PLD of Fe3O4 thin films: Influence of background gas on surface morphology and magnetic properties

Ablation of Fe₃O₄ targets has been performed using a pulsed UV laser (KrF, λ = 248 nm, 30 ns pulse duration) onto Si(100) substrates, in reactive atmospheres of O₂ and/or Ar, with different oxygen partial pressures. The as-deposited films were characterised by atomic force microscopy (AFM), X-ray diffraction (XRD), conversion electron Mössbauer spectroscopy (CEMS) and extraction magnetometry, in order to optimise the deposition conditions in the low temperature range. The results show that a background mixture of oxygen and argon improves the Fe:O ratio in the films as long as the oxygen partial pressure is maintained in the 10⁻² Pa range. Thin films of almost stoichiometric single phase polycrystalline magnetite, Fe_2.99O₄, have been obtained at 483 K and working pressure of 7.8 × 10⁻² Pa, with a high-field magnetization of ∼490 emu/cm³ and Verwey transition temperature of 112 K, close to the values reported in the literature for bulk magnetite.     

Superparamagnetic silica nanoparticles with immobilized metal affinity ligands for protein adsorption

Superparamagnetic silica-coated magnetite (Fe₃O₄) nanoparticles with immobilized metal affinity ligands were prepared for protein adsorption. First, magnetite nanoparticles were synthesized by co-precipitating Fe²⁺ and Fe³⁺ in an ammonia solution. Then silica was coated on the Fe₃O₄ nanoparticles using a sol–gel method to obtain magnetic silica nanoparticles. The condensation product of 3-Glycidoxypropyltrimethoxysilane (GLYMO) and iminodiacetic acid (IDA) was immobilized on them and after charged with Cu²⁺, the magnetic silica nanoparticles with immobilized Cu²⁺ were applied for the adsorption of bovine serum albumin (BSA). Scanning electron micrograph showed that the magnetic silica nanoparticles with an average size of 190 nm were well dispersed without aggregation. X-ray diffraction showed the spinel structure for the magnetite particles coated with silica. Magnetic measurement revealed the magnetic silica nanoparticles were superparamagnetic and the saturation magnetization was about 15.0 emu/g. Protein adsorption results showed that the nanoparticles had high adsorption capacity for BSA (73 mg/g) and low nonspecific adsorption. The regeneration of these nanoparticles was also studied.     

Study of polydiethylsiloxane-based ferrofluid with excellent frost resistance property

The polydiethylsiloxane-based ferrofluid was prepared by dispersing finely divided magnetic Fe₃O₄ particles which are modified with oleoyl sarcosine and lauroyl sarcosine. The optimized experiment parameters including molar ratio of surfactant to Fe₃O₄ (1:5), temperature (80 °C), stirring rate (300 RPM), the surfactant content of lauroyl sarcosine (0 to 33 mol%) and the modification time (25 min) were obtained by the orthogonal test. The magnetic liquid was characterized by a transmission electron microscope (TEM), infrared (IR) spectrometer, X-ray diffractometer (XRD), thermogravimetry (TG), vibrating sample magnetometer (VSM) and differential scanning calorimetry (DSC). It is indicated that the surfactant is mainly bonded to the surface of Fe₃O₄ nanoparticles through covalent bond between carboxylate (COO⁻) and Fe atom. The modified magnetic particles are equally dispersed into the carrier and remain stable below −12 °C over 4 months. The ferrofluids exhibit excellent frost resistance property and distinctly reduced temperature coefficient of viscosity compared with polydimethylsiloxane-based ferrofluids and hydrocarbon-based ferrofluids, respectively. The saturation magnetization could reach up to 27.7 emu/g.     

Synthesis and hyperthermia property of hydroxyapatite-ferrite hybrid particles by ultrasonic spray pyrolysis

Biocompatible hybrid particles composed of hydroxyapatite (Ca₁₀(PO₄)₆(OH)₂, HAp) and ferrite (γ-Fe₂O₃ and Fe₃O₄) were synthesized using a two-step procedure. First, the ferrite particles were synthesized by co-precipitation. Second, the suspension, which was composed of ferrite particles by a co-precipitation method, Ca(NO₃)₂, and H₃PO₄ aqueous solution with surfactant, was nebulized into mist ultrasonically. Then the mist was pyrolyzed at 1000 °C to synthesize HAp-ferrite hybrid particles. The molar ratio of Fe ion and HAp was (Fe²⁺ and Fe³⁺)/HAp=6. The synthesized hybrid particle was round and dimpled, and the average diameter of a secondary particle was 740 nm. The cross section of the synthesized hybrid particles revealed two phases: HAp and ferrite. The ferrite was coated with HAp. The synthesized hybrid particles show a saturation magnetization of 11.8 emu/g. The net saturation magnetization of the ferrite component was calculated as 32.5 emu/g. The temperature increase in the AC-magnetic field (370 kHz, 1.77 kA/m) was 9 °C with 3.4 g (the ferrite component was 1.0 g). These results show that synthesized hybrid particles are biocompatible and might be useful for magnetic transport and hyperthermia studies.     

Magnetic properties of amorphous Ge–Fe thin films

Thin films of Ge_100−xFe_x (x in at%) alloys, fabricated by thermal co-evaporation, have an amorphous structure at compositions x<∼40, although an unidentified crystalline phase with an FCC symmetry also exists at low Fe content. Magnetization versus temperature curves show that saturation magnetization is non-zero (1 to 2.5 emu/cm³) and remains nearly unchanged up to the highest measured temperature of 350 K. Magnetic hysteresis loops at room temperature show a typical ferromagnetic shape, complete saturation occurring by 1–2 kOe. These results may indicate ferromagnetic ordering at room temperature. No definite tendency is observed in the compositional dependence of saturation magnetization.     

Magnetoresistance of magnetite thin films grown by pulsed laser deposition on GaAs(1 0 0) and Al2O3(0 0 0 1)

Magnetotransport properties of magnetite thin films deposited on gallium arsenide and sapphire substrates at growth temperatures between 473 and 673 K are presented. The films were grown by UV pulsed laser ablation in reactive atmospheres of O₂ and Ar, at working pressure of 8 × 10⁻² Pa. Film stoichiometry was determined in the range from Fe_2.95O₄ to Fe_2.97O₄. Randomly oriented polycrystalline thin films were grown on GaAs(1 0 0) while for the Al₂O₃(0 0 0 1) substrates the films developed a (1 1 1) preferred orientation. Interfacial Fe³⁺ diffusion was found for both substrates affecting the magnetic behaviour. The temperature dependence of the resistance and magnetoresistance of the films were measured for fields up to 6 T. Negative magnetoresistance values of ∼5% at room temperature and ∼10% at 90 K were obtained for the as-deposited magnetite films either on GaAs(1 0 0) or Al₂O₃(0 0 0 1).     

Antiferromagnetism and spin-glass transition in the FeInxCr2−xSe4 series of selenides

The magnetic behavior of the FeIn_xCr_2−xSe₄ system (with x=0.0, 0.2 and 0.4) has been investigated by magnetic and Mössbauer spectroscopy. Hyperfine parameters indicate that iron is in the Fe²⁺ oxidation state, with a minor (∼9%) Fe³⁺ fraction, located at different layers in the structure. Low-field magnetization curves as a function of temperature showed that the antiferromagnetic (AFM) order temperature is T_N=208(2) K for FeCr₂Se₄ and decreases to 174(3) K for FeIn_0.4Cr_1.6Se₄. The effective magnetic moment μ_eff decreases with increasing In contents, and shows agreement with the expected values from the contribution of Fe²⁺ (⁵D) and Cr³⁺ (⁴F) electronic states. A second, low-temperature transition is observed at T_G∼13 K, which has been assigned to the onset of a glassy state.     

Effect of anions on the phase stability of γ-FeOOH nanoparticles and the magnetic properties of gamma-ferric oxide derived from lepidocrocite

The effect of anions such as Cl⁻, SO₄²⁻, and HPO₄²⁻ on the phase stability of FeOOH (α or γ) during precipitation is investigated. Oxidation of Fe(OH)₂·xH₂O from FeCl₂ solution with high Cl⁻ concentration ([Cl⁻]/[Fe]=R_Cl≥8) or (NH₄)₂Fe(SO₄)₂ (FAS) with [HPO₄²⁻]/[Fe]=R_P≥0.02 yields phase-pure γ-FeOOH. In the medium ranges of R_Cl and R_P, mixed phases of α-FeOOH and γ-FeOOH are obtained. Replacement of OH⁻ by Cl⁻ with the bridging cations or strongly bonded HPO₄²⁻ ions in the matrix of the intermediate phase (Fe_x²⁺Fe_y³⁺(OH)_2x+2y−nz·xH₂O(A)_zⁿ⁻, where A is anions such as Cl⁻, SO₄²⁻, HPO₄²⁻, etc.), promoted the lower density γ-FeOOH. However, the particles are less developed and have poor crystallinity as evidenced from transmission electron microscope and thermogravimetry-differential thermal analysis of the precipitates. Whereas, monophasic, uniformly sized, nano-lath shaped particles with high aspect ratio >10 are obtained when morphology-controlling cation additives such as Pt⁴⁺, Pd²⁺ or Rh³⁺ are present in FeCl₂ (R_Cl≥8) solution. Preferential adsorption of additives on (0k0) and (h00) planes limits the growth in the perpendicular directions leading to high aspect ratios. The effect of these additives are suppressed by the phosphate ion, a strong complexing ligand, giving rise to fibrous aggregate with the length of individual particles as small as 10-30 nm. While most of the Cl⁻ ion is removed from the final precipitates on washing, phosphate remained as HPO₄²⁻ as evidenced from IR absorption spectra. Maghemite obtained by dehydroxylating γ-FeOOH contains randomly distributed micropores bringing in the relaxation effects of spins on the surface atoms as deciphered from Mössbauer spectroscopy. This leads to the low σ_s (44-48 emu/g) and H_c (120-130 Oe) for γ-Fe₂O_3−δ particles. Whereas nearly pore-free single crystalline particles obtained by reduction followed by reoxidation has high value of σ_s (73 emu/g) and H_c (320 Oe), which decreases to 30 emu/g and 75 Oe, respectively, for nanoparticles obtained from phosphate stabilized lepidocrocite. The mobility of iron ions and counter mobility of vacancies during the topotactic transformation of γ-FeOOH to magnetite to γ-Fe₂O_3−δ renders the particles pore-free.     

The influence of pH and bath composition on the properties of Fe-Co alloy film electrodeposition

Fe-Co films were electrodeposited on ITO glass substrates from the electrolytes with different molar ratio of Co²⁺/Fe²⁺ and different pH values (2.1, 2.9, 3.7, and 4.3) at 25 °C. The properties of Fe-Co alloy films depend on both Co²⁺ and Fe²⁺ concentrations in electrolyte and pH values was studied. The content of Co increases from 40% to 85% as the mole ratio of CoSO₄/FeSO₄ increasing from 0.50/0.50 to 0.90/0.10 in electrolyte and slightly decreases from 77% to 63% as the pH values increasing from 2.1 to 4.3. The X-ray diffraction analysis reveals that the structures of the films strongly depend on the Co content in the binary films. The surface morphologies of the films are influenced by the combined action of composition and phase structure. The saturation magnetization reaches a maximum value of 2974.03 emu/cm³ and coercivity reaches a minimum value of 42.72 Oe of the Fe_0.30Co_0.70. The saturation magnetization reaches a maximum values of 2974.03 emu/cm³ and coercivity reaches a minimum values of 42.72 Oe of the Fe_0.30Co_0.70 at pH = 2.9.     

Synthesis of magnetite nanorods and porous hematite nanorods

Fe₃O₄ nanorods with average diameters of 40-50 nm and lengths of up to 1 μm were synthesized through hydrolysis of FeCl₃ and FeSO₄ solutions containing urea in the temperature range from 90 to 95 °C in reflux condition for 12 h, following an aging time of 12 h. The porous hematite nanorods were prepared by calcination of the precursor which was obtained from hydrolysis of FeCl₃ and FeSO₄ solutions containing urea at a temperature of 90 °C for 10 h in hydrothermal condition. The formation of the porosity of hematite was due to the decomposition of FeCO₃ and FeOOH. Urea played a key role in the formation of the iron oxide nanorods. Transmission electron microscopy (TEM) images showed that the morphology of magnetite particles is homogeneous in the shape of rods and hematite rods are full of porosity. The values of saturation magnetization (M) and coercivity (H) of magnetite nanorods are 67.55 emu/g and 114 Oe, respectively. The samples were also characterized by X-ray powder diffraction (XRD) and electron diffraction (ED). At last, the forming mechanism of both the magnetite and porous hematite nanorods was discussed.     

Ni80Fe20 permalloy nanoparticles: Wet chemical preparation, size control and their dynamic permeability characteristics when composited with Fe micron particles

Ni₈₀Fe₂₀ permalloy nanoparticles (NPs) have been prepared by the polyol processing at 180 °C for 2 h and their particle sizes can be precisely controlled in the size range of 20-440 nm by proper addition of K₂PtCl₄ agent. X-ray diffraction results show that the Ni-Fe NPs are of FCC structure, and a homogeneous composition and a narrow size distribution of these NPs have been confirmed by scanning electron microscopy assisted with energy dispersion spectroscopy of X-ray (SEM-EDX). The saturation magnetization of ~440nm NPs is 80.8 emu/g that is comparable to that of bulk Ni₈₀Fe₂₀ alloys, but it decreases to 28.7 emu/g for ~20 nm NPs. The coercive force decreases from 90 to 3 Oe with decreasing NP size. The wide range of particle size is exploited to seek for high permeability composite particles. The planar type samples composed of the NiFe NPs exhibit low initial permeability due to the deteriorated magnetic softness and low packing density. However, when they are mixed with Fe micron particles, the initial permeability significantly increases depending on the mixing ratio and the NiFe NP size. A maximum initial permeability is achieved to be ~9.1 at 1 GHz for the Fe-10 vol%NiFe (~20 nmΦ), which is about three times that of pure Fe micron particles. The effects of Ni-Fe particle size, volume percentage and solvent on the static and dynamic permeability are discussed.     

Improvement of the magnetic properties of barium hexaferrite nanopowders using modified co-precipitation method

Barium hexaferrite BaFe₁₂O₁₉ powders have been synthesized using the modified co-precipitation method. Modification was performed via the ultrasonication of the precipitated precursors at room temperature for 1 h and the additions of the 2% KNO₃, surface active agents and oxalic acid. The results revealed that single phase magnetic barium hexaferrite was formed at a low annealing temperature of 800 °C for 2 h with the Fe³⁺/Ba²⁺ molar ratio 8. The microstructure of the powders appeared as a homogeneous hexagonal platelet-like structure using 2% KNO₃ as the crystal modifier. A saturation magnetization (60.4 emu/g) was achieved for the BaFe₁₂O₁₉ phase formed at 1000 °C for 2 h with Fe³⁺/Ba²⁺ molar ratio 8 using 5 M NaOH solution at pH 10 in the presence of 2% KNO₃. Moreover, the saturation magnetization was 52.2 emu/g for the precipitated precursor at Fe³⁺/Ba²⁺ molar ratio 12 in was achieved for the precipitated precursor ultrasonicated for 1 h and then annealed at 1200 °C for 2 h. Coercivities from 956.9 to 4558 Oe were obtained at different synthesis conditions.     

Very high field magnetization and AC susceptibility of native horse spleen ferritin

The magnetization of native horse spleen ferritin protein is measured in pulsed magnetic fields to 55 T at T=1.52 K. The magnetization rises smoothly with negative curvature due to uncompensated Fe³⁺ spins and with a large high field slope due to the underlying antiferromagnetic ferritin core. Even at highest fields the magnetic moment is only ∼4% of the saturation moment of the full complement of Fe³⁺ in the ferritin molecule. The AC magnetic susceptibility, χ_AC(T,f), responding to the uncompensated spins, reaches a maximum near the superparamagnetic blocking temperature with the temperature of the maximum, T_M, varying with excitation frequency, T_M⁻¹ α log f for 10?f?10⁴ Hz.     

Growth temperature dependence of the hysteretic behavior of Ni0.5Zn0.5Fe2O4 thin films

Herein, a discussion of the effect of deposition temperature on the magnetic behavior of Ni_0.5Zn_0.5Fe₂O₄ thin films. The thin films were grown by r.f. sputtering technique on (1 0 0) MgO single-crystal substrates at deposition temperatures ranging between 400 and 800 °C. The grain boundary microstructure was analyzed via atomic force microscopy (AFM). AFM images show that grain size (φ∼70-112 nm) increases with increasing deposition temperature, according to a diffusion growth model. From magneto-optical Kerr effect (MOKE) measurements at room temperature, coercive fields, H_c, between 37and 131 Oe were measured. The coercive field, H_c, as a function of grain size, reaches a maximum value of 131 Oe for φ ∼93 nm, while the relative saturation magnetization exhibits a minimum value at this grain size. The behaviors observed were interpreted as the existence of a critical size for the transition from single- to multi-domain regime. The saturation magnetization (21 emu/g<M_s<60 emu/g) was employed to quantify the critical magnetic intergranular correlation length (L_c≈166 nm), where a single-grain to coupled-grain behavior transition occurs. Experimental hysteresis loops were fitted by the Jiles-Atherton model (JAM). The value of the k-parameter of the JAM fitted by means of this model (k/μ_o∼50 A m²) was correlated to the domain size from the behavior of k, we observed a maximum in the density of defects for the sample with φ∼93 nm.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

In situ hybridization to chitosan/magnetite nanocomposite induced by the magnetic field

Chitosan/magnetite nanocomposite was synthesized induced by magnetic field via in situ hybridization in ambient condition. Results of XRD patterns and TEM micrographs indicated that magnetite particles with 10–20 nm were dispersed in chitosan homogeneously. An interesting result is that magnetite nanoparticles were assembled to form chain-like structures under the influence of the external magnetic field, which mimics the magnetite chains inside of magnetotatic bacteria. The saturated magnetization (Ms) of nano-magnetite in chitosan was 50.54 emu/g, which is as high as 54% of bulk magnetite. The remanence (Mr) and coercivity (Hc) were 4 emu/g and14.8 Oe, respectively, which indicated that magnetite nanoparticles were superparamagnetic. The key of route is that a pre-precipitated chitosan hydrogel membrane, used as chemical reactor, which controlled the precipitation of chitosan precipitation and in situ transformation of magnetite from the precursor simultaneously in the magnetic field environment.     

Magnetic and structural properties of Fe ion-implanted GaN

The magnetic and structural properties of Fe ion-implanted GaN was investigated by various measurements. XRD results did not show any peaks associated with second phase formation. The magnetization curve at 5 K showed ferromagnetic behavior for 900 °C-annealed sample. In zero-field-cooled (ZFC) and field-cooled (FC) magnetization measurements, the irreversibility and a cusp-like behavior of the ZFC curve were observed for 900 °C-annealed sample. These behaviors are typically observed in superparamagnetic or spin glass phase. While the temperature dependence magnetization of 800 °C-annealed sample showed non-Brillouin-like curve and it is not exhibited ferromagnetic hysteresis at 5 K. In XPS measurement, the coexistence of metallic Fe (Fe⁰) and Fe–N bond (Fe²⁺ and Fe³⁺) for Fe 2p core level spectra is observed in as-implanted sample. But 700–900 °C-annealed samples showed only Fe–N bond (Fe²⁺ and Fe³⁺) spectra. For Ga 3d core level spectra only Ga–N bonds showed for as implanted with 700–900 °C-annealed samples. From XPS results, it could be explained that magnetic property of our films originated from FeN structures.     

Preparation and characterization of magnetic levan particles as matrix for trypsin immobilization

Magnetic levan was synthesized by co-precipitating D-fructofuranosyl homopolysaccharide with a solution containing Fe²⁺ and Fe³⁺ in alkaline conditions at 100 °C. The magnetic levan particles were characterized by scanning electron microscopy (SEM), magnetization measurements, X-ray diffractometry (XRD) and infrared spectroscopy (IR). Afterwards, magnetic levan particles were functionalized by NaIO₄ oxidation and used as matrices for trypsin covalent immobilization. Magnetite and magnetic levan particles were both heterogeneous in shape and levan-magnetite presented bigger sizes compared to magnetite according to SEM images. Magnetic levan particles exhibited a magnetization 10 times lower as compared to magnetite ones, probably, due to the coating layer. XRD diffractogram showed that magnetite is the dominant phase in the magnetic levan. Infrared spectroscopy showed characteristics absorption bands of levan and magnetite (O-H, C-O-C and Fe-O bonds). The immobilized trypsin derivative was reused 10 times and lost 16% of its initial specific activity only. Therefore, these magnetic levan particles can be proposed as an alternative matrices for enzyme immobilization.     

Simple recipe to synthesize single-domain BaFe12O19 with high saturation magnetization

We report a new synthesis route for preparation of single-domain barium hexaferrite (BaFe₁₂O₁₉) particles with high saturation magnetization. Nitric acid, known as a good oxidizer, is used as a mixing medium during the synthesis. It is shown that formation of BaFe₁₂O₁₉ phase starts at 800 °C, which is considerably lower than the typical ceramic process and develops with increasing temperature. Both magnetization measurements and scanning electron microscope micrographs reveal that the particles are single domain up to 1000 °C at which the highest coercive field of 3.6 kOe was obtained. The best saturation magnetization of ≈60 emu/g at 1.5 T was achieved by sintering for 2 h at 1200 °C. Annealing at temperatures higher than 1000 °C increased the saturation magnetization, on the other hand, decreased the coercive field which was due to the formation of multi-domain particles with larger grain sizes. It is shown that the best sintering to obtain fine particles of BaFe₁₂O₁₉ occurs at temperatures 900-1000 °C. Finally, magnetic interactions between the hard BaFe₁₂O₁₉ phase and impurity phases were investigated using the Stoner-Wohlfarth model.     

Synthesis and magnetic characterization of cobalt-substituted ferrite (CoxFe3−xO4) nanoparticles

Cobalt-substituted ferrite nanoparticles were synthesized with a narrow size distribution using reverse micelles formed in the system water/AOT/isooctane. Fe:Co ratios of 3:1, 4:1, and 5:1 were used in the synthesis, obtaining cobalt-substituted ferrites (Co_xFe_3−xO₄) and some indication of γ-Fe₃O₄ when 4:1 and 5:1 Fe:Co ratios were used. Inductively coupled plasma mass spectroscopy (ICP-MS) verified the presence of cobalt in all samples. Fourier transform infrared (FTIR) showed bands at ∼560 and ∼400 cm⁻¹, characteristic of the metal–oxygen bond in ferrites. Transmission electron microscopy showed that the number median diameter of the particles was ∼3 nm with a geometric deviation of ∼0.2. X-ray diffraction (XRD) confirmed the inverse spinel structure typical of ferrites with a lattice parameter of a=8.388 Å for Co_0.61Fe_0.39O₄, which is near that of CoFe₂O₄ (a=8.394 Å). Magnetic properties were determined using a superconducting quantum interference device (SQUID). Coercivities higher than 8 kOe were observed at 5 K, whereas at 300 K the particles showed superparamagnetic behavior. The anisotropy constant was determined based on the Debye model for a magnetic dipole in an oscillating field and an expression relating χ′ and the temperature of the in-phase susceptibility peak. Anisotropy constant values in the order of ∼10⁶ erg/cm³ were determined using the Debye model, whereas anisotropy constants in the order of ∼10⁷ erg/cm³ were calculated assuming Ωτ=1 at the temperature peak of the in-phase component of the susceptibility curve as commonly done in the literature. Our analysis demonstrates that the assumption Ωτ=1 at the temperature peak of χ′ is rigorously incorrect.