Zn掺杂β-Ga2O3薄膜的制备和特性研究

β-Ga₂O₃是一种宽带隙半导体材料,能带宽度E_g≈5.0eV,在光学和光电子学领域有广泛的应用。用射频磁控溅射方法在Si衬底和远紫外光学石英玻璃衬底制备了本征β-Ga₂O₃薄膜及Zn掺杂β-Ga₂O₃薄膜,用紫外 可见分光光度计、X射线衍射仪、荧光分光光度计对本征β-Ga₂O₃薄膜及Zn掺杂β-Ga₂O₃薄膜的光学透过、光学吸收、结构和光致发光进行了测量,研究了Zn掺杂和热退火对薄膜结构和光学性质的影响。退火后的β-Ga₂O₃薄膜为多晶结构,与本征β-Ga₂O₃薄膜相比,Zn掺杂β-Ga₂O₃薄膜的β-Ga₂O₃(111)衍射峰强度变小,结晶性变差,衍射峰位从35.69°减小至35.66°。退火后的Zn掺杂β-Ga₂O₃薄膜的光学带隙变窄,光学透过降低,光学吸收增强,出现了近边吸收,薄膜的紫外、蓝光及绿光发射增强。表明退火后Zn掺杂β-Ga₂O₃薄膜中的Zn原子被激活充当受主。     

SiO2/Si衬底上石墨烯的制备与结构表征

在分子束外延(MBE)设备中,利用直接沉积C原子的方法在覆盖有SiO₂的Si衬底(SiO₂/Si)上生长石墨烯,并通过Raman光谱和近边X射线吸收精细结构谱等实验技术对不同衬底温度(500℃,600℃,700℃,900℃,1100℃,1200℃)生长的薄膜进行结构表征.实验结果表明,在衬底温度较低时生长的薄膜是无定形碳,在衬底温度高于700℃时薄膜具有石墨烯的特征,而且石墨烯的结晶质量随着衬底温度的升高而改善,但过高的衬底温度会使石墨烯质量降低.衬底温度为1100℃时结晶质量最好.衬底温度较低时C原子活性较低,难以形成有序的C-sp²六方环.而衬底温度过高时(1200℃),衬底表面部分SiO₂分解,C原子与表面的Si原子或者O原子结合而阻止石墨烯的形成,并产生表面缺陷导致石墨烯结晶变差.     

氧分子的价壳层光学振子强度研究

在入射电子能量为1500eV、平均散射角为0°、能量分辨为60meV条件下，得到了氧分子在5.7—28.5eV能量区间的光学振子强度密度谱，获得了氧分子E³Σ^-_ｕ的ν′=0，1，2和2³Π_ｕ的ν′=0，1各振动能级的绝对光学振子强度，同时检验了我们的Bethe-Born转换因子外推到低能端的可靠性．将所得结果与前人的工作进行了比     

氧氩比对SnO2/Ag/SnO2透明导电膜光电性能的影响

在室温及不同的氧氩比条件下,采用射频磁控溅射Ag层和直流磁控溅射SnO₂层,在载玻片衬底上制备出了SnO₂/Ag/SnO₂多层薄膜.用霍尔效应测试仪、四探针电阻测试仪和紫外-可见-近红外光谱仪等表征了薄膜的电学性质和光学性质.实验结果表明:当氧氩比为1:14时,所制得的薄膜的光电性质优良指数最大,为1.69×10^-2 Ω^-1;此时,薄膜的电阻率为9.8×10^-5 Ω·cm,方电阻为9.68 Ω/sq,在400~800 nm可见光区的平均光学透射率达85%;并且,在氧氩比为1:14时,利用射频磁控溅射Ag层和直流磁控溅射SnO₂层在PET柔性衬底上制备出了光电性质优良的柔性透明导电膜,其在可见光区的平均光学透过率达85%以上,电阻率为1.22×10^-4 Ωcm,方电阻为12.05 Ω/sq.     

N掺杂Cu2O薄膜的光学性质及第一性原理分析

采用射频磁控溅射技术, 在不同温度下制备了N掺杂Cu₂O薄膜．透射光谱分析发现, N掺杂导致Cu₂O成为允许的带隙直接跃迁半导体, 并使Cu₂O的光学禁带宽度增加．不同温度下沉积的薄膜光学禁带宽度E_g=2.52± 0.03 eV．第一性原理计算表明, N掺杂导致Cu₂O的禁带宽度增加了约25%, 主要与价带顶下移和导带底上移有关, 与实验报道基本符合．N的2p电子态分布不同于O原子, 在价带顶附近具有较大的态密度是N掺杂Cu₂O变成允许的带隙直接跃迁半导体的根本原因．     

氮气退火对二氧化钛薄膜光学性能的影响

 提出了一种利用离子注入和后续退火制备氮掺杂TiO₂薄膜的方法。首先在室温下向石英玻璃中注入Ti离子,随后在氮气中退火到900 ℃,从而制备了氮掺杂的玻璃基TiO₂薄膜。SRIM2006程序模拟和卢瑟福背散射谱（RBS）研究表明注入离子从样品表面开始呈高斯分布,实验结果和模拟结果吻合很好。X射线光电子能谱（XPS）研究结果表明注入态样品中形成了金属Ti和TiO₂,900 ℃退火后金属Ti转变成TiO₂,同时N原子替代少量的晶格O原子形成了O－Ti－N化合物。紫外-可见吸收光谱（UV-Vis）结果显示,当退火温度至500 ℃时,在吸收光谱中开始出现TiO₂的吸收边,随退火温度升高到900 ℃,由于O－Ti－N化合物形成,TiO₂的吸收边从3.98 eV红移到3.30 eV,TiO₂吸收边末端延伸到可见光区,在可见光区的吸收强度明显增加。     

不同氧气流量对直流磁控溅射TiO2薄膜的影响

采用直流反应磁控溅射法,以高纯Ti为靶材,高纯O₂为反应气体,制备了TiO₂薄膜.研究了氧气流量对薄膜结晶取向、表面形貌和光学性能的影响.研究发现,TiO₂薄膜主要呈锐钛矿TiO₂(101)择优取向,当氧气流量较小时,薄膜中还含有金属Ti(100),氧气流量较大时,薄膜含TiO₂(101)和TiO₂(004),成多晶态;薄膜的粗糙度和颗粒大小都随氧气流量的增大而增大;薄膜在400~1100nm可见-近红外波段有较高的透射率并且其吸收峰随着氧气流量的增大而红移,当氧气流量为5sccm时,平均透射率最高.     

第2系列ZrO2(Y2O3)薄膜的慢正电子研究

用慢正电子技术研究了在溅射时不加偏压,衬底加热300℃,纯Ar气氛下制备的用Y_{2O3稳定的ZrO2薄膜材料(简称YSZ薄膜),发现了YSZ薄膜在不同 深度处的缺陷分布情况,退火温度对YSZ薄膜缺陷有影响.简要讨论了致密、优质YSZ薄膜的 制备方法.}     

In2O3 透明薄膜晶体管的制备及其电学性能的研究

采用磁控溅射方法在玻璃衬底上生长了In₂O₃晶体薄膜.该薄膜具有(111)晶面择优取向,晶粒尺寸达到33 nm.利用光刻工艺制作了以In₂O₃晶体薄膜为沟道层的底栅式薄膜晶体管.In₂O₃薄膜晶体管具有良好的栅压调制特性,场效应迁移率达到6.3 cm²/(V·s),开关电流比为3×10³,阈值电压为-0.9 V.结果表明,In相似文献   

Al掺杂原子分数及退火温度对ZnO薄膜光学特性的影响

 采用溶胶凝胶法在（0001）Al₂O₃衬底上制备了不同掺杂原子分数的ZnO:Al薄膜,在Ar气氛中进行了600～950 ℃不同温度的退火处理,研究了掺杂原子分数和退火温度对薄膜光致发光、光吸收和透射的影响。结果显示,薄膜的紫外峰强度随掺杂原子分数和退火温度的提高而增强,与缺陷相关的绿光强度却随着掺杂原子分数和退火温度的提高而降低;薄膜光学带隙随掺杂原子分数的提高从3.21 eV增大到3.25 eV;光吸收在可见光区随着退火温度的升高而增大,在紫外区却随着退火温度的升高而减小,透射与吸收的变化规律相反;薄膜吸收边随退火温度的升高出现轻微的红移。     

Spectroscopic ellipsometric study of the optical properties of Ag2O film prepared by direct-current magnetron reactive sputtering

The Ag2O film, as-deposited by direct-current magnetron reactive sputtering at a substrate temperature of 150℃, clearly shows a preferential orientation (111), and is capable of lowering the threshold value of the thermal decomposition temperature to about 200℃, which is helpful to its application in optical and magneto-optical storage. This paper fits its optical constants in terms of a general oscillator model by using measured ellipsometric parameters. The fitted oscillator energy 2.487 eV is close to the optical direct interband transition energy value of the Ag2O film determined by Tauc equation; whereas, the fitted oscillator energy 4.249 eV is far from the fitted plasma oscillator energy 4.756 eV by single-oscillator energy. The photoluminescence spectrum centred at about 2.31 eV indicates a direct-energy gap photoluminescence mechanism of the Ag2O film.     

反应气压对直流磁控反应溅射制备的氧化银薄膜的结构和光学性质的影响

利用直流磁控反应溅射技术,通过调节反应气压(RP),在250 ℃衬底温度下制备了一系列氧化银 (Ag_xO) 薄膜,并利用X射线衍射谱、能量色散谱和分光光度计重点研究了RP对Ag_xO薄膜的结构和光学性质的影响. 研究结果表明,随着RP从0.5 Pa升高到3.5 Pa,薄膜明显呈现了从两相(AgO+Ag₂O)到单相(Ag₂O)结构再到两相(Ag₂O+AgO)结构的演变. 特 关键词： 氧化银薄膜 直流磁控反应溅射 X射线衍射谱 光学性质     

Effects of the sputtering power on the crystalline structure and optical properties of the silver oxide films deposited using direct-current reactive magnetron sputtering

This paper reports that a series of silver oxide (Ag_xO) films are deposited on glass substrates by direct-current reactive magnetron sputtering at a substrate temperature of 250 oC and an oxygen flux ratio of 15:18 by modifying the sputtering power (SP). The Ag_xO films deposited apparently show a structural evolution from cubic biphased (AgO + Ag₂O) to cubic single-phased (Ag₂O), and to biphased (Ag₂O + AgO) structure. Notably, the cubic single-phased Ag₂O film is deposited at the SP = 105 W and an AgO phase with <220> orientation discerned in the Ag_xO films deposited using the SP > 105 W. The transmissivity and reflectivity of the Ag_xO films in transparent region decrease with the increase the SP, whereas the absorptivity inversely increases with the increase of the SP. These results may be due to the structural evolution and the increasing film thickness. A redshift of the films' absorption edges determined in terms of Tauc formula clearly occurs from 3.1 eV to 2.73 eV with the increase of the SP.     

Effect of substrate temperature on microstructure and optical properties of single-phased Ag2O film deposited by using radio-frequency reactive magnetron sputtering method

Using a radio-frequency reactive magnetron sputtering technique,a series of the single-phased Ag2O films are deposited in a mixture of oxygen and argon gas with a flow ratio of 2:3 by changing substrate temperature(T s).Effects of the T s on the microstructure and optical properties of the films are investigated by using X-ray diffractometry,scanning electron microscopy and spectrophotometry.The single-phased Ag2O films deposited at values of T s below 200℃ are(111) preferentially oriented,which may be due to the smallest free energy of the(111) crystalline face.The film crystallization becomes poor as the value of T s increases from 100℃ to 225℃.In particular,the Ag2O film deposited at T s = 225℃ loses the 111 preferential orientation.Correspondingly,the film surface morphology obviously evolves from a uniform and compact surface structure to a loose and gullied surface structure.With the increase of T s value,the transmissivity and the reflectivity of the films in the transparent region are gradually reduced,while the absorptivity gradually increases,which may be attributed to an evolution of the crystalline structure and the surface morphology of the films.     

Structural-optical study of high-dielectric-constant oxide films

High-k polycrystalline Pr₂O₃ and amorphous LaAlO₃ oxide thin films deposited on Si(0 0 1) are studied. The microstructure is investigated using X-ray diffraction and scanning electron microscopy. Optical properties are determined in the 0.75-6.5 eV photon energy range using spectroscopic ellipsometry. The polycrystalline Pr₂O₃ films have an optical gap of 3.86 eV and a dielectric constant of 16-26, which increases with film thickness. Similarly, very thin amorphous LaAlO₃ films have the optical gap of 5.8 eV, and a dielectric constant below 14 which also increases with film thickness. The lower dielectric constant compared to crystalline material is an intrinsic characteristic of amorphous films.     

Effects of the substrate temperature on the properties of CuIn5S8 thin films

Structural, optical and electrical properties of CuIn₅S₈ thin films grown by thermal evaporation have been studied relating the effects of substrate heating conditions of these properties. The CuIn₅S₈ thin films were carried out at substrate temperatures in the temperature range 100-300 °C. The effects of heated substrate on their physico-chemical properties were investigated using X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), optical transmission and hot probe method. X-ray diffraction revealed that the films are strong preferred orientation along the (3 1 1) plane upon substrate temperature 200 °C and amorphous for the substrate temperatures below 200 °C. No secondary phases are observed for all the films. The composition is greatly affected by heated substrate. From the optical transmission and reflection, an important absorption coefficient exceeds 10⁵ cm⁻¹ at 800 nm was found. As increasing the substrate temperature, the optical energy band gap decreases from 1.70 eV for the unheated films to 1.25 eV for the deposited films at 300 °C. It was found that CuIn₅S₈ thin film is an n-type semiconductor at 250° C.     

Structural,optical and gas sensing properties of Cu2O/CuO mixed phase: effect of the number of coated layers and (Cr + S) co-Doping

Thin films of Cu₂O/CuO mixed phase have been deposited on pre-cleaned glass substrate by a spin-coating technique. The influence of Cr-doping, (Cr?+?S) co-doping and the number of coated layers on the structures and optical behaviors of the films were investigated by X-ray diffraction (XRD), Fourier transform infrared (FTIR), Raman, and UV-Visible spectroscopies. From XRD, FTIR and Raman results; the films are composed of polycrystalline monoclinic CuO and cubic Cu₂O phases with crystallite sizes ranged from 10.05 to 23.08?nm. Increasing the thickness improves the films’ crystallinity and decreases the defects level in the films. Cr and S incorporation encourages the growth of CuO phase at the expense of Cu₂O one and affects the preferred growth direction. The doping with Cr and S blue shifted the B_g mode and multi-phonon transitions. The direct and indirect optical band gaps decreased from 2.25?eV and 1.60?eV to 2.10?eV and 1.20?eV by growing the number of deposited layers from 2 to 8 layers. The film sensitivity towards CO₂ at different gas flow rate was studied and compared with those of similar systems. Also; response time, recovery time, detection limit, and limit of quantification are estimated.     

真空热退火温度对单相Ag2O薄膜微结构和光学性质的影响

利用直流磁控反应溅射技术在玻璃衬底上沉积了单相Ag₂O薄膜,并采用真空热退火对单相Ag₂O薄膜在不同热退火温度 (T _{A) 下进行了1 h热处理.利用X射线衍射谱、扫描电子显微镜和分光光度计研究了 T A对单相Ag2O薄膜微结构和光学性质的影响.研究结果表明, T}A= 300 ℃ 时Ag₂O薄膜中开始出现Ag纳米颗粒,且随着 T _{A的升高薄膜中Ag的含量 关键词： 2}O薄膜')" href="#">Ag₂O薄膜 热退火温度 微结构 光学性质     

Thickness dependent optical dispersion parameters and nonlinear optical properties of nanostructured Cr doped CdO thin films

Cr doped CdO thin films were deposited on glass substrates by reactive DC magnetron sputtering with varying film thickness from 250 to 400 nm. XRD studies reveal that the films exhibit cubic structure with preferred orientation along the (2 0 0) plane. The optical transmittance of the films decreases from 92 to 72%, whereas the optical energy band gap of the films decreased from 2.88 to 2.78 eV with increasing film thickness. The Wemple–DiDomenico single oscillator model has been used to evaluate the optical dispersion parameters such as dispersion energy (E_d), oscillator energy (E_o), static refractive index (n_o) and high frequency dielectric constant (ε_∞). The nonlinear optical parameters such as optical susceptibility (χ⁽¹⁾), third order nonlinear optical susceptibility (χ⁽³⁾) and nonlinear refractive index (n₂) of the films were also determined.