Fabrication of textured SnO2:F thin films by spray pyrolysis

Transparent conductive SnO₂:F thin films with textured surfaces were fabricated on soda-lime-silica glass substrates by spray pyrolysis. Structure, morphology, optical and electrical properties of the films were investigated. Results show that the film structure, morphology, haze, transmittance and sheet resistance are dependent on the substrate temperature and film thickness. An optimal 810 nm-thick SnO₂:F film with textured surface deposited at 520 °C exhibits polycrystalline rutile tetragonal structure with a (2 0 0) orientation. The sheet resistance, average transmittance in visible region, and haze of this film were 8 Ω/□, 80.04% and 11.07%, respectively, which are suitable for the electrode used in the hydrogenated amorphous silicon solar cells.     

The structure and optical properties of evaporated Samarium fluoride films

Samarium fluoride (SmF₃) films have been deposited on quartz, silicon and germanium substrates by vacuum evaporation method. The crystal structure of the films deposited on silicon substrate is examined by X-ray diffraction (XRD). The films deposited at 100 °C, 150 °C and 250 °C have the (1 1 1) preferred growth orientation, but the film deposited at 200 °C has (3 6 0) growth orientation. The surface morphology evolution of the films with different thickness is investigated with optical microscopy. It is shown that the microcrack density and orientation of thin film is different from that of thick film. The transmission spectrum of SmF₃ films is measured from 200 nm to 20 μm. It is found that this material has good transparency from deep violet to far infrared. The optical constants of SmF₃ films from 200 nm to 12 μm are calculated by fitting the transmission spectrum of the films using Lorentz oscillator model.     

Microstructure, hydrogenation and optical behavior of Mg-Ni multilayer films deposited by magnetron sputtering

Mg-Ni multilayer films with sequential Mg and Ni layers were prepared by direct current magnetron sputtering. The substrate temperature influences the microstructure of the films greatly. The film deposited at 298 K exhibits multilayered structure, while the film shows nanocrystalline/amorphous composite structure at the deposition temperature of 473 K. The optical properties between hydrogenation/dehydrogenation states of the films were performed using spectrophotometer in visible light region. The film deposited at 473 K can switch from mirror-like metallic state towards brownish yellow transparent state under 0.6 MPa H₂ at 298 K, and the optical transmittance modulation reaches up to 20% both at a wavelength of 770 nm and IR region, while the film deposited at 298 K exhibits low optical change, and the optical switching behavior can hardly be found. The extra free energy stored in the boundary of the nanocrystallines benefits the formation of magnesium-based hydride, resulting in the enhancement of the optical switching properties of the Mg-Ni film deposited at 473 K.     

Effects of the substrate temperature on the properties of CuIn5S8 thin films

Structural, optical and electrical properties of CuIn₅S₈ thin films grown by thermal evaporation have been studied relating the effects of substrate heating conditions of these properties. The CuIn₅S₈ thin films were carried out at substrate temperatures in the temperature range 100-300 °C. The effects of heated substrate on their physico-chemical properties were investigated using X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), optical transmission and hot probe method. X-ray diffraction revealed that the films are strong preferred orientation along the (3 1 1) plane upon substrate temperature 200 °C and amorphous for the substrate temperatures below 200 °C. No secondary phases are observed for all the films. The composition is greatly affected by heated substrate. From the optical transmission and reflection, an important absorption coefficient exceeds 10⁵ cm⁻¹ at 800 nm was found. As increasing the substrate temperature, the optical energy band gap decreases from 1.70 eV for the unheated films to 1.25 eV for the deposited films at 300 °C. It was found that CuIn₅S₈ thin film is an n-type semiconductor at 250° C.     

Structural and optical properties of MgxAl1-xHy gradient thin films: a combinatorial approach

The structural, optical and dc electrical properties of Mg_xAl_1-x (0.2≤x≤0.9) gradient thin films covered with Pd/Mg are investigated before and after exposure to hydrogen. We use hydrogenography, a novel high-throughput optical technique, to map simultaneously all the hydride forming compositions and the kinetics thereof in the gradient thin film. Metallic Mg in the Mg_xAl_1-x layer undergoes a metal-to-semiconductor transition and MgH₂ is formed for all Mg fractions x investigated. The presence of an amorphous Mg-Al phase in the thin film phase diagram enhances strongly the kinetics of hydrogenation. In the Al-rich part of the film, a complex H-induced segregation of MgH₂ and Al occurs. This uncommon large-scale segregation is evidenced by metal and hydrogen profiling using Rutherford backscattering spectrometry and resonant nuclear analysis based on the reaction ¹H(¹⁵N,αγ)¹²C. Besides MgH₂, an additional semiconducting phase is found by electrical conductivity measurements around an atomic [Al]/[Mg] ratio of 2 (x=0.33). This suggests that the film is partially transformed into Mg(AlH₄)₂ at around this composition. PACS 78.20.-e; 68.55.-a; 64.75.+g     

Effect of substrate temperature on the surface and interface oxidation of NiTi thin films

NiTi shape memory alloy thin films are deposited on pure Cu substrate at substrate ambient temperatures of 300 °C and 450 °C. The surface and interface oxidation of NiTi thin films are characterized by X-ray photoelectron spectroscopy (XPS). After a subsequent annealing treatment the crystallization behavior of the films deposited on substrate at different temperatures is studied by X-ray diffraction (XRD). The effects of substrate temperature on the surface and interface oxidation of NiTi thin films are investigated. In the film surface this is an oxide layer composed of TiO₂. The Ni atom has not been detected on surface. In the film/substrate interface there is an oxide layer with a mixture Ti₂O₃ and NiO in the films deposited at substrate temperatures 300 °C and 450 °C. In the films deposited at ambient temperature, the interface layer contains Ti suboxides (TiO) and metallic Ni.     

Thickness dependent activity of nanostructured TiO2/α-Fe2O3 photocatalyst thin films

The effect of thickness of TiO₂ coating on synergistic photocatalytic activity of TiO₂ (anatase)/α-Fe₂O₃/glass thin films as photocatalysts for degradation of Escherichia coli bacteria in a low-concentration H₂O₂ solution and under visible light irradiation was investigated. Nanograined α-Fe₂O₃ films with optical band-gap of 2.06 eV were fabricated by post-annealing of thermal evaporated iron oxide thin films at 400 °C in air. Increase in thickness of the Fe₂O₃ thin film (here, up to 200 nm) resulted in a slight reduction of the optical band-gap energy and an increase in the photoinactivation of the bacteria. Sol-gel TiO₂ coatings were deposited on the α-Fe₂O₃ (200 nm)/glass films, and then, they were annealed at 400 °C in air for crystallization of the TiO₂ and formation of TiO₂/Fe₂O₃ heterojunction. For the TiO₂ coatings with thicknesses ≤50 nm, the antibacterial activity of the TiO₂/α-Fe₂O₃ (200 nm) was found to be better than the activity of the bare α-Fe₂O₃ film. The optimum thickness of the TiO₂ coating was found to be 10 nm, resulting in about 70 and 250% improvement in visible light photo-induced antibacterial activity of the TiO₂/α-Fe₂O₃ thin film as compared to the corresponding activity of the bare α-Fe₂O₃ and TiO₂ thin films, respectively. The improvement in the photoinactivation of bacteria on surface of TiO₂/α-Fe₂O₃ was assigned to formation of Ti-O-Fe bond at the interface.     

Dielectric properties of continuous composition spreaded MgO-Ta2O5 thin films

The dielectric properties of MgO-Ta₂O₅ continuous composition spread (CCS) thin films were investigated. The MgO-Ta₂O₅ CCS thin films were deposited on Pt/Ti/SiO₂/Si substrates by off-Axis RF magnetron sputtering system, and then the films were annealed at 350 °C with rapid thermal annealing system in vacuum. The dielectric constant and loss of MgO-Ta₂O₅ CCS thin films were plotted via 1500 micron-step measuring. The specific point of Ta₂O₅-MgO CCS thin film (post annealed at 350 °C) showing superior dielectric properties of high dielectric constant (k ∼ 28) and low dielectric loss (tan δ < 0⋅004) at 1 MHz were found in the area of 3-5 mm apart from Ta₂O₅ side on the substrate. The cation's composition of thin film was Mg:Ta = 0.4:2 at%.     

Thermal stability of alumina thin films containing γ-Al2O3 phase prepared by reactive magnetron sputtering

The paper reports on thermal stability of alumina thin films containing γ-Al₂O₃ phase and its conversion to a thermodynamically stable α-Al₂O₃ phase during a post-deposition equilibrium thermal annealing. The films were prepared by reactive magnetron sputtering and subsequently post-deposition annealing was carried out in air at temperatures ranging from 700 °C to 1150 °C and annealing times up to 5 h using a thermogravimetric system. The evolution of the structure was investigated by means of X-ray diffraction after cooling down of the films. It was found that (1) the nanocrystalline γ-Al₂O₃ phase in the films is thermally stable up to 1000 °C even after 5 h of annealing, (2) the nanocrystalline θ-Al₂O₃ phase was observed in a narrow time and temperature region at ≥1050 °C, and (3) annealing at 1100 °C for 2 h resulted in a dominance of the α-Al₂O₃ phase only in the films with a sufficient thickness.     

Effects of post-thermal treatments on morphological and optical properties of NiO/Ni(OH)2 thin films synthesized by solution growth

Room temperature deposition of PVP capped nanostructured NiO/Ni(OH)₂ thin film, the morphological and optical characterizations by solution growth technique are reported. The nanostructured thin films which were deposited on optical glass substrates were annealed at different temperatures and then subjected to structural, morphological and optical characterizations. X-ray diffraction measurements of the films revealed that higher temperatures during the thermal treatment enhanced the crystallinity of the thin films. The SEM surface micrographs show non-interconnected uniformly deposited fibre-like structures with approximate lengths between 400 and 1200 nm. The optical band gap energy roughly decreased from about 2.7 eV to about 2.2 eV with thermal treatment. The absorbance of the thin films annealed at 300 and 400 °C was as high as 90% in the visible region of the electromagnetic spectrum. These materials could be useful in solar thermal conversion processes.     

Influence of temperature annealing on optical properties of SrTiO3/BaTiO3 multilayered films on indium tin oxide

We have prepared SrTiO₃/BaTiO₃ thin films with multilayered structures deposited on indium tin oxide (ITO) coated glass by a sol-gel deposition and heating at 300-650 °C. The optical properties were obtained by UV-vis spectroscopy. The films show a high transmittance (approximately 85%) in the visible region. The optical band gap of the films is tunable in the 3.64-4.19 eV range by varying the annealing temperature. An abrupt decrease towards the bulk band gap value is observed at annealing temperatures above 600 °C. The multilayered film annealed at 650 ° C exhibited the maximum refractive index of 2.09-1.91 in the 450-750 nm wavelength range. The XRD and AFM results indicate that the films annealed above 600 ° C are substantially more crystalline than the films prepared at lower temperatures which were used to change their optical band gap and complex refractive index to an extent that depended on the annealing temperature.     

Structure and magnetic properties of γ′-Fe4N films grown on MgO-buffered Si (0 0 1)

γ′-Fe₄N thin films were grown on MgO-buffered Si (1 0 0) by pulsed laser deposition technique. Different crystallographic orientations and in-plane magnetic anisotropies were achieved by varying the growth temperature of the MgO buffer layer. When the MgO buffer layer was grown at room temperature, the γ′-Fe₄N film shows isotropic in-plane magnetic properties without obvious texture; while in-plane magnetic anisotropy was recorded for the γ′-Fe₄N films deposited on a 600 °C-grown-MgO buffer due to the formation of a (1 0 0)-oriented biaxial texture. Such a difference in in-plane magnetic anisotropy is attributed to the epitaxial growth of γ′-Fe₄N film on an MgO buffer with relaxed strain when the MgO layer was grown at a high temperature of 600 °C.     

CuInS2 thin films obtained through the annealing of chemically deposited In2S3-CuS thin films

In this work, we report the formation of CuInS₂ thin films on glass substrates by heating chemically deposited multilayers of copper sulfide (CuS) and indium sulfide (In₂S₃) at 300 and 350 °C in nitrogen atmosphere at 10 Torr. CIS thin films were prepared by varying the CuS layer thickness in the multilayers with indium sulfide. The XRD analysis showed that the crystallographic structure of the CuInS₂ (JCPDS 27-0159) is present on the deposited films. From the optical analysis it was estimated the band gap value for the CIS film (1.49 eV). The electrical conductivity varies from 3 × 10⁻⁸ to 3 Ω⁻¹ cm⁻¹ depending on the thickness of the CuS film. CIS films showed p-type conductivity.     

Preparation and characterization of iron oxide thin films by spray pyrolysis using methanolic and ethanolic solutions

Iron oxide thin films have been obtained by spray pyrolysis using 100% methanolic and ethanolic solutions of iron tri-chloride. The films were deposited onto ITO-coated glass substrates. The preparative conditions have been optimized to obtain compact, pin-hole-free and smooth thin films which are adherent to the substrate. The structural, morphological and compositional characterizations have been carried out by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray analysis. The films deposited using ethanolic solution results into pure hematite; α-Fe₂O₃ thin films, however, films deposited using methanolic solution consists of hematite and maghemite-c phases of iron oxide. The films are nanocrystalline with particle size of 30-40 nm. The optical absorbance of the film was of the order of 10⁵ cm⁻¹. The optical band gap of films was found to be 2.26 and 2.20 eV for the films deposited using methanolic and ethanolic solutions, respectively.     

Stress dependence of growth mode change of epitaxial layered cobaltite γ-Na0.7CoO2

We report stress dependence of growth characteristics of epitaxial γ-Na_0.7CoO₂ films on various substrates deposited by pulsed laser deposition method. On the sapphire substrate, the γ-Na_0.7CoO₂ thin film exhibits spiral surface growth with multi-terraces and highly crystallized texture. For the γ-Na_0.7CoO₂ thin film grown on the (1 1 1) SrTiO₃ substrate, the nano-islands of ∼30 nm diameter on the hexagonal grains are observed. These islands indicate that the growth mode changes from step-flow growth mode to Stranski-Krastanow (SK) growth mode. On the (1 1 1) MgO substrate, the large grains formed by excess adatoms covering an aperture between hexagonal grains are observed. These experimental demonstrations and controllability could provide opportunities of strain effects of Na_xCoO₂, physical properties of thin films, and growth dynamics of heterogeneous epitaxial thin films.     

Mg diffusion in K(Ta0.65Nb0.35)O3 thin films grown on MgO evidenced by Auger electron spectroscopy investigation

The diffusion of Mg in pulsed laser deposited K(Ta_0.65Nb_0.35)O₃ thin films epitaxially grown on (1 0 0) MgO single crystal substrate were investigated by Auger electron spectroscopy (AES). A diffusion of Mg from the substrate into the whole thickness (400 nm) of the as-deposited K(Ta_0.65Nb_0.35)O₃ films was observed with an accumulation of Mg at the surface. Ex situ post-annealing (750 °C/2 h) has led to a homogeneous distribution of Mg in all the ferroelectric coating. This strong reaction between film and substrate promotes a doping effect, responsible for the reduction of K(Ta_0.65Nb_0.35)O₃ dielectric losses in comparison with films grown on other substrates.     

Effect of temperature of annealing on optical, structural and electrochromic properties of sol-gel dip coated molybdenum oxide films

The sol-gel dip-coating method is used for the preparation of MoO₃ thin films. The 6 layered MoO₃ films were prepared and annealed at various temperatures in the range of 200-350 °C. The band gap value for MoO₃ films were calculated from optical absorption measurements and it is in the range of 3.55-3.73 eV. XRD spectrum reveals (0 2 0) is the major diffraction plane for the films prepared above 250 °C, which reveals the formation of MoO₃ in α-orthorhombic phase. The films prepared at 200 °C and 250 °C exhibits amorphous nature. The FTIR spectrum confirms the presence of Mo-O-Mo and MoO bonds. Nanorods were observed in the SEM images in the case of MoO₃ films prepared above 250 °C. The films prepared at 250 °C exhibit maximum anodic diffusion coefficient of 9.61 × 10⁻¹¹ cm²/s. The same film exhibits the change in optical transmission of 58.4% at 630 nm with the optical density of 0.80.     

Preparation and characterization of Mg-doped ZnO thin films by sol-gel method

Undoped and Mg-doped ZnO thin films were deposited on Si(1 0 0) and quartz substrates by the sol-gel method. The thin films were annealed at 873 K for 60 min. Microstructure, surface topography and optical properties of the thin films have been measured by X-ray diffraction (XRD), atomic force microscope (AFM), UV-vis spectrophotometer, and fluorophotometer (FL), respectively. The XRD results show that the polycrystalline with hexagonal wurtzite structure are observed for the ZnO thin film with Mg:Zn = 0.0, 0.02, and 0.04, while a secondary phase of MgO is evolved for the thin film with Mg:Zn = 0.08. The ZnO:Mg-2% thin film exhibits high c-axis preferred orientation. AFM studies reveal that rms roughness of the thin films changes from 7.89 nm to 16.9 nm with increasing Mg concentrations. PL spectra show that the UV-violet emission band around 386-402 nm and the blue emission peak about 460 nm are observed. The optical band gap calculated from absorption spectra and the resistivity of the ZnO thin films increase with increasing Mg concentration. In addition, the effects of Mg concentrations on microstructure, surface topography, PL spectra and electrical properties are discussed.     

Sputter deposition of high transparent TiO2−xNx/TiO2/ZnO layers on glass for development of photocatalytic self-cleaning application

In this study, TiO_2−xN_x/TiO₂ double layers thin film was deposited on ZnO (80 nm thickness)/soda-lime glass substrate by a dc reactive magnetron sputtering. The TiO₂ film was deposited under different total gas pressures of 1 Pa, 2 Pa, and 4 Pa with constant oxygen flow rate of 0.8 sccm. Then, the deposition was continued with various nitrogen flow rates of 0.4, 0.8, and 1.2 sccm in constant total gas pressure of 4 Pa. Post annealing was performed on as-deposited films at various annealing temperatures of 400, 500, and 600 °C in air atmosphere to achieve films crystallinity. The structure and morphology of deposited films were evaluated by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and atomic force microscopy (AFM). The chemical composition of top layer doped by nitrogen was evaluated by X-ray photoelectron spectroscopy (XPS). Photocatalytic activity of samples was measured by degradation of Methylene Blue (MB) dye. The optical transmittance of the multilayer film was also measured using ultraviolet-visible light (UV-vis) spectrophotometer. The results showed that by nitrogen doping of a fraction (∼1/5) of TiO₂ film thickness, the optical transmittance of TiO_2−xN_x/TiO₂ film was compared with TiO₂ thin film. Deposited films showed also good photocatalytic and hydrophilicity activity at visible light.     

Structure and photoluminescence properties of epitaxial SnO2 films grown on α-Al2O3 (0 1 2) by MOCVD

SnO₂ thin films have been successfully deposited on α-Al₂O₃ (0 1 2) substrates by metalorganic chemical vapor deposition (MOCVD) in the temperature range 500-700 °C. The films were epitaxially grown in the tetragonal SnO₂ phase and were (1 0 1) oriented. In-plane orientation relationship [0 1 0]SnO₂||[1 0 0]Al₂O₃ and [1 0 1?]SnO₂||[1? 2? 1]Al₂O₃ was determined between the film and substrate. Photoluminescence (PL) spectra measured at room temperature revealed that the film grown at 700 °C showed an intense ultra-violet (UV) PL peak at 333 nm, which was a band-edge emission peak in SnO₂ films. At a temperature of 13 K, a new broad PL band centered at about 480 nm was observed. The corresponding PL mechanisms are discussed in detail.