Preparing nanometer scaled Tb-doped Y2O3 luminescent powders by the polyol method

Sub-micrometer Tb-doped Y₂O₃ luminescent powders were prepared from nitrate precursors using the polyol method. Just after precipitation, the powders consist of agglomerates with a spherical shape and a size ranging between 400 and 500 nm. Each agglomerate is composed of ultra-small crystallites (from 3 to 6 nm) of a bcc oxide phase whose luminescence presents original features in comparison with bulk materials. Powders were further calcinated at different temperatures and for annealing below 900 °C, highly crystalline samples with the classical green ⁵D₄→⁷F₅ luminescent transitions of Tb³⁺ ions are obtained. For optimized annealing temperatures, sintering between the agglomerates is avoided and a sub-micrometric powder with a narrow size distribution and a high luminescence is obtained.     

Synthesis of SiO2/Y2O3:Eu core-shell materials and hollow spheres

The SiO₂/Y₂O₃:Eu core-shell materials and hollow spheres were first synthesized by a template-mediated method. X-ray diffraction patterns indicated that the broadened diffraction peaks result from nanocrystals of Y₂O₃:Eu shells and hollow spheres. X-ray photoelectron spectra showed that the Y₂O₃:Eu shells are linked with silica cores by Si-O-Y chemical bond. SEM and TEM observations showed that the size of SiO₂/Y₂O₃:Eu core-shell structure is in the range of 140-180 nm, and the thickness of Y₂O₃:Eu hollow spherical shell is about 20-40 nm. The photoluminescence spectra of SiO₂/Y₂O₃:Eu core-shell materials and Y₂O₃:Eu hollow spheres have better red luminescent properties, and the broadened emission bands came from the size effects of nanocrystals composed of Y₂O₃:Eu shell.     

The formation and physicochemical characterization of Al2O3-doped manganese ferrites

Mn/Fe mixed oxide solids doped with Al₂O₃ (0.32-1.27 wt.%) were prepared by impregnation of manganese nitrate with finely powdered ferric oxide, then treated with different amounts of aluminum nitrate. The obtained samples were calcined in air at 700-1000 °C for 6 h. The specific surface area (S_BET) and the catalytic activity of pure and doped precalcined at 700-1000 °C have been measured by using N₂ adsorption isotherms and CO oxidation by O₂. The structure and the phase changes were characterized by DTA and XRD techniques. The obtained results revealed that Mn₂O₃ interacted readily with Fe₂O₃ to produce well-crystallized manganese ferrite (MnFe₂O₄) at temperatures of 800 °C and above. The degree of propagation of this reaction increased by Al₂O₃-doping and also by increasing the heating temperature. The treatment with 1.27 wt.% Al₂O₃ followed by heating at 1000 °C resulted in complete conversion of Mn/Fe oxides into the corresponding ferrite phase. The catalytic activity and S_BET of pure and doped solids were found to decrease, by increasing both the calcination temperature and the amount of Al₂O₃ added, due to the enhanced formation of MnFe₂O₄ phase which is less reactive than the free oxides (Mn₂O₃ and Fe₂O₃). The activation energy of formation (ΔE) of MnFe₂O₄ was determined for pure and doped solids. The promotion effect of aluminum in formation of MnFe₂O₄ was attributed to an effective increase in the mobility of reacting cations.     

Thermodynamic stability of Sr2CeO4

Thermochemistry of the reaction between SrCO₃ and SrCeO_3, represented as

SrCO₃(s) + SrCeO₃(s) = Sr₂CeO₄(s) + CO₂(g),     

High-pressure transitions in MgAl2O4 and a new high-pressure phase of Mg2Al2O5

Phase transitions in MgAl₂O₄ were examined at 21-27 GPa and 1400-2500 °C using a multianvil apparatus. A mixture of MgO and Al₂O₃ corundum that are high-pressure dissociation products of MgAl₂O₄ spinel combines into calcium-ferrite type MgAl₂O₄ at 26-27 GPa and 1400-2000 °C. At temperature above 2000 °C at pressure below 25.5 GPa, a mixture of Al₂O₃ corundum and a new phase with Mg₂Al₂O₅ composition is stable. The transition boundary between the two fields has a strongly negative pressure-temperature slope. Structure analysis and Rietveld refinement on the basis of the powder X-ray diffraction profile of the Mg₂Al₂O₅ phase indicated that the phase represented a new structure type with orthorhombic symmetry (Pbam), and the lattice parameters were determined as a=9.3710(6) Å, b=12.1952(6) Å, c=2.7916(2) Å, V=319.03(3) Å³, Z=4. The structure consists of edge-sharing and corner-sharing (Mg, Al)O₆ octahedra, and contains chains of edge-sharing octahedra running along the c-axis. A part of Mg atoms are accommodated in six-coordinated trigonal prism sites in tunnels surrounded by the chains of edge-sharing (Mg, Al)O₆ octahedra. The structure is related with that of ludwigite (Mg, Fe²⁺)₂(Fe³⁺, Al)(BO₃)O₂. The molar volume of the Mg₂Al₂O₅ phase is smaller by 0.18% than sum of molar volumes of 2MgO and Al₂O₃ corundum. High-pressure dissociation to the mixture of corundum-type phase and the phase with ludwigite-related structure has been found only in MgAl₂O₄ among various A²⁺B³⁺₂O₄ compounds.     

K2Mo4O13 phases prepared by hydrothermal synthesis

Hydrothermal synthesis in the K-Mo oxide system was investigated as a function of the pH of the reaction medium. Four compounds were formed, including two K₂Mo₄O₁₃ phases. One is a new low-temperature polymorph, which crystallizes in the orthorhombic, space group Pbca, with Z=8 and unit cell dimensions a=7.544(1) Å, b=15.394(2) Å, c=18.568(3) Å. The other is the known triclinic K₂Mo₄O₁₃, whose structure was re-determined from single crystal data; its cell parameters were determined as a=7.976(2) Å, b=8.345(2) Å, c=10.017(2) Å, α=107.104(3)°, β=102.885(3)°, γ=109.760(3)°, which are the standard settings of the crystal lattice. The orthorhombic phase converts endothermically into triclinic phase at ca. 730 K with a heat of transition of 8.31 kJ/mol.     

Structural and electrical properties of the 2Bi2O3·3ZrO2 system

Powder mixtures of α-Bi₂O₃ (bismite) and monoclinic m-ZrO₂ (baddeleyite) in the molar ratio 2:3 were mechanochemically and thermally treated with the goal to examine the phases, which may appear during such procedures. The prepared samples were characterized by X-ray powder diffraction, differential scanning calorimetry (DSC), electrical measurements, as well as scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The mechanochemical reaction leads to the gradual formation of a nanocrystalline phase, which resembles δ-Bi₂O₃, a high-temperature Bi₂O₃ polymorph. Isothermal sintering in air at a temperature of 820 °C for 24 h followed by quenching to room temperature yielded a mixture of ZrO₂-stabilized β-Bi₂O₃ and m-ZrO₂ phases, whereas in slowly cooled products, the complete separation of the initial α-Bi₂O₃ and m-ZrO₂ constituents was observed. The dielectric permittivity of the sintered samples significantly depended on the temperature. The sintered and quenched samples exhibited a hysteresis dependence of the dielectric shift, showing that the ZrO₂-doped β-Bi₂O₃ phase possess ferroelectric properties, which were detected for the first time. This fact, together with Rietveld refinement of the β-Bi₂O₃/m-ZrO₂ mixture based on neutron powder diffraction data showed that ZrO₂-doped β-Bi₂O₃ has a non-centrosymmetric structure with as the true space group. The ZrO₂ content in the doped β-Bi₂O₃ and the crystal chemical reasons for the stabilization of the β-Bi₂O₃ phase by the addition of m-ZrO₂ are discussed.     

XRD and Si MAS-NMR spectroscopy across the β-Lu2Si2O7-β-Y2Si2O7 solid solution

Samples in the system Lu_2−xY_xSi₂O₇ (0?x?2) have been synthesized following the sol-gel method and calcined to 1300 °C, a temperature at which the β-polymorph is known to be the stable phase for the end-members Lu₂Si₂O₇ and Y₂Si₂O₇. The XRD patterns of all the compositions studied are compatible with the structure of the β-polymorph. Unit cell parameters are calculated as a function of composition from XRD patterns. They show a linear change with increasing Y content, which indicates a solid solubility of β-Y₂Si₂O₇ in β-Lu₂Si₂O₇ at 1300 °C. ²⁹Si MAS NMR spectra of the different members of the system agree with the XRD results, showing a linear decrease of the ²⁹Si chemical shift with increasing Y content. Finally, a correlation reported in the literature to predict ²⁹Si chemical shifts in silicates is applied here to obtain the theoretical variation in ²⁹Si chemical shift values in the system Lu₂Si₂O₇-Y₂Si₂O₇ and the results compare favorably with the values obtained experimentally.     

Effect of sintering on the ionic conductivity of garnet-related structure Li5La3Nb2O12 and In- and K-doped Li5La3Nb2O12

Garnet-structure related metal oxides with the nominal chemical composition of Li₅La₃Nb₂O₁₂, In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ and K-substituted Li_5.5La_2.75K_0.25Nb₂O₁₂ were prepared by solid-state reactions at 900, 950, and 1000 °C using appropriate amounts of corresponding metal oxides, nitrates and carbonates. The powder XRD data reveal that the In- and K-doped compounds are isostructural with the parent compound Li₅La₃Nb₂O₁₂. The variation in the cubic lattice parameter was found to change with the size of the dopant ions, for example, substitution of larger In³⁺(r_CN6: 0.79 Å) for smaller Nb⁵⁺ (r_CN6: 0.64 Å) shows an increase in the lattice parameter from 12.8005(9) to 12.826(1) Å at 1000 °C. Samples prepared at higher temperatures (950, 1000 °C) show mainly bulk lithium ion conductivity in contrast to those synthesized at lower temperatures (900 °C). The activation energies for the ionic conductivities are comparable for all samples. Partial substitution of K⁺ for La³⁺ and In³⁺ for Nb⁵⁺ in Li₅La₃Nb₂O₁₂ exhibits slightly higher ionic conductivity than that of the parent compound over the investigated temperature regime 25-300 °C. Among the compounds investigated, the In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ exhibits the highest bulk lithium ion conductivity of 1.8×10⁻⁴ S/cm at 50 °C with an activation energy of 0.51 eV. The diffusivity (“component diffusion coefficient”) obtained from the AC conductivity and powder XRD data falls in the range 10⁻¹⁰-10⁻⁷ cm²/s over the temperature regime 50-200 °C, which is extraordinarily high and comparable with liquids. Substitution of Al, Co, and Ni for Nb in Li₅La₃Nb₂O₁₂ was found to be unsuccessful under the investigated conditions.     

Preparation and performances of nanosized Ta2O5 powder photocatalyst

Nanosized-Ta₂O₅ powder photocatalyst was successfully synthesized by using sol-gel method via TaCl₅ butanol solution as a precursor. Ta₂O₅ species can be formed under 500 °C via the decomposition of the precursor. The crystalline phase of Ta₂O₅ powder photocatalyst can be obtained after being calcined above 600 °C for 4 h. The crystal size and particle size of Ta₂O₅ powder photocatalyst was about 50 nm. A good photocatalytic performance for the degradation of gaseous formaldehyde was obtained for the nanosized-Ta₂O₅ powder. The Ta₂O₅ powder formed at 700 °C for 4 h and at 650 °C for 12 h showed the best performance. The calcination temperature and time play an important role in the crystallization and photocatalytical performance of nanosized-Ta₂O₅ powder.     

Preparation and characterization of mesoporous TiO2-CeO2 nanopowders respond to visible wavelength

Mesoporous TiO₂-CeO₂ nanopowders responding to visible wavelength were synthesized by using a surfactant assisted sol-gel technique. They were obtained using metal alkoxide precursors modified with acetylacetone (ACA) and laurylamine hydrochloride (LAHC) as surfactant. The samples were characterized by XRD, nitrogen adsorption isotherm, SEM, TEM, and selected area electron diffraction (SAED), respectively. The 95 mol% TiO₂-5 mol% CeO₂ system yielded single anatase phase, however, further addition of the CeO₂ formed cubic CeO₂ structure while anatase TiO₂ decreased. Additions of 5 and 10 mol% CeO₂ increased the surface area, but those of 25, 50, and 75 mol% CeO₂ did not affect it very much. By using this mixed metal oxides system, TiO₂ can be modified to respond to the visible wavelength. The mixed metal oxides had catalytic activity (evaluating the formation rate of I₃⁻) about 2-3 times higher than pure CeO₂, while nanosize anatase type TiO₂ materials had no catalytic activity under visible light. The catalytic activity was almost proportional to the specific surface area. The formation rate of I₃⁻ was much improved by changing the calcination temperature and calcination period. Highest catalytic activity in this study was obtained for the 50 mol% TiO₂-50 mol% CeO₂ nanopowders calcined at 250 °C for 24 h.     

Structural studies on a high-pressure polymorph of NaYSi2O6

High-pressure synthesis experiments in the system Na₂O-Y₂O₃-SiO₂ revealed the existence of a previously unknown polymorph of NaYSi₂O₆ or Na₃Y₃[Si₃O₉]₂ which was quenched from 3.0 GPa and 1000 °C. Structural investigations on this modification have been performed using single-crystal X-ray diffraction data collected at ambient conditions. Furthermore, unpolarized micro-Raman spectra have been obtained from single-crystal material. The high-P modification of NaYSi₂O₆ crystallizes in the centrosymmetric space group C2/c with 12 formula units per cell (a=8.2131(9) Å, b=10.3983(14) Å, c=17.6542(21) Å, β=100.804(9)°, V=1481.0(3) Å³, R(|F|)=0.033 for 1142 independent observed reflections) and belongs to the group of cyclo-silicates. Basic building units are isolated three-membered [Si₃O₉] rings located in layers parallel to (010). Within a single layer the rings are concentrated in strings parallel to [100]. The sequence of directedness of up (U) or down (D) pointing tetrahedra of a single ring is UUU or DDD, respectively. Stacking of the layers parallel to b results in the formation of a three-dimensional structure in which yttrium and sodium cations are incorporated for charge compensation. In more detail, four non-tetrahedral cation positions can be differentiated which are coordinated by 6 and 8 oxygen ligands. Refinements of the site occupancies did not reveal any indication for mixed Na-Y populations on these positions. Finally, several geometrical parameters of rings occurring in cyclo-trisilicate structures have been compiled and are discussed.     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

The mercury chromates Hg6Cr2O9 and Hg6Cr2O10—Preparation and crystal structures, and thermal behaviour of Hg6Cr2O9

The basic mercury(I) chromate(VI), Hg₆Cr₂O₉ (=2Hg₂CrO₄·Hg₂O), has been obtained under hydrothermal conditions (200 °C, 5 days) in the form of orange needles as a by-product from reacting elemental mercury and K₂Cr₂O₇. Hydrothermal treatment of microcrystalline Hg₆Cr₂O₉ in demineralised water at 200 °C for 3 days led to crystal growth of red crystals of the basic mercury(I, II) chromate(VI), Hg₆Cr₂O₁₀ (=2Hg₂CrO₄·2HgO). The crystal structures were solved and refined from single crystal X-ray data sets. Hg₆Cr₂O₉: space group P2₁2₁2₁, Z=4, a=7.3573(12), b=8.0336(13), , 3492 structure factors, 109 parameters, R[F²>2σ(F²)]=0.0371, wR(F² all)=0.0517; Hg₆Cr₂O₁₀: space group Pca2₁, Z=4, a=11.4745(15), b=9.4359(12), , 3249 structure factors, 114 parameters, R[F²>2σ(F²)]=0.0398, wR(F² all)=0.0625. Both crystal structures are made up of an intricate mercury-oxygen network, subdivided into single building blocks [O-Hg-Hg-O] for the mercurous compound, and [O-Hg-Hg-O] and [O-Hg-O] for the mixed-valent compound. Hg₆Cr₂O₉ contains three different Hg₂²⁺ dumbbells, whereas Hg₆Cr₂O₁₀ contains two different Hg₂²⁺ dumbbells and two Hg²⁺ cations. The Hg^I-Hg^I distances are characteristic and range between 2.5031(15) and 2.5286(9) Å. All Hg₂²⁺ groups exhibit an unsymmetrical oxygen environment. The oxygen coordination of the Hg²⁺ cations is nearly linear with two tightly bonded O atoms at distances around 2.07 Å. For both structures, the chromate(VI) anions reside in the vacancies of the Hg-O network and deviate only slightly from the ideal tetrahedral geometry with average Cr-O distances of ca. 1.66 Å. Upon heating at temperatures above 385 °C, Hg₆Cr₂O₉ decomposes in a four-step mechanism with Cr₂O₃ as the end-product at temperatures above 620 °C.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

Interactions of Ba2YCu3O6+y with the Gd3NbO7 buffer layer in coated conductors

A systematic study of the chemical interaction of Ba₂YCu₃O_6+y and Gd₃NbO₇ was conducted under two processing conditions: purified air (21% p_o2), and 100 Pa p_o2 (0.1% p_o2). Phases present along the pseudo-binary join Ba₂YCu₃O_6z and Gd₃NbO₇ were found to be in two five-phase volumes within the system. Three common phases that are present in all samples are (Y,Gd)₂Cu₂O₅, Ba(Y,Gd)₂CuO₅ and Cu₂O or CuO (depending on the processing conditions). The assemblies of phases can be categorized in three regions, with Ba₂YCu₃O_6+y: Gd₃NbO₇ ratios of (I)<5.5:4.5; (II)=5.5:4.5; and (III)>5.5:4.5. The lowest melting temperature of the system was determined to be ≈938 °C in air, and 850 °C at 100 Pa p_o2. Structure determinations of two selected phases, Ba₂(Gd_xY_1−x)NbO₆ (Fm3¯m, No. 225), and (Gd_xY_3−x)NbO₇ (C222₁, No. 20 and Ccmm, No. 63), were completed using the X-ray Rietveld refinement technique. Reference X-ray powder diffraction patterns for selected phases of Ba₂(Gd_xY_1−x)NbO₆ (x=0.2, 0.4, 0.6, and 0.8) and (Gd_xY_3−x)NbO₇ (x=0.6, 1.2, 1.8, 2.4 and 3) have been prepared for inclusion in the Powder Diffraction File (PDF).     

Preparation of a new pyrochlore-type compound Na0.32Bi1.68Ti2O6.46(OH)0.44 by hydrothermal reaction

A new pyrochlore-type Na_0.32Bi_1.68Ti₂O_6.46(OH)_0.44 with the cubic cell of a=10.339(5) Å was prepared by hydrothermal reaction using TiO₂ (anatase) and Bi₂O₃ in NaOH solution. This compound was obtained when the molar ratio of NaOH/TiO₂ was above 2 and the reaction temperature was above 240 °C. The TG-curve of as-prepared sample showed a mass loss of 0.8 mass% which was caused by release of OH group. This compound decomposed to a pyrochlore-type compound and a layered-type Na_0.5Bi_4.5Ti₄O₁₅ above 800 °C. The optical band gap of Na_0.32Bi_1.68Ti₂O_6.46(OH)_0.44 was estimated to be 2.5 eV.     

Hydrogen production from water decomposition by redox of Fe2O3 modified with single- or double-metal additives

Iron oxide modified with single- or double-metal additives (Cr, Ni, Zr, Ag, Mo, Mo-Cr, Mo-Ni, Mo-Zr and Mo-Ag), which can store and supply pure hydrogen by reduction of iron oxide with hydrogen and subsequent oxidation of reduced iron oxide with steam (Fe₃O₄ (initial Fe₂O₃)+4H₂↔3Fe+4H₂O), were prepared by impregnation. Effects of various metal additives in the samples on hydrogen production were investigated by the above-repeated redox. All the samples with Mo additive exhibited a better redox performance than those without Mo, and the Mo-Zr additive in iron oxide was the best effective one enhancing hydrogen production from water decomposition. For Fe₂O₃-Mo-Zr, the average H₂ production temperature could be significantly decreased to 276 °C, the average H₂ formation rate could be increased to 360.9-461.1 μmol min⁻¹ Fe-g⁻¹ at operating temperature of 300 °C and the average storage capacity was up to 4.73 wt% in four cycles, an amount close to the IEA target.     

A study on methanol steam reforming to CO2 and H2 over the La2CuO4 nanofiber catalyst

The La₂CuO₄ crystal nanofibers were prepared by using single-walled carbon nanotubes as templates under mild hydrothermal conditions. The steam reforming of methanol (SRM) to CO₂ and H₂ over such nanofiber catalysts was studied. At the low temperature of 150 °C and steam/methanol=1.3, methanol was completely (100%, 13.8 g/h g catalyst) converted to hydrogen and CO₂ without the generation of CO. Within the 60 h catalyst lifespan test, methanol conversion was maintained at 98.6% (13.6 g/h g catalyst) and with 100% CO₂ selectivity. In the meantime, for distinguishing the advantage of nanoscale catalyst, the La₂CuO₄ bulk powder was prepared and tested for the SRM reaction for comparison. Compared with the La₂CuO₄ nanofiber, the bulk powder La₂CuO₄ showed worse catalytic activity for the SRM reaction. The 100% conversion of methanol was achieved at the temperature of 400 °C, with the products being H₂ and CO₂ together with CO. The catalytic activity in terms of methanol conversion dropped to 88.7% (12.2 g/h g catalyst) in 60 h. The reduction temperature for nanofiber La₂CuO₄ was much lower than that for the La₂CuO₄ bulk powder. The nanofibers were of higher specific surface area (105.0 m²/g), metal copper area and copper dispersion. The in situ FTIR and EPR experiments were employed to study the catalysts and catalytic process. In the nanofiber catalyst, there were oxygen vacancies. H₂-reduction resulted in the generation of trapped electrons [e] on the vacancy sites. Over the nanofiber catalyst, the intermediate H₂CO/HCO was stable and was reformed to CO₂ and H₂ by steam rather than being decomposed directly to CO and H₂. Over the bulk counterpart, apart from the direct decomposition of H₂CO/HCO to CO and H₂, the intermediate H₂COO might go through two decomposition ways: H₂COO=CO+H₂O and H₂COO=CO₂+H₂.     

Preparation of COF2 using CO2 and F2 in the electrochemical cell with PbSnF4 as a solid electrolyte

Tetragonal PbSnF₄ was prepared by precipitation method with Pb(NO₃)₂ and SnF₂ aqueous solutions. The product was characterized using X-ray diffraction (XRD), X-ray fluorescence spectroscopy (XFS), and the other chemical analyses. Tetragonal PbSnF₄ exhibited the highest electric conductivity of 3.2 Sm⁻¹ at 473 K in air as a fluoride ion conductor. We have investigated the possibility of COF₂ formation using CO₂ and F₂ in an electrochemical cell with PbSnF₄ as a solid electrolyte. At same time, we tried to produce an electric power from an electrochemical cell. This CO₂/F₂ electrochemical cell was constructed with a tetragonal PbSnF₄ disk having Au electrodes. The electromotive force was about 0.9 V at room temperature for 0.1 MPa CO₂/(0.01 MPa F₂ + 0.09 MPa Ar). However, the short circuit current density was 0.24 A m⁻², which was quite small. This current density was so small that no fluorocarbon compound was detected after 3 h discharge using FT-IR.