An efficient blue-emitting phosphor LiCaPO4:Eu2+ for white LEDs

A new blue-emitting phosphor LiCaPO₄: Eu²⁺ was synthesized by solid state reaction at a relatively low temperature of 900 °C. It gives a single intense emission band centering at 470 nm, which corresponds to the 4f⁶5d¹→4f⁷ transition of Eu²⁺. The dependence of luminescence intensities on Eu²⁺ concentration was investigated. The phosphor, with a single excitation band extending from 250 to 400 nm, could be efficiently excited by near-ultraviolet light-emitting diodes and is believed to be a promising blue-emitting phosphor for white light-emitting diodes.     

白光LED用单基质荧光粉BaSrMg( PO4)2∶Eu2+的制备及发光性能研究

采用高温固相反应法在1 200℃下制备了 Eu2+激活的BaSrMg( PO4)2高亮度白光荧光粉,并对其晶体结构和发光性能进行了研究.荧光光谱研究表明该荧光粉的发射光谱由两个谱带组成,其中心分别位于424和585 nm处,归结为Eu2+分别占据了基质中Sr2+,Ba2+格位而导致的4f 65d1→4f7电子跃迁.两个...     

Luminescent properties of Mg3Ca3(PO4)4: Eu2+ blue-emitting phosphor for white light emitting diodes

A blue-emitting phosphor, Eu²⁺-activated Mg₃Ca₃(PO₄)₄ phosphor was synthesized by conventional solid-state reaction. X-ray powder diffraction (XRD) analysis confirmed the phase formation. Photoluminescence (PL) results showed that Mg₃Ca₃(PO₄)₄: Eu²⁺ could be efficiently excited by UV–visible light from 250 to 430 nm, which matched well with the emission wavelengths of near-UV and UV LED chips. The effects of the doped-Eu²⁺ concentration in Mg₃Ca₃(PO₄)₄: Eu²⁺ on the PL were also investigated. The result reveals that Mg₃Ca₃(PO₄)₄: Eu²⁺ is a potential blue-emitting phosphor for white LEDs.     

Thermally stable blue-emitting NaSrPO4:Eu phosphor for near UV white LEDs

A novel blue light emitting NaSr_1 − xPO₄:Eu²⁺_x (x = 0.001 to 0.02) phosphors were prepared by solid-state reaction method to investigate its optical properties and thermal stability for its application in white light-emitting diodes (w-LEDs). The excitation and emission spectra of the prepared phosphor reveal a broad emission peak centered at 460 nm which arises due to 4f-5d transitions of Eu²⁺ upon the near ultra-violet (n-UV) excitation wavelength at 380 nm. The effect of Eu²⁺ doping concentration and sintering temperature on the emission intensity of NaSrPO₄:Eu²⁺ was investigated along with its chromaticity coordinates. The temperature dependent luminescence properties of the prepared phosphor show better results than that of the commercial YAG:Ce³⁺phosphor. Besides, their XRD, FT-IR, SEM, TG, and DTA profiles have also been analyzed to explore its structural details.     

A potential red emitting K4Ca(PO4)2: Eu3+ phosphor for white light emitting diodes

Europium (III) ions doped red phosphors K₄Ca(PO₄)₂ were prepared first time by high temperature solid state reaction method. The prepared phosphors structure was examined by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS) analyses. The thermal properties of the synthesized phosphor were investigated by differential scanning calorimetry (DSC) analysis. Photoluminescence (PL) spectra of K₄Ca(PO₄)₂:Eu³⁺ phosphors have shown strong red emission at 618 nm (⁵D₀→⁷F₂) with near UV an excitation wavelength of λ_exc=394 nm (⁷F₀→⁵L₆). In addition, the decay curves and CIE color coordinate measurements are also carried out. Hence, emission and excitation characterization of synthesized phosphors shows that the phosphors may be a promising red component for the application in the white light emitting diodes (WLEDs).     

Intense green-emitting Sr2LiSiO4F:Eu2+ phosphor for n-UV white LEDs

Eu²⁺-activated Sr₂LiSiO₄F phosphors were synthesized at 900°C by solid-state reaction in reducing atmosphere, and their photoluminescence (PL) properties were systematically investigated by diffuse reflection spectra, PL excitation and emission spectra, and by the fluorescence decay curve. Sr₂LiSiO₄F:Eu²⁺ emits intense green light at 520 nm originating from the 5d¹4f⁶−4f⁷ transition of Eu²⁺ under 365 nm n-UV excitation. The PL excitation spectrum matches the emission from n-UV chips. These materials could be promising green phosphors for use in generating white light in phosphor-converted white light-emitting-diodes (LEDs).     

Eu2+激活的Ca3SiO5绿色荧光粉的制备和发光特性研究

研究了Eu2+激活的绿色发光材料Ca3SiO5的制备条件和发光性质. Eu2+中心形成主峰值为501 nm和次峰值为570 nm的特征宽带,两峰值叠加形成发射峰值为502 nm的绿色发射光谱带. 利用这些光谱结果和Van Uitert 经验公式,确认Ca3SiO5:Eu2+中存在两种性质有差异的Eu2+发光中心,它们分别占据基质中八配位的Ca2+(Ⅰ)格位和四配位的Ca2+(Ⅱ)格位. 其激发光谱分布在250-450 nm的波长范围,峰值位于375 nm处,可以被InGaN管芯产生的350-410 nm辐射有效激发.     

The luminescence properties of Eu2+ doped Na2CaMg(PO4)2 phosphor

The blue-emitting phosphors of Eu²⁺-doped Na₂CaMg(PO₄)₂ were prepared by high-temperature solid-state reaction. The crystal phase formation was confirmed by X-ray powder diffraction measurement. The luminescence properties were investigated by photoluminescence excitation and emission spectra. The phosphor exhibited the blue luminescence due to the 4f⁶5d¹→4f⁷ transition of Eu²⁺ ions under the excitation of near UV light. The influence of temperature on the luminescence intensities and decay lifetimes of Eu²⁺ was investigated. An unusual increase of the decay lifetimes of the 4f⁶5d emission of Eu²⁺ ion is observed in Na₂CaMg(PO₄)₂ from 10 K to room temperature. The thermal stability of the luminescence of Eu²⁺-doped Na₂CaMg(PO₄)₂ was discussed.     

Persistent luminescence in Ca8Zn(SiO4)4Cl2:Eu2+

A new persistent, green emission is reported for europium activated Calcium Zinc Chlorosilicate (CZCS). The phosphor was prepared by the solid state reaction and characterized using XRD, PL and TL techniques. The decay was characterized by admixture of two exponential components with decay constants 20.2 and 101 s.     

Luminescent properties and energy transfer of double-emitting NaSrPO4:Eu2+,Tb3+ phosphor for near-UV white LEDs

Novel blue/green NaSrPO₄ phosphors co-doped with Eu²⁺ and Tb³⁺ were synthesized by a conventional solid-state reaction. Their luminescent properties were characterized by using powder X-ray diffraction, photoluminescence excitation and emission spectra, lifetime, and temperature dependent emission spectra, respectively. The NaSrPO₄:Eu²⁺,Tb³⁺,Na⁺ phosphor showed an intense broad excitation band between 250 and 430 nm, which was in agreement with the near-UV chip (350–420 nm), and it exhibited two dominating emission bands at 445 and 545 nm, corresponding to the allowed 4f⁶5d¹→4f⁷(⁸S_7/2) transition of Eu²⁺ ion and the ⁵D₄→⁷F₅ transition of Tb³⁺ ion, respectively. The emission intensity and lifetime of Eu²⁺ ion decreased with the increasing concentration of Tb³⁺ ion, which strongly indicated that an effective energy transfer occurred from Eu²⁺ to Tb³⁺ in NaSrPO₄ host. The principle of the energy transfer should be the combined effect of the non-radiative resonant energy transfer and the phonon-assisted non-radiative process.     

Photoluminescence properties of blue-emitting Li4SrCa(SiO4)2:Eu2+ phosphor for solid-state lighting

Blue-emitting Li₄SrCa(SiO₄)₂:Eu²⁺ phosphors have been synthesized by solid-state reaction. The photoluminescence (PL) excitation spectrum shows broad-band absorption and matches well with the emission of a near-UV (n-UV) chip. The PL emission spectrum exhibits a broad-band emission peaking at 430 nm, which is the characteristic emission of the f–d transition of the Eu²⁺ ion. The diffuse reflection spectra, temperature-dependent emission spectra, fluorescence decay, and mechanism of concentration quenching are also studied in detail. Li₄SrCa(SiO₄)₂:Eu²⁺ is a candidate blue phosphor for n-UV excited solid-state lighting.     

A novel red-emitting phosphor Ca9Bi(PO4)7:Eu3+ for near ultraviolet white light-emitting diodes

Red phosphors Ca₉Bi_1-x(PO₄)₇:xEu³⁺ (x = 0.06, 0.10, 0.20, 0.30, 0.40, 0.50, 0.60, 0.70, 0.80 and 1.00) were synthesized by a conventional solid-state reaction (SSR) route. The X-ray diffraction patterns, photoluminescence spectra, ultraviolet–visible reflection spectroscopy, decay time and the International Commission on Illumination (CIE) chromaticity coordinates of these compounds were characterized and analyzed. The Eu-doped Ca₉Bi(PO₄)₇ phosphors exhibited strong red luminescence which peaks located at 615 nm due to the ⁵D₀→⁷F₂ electric dipole transition of Eu³⁺ ions after excitation at 393 nm. Ultraviolet–visible spectra indicated that the band-gap of Ca₉Bi_0.30(PO₄)₇:0.70Eu³⁺ is larger than that of Ca₉Bi(PO₄)₇. The results indicate that the phosphor Ca₉Bi_0.30(PO₄)₇:0.70Eu³⁺ can be a suitable red-emitting phosphor candidate for LEDs.     

Concentration quenching of Eu2+ in a thermal-stable yellow phosphor Ca2BO3Cl:Eu2+ for LED application

A piece-shaped phosphor Ca₂BO₃Cl: Eu²⁺ was synthesized by solid-state reaction method. This phosphor exhibited wide absorption in ultra-violet and visible range, and bright yellow emission band centering at 570 nm. The concentration quenching mechanism was verified to be a dipole–dipole interaction, and its critical transfer distance was about 17 Å by both calculated crystal structural method and experimental spectral method. This phosphor has a good thermal stability with a quenching temperature (T_1/2) of 200 °C. Yellow and white LEDs were fabricated with this phosphor and near UV chips, and the yellow LED has a high color purity of 97.0% and promising current tolerant property, while the white LED shows a luminous efficiency of 11.68 lm/W.     

用于白光LED的单一基质白光荧光粉Ca2SiO3Cl2:Eu2+,Mn2+的发光性质

用高温固相法合成了Eu2+,Mn2+共激活的Ca2SiO3Cl2高亮度白色发光材料,并对其发光性质进行了研究.该荧光粉在近紫外光激发下发出强的白色荧光,Eu2+中心形成峰值为419 nm和498 nm的特征宽带,通过Eu2+中心向Mn2+中心的能量传递导致了峰值为578 nm的发射,三个谱带叠加从而在单一基质中得到了白光.激发光谱均分布在250-415 nm的波长范围,红绿蓝三个发射带的激发谱峰值分别位于385 nm,412 nm,370 nm和396 nm处,可以被InGaN管芯产生的紫外辐射有效激发.Ca2SiO3Cl2:Eu2+,Mn2+是一种很有前途的单一基质白光LED荧光粉.     

Synthesis and luminescence properties of a broad-band red phosphor Ca3Si2O7:Eu2+ for warm white light-emitting diodes

Single-phase broad-band red-emitting Ca₃Si₂O₇:Eu²⁺ phosphors, with photoluminescence features that qualify them as candidates for white light-emitting diodes applications, were successfully synthesized via a modified solid-state reaction method that employed H₃BO₃ as a flux. The phosphors produced have an intense broad red emission band, with a peak at 603 nm, a full width at half maximum of 110 nm, and color coordinates of (0.550, 0.438). Concentration quenching occurred at 0.01 mol Eu²⁺. The discussion of the results shows that Eu²⁺ ions should be accommodated at the Ca-sites of the lattice, dipole–dipole interactions should predominantly govern the energy transfer mechanism among them, and the critical distance between them is ～31 Å.     

Photoluminescence and structural characteristics of a new orange phosphor: Ca2.6Sr2.4(PO4)3Cl:Eu3+

A novel orange-emitting phosphor, Ca_2.6Sr_2.4(PO₄)₃Cl:Eu³⁺, was prepared by a modified solid-state reaction and X-ray powder diffraction (XRD) analysis confirmed the formation of Ca_2.6Sr_2.4(PO₄)₃Cl:Eu³⁺. Photoluminescence (PL) results showed that the phosphor can be efficiently excited by UV-visible light from 380 to 500 nm, and exhibited bright orange emission. The effects of the doped-Eu³⁺ concentration in Ca_2.6Sr_2.4(PO₄)₃Cl:Eu³⁺ on the PL were investigated in detail. The results showed that the relative PL intensity decreases with Eu³⁺ concentration increasing due to concentration quenching. TEM images show that the grain size of Ca_2.6Sr_2.4(PO₄)₃Cl:Eu³⁺ is about 45 nm, which is in full agreement with the theoretical calculation data from the XRD patterns.     

Sr9Ca(PO4)6Cl2:Eu2+晶体中的两种发光中心

Sr9Ca(PO4)6Cl2:Eu2+是一种性能良好效率较高的发光材料.作者合成并生长了Sr9Ca(PO4)6Cl:Eu2+的单晶体.从晶体的结构测定和光谱学研究,确证了晶体中存在有两种发光中心,即Eu(Ⅰ)中心和Eu(Ⅱ)中心.