Ferroelectric properties of Pr6O11-doped Bi4Ti3O12

Praseodymium doped Bi₄Ti₃O₁₂ (BIT) ceramics with composition Bi_2.9Pr_0.9Ti₃O₁₂ (BPT) were prepared by solid state reaction. These samples have polycrystalline Bi-layered perovskite structure without preferred orientation, and consist of well-developed plate-like grains with random orientation. Pr doping into BIT causes a large shift of the Curie temperature (T_C) of the BIT from 675 to 398 °C. At an electric field of 87 kV/cm, the remanent polarization and the coercive field of the BPT ceramics are 30 μC/cm² and 52 kV/cm, respectively. Furthermore, the dielectric permittivity and the dissipation factor of the BPT ceramics are 300 and 0.003 at 1 MHz, 1 V, and room temperature. Ferroelectric properties of the BPT ceramics are superior to V-doped Bi₄Ti₃O₁₂ (∼20 μC/cm² and 80 kV/cm) and (Sr, Ta)-doped Bi₄Ti₃O₁₂ (∼12 μC/cm² and 71 kV/cm) ceramics. In addition, the dense ceramics of praseodymium-doped B₄Ti₃O₁₂ were obtained by sintering at 1100 °C, about 100-200 °C lower than those of the SrBi₂Ta₂O₉ system.     

Low temperature fired Ni-Cu-Zn ferrite with Bi4Ti3O12

The Ni-Cu-Zn ferrites with different contents of Bi₄Ti₃O₁₂ ceramics (1-8 wt%) as sintering additives were prepared by the usual ceramic technology and sintered at 900 °C to adapt to the low temperature co-fired ceramic (LTCC) technology. The magnetic and dielectric properties of the ferrite can be effectively improved with the effect of an appropriate amount of Bi₄Ti₃O₁₂. For all samples, the ferrite sintered with 2 wt% Bi₄Ti₃O₁₂ has relatively high density (98.8%) and permeability, while the ferrite with 8 wt% Bi₄Ti₃O₁₂ has relatively good dielectric properties in a wide frequency range. The influences of Bi₄Ti₃O₁₂ addition on microstructure, magnetic and dielectric properties of the ferrite have been discussed.     

Infrared active phonon modes and ionicity of single crystal MgAl2O4

Near-normal incident infrared reflectivity spectra of （100） MgAl2O4 spinel single crystal have been measured at different temperatures in the frequency region between 50 and 6000 cm^-1. Eight infrared-active phonon modes are identified, which are fitted with the factorized form of the dielectric function. The dielectric property and optical conductivity of the MgAl2O4 crystal are analysed. From TO/LO splitting, the effective Szigeti charges and Born effective charges at different temperatures are calculated for studying the ionicity and the effect of polarization. Based on the relationship between the （LO-TO）1 splitting, which represents the transverse and longitudinal frequencies splitting of the highest energy phonon band in the reflectivity spectrum, and the ionic-covalent parameter, the four main phonon modes are assigned. MgA1204 can be considered as a pure ionic crystal and its optical characters do not change with decreasing temperature, so it may be used as a suitable substrate for high-Tc superconducting thin films.     

Lanthanum-doped Bi4Ti3O12 ceramics prepared by high-pressure technique

We present an effective way in this paper to increase the density of lanthanum doped bismuth titanate ceramics, Bi4-xLaxTi3O12 (BLT), thereby significantly improving the performance of the BLT ceramics. Dense BLT ceramicses, Bi4-xLaxTi3O12 (x = 0.25, 0.5, 0.75, 1.0), are prepared by using nanocrystalline powders fabricated by a-gel method and high-pressure technique. The microstructures of the BLT ceramicses prepared separately by conventional-pressure and high-pressure techniques are investigated by using x-ray diffraction and transmission electron microscope. The influence of La-doping on the densification of bismuth titanate ceramics is investigated. The experimental results indicate that the phase compositions of all samples with various lanthanum dopings sintered at 900°C possess layer-structure of Bi4Ti3O12 . The green compacts are pressed under 2.5 GPa, 3.0 GPa, 3.5 GPa and 4.0 GPa, separately. It is found that the density of BLT ceramics is significantly increased due to the decreasing of porosity in the green compacts by high-pressure process.     

Synthesis, structural and electrical properties of La and Nb modified Bi4Ti3O12 ferroelectric ceramics

Polycrystalline ceramic samples of Bi_4−xLa_xTi₃O₁₂ (x=0.0, 0.5 and 1) and Bi_3.5La_0.5Ti_3−yNb_yO₁₂ (y=0.02 and 0.04) have been synthesized by standard high temperature solid state reaction method using high purity oxides and carbonates. The effect of lanthanum doping on Bi-site and Nb doping on Ti-site on the structural and electrical properties of Bi₄Ti₃O₁₂ powders was investigated by X-ray diffraction, scanning electron microscopy, dc conductivity and dielectric studies. A better agreement between the observed and calculated X-ray diffraction pattern was obtained by performing the Rietveld refinement with a structural model using the non-centrosymmetric space group Fmmm in all the cases. A better agreement between observed and calculated d-values also shows that the lattice parameters calculated using the Rietveld refinement analysis are better. The increase in lanthanum and niobium contents does not lead to any secondary phases. It is found that La³⁺ doping reduces the material grain size and changes its morphology from the plate-like form to a spherical staking like form. The substitution of Nb for Ti ions affected the degree of disorder and modified the dielectric properties leading to more resistive ceramic compounds. The shape and size of the grains are strongly influenced by the addition of niobium to the system. The activation energies of all the compounds were calculated by measuring their dc electrical conductivities. The frequency and temperature dependent dielectric behavior of all the compounds have also been studied and the results are discussed in detail. The substitution of La and Nb on the Bi and Ti sites decreased the T_c and improved the dielectric and ferroelectric behavior.     

Underdamped soft mode in bismuth titanate (Bi4Ti3O12)

We have observed an underdamped soft mode in the Raman spectra of bismuth titanate. The soft mode decreases its frequency on approaching 200°C from both above and below, but the frequency does not drop to zero at this temperature. There seems to be additional quasi-elastic scattering near 200°C. Another phase transition could be expected in bismuth titanate.     

Temperature dependent Raman scattering in polycrystalline Bi4Ti3O12 thin films

Polycrystalline Bi₄Ti₃O₁₂ thin films were prepared on quartz substrates by pulsed laser deposition. The films were crystallized in the orthorhombic layer perovskite structure confirmed by X-ray diffraction and Raman spectroscopy. The Raman spectra are strongly dependent on temperature. A subtle phase transition in the temperature range 473-573 K exists in polycrystalline BTO thin films, which is evidenced by the disappearance of the Raman band at 116 cm⁻¹ and appearance of a new Raman band at 151 cm⁻¹. The two broad Raman bands centered at the 57 and 93 cm⁻¹ at 300 K break up into clusters of several sharp Raman peaks at 77 K, due to monoclinic distortion of orthorhombic structure at low temperature in the as-prepared Bi₄Ti₃O₁₂ thin films.     

SrBi2Ta2O9/Bi4Ti3O12复合铁电薄膜的制备与特性研究

采用溶胶凝胶工艺在p-Si衬底上制备了SrBi₂Ta₂O₉/Bi₄Ti₃O₁₂复合铁电薄膜. 研究了SrBi₂Ta₂O₉/Bi₄Ti₃O₁₂复合薄膜的微观结构与生长行为、铁电性能和疲劳特性. 研究表明: Si衬底Bi₄Ti< 关键词： 2Ta₂O₉')" href="#">SrBi₂Ta₂O₉ 4Ti₃O₁₂')" href="#">Bi₄Ti₃O₁₂ 复合铁电薄膜 溶胶凝胶工艺     

Preparation, characterization and oxide ion conductivity in U-substituted Bi4V2O11

A Bi₂V_{1 − x − y}U_xBi_yO_{5.5 + 0.5x − y} solid solution derived from Bi₄V₂O₁₁ has been prepared and characterized with x up to 0.125 for y = 0. Partial substitution of U⁶⁺ for V⁵⁺ in Bi₄V₂O₁₁ leads to the stabilization at room temperature of the high-oxide ion conducting γ-phase, in contrast with other M⁶⁺ dopants which stabilize the β-phase. The lower conductivity in U substituted system compared with BICUVOX.10 is attributed to its higher activation energy. Conductivity values and activation energies of the U substituted phases compare well with Bi₂UO₆.     

Ferroelectric and dielectric properties of La/Mn co-doped Bi4Ti3O12 ceramics

La/Mn co-doped Bi4Ti3O12 ceramics,Bi3.25La0.75Ti3-xMnxO12(x=0.02,0.04,0.06,0.08),were prepared by the solid-state reaction method.The influence of manganese substitution for the titanium part in Bi 3.25 La 0.75 Ti 3 O 12 on the sintering behaviour,microstructure,Raman spectra and electrical properties was investigated.The experimental results show that the phase composition of all samples with and without manganese doping,sintered at 1000 ℃,consists of a single phase with a bismuth-layered structure belonging to the crystalline phase Bi4Ti3O12.There is no evidence of any impurity phase,but a small change in crystallographic orientation is observed.The Curie temperature of Bi3.25La0.75Ti3-xMnxO12 ceramics is steadily shifted to lower temperature with increasing Mn-doping content.Moreover,the remnant polarisation(Pr) of Bi3.25La0.75Ti2.92Mn0.08O12 samples increases with Mn-doping content,and the Bi3.25La0.75Ti2.92Mn0.08O12 sample exhibits the largest P r of 16.6 μC/cm 2.     

Large memory window in the vanadium doped Bi4Ti3O12 thin films

We report the enhancement of ferroelectric properties in vanadium-doped Bi₄Ti₃O₁₂ (BIT) thin films prepared by rf magnetron sputtering method for MFM and MFIS structures. The optimal sputtering parameters of the as-deposited Bi_3.9Ti_2.9V_0.08O₁₂ (BTV) ferroelectric films for different depositing times were obtained. Compared to the undoped BIT, vanadium doped BIT (BTV) showed better physical and electrical characteristics. The as-deposited BTV showed a remanent polarization (2P _r ) of 23 μC/cm², higher than the value of 16 μC/cm² for BIT, as the measured frequency was 100 kHz. For BTV thin films in the MFIS structure, the leakage current density and the memory window decreased, the change ratio of capacitance critically increased as the depositing time increased from 30 to 120 min. Regarding the measured physical properties, the micro-structure and thickness of as-deposited undoped and vanadium doped BIT thin films were obtained and compared by XRD patterns and SEM images.     

Optical phonon modes and structure of ZnGa2Se4 and ZnGa2S4

We present the infrared and Raman study of the optical phonon modes of the defective compounds ZnGa₂Se₄ and ZnGa₂S₄. Most of the compounds have been found to crystallize in the thiogallate structure (defect chalcopyrite) with space group where all cations and vacancies are ordered. For some Zinc compounds a partially disordered cationic sublattice with various degrees of cation and vacancy statistical distribution, which lead to the higher symmetry (defect stannite), has been reported. For ZnGa₂Se₄ we have found three modes of A symmetry, showing Raman activity only. In addition, we have observed each five modes of B and E symmetry, showing infrared as well as Raman activity. The number of modes and their symmetry assignment, based on polarized measurements, clearly indicate space group for the investigated crystals of ZnGa₂Se₄.Regarding ZnGa₂S₄ we have found three modes exclusively showing Raman activity (2A⊕1B₁), and only eight modes showing infrared as well as Raman activity (3B₂⊕5E). The assignment of the modes has been derived by analyzing the spectral positions of the vibrational modes in comparison to a number of compounds. From the number and symmetry assignment of the optical phonon modes we confirm that ZnGa₂S₄ most likely crystallizes in space group .     

Electron energy-loss spectroscopy of LiMn2O4, LiMn1.6Ti0.4O4 and LiMn1.5Ni0.5O4

The dielectric properties of LiMn₂O₄, LiMn_1.6Ti_0.4O₄ and LiMn_1.5Ni_0.5O₄ powders, synthesized by sol-gel method, were determined by analyzing the low-loss region of the electron energy-loss spectroscopy (EELS) spectrum in a transmission electron microscope. From these data, the optical joint density of states (OJDS) was obtained by Kramers-Kronig analysis. Since maxima observed in the OJDS spectra are assigned to interband transitions above the Fermi level, these spectra can be interpreted on the basis of calculated density of states (DOS), carried out with the CASTEP code. Experimental and theoretical results are in good agreement.     

Reduced dielectric loss and leakage current in CaCu3Ti4O12/SiO2/CaCu3Ti4O12 multilayered films

The CaCu₃Ti₄O₁₂/SiO₂/CaCu₃Ti₄O₁₂ (CCTO/SiO₂/CCTO) multilayered films were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition method. It has been demonstrated that the dielectric loss and the leakage current density were significantly reduced with the increase of the SiO₂ layer thickness, accompanied with a decrease of the dielectric constant. The CCTO film with a 20 nm SiO₂ layer showed a dielectric loss of 0.065 at 100 kHz and the leakage current density of 6×10⁻⁷ A/cm² at 100 kV/cm, which were much lower than those of the single layer CCTO films. The improvement of the electric properties is ascribed to two reasons: one is the improved crystallinity; the other is the reduced free carriers in the multilayered films.     

Bi2Ti2O7/Si薄膜的制备及C-V特性研究

采用化学溶液分解法(CSD)在Si衬底上制备了Bi₂Ti₂O₇薄膜.X射线双晶衍射和原子力显微镜检测表明,所制备的薄膜主要为Bi₂Ti₂O₇相的多晶材料.同时还研究了AuBi₂Ti₂O₇/n-Si(100)结构的电容电压(C-V)特性,结果表明,在Bi₂Ti₂O关键词： C-V特性 2Ti₂O₇薄膜')" href="#">Bi₂Ti₂O₇薄膜 电荷迁移     

R型铁氧体BaFe4-xTi2+xO11的化学组态以及磁性行为的研究

本文通过传统的固相反应法制备了R型六角铁氧体BaFe_4-xTi_2+xO₁₁ (x= 0, 0.25, 0.5, 0.75, 1), 并且对它的原子价态以及磁性行为进行了研究. X 射线光电子能谱(XPS)结果显示了随着掺杂含量的增加, 体系中Fe³⁺离子逐渐减少而Fe²⁺离子逐渐增加. 由于具有非对称结构的阻挫晶格中存在各种关联作用的竞争, 使得BaFe_4-xTi_2+xO₁₁体系表现出了复杂的磁有序行为, 在T₁～250 K和T₂～83 K两处存在磁转变. 对这一系列掺杂样品, 在相变温度T₁之上表现顺磁行为, 而在相变温度T₂前后的磁化强度都表现出低场下随磁场的增加快速增加, 高场下则线性变化且在5×10⁴ Oe时还未达到饱和的行为, 表明这一系列掺杂样品是典型的倾斜反铁磁态(canted antiferromagnetic) 或者亚铁磁态.     

Ag/Bi4Ti3O12栅n沟道铁电场效应晶体管制备及存储特性

在溶胶-凝胶工艺获得高质量Bi₄Ti₃O₁₂薄膜的基础上 ，制备了Ag/Bi₄Ti₃O₁₂栅n沟道铁电场效应晶体管. 研 究了Si基Bi₄Ti₃O₁₂薄膜的生长特性及其对铁电薄膜/ 硅的界面状态和铁电场效应晶体管存储特性的影响. 研究表明，在合理的工艺条件下可以获 得具有较高c-轴择优取向的纯钙钛矿相Si基Bi₄Ti₃O₁₂ 铁电薄膜并有利于改善Bi₄Ti₃O₁₂/Si之间的界面特性; 顺时针回滞的C-V特性曲线和C-T曲线表明Ag/Bi₄Ti₃O_{12栅n沟道铁电场效应晶体管具有极化存储效应和一定的极化电荷保持能力; 器件的转移(I< sub>sd}-V_G)特性曲线显示Ag/Bi₄Ti₃O_{12栅n沟道铁电场效应晶体管具有明显的栅极化调制效应. 关键词： 铁电场效应晶体管 4}Ti₃O₁₂')" href="#">Bi₄Ti₃O₁₂ 存储 特性 溶胶-凝胶工艺     

Combinatorial exploration of flux material for Bi4Ti3O12 single crystal film growth

The combinatorial approach to materials synthesis was employed for the quick screening of a flux material for liquid phase-mediated epitaxy of Bi₄Ti₃O₁₂ single crystal film. A series of ternary flux libraries composed of two self-fluxes (Bi₂O₃ and Bi₄Ti₃O₁₂) and an impurity flux (VO_x, WO_x, CuO_x, BiPO_x, BaO, MoO_x) were fabricated on the SrTiO₃ (0 0 1) substrates. Then, stoichiometric Bi₄Ti₃O₁₂ was grown on each one of these flux libraries at a temperature presumed to melt the flux. High-throughput characterization with the concurrent X-ray diffraction (XRD) method resulted in the discovery of a novel flux material, CuO, containing Bi₂O₃, for Bi₄Ti₃O₁₂ single crystal film.     

La掺杂对Bi4Ti3O12薄膜铁电性能的影响

利用Sol-Gel法在Pt/Ti/SiO₂/Si衬底上制备出Bi₄Ti₃O₁₂和Bi_3.25La_0.75Ti₃O₁₂薄膜，研究了La掺杂对Bi₄Ti₃O₁₂薄膜的晶体结构、铁电性能和疲劳特性的影响，发现La掺杂没有改变Bi₄Ti₃O₁₂薄膜的基本晶体结构，并且提高了Bi₄Ti₃O₁₂铁电薄膜的剩余极化值和抗疲劳性能，对La掺杂改善Bi₄Ti₃O₁₂铁电薄膜性能的机理进行了讨论. 关键词： 铁电性能 4Ti₃O₁₂薄膜')" href="#">Bi₄Ti₃O₁₂薄膜 3.25La_0.75Ti₃O₁₂薄膜')" href="#">Bi_3.25La_0.75Ti₃O₁₂薄膜 sol-gel法 La掺杂     

Polymorphism in Bi2Sn2O7

Single crystals of Bi₂Sn₂O₇ were grown in a Bi₂O₃ flux. Phase transitions were identified at about 90 and 680° using X-ray, SHG, DSC, dielectric, and optical data. γ-Bi₂Sn₂O₇, which exists above 680°C is centric and cubic with a = 10.73 Å at 700°, and it probably has the ideal pyrochlore structure. β-Bi₂Sn₂O₇, which exists between 680° and about 90°C, is acentric but remains cubic with a = 21.40 Å. α-Bi₂Sn₂O₇, which exists from about 90°C to below room temperature, is acentric and noncubic, probably tetragonal with a = 21.328 and c = 21.545 Å. The α-β transition is first order, and the β-γ transition appears to be second order. Substitutions of Pb²⁺ or Cd²⁺ for Bi³⁺ and of Ga³⁺, Rh³⁺ Sc³⁺, In³⁺, Sb⁵⁺ Nb⁵⁺ or Ta⁵⁺ for Sn⁴⁺ lower the α-β transition temperature.