased with the increasing T_a to reach a maximum of 75% at 600 °C but then decreased. In the PL spectra, A⁰X emission at 3.321 eV was observed for T_a = 400 °C besides the main D⁰X emission. The intensity of the A⁰X emission was decreased with the increasing T_a whereas D⁰X emission became sharper and more optical emission centers were observed when T_a is increased above 400 °C.     

Synthesis of P-type transparent conducting silver:indium oxide (AIO) thin films by reactive electron beam evaporation technique

Present paper reports the synthesis, electrical and optical properties of p-type conducting and transparent silver indium oxide (AIO) thin films prepared on glass substrates by reactive electron beam evaporation technique at three substrate temperatures (50, 200 and 250 °C) and at five evaporation rates (0.05 to 16.0 nm/s). The source material is pure powders of Ag₂O:In₂O₃=50:50 mol%. The AIO films are amorphous. The films, though not corresponding to Delafossite crystal structure, exhibit p-type conductivity, when prepared at an evaporation rate of 0.05 nm/s at all the three substrate temperatures. With increasing filament current, it is observed that (i) the electrical resistivity decreases and (ii) the refractive index of the films (at 632.8 nm, and is in the range: 1.219-1.211) decreases. The work function (effective Fermi level) has been measured on these samples by Kelvin Probe method. The results are explained on the basis of partial ionic charge and localization of covalent bonds in the AIO thin films.     

Dielectric behavior of spin-deposited nanocrystalline nickel-zinc ferrite thin films processed by citrate-route

Nanocrystalline nickel-zinc ferrite thin films with the general formula Ni_1−xZn_xFe₂O₄, where x=0.0, 0.2, 0.4 and 0.6 were fabricated via a chemical route known as the citrate precursor route. These films were spin-deposited on indium-tin oxide coated glass, fused quartz and amorphous Si-wafer substrates, and annealed at various temperatures up to 650 °C. The films annealed below 400 °C were found to be X-ray amorphous, while the films annealed at and above 400 °C were polycrystalline exhibiting a single-phase spinel structure. The average grain size of the films evaluated by transmission electron microscopy, is found to be in the range 4-8.5 nm. The room temperature DC resistivity of the films is in the range 10³-10⁷ Ω m. Dielectric constant and dielectric loss were measured in the frequency range 100 Hz-1 MHz. Dielectric constant of the films is found to lie between 25 and 44, while the loss factor is if the order of 10⁻². The higher values of the dielectric constant for films having higher zinc concentration are attributable to the enhanced hopping between Fe²⁺ and Fe³⁺ ions in these samples. The M-H hysteresis measurement of the nickel ferrite thin films annealed at 650 °C showed narrow hysteresis loop—a characteristic of soft ferromagnetic material.     

Growth, structural and optical transport properties of nanocrystal Zn1−xCdS thin films deposited by solution growth technique (SGT) for photosensor applications

Solution Growth Technique (SGT) has been used for deposition of Zn_1−xCdS nanocrystalline thin films. Various parameters such as solution pH (10.4), deposition time, concentration of ions, composition and deposition and annealing temperatures have been optimized for the development of device grade thin film. In order to achieve uniformity and adhesiveness of thin film on glass substrate, 5 ml triethanolamine (TEA) have been added in deposition solution. The as-deposited films have been annealed in Rapid Thermal Annealing (RTA) system at various temperature ranges from 100 to 500 °C in air. The changes in structural formation and optical transport phenomena have been studied with annealing temperatures and composition value (x). As-deposited films have two phases of ZnS and CdS, which were confirmed by X-ray diffraction studies; further the X-ray analysis of annealed (380 °C) films indicates that the films have nanocrystalline size (150 nm) and crystal structure depends on the films stoichiometry and annealing temperatures. The Zn_0.4CdS films annealed at 380 °C in air for 5 min have hexagonal structure where as films annealed at 500 °C have represented the oxide phase with hexagonal structure. Optical properties of the films were studied in the wavelength range 350-1000 nm. The optical band gap (E_g=2.94-2.30 eV) decreases with the composition (x) value. The effect of air rapid annealing on the photoresponse has also been observed on Zn_1−xCdS nanocrystal thin films. The Zn_1−xCdS thin film has higher photosensitivity at higher annealing temperatures (380-500 °C), and films also have mixed Zn_1−xCdS/Zn_1−xCdSO phase with larger grain size than the as-deposited and films annealed up to 380 °C. The present results are well agreed with the results of other studies.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Structure and optical properties of nanostructured zinc oxide films with different growth temperatures

ZnO films were prepared by pulsed laser deposition (PLD) on glass substrate with temperature ranging from room temperature (RT) to 500 °C. All the films formed the hexagonal wurtzite structure and showed the c-axis (0 0 2) preferred orientation. The films deposited at 200 °C showed the narrowest full width at half maximum of both X-ray diffraction (XRD) and rocking curve, largest height grain size, smallest macrostress and least point defects. Meanwhile, it was found that the films deposited at 350 °C displayed the most intense diffraction peak in XRD and a strong UV emission while it showed the most intense defect-related green emission, fastest growth rate and larger macrostress. In addition, the cross section images showed all films grew with a columnar form along (0 0 2) orientation.     

Structural, optical and electrical properties of ZnO/Zn2GeO4 porous-like thin film and wires

Zinc oxide/zinc germanium oxide (ZnO/Zn₂GeO₄) porous-like thin film and wires has been fabricated by simple thermal evaporation method at temperature about 1120 °C for 2.5 h. The structural and optical properties of the porous-like-thin film and wires have been investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and photoluminescence (PL) spectroscopy. Metal semiconductor metal (MSM) photodetector structure was used to evaluate the electrical characteristics by using current-voltage (I-V) measurements. Room temperature photoluminescence spectrum of the sample shows one prominent ultraviolet peak at 378 nm and a shoulder at 370 nm. In addition, broad visible blue emission peak at wavelength 480 nm and green emission peak at 500 nm are also observed. Strong photoelectric properties of the MSM in the UV demonstrated that the porous-like-thin film and wires contribute to its photosensitivity and therefore making ZnO/Zn₂GeO₄ wires potential photodetector in the shorter wavelength applications.     

Defects in nanocrystalline Nb films: Effect of sputtering temperature

Thin niobium (Nb) films (thickness 350-400 nm) were prepared on (1 0 0)Si substrate in a UHV chamber using the cathode beam sputtering. The sputtering temperature T_s was varied from 40 up to 500 °C and the influence of the sputtering temperature on the microstructure of thin Nb films was investigated. Defect studies of the thin Nb films sputtered at various temperatures were performed by slow positron implantation spectroscopy (SPIS) with measurement of the Doppler broadening of the annihilation line. SPIS was combined with transmission electron microscopy (TEM) and X-ray diffraction (XRD). We have found that the films sputtered at T_s = 40 °C exhibit elongated, column-like nanocrystalline grains. No significant increase of grain size with T_s (up to 500 °C) was observed by TEM. The thin Nb films sputtered at T_s = 40 °C contain a high density of defects. It is demonstrated by shortened positron diffusion length and a high value of the S parameter for Nb layer compared to the well-annealed (defect-free) bulk Nb reference sample. A drastic decrease of defect density was found in the films sputtered at T_s ≥ 300 °C. It is reflected by a significant increase of the positron diffusion length and a decrease of the S parameter for the Nb layer. The defect density in the Nb layer is, however, still substantially higher than in the well-annealed reference bulk Nb sample. Moreover, there is a layer at the interface between the Nb film and the substrate with very high density of defects comparable to that in the films sputtered at T_s < 300 °C. All the Nb films studied exhibit a strong (1 1 0) texture. The films sputtered at T_s < 300 °C are characterized by a compressive macroscopic in-plane stress due to lattice mismatch between the film and the substrate. Relaxation of the in-plane stress was observed in the films sputtered at T_s ≥ 300 °C. The width of the XRD profiles of the films sputtered at T_s ≥ 300 °C is significantly smaller compared to the films sputtered at lower temperatures. This is most probably due to a lower defect density which results in reduced microstrains in the films sputtered at higher temperatures.     

Pure UV photoluminescence from ZnO thin film by thermal retardation and using an amorphous SiO2 buffer layer

ZnO/SiO₂ thin films were fabricated on Si substrates by E-beam evaporation with thermal retardation. The as-prepared films were annealed for 2 h every 100 °C in the temperature range 400-800 °C under ambient air. The structural and optical properties were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM) and photoluminescence (PL). The XRD analysis indicated that all ZnO thin films had a highly preferred orientation with the c-axis perpendicular to the substrate. From AFM images (AFM scan size is 1 μm×1 μm), the RMS roughnesses of the films were 3.82, 5.18, 3.65, 3.40 and 13.2 nm, respectively. PL measurements indicated that UV luminescence at only 374 nm was observed for all samples. The optical quality of the ZnO film was increased by thermal retardation and by using an amorphous SiO₂ buffer layer.     

Effect of ZnO on phase emergence, microstructure and surface modifications of calcium phosphosilicate glass/glass-ceramics having iron oxide

The effect of ZnO on phase emergence and microstructure properties of glass and glass-ceramics with composition 25SiO₂-50CaO-15P₂O₅-(10 − x)Fe₂O₃-xZnO (where x = 0, 2, 5, 7 mol%) has been studied. They have been characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Surface modifications of these glass-ceramics in simulated body fluid have been studied using Fourier transform infrared reflection spectroscopy (FTIR), XPS and SEM. Results have shown a decrease in the fraction of non-bridging oxygen with increase in zinc oxide content. Emergence of crystalline phases in glass-ceramics at different heat treatment temperatures was studied using XRD. When glass is heat treated at 800 °C calcium phosphate, hematite and magnetite are developed as major phases in the glass-ceramics samples with ZnO up to 5 mol%. In addition to these, calcium silicate (Ca₃Si₂O₇) phase is also observed when glass is heat treated at 1000 °C. The microstructure of the glass-ceramics heat treated at 800 °C exhibits the formation of nano-size (40-50 nm) grains. On heat treatment at 1000 °C crystallites grow to above 50 nm size and more than one phase are observed in the microstructure. The formation of thin flake-like structure with coarse particles is observed at high zinc oxide concentration (x = 7 mol%). In vitro studies have shown the surface modifications and formation of Ca-P-rich layer on the glass-ceramics when immersed in simulated body fluids (SBF) for different durations. The bioactive response was found to depend on ZnO content.     

Influence of temperature annealing on optical properties of SrTiO3/BaTiO3 multilayered films on indium tin oxide

We have prepared SrTiO₃/BaTiO₃ thin films with multilayered structures deposited on indium tin oxide (ITO) coated glass by a sol-gel deposition and heating at 300-650 °C. The optical properties were obtained by UV-vis spectroscopy. The films show a high transmittance (approximately 85%) in the visible region. The optical band gap of the films is tunable in the 3.64-4.19 eV range by varying the annealing temperature. An abrupt decrease towards the bulk band gap value is observed at annealing temperatures above 600 °C. The multilayered film annealed at 650 ° C exhibited the maximum refractive index of 2.09-1.91 in the 450-750 nm wavelength range. The XRD and AFM results indicate that the films annealed above 600 ° C are substantially more crystalline than the films prepared at lower temperatures which were used to change their optical band gap and complex refractive index to an extent that depended on the annealing temperature.