一氧化碳合成金刚石薄膜的形貌和结构分析

利用微波等离子体化学气相沉积(MPCVD)技术，采用偏压增加成核(BEN)、两步生长的方法在一氧化碳(CO)和氢气(H₂)的环境下制备了金刚石薄膜. 利用扫描电子显微镜(SEM)、Raman光谱仪和透射电子显微镜(TEM)对金刚石薄膜的形貌和结构进行了分析. 研究发现金刚石晶粒在第一步成核及生长的过程中产生了层错和孪晶，而在第二步的生长过程中产生的层错和孪晶很少，最终形成的金刚石晶粒外表面比较光滑，包含有近五次对称或者平行的片状的孪晶，并可以观察到少量的位错. 而在样品的边缘由于等离子体的不均匀产生了比样品中心成核密度低的区域. 在这个区域中，发现了一个新的非金刚石的碳结构.     

To the synthesis of polycrystalline diamond

Abstract

The sintering system “Diamond-Graphite-Cobalt” is investigated by means of a High Pressure - High Temperature - Belt - Apparatus. Described are the sintering conditions used and some of the properties of the compacts obtained. Good sintering structures and hard PCD (up to 50 GPa) were obtained at 7,5 GPa and 1500°C.     

硼硫协同掺杂金刚石的高压合成与电学性能研究

FeNiMnCo-C体系中,在压力6.5 GPa、温度1280—1300℃的极端物理条件下,采用温度梯度法成功合成了硼(B)、硫(S)协同掺杂金刚石大单晶.通过傅里叶红外光谱测试对高温高压所制备金刚石中的杂质进行了表征.借助霍尔效应对典型金刚石样品的电输运性能进行了测试,测试结果表明:硼硫协同掺杂有利于提高p型金刚石的电导率,而且硼硫在合成体系中的添加比例可以决定金刚石的p, n特性.此外,第一性原理计算结果表明,合成体系中不同比例的硼硫协同掺杂对金刚石的p, n特性以及电导率有着直接的影响,计算结果与实验测试结果相吻合.     

High-temperature calibration of a multi-anvil high pressure apparatus

Fusion and solidification of Al and Ag samples, as well as Fe₉₃–Al₃–C₄, Fe₅₆–Co₃₇–Al₃–C₄, and Fe_57.5–Co₃₈–Al₁–Pb_0.5–C₃ alloys (in wt%), have been investigated at 6.3?GPa. Heater power jumps due to heat consumption and release on metal fusion and solidification, respectively, were used to calibrate the thermal electromotive force of the thermocouple against the melting points (mp) for Ag and Al. Thus, obtained corrections are +100°C (for sample periphery) and +65°C (center) within the 1070–1320°C range. For small samples positioned randomly in the low-gradient zone of a high pressure cell, the corrections should be +80°C and +84°C at the temperatures 1070°C and 1320°C, respectively. The temperature contrast recorded in the low-gradient cell zone gives an error about ±17°C. The method has been applied to identify the mp of the systems, which is especially important for temperature-gradient growth of large type IIa synthetic diamonds.     

Nano-polycrystalline diamond anvils: key devices for XAS at extreme conditions: their use,scientific impact,present status and future needs

ABSTRACT

Nano-polycrystalline diamonds (NPDs) have become fundamental tools for cutting-edge X-ray absorption spectroscopy (XAS) studies at high P/T conditions that opened up new research directions by overcoming previous limitations. Indeed, NPDs yield a continuous and weak X-ray background signal which enables the collection of high-quality XAS data of materials compressed in diamond anvil cells. This is a critical advantage over the classically used single-crystal diamonds that generate strong parasitic signals (glitches) which render the analysis of XAS data in many cases impossible. In this contribution we give an overview of the impact and the scientific opportunities that NPDs opened up for extreme condition XAS spectroscopy at the European Synchrotron Radiation Facility and discuss future needs.     

Boron-doped diamond synthesized by chemical vapor deposition as a heating element in a multi-anvil apparatus

ABSTRACT

We tested boron-doped diamond (BDD) synthesized by chemical vapor deposition (CVD) as a heating element in a multi-anvil apparatus. We succeeded in manufacturing BDD into a tubular shape by laser cutting and electric discharging machining. The BDD tube shaped by the electric discharging machining was contaminated by discharging electrode materials (Mo and W), which affected the heating performance. The laser-cut BDD tube has a clean surface and, therefore, had a good heating performance. We succeeded in generating temperature as high as 2670?K at a pressure around 30?GPa with laser-cut heater. Heating reproducibility was confirmed through repeated heating and cooling cycles. The recovered sample shows that a higher temperature generation above 2670?K was prevented by eutectic melting of ZrO₂ thermal insulator and Al₂O₃ sample. Owing to the commercial availability with a reasonable price, CVD–BDD heaters are more practical than a high-pressure synthesized BDD heaters for wide applications.     

Synthesis of nano-polycrystalline diamond from glassy carbon at pressures up to 25 GPa

ABSTRACT

Nano-polycrystalline diamond (NPD) with various grain sizes has been synthesized from glassy carbon at pressures 15–25?GPa and temperatures 1700–2300°C using multianvil apparatus. The minimum temperature for the synthesis of pure NPD, below which a small amount of compressed graphite was formed, significantly increased with pressure from ～1700°C at 15?GPa to ～1900°C at 25?GPa. The NPD having grain sizes less than ～50?nm was synthesized at temperatures below ～2000°C at 15?GPa and ～2300°C at 25?GPa, above which significant grain growth was observed. The grain size of NPD decreases with increasing pressure and decreasing temperature, and the pure NPD with grain sizes less than 10?nm is obtained in a limited temperature range around 1800–2000°C, depending on pressure. The pure NPD from glassy carbon is highly transparent and exhibits a granular nano-texture, whose grain size is tunable by selecting adequate pressure and temperature conditions.     

High pressure generation in the Kawai-type multianvil apparatus equipped with sintered diamond anvils

ABSTRACT

Generation of high pressure is a key to the investigation of the interior of the Earth. The Kawai-type multianvil apparatus (KMA) has been widely used in the fields of Earth science and material science. In conventional KMA, tungsten carbide (WC) has been used as the second stage anvil material. However, attainable pressure is limited to ～70?GPa even if newly developed WC is used. Recently, on the other hand, second stage anvils of sintered diamond that is much harder than WC have enabled us to extend the pressure range of KMA up to 120?GPa, corresponding to the pressure of the D” layer in the Earth’s mantle. It is evident that our development of pressure generation facilitates the investigation of the structure and dynamics of the deep mantle of the Earth.     

微波等离子体化学气相沉积合成掺氮金刚石薄膜的缺陷和结构特征及其生长行为

Diamond film was deposited in CH₄ and H₂ gas mixture with a small amount of N₂ by microwave plasma assisted chemical vapor deposition (MPCVD). Scanning electron microscopy, Raman spectroscopy and transmission electron microscopy were applied to characterize the film. The results showed that the growth of grains are different the central region and the edge. In the central region, diamond grains nucleated with a density as high as 4.8×10⁸ cm^-2 and were preferential in 〈001〉 orientation. The inner grains formed an area without stacking faults,which was surrounded by a rim with a high density of stacking faults. A growth model was suggested to interpret the morphological feature and the behavior of preferential growth. At the edge, the grains were identified to be 6H polytypes of diamond and a new twin relationship of grains was found. Besides, the effect of the N dopant on the growth behavior of the diamond film deposited by MPCVD was discussed in connection with the growth rate of the film. 关键词： 金刚石 结构表征 透射电子显微镜 多型金刚石     

纯铁触媒合成磨料级金刚石及表征

本文报道了高温高压下纯铁触媒与石墨体系合成磨料级金刚石的过程,并给出了P-T相图.在此基础上,通过调整工艺参数,控制再结晶石墨量与金刚石生长速度,合成出无色透明的金刚石样品,解决了纯铁触媒合成的金刚石透明度较差及包裹体较多的问题.采用穆斯堡尔谱仪和傅里叶红外光谱仪等测试手段,对金刚石样品内部包裹体以及氮元素含量进行了表征,在揭示包裹体形成机理的基础上提出了减少包裹体的方法,同时阐明了纯铁触媒合成的金刚石样品颜色变浅的原因. 关键词： 铁触媒 金刚石 生长速度 高温高压     

Dependence of nitrogen vacancy color centers on nitrogen concentration in synthetic diamond

Crystallization of diamond with different nitrogen concentrations was carried out with a FeNiCo-C system at pressure of 6.5 GPa. As the nitrogen concentration in diamond increased, the color of the synthesized diamond crystals changed from colorless to yellow and finally to atrovirens (a dark green). All the Raman peaks for the obtained crystals were located at about 1330 cm^-1 and contained only the sp³ hybrid diamond phase. Based on Fourier transform infrared results, the nitrogen concentration of the colorless diamond was < 1 ppm and absorption peaks corresponding to nitrogen impurities were not detected. However, the C-center nitrogen concentration of the atrovirens diamond reached 1030 ppm and the value of A-center nitrogen was approximately 180 ppm with a characteristic absorption peak at 1282 cm^-1. Furthermore, neither the NV⁰ nor the NV^- optical color center existed in diamond crystal with nitrogen impurities of less than 1 ppm by photoluminescence measurement. However, Ni-related centers located at 695 nm and 793.6 nm were observed in colorless diamond. The NE8 color center at 793.6 nm has more potential for application than the common NV centers. NV⁰ and NV^- optical color centers coexist in diamond without any additives in the synthesis system. Importantly, only the NV^- color center was noticed in diamond with a higher nitrogen concentration, which maximized optimization of the NV^-/NV⁰ ratio in the diamond structure. This study has provided a new way to prepare diamond containing only NV^- optical color centers.     

Effects of a carbon convection field on large diamond growth under high-pressure high-temperature conditions

Large diamond crystals were successfully synthesized by a FeNi-C system using the temperature gradient method under high-pressure high-temperature conditions. The assembly of the growth cell was improved and the growth process of diamond was investigated. Effects of the symmetry of the carbon convection field around the growing diamond crystal were investigated systematically by adjusting the position of the seed crystal in the melted catalyst/solvent. The results indicate that the morphologies and metal inclusion distributions of the synthetic diamond crystals vary obviously in both symmetric and non-symmetric carbon convection fields with temperature. Moreover, the finite element method was applied to analyze the carbon convection mode of the melted catalyst/solvent around the diamond crystal. This work is helpful for understanding the growth mechanism of diamond.     

Peculiarities of phase transitions when synthesizing diamond in high pressure apparatus of various types

Abstract

The influence of P, T-parmeters and duration of heat when synthesizing diamond in high pressure apparatus both of recessed anvil-type and cylindrical type (belt-type) on properties of diamond powders was studied. The dependence of pressure in reaction cells on temperature of force elements of apparatus in initial state and on efficiency of high pressure production in a reaction cell before heating was shown.     

Effects of carbon convection field on large diamond growth under high-pressure high-temperature conditions

Large diamond crystals were successfully synthesized by FeNi-C system using temperature gradient method under high-pressure high-temperature conditions. The assembly of the growth cell was improved and the growth process of diamond was investigated. Effects of the symmetry of carbon convection field around the growing diamond crystal were investigated systematically by adjusting the position of seed crystal in the melted catalyst/solvent. The results indicate that morphologies and metal inclusion distributions of the synthetic diamond crystals vary obviously in both symmetric and non-symmetric carbon convection fields with temperature. Moreover, finite element method was applied to analyze carbon convection mode of the melted catalyst/solvent around the diamond crystal. This work is helpful for understanding the growth mechanism of diamond.     

硼氢协同掺杂Ib型金刚石大单晶的高温高压合成与电学性能研究

在压力6.0 GPa和温度1600 K条件下, 利用温度梯度法研究了(111)晶面硼氢协同掺杂Ib型金刚石的合成. 傅里叶红外光谱测试表明: 氢以sp³杂化的形式存在于所合成的金刚石中, 其对应的红外特征吸收峰位分别位于2850 cm^-1和2920 cm^-1处. 此外, 霍尔效应测试结果表明: 所合成的硼氢协同掺杂金刚石具有p型半导体材料特性. 相对于硼掺杂金刚石而言, 由于氢的引入导致硼氢协同掺杂金刚石电导率显著提高. 为了揭示硼氢协同掺杂金刚石电导率提高的原因, 对不同体系进行了第一性原理理论计算, 计算结果表明其与实验结果符合. 该研究对金刚石在半导体领域的应用有重要的现实意义.     

High pressure sintering behavior of polycrystalline diamond with tungsten

Polycrystalline diamond was investigated under high pressure and high temperature of 5.0 GPa and 1100–1500 °C in the presence of tungsten. In situ resistance measurements indicated that reactions between diamond and tungsten happened at about 960 °C. Phase analysis demonstrated that WC increased and meta-stability of W₂C decreased clearly at the higher temperature. It is clear from the characterization of the sintered body that the electrical resistance decreased and the density of specimens increased as the sintering temperature rose. The specimen sintered at 1500 °C has a homogeneous microstructure and good conductivity.     

Large single crystal diamond grown in FeNiMnCo-S-C system under high pressure and high temperature conditions

Large diamonds have successfully been synthesized from FeNiMnCo-S-C system at temperatures of 1255-1393 ℃and pressures of 5.3-5.5 GPa.Because of the presence of sulfur additive,the morphology and color of the large diamond crystals change obviously.The content and shape of inclusions change with increasing sulfur additive.It is found that the pressure and temperature conditions required for the synthesis decrease to some extent with the increase of S additive,which results in left down of the V-shape region.The Raman spectra show that the introduction of additive sulfur reduces the quality of the large diamond crystals.The x-ray photoelectron spectroscopy(XPS) spectra show the presence of S in the diamonds.Furthermore,the electrical properties of the large diamond crystals are tested by a four-point probe and the Hall effect method.When sulfur in the cell of diamond is up to 4.0 wt.%,the resistance of the diamond is 9.628×10~5 Ω·cm.It is shown that the large single crystal samples are n type semiconductors.This work is helpful for the further research and application of sulfur-doped semiconductor large diamond.     

Influence of annealing treatment on as-grown Ib-type diamond crystal at a high temperature and high pressure

In this paper,we report on the influence of annealing treatment on as-grown Ib-type diamond crystal under high pressure and high temperature in a china-type cubic anvil high-pressure apparatus.Experiments are carried out at a pressure of 7.0 GPa and temperatures ranging from 1700 C to 1900 C for 1 h.Annealing treatment of the diamond crystal shows that the aggregation rate constant of nitrogen atoms in the as-grown Ib-type diamond crystal strongly depends on diamond morphology and annealing temperature.The aggregation rate constant of nitrogen remarkably increases with the increase of annealing temperature and its value in octahedral diamond is much higher than that in cubic diamond annealed at the same temperature.The colour of octahedral diamond crystal is obviously reduced from yellow to nearly colorless after annealing treatment for 1 h at 1900 C,which is induced by nitrogen aggregation in a diamond lattice.The extent of nitrogen aggregation in an annealed diamond could approach approximately 98% indicated from the infrared absorption spectra.The micro-Raman spectrum reveals that the annealing treatment can improve the crystalline quality of Ib-type diamond characterized by a half width at full maximum at first order Raman peak,and therefore the annealed diamond crystals exhibit nearly the same properties as the natural IaA-type diamond stones of high quality in the Raman measurements.     

Growth and annealing study of hydrogen-doped single diamond crystals under high pressure and high temperature

A series of diamond crystals doped with hydrogen is successfully synthesized using LiH as the hydrogen source in a catalyst-carbon system at a pressure of 6.0 GPa and temperature ranging from 1255 C to 1350 C.It is shown that the high temperature plays a key role in the incorporation of hydrogen atoms during diamond crystallization.Fourier transform infrared micro-spectroscopy reveals that most of the hydrogen atoms in the synthesized diamond are incorporated into the crystal structure as sp 3-CH 2-symmetric(2850 cm-1) and sp 3 CH 2-antisymmetric vibrations(2920 cm-1).The intensities of these peaks increase gradually with an increase in the content of the hydrogen source in the catalyst.The incorporation of hydrogen impurity leads to a significant shift towards higher frequencies of the Raman peak from 1332.06 cm-1 to 1333.05 cm-1 and gives rise to some compressive stress in the diamond crystal lattice.Furthermore,hydrogen to carbon bonds are evident in the annealed diamond,indicating that the bonds that remain throughout the annealing process and the vibration frequencies centred at 2850 and 2920 cm-1 have no observable shift.Therefore,we suggest that the sp 3 C-H bond is rather stable in diamond crystals.     

高温高压下氮氢协同掺杂对{100}晶面生长宝石级金刚石的影响

在压力为5.5–6.2 GPa, 温度为1280–1450 ℃的条件下, 利用温度梯度法详细考察了氮氢协同掺杂对100晶面生长宝石级金刚石的影响. 实验结果表明伴随合成腔体内氮、氢浓度的升高, 合成条件明显升高, 金刚石生长V形区间上移; 晶体的红外光谱中与氮相关的吸收峰急剧增强, 氮含量可达2000 ppm, 同时位于2850 cm^-1和2920 cm^-1对应于 sp³杂化 C–H 键的对称伸缩振动和反对称伸缩振动的红外特征峰逐渐增强, 表明晶体中既有高的氮含量, 同时又含有氢. 对晶体进行电镜扫描发现, 氮氢协同掺杂对晶体形貌影响明显, 出现拉长的{111}面, 且晶体表面上有三角形生长纹理. 拉曼测试表明, 晶体的峰位向高频偏移、半峰宽变大, 说明氮、氢杂质的进入对晶体内部产生了应力. 本文成功地以{100}晶面为生长面合成出高氮含氢宝石级金刚石单晶, 在探究氮氢共存环境下金刚石生长特性的同时, 也可为理解天然金刚石的形成机理提供帮助.