Preparation of photocatalytic Fe2O3-TiO2 coatings in one step by metal organic chemical vapor deposition

There are two major difficulties in the TiO₂ liquid-solid photocatalytic system: effective immobilization of the TiO₂ particles; and improving the catalytic activity under visible light. To simultaneously solve these two problems, Fe₂O₃-TiO₂ coatings supported on activated carbon fiber (ACF), have been prepared in one step by a convenient and efficient method—metal organic chemical vapor deposition (MOCVD). XRD results revealed that Fe₂O₃-TiO₂ coatings mainly composed of anatase TiO₂, α-Fe₂O₃ phases and little Fe₂Ti₃O₉. The pore structure of ACF was preserved well after loading with Fe₂O₃-TiO₂ coatings. UV-vis diffuse reflectance spectra showed a slight shift to longer wavelengths and an enhancement of the absorption in the visible region for Fe₂O₃-TiO₂ coatings, compared to the pure TiO₂ sample. A moderate Fe₂O₃-TiO₂ loading (13.7 wt%) was beneficial to mineralizing wastewater because the intermediates could be adsorbed onto the surface of photocatalyst following decomposition. The stable performance revealed that the Fe₂O₃-TiO₂ coatings were strongly adhered to the ACF surface, and the as prepared catalysts could be reused showing potential application for wastewater treatment.     

Strongly interacting superspins in Fe3O4 nanoparticles

In this paper we report structural and magnetic properties of Fe₃O₄ nanoparticles synthesized by thermal decomposition of ball milled iron nitrate and citric acid in N₂ and air ambient. The XRD pattern of samples which are prepared in air shows some impurity phases, while the samples synthesized in the N₂ atmosphere are almost pure Fe₃O₄ phase. The result shows that by increasing the particle size, the magnetization of the samples increases. The increase of magnetization by increasing the particle size could be attributed to the lower surface spin canting and surface spin disorder of the larger magnetic nanoparticles. The results of ac magnetic susceptibility measurements show that the susceptibility data are not in accordance with the Néel -Brown model for superparamagnetic relaxation, but fit well with conventional critical slowing down model which indicates that the dipole-dipole interactions are strong enough to cause superspin-glass like phase in these samples.     

Green synthesis of soya bean sprouts-mediated superparamagnetic Fe3O4 nanoparticles

Superparamagnetic Fe₃O₄ nanoparticles were first synthesized via soya bean sprouts (SBS) templates under ambient temperature and normal atmosphere. The reaction process was simple, eco-friendly, and convenient to handle. The morphology and crystalline phase of the nanoparticles were determined from scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray diffraction (XRD) spectra. The effect of SBS template on the formation of Fe₃O₄ nanoparticles was investigated using X-ray photoemission spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FT-IR). The results indicate that spherical Fe₃O₄ nanoparticles with an average diameter of 8 nm simultaneously formed on the epidermal surface and the interior stem wall of SBS. The SBS are responsible for size and morphology control during the whole formation of Fe₃O₄ nanoparticles. In addition, the superconducting quantum interference device (SQUID) results indicate the products are superparamagnetic at room temperature, with blocking temperature (T_B) of 150 K and saturation magnetization of 37.1 emu/g.     

Microwave synthesis of magnetic Fe3O4 nanoparticles used as a precursor of nanocomposites and ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the surface of particles are presented in the present investigation. Fe₃O₄ magnetic nanoparticles were prepared by the co-precipitation of Fe³⁺ and Fe²⁺, NH₃·H₂O was used as the precipitating agent to adjust the pH value, and the aging of Fe₃O₄ magnetic nanoparticles was accelerated by microwave (MW) irradiation. The obtained Fe₃O₄ magnetic nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). The average size of Fe₃O₄ crystallites was found to be around 8–9 nm. Thereafter, the surface of Fe₃O₄ magnetic nanoparticles was modified by stearic acid. The resultant sample was characterized by FT-IR, scanning electron microscopy (SEM), XRD, lipophilic degree (LD) and sedimentation test. The FT-IR results indicated that a covalent bond was formed by chemical reaction between the hydroxyl groups on the surface of Fe₃O₄ nanoparticles and carboxyl groups of stearic acid, which changed the polarity of Fe₃O₄ nanoparticles. The dispersion of Fe₃O₄ in organic solvent was greatly improved. Effects of reaction time, reaction temperature and concentration of stearic acid on particle surface modification were investigated. In addition, Fe₃O₄/polystyrene (PS) nanocomposite was synthesized by adding surface modified Fe₃O₄ magnetic nanoparticles into styrene monomer, followed by the radical polymerization. The obtained nanocomposite was tested by thermogravimetry (TG), differential scanning calorimetry (DSC) and XRD. Results revealed that the thermal stability of PS was not significantly changed after adding Fe₃O₄ nanoparticles. The Fe₃O₄ magnetic fluid was characterized using UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the magnetic fluid had excellent stability, and had susceptibility of 4.46×10⁻⁸ and saturated magnetization of 6.56 emu/g. In addition, the mean size d (0.99) of magnetic Fe₃O₄ nanoparticles in the fluid was 36.19 nm.     

Synthesis and characterization of TiO2/Fe2O3 core-shell nanocomposition film and their photoelectrochemical property

TiO₂/Fe₂O₃ core-shell nanocomposition film has been fabricated via two-step method. TiO₂ nanorod arrays are synthesized by a facile hydrothermal method, and followed by Fe₂O₃ nanoparticles deposited on TiO₂ nanorod arrays through an ordinary chemical bath deposition. The phase structures, morphologies, particle size, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and ultraviolet-visible (UV-vis) spectrophotometer. The results confirm that Fe₂O₃ nanoparticles of mean size ca. 10 nm coated on the surface of TiO2 NRs. After depositing Fe₂O₃, UV-vis absorption property is induces the shift to the visible-light range, the annealing temperature of 600 °C is the best condition for UV-vis absorption property of TiO₂/Fe₂O₃ nanocomposite film, and increasing Fe content, optical activity are enhanced one by one. The photoelectrochemical (PEC) performances of the as-prepared composite nanorods are determined by measuring the photo-generated currents under illumination of UV-vis light. The TiO₂ NRs modified by Fe₂O₃ show the photocurrent value of 1.36 mA/cm² at 0 V vs Ag/AgCl, which is higher than those of unmodified TiO₂ NRs.     

Fabrication, characterization and photoelectrochemical properties of Fe2O3 modified TiO2 nanotube arrays

TiO₂ nanotube (NT) arrays modified by Fe₂O₃ with high sensibility in the visible spectrum were first prepared by annealing anodic titania NTs pre-loaded with Fe(OH)₃ which was uniformly clung to the titania NTs using sequential chemical bath deposition (S-CBD). The photoelectrochemical performances of the as-prepared composite nanotubes were determined by measuring the photo-generated currents and voltages under illumination of UV-vis light. The titania NTs modified by Fe₂O₃ showed higher photopotential and photocurrent values than those of unmodified titania NTs. The enhanced photoelectrochemical behaviors can be attributed to the modified Fe₂O₃ which increases the probability of charge-carrier separation and extends the range of the TiO₂ photoresponse from ultraviolet (UV) to visible region due to the low band gap of 2.2 eV of Fe₂O₃.     

Preparation and characterization of visible light responsive Fe2O3-TiO2 composites

In this study we present the effects of iron oxide (Fe₂O₃) on titanium dioxide (TiO₂) in synthesising visible-light reactive photocatalysts. A Fe₂O₃-TiO₂ composite photocatalyst was synthesized from Fe₂(SO₄)₃ and Ti(SO₄)₂ by a ethanol-assisted hydrothermal method. The preparation conditions were optimized through the investigation of the effects of hydrothermal temperature and time as well as molar ratio of Ti to Fe on the photocatalytic activity. The visual, physical and chemical properties of the Fe₂O₃-TiO₂ composites were investigated. The results showed that α-Fe₂O₃ and anatase TiO₂ were present in the composites. The Fe₂O₃-TiO₂ synthesized under optimum condition consisted of mesoporous structure with an average pore size of 4 nm and a surface area of 43 m²/g. Under visible and solar light irradiation, the photocatalytic activity of optimized sample was significantly higher than that of pure TiO₂. This sample led to a photodegradation efficiency of 90% and 40% of auramine under visible light and solar light, respectively.     

MoO3/Al2O3催化剂中Mo分散的正电子研究

用浸渍法制备了一系列不同Mo含量的MoO₃/Al₂O₃催化剂.测量了这些样品的正电子湮没寿命谱(PALS)与符合多普勒展宽(CDB)谱,以研究其孔洞结构以及Mo分散.正电子寿命测量结果表明,Al₂O₃载体中存在两种不同尺寸的孔洞.掺入MoO₃之后,Mo原子主要进入Al₂O₃的大孔中,使孔洞体积减小.符合多普勒展宽谱结果表明,当MoO 关键词： 3/Al₂O₃催化剂')" href="#">MoO₃/Al₂O₃催化剂 正电子湮没寿命谱 符合多普勒展宽 Mo 分散     

海藻酸改性的空心Fe3O4纳米颗粒的制备与应用

不使用任何模板一步制得空心Fe₃O₄纳米颗粒,然后将海藻酸钠嫁接在氨基化的空心Fe₃O₄表面,再利用海藻酸盐与钙离子的作用,在空心Fe₃O₄表面形成一个凝胶化层,制得海藻酸盐凝胶化的空心Fe₃O₄纳米颗粒,粒径约为400～500 nm．采用TEM、XRD、XPS、VSM等手段对纳米微球进行表征．VSM表征结果表明在室温下样品磁性材料为超顺磁性．改性Fe₃O₄纳米颗粒成功地用于柔红霉素的载负和缓释,最大载负率和载药量分别为28.4%和14.2%．缓释结果表明,海藻酸盐凝胶化层的存在,能更有效控制柔红霉素缓慢地释放．     

Chemical quenching of positronium in Fe2O3/Al2O3 catalysts

Fe₂O₃/Al₂O₃ catalysts were prepared by solid state reaction method using α-Fe₂O₃ and γ-Al₂O₃ nano powders. The microstructure and surface properties of the catalyst were studied using positron lifetime and coincidence Doppler broadening annihilation radiation measurements. The positron lifetime spectrum shows four components. The two long lifetimes τ₃ and τ₄ are attributed to positronium annihilation in two types of pores distributed inside Al₂O₃ grain and between the grains, respectively. With increasing Fe₂O₃ content from 3 wt% to 40 wt%, the lifetime τ₃ keeps nearly unchanged, while the longest lifetime τ₄ shows decrease from 96 ns to 64 ns. Its intensity decreases drastically from 24% to less than 8%. The Doppler broadening S parameter shows also a continuous decrease. Further analysis of the Doppler broadening spectra reveals a decrease in the p-Ps intensity with increasing Fe₂O₃ content, which rules out the possibility of spin-conversion of positronium. Therefore the decrease of τ₄ is most probably due to the chemical quenching reaction of positronium with Fe ions on the surface of the large pores.     

Biosynthesis and magnetic properties of mesoporous Fe3O4 composites

Magnetic Fe₃O₄ materials with mesoporous structure are synthesized by co-precipitation method using yeast cells as a template. The X-ray diffraction (XRD) pattern indicates that the as-synthesized mesoporous hybrid Fe₃O₄ is well crystallized. The Barrett-Joyner-Halenda (BJH) models reveal the existence of mesostructure in the dried sample which has a specific surface area of 96.31 m²/g and a pore size distribution of 8-14 nm. Transmission electron microscopy (TEM) measurements confirm the wormhole-like structure of the resulting samples. The composition and chemical bonds of the Fe₃O₄/cells composites are studied by Fourier transform infrared (FT-IR) spectroscopy. Preliminary magnetic properties of the mesoporous hybrid Fe₃O₄ are characterized by a vibrating sample magnetometer (VSM). The magnetic Fe₃O₄/cells composites with mesoporous structure have potential applications in biomedical areas, such as drug delivery.     

Mechanism of amorphous Ge2Sb2Te5 removal during chemical mechanical planarization in acidic H2O2 slurry

In this paper, chemical mechanical planarization (CMP) of amorphous Ge2Sb2Te5 (a-GST) in acidic H2O2 slurry is investigated. It was found that the removal rate of a-GST is strongly dependent on H2O2 concentration and gradually increases with the increase in H2O2 concentration, but the static etch rate first increases and then slowly decreases with the increase in H2O2 concentration. To understand the chemical reaction behavior of H2O2 on the a-GST surface, the potentiodynamic polarization curve, surface morphology and cross-section of a-GST immersed in acidic slurry are measured and the results reveal that a-GST exhibits a from active to passive behavior for from low to high concentration of H2O2 . Finally, a possible removal mechanism of a-GST in different concentrations of H2O2 in the acidic slurry is described.     

Cocktail effect of Fe2O3 and TiO2 semiconductors for a high performance dye-sensitized solar cell

The bi-semiconductors of TiO₂ and Fe₂O₃ were used as a photoelectrode material in a high performance dye-sensitized solar cell due to cocktail effects from the two conduction bands. The size of the semiconductors was reduced by using a paint shaker to enlarge the contact area of the semiconductor with the dye or electrolyte. The fill factor and the efficiency of the prepared dye-sensitized solar cell were improved by over 16% and 300%, respectively; these parameters were measured from a current-voltage curve that was based on the effects of the Fe₂O₃ co-semiconductor and the size reduction. A mechanism is suggested wherein the conduction band of Fe₂O₃ works to prohibit the trapping effects of electrons in the conduction band of TiO₂. This result is attributed to the prevention of electron recombination between electrons in the TiO₂ conduction band with dye or electrolytes. The mechanism is suggested based on impedance results, which indicate improved electron transport at the interface of the TiO₂/dye/electrolyte.     

Effect of Li2O and CoO-doping of CuO/Fe2O3 system on its surface and catalytic properties

Physicochemical, surface and catalytic properties of pure and doped CuO/Fe₂O₃ system were investigated using X-ray diffraction (XRD), energy dispersive X-ray analysis (EDX), nitrogen adsorption at −196 °C and CO-oxidation by O₂ at 80-220 °C using a static method. The dopants were Li₂O (2.5 mol%) and CoO (2.5 and 5 mol%). The results revealed that the increase in precalcination temperature from 400 to 600 °C and Li₂O-doping of CuO/Fe₂O₃ system enhanced CuFe₂O₄ formation. However, heating both pure and doped solids at 600 °C did not lead to complete conversion of reacting oxides into CuFe₂O₄. The promotion effect of Li₂O dopant was attributed to dissolution of some of dopant ions in the lattices of CuO and Fe₂O₃ with subsequent increase in the mobility of reacting cations. CoO-doping led also to the formation of mixed ferrite Co_xCu_1−xFe₂O₄. The doping process of the system investigated decreased to a large extent the crystallite size of unreacted portion of Fe₂O₃ in mixed solids calcined at 600 °C. This process led to a significant increase in the S_BET of the treated solids. Doping CuO/Fe₂O₃ system with either Li₂O or CoO, followed by calcination at 400 and 600 °C decreased its catalytic activity in CO-oxidation by O₂. However, the activation energy of the catalyzed reaction was not much affected by doping.     

Fabrication of flower-shaped Bi2O3 superstructure by a facile template-free process

A novel flower-shaped Bi₂O₃ superstructure has been successfully synthesized by calcination of the precursor, which was prepared via a citric acid assisted hydrothermal process. The precursor and Bi₂O₃ were characterized with respect to morphology, crystal structure and elemental chemical state by field-emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). It was shown that both the precursor and Bi₂O₃ flower-shaped superstructure were constructed of numerous nanosheets while the nanosheets consisted of a great deal of nanoparticles. Furthermore, key factors for the formation of the superstructures have been proposed; a mechanism for the growth of the superstructure has been presented based on the FESEM investigation of different growth stages.     

钴改性Fe3O4-MnO2催化转化生物质合成气制备液体燃料

本文制备了用于费托合成反应的钴改性Fe₃O₄-MnO₂双功能催化剂,并探究了钴负载量对Fe-Co协同效应的影响以及Fe₁Co_xMn₁催化剂的费托合成反应性能. 实验发现,在Fe₃O₄-Mn催化剂中加入Co可促进铁氧化物的还原、增加反应过程中铁位点的活性. 此外,Co的加入可增强Fe-Co金属间的电子转移,加强两者的协同作用,提高催化性能. Co负载较高的Fe₁Co_xMn₁催化剂可进一步促进加氢反应能力,使产品分布向短链烃方向转移. 在280 ^°C、2.0 MPa和3000 h^-1的最佳工况条件下,Fe₁Co₁Mn₁催化剂的液体燃料收率最高.     

Silane treatment of Fe3O4 and its effect on the magnetic and wear properties of Fe3O4/epoxy nanocomposites

In this study, the effect of silane treatment of Fe₃O₄ on the magnetic and wear properties of Fe₃O₄/epoxy nanocomposites was investigated. Fe₃O₄ nanopowders were prepared by coprecipitation of iron(II) chloride tetrahydrate with iron(III) chloride hexahydrate, and the surfaces of Fe₃O₄ were modified with 3-aminopropyltriethoxysilane. The magnetic properties of the powders were measured on unmodified and surface-modified Fe₃O₄/epoxy nanocomposites using SQUID magnetometer. Wear tests were performed on unmodified and surface-modified Fe₃O₄/epoxy nanocomposites under the same conditions (sliding speed: 0.18 m/s, load: 20 N).The results showed that the saturation magnetization (M_s) of surface-modified Fe₃O₄/epoxy nanocomposites was approximately 110% greater than that of unmodified Fe₃O₄/epoxy nanocomposites. This showed that the specific wear rate of surface-modified Fe₃O₄/epoxy nanocomposites was lower than that of unmodified Fe₃O₄/epoxy nanocomposites. The decrease in wear rate and the increase in magnetic properties of surface-modified Fe₃O₄/epoxy nanocomposites occurred due to the improved dispersion of Fe₃O₄ into the epoxy matrix.     

Ni与Co掺杂Fe2O3（0001）表面增强析氧反应活性

Fe based oxides are considered as a promising catalyst for the oxygen evolution reaction (OER) due to their low cost and high stability. Here, based on density functional theory calculations, the electrocatalytic behaviors of pure and metal (Ni, Co) doped Fe-terminated Fe₂O₃(0001) are investigated. The potential-limiting step for OER is determined as the formation of O^* by dehydrogenating surface hydroxyl and it is suggested that the doping enhances the catalytic activity of Fe₂O₃(0001) by reducing the free energy change of rate limiting step on doped Ni or Co atom. Especially, the calculated over-potential of Co-doped Fe₂O₃ (0001) surface is about 0.63 eV on Co site, which is comparable with the theoretical over-potential of 0.56 eV for RuO₂.     

High heat generation ability in AC magnetic field for nano-sized magnetic Y3Fe5O12 powder prepared by bead milling

Nano-sized magnetic Y₃Fe₅O₁₂ ferrite having a high heat generation ability in an AC magnetic field was prepared by bead milling. A commercial powder sample (non-milled sample) of ca. 2.9 μm in particle size did not show any temperature enhancement in the AC magnetic field. The heat generation ability in the AC magnetic field improved with a decrease in the average crystallite size for the bead-milled Y₃Fe₅O₁₂ ferrites. The highest heat ability in the AC magnetic field was for the fine Y₃Fe₅O₁₂ powder with a 15-nm crystallite size (the samples were milled for 4 h using 0.1 mm? beads). The heat generation ability of the excessively milled Y₃Fe₅O₁₂ samples decreased. The main reason for the high heat generation property of the milled samples was ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability was not influenced by the concentration of the ferrite powder. For the samples milled for 4 h using 0.1 mm? beads, the heat generation ability (W g⁻¹) was estimated using a 3.58×10⁻⁴ fH² frequency (f/kHz) and the magnetic field (H/kA m⁻¹), which is the highest reported value of superparamagnetic materials.     

Positive and negative magnetoresistance in Fe3O4-based heterostructures

Fe₃O₄-based heterostructures, including Fe₃O₄/MgO/Fe₃O₄, Fe₃O₄/MgO/Si and Fe₃O₄/SiO₂/Si, were fabricated by magnetron sputtering to investigate the perpendicular-to-plane magneto-transport properties. In the Fe₃O₄/MgO/Fe₃O₄ and Fe₃O₄/MgO/Si heterostructures, the typical magneto-transport properties of single Fe₃O₄ films, such as negative magnetoresistance (MR) and extreme values of MR−T curves at 120 K, were observed, suggesting that the spin polarization of conducting electrons conserves through MgO barrier. MR in the Fe₃O₄/MgO/Fe₃O₄ heterostructure is larger than that in the Fe₃O₄/MgO/Si heterostructure, because the spin of electrons is disturbed in the depletion layer of Si and the SiO₂ layer introduced by Fe₃O₄/MgO growth. The Fe₃O₄/SiO₂/Si heterostructure has a positive MR of 2% at 120 K, which may originate from the scattering of conducting electrons in amorphous SiO₂ and the spin polarization reversal at the Fe₃O₄/SiO₂ interface.