磁性Y-MOF@SiO2@Fe3O4催化剂的制备及其在Aza-Micheal加成反应中的性能

在磁性SiO₂@Fe₃O₄纳米微球表面原位合成包覆不同含量的Y-MOF,从而制备出新型磁性Y-MOF@SiO₂@Fe₃O₄催化剂。采用XRD、TEM、FT-IR、VSM和N₂吸附-脱附测试等手段对催化剂的结构进行表征,并且评价了催化剂对苯胺和丙烯酸甲酯的Aza-Micheal加成反应性能。结果表明Y-MOF能均匀包覆在磁性SiO₂@Fe₃O₄纳米微球表面,形成具有核壳结构的磁性Y-MOF@SiO₂@Fe₃O₄催化剂,催化剂具有良好的超顺磁性。Y-MOF含量为43.3%（w/w）的Y-MOF@SiO₂@Fe₃O₄催化剂,在苯胺和丙烯酸甲酯的Aza-Micheal加成反应表现出最好的催化性能,丙烯酸甲酯的转化率为88.3%时,N-（β-甲氧碳酰乙基）苯胺的选择性可达99.8%。反应后的催化剂可以通过外磁场容易回收,并且重复使用5次其转化率和选择性没有明显下降。     

一维纳米Co_3O_4,Ag/Co_3O_4及CuO/Co_3O_4的合成与电催化性能(英文)

采用水热合成法制备了Co3O4及复合Ag/Co3O4、CuO/Co3O4一维纳米产品。用XRD,FE-SEM和TEM手段对产品进行了表征。采用循环伏安法研究了合成产品修饰的玻碳电极在碱性溶液中对对硝基苯酚的电催化还原性能。与裸玻碳电极相比,1mmol·L-1的对硝基苯酚在用Co3O4、特别是CuO/Co3O4修饰的玻碳电极上还原的峰电流明显增大,用Ag/Co3O4(Ag/Co原子比分别为1∶5和2∶5)修饰的玻碳电极催化还原对硝基苯酚时,尽管还原峰电流增大不是太大,但其峰电位明显降低(分别降低0.265和0.371V)。     

MgAl2O4尖晶石对锂离子电池正极材料LiMn2O4的循环性能影响研究

MgAl₂O₄ spinel doping into cathode materials LiMn₂O₄ was used to improve the cyclic performance of the cathode. X-ray analysis results showed, when MgAl₂O₄ precursors were mixed with LiMn₂O₄ and sintered at 770 ℃ for 12 hour, MgAl₂O₄-LiMn₂O₄ mulriple spinel with the same physical characteristics as pure LiMn₂O₄ were synthesized. The electro-chemical performance testing showed, comparing with pure LiMn₂O₄, the first charge-discharge capacity of doping materials somewhat reduced, but the cyclic performance improved. The mechanism for doping material was also discussed.     

Magnetic diphase nanostructure of ZnFe2O4/γ-Fe2O3

Magnetic diphase nanostructures of ZnFe₂O₄/γ-Fe₂O₃ were synthesized by a solvothermal method. The formation reactions were optimized by tuning the initial molar ratios of Fe/Zn. All samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, and Raman spectra. It is found that when the initial molar ratio of Fe/Zn is larger than 2, a diphase magnetic nanostructure of ZnFe₂O₄/γ-Fe₂O₃ was formed, in which the presence of ZnFe₂O₄ enhanced the thermal stability of γ-Fe₂O₃. Further increasing the initial molar ratio of Fe/Zn larger than 6 destabilized the diphase nanostructure and yielded traces of secondary phase α-Fe₂O₃. The grain surfaces of diphase nanostructure exhibited a spin-glass-like structure. At room temperature, all diphase nanostructures are superparamagnetic with saturation magnetization being increased with γ-Fe₂O₃ content.     

Co3O4纳米片的制备及对H2O2电还原反应的催化性能简

通过恒电势电沉积和加热处理在泡沫镍基体上制备了Co3O4纳米片. 利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射(XRD)、傅里叶变换红外光谱(FTIR)和X射线光电子能谱(XPS)等手段对纳米片的形貌和结构进行了表征. 采用线性伏安扫描和计时电流技术研究了Co3O4纳米片电极对H2O2的电还原性能. 结果表明,在3.0 mol/L KOH 和 0.4 mol/L H2O2溶液中,当电压为-0.4 V(vs. Ag/AgCl)时,线性伏安扫描电流密度达到-0.386 A/cm2,在1000 s 测试时间内,计时电流密度衰减很小,表明Co3O4纳米片电极对H2O2具有很高的活性和稳定性.     

MgFe2O4-Fe2O3纳米粉体的软化学合成及电磁学特性

Nano-MgFe₂O₄-Fe₂O₃ magnetic powders were synthesized by citrate gel under microwave irradiation. The structure，particle size distribution，electromagnetic characteristics of nano-MgFe₂O₄-Fe₂O₃ were characterized by using TG-DTA, X-ray, electronic microscope, nano-size measurement and electromagnetism measurement apparatus。The results show that the product is a mixture of MgFe₂O₄ and Fe₂O₃ with average size of 44 nm, tanδ for the product is 0.265 and 0.610 at frequency of 1.0 GHz and 1.8 GHz respectively.     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃-Bi₂O₃-ZnO-Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1 350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1 364,介电损耗低至1.2%。     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃‐Bi₂O₃‐ZnO‐Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1364,介电损耗低至1.2%。     

La2O3对Ni/γ-Al2O3甲烷化催化剂的助催化作用

我国将稀土作为助剂引入镍基甲烷化催化剂,大大提高了催化剂的活性和热稳定性,并已投入工业应用［1－3］．稀土对不同镍催化剂反应性能及其作用机理的研究已有一些报导［3－7］．谢有畅等观察到镍负载在经单层La2O3改性的γ－Al2O3表面,其晶粒要比没有La2O3时小得多．Rotgerink等认为添加La后反应速率的增加不只是由于几何效应,而是La对甲烷化本身有促进作用,单位镍表面的活性是随La含量不同而改变的,活性增加的同时表观活化能也增加［5］．作为助剂的La2O3在氢还原和反应过程中的变化及其作用的研究和讨论较少,目前一般认为添…     

复合多铁材料NiFe2O4/BaTiO3的制备及性能

采用溶胶-凝胶与固相反应相结合的方法制备了xNiFe2O4/(1-x)BaTiO3(x=0.1,0.2,0.3,0.4,0.5,0.6)系列复合多铁材料.X射线衍射(XRD)结果表明,复合材料中只含有钙钛矿结构的BaTiO3和尖晶石结构的NiFe2O4,说明共烧过程中两者未发生明显的化学反应,铁电相与铁磁相共存.扫描电子显微镜(SEM)观测结果表明材料内部是异质结构的,高分辨透射电子显微镜(HRTEM)观测结果进一步说明了NiFe2 O4和BaTiO3共存,并且在两种物质的接触处能够看到清晰的界面.这种由BaTiO3和NiFe2 O4组成的复合材料对外同时表现出铁电性和铁磁性.电滞回线结果表明,该复合材料具有铁电性,但存在着一定的漏电.介电频谱表明材料的介电常数随着频率的升高而下降,在低频下达到定值,并且铁磁相的含量对材料的介电性有影响.磁性能测试结果表明材料的磁性源于NiFe2O4,并且磁性随着NiFe2O4含量的增加而增强.     

Structure and magnetism of NaRu2O4 and Na2.7Ru4O9

The structures of NaRu₂O₄ and Na_2.7Ru₄O₉ are refined using neutron diffraction. NaRu₂O₄ is a stoichiometric compound consisting of double chains of edge sharing RuO₆ octahedra. Na_2.7Ru₄O₉ is a non-stoichiometric compound with partial occupancy of the Na sublattice. The structure is a mixture of single, double and triple chains of edge-shared RuO₆ octahedra. NaRu₂O₄ displays temperature independent paramagnetism with . Na_2.7Ru₄O₉ is paramagnetic, χ₀= with and a Curie constant of 0.0119 emu/mol Oe K. Specific heat measurements reveal a small upturn at low temperatures, similar to the upturn observed in La₄Ru₆O₁₉. The electronic contribution to the specific heat (γ) for Na_2.7Ru₄O₉ was determined to be15 mJ/mole_Ru K².     

Preparation of Mn2O3 and Mn3O4 nanofibers via an electrospinning technique

Thin PVA/manganese acetate composite fibers were prepared by using sol-gel processing and electrospinning technique. After calcinations of the above precursor fibers, Mn₂O₃ and Mn₃O₄ nanofibers with a diameter of 50-200 nm could be successfully obtained. The fibers were characterized by TG-DTA, Scanning electron microscopy, FT-IR, WAXD, respectively. The results showed that the crystalline phase and morphology of nanofibers were largely influenced by the calcination temperature.     

四角星形BiVO4/Bi2O3催化剂的制备及性能

采用水热法合成具有四角星形貌的钒酸铋,再将钒酸铋浸渍在碱溶液里二次水热,制备出BiVO_4/Bi_2O_3催化剂。采用X射线粉末衍射(XRD)、扫描电子显微镜(SEM),紫外-可见漫反射(UV-Vis DRS)等方法对样品进行表征。可见光下,BiVO_4/Bi_2O_3复合物的光催化降解罗丹明B性能及光电流响应均优于纯BiVO_4。这是由于BiVO_4/Bi_2O_3复合材料形成了异质结构,有效抑制了光生电子与空穴的复合效率。     

四角星形BiVO4/Bi2O3催化剂的制备及性能研究

采用水热法合成具有四角星形貌的钒酸铋,再将钒酸铋浸渍在碱溶液里二次水热,制备出BiVO₄/Bi₂O₃催化剂。采用X射线粉末衍射(XRD)、扫描电子显微镜(SEM),紫外-射(UV-Vis DRS)等方法征。可见光下,BiVO₄/Bi₂O₃复合物的光催化降解丹明B性能及光电优于纯BiVO₄。BiVO₄/Bi₂O₃复合材料形成了异质结构,有效抑制了光电子与空穴的复合效率。     

BaO-Al2O3-B2O3系密封玻璃的结构与性质

The BaO-Al₂O₃-B₂O₃ glasses manufactured for solid oxide fuel cell(SOFC) sealing were studied. The effect of different n_BaO/n_B2O3 on crystal, thermal properties, density and infrared spectra of this system has been discussed. The results show that the trends of crystallization, glass transformation temperature, dilatometric softening temperature and density increase with n_BaO/n_B2O3 values. But a typical property deviation occurs when n_BaO/n_B2O3 is 0.875, and its coefficient of thermal expansion has the maximum at this point. The changes of properties can attribute to the conversion of boron from tetrahedral coordination to trigonal, breakage of the local glass network and interaction between the network modifiers. These can be proved by infrared spectra of glasses. Thermal properties of some studied samples are suitable for the sealing of SOFC using Sm doped ceria electrolyte and operating at 400～600 ℃.     

WS2/CuGa2O4复合材料的制备及其气敏性

采用共沉淀法制备了CuGa₂O₄纳米材料,并利用水热法制备了一系列WS₂/CuGa₂O₄复合材料。结合X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)等对制备的材料进行了物相组成、表面形貌以及元素价态的分析。研究了WS₂的复合量对 CuGa₂O₄材料检测乙醇气体敏感性能的影响。实验结果表明,当 WS₂与 CuGa₂O₄质量比为 1%时,该复合材料制备的传感器在室温下对 100 μL·L^-1乙醇气体表现出 345.3 的灵敏度,响应时间和恢复时间分别为 184 和 69 s,且最低检测限为 0.1μL·L^-1。     

WS2/CuGa2O4复合材料的制备及其气敏性

采用共沉淀法制备了CuGa₂O₄纳米材料,并利用水热法制备了一系列WS₂/CuGa₂O₄复合材料。结合X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)等对制备的材料进行了物相组成、表面形貌以及元素价态的分析。研究了WS₂的复合量对CuGa₂O₄材料检测乙醇气体敏感性能的影响。实验结果表明,当WS₂与CuGa₂O₄质量比为1%时,该复合材料制备的传感器在室温下对100μL·L^-1乙醇气体表现出345.3的灵敏度,响应时间和恢复时间分别为184和69 s,且最低检测限为0.1μL·L^-1。     

层状Co3O4的制备及其电化学电容行为

以P123为模板水热合成制备了Co₂(OH)₂CO₃前驱体，200 ℃热处理后得到了具有层状结构的Co₃O₄。循环伏安、恒流放电等电化学测试表明，200 ℃所得Co₃O₄电极在6 mol·L^-1 KOH溶液中和-0.1～0.5 V(vs Ag/AgCl)电位范围内，具有较好的循环稳定性能，单电极比电容达到505 F·g^-1。     

添加Al2O3对Ni0.5Zn0.5Fe2O4纳米纤维结构和磁性能的影响

采用静电纺丝技术制备了添加0～20wt%Al2O3的Ni0.5Zn0.5Fe2O4纳米纤维。通过XRD、FESEM、TEM和VSM对样品的物相结构、形貌和磁性能进行了表征。结果表明,所合成的复合纳米纤维的直径都分布在40～150 nm之间,添加到纤维中的Al2O3主要以非晶态形式分布于铁氧体晶粒边界;随着Al2O3添加量的增加,可观察到γ-Fe2O3相逐渐析出,Ni-Zn铁氧体的晶格常数单调减小,说明有一些Al2O3进入到尖晶石晶格中取代了B位的Fe3+离子,Ni-Zn铁氧体的平均晶粒尺寸先增大后减小,在Al2O3添加量为8wt%时达到最大值39.2 nm;比饱和磁化强度和矫顽力随Al2O3添加量的增加呈现出相同的变化规律,先减小后增大,当Al2O3添加量超过5wt%时又开始变小。     

荧光XAFS表征Pt/BaAl2O4-Al2O3催化剂中的微量铂物种

随着稀薄燃烧(lean-burn)发动机的推广使用和环保法规的日趋严格,消除稀燃尾气中的氮氧化物(N O x)已刻不容缓。N O x储存还原技术被认为是最具应用前景的方法之一[1,2]。目前,对Pt/BaA l2O4-A l2O3体系中N O x储存与还原机制的研究较多[1￣4],但对该体系中微量铂物种微观结构及其与性能的关系研究较少,这主要是由于Pt含量(0.1w t%￣0.5wt%)太低,分散度较高,使表征方法受到很大限制。本文采用共沉淀-浸渍法制得具有较高比表面积和热稳定性的N O x储存还原催化剂Pt/BaA l2O4-A l2O3,应用荧光X-射线吸收精细结构方法(Fluores-cence-…