Soft magnetic properties of FeCo films with Co underlayer

Bilayered Fe₆₅Co₃₅ (=FeCo)/Co films were prepared by facing targets sputtering with 4πM_s∼24 kg. The soft magnetic properties of FeCo films were induced by a Co underlayer. H_c decreased rapidly when the Co underlayer was 2 nm or more. The films showed well-defined in-plane uniaxial anisotropy with the typical values of H_ce=10 Oe and H_ch=3 Oe, respectively. High frequency characteristics of the films show the films can work at 0.8 GHz with real permeability as high as 250.     

Microstructure and microwave permeability of FeCo thin films with Co underlayer

Microstructure, static magnetic properties and microwave permeability of sputtered FeCo films were examined. Fe₆₀Co₄₀ films (100 nm in thickness) deposited on glass substrates exhibited in-plane isotropy and a large coercivity of 161.1 Oe. When same thickness films were deposited on 2.5 nm Co underlayer, well-defined in-plane anisotropy was formed with an anisotropy field of 65 Oe. The sample had a static initial permeability of about 285, maximum imaginary permeability of 1255 and ferromagnetic resonance frequency of 2.71 GHz. Cross-sectional TEM image revealed that the Co underlayer had induced a columnar grain structure with grain diameter of 10 nm in the FeCo films. In comparison, FeCo films without Co underlayer showed larger grains of 70 nm in diameter with fewer distinct vertical grain boundaries. In addition, the Co underlayer changed the preferred orientation of the FeCo from (1 0 0) to (1 1 0). The improvement in soft magnetic properties and microwave behavior originates from the modification of the film microstructure, which can be well understood by the random anisotropy theory.     

Effects of the Hf content on the microstructure and magnetic properties of Co-Hf-Ta thin films

Effects of the Hf content in Co-Hf-Ta thin films on the microstructure and magnetic properties were investigated in this study. It was found that appropriate Hf addition can effectively refine the Co grain size. Co grain sizes sharply decreased from 50 nm down to 2.3 nm with increasing the Hf content from 1.02 at.% to 2.81 at.%, leading to the reduced magneto-crystalline anisotropy. The Co-Hf-Ta thin films with small Co grains reveal low anisotropy field, low coercivity, and high resistivity. By optimizing the Hf content, the film with Hf concentration of 2.81 at.% exhibits excellent soft magnetic properties: high saturation magnetization (4πM_S ∼ 13.6 kG), and low coercivity (H_C ∼ 0.6 Oe). The effective permeability of the film reaches 800 and remains constant up to 1 GHz.     

Effect of Cr100−xTix (x = 0-19 at.%) alloy underlayers on the high coercivity of FePt thin film below the substrate temperature of 250 °C

The effect of Cr_100−xTi_x underlayer on orderd-L1₀ FePt films was investigated. A low-temperature ordering of FePt films could be attained through changing the Ti content of Cr_100−xTi_x underlayer. The ordering temperature of the 30 nm FePt film grown on 20 nm Cr₉₀Ti₁₀ underlayer was reduced to 250 °C which is practical manufacture process temperature. An in-plane coercivity was very high to 6000 Oe and a ratio of remnant magnetization (M_r) to saturation magnetization (M_s) was as large as 0.85. This result indicates that the coercivity obtained at 250 °C by the effect of CrTi underlayer is significantly higher than those obtained at 250-275 °C by the effect of underlayers in other conventional studies. The prominent improvement of the magnetic properties of ordered FePt thin films at low temperature of 250 °C could be understood with considering the strain-induced ordering phase transformation associated with lattice mismatch between Cr underlayer and FePt magnetic layer due to an addition of Ti content.     

Microstructure and magnetic properties of nanocomposite FePt/MgO and FePt/Ag films

An in-plane magnetic anisotropy of FePt film is obtained in the MgO 5 nm/FePt t nm/MgO 5 nm films (where t=5, 10 and 20 nm). Both the in-plane coercivity (H_c∥) and the perpendicular magnetic anisotropy of FePt films are increased when introducing an Ag-capped layer instead of MgO-capped layer. An in-plane coercivity is 3154 Oe for the MgO 5 nm/FePt 10 nm/MgO 5 nm film, and it can be increased to 4846 Oe as a 5 nm Ag-capped layer instead of MgO-capped layer. The transmission electron microscopy (TEM)-energy disperse spectrum (EDS) analysis shows that the Ag mainly distributed at the grain boundary of FePt, that leads the increase of the grain boundary energy, which will enhance coercivity and perpendicular magnetic anisotropy of FePt film.     

Amorphous Ni-Al underlayer-accelerated L10 ordering transition of FePt thin films

In the present study, we succeeded in accelerating the L1₀ ordering transition of FePt thin films by employing amorphous Ni-Al as underlayers. The coercivity H_c = 5 kOe and ordering parameter S = 0.67 of FePt thin films deposited on a Ni-Al underlayer with a thickness of ∼5 nm after 380 °C annealing for 30 min are significantly higher than those H_c = 0.4 kOe and S = 0.35 of the films without the Ni-Al underlayer. The L1₀ ordering process of and the coercivity of FePt thin films can be significantly tuned by varying the thickness of the Ni-Al underlayer.     

Effect of oxygen pressure on microstructure and magnetic properties of strontium hexaferrite (SrFe12O19) film prepared by pulsed laser deposition

The effects of oxygen pressure during deposition on microstructure and magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films grown on Si (100) substrate with Pt (111) underlayer by pulsed laser deposition have been investigated. X-ray diffraction pattern confirms that the films have c-axis perpendicular orientation. The c-axis dispersion (Δθ₅₀) increases and c-axis lattice parameter decreases with increasing oxygen pressure. The films have hexagonal shape grains with diameter of 150-250 nm as determined by atomic force microscopy. The coercivities in perpendicular direction are higher than those in in-plane direction, which shows the films have perpendicular magnetic anisotropy. The saturation magnetization and anisotropy field for the film deposited in oxygen pressure of 0.13 mbar are comparable to those of the bulk strontium hexaferrite. Higher oxygen pressure leads to the films having higher coercivity and squareness. The coercivity in perpendicular and in-plane directions of the film deposited in oxygen pressure of 0.13 mbar are 2520 Oe and 870 Oe, respectively.     

Exchange coupling in CoO–Co bilayer

In this work, exchange bias and coercivity enhancement in ferromagnet (FM)–antiferromagnet (AFM) bilayer have been investigated. CoO film (50 nm) was deposited by sputtering with a relatively high oxygen partial pressure. The deposited films were subsequently annealed at varied temperature up to 973 K in the air atmosphere. The CoO film shows a disordered structure in the as-deposited state and an increase of crystallinity after annealing characterized by XRD and Raman spectra. A 40-nm Co film was deposited on the as-deposited CoO and annealed films. The Co–CoO bilayer shows a large exchange bias up to 1600 Oe and relatively high coercivity up to 3200 Oe (H_C−) at 5 K, which is much larger than that of crystalline Co–CoO bilayer films without any treatment. The spin glass behavior combined with increasing crystallinity, surface roughness of CoO after annealing may be attributed to the large exchange bias and high coercivity.     

Magnetic properties of strontium hexaferrite films prepared by pulsed laser deposition

The magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films fabricated by pulsed laser deposition on the Si(100) substrate with Pt(111) underlayer have been studied as a function of film thickness (50–700 nm). X-ray diffraction patterns confirm that the films have c-axis perpendicular orientation. The coercivities in perpendicular direction are higher than those for in-plane direction which indicates the films have perpendicular magnetic anisotropy. The coercivity was found to decrease with increasing of thickness, due to the increasing of the grain size and relaxation in lattice strain. The 200 nm thick film exhibits hexagonal shape grains of 150 nm and optimum magnetic properties of M_s=298 emu/cm³ and H_c=2540 Oe.     

Synthesis and characterization of Ni-doped ZnO: A transparent magnetic semiconductor

We report synthesis of a transparent magnetic semiconductor by incorporating Ni in zinc oxide (ZnO) matrix. ZnO and nickel-doped zinc oxide (ZnO:Ni) thin films (∼60 nm) are prepared by fast atom beam (FAB) sputtering. Both undoped and doped films show the presence of ZnO phase only. The Ni concentration (in at%) as determined by energy dispersive X-ray (EDX) technique is ∼12±2%. Magnetisation measurement using a SQUID magnetometer shows that the Ni-doped films are ferromagnetic, having coercivity (H_c) values 192, 310 and 100 Oe and saturation magnetization (M_s) values of 6.22, 5.32 and 4.73 emu/g at 5, 15 and 300 K, respectively. The Ni-doped film is transparent (>80%) across visible wavelength range. Resistivity of the ZnO:Ni film is ∼2.5×10⁻³ Ω cm, which is almost two orders of magnitude lower than the resistivity (∼4.5×10⁻¹ Ω cm) of its undoped counterpart. Impurity d-band splitting is considered to be the cause of increase in conductivity. Interaction between free charges generated by doping and localized d spins of Ni is discussed as the reason for ferromagnetism in the ZnO:Ni film.     

Exchange coupling and remanence enhancement in nanocomposite Nd–Fe–B/FeCo multilayer films

Nd–Fe–B-type hard phase single layer films and nanocomposite Nd₂₈Fe₆₆B₆/Fe₅₀Co₅₀ multilayer films with Mo underlayers and overlayers have been fabricated on Si substrates by rf sputtering. The hysteresis loops of all films indicated simple single loops for fixed Nd–Fe–B layer thickness (10 nm) and different FeCo layer thickness (d_FeCo=1–50 nm). The remanence of these films is found to increase with increasing d_FeCo and the coercivity decrease with increasing d_FeCo. It is shown that high remanence is achieved in the nanocomposite multilayer films consisting of the hard magnetic Nd–Fe–B-type phase and soft magnetic phase FeCo with 20 nm?d_FeCo?3 nm. The sample of maximum energy product is 27 MG Oe for d_FeCo=5 nm at room temperature. The enhancement of the remanence and energy products in nanocomposite multilayer films is attributed to the exchange coupling between the magnetically soft and hard phases.     

Thickness-dependent magnetization reversal in CoZrNb amorphous films

Structure and magnetization of CoZrNb amorphous films prepared by DC magnetron sputtering have been studied as a function of film thickness (t), from 35 to 840 nm. Using comprehensive characterization, we show that the CoZrNb amorphous films possess a single phase and no nanocrystalline can be detected. The magnetic measurements indicate that the magnetization reversal of CoZrNb films is strongly dependent on t. That is, the coercivity is abruptly reduced to be lower than 4 Oe with t increasing from 35 to 105 nm, and then gradually decreases to ∼0.2 Oe as t increases. This coercivity transition versus t is accompanied by the strong magnetization reversal when t is larger than 105 nm. The results reveal that CoZrNb amorphous films with comparatively large film thickness (>100 nm) are suitable for sensors and anti-faked materials.     

Growth temperature dependence of the hysteretic behavior of Ni0.5Zn0.5Fe2O4 thin films

Herein, a discussion of the effect of deposition temperature on the magnetic behavior of Ni_0.5Zn_0.5Fe₂O₄ thin films. The thin films were grown by r.f. sputtering technique on (1 0 0) MgO single-crystal substrates at deposition temperatures ranging between 400 and 800 °C. The grain boundary microstructure was analyzed via atomic force microscopy (AFM). AFM images show that grain size (φ∼70-112 nm) increases with increasing deposition temperature, according to a diffusion growth model. From magneto-optical Kerr effect (MOKE) measurements at room temperature, coercive fields, H_c, between 37and 131 Oe were measured. The coercive field, H_c, as a function of grain size, reaches a maximum value of 131 Oe for φ ∼93 nm, while the relative saturation magnetization exhibits a minimum value at this grain size. The behaviors observed were interpreted as the existence of a critical size for the transition from single- to multi-domain regime. The saturation magnetization (21 emu/g<M_s<60 emu/g) was employed to quantify the critical magnetic intergranular correlation length (L_c≈166 nm), where a single-grain to coupled-grain behavior transition occurs. Experimental hysteresis loops were fitted by the Jiles-Atherton model (JAM). The value of the k-parameter of the JAM fitted by means of this model (k/μ_o∼50 A m²) was correlated to the domain size from the behavior of k, we observed a maximum in the density of defects for the sample with φ∼93 nm.     

Low-temperature ordering and enhanced coercivity of L10-FePt thin films with Al underlayer

FePt multilayer films with and without Al underlayer were prepared by magnetron sputtering on SiO₂ substrate and subsequently annealed in vacuum. Experimental results suggest that the existence of Al underlayer can effectively reduce the ordering temperature and increase the coercivity of FePt films. Due to the slight larger lattice constant of Al underlayer than that of FePt films, [Fe (0.66 nm)/Pt (0.84 nm)]₃₀ films begin to order at 350 °C and the coercivity of them reach to 5.7 kOe after annealing at 400 °C for half an hour.     

Studies on high-moment soft magnetic FeCo/Co thin films

The dependences of soft magnetic properties and microstructures of the sputtered FeCo (=FeFeCo薄膜 溅射条件 软磁性 高饱和磁化强度FeCo film, sputtering conditions, high saturation magnetization, soft magnetic properties2005-10-263/7/2006 12:00:00 AMThe dependences of soft magnetic properties and microstructures of the sputtered FeCo （=Fe65Co35） films on Co underlayer thickness tCo, FeCo thickness tFeCo, substrate temperature Ts and taxget-substrate spacing dT-s are studied. FeCo single layer generally shows a high coercivity with no obvious magnetic anisotropy. Excellent soft magnetic properties with saturation magnetization μ0Ms of 2.35 T and hard axis coercivity Hch of 0.25 kA/m in FeCo films can be achieved by introducing a Co underlayer. It is shown that sandwiching a Co underlayer causes a change in orientation and reduction in grain size from 70 nm to about 10 nm in the FeCo layer. The magnetic softness can be explained by the Hoffmann＇s ripple theory due to the effect of grain size. The magnetic anisotropy can be controlled by changing dT-S, and a maximum of 14.3 kA/m for anisotropic field Hk is obtained with dT-S=18.0 cm.     

Low-temperature ordering of L10 FePt phase in FePt thin film with AgCu underlayer

FePt (20 nm) films with AgCu (20 nm) underlayer were prepared on thermally oxidized Si (0 0 1) substrates at room temperature by using dc magnetron sputtering, and the films annealed at different temperature to examine the disorder–order transformation of the FePt films. It is found that the ordered L1₀ FePt phase can form at low annealing temperature. Even after annealing at 300 °C, the in-plane coercivity of 5.2 kOe can be obtained in the film. With increase in annealing temperature, both the ordering degree and coercivity of the films increase. The low-temperature ordering of the films may result from the dynamic stress produced by phase separation in AgCu underlayer and Cu diffusion into FePt phase during annealing.     

Structural and magnetic properties of self-assembled Sm-Co spherical aggregates

Self-assembled Sm-Co nanoparticles in the form of spherical aggregates (referred as nanospheres) with diameter ranging from 50 to 180 nm were achieved by means of polyol technique. The size distribution of the Sm-Co nanospheres can be regulated close to ∼100 nm by controlling the molar ratio of Sm:Co precursor. The spherical aggregates exhibited Sm₂Co₇ phase as a major constituent; while the aggregates obtained at higher Co concentration showed co-existence of Co-phase with Sm₂Co₇ phase. Upon annealing, the biphasic nature of nanospheres (Sm₂Co₇/Co) transformed into Sm₂Co₁₇ structure. By varying the Sm:Co precursor ratio from 1:5 to 1:9, the coercivity (H_c) and magnetization (M_s) values of the as-synthesized nanospheres can be tuned from 336 to 140 Oe and from 63.7 to 108 emu/g, respectively, and these values significantly improved after annealing. Maximum values of H_c (1050 Oe) at the Sm:Co molar ratio of 1:5 and M_s of 184.6 emu/g at the Sm:Co molar ratio of 1:9 were achieved in the annealed samples.     

Enhanced antiferromagnetic coupling in dual-synthetic antiferromagnet with Co2FeAl electrodes

We study dual-synthetic antiferromagnets (DSyAFs) using Co₂FeAl (CFA) Heusler electrodes with a stack structure of Ta/CFA/Ru/CFA/Ru/CFA/Ta. When the thicknesses of the two Ru layers are 0.45 nm, 0.65 nm or 0.45 nm, 1.00 nm, the CFA-based DSyAF has a strong antiferromagnetic coupling between adjacent CFA layers at room temperature with a saturation magnetic field of ∼11,000 Oe, a saturation magnetization of ∼710 emu/cm³ and a coercivity of ∼2.0 Oe. Moreover, the DSyAF has a good thermal stability up to 400 °C, at which CFA films show B2-ordered structure. Therefore, the CFA-based DSyAFs are favorable for applications in future spintronic devices.     

Synthesis and magnetic properties of Au-coated amorphous Fe20Ni80 nanoparticles

Gold-coated nanoparticles of Fe₂₀Ni₈₀ (permalloy) have been synthesized by a microemulsion process. The as-prepared samples consist of ∼5 nm diameter particles of amorphous Fe₂₀Ni₈₀ that are likely encapsulated in B₂O₃. One or more Fe₂₀Ni₈₀@B₂O₃ particles are subsequently encapsulated in 8-20 nm gold nanospheres, as determined by TEM and X-ray powder diffraction (XRD) line broadening. The gold shells were found to be under expansive strain. Magnetic data confirm the existence of a superparamagnetic phase with a blocking temperature, T_B, of ∼33 K. The saturation magnetization, M_S, of the as-prepared, Au-coated sample is ∼65 emu g⁻¹ at 5 K and ∼16 emu g⁻¹ at 300 K. The coercivity, H_C, is ∼280 Oe at 5 K.     

Control of crystallographic orientation in L10 FePt films by using Cr and CrW underlayers

The microstructure and magnetic properties of FePt films grown on Cr and CrW underlayers were investigated. The FePt films that deposited on Cr underlayer show (2 0 0) orientation and low coercivity because of the diffusion between FePt and Cr underlayer. The misfit between FePt magnetic layer and underlayer increases by small addition of W element in Cr underlayer or using a thin Mo intermediate layer, which is favorable for the formation of (0 0 1) orientation and the transformation of FePt from fcc to fct phase. A good FePt (0 0 1) texture was obtained in the films with Cr₈₅W₁₅ underlayer with substrate temperature of 400 °C. The FePt films deposited on Mo/Cr underlayer exhibit larger coercivity than that of the films grown on Pt/Cr₈₅W₁₅ because 5 nm Mo intermediate layer depressed the diffusion of Cr into magnetic layer.