激光熔覆NiCrBSi涂层组织及摩擦磨损性能

采用激光熔覆技术在H13钢表面制备了NiCrBSi合金涂层,利用OM,SEM,EDX和XRD等对熔覆层的微观组织进行了分析,测试了熔覆层的显微硬度和摩擦磨损性能。结果表明,激光熔覆层与基体形成了良好的冶金结合,熔覆层的组织主要由γ-Ni,Cr7C3和CrB等相组成。熔覆层显微硬度在650~850HV之间,明显高于H13钢基体的硬度。摩擦磨损实验表明,在相同的条件下,熔覆层的耐磨性比基体有了明显的提高,磨损体积减少了92.4%。通过对磨损后的试样进行粗糙度测试后表明,涂层具有更平滑的表面。     

激光熔覆TiC-Ni复合涂层的摩擦磨损性能和磨损机制研究

利用光学显微镜和扫描电镜观察了钛合金表面TiC-Ni激光熔覆层的宏观形貌和微观组织,测试了激光熔覆层的硬度、摩擦系数和磨损量。利用SEM观察了磨损的表面形貌和磨屑的形貌,分析了激光熔覆层的磨损机制。结果表明:激光熔覆层组织致密,无气孔和裂纹,硬度为基材的3倍;激光熔覆层的摩擦系数随环境压力的降低而提高,磨损量随环境压力的降低、法向载荷的增加而增加;低载时为轻微的磨粒磨损,高载时为严重的剥层磨损。     

40Cr钢表面激光熔覆层的磨损性能

 为研究模具钢熔覆层的磨损性能,采用铁基粉在40Cr钢表面进行激光熔覆,以激光熔覆层为上试样,GCr15钢珠为下试样,采用HT－500磨损试验机进行摩擦磨损试验,并与40Cr基体的磨损性能相对比。利用表面形貌仪测量磨痕深度和宽度。研究结果表明：载荷小于250 g时,相同载荷下基体的摩擦系数大。载荷小于300 g时,随磨损时间延长,熔覆层、基体的摩擦系数都随着载荷增加而减小。当载荷为300 g时,基体的摩擦系数在0.563～0.589之间变化,平均值为0.576,且随时间逐渐升高,耐磨性变差;熔覆层的磨擦系数在0.431～0.457之间变化,平均摩擦系数为0.444,磨痕深度和宽度分别是0.65 mm和1.096 μm,且随时间逐渐下降,表现了良好的耐磨性能。当载荷增加到500 g时,平均摩擦系数和磨痕深度比300 g时分别增加了75％和47倍,且摩擦系数逐渐升高,磨损性能下降。     

40Cr钢表面激光熔覆层的磨损性能

为研究模具钢熔覆层的磨损性能,采用铁基粉在40Cr钢表面进行激光熔覆,以激光熔覆层为上试样,GCr15钢珠为下试样,采用HT－500磨损试验机进行摩擦磨损试验,并与40Cr基体的磨损性能相对比。利用表面形貌仪测量磨痕深度和宽度。研究结果表明：载荷小于250 g时,相同载荷下基体的摩擦系数大。载荷小于300 g时,随磨损时间延长,熔覆层、基体的摩擦系数都随着载荷增加而减小。当载荷为300 g时,基体的摩擦系数在0.563～0.589之间变化,平均值为0.576,且随时间逐渐升高,耐磨性变差;熔覆层的磨擦系数在0.431～0.457之间变化,平均摩擦系数为0.444,磨痕深度和宽度分别是0.65 mm和1.096 μm,且随时间逐渐下降,表现了良好的耐磨性能。当载荷增加到500 g时,平均摩擦系数和磨痕深度比300 g时分别增加了75％和47倍,且摩擦系数逐渐升高,磨损性能下降。     

激光熔覆Al+SiC涂层对镁合金表面耐磨性能的改性

通过脉冲激光器(Nd-YAG)在AZ91D镁合金基底上熔覆Al+SiC粉体。采用扫描电子显微镜、能量色散谱（EDS）和X-射线衍射测定分析熔覆层的显微组织、化学成分和物相组成。研究表明：Al+SiC涂层主要由SiC,b-Mg17Al12及Mg和Al相组成,激光熔覆层与镁合金基底表现出良好的冶金结合。所有样品都具有树枝状结构,且随着SiC质量分数的增大,树枝状和胞状结构的间隔变得更大。熔覆涂层的表面硬度高于基底,并且随着熔覆层中的SiC质量分数的增加而增大,SiC质量分数为40%的熔覆层具有最大的显微硬度,达到180 HV,然而质量分数为10%的熔覆层硬度为136 HV。销盘滑动磨损试验表明,复合涂层中的SiC颗粒和原位合成的Mg17Al12相显著提高了AZ91D镁合金的耐磨损性,其中,SiC质量分数从10%增加到30%过程中磨损体积损失逐渐减少,SiC质量分数在20%～30%时熔覆层具有最好的耐磨性。     

激光熔覆Al+SiC涂层对镁合金表面耐磨性能的改性

通过脉冲激光器(Nd-YAG)在AZ91D镁合金基底上熔覆Al+SiC粉体。采用扫描电子显微镜、能量色散谱(EDS)和X-射线衍射测定分析熔覆层的显微组织、化学成分和物相组成。研究表明:Al+SiC涂层主要由SiC,β-Mg_(17)Al_(12)及Mg和Al相组成,激光熔覆层与镁合金基底表现出良好的冶金结合。所有样品都具有树枝状结构,且随着SiC质量分数的增大,树枝状和胞状结构的间隔变得更大。熔覆涂层的表面硬度高于基底,并且随着熔覆层中的SiC质量分数的增加而增大,SiC质量分数为40%的熔覆层具有最大的显微硬度,达到180 HV,然而质量分数为10%的熔覆层硬度为136 HV。销盘滑动磨损试验表明,复合涂层中的SiC颗粒和原位合成的Mg_(17)Al_(12)相显著提高了AZ91D镁合金的耐磨损性,其中,SiC质量分数从10%增加到30%过程中磨损体积损失逐渐减少,SiC质量分数在20%~30%时熔覆层具有最好的耐磨性。     

激光工艺参数对钛合金表面NiCrBSi合金熔覆层组织及硬度的影响

在TC4合金表面进行了激光熔覆NiCrBSi合金涂层的试验 ,利用SEM和XRD等对熔覆层的微观组织进行了分析 ,测试了熔覆层的显微硬度。结果表明 ,激光工艺参数对熔覆层的组织和硬度有极大的影响 ,随稀释率的增加 ,激光熔覆层中形成了TiB2 和TiC等颗粒增强相 ,熔覆层的硬度明显提高。     

磁场辅助激光熔覆制备Ni60CuMoW复合涂层

采用磁场辅助激光熔覆技术,在Q235钢表面制备了Ni60CuMoW复合涂层,借助SEM,EDS 和XRD 等表征手段对涂层进行了微观组织和物相分析,利用维氏硬度计测试了复合涂层截面的显微硬度分布,通过摩擦磨损实验和电化学测试系统研究了复合涂层的磨损性能和耐腐蚀性能。研究结果表明：涂层主要由-Ni,Cu）固溶体、硅化物和硼化物组成,Cr3Si晶粒细化且均匀致密;磁场辅助作用下,激光熔覆涂层平均显微硬度达到913HV0.5,为无磁场辅助涂层的1.5 倍,磨损失重仅为无磁场涂层的36%,自腐蚀电位上升了100 mV,腐蚀电流密度降低了70%,耐磨耐蚀性能得到了显著改善。     

稀土CeO_2对镍基纳米Al_2O_3激光熔覆复合涂层组织和性能的影响

采用激光熔覆技术在45钢基体上制备了不同CeO2含量的镍基纳米Al2O3复合涂层,对熔覆层进行了微观组织分析和显微硬度测试。结果表明,随着CeO2含量的增加,熔覆层组织由亚共晶向共晶组织转变;加入1.0%CeO2对镍基纳米Al2O3熔覆层的组织起到明显的细化和净化作用,枝晶生长的方向性减弱,组织趋向均匀,熔覆涂层的显微硬度值比未加稀土的涂层提高了60-95HV0.2。     

金属陶瓷复合涂层的激光熔覆与无裂纹的实现

鉴于传统的激光熔覆金属陶瓷复合涂层技术主要存在2方面不足：其一,熔覆效率低,导致大面积熔覆时成本昂贵;其二,由于激光熔覆本身的特点,即快速加热与快速凝固,在激光熔覆过程中,热应力极易诱导熔覆层开裂。基于此,综述了国内外激光熔覆金属陶瓷复合涂层的研究进展,指出其存在的主要问题,并提出了激光感应复合快速熔覆的新方法,即感应预热基材的同时快速激光熔覆。该方法不仅可使熔覆效率大大提高而且获得了无裂纹的金属陶瓷复合涂层。     

激光熔敷镍石墨烯立方氮化硼涂层的耐磨性能

在AISI 4140基体上采用预置材料激光熔敷的方法制备了镍石墨烯立方氮化硼(Ni-Graphene-CBN)复合材料涂层。X射线衍射(XRD)和Raman测试证明了石墨烯和CBN存在于所制备的涂层材料中。扫描电镜(SEM)图片给出了所制备的复合材料涂层的表面和断面形貌。进行了复合材料涂层的纳米机械性能和耐磨性的测试。测试结果表明:随着CBN含量的增加,复合涂层的硬度及弹性模量相应提高,分别由4.3 GPa提高到6.2 GPa和101 GPa提高到140 GPa; 同时其耐磨性也有明显改善,6% CBN含量的涂层摩擦系数由基体材料的0.2降低到0.15,最大磨损量降到基体磨损量的一半。     

Microstructure and friction and wear behavior of laser boronizing composite coatings on titanium substrate

Three kinds of laser boronizing composite coatings were in situ synthesized on Ti substrate by using powders of B, BN and B₄C as starting materials. Microstructures of the laser boronizing composite coatings were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM); and their worn surface morphologies were also observed by using SEM. Moreover, the friction and wear behavior of the boronizing composite coatings under dry sliding condition were evaluated using a UMT-2MT friction and wear tester. It was found that all the three types of laser boronizing composite coatings had higher microhardness and better wear resistance than pure Ti substrate; and their microstructure and wear resistance varied with varying pre-placed powders of B, BN, and B₄C. Under the same dry sliding test conditions, the wear resistance of the three kinds of laser boronizing composite coatings, i.e., sample 1 prepared from pre-placed B, sample 2 obtained from pre-placed BN, and sample 3 fabricated from pre-placed B₄C, is ranked in an order of sample 1 > sample 2 > sample 3, which, surprisingly, well conforms to their order of hardness and friction coefficients.     

激光沉积修复BT20合金的显微组织和力学性能

针对BT20钛合金锻件当量孔损伤进行激光沉积修复试验,考察了修复试样的组织和力学特点。修复区与基材之间形成了致密冶金结合,Al,Zr,Mo,V合金元素由锻件基体到激光修复区均匀分布,无宏观偏析,硬度分布从基材到修复区依次提高。热影响区组织是由基材的双态组织过渡到网篮组织;修复区组织为粗大的原始柱状β晶,晶粒内为α/β网篮组织,晶内α片层取向随机,宽0.4~0.5μm。修复过程中发现,激光加工工艺参数选择不当、坡度过大等原因会造成修复区组织形成气孔和熔合不良等缺陷,但是通过优化工艺参数可以获得无缺陷修复试样。修复试样的室温静拉伸结果表明,试样的抗拉强度接近锻件基体强度,但修复件的韧性比锻件稍有提高。     

激光沉积修复BT20合金的显微组织和力学性能

针对BT20钛合金锻件当量孔损伤进行激光沉积修复试验,考察了修复试样的组织和力学特点。修复区与基材之间形成了致密冶金结合,Al,Zr,Mo,V合金元素由锻件基体到激光修复区均匀分布,无宏观偏析,硬度分布从基材到修复区依次提高。热影响区组织是由基材的双态组织过渡到网篮组织;修复区组织为粗大的原始柱状晶,晶粒内为/网篮组织,晶内片层取向随机, 宽0.4~0.5 m。修复过程中发现,激光加工工艺参数选择不当、坡度过大等原因会造成修复区组织形成气孔和熔合不良等缺陷,但是通过优化工艺参数可以获得无缺陷修复试样。修复试样的室温静拉伸结果表明,试样的抗拉强度接近锻件基体强度,但修复件的韧性比锻件稍有提高。     

Microstructure and wear resistance of laser clad cobalt-based alloy multi-layer coatings

Multi-layer Co-based alloy (HMSP 2537) were deposited on Ni-based superalloy plate with a TJ-TL-T5000 type CO₂ laser. Sections of such coatings were examined to reveal their microstructure and phase composition using optical microscope, scanning electron microscope (SEM), and X-ray diffractometer (XRD). The hardness and wear resistance of the coatings were tested. The results showed that the prime phase (γ-Co dendrite) and other phases, such as CrNi, Co₇W₆, and Cr₂₃C₆ existed in the coatings. Dendrite or cellular microstructures were observed perpendicular to the interface, and coarsening microstructures were obtained as more layers deposited. Dendrite paralleling to laser scan speed was also found near the top surface of the last layer. Fine microstructures of γ-Co dendrite and lamellar eutectic in inter-dendritic regions strengthened the coatings. Microhardness and wear resistance of the coatings were much higher than that of substrate but slightly decreased with layers increased.     

Microstructure and high-temperature wear resistance of a laser surface alloyed γ-TiAl with carbon

TiC reinforced composite coating on γ-TiAl alloy was successfully fabricated by laser surface alloying with carbon. The fine TiC reinforcing phase had a gradient distribution in the coating, and its growth morphology of TiC in laser surface alloyed coating was in unique faceted platelet-like. The composite coating exhibited high hardness and excellent high-temperature sliding wear resistance.     

不锈钢表面激光熔覆层与喷焊层耐磨性对比研究

本文研究在１Ｃｒ１８Ｎｉ９Ｔｉ基体上采用激光熔覆和离子喷焊二种工艺形成的涂层对耐磨性的影响。使用５ｋＷ横流ＣＯ２激光器对预置在基体上的Ｃｏ基自熔合金粉末进行单道或多道扫描，得到的熔层与等离子焊层对比结果是：激光熔层缺陷率低，成品率高，其结构致密均匀，晶粒细小，成分稀释率更小，对基体热影响小，熔层硬度与强韧性更高。性能试验证明：激光熔层具有更高的抗擦伤磨损和抗冲击滑动高温磨损性能，耐磨性提高了一倍左右。