In situ Raman spectroscopic monitoring of hydroxyapatite as human mesenchymal stem cells differentiate into osteoblasts

The differentiation of stem cells into specific cell types is playing an essential role in the development of stem cell therapy, tissue engineering, and regenerative medicine. In this research, Raman microspectroscopy was applied to monitor the development of hydroxyapatite [HA, Ca₅ (PO₄)₃ (OH)], which is associated with the differentiation of the human mesenchymal stem cells (hMSCs) into osteoblasts. Raman spectra exhibited dramatic changes in the HA region, 950–970 cm⁻¹, over the period of 7–21 days after the start of differentiation. This work demonstrates the successful application of Raman spectroscopy for monitoring and quantitatively evaluating hMSC differentiation into osteoblasts. Copyright © 2008 John Wiley & Sons, Ltd.     

Confocal Raman and electronic microscopy studies on the topotactic conversion of calcium carbonate from Pomacea lineate shells into hydroxyapatite bioceramic materials in phosphate media

Conversion of Pomacea lineate shells into hydroxyapatite (HA) bioceramic materials was investigated by their in vitro treatment with phosphate solutions, at room temperature. Confocal Raman microscopy revealed that the conversion proceeds at distinct rates through the nacreous or periostracum sides of the shell. The conversion can be accelerated using powdered samples, yielding biocompatible materials of great interest in biomedicine.     

Monodispersed Bioactive Glass Nanoparticles Enhance the Osteogenic Differentiation of Adipose‐Derived Stem Cells through Activating TGF‐Beta/Smad3 Signaling Pathway

It is important to understand the interaction mechanisms between nanomaterials and adipose‐derived stem cells for biomedical application. Nanoscale bioactive glass has positive effects on guiding osteoblasts differentiation and bone regeneration. However, the effects and molecular mechanism of monodispersed bioactive glass nanoparticles on the osteogenic differentiation of adipose‐derived stem cells are still not clear up to now. In this study, the effects and underlying molecular mechanism of monodispersed bioactive glass nanoparticles on the osteogenic differentiation of adipose‐derived stem cells are investigated in minute detail. The results show that nanoparticles (100–200 nm) can be absorbed by stem cells and is distributed in cytoplasm and nucleus. In both culture conditions (normal and osteoinductive), nanoparticles (80 µg mL⁻¹) can significantly enhance the osteogenic differentiation of stem cells through upregulating the alkaline phosphatase activity, osteogenic genes and protein expressions, as well as calcium deposition. Further study suggests that the activation of transforming growth factor‐beta/Smad3 signaling pathway plays an important role in the osteogenic differentiation of adipose‐derived stem cells enhanced by monodispersed nanoparticles. This study may have important implications for better understanding of stem cells fate induced by monodispersed nanoparticles and provide a promising approach toward stem cells‐based bone regeneration.     

Monodisperse Branched Molybdenum‐Based Bioactive Nanoparticles Significantly Promote Osteogenic Differentiation of Adipose‐Derived Stem Cells

Adipose‐derived stem cells (ADSCs) are considered to be ideal stem cell sources for bone‐tissue regeneration owing to their ease of collection and high activity. However, the regulation of osteogenic differentiation of ADSCs using biomaterials without adding growth factors is still not satisfactory. For the first time, molybdenum‐doped bioactive glass nanoparticles with a radial porous morphology (Mo‐rBGNs) are reported and their role in the osteogenic differentiation of ADSCs is investigated. The results show that Mo‐rBGNs exhibit radially porous and spherical morphology, relatively homogeneous particle size (200–400 nm), and excellent apatite‐forming bioactivity. They do not affect the proliferation of ADSCs, but significantly regulate their osteogenic differentiation and biomineralization. 5% Mo‐rBGNs significantly enhance the alkaline phosphatase activity and biomineralization ability and promote the osteogenic gene expressions of collagen I secretion and bone sialo protein in ADSCs. A reasonable and promising strategy for designing nanoscale bioactive materials with the excellent osteogenic ability for stem cell–based bone tissue regeneration is provided.     

High-affinity integration of hydroxyapatite nanoparticles with chemically modified silk fibroin

Hydroxyapatite (HA)-based nanocomposites were prepared by a co-precipitation method with silk fibroin (SF) serving as organic matrix. Silk fibroin was chemically modified with an alkali solution or an enzyme attempting to improve the interface between the mineral and the organic matrix. The influences of the alkali and enzyme pretreatments on microstructure and physicochemical properties of HA–SF composite were examined and compared. The results reveal that both the two kinds of pretreatments facilitate the formation of highly ordered three-dimensional porous network throughout the composites, increase the microhardness of the composite, and promote the preferential growth of HA crystallites along c-axis. Among all the as-prepared samples, the composite containing the enzyme pretreated SF shows desirable hierarchical microstructure with higher degree of organization and more uniform pore size distribution. Due to the enzyme pretreatment, HA crystallites undergo obvious changes in morphology from rod-like to␣whisker-like and in crystal growth towards more apparent epitaxy along c-axis. The alkali pretreatment induces the stronger chemical interactions between HA and SF and thus to strengthen the inorganic–organic interfacial adhesion. The newly developed HA–SF composites are expected to be attractive biomedical materials for bone repair and remodeling.     

In situ Raman imaging of osteoblastic mineralization

Hydroxyapatite (HA) is synthesized at early stages of bone formation by osteoblasts. Nondestructive observation of early stages of osteoblastic mineralization provides crucial information for biological mechanism of bone formation. Raman microscopy serves as an ideal tool to observe the osteoblastic mineralization process because it shows the chemical information of the sample at a minimally invasive level. In addition, HA is a marker for osteoblastic mineralization, and HA Raman signal is strong enough to identify mineralized spots in osteoblasts. In this research, we visualized the distribution of HA in cultured mouse osteoblasts by Raman imaging and observed the location of the mineralized spots in the culture. We monitored HA Raman signal from osteoblast culture for 3 days after administrating the osteogenic differentiation medium and observed Raman signal associated with HA. We identified mineralized spots of KUSA‐A1 by Raman imaging constructed from the distribution of HA Raman signal. We successfully visualized the distribution of the mineralized spots in the culture of KUSA‐A1. We compared our Raman images with Alizarin red S staining assay, which was a conventional method to evaluate the mineralization process. Raman imaging of the KUSA‐A1 culture visualized the mineralized spots more accurately than Alizarin red S staining assay. Raman imaging of HA serves as a powerful tool to identify the mineralized spots in an in vitro culture of osteogenic lineage cells. Copyright © 2014 John Wiley & Sons, Ltd.     

Plasticity of human dental pulp stromal cells with bioengineering platforms: A versatile tool for regenerative medicine

In recent years, human dental pulp stromal cells (DPSCs) have received growing attention due to their characteristics in common with other mesenchymal stem cells, in addition to the ease with which they can be harvested. In this study, we demonstrated that the isolation of DPSCs from third molar teeth of healthy individuals allowed the recovery of dental mesenchymal stem cells that showed self-renewal and multipotent differentiation capability. DPSCs resulted positive for CD73, CD90, CD105, STRO-1, negative for CD34, CD45, CD14 and were able to differentiate into osteogenic and chondrogenic cells. We also assayed the angiogenic potential of DPSCs, their capillary tube-like formation was assessed using an in vitro angiogenesis assay and the uptake of acetylated low-density lipoprotein was measured as a marker of endothelial function. Based on these results, DPSCs were capable of differentiating into cells with phenotypic and functional features of endothelial cells. Furthermore, this study investigated the growth and differentiation of human DPSCs under a variety of bioengineering platforms, such as low frequency ultrasounds, tissue engineering and nanomaterials. DPSCs showed an enhanced chondrogenic differentiation under ultrasound application. Moreover, DPSCs were tested on different scaffolds, poly(vinyl alcohol)/gelatin (PVA/G) sponges and human plasma clots. We showed that both PVA/G and human plasma clot are suitable scaffolds for adhesion, growth and differentiation of DPSCs toward osteoblastic lineages. Finally, we evaluated the interactions of DPSCs with a novel class of nanomaterials, namely boron nitride nanotubes (BNNTs). From our investigation, DPSCs have appeared as a highly versatile cellular tool to be employed in regenerative medicine.     

Overview of Hydroxyapatite–Graphene Nanoplatelets Composite as Bone Graft Substitute: Mechanical Behavior and In-vitro Biofunctionality

Hydroxyapatite (HA) and related materials have been frequently studied as ceramic-based bone graft materials due to their outstanding biocompatibility and osteoconduction. Since the bones are the load supporting parts of a vertebrate, they must have good fracture toughness (K_IC) to avoid fracture at high loading during limb movements. However, the main shortcomings of HA are the poor fracture toughness and brittleness. The mechanical properties of HA need to be improved for orthopedic applications, therefore it is often fabricated with other materials into a composite. This article focuses on the effect of carbon nanostructures (CNSs) especially graphene nanoplatelets (GNPs) on the mechanical, physicochemical properties and in-vitro bio-functional performances of HA. We provide an overview on the preparation and characterization of the HA–GNPs composites. To conclude, the challenges in the fabrication of multi-substituted HA–GNPs composites and future outlooks in the biomedical domain are discussed.     

Effect of gold nanoparticles on adipogenic differentiation of human mesenchymal stem cells

Gold nanoparticles are very attractive for biomedical products. However, there is a serious lack of information concerning the biological activity of nanosized gold in human tissue cells. An influence of nanoparticles on stem cells might lead to unforeseen consequences to organ and tissue functions as long as all cells arising from the initial stem cell might be subsequently damaged. Therefore the effect of negatively charged gold nanoparticles (9 and 95 nm), which are certified as reference material for preclinical biomedical research, on the adipogenic differentiation of human mesenchymal stem cells (hMSCs) is investigated here. Bone marrow hMSCs are chosen as differentiation model since bone marrow hMSCs are well characterized and their differentiation into the adipogenic lineage shows clear and easily detectable differentiation. In this study effects of gold nanoparticles on adipogenic differentiation are analyzed regarding fat storage and mitochondrial activity after different exposure times (4–21 days). Using time lapse microscopy the differentiation progress under chronically gold nanoparticle treatment is continuously investigated. In this preliminary study, chronically treatment of adipogenic differentiating hMSCs with gold nanoparticles resulted in a reduced number and size of lipid vacuoles and reduced mitochondrial activity depending on the applied concentration and the surface charge of the particles.     

Influence of the calcium phosphate content of the target on the phase composition and deposition rate of sputtered films

Calcium phosphate was coated from tetracalcium phosphate (TTCP), hydroxyapatite (HA), β-tricalcium phosphate (TCP), β-calcium pyrophosphate (CPP), and β-calcium metaphosphate (CMP) powder targets using radio frequency magnetron sputtering. The composition of the crystal phase of the coated films was changed, depending on the target materials, and the Ca/P molar ratios of the films varied from 0.74 to 2.54, increasing with the Ca/P molar ratio of the target. The solubility of the target, determined using a microwave-induced plasma-mass spectrometer was: TTCP ≈ β-CMP > β-TCP > β-CPP > HA, and the deposition rate from each target showed a similar order to the solubility: TTCP ≈ β-CMP > β-TCP > β-CPP ≈ HA.     

An investigation into the effects of high laser fluence on hydroxyapatite/calcium phosphate films deposited by pulsed laser deposition

Pulsed laser deposited mixed hydroxyapatite (HA)/calcium phosphate thin films were prepared at room temperature using KrF laser source with different laser fluence varying between 2.4 J/cm² and 29.2 J/cm². Samples deposited at 2.4 J/cm² were partially amorphous and had rough surfaces with a lot of droplets while higher laser fluences showed higher level of crytallinity and lower roughness of surfaces of obtained samples. Higher laser fluences also decreased ratio Ca/P of as-deposited samples. X-ray photoelectron spectroscopy (XPS) revealed traces of carbonate groups in obtained samples, which were removed after thermal annealing. The decomposition of HA into TCP was observed to start at about 400 °C. The formation of new crystalline phase of HA was found after annealing as well. The cracks observed on surface of sample deposited at 29.2 J/cm² after annealing indicated that the HA/ calcium phosphate films deposited at higher laser energy densities were probably more densed.     

Characterization of calcium phosphate coatings doped with Mg, deposited by pulsed laser deposition technique using ArF excimer laser

Calcium phosphate layers were deposited on Ti6Al4V substrates with TiN buffer layers by use of pulsed laser deposition method. With this technique three pressed pellets consisted of tricalcium phosphate (TCP, Ca(3)(PO(4))(2)), hydroxyapatite (HA, Ca(10)(PO(4))(6)(OH)(2)) and hydroxyapatite-doped with magnesium (HA with 4% of Mg and trace amount of (Ca,Mg)(3)(PO(4))(2)) were ablated using ArF excimer laser (lambda=193 nm). The using of different targets enabled to determine the influence of target composition on the nature of deposited layers. The obtained deposits were characterized by means of Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction method (XRD). The obtained Fourier spectras revealed differences in terms of intensity of spectral bands of different layers. The analysis from XRD showed that Mg-doped HA layer has crystalline structure and TCP and HA layers composition is characterized by amorphous nature.     

Embedding methods for poly(l-lactic acid) microfiber mesh/human mesenchymal stem cell constructs

Fiber mesh scaffolds were recently investigated in tissue engineering as possible support for stem cell growth and differentiation, in order to repair lesion areas in clinical practice. In particular, the literature is focused on fiber mesh scaffolds constituted of biocompatible and resorbable polymeric structures, like poly(l-lactic acid) (PLLA). However, as regards the study of constructs constituted of PLLA microfibers and cells, only quantitative and SEM analyses were reported, lacking histological analysis. Histological evaluation of these constructs could give important information about cellular distribution in the scaffold, cell–scaffold interactions and extracellular matrix production. The purpose of our study was to find a valid method to analyze PLLA microfiber/cell constructs from both histological and histochemical angles. Biodegradable non-woven fiber meshes were prepared using hollow microfibers, based on PLLA.We first evaluated different embedding methods useable for histological analysis and the results showed that among the paraffin, Killik, and acrylic resin the only suitable medium was the latter. Then we employed the acrylic resin to embed the constructs made up of PLLA microfibers and bone marrow-derived human mesenchymal stromal cells, which we then analyzed with Toluidine Blue, PAS and Alcian Blue staining. These constructs, previously analyzed for cell viability by MTT and CCK-8 tests, showed viable/proliferating cells until 6 weeks of culture. The stainings performed on constructs confirmed viability data obtained with SEM and MTT/CCK-8 and supplied other information on the cell behaviors such as the distribution and organization onto the scaffold and the production of extracellular matrix molecules. In conclusion, this methodological study mainly suggests a suitable method to analyze PLLA microfiber/cell constructs, at the same time confirming and enriching the literature data on the compatibility between PLLA microfibers and hMSCs.     

Influence of Addition of Hyaluronic Acid (HA) on the Properties of Collagen/HA Composite Scaffolds

In order to develop a scaffolding material for tissue regeneration, porous matrices containing varying composites of collagen and hyaluronic acid (HA) (from 1:0 to 0:1) were fabricated using a freeze-drying method. The effect of the composition on the morphology, hydrophilicity, swelling behavior, mechanical properties, and in vitro cytotoxicity was investigated. The results showed that all the scaffolds had an interconnected pore structure with sufficient pore size for use as a support for the growth of fibroblasts. The addition of HA improved the swelling property, but reduced the compressive strength. The contact angle decreased with increasing HA content. In in vitro cytotoxicity tests using fibroblastic cells, the collagen/HA scaffolds showed no toxicity. All these results suggest that collagen/HA composite scaffolds are a potential candidate for tissue engineering scaffolds.     

Doped biocompatible layers prepared by laser

The contribution deals with KrF laser synthesis and study of doped biocompatible materials with focus on diamond-like carbon (DLC) and hydroxyapatite (HA). Overview of materials used for dopation is given. Experimental results of study of HA layers doped with silver are presented. Films properties were characterized using profilometer, SEM, WDX, XRD and optical transmission. Content of silver in layers moved from 0.06 to 13.7 at %. The antibacterial properties of HA, silver and doped HA layers were studied in vivo using Escherichia coli cells.     

Mechanical characteristics of composites of polylactide and nanosized calcium phosphates formed in supercritical carbon dioxide

Composite materials for biomedical applications based on polylactide, a bioresorbable polymer, and nanosized calcium phosphate (hydroxyapatite) were produced using supercritical (SC) carbon dioxide. For composites with different polymer-to-mineral ratios, the bending stress-strain diagrams were investigated. The elasticity moduli of composites obtained in SC-CO₂ from powdered bioresorbable polymer and bioactive nanoceramics ranged elastic modulus of natural bone. Experiments on adhesion of human embryonic fibroblasts demonstrated the suitability of generated samples for use in bone tissue scaffold engineering and regenerative medicine.     

Biopolymer-Hydroxyapatite Scaffolds for Advanced Prosthetics

Biocompatibility in research and development of advanced prosthetics is a current problem faced by medical researchers. A major challenge in tissue engineering is to find materials and processing techniques that allow them to produce extracellular matrices (ECM) mimicking scaffolds that promote cell growth and organization into a specific architecture, inducing cell differentiation and subsequent cell function. The ideal tissue repair material thus should consist of synthetic biomaterials, such as natural polymers mimicking the mechanical and biological functionality of the ECM. Cellulose acetate membranes were used as scaffolds for microvascular cell growth. Hydroxyapatite (HA) is a natural ceramic (responsible for strength and stability in the human skeletal system) operable as a biocomposite coating to improve the biocompatibility of implant substrates. In this work, HA was prepared from low cost natural calcium source — eggshells. Its structural properties were investigated by scanning (SEM), transmission (TEM) electron microscopies and Fourier Transformed Infrared spectroscopy (FT-IR). The composition analyses of HA were measured by the total reflection X-ray fluorescence spectrometer (TXRF) and by prompt gamma activation analysis (PGAA). Hydroxyapatite added biodegradable scaffolds have been prepared by electrospinning method to enhance biological functionality.     

In vitro and in vivo biocompatibility study on laser 3D microstructurable polymers

Films and microstructured scaffolds have been fabricated using direct laser writing out of different polymers: hybrid organic-inorganic ORMOCORE b59, acrylate-based AKRE23, novel organic-inorganic Zr containing hybrid SZ2080, and biodegradable PEG-DA-258. Adult myogenic stem cells were grown on these surfaces in vitro. Their adhesion, growth, and viability test results suggest good potential applicability of the materials in biomedical practice. Pieces of these polymers were implanted in rat’s paravertebral back tissue. Histological examination of the implants and surrounding tissue ex vivo after 3 weeks of implantation was conducted and results show the materials to be at least as biocompatible as surgical clips or sutures. The applied direct laser writing technique seems to offer good future prospects in a polymeric 3D scaffold design for artificial tissue engineering with autologous stem cells.     

Bone‐nanohydroxyapatite spheres interface evaluation by synchrotron radiation X‐ray microfluorescence

Hydroxyapatite (HA) is largely used as bone graft; it seems to be the most promising synthetic implant material, mainly because of its excellent biocompatibility. The crystallinity, particle and pore size of HA are important characteristics and can be modified by decreasing basic structural form below 100 nm and have evoked a great amount of attention for improving prevention, diagnosis, and disease treatment, besides improving bone repair through the biodegradation of the material. The aim of this study was to investigate bone mineral content in bone samples with nanohydroxyapatite and HA spheres, specially its spatial distribution on bone microarchitecture. Circular bone defects were made in both tibiae of 12 White New Zeland adult rabbits (Oryctolagus cuniculus) and were divided randomly into five groups – blood clot (control group), sintered HA, non‐sintered HA, sintered nanoHA and non‐sintered nanoHA – all materials in spherical shape, to smooth handling and accommodation of the surgical bed, and to minimize inflammatory response. The rabbits were euthanatized according to the experimental period of 1 and 4 weeks after surgery. The samples were evaluated by polarized microscopy as well as X‐ray microfluorescence in order to account the bone mineral content bone‐implant interfaces, through synchrotron radiation. Our results revealed greater newly formed bone area in the non‐sintered materials and control groups, and the used technique showed that the amount of calcium of new bone was consistent with both mature bone and HA spheres. In conclusion, the present findings suggest that HA‐based biomaterials are biocompatible, promote osteoconduction and favored bone repair. Copyright © 2011 John Wiley & Sons, Ltd.     

Mechanical behaviour of ceramic matrix composites

Thermomechanical ceramics have interesting properties: mainly high hardness, high wear resistance, good chemical resistance, good mechanical strength at high temperatures and generally low thermal conductivity. But, the engineering use of ceramics as structural parts is at the moment limited by their inherent brittleness. The toughness values of ceramics are between about to 5 MPa √m whereas the toughness values of metals are much higher (from 20 to 200 MPa √m). To avoid this brittleness, composite ceramics have to be used. Two types of composite materials can be developed: particle-reinforced composites and fiber-reinforced composites. In this paper, some examples of reinforcement of ceramics are presented. Two cases will be developed: second-phase reinforcement with zirconia particles or other particles, and the composites reinforced by fibers or whiskers.