Synthesis and characterization of random copolymers of (2,2-dimethyl-1,3-dioxolan-4-yl)methyl methacrylate and 2,3-dihydroxypropyl methacrylate

Poly[(2,2-dimethyl-1,3-dioxolan-4-yl)methyl methacrylate)] [poly(solketal methacrylate) (PSMA)] was synthesized by free radical polymerization. By partial hydrolysis of the acetal group, random copolymers of SMA with 2,3-dihydroxypropyl methacrylate (DHPMA) were synthesized whereas complete cleavage lead to poly(2,3-dihydroxypropyl methacrylate) (PDHPMA). The copolymer composition was determined by ¹H NMR spectroscopy. FTIR spectroscopy indicates the synthesis of random copolymers with different degrees of hydrogen bonding as measured by a shift of the OH vibration bands. The glass transition temperature of the random copolymers increases linearly with increasing DHPMA content, resulting in a positive deviation from the Fox equation. The thermal degradation of both homopolymers and their random copolymers has been studied. Finally, the solution behaviour of the copolymers and PDHPMA in water studied by dynamic light scattering showed a strong tendency of the polymer chains to form clusters in the size range of 15-62 nm. The size and the kind of associating interactions within the clusters strongly depend on the copolymer composition.     

Characterization and optimization of poly(glycidyl methacrylate-co-styrene) synthesized by atom transfer radical polymerization

Styrene (S) and glycidyl methacrylate (GMA) copolymers were synthesized by atom transfer radical polymerization (ATRP) under different conditions. The effect of initiators, ligands, solvents, and temperature to the linear first-order kinetics and polydispersity index (PDI) was investigated for bulk polymerization. First-order kinetics was observed between linearly increasing molecular weight versus conversion and low polydispersities (PDI) were achieved for ethyl 2-bromo isobutyrate (EBiB) as an initiator and N,N′,N′,N″,N″-pentamethyldiethylenetriamine (PMDETA)/CuBr as a catalyst. The copolymers with different compositions were synthesized using different in-feed ratios of monomers. Copolymers composition was calculated from ¹H NMR spectra which were further confirmed by quantitative ¹³C{¹H} NMR spectra. The monomer reactivity ratios were obtained with the help of Mayo-Lewis equation using genetic algorithm method. The values of reactivity ratios for glycidyl methacrylate and styrene monomers are r_G = 0.73 and r_S = 0.42, respectively.     

Homopolymer and copolymers of 4-nitro-3-methylphenyl methacrylate with glycidyl methacrylate: Synthesis, characterization, monomer reactivity ratios and thermal properties

The novel methacrylic monomer, 4-nitro-3-methylphenyl methacrylate (NMPM) was synthesized by reacting 4-nitro-3-methylphenol dissolved in ethyl methyl ketone (EMK) with methacryloyl chloride in the presence of triethylamine as a catalyst. The homopolymer and copolymers of NMPM with glycidyl methacrylate having different compositions were synthesized by free radical polymerization in EMK solution at 70 ± 1 °C using benzoyl peroxide as free radical initiator. The homopolymer and the copolymers were characterized by FT-IR, ¹H NMR and ¹³C NMR spectroscopic techniques. The solubility tests were tested in various polar and non-polar solvents. The molecular weight and polydispersity indices of the copolymers were determined using gel permeation chromatography. The glass transition temperature of the copolymers increases with increase in NMPM content. The thermogravimetric analysis of the polymers performed in air showed that the thermal stability of the copolymer increases with NMPM content. The copolymer composition was determined using ¹H NMR spectra. The monomer reactivity ratios were determined by the application of conventional linearization methods such Fineman-Ross (r₁ = 1.862, r₂ = 0.881), Kelen-Tudos (r₁ = 1.712, r₂ = 0.893) and extended Kelen-Tudos methods (r₁ = 1.889, r₂ = 0.884).     

Synthesis and characterization of syndiotactic polystyrene-graft-poly(glycidyl methacrylate) copolymer by atom transfer radical polymerization

Syndiotactic polystyrene-graft-poly(glycidyl methacrylate) (sPS-graft-PGMA) copolymer was synthesized by a heterogenous atom transfer radical polymerization (ATRP) using 2-bromo-2-methylpropanoyl bromide modified syndiotactic polystyrene (BMPsPS) as macroinitiator and copper bromide combined with 2,2′-bipyridine as catalyst in anisole at room temperature. The macroinitiator with 7.0 mol% bromine content was prepared from Friedel-Crafts acylation reaction of sPS with 2-bromo-2-methylpropanoyl bromide in a heterogeneous process. It was found that BMsPS macroinitiator was well swelled in the mixture of anisole and GMA, the equilibrium swelling degree could reach 370%. The resultant polymer was characterized by FTIR and NMR spectroscopies. In addition, the thermal properties of the graft copolymers were also investigated with differential scanning calorimetry (DSC).     

A successive route to amphiphilic graft copolymers with a hydrophilic poly(3‐hydroxypropyl methacrylate) backbone and hydrophobic polystyrene side chains

A successive method for preparing novel amphiphilic graft copolymers with a hydrophilic backbone and hydrophobic side chains was developed. An anionic copolymerization of two bifunctional monomers, namely, allyl methacrylate (AMA) and a small amount of glycidyl methacrylate (GMA), was carried out in tetrahydrofuran (THF) with 1,1‐diphenylhexyllithium (DPHL) as the initiator in the presence of LiCl ([LiCl]/[DPHL]₀ = 2), at −50 °C. The copolymer poly(AMA‐co‐GMA) thus obtained possessed a controlled molecular weight and a narrow molecular weight distribution (M_w /M_n = 1.08–1.17). Without termination and polymer separation, a coupling reaction between the epoxy groups of this copolymer and anionic living polystyrene [poly(St)] at −40 °C generated a graft copolymer with a poly(AMA‐co‐GMA) backbone and poly(St) side chains. This graft copolymer was free of its precursors, and its molecular weight as well as its composition could be well controlled. To the completed coupling reaction solution, a THF solution of 9‐borabicyclo[3.3.1]nonane was added, and this was followed by the addition of sodium hydroxide and hydrogen peroxide. This hydroboration changed the AMA units of the backbone to 3‐hydroxypropyl methacrylate, and an amphiphilic graft copolymer with a hydrophilic poly(3‐hydroxypropyl methacrylate) backbone and hydrophobic poly(St) side chains was obtained. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1195–1202, 2000     

Novel photocurable polyethers with methacrylate pendant groups

A method for preparation of novel fast photocurable polyethers is described. Thus, novel polyether, poly(3-methacryloxy propylene oxide) was obtained in low molecular weights (M_n: 1700 Da) by cationic ring opening polymerization of the epoxy group of glycidyl methacrylate (GMA) in presence of trimethylsilyl trifilate (TMSTF) as initiator. Copolymerization of the monomer with cyclohexene oxide (CHO) in the same reaction conditions yielded copolyethers with methacylate pendant groups. A series of copolymers with various GMA contents (10-100% mol/mol) were prepared using CHO as diluting comonomer. ¹H NMR spectra showed that oxirane function of GMA is somewhat less reactive than CHO. Having methacylate pendant groups the resulting waxy polymers underwent rapid photocrosslinking to give glassy hard materials upon UV irradiation at 350 nm, in the presence of benzoin as photoinitiator. Photocuring abilities of the copolymers were investigated by real time FT-IR using in dimethoxyethane solutions (14.7% w/w). The results showed that, 60% double bonds disappear within 150-300 s by irradiation of diluted copolymer solutions with Xenon lamp (150 W).     

One-pot, novel chemical modification of glycidyl methacrylate copolymers with very bulky organosilicon side chain substituents

Glycidyl methacrylate (GM) random copolymers with styrene and methylstyrene (in a 1:1 and 1:3 mole ratio) were synthesized by solution free radical polymerizations at 70 ± 1 °C using α,α′-azoisobutyronitrile as an initiator. The copolymer compositions were obtained using related ¹H NMR spectra and the polydispersity indices of the copolymers determined using gel permeation chromatography (GPC). Both types of polymer could be modified by incorporation of the highly sterically demanding tris(trimethylsilyl)methyl substituent (Me₃Si)₃C-(Tsi = trisyl) through the ring opening reaction of the epoxy groups in copolymers. Chemical modification was determined by ¹H NMR and infrared spectroscopies. The glass transition temperature T_g of all copolymers was determined by differential scanning calorimetry (DSC). The T_g value of the copolymers containing bulky trisyl groups was found to increase with incorporation of trisyl groups in polymer structures. The presence of trisyl groups in the polymer side chain created new macromolecules with novel modified properties and potential use as membranes for fluid separation.     

Preparation of poly(methyl methacrylate) microcapsules by in situ polymerization on the surface of calcium carbonate particles

Poly(methyl methacrylate) (PMMA) microcapsules were prepared by the in situ polymerization of methyl methacrylate (MMA) and N,N′-methylenebisacrylamide on the surface of calcium carbonate (CaCO₃) particles, followed by the dissolution of the CaCO₃ core in ethylenediaminetetraacetic acid solution. The microcapsules were characterized using fluorescence microscopy, atomic force microscopy, scanning electron microscopy, and Fourier transform infrared spectroscopy. The average sizes of the CaCO₃ particles and PMMA capsules were 3.8 ± 0.6 and 4.0 ± 0.6 μm, respectively. A copolymer consisting of MMA and rhodamine B-bearing MMA was also used to prepare microcapsules for fluorescent microscopy observations. Fluorescein isothiocyanate-labeled bovine serum albumin was enclosed in the PMMA microcapsules and its release properties were studied.     

Ambient temperature ATRP of benzyl methacrylate as a tool for the synthesis of block copolymers with styrene

The rapid atom transfer radical polymerization (ATRP) of benzyl methacrylate (BnMA) at ambient temperature was used to synthesize block copolymers with styrene as the second monomer. Various block copolymers such as AB diblock, BAB symmetric and asymmetric triblock, and ABABA pentablock copolymers were synthesized in which the polymerization of one of the blocks namely BnMA was performed at ambient temperature. It is demonstrated that the block copolymerization can be performed in a controlled manner, regardless of the sequence of monomer addition via halogen exchange technique. Using this reaction condition, the composition (ratio) of one block (here BnMA) can be varied from 1 to 100. It is further demonstrated that in the multiblock copolymer syntheses involving styrene and benzyl methacrylate, it is better to start from the PS macroinitiator compared with PBnMA macroinitiator. The polymers synthesized are relatively narrow dispersed (<1.5). It is identified that the ATRP of BnMA is limited to certain molecular weights of the PS macroinitiator. Additionally, a preliminary report about the synthesis of the block copolymer of BnMA‐methyl methacrylate (MMA), both at ambient temperature, is demonstrated. Subsequent deprotection of the benzyl group using Pd/C? H₂ results in methacrylic acid (MAA)–methyl methacrylate (MAA–MMA) amphiphilic block copolymer. GPC, IR, and NMR are used to characterize the synthesized polymers. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2848–2861, 2006     

Preparation and proton conductivity of acid-doped 5-aminotetrazole functional poly(glycidyl methacrylate)

Proton conducting polymer membranes have become crucial due their applications in fuel cells as source of clean energy. In this work, we synthesized poly(glycidyl methacrylate) (PGMA) by conventional free radical polymerization of GMA using azobisisobutyronitrile (AIBN) as initiator. PGMA was modified with 5-aminotetrazole by ring opening of the epoxide group. The composition of the polymer was studied by elemental analysis (EA) and the structures were characterized by FT-IR and solid ¹³C NMR spectra. Thermogravimetry analysis (TG) and differential scanning calorimetry (DSC) were employed to examine the thermal stability and homogeneity of the materials, respectively. Polymers were doped with H₃PO₄ at several stoichometric ratios. The effect of doping on the proton conductivity was studied via impedance spectroscopy. Maximum proton conductivity of acid-doped PGMA-aminotetrazole was found to be 0.01 S/cm at 150 °C in the anhydrous state.     

Diblock copolymers based on allyl methacrylate: Synthesis,characterization, and chemical modification

Different diblock copolymers constituted by one segment of a monomer supporting a reactive functional group, like allyl methacrylate (AMA), were synthesized by atom transfer radical polymerization (ATRP). Bromo‐terminated polymers, like polystyrene (PS), poly(methyl methacrylate) (PMMA), and poly(butyl acrylate) (PBA) were employed as macroinitiators to form the other blocks. Copolymerizations were carried out using copper chloride with N,N,N′,N″,N″‐pentamethyldiethylenetriamine (PMDETA) as the catalyst system in benzonitrile solution at 70 °C. At the early stage, the ATRP copolymerizations yielded well‐defined linear block copolymers. However, with the polymerization progress a change in the macromolecular architecture takes place due to the secondary reactions caused by the allylic groups, passing to a branched and/or star‐shaped structure until finally yielding gel at monomer conversion around 40% or higher. The block copolymers were characterized by means of size exclusion chromatography (SEC), ¹H NMR spectroscopy, and differential scanning calorimetry (DSC). In addition, one of these copolymers, specifically P(BA‐b‐AMA), was satisfactorily modified through osmylation reaction to obtain the subsequent amphiphilic diblock copolymer of P(BA‐b‐DHPMA), where DHPMA is 2,3‐dihydroxypropyl methacrylate; demonstrating the feasibility of side‐chain modification of the functional obtained copolymers. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 3538–3549, 2007     

Synthesis and micelle formation of triblock copolymers of poly(methyl methacrylate)-b-poly(ethylene oxide)-b-poly(methyl methacrylate) in aqueous solution

Amphiphilic triblock copolymers of poly(methyl methacrylate)-b-poly(ethylene oxide)-b-poly(methyl methacrylate) (PMMA-b-PEO-b-PMMA) with well-defined structure were synthesized via atom transfer radical polymerization (ATRP) of methyl methacrylate (MMA) initiated by the PEO macroinitiator. The macroinitiator and triblock copolymer with different PMMA and/or PEO block lengths were characterized with ¹H and ¹³C NMR and gel permeation chromatography (GPC). The micelle formed by these triblock copolymers in aqueous solutions was detected by fluorescence excitation and emission spectra of pyrene probe. The critical micelle concentration (CMC) ranged from 0.0019 to 0.016 mg/mL and increased with increasing PMMA block length, while the PEO block length had less effect on the CMC. The partition constant K_v for pyrene in the micelle and in aqueous solution was about 10⁵. The triblock copolymer appeared to form the micelles with hydrophobic PMMA core and hydrophilic PEO loop chain corona. The hydrodynamic radius R_h,app of the micelle measured with dynamic light scattering (DLS) ranged from 17.3 to 24.0 nm and increased with increasing PEO block length to form thicker corona. The spherical shape of the micelle of the triblock copolymers was observed with an atomic force microscope (AFM). Increasing hydrophobic PMMA block length effectively promoted the micelle formation in aqueous solutions, but the micelles were stable even only with short PMMA blocks.     

Copolymerization of N‐vinylcaprolactam and glycidyl methacrylate: Reactivity ratio and composition control

Free‐radical copolymerizations of N‐vinylcaprolactam (VCL) and glycidyl methacrylate (GMA) were investigated to synthesize temperature‐responsive reactive copolymers with minimized compositional heterogeneity. The average copolymer composition was determined by Fourier transform infrared and nuclear magnetic resonance techniques. The reactivity ratios for VCL and GMA were found to be 0.0365 ± 0.0009 and 6.44 ± 0.36 by the Fineman–Ross method and 0.039 ± 0.006 and 6.75 ± 0.29 by the Kelen–Tudos method, respectively. When prepared by batch polymerization, VCL–GMA copolymers had a highly heterogeneous composition and fractions of different solubilities in water. The use of a gradual feeding technique, which included the sequential addition of more reactive GMA monomer into the reaction, yielded copolymers with much more homogeneous composition. The produced copolymers with 0.9 and 0.11 fractional GMA contents preserved their temperature‐responsive properties and precipitated from aqueous solutions when the temperature exceeded 31 °C. The GMA units in the VCL–GMA copolymers were capable of reacting with amino end‐functionalized poly(ethylene oxide) at room temperature to produce poly(N‐vinylcaprolactam)–poly(ethylene oxide) graft copolymers. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 183–191, 2006     

Synthesis of bis-allyloxy functionalized polystyrene and poly (methyl methacrylate) macromonomers using a new ATRP initiator

A new bis-allyloxy functionalized ATRP initiator, viz, 4,4-bis (4-(allyloxy) phenyl) pentyl-2-bromo-2-methylpropanoate was synthesized starting from commercially available 4,4-bis (4-hydroxyphenyl) pentanoic acid. Atom transfer radical polymerization of styrene in bulk and that of methyl methacrylate in anisole using CuBr/N,N,N′,N′,N″-pentamethyldiethylenetriamine system was carried out. The kinetic study of styrene polymerization showed controlled polymerization behavior. Bis-allyloxy functionalized well-defined polystyrene (M_n^GPC: 13,600–28,250, PDI: 1.07–1.09) and poly (methyl methacrylate) (M_n^GPC: 10,100–18,450, PDI: 1.23–1.34) macromonomers were obtained. The presence of allyloxy functionality was confirmed by ¹H NMR spectroscopy. The reactivity of allyloxy functionality was demonstrated by carrying out organic reactions such as addition of bromine and hydrosilylation on polystyrene macromonomer. Polystyrene macromonomer with bis-allyloxy functionality was transformed into bis-epoxy functionalized polystyrene macromonomer using 3-chloroperoxybenzoic acid.     

Synthesis and characterization of original 2-(dimethylamino)ethyl methacrylate/poly(ethyleneglycol) star-copolymers

Novel synthetic transfection vectors with linear triblock and star-shaped diblock copolymer architectures have been synthesized by atom transfer radical polymerization (ATRP). Based on 2-(dimethylamino)ethyl methacrylate (DMAEMA) and copolymerization with poly(ethyleneglycol) α-methoxy, ω-methacrylate (MAPEG), the synthesis was realized using CuBr ligated with 1,1,4,7,10,10-hexamethyltriethylenetetramine (HMTETA) as catalytic complex and either ethyl 2-bromoisobutyrate (EBⁱB) or bis(α-bromoisobutyryl) N-methyl diethanolamine (DEA) or tris(α-bromoisobutyryl) triethanolamine (TEA) as (multifunctional)initiator. The polymers were characterized by GPC and NMR. The solution properties of these homopolymers and palm-tree-like copolymers were investigated by viscometry either in pure water or in buffered aqueous solutions. Interestingly, all the synthesized polymers show polyelectrolyte effect in Millipore water (25 °C) and in Hepes (20 mM) buffer solution (pH 7.4, NaCl 155 mM, 25 °C). Fitting of these viscometric data according to either Fuoss or Fedors equation allows for calculating the intrinsic viscosity of the polymers. These results are compared with dynamic light scattering (DLS) experiments to determine absolute masses. Finally, DEA based palm-tree-like copolymer is investigated to AFM measurement and micelles were observed at pH 8.     

Synthesis and characterization of poly(methyl methacrylate)‐block‐poly(methylphenylsilane)‐ block‐poly(methyl methacrylate) by atom transfer radical polymerization

ABA block copolymers of methyl methacrylate and methylphenylsilane were synthesized with a methodology based on atom transfer radical polymerization (ATRP). The reaction of samples of α,ω‐dihalopoly(methylphenylsilane) with 2‐hydroxyethyl‐2‐methyl‐2‐bromoproprionate gave suitable macroinitiators for the ATRP of methyl methacrylate. The latter procedure was carried out at 95 °C in a xylene solution with CuBr and 2,2‐bipyridine as the initiating system. The rate of the polymerization was first‐order with respect to monomer conversion. The block copolymers were characterized with ¹H NMR and ¹³C NMR spectroscopy and size exclusion chromatography, and differential scanning calorimetry was used to obtain preliminary evidence of phase separation in the copolymer products. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 30–40, 2003     

Reactivity ratios in conventional and nickel-mediated radical copolymerization of methyl methacrylate and functionalized methacrylate monomers

Copolymerization of an excess of methyl methacrylate (MMA) relative to 2-hydroxyethyl methacrylate (HEMA) was carried out in toluene at 80 °C according to both conventional and controlled Ni-mediated radical polymerizations. Reactivity ratios were derived from the copolymerization kinetics using the Jaacks method for MMA and integrated conversion equation for HEMA (r_MMA = 0.62 ± 0.04; r_HEMA = 2.03 ± 0.74). Poly(ethylene glycol) α-methyl ether, ω-methacrylate (PEGMA, M_n = 475 g mol⁻¹) was substituted for HEMA in the copolymerization experiments and reactivity ratios were also determined (r_MMA = 0.75 ± 0.07; r_PEGMA ∼ 1.33). Both the functionalized comonomers were consumed more rapidly than MMA indicating the preferred formation of heterogeneous bottle-brush copolymer structures with bristles constituted by the hydrophilic (macro)monomers. Reactivity ratios for nickel-mediated living radical polymerization were comparable with those obtained by conventional free radical copolymerization. Interactions between functional monomers and the catalyst (NiBr₂(PPh₃)₂) were observed by ¹H NMR spectroscopy.     

Direct synthesis of amphiphilic block copolymers, consisting of poly(methyl methacrylate) and poly(sodium styrene sulfonate) blocks through atom transfer radical polymerization

Amphiphilic block copolymers of methyl methacrylate (MMA) and sodium styrene sulfonate (SSNa) were successfully synthesized via direct atom transfer radical polymerization (ATRP) of SSNa. First, poly(sodium styrene sulfonate) (PSSNa) or poly(methyl methacrylate) (PMMA) macroinitiators were prepared using proper ATRP systems for each case. In some cases, functional initiators, which allow further reactions, were used. The macroinitiators were characterized and further used to synthesize PSSNa/PMMA block copolymers, by using proper solvent combinations, such as N,N-dimethylformamide/water or methanol/water at appropriate volume ratios, in order to ensure solubility of the synthesized amphiphilic copolymers. The molecular weight of the copolymers was determined by gel permeation chromatography, using water as eluent. By using a combination of analytical techniques like ¹H NMR, FTIR and thermogravimetry, the chemical structure and the actual copolymer composition were determined. Since, the block copolymers were soluble in water, forming hydrophilic/hydrophobic domains in aqueous solution, their micellization behavior was further studied by pyrene fluorescence probing.     

The synthesis and solution behaviors of novel amphiphilic block copolymers based on d-galactopyranose and 2-(dimethylamino)ethyl methacrylate

A series of novel stimuli-responsive AB, ABA, and BAB type block copolymers based on 6-O-methacryloyl-1,2:3,4-di-O-isopropylidene-d-galactopyranose (MAIpGP:A block) and 2-(N,N-dimethylamino)ethyl methacrylate (DMAEMA: B block) were synthesized via ATRP techniques using ethyl 2-bromoisobutyrate (EBiB) as monofunctional ATRP initiator in the case of diblock copolymer and diethyl meso-2,5-dibromoadipate (DEDBA) as bifunctional ATRP initiator in the case of triblock copolymers. The PMAIpGP blocks of the AB, ABA, and BAB type linear block copolymers were converted to water soluble PMAGP blocks via deprotection process under mild acidic conditions. Both proton NMR and DLS studies demonstrated that block copolymers were temperature-sensitive, whereby the lower critical solution temperature (LCST) of polymers varied with the polymerization degrees of comonomers in the block copolymers. LCST was determined to be between ∼35 °C and 55 °C depending on the type and the comonomer compositions of the block copolymers. It was observed that an increase on the percentage of hydrophilic PMAGP block in block copolymer caused an increase on the LCST value as expected.     

新型聚乙烯醇系亲和吸附剂的制备及其在糖蛋白纯化中的应用 (I)基质合成

以醋酸乙烯酯（ＶＡＣ）和甲基丙烯酸缩水甘油酯（ＧＭＡ）为单体,甲基丙烯酸烯丙酯（ＡＭＡ）为交联剂,在致孔剂正庚烷／乙酸丁酯的存在下,悬浮聚合,制得了一系列大孔共聚物;醇解后得到一种新型聚乙烯醇系亲和层析基质。依据单体的Ｑ、ｅ值,计算了体系的竞聚率,讨论了不同交联度、ＧＭＡ含量、致孔剂用量及配比对基质孔结构和性能的影响。