Photoluminescence properties of Eu and Mn-activated BaMgP2O7 as a potential red phosphor for white-emission

A phosphate compound, BaMgP₂O₇ was co-doped with Eu²⁺ and Mn²⁺ for making a red-emitting phosphor. The phosphor was prepared by a solid-state reaction at high temperature. The photoluminescence properties were investigated under ultraviolet (UV) ray excitation. From a powder X-ray diffraction (XRD) analysis, the formation of single-phased BaMgP₂O₇ with a monoclinic structure was confirmed. In the photoluminescence spectra, the BaMgP₂O₇:Eu,Mn phosphor emits two distinctive colors: a blue band centered at 409 nm originating from Eu²⁺ and a red band at 615 nm caused by Mn²⁺. Also, efficient energy transfer from Eu²⁺ to Mn²⁺ in the BaMgP₂O₇:Eu,Mn system was verified by observing that the excitation spectra of BaMgP₂O₇:Eu,Mn emitted at 409 and 615 nm by Eu²⁺ emission and Mn²⁺ emission, respectively, are almost the same as that of BaMgP₂O₇:Eu monitored at 409 nm. The optimum concentration of Eu²⁺ ions in BaMgP₂O₇:0.015Eu excited at 309 nm wavelength is 1.5 mol%. With an increase of Mn²⁺ content up to 17.5 mol%, a systematic decline in the intensity of the excitation spectrum by Eu²⁺ and a gradual growth in the intensity of emission band by Mn²⁺ were observed. Accordingly, the optimum concentration of Mn²⁺ in BaMgP₂O₇:0.015Eu,Mn is 17.5 mol%. The maximum spectral overlap between emission of Eu²⁺ and excitation of Mn²⁺ is achieved in a composition of BaMgP₂O₇:0.015Eu,0.175Mn, resulting in considerable red-emission at 615 nm.     

Luminescence properties and energy transfer in Eu2+, Mn2+ codoped Na(Sr,Ba)PO4 phosphor

Eu²⁺ and Mn²⁺ singly doped and codoped Na(Sr,Ba)PO₄ phosphors were synthesized, and their luminescent properties were investigated. A broad blue emission and a broad orange emission band were observed in Na(Sr,Ba)PO₄:Eu²⁺, Mn²⁺ phosphor. The resonant-type energy transfer from Eu²⁺ to Mn²⁺ was demonstrated, and the energy transfer efficiency was also calculated according to their emission spectra. Based on the principle of energy transfer, the emission intensity ration of Eu²⁺ and Mn²⁺ could be appropriately tuned by adjusting the contents of activators. Due to the strong absorption in the 250–400 nm range, Na(Sr,Ba)PO₄:Eu²⁺, Mn²⁺ phosphor could be used as a potential candidate for near-UV white light-emitting diodes (LEDs).     

Color tunability of nanophosphors by changing cations for solid-state lighting

X₃MgSi₂O₈: Eu²⁺, Mn²⁺ (X=Ba, Sr, Ca) phosphors with the mean particle size of 200 nm and the spherical shape are synthesized through combustion method. They show three emission colors under near-ultraviolet light: the blue and green colors from Eu²⁺ ions and the red color from Mn²⁺ ions. Three emission bands show the different emission colors with changing X²⁺ cations. These color shifts are discussed in terms of two competing factors of the crystal field strength and the covalency. These phosphors with maximum excitation of around 375 nm can be applied as color-tunable phosphors for white-light-emitting diode based on ultraviolet/phosphor technology.     

Synthesis and luminous characteristics of Ba2MgSi2−xAlxO7: 0.1Eu, 0.1Mn phosphor for WLED

The shift of the emission band to longer wavelength (yellow-orange) of the Ba₂MgSi_2−xAl_xO₇: 0.1Eu²⁺ phosphor under the 350-450 nm excitation range has been achieved by adding the codoping element (Mn²⁺) in the host. The single-host silicate phosphor for WLED, Ba₂MgSi_2−xAl_xO₇: 0.1Eu²⁺, 0.1Mn²⁺ was prepared by high-temperature solid-state reaction. It was found experimentally that, its three-color emission peaks are situated at 623, 501 and 438 nm, respectively, under excitation of 350-450 nm irradiation. The emission peaks at 438 and 501 nm originate from the transition 5d to 4f of Eu²⁺ ions that occupy the two Ba²⁺ sites in the crystal of Ba₂MgSi_2−x Al_xO₇, while the 623 nm emission is attributed to the energy transfer from Eu²⁺ ions to Mn²⁺ ions. The white light can be obtained by mixing the three emission colors of blue (438 nm), green (501 nm) and red (623 nm) in the single host. When the concentrations of the Al³⁺, Eu²⁺ and Mn²⁺ ions were 0.4, 0.1 and 0.1 mol, respectively, the sample presented intense white emission. The addition of Al ion to the host leads to a substantial change of intensity ratio between blue and green emissions. White light could be obtained by combining this phosphor with 405 nm light-emitting diodes. The near-ultraviolet GaN-based Ba₂MgSi_1.7 Al_0.3O₇: 0.1Eu²⁺, 0.1Mn²⁺ LED achieves good color rendering of over 85.     

Line emission of SrBe2Si2O7:Eu2+ and BaBe2Si2O7:Eu2+

The compounds SrBe₂Si₂O₇ and BaBe₂Si₂O₇ both have the barylite structure. With 254 nm excitation, the Eu²⁺-activated compounds give UV emission peaking at 360 nm (Sr) and at 375 nm (Ba). Maximum quantum efficiencies of 40% (Sr) and 65% (Ba) were measured. The emission consists of a 5d-4f band emission as well as 4f-4f line emission, in contrast to many other Eu²⁺-activated oxides which generally show only 5d-4f band emission. At 77°K, both compounds show only the 4f-4f line emission peaking at 360 nm. At higher temperatures, 5d-4f band emission shows up at the cost of the line emission. A thermal equilibrium is assumed between the lowest excited 5d and 4f levels. The energy difference between these levels, calculated from the variation in the line-band intensity ratio with temperature, was computed to be 0.15 eV (Sr) and 0.09 eV (Ba). The occurrence of the line emission in the barylites is correlated with the weakness of the crystal field at the Eu²⁺ ions and with the high quenching temperature of the 5d-4f band emission.     

Eu2+, Cr3+共掺杂的MAl12O19 (M=Ca, Sr, Ba) 的发光性质及能量传递

三基色荧光粉中, 红色荧光粉性能较差, 为获得性能优良的红色荧光粉, 本文采用高温固相法合成了Eu²⁺, Cr³⁺单掺杂及共掺杂的碱土金属多铝酸盐MAl₁₂O₁₉ (M =Ca, Sr, Ba) 发光体. 实验表明, 在以上三种基质中均存在Eu²⁺→Cr³⁺的能量传递, 利用能量传递可以有效将Eu²⁺的蓝光或绿光转换为红光. 三种碱土金属多铝酸盐基质的晶体结构相似,但Eu²⁺, Cr³⁺发光受晶体场影响,导致在不同的基质中Eu²⁺, Cr³⁺间能量传递效率不同.通过光谱分析及能量传递效率计算发现, 相同掺杂浓度下,CaAl₁₂O₁₉中Eu²⁺→Cr³⁺的能量传递效率最高,SrAl₁₂O₁₉次之, BaAl₁₂O₁₉最低.红光转换率在CaAl₁₂O₁₉中最高.     

Luminescence and energy transfer in Eu2+,Mn2+ codoped Na2BaMgP2O8 phosphor

Eu²⁺ single-doped and Eu²⁺/Mn²⁺-codoped Na₂BaMgP₂O₈ phosphors were prepared by a combustion-assisted synthesis method. The phase formation was confirmed by X-ray powder diffraction measurement. Na₂BaMgP₂O₈:Eu²⁺,Mn²⁺ shows a broad blue emission band and a red emission band, which originate from Eu²⁺ occupying the Ba²⁺ sites and Mn²⁺ occupying the Mg²⁺ sites, respectively. The efficient energy transfer from Eu²⁺ to Mn²⁺ is verified by the excitation and emission spectra together with the luminescence decay curves. Based on the principle of energy transfer, the relative intensities of blue and red emissions could be tuned by adjusting the contents of Eu²⁺ and Mn²⁺.     

Luminescent properties of SrMg<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>2</Subscript>:Eu<Superscript>2+</Superscript>, and Mn<Superscript>2+</Superscript> as a potential phosphor for ultraviolet light-emitting diodes

Eu²⁺ and Mn²⁺ co-doped SrMg₂(PO₄)₂ phosphors with blue and red two emission bands were prepared by the high temperature solid state method and their luminescent properties have been investigated as a function of activator and co-activator concentrations. Resonance-type energy transfers from Eu²⁺ to Mn²⁺ were discovered by directly overlapping the Eu²⁺ emission spectrum and the excitation spectrum of Mn²⁺. Efficiencies of energy transfer were also calculated according to the changes of relative intensities of Eu²⁺ and Mn²⁺ emission. According to the principle of energy transfer, we demonstrated that the phosphor SrMg₂(PO₄)₂:Eu²⁺,Mn²⁺ with double emission bands exhibited a great potential as a phosphor for ultraviolet light-emitting diodes and the relative intensities of blue and red emission could be tuned by adjusting the contents of Eu²⁺ and Mn²⁺. PACS 78.55.-m     

A novel white light-emitting diode (w-LED) fabricated with Sr<Subscript>6</Subscript>BP<Subscript>5</Subscript>O<Subscript>20</Subscript>:Eu<Superscript>2+</Superscript> phosphor

Sr₆BP₅O₂₀:Eu²⁺ phosphor was prepared by the solid-state reaction method under a weak reductive atmosphere and the photoluminescence properties were studied systematically. The bluish-green emission band of Sr₆BP₅O₂₀:Eu²⁺ phosphor is peaking at 475 nm, and the excitation bands are broad with peaks at about 290 and 365 nm with a shoulder around 390 nm, respectively. By combining with Ga(In)N-based near-ultraviolet LEDs, a bluish-green LED was fabricated based on the Sr₆BP₅O₂₀:Eu²⁺ phosphor, and a novel intense white LED was fabricated based on the bluish-green phosphor Sr₆BP₅O₂₀:Eu²⁺ and the red phosphor (Sr,Ca)₅(PO₄)₃Cl:Eu²⁺,Mn²⁺. When this two-phosphor white LED is operated under 20-mA forward-bias current at room temperature, the Commission Internationale de l’Eclairage(CIE) chromaticity coordinates (x,y), the correlated color temperature Tc, and the color rendering index Ra are calculated to be (0.3281,0.3071), 5687 K, and 87.3, respectively. The dependence of the bluish-green and two-phosphor white LEDs on different forward-bias currents from 5 mA to 50 mA shows a similar behavior. As the current increases, the relative intensity simultaneously increases. The CIE chromaticity coordinates (x,y) of the two-phosphor white LED tend to decrease. Consequently, the correlated color temperature Tc increases from 3800 K to 9400 K and the color rendering index Ra of the two-phosphor white LED increases from 83.4 to 91.8 simultaneously. PACS 07.60.-j; 42.70.-a; 71.55.Eq     

Luminescence spectroscopy of Eu3+ and Mn2+ ions in MgGa2O4 spinel

Photoluminescence and excitation spectra of the spinel-type MgGa₂O₄ with 0.5 mol. % Mn²⁺ ions and Eu³⁺ content from 0 to 8 mol. % have been investigated in this work at room temperature. Polycrystalline samples were synthesized via high-temperature solid-state reaction method. Photoluminescence spectra of all samples exhibit host emission presented by a broad “blue” band peaking ∼430 nm, which consists of at least three elementary bands that correspond to different host defects. Excitation of the host luminescence showed the broad band with a maximum at 360 nm. Characteristic bands of d–d transitions of Mn²⁺ ions and f–f transitions of Eu³⁺ ions together with charge-transfer bands (CTB) of these ions were also found on the excitation spectra. Mn²⁺ and Eu³⁺ co-doped samples emit in green and red spectral regions. Mn²⁺ ions are responsible for the green emission band at 505 nm (⁴Т₁→⁶А₁ transition). The studies of photoluminescence spectra of activated samples with different Eu³⁺ ions content show characteristic f–f luminesecence of Eu³⁺ ions. The maximum of Eu³⁺ emission was found at 618 nm (⁵D₀→⁷F₂) and optimal concentration of activator ions was around 4 mol. %.     

Green Eu-doped Ba3Si6O12N2 phosphor for white light-emitting diodes: Synthesis, characterization and theoretical simulation

The Eu²⁺-doped Ba₃Si₆O₁₂N₂ green phosphor (Eu_xBa_3−xSi₆O₁₂N₂) was synthesized by a conventional solid state reaction method. It could be efficiently excited by UV-blue light (250-470 nm) and shows a single intense broadband emission (480-580 nm). The phosphor has a concentration quenching effect at x=0.20 and a systematic red-shift in emission wavelength with increasing Eu²⁺ concentration. High quantum efficiency and suitable excitation range make it match well with the emission of near-UV LEDs or blue LEDs. First-principles calculations indicate that Ba₃Si₆O₁₂N₂:Eu²⁺ phosphor exhibits a direct band gap, and low band energy dispersion, leading to a high luminescence intensity. The origin of the experimental absorption peaks is clearly identified based on the analysis of the density of states (DOS) and absorption spectra. The photoluminescence properties are related to the transition between 4f levels of Eu and 5d levels of both Eu and Ba atoms. The 5d energy level of Ba plays an important role in the photoluminescence of Ba₃Si₆O₁₂N₂:Eu²⁺ phosphor. The high quantum efficiency and long-wavelength excitation are mainly attributed to the existence of Ba atoms. Our results give a new explanation of photoluminescence properties and could direct future designation of novel phosphors for white light LED.     

Effect of Sr substitution on photoluminescent properties of BaAl2O4:Eu, Dy

Phosphor material BaAl₂O₄:Eu²⁺, Dy³⁺ with varying compositions of Sr substitution were prepared by the solid-state synthesis method. The phosphor compositions were characterized for their phase and crystallinity by XRD, SEM and TEM. Photoluminescence (PL) properties were investigated measuring PL and decay time for varying Ba/Sr compositions. The PL results show the blue shift in the luminescence properties in Sr substituted BaAl₂O₄:Eu²⁺, Dy³⁺ compared to parent BaAl₂O₄:Eu²⁺, Dy³⁺. It is probably due to the influence of 5d electron states of Eu²⁺ in the crystal field because of atomic size variation causing crystal defects. Dy³⁺ ion doping in the phosphor generates deep traps, which results in long afterglow phosphorescence.     

Investigation on Eu doped Sr2MgSi2O7 red-emitting phosphors for white-light-emitting diodes

In this work, we report the high temperature solid-state synthesis of red phosphors Sr₂MgSi₂O₇: Eu³⁺ with various Eu³⁺ concentrations. Their luminescent properties at room temperature are investigated. The X-ray diffraction patterns indicate that the red phosphors powder conforms to the tetragonal Sr₂MgSi₂O₇. Impurity structure appears when more than 20% Eu³⁺ is doped. The samples show a strong emission line at 615 nm and the intensity increases with the increase of Eu³⁺ concentration until concentration quenching occurs. Charge compensation assists in the reduction of the impurity structure and vacancies; hence the luminescent intensity is enhanced. The decay measurement indicates that the lifetime of Eu³⁺ emission is about 2-3 ms. Some of the Eu³⁺ can be reduced to Eu²⁺; this is also discussed.     

Luminescence properties of Eu2+ in M2MgSi2O7 (M=Ca, Sr, and Ba) phosphors

The photoluminescence properties of alkali-earth magnesium silicates (M₂MgSi₂O₇, M=Ca, Sr, and Ba) doped with Eu²⁺ were investigated. Solid solutions of Ba _x Sr_2−x Si₂O₇, Ca₂MgSi₂O₇, and Sr₂MgSi₂O₇ were prepared. Ba _x Sr_2−x Si₂O₇ retained a tetragonal crystal structure similar to the structure of the other compounds up to a stoichiometry of x=1.6, which enabled a systematic study of the common structure. Monoclinic Ba₂MgSi₂O₇ was prepared, and the luminescence properties were compared with those of other samples. The emission and excitation spectra of tetragonal M₂MgSi₂O₇ (M=Ca, Sr, and Ba) changed as a function of the covalency, site symmetry, and crystal field strength. The luminescence properties showed excellent agreement with theoretical predictions based on these factors. The Stokes shift differentiated the emission behaviors of the tetragonal and monoclinic structures.     

Eu2+掺杂浓度对Ca2MgSi2O7∶Eu2+荧光粉发光特性的影响

采用化学共沉淀法制备了Ca_2-xMgSi₂O₇:xEu²⁺绿色荧光粉.用X射线衍射仪、荧光分光光度计及光色综合测试系统对Ca_2-xMgSi₂O₇:xEu²⁺绿色荧光粉的相结构、发光性能进行了测试.结果表明:其激发光谱分布在300–480 nm波长范围,谱峰位于389,430 nm处,可以被InGaN管芯产生的360–480 nm辐射有效激发;在波长为430 nm蓝光激发下,其发射光谱谱峰位于531 nm处.Ca_2-xMgSi₂O₇:xEu²⁺绿色荧光粉的发光强度随Eu²⁺掺杂量的增加而增强,当Eu²⁺掺杂量x为0.04时,发光强度达到最大值,而后开始降低,发生浓度猝灭.根据Dexter能量共振理论,浓度猝灭是由电偶极-电偶极相互作用引起的. 关键词： 2MgSi₂O₇∶Eu²⁺')" href="#">Ca₂MgSi₂O₇∶Eu²⁺ 绿色荧光粉 发光特性 白光发光二极管     

Effects of dopant concentrations on phosphorescence properties of Eu/Dy-doped Sr3MgSi2O8

Long afterglow Sr₃MgSi₂O₈: Eu, Dy phosphor with high brightness was prepared by sintering at high temperature and weak reductive atmosphere. The luminescent properties of this photoluminescent pigment were studied systematically by investigating concentration effects. The analytical results indicated that the main emission peaks appear at 482 nm. The excitation and emission spectra of this phosphor show that both of them are broadband. This is ascribed to the 4f⁷→4f⁶5d¹ transition of Eu²⁺ in the pigment matrix, which is in good agreement with the calculated value of 470 nm, and implies that luminescent centers Eu²⁺ occupy the deca-coordinated Sr²⁺ sites with the host of Sr₃MgSi₂O₈.     

Orange emissive Sr3Al2O5Cl2:Eu2+ phosphor for warm-white light-emitting diodes

Orange-emitting Sr₃Al₂O₅Cl₂:Eu²⁺ phosphors were synthesized by a high-temperature solid-state reaction. The excitation spectrum shows a broad band from the UV region to the blue region. The emission spectrum shows strong orange emission peaking at 610 nm, attributed to the d–f transition of the Eu²⁺ ion. By combining the Sr₃Al₂O₅Cl₂:Eu²⁺ phosphor with 420 nm and 460 nm chips, three white light-emitting diodes (LEDs) were fabricated. The warm-white LEDs show color rendering indexes of 76, 66 and 90 with color temperatures of 2447, 3546 and 4300 K, respectively. This new phosphor exhibits the potential to act as a single host doped with Eu²⁺ phosphor for UV or blue chip excited white LEDs.     

Emission properties of Eu, Mn in MAl2Si2O8 (M=Sr, Ba)

The emission properties of Eu²⁺ and Mn²⁺ in monoclinic SrAl₂Si₂O₈ (M-SAS) and hexagonal BaAl₂Si₂O₈ (H-BAS), both of which have only one alkaline-earth site, were studied. The emission peaks of both Eu²⁺ (405 nm) and Mn²⁺ (564 nm) in SrAl₂Si₂O₈, are located at longer wavelengths, compared with those in H-BAS (373 nm for Eu²⁺ and 518 nm for Mn²⁺), because of the stronger crystal field strength at the Sr site. EPR spectra showed that the g values of Mn²⁺ are 4.5065 in M-SAS:Mn and 2.0247 in H-BAS:Mn. Magnetic measurements proved that Mn²⁺ was at high-spin state in both hosts. The large g value of Mn²⁺ in M-SAS was ascribed to the mixing of the first excitation state to the ground state, both of which have lower d orbital degeneracy due to the lower symmetry of Mn²⁺ site. The transfer efficiency from Eu²⁺ to Mn²⁺was about 10% in M-SAS, higher than that in H-BAS (5%). This was probably because Eu²⁺ emission overlaps the relatively low excitation level of Mn²⁺ in M-SAS. In order to obtain high transfer efficiency, it was necessary for the Eu²⁺ emission to overlap the lowest excitation level of Mn²⁺. The results obtained in this work may be helpful to design the new white or red phosphors for white-light emitting diode (w-LED) applications.     

Sr和Ba替代对Eu掺杂Ca2.955Si2O7的结构和发光特性的影响研究

利用固相反应法制备了Sr和Ba替代的Ca_2.955-xM_xSi₂O₇: 0.045Eu²⁺ (M= Sr, Ba, x= 0.1-0.5)系列荧光粉, 利用较大离子半径的Sr和Ba元素替代Eu掺杂Ca_2.955-xM_xSi₂O₇ 中的Ca元素,研究Sr和Ba替代对样品结构和发光特性的影响. X射线衍射测试结果表明,少量Sr和Ba替代不会改变基质的晶体结构, 样品仍然为单斜晶系.未替代前, Ca_2.955Si₂O₇: 0.045Eu²⁺ 样品的发射峰在574 nm左右,随着Sr含量的增加,样品的发射峰发生蓝移; 而Ba含量在x= 0.1-0.4时不会引起发射峰位置的移动, 但x= 0.5样品的发射峰发生蓝移.同等含量的Sr和Ba部分替代样品中的Ca元素, Ba替代样品的光谱强度较强.     

Crystal structure of BaCa2MgSi2O8 and the photoluminescent properties activated by Eu

Rietveld refinements of X-ray powder diffraction data have confirmed the crystal structure of BaCa₂MgSi₂O₈ prepared by a standard solid-state method. The final reliable factors were R_wp=10.91%, R_p=8.10%, R_I=2.71%, and R_F=1.14%. BaCa₂MgSi₂O₈ crystallizes in the trigonal space group P3¯m1 (no. 164) with a=5.430(3) Å and c=6.807(2) Å. The oxide has a layered structure constructed from the unit layers built up by corner-sharing MgO₆ octahedra and SiO₄ tetrahedra. Ba and Ca atoms occupy the distinct crystallographic sites; Ba atom is sited in the interlayer space and Ca atom is embedded in the layer framework. This structure was not disrupted by doping of Eu²⁺ ions.The Eu²⁺-doped BaCa₂MgSi₂O₈ exhibited an intense blue emission based on 5d-4f electron transitions of Eu²⁺ ions under 254 nm excitation. This emission has a sufficient chromaticity as a blue phosphor. An additional analysis of the emission spectra using an empirical formula indicates that Eu²⁺ is distributed into both Ba and Ca sites.