Mechanism underlying bioinertness of self-assembled monolayers of oligo(ethyleneglycol)-terminated alkanethiols on gold: protein adsorption, platelet adhesion, and surface forces

The mechanism underlying the bioinertness of the self-assembled monolayers of oligo(ethylene glycol)-terminated alkanethiol (OEG-SAM) was investigated with protein adsorption experiments, platelet adhesion tests, and surface force measurements with an atomic force microscope (AFM). In this work, we performed systematic analysis with SAMs having various terminal groups (-OEG, -OH, -COOH, -NH(2), and -CH(3)). The results of the protein adsorption experiment by the quartz crystal microbalance (QCM) method suggested that having one EG unit and the neutrality of total charges of the terminal groups are essential for protein-resistance. In particular, QCM with energy dissipation analyses indicated that proteins absorb onto the OEG-SAM via a very weak interaction compared with other SAMs. Contrary to the protein resistance, at least three EG units as well as the charge neutrality of the SAM are found to be required for anti-platelet adhesion. When the identical SAMs were formed on both AFM probe and substrate, our force measurements revealed that only the OEG-SAMs possessing more than two EG units showed strong repulsion in the range of 4 to 6 nm. In addition, we found that the SAMs with other terminal groups did not exhibit such repulsion. The repulsion between OEG-SAMs was always observed independent of solution conditions [NaCl concentration (between 0 and 1 M) and pH (between 3 and 11)] and was not observed in solution mixed with ethanol, which disrupts the three-dimensional network of the water molecules. We therefore concluded that the repulsion originated from structured interfacial water molecules. Considering the correlation between the above results, we propose that the layer of the structured interfacial water with a thickness of 2 to 3 nm (half of the range of the repulsion observed in the surface force measurements) plays an important role in deterring proteins and platelets from adsorption or adhesion.     

Mixed self-assembled monolayers (SAMs) consisting of methoxy-tri(ethylene glycol)-terminated and alkyl-terminated dimethylchlorosilanes control the non-specific adsorption of proteins at oxidic surfaces

Monolayers from the newly synthesized compound methoxy-tri(ethylene glycol)-undecenyldimethylchlorosilane (CH3O(CH2CH2O)3(CH2)11Si(CH3)2Cl, MeO(EG)3C11DMS) and dodecyldimethylchlorosilane (DDMS), both pure and mixed, were prepared by self-assembly from organic solution in the presence of an organic base. The films obtained were characterized by advancing and receding contact angle measurements and ellipsometry to confirm the formation of self-assembled monolayers (SAMs). The resulting data on the covalently attached dimethylsilanes were compared to known oligo(ethylene glycol) (OEG)-terminated SAM systems based on terminal alkenes, thiolates or trihydrolyzable silanes. The composition of the mixed SAMs was found to depend directly and linearly on the composition of the silanization solution. Enhanced protein repellent properties were found for the SAMs using a variety of proteins, including the Ras Binding Domain (RBD), a protein with high relevance for cancer diagnostics. Roughly a RBD protein monolayer amount was adsorbed to silicon oxide surfaces silanized with DDMS or non-silanized silicon wafers, and in contrast, no RBD was adsorbed to surfaces silanized with MeO(EG)3C11DMS or to mixed monolayers consisting of DDMS and MeO(EG)3C11DMS if the content of OEG-silane overcame a critical content of X(EG) approximately 0.9.     

Interfacial Tension Analysis of Oligo(ethylene glycol)-Terminated Self-Assembled Monolayers and Their Resistance to Bacterial Attachment

The fouling resistance of oligo(ethylene glycol) (OEG)-terminated self-assembled monolayers (SAMs) of alkanethiolates on gold has been well established. Although hydration of the OEG chains seems key to OEG-SAM resistance to macromolecular adsorption and cellular attachment, the details of how hydration prevents biofouling have been inferred largely through computational methods. Because OEG-SAMs of different lengths exhibit differing degrees of fouling resistance, the interactions between water and OEG-SAMs leading to fouling resistance can be deduced by comparing the properties of fouling and nonfouling OEG-SAMs. While all OEG-SAMs had similar water contact angles, contact angles taken with glycerol were able to individuate between different OEG-SAMs and between fouling and nonfouling OEG-SAMs. Subsequent estimation of surface and interfacial tension using a colloidal model showed that nonfouling surfaces are associated with an increased negative interfacial tension between those OEG-SAMs that resisted attachment and water. Further analysis of this interfacial tension experimentally confirmed current mathematical models that cite OEG-water hydrogen-bond formation as a driving force behind short-term fouling resistance. Finally, we found a correlation between solid-water interfacial tension and packing density and molecular density of ethylene glycol.     

Self-assembled monolayers of an oligo(ethylene oxide) disulfide and its corresponding thiol assembled from water: characterization and protein resistance

Self-assembled monolayers (SAMs) of the disulfide [S(CH2CH2O)6CH3]2 ([S(EO)6]2) on Au from 95% ethanol and from 100% water are described. Spectroscopic ellipsometry and reflection-absorption infrared spectroscopy indicate that the [S(EO)6]2 films are similar to the disordered films of HS(CH2CH2O)6CH3 ((EO)6) and HS(CH2)3O(CH2CH2O)5CH3 (C3EO5) at their protein adsorption minima. The [S(EO)6]2 SAMs exhibit constant film thickness (d) of 1.2 +/- 0.2 nm over long immersion times (up to 20 days) and do not attain the highly ordered, 7/2 helical structure of the (EO)6 and C3EO5 SAMs (d = 2.0 nm). Exposure of these self-limiting [S(EO)6]2 SAMs to bovine serum albumin show high resistance to protein adsorption.     

Designing highly specific biosensing surfaces using aptamer monolayers on gold

To build highly specific surfaces using aptamer affinity reagents, the effects of linker and coadsorbents were investigated for maximizing target binding and specificity for aptamer-based self-assembled monolayers (SAMs) supported on gold. An aptamer that binds the protein thrombin was utilized as a model system to compare different mixed monolayer systems toward maximizing binding and selectivity to the immobilized aptamer. Important factors used to optimize binding characteristics of thrombin to the aptamer-based monolayer films include changes in design elements of the linker and different coadsorbent thiols. Binding events measured by surface plasmon resonance (SPR) and ellipsometry showed that the binding performance of the aptamer SAMs depends principally on the linker and to a lesser extent on the coadsorbent. SAMs formed with HS-(CH2)6-OP(O)2O-(CH2CH2O)6-TTTTT-aptamer exhibited a 4-fold increase in binding capacity versus SAMs made using HS-(CH2)6-TTTTT-aptamer. Furthermore, SAMs made using HS-(CH2)6-OP(O)2O-(CH2CH2O)6-TTTTT-aptamer showed nearly complete specificity for thrombin versus bovine serum albumin (BSA, less than 2% bound), while a SAM incorporating a random DNA fragment (HS-(CH2)6-OP(O)2O-(CH2CH2O)6-TTTTT-RANDOM) showed little binding of thrombin. Irrespective of the aptamer-linker system, use of HS-(CH2)11(OCH2CH2)3OH, referred to as EG(3), as a coadsorbent enhanced binding of thrombin by approximately 2.5-fold compared to that of HS-(CH2)6-OH (mercaptohexanol, MCH).     

In-situ characterization of self-assembled monolayers of water-soluble oligo(ethylene oxide) compounds

In-situ spectroscopic ellipsometry (SE) was utilized to examine the formation of the self-assembled monolayers (SAMs) of the water-soluble oligo(ethylene oxide) [OEO] disulfide [S(CH(2)CH(2)O)(6)CH(3)](2) {[S(EO)(6)](2)} and two analogous thiols - HS(CH(2)CH(2)O)(6)CH(3) {(EO)(6)} and HS(CH(2))(3)O(CH(2)CH(2)O)(5)CH(3) {C(3)(EO)(5)} - on Au from aqueous solutions. Kinetic data for all compounds follow simple Langmuirian models with the disulfide reaching a self-limiting final state (d=1.2nm) more rapidly than the full coverage final states of the thiol analogs (d=2.0nm). The in-situ ellipsometric thicknesses of all compounds were found to be nearly identical to earlier ex-situ ellipsometric measurements suggesting similar surface coverages and structural models in air and under water. Exposure to bovine serum albumin (BSA) shows the self-limiting (d=1.2nm) [S(EO)(6)](2) SAMs to be the most highly protein resistant surfaces relative to bare Au and completely-formed SAMs of the two analogous thiols and octadecanethiol (ODT). When challenged with up to near physiological levels of BSA (2.5mg/mL), protein adsorption on the final state [S(EO)(6)](2) SAM was only 3% of that which adsorbed to the bare Au and ODT SAMs.     

Preparation, characterization, resistance to protein adsorption, and specific avidin-biotin binding of poly(amidoamine) dendrimers functionalized with oligo(ethylene glycol) on gold

Protein-resistant films derived from the fifth-generation poly(amidoamine) dendrimers (PAMAM G5) functionalized with oligo(ethylene glycol) (OEG) derivatives consisting of various ethylene glycol units (EG(n), n = 3, 4, and 6) were prepared on the self-assembled monolayers (SAMs) of 11-mercaptoundecanoic acid (MUA) on gold substrates. The resulting films were characterized by ellipsometry, contact angle goniometry, and X-ray photoelectron spectroscopy (XPS). About 35% of the peripheral amines of the dendrimers were reacted with N-hydroxysuccinimide-terminated EG(n) derivatives (NHS-EG(n)). The dendrimer films showed improved stability over octadecanethiolate SAMs on gold in hot solvents, attributed to the formation of multiple amide bonds per PAMAM unit with underlying NHS-activated MUA monolayer. The EG(n)-attached PAMAM surfaces with n = 3 reduced the adsorption of fibrinogen to approximately 20% monolayer, whereas 2-3% for n = 4 or 6. The dendrimer films with various densities of EG(n) molecules on PAMAM surfaces were prepared by immersion of the NHS-terminated MUA-functionalized gold substrates in ethanolic solutions containing PAMAM and NHS-EG(n) of various mole ratios. The density (r) of the EG(n) molecules on the PAMAM surfaces is consistent with the mole ratio (r') of NHS-EG(n)/free amine of PAMAM in solutions. The resistance to protein adsorption of the resulting surfaces is correlated with the surface density and the length of the EG chains. At their respective r, the EG(n)-modified dendrimer films resisted approximately 95% adsorption of fibrinogen on gold surfaces. Finally, the specific binding of avidin to the approximately 5% and approximately 40% biotinylated EG3 dendrimers (surface density of biotin with respect to the total number of terminal amino groups on PAMAM G5) gave rise to about 50% and 100% surface coverage by avidin, respectively.     

Synthesis and self-assembly of galactose-terminated alkanethiols and their ability to resist proteins

The synthesis of two galactose-terminated alkanethiols with the structural formula X-OC2H5NHCO(CH2)15SH (X = 2,3,4,6-tetra-O-methyl-beta-D-Gal or beta-D-Gal) is described. Single-component and mixed self-assembled monolayers (SAMs) of the methylated and nonmethylated compounds were prepared on gold and subsequently characterized with ellipsometry, contact angle goniometry, and infrared reflection-absorption spectroscopy. Studies of the irreversible protein adsorption onto the SAMs using ex-situ ellipsometry revealed very low levels of fibrinogen and lysozyme adsorption onto mixed SAMs displaying advancing water contact angles between 24 degrees and 45 degrees and below 45 degrees , respectively. A monomethylated compound (X = 6-O-methyl-beta-D-Gal) was also synthesized and assembled on gold. This particular compound was found to possess wettability properties corresponding to the low adsorption regime of the mixed SAMs, and the results from the same set of fibrinogen and lysozyme adsorption experiments showed very low levels of protein adsorption. Our findings suggest that the protein rejecting properties rely on a fine balance between the surface energy and/or hydrogen bond donating/accepting properties of the SAM surface.     

Strong resistance of a thin crystalline layer of balanced charged groups to protein adsorption

Resistance of mixed self-assembled monolayers (SAMs) with various counter-charged terminal groups of different valence and protonation/deprotonation states to nonspecific protein adsorption is investigated. It is demonstrated that excellent nonfouling surfaces can be readily constructed from mixed positively and negatively charged components of equal valence in a wide range of thiol solution compositions. Furthermore, the lattice structure of one of the mixed SAM systems studied is revealed by atomic force microscopy (AFM) to be (5.2 +/- 0.2 A x 5.2 +/- 0.2 A)60 degrees . Results indicate that the packing structure of mixed charged SAMs is determined by strong charge-charge interactions of the terminal groups rather than S-Au and chain-chain interactions. This work provides direct evidence that conformational flexibility is not required for protein resistance of a surface and even a single compact layer of charged groups of balanced charge with a crystalline structure can resist nonspecific protein adsorption, suggesting that tightly bound water molecules on the topmost part of the mixed SAMs play a dominant role in surface resistance to nonspecific protein adsorption.     

Platelet compatibility improvement by proper choice of acidic terminal functionality for mixed-charge self-assembled monolayers

In this study two different series of mixed-charge self-assembled monolayers (SAMs) prepared with -N(+)(CH(3))(3)-terminated alkanethiol and strong dissociated monovalent -SO(3)H acid-terminated or weaker dissociated divalent -PO(3)H(2) acid-terminated alkanethiol in pure ethanol were characterized. The influence of the acidity of the anionic functionality in the mixed-charge SAMs on the surface characteristics and platelet compatibility was investigated. X-ray photoelectron spectroscopy indicated that a nearly equivalent amount of countercharged terminal groups was noted on the surface of -SO(3)H/-N(+)(CH(3))(3) mixed SAMs, while "-N(+)(CH(3))(3) thiol poor" phenomena were found on -PO(3)H(2)/-N(+)(CH(3))(3) mixed SAMs instead. This was caused by the distinct differences in solvation capability between the acidic anionic functional groups and solvent molecules and/or the interactions among the terminal ends of the thiols. This acidity difference also affected other interfacial properties and the platelet compatibility. The mixed SAMs formed from the mixture of -SO(3)H- and -N(+)(CH(3))(3)-terminated thiols showed higher surface hydrophilicity and exhibited the least amount of platelets adhered, but these two mixed SAMs were all fairly negatively surface charged. The structure of the hydration layer near the surfaces was likely affected by the acidity of the anionic functionality, and this would cause such a distinct behavior in platelet compatibility. It was concluded that the hydrophilic surfaces with nearly equal amounts of surface positively and negatively charged components could exhibit better platelet compatibility. This work demonstrated that the nature of the acidic terminal ends of alkanethiol is also a key factor for preparing mixed-charge SAMs with good platelet compatibility.     

Improving the surface biocompatibility with the use of mixed zwitterionic self-assembled monolayers prepared by a proper solvent

In this study, the mixed self-assembled monolayers (SAMs) containing the mixture of long-chain alkanethiol, SH(CH(2))(11)NH(2) and SH(CH(2))(10)SO(3)H, was prepared as a model surface to examine the interaction between the biological environment and artificial surface. The 10% (v/v) NH(4)OH ethanolic solution and DMSO were chosen as the solvents for the preparation of these mixed SAMs and the "solvent effect" was discussed. X-ray photoelectron spectroscopy (XPS) has indicated that -SO(3)H/-NH(2) mixed SAMs formed from 10% (v/v) NH(4)OH ethanolic solution were surface "-SO(3)H poor", while a nearly equivalent amount of surface -SO(3)H functionality was presented on the mixed SAMs formed from DMSO. This has resulted from the different solvation capability between solvent molecules and the alkanethiol. Such solvent effects were also reflected in various surface properties such as surface wettability and surface zeta potential. The mixed SAMs formed from DMSO were more surface hydrophilic and less negatively surface charged than from 10% (v/v) NH(4)OH ethanolic solution. In addition, these mixed SAMs formed from DMSO exhibited the least amount of protein adsorbed as well as a better platelet compatibility than its counterpart from 10% (v/v) NH(4)OH ethanolic solution. These findings indicated that choosing a proper solvent for mixed zwitterionic SAM can greatly affect its surface properties and biocompatibility, such as to form a surface with near neutrality for reducing protein adsorption and subsequent platelet adhesion and activation.     

Chemical Force Microscopy Study of Adhesion and Friction between Surfaces Functionalized with Self-Assembled Monolayers and Immersed in Solvents

Adhesive and frictional forces between surfaces modified with self-assembled monolayers (SAMs) and immersed in solvents were measured with chemical force microscopy as functions of surface functionality and solvent. Si/SiO2 substrates were modified with SAMs of alkylsiloxanes (SiCl3(CH2)n-X), and gold-coated AFM tips were modified with SAMs of alkylthiolates (HS-(CH2)n-X). SAMs of alkylsiloxanes terminated in a methyl or oxidized vinyl group; SAMs of alkanethiolates terminated in a methyl or carboxyl group. Adhesive and frictional forces were measured in hexadecane, ethanol, 1,2-propanediol, 1,3-propanediol, and water. The work of adhesion (W) was calculated with the Johnson-Kendall-Roberts theory of adhesive contact. The JKR values agreed well with values derived from the Fowkes-van Oss-Chaudhury-Good surface tension model and from contact angle results. Calculated values of W for all combinations of contacting surfaces and solvents spanned two orders of magnitude. W correlated with the surface tension of the solvent for hydrophobic/hydrophobic interactions; hydrophilic/hydrophilic and hydrophobic/hydrophilic interactions were more complex. Friction forces were fit to a modified form of Amonton's law. For any solvent, friction coefficients were largest for the hydrophilic/hydrophilic contacting surfaces. The friction coefficient for any contacting pair was largest in hexadecane. In polar solvents, friction coefficients scaled with solvent polarity only for hydrophobic/hydrophobic contacting pairs. Copyright 1999 Academic Press.     

Versatility of aqueous micellar solutions for self-assembled monolayers engineering

Self-assembly of aliphatic as well as aromatic thiol-terminated molecules was achieved onto a variety of gold surfaces using aqueous micellar solutions. Scanning tunneling microscopy experiments allowed us to demonstrate that the increase in the density of self-assembled monolayers (SAMs) prepared from micellar aqueous solvent compared to that prepared from ethanol directly originates from the decrease in defect density in the SAM (etch pits, domain boundaries) and not from a denser local packing of the molecules. Extending the use of such an aqueous solvent to various conjugated molecules, we report for the first time the insertion of these molecules from an aqueous solution in a dodecanethiol (DT) SAM and the ligand-exchange on the surface of DT stabilized gold nanoparticles deposited as a Langmuir-Blodgett film. Finally, we show that aqueous micellar DT solutions allow the preparation of DT SAMs on gold through a micropatterned resist mask. These results make possible the use of water to deliver molecules on a solid substrate to build molecular devices in a way compatible with lithography requirements in microelectronic processes.     

Packing density of HS(CH2)(n)COOH self-assembled monolayers

Self-assembled monolayers (SAMs) of HS(CH(2))(n)COOH, n = 5, 10, 15 deposited from ethanol solution onto gold are prepared by five approaches, and their packing densities are evaluated by X-ray photoelectron spectroscopy (XPS) measurements. The five approaches are: (1) direct deposition; (2) acetic-acid-assisted deposition; (3) butyl-amine-assisted deposition; (4) displacement of a preformed HS(CH(2))(n)CH(3) (n = 5, 10, 15) SAMs; and (5) co-deposition with HS(CH(2))(n)CH(3) (n = 5, 10, 15). Packing density metrics are calculated from measurements of SAM and substrate photoemission intensities and their attenuations by two methods. In one case the attenuated photoemissions are expressed as a ratio relative to comparable measurements on an experimental HS(CH(2))(n)CH(3) model system. In the other case a new method is introduced where a calculated attenuation based on theoretical random coil and extended chain models is used as the reference to determine a packing density fraction. Packing densities are also correlated with the S2p(Au-bonded):Au4f peak area ratios and with shifts in the C1s binding energies. SAMs prepared by the direct deposition are a partial multilayer where a second molecular layer is physisorbed onto the SAM and not removable by solvent washing. The addition of acetic acid to the deposition solution disrupts dimer associations of HS(CH(2))(n)COOH in solution and at the surface of the monolayer and yields the most ordered monolayer with the highest density of -COOH groups. The addition of butyl amine results in a labile ammonium carbonate ion pair formation but results in a lower packing density in the SAM. The displacement of the preformed HS(CH(2))(n)CH(3) SAM and the co-deposition of HS(CH(2))(n)CH(3) with HS(CH(2))(n)COOH result in SAMs with little incorporation of the -COOH component.     

Systematic control of the packing density of self-assembled monolayers using bidentate and tridentate chelating alkanethiols

The structural and interfacial properties of self-assembled monolayers (SAMs) on gold derived from the adsorption of a series of 1,1,1-tris(mercaptomethyl)alkanes (i.e., CH3(CH2)mC[CH2SH]3, where m = 9, 11, 13, 15) were investigated. The new SAMs, which possess uniformly low densities of alkyl chains, were characterized by ellipsometry, contact angle goniometry, and polarization modulation infrared reflection absorption spectroscopy. Additional analysis of the SAMs by X-ray photoelectron spectroscopy permitted a direct calculation of the packing densities of the SAMs on gold. The results as a whole, when compared to those obtained on SAMs generated from normal alkanethiols (CH3(CH2)m+2SH), 2-alkylpropane-1,3-dithiols (CH3(CH2)mCH[CH2SH]2), and 2-alkyl-2-methylpropane-1,3-dithiols (CH3(CH2)mC(CH3)[CH2SH]2) having analogous chain lengths, demonstrate that the 1,1,1-tris(mercaptomethyl)alkanes afford SAMs with alkyl chains having the lowest packing density and least conformational order.     

Binary self-assembled monolayers of alkanethiols on gold: deposition from solution versus microcontact printing and the study of surface nanobubbles

The coadsorption of alkanethiols on noble metals has been recognized for a long time as a suitable means of affording surfaces with systematically varied wettability and other properties. In this article, we report on a comparative study of the composition of the mixed self-assembled monolayers (SAMs) obtained (i) by the coadsorption of octadecanethiol (ODT) and 16-mercaptohexadecanoic acid (MHDA) from ethanol and chloroform onto gold substrates and (ii) by microcontact printing using poly(dimethyl siloxane) (PDMS) stamps. SAMs prepared by coadsorption from solution showed a preferential adsorption of ODT for both solvents, but this trend was reversed in microcontact-printed SAMs when using chloroform as a solvent, as evidenced by contact angle and Fourier transform infrared (FTIR) spectroscopy measurements. An approximately linear relationship between the static contact angle and the degree of swelling with different solvents was observed, which suggests that the surface composition can be controlled by the interaction of the solvent and the PDMS elastomer. The altered preference is attributed to the different partitioning of the two thiols into solvent-swelled PDMS, as shown by (1)H NMR spectroscopy. Finally, molecularly mixed binary SAMs on ODT and MHDA on template-stripped gold were applied to study the effect of surface nanobubbles on wettability by atomic force microscopy (AFM). With a decreasing macroscopic contact angle measured through water, the nanoscopic contact angle was found to decrease as well.     

Reversible protein adsorption and bioadhesion on monolayers terminated with mixtures of oligo(ethylene glycol) and methyl groups

Surface-grafted, environmentally responsive polymers have shown great promise for controlling adsorption and desorption of macromolecules and cells on solid surfaces. In the paper, we demonstrate that certain mixed self-assembled monolayers (SAMs) of oligo(ethylene glycol) (OEG) and methyl-terminated alkanethiolates on gold form surfaces with switchable hydrophobicity and tendency for protein adsorption and cellular attachment. At temperatures above 32 degrees C, SAMs with a surface density of approximately 50% OEG adsorbed significant amounts of pyruvate kinase and lysozyme, whereas below this temperature, these same SAMs were resistant to the adsorption of these proteins. Furthermore, protein layers adsorbed to these SAMs above 32 degrees C were removed upon rinsing with water below this temperature. Similar results were seen for attachment and release of the marine bacterium, Cobetia marina. The change from nonresistance to adsorptive state of the SAMs was concomitant with a change in advancing water contact angle. Vibrational sum frequency generation spectroscopy suggests that the temperature-induced changes coincide with a disorder-to-partial order transition of the hydrated methylene chains of the OEG moieties within the SAMs. Mixed OEG-methyl SAMs represent both a convenient means of controlling macromolecular and cellular adsorption within the laboratory and a useful tool for relating adsorption properties to molecular structures within the SAMs.     

An in situ study of the adsorption behavior of functionalized particles on self-assembled monolayers via different chemical interactions

The formation of particle monolayers by convective assembly was studied in situ with three different kinds of particle-surface interactions: adsorption onto native surfaces, with additional electrostatic interactions, and with supramolecular host-guest interactions. In the first case carboxylate-functionalized polystyrene (PS-COOH) particles were assembled onto native silicon oxide surfaces, in the second PS-COOH onto protonated amino-functionalized (NH3+) self-assembled monolayers (SAMs), and in the third beta-CD-functionalized polystyrene (PS-CD) particles onto beta-CD SAMs with pre-adsorbed ferrocenyl-functionalized dendrimers. The adsorption and desorption behaviors of particles onto and from these surfaces were observed in situ on a horizontal deposition setup, and the packing density and order of the adsorbed particle lattices were compared. The desorption behavior of particles from surfaces was evaluated by reducing the temperature below the dew point, thus initiating water condensation. Particle lattices on native oxide surfaces formed the best hexagonal close packed (hcp) order and could be easily desorbed by reducing the temperature to below the dew point. The electrostatically modified assembly resulted in densely packed, but disordered particle lattices. The specificity and selectivity of the supramolecular assembly process were optimized by the use of ferrocenyl-functionalized dendrimers of low generation and by the introduction of competitive interaction by native beta-CD molecules during the assembly. The fine-tuned supramolecularly formed particle lattices were nearly hcp packed. Both electrostatically and supramolecularly formed lattices of particles were strongly attached to the surfaces and could not be removed by condensation.     

First-principle DFT and MP2 modeling of infrared reflection-absorption spectra of oriented helical ethylene glycol oligomers

First-principle modeling is used to obtain a comprehensive understanding of infrared reflection absorption (RA) spectra of helical oligo(ethylene glycol) (OEG) containing self-assembled monolayers (SAMs). Highly ordered SAMs of methyl-terminated 1-thiaoligo(ethylene glycols) [HS(CH2CH2O)(n)CH3, n = 5, 6] on gold recently became accessible for systematic infrared analyses [Vanderah et al., Langmuir, 2003, 19, 3752]. We utilized the quoted experimental data to validate the first-principle modeling of infrared RA spectra of HS(CH2CH2O)(5,6)CH3 obtained by (i) DFT methods with gradient corrections (using different basis sets, including 6-311++G) and (ii) HF method followed by a M?ller-Plesset (MP2) correlation energy correction. In focus are fundamental modes in the fingerprint and CH-stretching regions. The frequencies and relative intensities in the calculated spectra for a single molecule are unambiguously identified with the bands observed in the experimental RA spectra of the corresponding SAMs. In addition to confirming our earlier assignment of the dominating peak in the CH-stretching region to CH2 asymmetric stretching vibrations, all other spectral features observed in that region have received an interpretation consistent (but not in all cases coinciding) with previous investigations. The obtained results provide an improved understanding of the orientation and conformation of the molecular building blocks within OEG-containing assemblies, which, in our opinion, is crucial for being able to predict the folding and phase characteristics and interaction of OEG-SAMs with water and proteins.     

Gas-surface scattering dynamics of CO2, NO2, and O3 in collisions with model organic surfaces

High-energy (70 kJ/mol) molecular beams of CO(2), NO(2), and O(3) were scattered from long-chain methyl (CH(3)-), hydroxyl (OH-), and perfluoro (CF(3)(CF(2))(8)-, or F-) ω-functionalized alkanethiol self-assembled monolayers (SAMs) on gold to study the dynamics of energy exchange and thermal accommodation of atmospherically important triatomic molecules on model organic surfaces. Overall, the extent of energy transfer in gas collisions with all of the surfaces studied was substantial. Specifically, the triatomics scatter from each surface only after dissipating greater than 80% of their incident energy. Furthermore, although the OH-SAM is a more rigid surface, the extent of energy transfer and accommodation of these molecules to the CH(3)- and OH-SAMs were approximately the same. The similar scattering dynamics are likely due to significant gas-surface attractive forces between the triatomics and the OH terminal groups, which compensate for the rigidity of this monolayer. In contrast to the OH- and CH(3)-SAMs, the dominant pathway in collisions of the gases with the F-SAM was impulsive scattering. The portion of molecules that accommodated (<40%) to the F-SAM was about half of the amount that accommodated (～70%) to the CH(3)- and OH-SAMs. Although differences in the surface properties had a significant effect on the dynamics, variances in the chemical and physical properties of the three gases, CO(2), NO(2), and O(3), were found to have little effect on the extent of energy transfer and accommodation for collisions with any one surface.