TS分子筛的催化氧化性能研究5: 环己酮氨肟化反应

研究了自制的钛硅分子筛(TS-1)催化H~2O~2参与的环己酮氨肟化反应。结果表明,降低反应溶液中H~2O~2的浓度、增加NH~3用量有利于H~2O~2利用率、环己酮肟收率和选择性的提高,适宜的n(H~2O~2):n(酮)<1.0,n(NH~3):n(酮)>2.0。反应时间应控制在3.5h左右。对溶剂的研究显示,叔丁醇在溶剂中所占的体积对反应有较大的影响,在叔丁醇体积分数为0.2到0.8之间,实验获得了较好的结果。当n(NH~3):n(H~2O~2):n(酮)=2.0:1.0:1.0,叔丁醇体积分数为0.5,反应时间2.5h,反应温度353K时,H~2O~2利用率、环己酮肟收率和选择性分别达95%,94%和97%以上。并对空白实验结果和TS-1的重复性试验进行了讨论。     

TS分子筛的催化氧化性能研究5: 环己酮氨肟化反应

研究了自制的钛硅分子筛(TS-1)催化H~2O~2参与的环己酮氨肟化反应。结果表明,降低反应溶液中H~2O~2的浓度、增加NH~3用量有利于H~2O~2利用率、环己酮肟收率和选择性的提高,适宜的n(H~2O~2):n(酮)<1.0,n(NH~3):n(酮)>2.0。反应时间应控制在3.5h左右。对溶剂的研究显示,叔丁醇在溶剂中所占的体积对反应有较大的影响,在叔丁醇体积分数为0.2到0.8之间,实验获得了较好的结果。当n(NH~3):n(H~2O~2):n(酮)=2.0:1.0:1.0,叔丁醇体积分数为0.5,反应时间2.5h,反应温度353K时,H~2O~2利用率、环己酮肟收率和选择性分别达95%,94%和97%以上。并对空白实验结果和TS-1的重复性试验进行了讨论。     

离子液体热合成磷仲钨酸铯杂多酸盐催化环己醇制备环己酮

采用离子液体热合成法合成新型磷仲钨酸铯杂多酸盐Cs_3PW_(12)0_(40)’系列催化剂并对其物化性能进行了表征.同时以Cs_3PW_(12)0_(40)’-80(简称CsPW’-80)为催化剂, 30%H_2O_2为氧化剂,乙腈为溶剂,以氧化环己醇合成环己酮为催化剂性能测试反应进行催化性能评估.考察了合成催化剂溶剂离子液体占比、催化剂用量、氧化剂用量、反应温度以及反应时间对催化性能的影响.实验结果表明:在合成催化剂离子液体占比为80%、乙腈溶剂5 mL、氧化剂与反应物n(30%H_2O_2)/n(cyclohexanol)=4、反应温度70℃、反应时间8 h的最优条件下,环己醇转化率为100%,环己酮的选择性为98.46%,环己酮总收率达到98.46%.     

磷钨杂多酸类离子液体催化环戊烯选择性氧化制备戊二醛

以H_2O_2为氧化剂,将一系列磷钨杂多酸类离子液体用于催化环戊烯(CPE)选择性氧化制备戊二醛(GA)反应,筛选出催化活性最高的催化剂为[π-C_5H_5NC_(16)H_(33)]_3PW_4O_(16).分别探讨了溶剂种类、用量、催化剂用量、H_2O_2用量、反应温度和反应时间等因素对反应的影响.确定了优化的反应条件:5 mL乙酸乙酯,n(Cat.)∶n(H_2O_2)∶n(CPE)=0.03∶50∶33,35℃,18 h,环戊烯的转化率达100%,戊二醛的选择性达87%.催化剂[π-C_5H_5NC_(16)H_(33)]_3PW_4O_(16)循环使用7次后,戊二醛的选择性仍保持在80%以上.     

GoAggⅡ体系催化氧化环己烷为环己酮

研究了Gif体系成员之一GoAggⅡ体系催化氧化环己烷为环己酮的反应.考察了催化剂用量、氧化剂用量、溶剂配比、反应温度和反应时间等对产率的影响.最佳反应条件为:1 40 mmol,催化剂[NH4Fe(SO4)2]1mmol,氧化剂[30%H2O2]80 mmol,溶剂[y(吡啶):V(乙酸)=5.6:1.0]33 mL,于40℃反应16 h.在此条件下,收率达10.33%,n(环己酮):n(环己醇)=5.61.     

过渡金属改性的Pd/TS-1催化氢、氧直接合成H_2O_2的性能

利用等体积浸渍法制备了M-Pd/TS-1(M=Ce,La,Pt,Fe,Co,Ni,Cr,Mn,Zn,Cd,Cu)系列催化剂,并将制得的催化剂用于常压下氢、氧直接合成过氧化氢的反应。考察了M的类型及负载量对M-Pd/TS-1催化剂催化性能的影响。结果表明,M选Ce时,催化剂的性能最好。Ce的最佳掺入量,n_(Ce)/(n_(Ce)+n_(Pd))=0.5%。对Ce改性与未改性的催化剂进行了TEM及静态化学吸附分析,结果表明,掺入Ce可使Pd在TS-1分子筛表面的粒度及分散度得到改善。考察了n_(O_2)/n_(H_2)比,气体流量,反应时间等反应条件对H_2转化率、H_2O_2选择性及收率的影响。在相对优化的工艺条件下,即n_(O_2)/n_(H_2)=3,气体流量为25 mL·min~(-1),反应时间为3 h时,H_2O_2,的收率可达到25.7%,TOF值为18.7 mol·mol~(-1)·h~(-1),此时溶液中H_2O_2的质量百分数为0.8%。     

Al2O3-SiO2催化环己胺氧化制备环己酮肟

以Al2O3-SiO2为催化剂,用双氧水氧化环己胺制备了环己酮肟。考察了溶剂用量、催化剂用量、反应时间和反应温度等因素对催化性能的影响。结果表明,在溶剂乙腈与环己胺体积比为3∶1,催化剂质量分数31.0%,75℃反应5 h后的环己胺转化率为100%,环己酮肟选择性可达83.6%。并对环己胺催化氧化的反应机理作了初步的探讨。     

磷钨酸镧催化合成缩醛(酮)的研究

以磷钨酸镧为催化剂催化合成了苯甲醛乙二醇缩醛、苯甲醛1,2-丙二醇缩醛及环己酮乙二醇缩酮.较系统研究了反应物料配比、催化剂用量、反应时间、催化剂重复使用性能等因素对反应的影响.结果表明:在醛(酮)/二元醇(乙二醇、1,2-丙二醇)=1.0:1.5(mol/mol),催化剂用量为反应物料总质量的1.0%,环己烷为带水剂,在反应温度86～96℃条件下,反应时间2.0h,苯甲醛乙二醇缩醛收率为78.5%,苯甲醛1,2-丙二醇缩醛收率为76.1%,环己酮乙二醇缩酮收率为79.5%.     

干胶转化法合成条件及磷酸处理对TS-1分子筛性能的影响

以正硅酸乙酯(TEOS)、钛酸丁酯(TBOT)、四丙基氢氧化铵(TPAOH)分别作硅源、钛源及模板剂,用干胶转化法合成TS-1分子筛.考察了TEOS水解时的水硅比、水解温度、除醇条件、晶化时间及磷酸处理对TS-1分子筛性能的影响.采用XRD、SEM、IR、ICP及N2吸附等手段对样品进行表征,同时以环己酮氨肟化反应考察样品的催化活性.结果表明,使用少量的TPAOH(n(TPAOH)/n(SiO2)=0.15)即可得到性能较好的TS-1,而用磷酸对所得TS-1分子筛处理则能进一步改善TS-1分子筛的性能.当n(SiO2):n(TPAOH):n(H2O)=1:0.15:16时在20℃下水解TEOS,钛硅溶液能自行胶凝,将所得凝胶在75℃下除醇至失重率达65%左右,晶化6d得到TS-1分子筛,产品经磷酸改性后,环己酮转化率达到99.5%,环己酮肟选择性达到98.7%,催化活性与高TPAOH用量合成的TS-1接近,而TPAOH的用量大大降低.     

D-72磺酸树脂催化环己酮肟液相贝克曼重排制己内酰胺

在以二甲亚砜作溶剂,以D-72固体磺酸树脂为催化剂的两相体系中,实现了由环己酮肟液相贝克曼重排制备己内酰胺的反应.主要考察了环己酮肟在固体酸催化剂上的吸附热力学规律以及溶剂、反应温度、反应时间、催化剂用量以及催化剂的重复使用性等因素对重排反应的影响.结果表明,环己酮肟在磺酸树脂上的等温吸附过程符合Langmuir吸附模型,吸附等温线可用Langmuir等温方程和速率方程来描述.在二甲亚砜溶剂中,当反应温度在130℃,催化剂用量为0.5 g(催化剂:环己酮肟=1:2(质量比))的条件下反应6小时,环己酮肟的转化率高达100%,己内酰胺的选择性为86.2%,主要副产物为环己酮.该法对环境无害,反应条件温和,催化剂容易分离和可重复使用等优点.     

Dichroism of absorption and polarization of phosphorescence of molecules of the closed form of nitrobenzospirothiopyran

The spectral-polarization characteristics of absorption and phosphorescence of molecules of the initial form of nitro-substituted indolinospirobenzothiopyran were studied in oriented polyethylene films and in solutions with different polarity. An oscillator model of the electron transitions responsible for the formation of absorption and luminescence spectra was suggested. It was established that the principal differences in the spectral and photophysical properties of the compound studied and its oxygen-containing analog are associated with the fact that the electronegativity of the S atom is lower than that of the O atom. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 6, pp. 1143–1146, June, 1997.     

非那雄胺合成工艺改进

非那雄胺能抑制5α-还原酶的活性,明显降低二氢睾酮水平,是一种治疗良性前列腺增生的有效药品。该合成工艺以甾烯酮酸为原料,将其与氯化亚砜反应,无须分离即与叔丁胺反应得17β-酰胺化合物,再氧化开环,环合,氢化,脱氢合成了非那雄胺。经元素分析、IR、1HNMR、13CNMR、MS分析表征了其结构。该法无须使用昂贵的2,2-二吡啶二硫化物和剧毒药品苯亚硒酸酐,且以乙酸铵代替氨气,降低了对设备的要求和腐蚀,更适用于工业生产。     

Determination of heats of detonation and influence of components of composite explosives on heats of detonation of high explosives

The heats of detonation of 20 simple high explosives and explosive mixtures were determined by means of an adiabatic detonation calorimeter designed by the authors. The results indicated that the performance of the instrument was reliable and the experimental data were very accurate. For explosive mixtures, there was a linear accumulative relationship between the heats of detonation of the explosive mixture and its components. Accordingly, the heats of detonation of explosive mixtures could be calculated directly from the heats of detonation of simple explosives and the characteristic heats of other components. The experiments showed that the gold or brass shell of the cylindrical charge could be substituted by a thick-walled porcelain shell, which had the advantage of cheapness.

     

Synthesis of phenolic components of Grains of Paradise

Two vanilloids, (5E)-8-(4-hydroxy-3-methoxyphenyl)oct-5-en-4-one (1) and 4-[3-hydroxydecyl]-2-methoxyphenol (2), isolated from the dried seeds of Grains of Paradise (Aframomum melegueta), were synthesized; the latter compound was made as the S-enantiomer and the material derived from the seeds was found to be a 1:1.7 mixture of the R and S isomers. The synthetic route used should allow the preparation of analogs having extended alkyl chains and consequently different lipophilicity, and 3, a homolog of 2, was also prepared.     

Summary of development of the theory of stability of colloids and thin films

In this review, the research of the author in the field of colloidal systems is summarized. The factors influencing colloidal stability are systematized and analyzed. Examples are presented to illustrate the practical utilization of the theory of stability of colloids and thin films.This review was prepared on the basis of the works of the author, which were awarded the State Premium for 1991 in the field of science and technology, chemistry section.Institute of Physical Chemistry, Russian Academy of Sciences, 117915 Moscow. Translated from Izvestiya Akademii Nauk, Seriya Khimicheskaya, No. 8, pp. 1708–1717, August, 1992.     

Study of hydration of two cements of different strengths

Main hydration products of two cement pastes, i.e. CSH-gel, portlandite (P) (and specific surface S) were studied by static heating, and by SEM, TEM and XRD, as a function of cement strength (C-33 and C-43) hydration time (th) and subsequent hydration in water vapour.Total change in mass on hydration and air drying, M_o, increased with strength of cement paste and with hydration time. Content of water escaping at 110 to 220°C, defined as water bound with low energy, mainly interlayer and hydrate water, was independent on cement strength but its content increased with (th). Content of chemically bound (zeolitic) water in CSH-gel, escaping at 220-400°C, was slightly dependent on strength and increased with (th). It was possibly derived from the dehydroxylation of CSH-gel and AFm phase. Portlandite water, escaping at 400-500°C, was independent on cement strength and was higher on longer hydration. Large P crystals were formed in the weaker cement paste C-33. Smaller crystals were formed in C-43 but they increased with (th). Carbonate formated on contact with air (calcite, vaterite and aragonite), decomposed in cement at 600-700^oC. It was high in pastes C-33(1 month) and C-43(1 month), i.e. 5.7 and 3.3%, respectively; it was less than 1% after 6 hydration months (low sensitivity to carbonation) in agreement with the XRD study showing carbonates in the air dry paste (1month), and its absence on prolonged hydration (6 months) and on acetone treatment. Water vapour treatment of (6 months) pastes or wetting-drying increased this sensitivity.Nanosized P-crystals, detected by TEM, could contribute to the cement strength; carbonate was observed on the rims of gel clusters.This revised version was published online in November 2005 with corrections to the Cover Date.     

氯氧化镁生成热的研究

用氧化镁氯化镁水溶液制备了8水合氯氧化镁[nMg(OH)2·MgCl2·8H2O], 并测定了其在盐酸中的溶解热, 实验结果表明, 氯氧化镁溶解热与n值呈线性关系, 根据溶解热求出5Mg(OH)2·MgCl2·8H2O和3Mg(OH)2·MgCl2·8H2O的生成热分别为-7727.1和5888.1kJ·mol^1^-。     

Thermodynamics of the formation of oxosulfides of rare-earth elements

The enthalpies of solution of several oxosulfides of rare-earth elements and the high-temperature enthalpies of oxosulfides and oxosulfates of lanthanum and yttrium were measured using solution calorimetry and high-temperature microcalorimetry techniques. Standard enthalpies of formation and some thermodynamic properties of oxosulfides and oxosulfates were calculated. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 2 pp. 294–297, February, 1997.     

探究“铁的锈蚀条件”实验创新设计

设计了铁的锈蚀实验,说明了铁钉的处理方法,增加了温度、酸、碱的影响条件,实现了铁跟蒸馏水及空气中氧气快速反应而生锈,使实验在5 min左右就能够得到准确的结果。