Living radical graft polymerization of methyl methacrylate to polyethylene film with typical and reverse atom transfer radical polymerization

Nickel‐mediated atom transfer radical polymerization (ATRP) and iron‐mediated reverse ATRP were applied to the living radical graft polymerization of methyl methacrylate onto solid high‐density polyethylene (HDPE) films modified with 2,2,2‐tribromoethanol and benzophenone, respectively. The number‐average molecular weight (M_n) of the free poly(methyl methacrylate) (PMMA) produced simultaneously during grafting grew with the monomer conversion. The weight‐average molecular weight/number‐average molecular weight ratio (M_w/M_n) was small (<1.4), indicating a controlled polymerization. The grafting ratio showed a linear relation with M_n of the free PMMA for both reaction systems. With the same characteristics assumed for both free and graft PMMA, the grafting was controlled, and the increase in grafting ratio was ascribed to the growing chain length of the graft PMMA. In fact, M_n and M_w/M_n of the grafted PMMA chains cleaved from the polyethylene substrate were only slightly larger than those of the free PMMA chains, and this was confirmed in the system of nickel‐mediated ATRP. An appropriate period of UV preirradiation controlled the amount of initiation groups introduced to the HDPE film modified with benzophenone. The grafting ratio increased linearly with the preirradiation time. The graft polymerizations for both reaction systems proceeded in a controlled fashion. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3350–3359, 2002     

Synthesis of poly(methyl methacrylate)‐b‐polystyrene containing a crown ether unit at the junction point via combination of atom transfer radical polymerization and nitroxide mediated radical polymerization routes

Poly(methyl methacrylate)‐b‐polystyrene (PMMA‐b‐PS) containing a benzo‐15‐crown‐5 unit at the junction point was prepared by combining atom transfer radical polymerization and nitroxide‐mediated radical polymerization. For this purpose, 6,7,9,10,12,13,15,16‐octahydro‐5,8,11,14,17‐pentaoxa‐benzocyclopentadecene‐2‐carboxylic acid 3‐(2‐bromo‐2‐methyl‐propionyloxy)‐2‐methyl‐2‐[2‐phenyl‐2‐(2,2,6,6‐tetramethyl‐piperidin‐1‐yloxy)‐ethoxycarbonyl]‐propyl ester ( 3 ) was synthesized and used as an initiator in atom transfer radical polymerization of methyl methacrylate in the presence of CuCl and pentamethyldiethylenetriamine at 60°C. A linear behavior was observed in both plots of ln([M]₀/[M]) versus time and M_n,_GPC versus conversion indicating that the polymerization proceeded in a controlled/living manner. Thus obtained PMMA precursor was used as a macroinitiator in nitroxide‐mediated radical polymerization of styrene (St) at 125°C to give well‐defined PMMA‐b‐PS with crown ether per chain. Kinetic data were also obtained for copolymerization. Moreover, potassium picrate (K⁺ picrate) complexation of 3 and PMMA‐b‐PS copolymer was studied. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3242–3249, 2006     

Atom transfer radical polymerization of styrene and methyl methacrylate catalyzed by FeCl2/iminodiacetic acid

The atom transfer radical polymerization of styrene and methyl methacrylate with FeCl₂/iminodiacetic acid as the catalyst system in bulk was successfully implemented at 70 and 110 °C, respectively. The polymerization was controlled: the molecular weight of the resultant polymer was close to the calculated value, and the molecular weight distribution was relatively narrow (weight‐average molecular weight/number‐average molecular weight ∼ 1.5). Block copolymers of polystyrene‐b‐poly(methyl methacrylate) and poly(methyl methacrylate)‐b‐poly(methyl acrylate) were successfully synthesized, confirming the living nature of the polymerization. A small amount of water added to the reaction system increased the reaction rate and did not affect the living nature of the polymerization system. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 4308–4314, 2000     

Reverse atom transfer radical solution polymerization of methyl methacrylate under pulsed microwave irradiation

The reverse atom transfer radical polymerization (RATRP) of methyl methacrylate (MMA) was successfully carried out under pulsed microwave irradiation (PMI) at 69 °C with N,N‐dimethylformamide as a solvent and with azobisisobutyronitrile (AIBN)/CuBr₂/tetramethylethylenediamine as an initiation system. PMI resulted in a significant increase in the polymerization rate of RATRP. A 10.5% conversion for a polymer with a number‐average molecular weight of 34,500 and a polydispersity index of 1.23 was obtained under PMI with a mean power of 4.5 W in only 52 min, but 103 min was needed under a conventional heating process (CH) to reach a 8.3% conversion under identical conditions. At different [MMA]₀/[AIBN]₀ molar ratios, the apparent rate constant of polymerization under PMI was 1.5–2.3 times larger than that under CH. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3823–3834, 2002     

Synthesis of 4-arm methyl methacrylate star polymer by atom transfer radical polymerization

The synthesis of 4-arm methyl methacrylate star polymer had been achieved successfully by atom transfer radical polymerization using CuCl as catalyst, 2, 2′-bipyridyl as ligand and pentaerythritol tetrakis (2-bromoisobutyrate) as the initiator. The star polymer was characterized by ¹H-NMR and GPC, by which the precise 4-arm structure of the PMMA was confirmed. __________ Translated from Journal of Shaanxi Normal University (Natural Science Edition), 2008, 36(2) (in Chinese)     

Synthesis of diblock copolymers by combining stable free radical polymerization and atom transfer radical polymerization

A stable nitroxyl radical functionalized with an initiating group for atom transfer radical polymerization (ATRP), 4‐(2‐bromo‐2‐methylpropionyloxy)‐2,2,6,6‐tetramethyl‐1‐piperidinyloxy (Br‐TEMPO), was synthesized by the reaction of 4‐hydroxyl‐2,2,6,6‐tetramethyl‐1‐piperidinyloxy with 2‐bromo‐2‐methylpropionyl bromide. Stable free radical polymerization of styrene was then carried out using a conventional thermal initiator, dibenzoyl peroxide, along with Br‐TEMPO. The obtained polystyrene had an active bromine atom for ATRP at the ω‐end of the chain and was used as the macroinitiator for ATRP of methyl acrylate and ethyl acrylate to prepare block copolymers. The molecular weights of the resulting block copolymers at different monomer conversions shifted to higher molecular weights and increased with monomer conversion. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2468–2475, 2006     

Synthesis and characterization of well‐defined ABC‐type triblock copolymers via atom transfer radical polymerization and stable free‐radical polymerization

An asymmetric difunctional initiator 2‐phenyl‐2‐[(2,2,6,6 tetramethylpiperidino)oxy] ethyl 2‐bromo propanoate ( 1 ) was used for the synthesis of ABC‐type methyl methacrylate (MMA)‐tert‐butylacrylate (tBA)‐styrene (St) triblock copolymers via a combination of atom transfer radical polymerization (ATRP) and stable free‐radical polymerization (SFRP). The ATRP‐ATRP‐SFRP or SFRP‐ATRP‐ATRP route led to ABC‐type triblock copolymers with controlled molecular weight and moderate polydispersity (M_w/M_n < 1.35). The block copolymers were characterized by gel permeation chromatography and ¹H NMR. The retaining chain‐end functionality and the applying halide exchange afforded high blocking efficiency as well as maintained control over entire routes. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2025–2032, 2002     

Atom transfer radical polymerization of methyl acrylate,methyl methacrylate and styrene in the presence of trolamine as a highly effective promoter

Transition metal-mediated atom transfer radical polymerization(ATRP) is a ‘‘living'/controlled radical polymerization. Recently, there has been widely increasing interest in reducing the high costs of catalyst separation and post-polymerization purification in ATRP. In this work, trolamine was found to significantly enhance the catalytical performance of Cu Br/N,N,N0,N0-tetrakis(2-pyridylmethyl) ethylenediamine(Cu Br/TPEN) and Cu Br/tris[2-(dimethylamino) ethylamine](Cu Br/Me6TREN). With the addition of 25-fold molar amount of trolamine relative to Cu Br, the catalyst loadings of Cu Br/TPEN and Cu Br/Me6 TREN were dramatically reduced from a catalyst-to-initiator ratio of 1 to 0.01 and 0.05,respectively. The polymerizations of methyl acrylate, methyl methacrylate and styrene still showed first-order kinetics in the presence of trolamine and produced poly(methyl acrylate), poly(methyl methacrylate) and polystyrene with molecular weights close to theoretical values and low polydispersities. These results indicate that trolamine is a highly effective and versatile promoter for ATRP and is promising for potential industrial application.     

Atom transfer radical polymerization of methyl methacrylate catalyzed by cobalt catalyst system

A new catalyst system, CoCl₂/tris(2‐(dimethyl amino) ethyl)amine (Me₆ TREN), was used to catalyze the polymerization of methyl methacrylate (MMA) successfully through atom transfer radical polymerization mechanism. The control over the polymerization was not ideal, the molecular weight distribution of the resulting polymer (PMMA) was relatively broad (M_w/M_n = 1.63–1.80). To improve its controllability, a small amount of hybrid deactivator (FeBr₃/Me₆TREN or CuBr₂/Me₆TREN) was added in the cobalt catalyst system. The results showed that the level of control over the polymerization was significantly improved with the hybrid cobalt–iron (or cobalt–copper) catalyst system; the polydispersity index of the resulting polymer was reduced to a low level (M_w/M_n = 1.15–1.46). Furthermore, with the hybrid cobalt–iron catalyst, the dependence of the propagation rate on the temperature and the copolymerization of methacrylate (MA) with PMMA‐Br as macroinitiator were also investigated. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5207–5216, 2005     

Synthesis of styrene/methyl methacrylate copolymers by atom transfer radical polymerization: 2D NMR investigations

Copolymers of styrene and methyl methacrylate were synthesized by atom transfer radical polymerization using methyl 2‐bromopropionate as initiator and CuBr/N,N,N′,N′,N″‐pentamethyldiethylenetriamine as catalyst. Molecular weight distributions were determined by gel permeation chromatography. The composition of the copolymer was determined by ¹H NMR. The comonomer reactivity ratios, determined by both Kelen–Tudos and nonlinear error‐in‐variables methods, were r_S = 0.64 ± 0.08, r_M = 0.63 ± 0.08 and r_S = 0.66, r_M = 0.65, respectively. The α‐methyl and carbonyl carbon resonances were found to be compositionally and configurationally sensitive. Complete spectral assignments of the ¹H and ¹³C NMR spectra of the copolymers were done by distortionless enhancement by polarization transfer and two‐dimensional NMR techniques such as heteronuclear single quantum coherence and heteronuclear multiple quantum coherence. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2076–2085, 2006     

Synthesis of miktoarm star and miktoarm star block copolymers via a combination of atom transfer radical polymerization and stable free‐radical polymerization

A trifunctional initiator, 2‐phenyl‐2‐[(2,2,6,6‐tetramethyl)‐1‐piperidinyloxy] ethyl 2,2‐bis[methyl(2‐bromopropionato)] propionate, was synthesized and used for the synthesis of miktoarm star AB₂ and miktoarm star block AB₂C₂ copolymers via a combination of stable free‐radical polymerization (SFRP) and atom transfer radical polymerization (ATRP) in a two‐step or three‐step reaction sequence, respectively. In the first step, a polystyrene (PSt) macroinitiator with dual ω‐bromo functionality was obtained by SFRP of styrene (St) in bulk at 125 °C. Next, this PSt precursor was used as a macroinitiator for ATRP of tert‐butyl acrylate (tBA) in the presence of Cu(I)Br and pentamethyldiethylenetriamine at 80 °C, affording miktoarm star (PSt)(PtBA)₂ [where PtBA is poly(tert‐butyl acrylate)]. In the third step, the obtained St(tBA)₂ macroinitiator with two terminal bromine groups was further polymerized with methyl methacrylate by ATRP, and this resulted in (PSt)(PtBA)₂(PMMA)₂‐type miktoarm star block copolymer [where PMMA is poly(methyl methacrylate)] with a controlled molecular weight and a moderate polydispersity (weight‐average molecular weight/number‐average molecular weight < 1.38). All polymers were characterized by gel permeation chromatography and ¹H NMR. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2542–2548, 2003     

Reverse atom transfer radical polymerization of methyl methacrylate initiated by p‐chlorobenzenediazonium tetrafluoroborate

The controlled polymerization of methyl methacrylate (MMA) in bulk was initiated with p‐chlorobenzenediazonium tetrafluoroborate ( 1 ) and Cu(II) or Cu(I)/Cu(II)/N,N,N′,N″,N″‐pentamethyldietylene triamine (PMDETA) complex system at various temperatures (20, 60, and 90 °C). The proposed polymerization mechanism is based on the Meerwein‐type arylation reaction followed by a reverse atom transfer radical polymerization. In this mechanism, aryl radicals formed by the reaction with 1 and Cu(I) and/or PMDETA initiated the polymerization of MMA. The polymerization is controlled up to a molecular weight of 46,000 at 90 °C. Chain extension was carried out to confirm the controlled manner of the polymerization system. In all polymerization systems, the polydispersity index and initiator efficiency ranged from 1.10–1.57 to 0.10–0.21, respectively. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2019–2025, 2003     

Synthesis of methyl methacrylate,styrene, and isobutylene multiblock copolymers using atom transfer and cationic polymerization

ABCBA‐type pentablock copolymers of methyl methacrylate, styrene, and isobutylene (IB) were prepared by the cationic polymerization of IB in the presence of the α,ω‐dichloro‐PS‐b‐PMMA‐b‐PS triblock copolymer [where PS is polystyrene and PMMA is poly(methyl methacrylate)] as a macroinitiator in conjunction with diethylaluminum chloride (Et₂AlCl) as a coinitiator. The macroinitiator was prepared by a two‐step copper‐based atom transfer radical polymerization (ATRP). The reaction temperature, ?78 or ?25 °C, significantly affected the IB content in the resulting copolymers; a higher content was obtained at ?78 °C. The formation of the PIB‐b‐PS‐b‐PMMA‐b‐PS‐b‐PIB copolymers (where PIB is polyisobutylene), prepared at ?25 (20.3 mol % IB) or ?78 °C (61.3 mol % IB; rubbery material), with relatively narrow molecular weight distributions provided direct evidence of the presence of labile chlorine atoms at both ends of the macroinitiator capable of initiation of cationic polymerization of IB. One glass‐transition temperature (T_g), 104.5 °C, was observed for the aforementioned triblock copolymer, and the pentablock copolymer containing 61.3 mol % IB showed two well‐defined T_g's: ?73.0 °C for PIB and 95.6 °C for the PS–PMMA blocks. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3823–3830, 2005     

Growth of poly(methyl methacrylate) brushes on silicon surfaces by atom transfer radical polymerization

Poly(methyl methacrylate) (PMMA) brushes are grown by surface‐initiated atom transfer radical polymerization on silicon surfaces at various polymerization temperatures. Kinetic studies show that the layer thickness scales linearly with the degree of polymerization of the polymers under some conditions, indicating a constant graft density of the surface‐attached chains. At high temperatures, the layer growth is a controlled process only for short reaction times, and after a rapid increase, the film growth levels off, and a constant thickness is obtained. At lower reaction temperatures, polymers with a lower polydispersity are obtained, but at the expense of a much slower growth rate. Accordingly, intermediate temperatures yield the highest film thickness on experimentally feasible timescales. The reinitiation of these surface‐grafted PMMA chains at room temperature to either extend the chains or grow a chemically different polyglycidylmethacrylate block demonstrates the presence of active ends and the living nature of the surface‐grafted PMMA chains. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1758–1769, 2006     

Atom transfer radical polymerization of styrene under pulsed microwave irradiation

A homogeneous solution atom transfer radical polymerization (ATRP) and reverse atom transfer radical polymerization (RATRP) of styrene (St) in N,N-dimethylformamide (DMF) were successfully carried out under pulsed microwave irradiation (PMI), using 1-bromo-1-phenylethane (1-PEBr)/CuCl/N,N,N′,N′′,N′′-pentamethyldiethylenetriamine (PMDETA) as an initiating system at 85°C and 2,2′-azo-bis-isobutyrontrile (AIBN)/CuCl₂/PMDETA as an initiating system at 95°C, respectively. The polymerization rates under PMI were greatly increased in comparison with those under identical conventional heating (CH).     

Probing the effects of π–π stacking on the controlled radical polymerization of styrene and fluorinated styrene

The addition of the π–π stacking agent octafluorotoluene (OFT) resulted in up to a 50% reduction in monomer conversion after 24 h for atom transfer radical polymerization (ATRP) reactions of styrene, when performed at 85 °C with 1 eq of OFT compared with styrene in the initial reaction mixture. Monitoring the progress showed that the ATRP of styrene in the presence of either OFT or hexafluorobenzene (HFB) maintained a linear relationship between monomer conversion and number average molecular weights, while showing a first order rate dependence on monomer. The effects of π–π stacking on the K_ATRP could be overcome by using adjusting the redox activity of the metal‐ligand complex while maintaining reaction temperatures of 85 °C. Further experiments showed that nitroxide‐mediated polymerizations of St were affected to an identical extent by the presence of the π–π stacking agent HFB. The ATRP of pentafluorostyrene (PFSt) in the presence of π–π stackers benzene or toluene showed an increase in monomer conversion compared with reactions in their absence, consistent with M_n π–π stacking increasing the stability of the active radical. Interactions between the π–π stacking agents OFT and HFB and the aromatic groups in the ATRP of St or PFSt were verified by ¹H NMR analysis. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Ruthenium carborane complexes in the controlled radical polymerization of methyl methacrylate

New initiators based on closo-and exo-nido-ruthenacarboranes with phosphine and diphosphine ligands were proposed as chain growth regulators. They allow conducting the controlled synthesis of poly(methyl methacrylate) under radical initiation conditions. Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 1, pp. 85–89, January, 2006.     

Reverse atom transfer radical polymerization of methyl methacrylate in room‐temperature ionic liquids

The reverse atom transfer radical polymerization (ATRP) of methyl methacrylate (MMA) was successfully carried out in 1‐butyl‐3‐methylimidazolium hexafluorophosphate with 2,2′‐azobisisobutyronitrile/CuCl₂/bipyridine as the initiating system, which had been reported as not able to promote a controlled process of MMA in bulk. The living nature of the polymerization was confirmed by kinetic studies, end‐group analysis, chain extension, and block copolymerization results. The polydispersity of the polymer obtained was quite narrow, with a weight‐average molecular weight/number‐average molecular weight ratio of less than 1.2. In comparison with other reverse ATRPs in bulk or conventional solvents, a much smaller amount of the catalyst was used. After a relatively easy removal of the polymer and residue monomer, the ionic liquid and catalytic system could be reused without further treatment. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 143–151, 2003