The synthesis and kinetic growth of anisotropic silver particles loaded on TiO2 surface by photoelectrochemical reduction method

Silver nanorods with average diameters of 120-230 nm and aspect ratio of 1.7-5.0 were deposited on the surface of TiO₂ films by photoelectrochemical reduction of Ag⁺ to Ag under UV light. The composite films prepared on soda-lime glass substrates were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The results show that the TiO₂ film after UV irradiation in AgNO₃ solution is composed of anatase phase TiO₂ and metallic silver with face centered cubic structure. Other compounds cannot be found in the final films. The maximum deposition content of silver particles on the surface of TiO₂ film was obtained with the AgNO₃ concentration of 0.1 M. The kinetic growth rates of silver particles can be controlled by photocatalytic activity of TiO₂ films. The studies suggest that the growth rates of silver particles increase with the enhancement of photocatalytic activity of TiO₂ films. The maximum growth rate of silver particles loaded on TiO₂ films can be up to 0.353 nm min⁻¹ among samples 1#, 2# and 3#, while the corresponding apparent rate constant of TiO₂ is 1.751 × 10⁻³ min⁻¹.     

Structural, optical and electrochemical properties of TiO2 thin films grown by APCVD method

Atmospheric pressure chemical vapor deposition (APCVD) of TiO₂ thin films has been achieved onto glass and onto ITO-coated glass substrates, from the reaction of TiCl₄ with ethyl acetate (EtOAc). The effect of the synthesis temperature on the optical, structural and electrochemical properties was studied through spectral transmittance, X-ray diffraction (XRD) and electrochemical impedance spectroscopy (EIS) measurements. It was established that the TiO₂ films deposited onto glass substrate, at temperatures greater than 400 °C grown with rutile type tetragonal structure, whereas the TiO₂ films deposited onto ITO-coated glass substrate grown with anatase type structure. EIS was applied as suitable method to determine the charge transfer resistance in the electrolyte/TiO₂ interface, typically found in dye-sensitized solar cells.     

Transparent nano composite PVA–TiO2 and PMMA–TiO2 thin films: Optical and dielectric properties

Transparent nano composite PVA–TiO₂ and PMMA–TiO₂ thin films were prepared by an easy and cost effective dip coating method. Al/PVA–TiO₂/Al and Al/PMMA–TiO₂/Al sandwich structures were prepared to study the dielectric behavior. The presence of metal–oxide (Ti–O) bond in the prepared films was confirmed by Fourier transform infrared spectroscopy. X-ray diffraction pattern indicated that the prepared films were predominantly amorphous in nature. Scanning electron micrographs showed cluster of TiO₂ nanoparticles distributed over the film surface and also there were no cracks and pin holes on the surface. The transmittance of the films was above 80% in the visible region and the optical band gap was estimated to be about 3.77 eV and 3.78 eV respectively for PVA–TiO₂ and PMMA–TiO₂ films by using Tauc's plot. The determined refractive index (n) values were between 1.6 and 2.3. High value of dielectric constant (?′ = 24.6 and ?′ = 26.8) was obtained for the prepared composite films. The conduction in the composite films was found to be due to electrons. The observed amorphous structure, good optical properties and dielectric behavior of the prepared nano composite thin films indicated that these films could be used in opto-electronic devices and in thin film transistors.     

The enhanced conductivity and stability of AZO thin films with a TiO2 buffer layer

Aluminum doped zinc oxide (AZO) films were substitutes of the SnO₂:F films on soda lime glass substrate in the amorphous thin-film solar cells due to good properties and low cost. In order to improve properties of AZO films, the TiO₂ buffer layer had been introduced. AZO films with and without TiO₂ buffer layer were deposited on soda lime glass substrates by r.f. magnetron sputtering. Subsequently, one group samples were annealed in vacuum (0.1 Pa) at 500 °C for 120 s using the RTA system, and the influence of TiO₂ thickness on the properties of AZO films had been discussed. The XRD measurement results showed that all the films had a preferentially oriented (0 0 2) peak, and the intensity of (0 0 2) peak had been enhanced for the AZO films with TiO₂ buffer layer. The resistivity of TiO₂ (3.0 nm)/AZO double-layer film is 4.76×10⁻⁴ Ω cm with the maximum figure merit of 1.92×10⁻² Ω⁻¹, and the resistivity has a remarkable 28.7% decrease comparing with that of the single AZO film. The carrier scattering mechanism of TiO₂ (3.0 nm)/AZO double-layer film had been described by Hall measurement in different temperatures. The average transmittance of all the films exceeded 92% in the visible spectrum. Another group samples were heat treated in the quartz tube in air atmosphere, and the effect of TiO₂ thickness on thermal stability of AZO films had been discussed.     

The photocatalytic application and regeneration of anatase thin films with embedded commercial TiO2 particles deposited on glass microrods

Anatase thin films (<200 nm in thickness) embedding Degussa P25 TiO₂ were prepared by sol-gel method. TiO₂-anatase thin films were deposited on a fiberglass substrate and then ground to obtain glass microrods containing the composite films. The film structure was characterized using Raman spectroscopy, atomic absorption and UV-vis spectrophotometry, and atomic force microscopy. The photocatalytic activity of the composite films, calcined at 450 °C, and the regeneration of the activity under the same experimental conditions, were assessed using gas chromatography to study the photodegradation of phenol, an industrial pollutant, in water under 365 nm irradiation. The film with 15.0 wt.% of P25 TiO₂ was found to be more photoactive (54 ppm of degraded phenol at 6 h of illumination) than the other ones.     

Optical properties of ITO/TiO2 single and double layer thin films deposited by RPLAD

Indium tin oxide (ITO) and titanium dioxide (TiO₂) single layer and double layer ITO/TiO₂ films were prepared using reactive pulsed laser ablation deposition (RPLAD) with an ArF excimer laser for applications in dye-sensitized solar cells (DSSCs). The films were deposited on SiO₂ substrates either at room temperatures (RT) or heated to 200-400 °C. Under optimized conditions, transmission of ITO films in the visible (vis) range was above 89% for films produced at RT and 93% for the ones deposited at higher temperatures. Increasing the substrate temperature from RT to 400 °C enhances the transmission of TiO₂ films in the vis-NIR from about 70% to 92%. High transmission (≈90%) was observed for the double layer ITO/TiO₂ with a transmission cut-off above 900 nm. From the transmission data, the energies gaps (E_g), as well as the refractive indexes (n) for the films were estimated. n ≈ 2.03 and 2.04, respectively for ITO films and TiO₂ film deposited at 400 °C in the visible region. Post-annealing of the TiO₂ films for 3 h at 300 and 500 °C was performed to enhance n. The refractive index of the TiO₂ films increases with the post-annealing temperature. The direct band gap is 3.6, 3.74 and 3.82 eV for ITO films deposited at RT, 200, and 400 °C, respectively. The TiO₂ films present a direct band gap of 3.51 and 3.37 eV for as deposited TiO₂ films and when annealed at 400 °C, respectively. There is a shift of about 0.1 eV between ITO and ITO/TiO₂ films deposited at 200 °C. The shift decreases by half when the TiO₂ film was deposited at 400 °C. Post-annealing was also performed on double layer ITO/TiO₂.     

Surface effect of natural zeolite (clinoptilolite) on the photocatalytic activity of TiO2

The surface interaction between TiO₂ and natural zeolite, clinoptilolite, has been investigated by means of transmission electron microscope (TEM), atom force microscope (AFM), X-ray diffractometer (XRD), diffuse reflectance infrared Fourier transform (DRIFT) and far Fourier transform infrared ray (FTIR) spectroscopy. And the photocatalytic degradation (PCD) rate of methyl orange (MO), a model of recalcitrant azo dye, in aqueous system has been measured to compare the photocatalytic activities of different photocatalysts. A model has been carried out to explain the incorporation between TiO₂ particles and natural zeolite. The results show that the TiO₂ particles loaded on zeolite are 50 nm or so, smaller than the pure one, and combine with zeolite via chemical force. Since the reserved adsorption ability and the existence of electron trapper, the TiO₂-zeolite performed more efficient at low initial concentration and in the later period of PCD process, as compared with pure TiO₂ nanopowders.     

IR and XPS investigation of visible-light photocatalysis—Nitrogen-carbon-doped TiO2 film

To use solar irradiation or interior lighting efficiently, we sought a photocatalyst with high reactivity under visible light. Nitrogen and carbon doping TiO_2−x−yN_xC_y films were obtained by heating the TiO₂ gel in an ionized N₂ gas and then were calcined at 500 °C. The TiO_2−x−yN_xC_y films have revealed an improvement over the TiO₂ films under visible light (wavelength, 500 nm) in optical absorption and photocatalytic activity such as photodegradation of methyl orange. X-ray photoemission spectroscopy, infrared spectrum and UV-visible (UV-vis) spectroscopy were used to find the difference of two kinds of films. Nitrogen and carbon doped into substitutional sites of TiO₂ has been proven to be indispensable for band-gap narrowing and photocatalytic activity.     

Sputter deposition of high transparent TiO2−xNx/TiO2/ZnO layers on glass for development of photocatalytic self-cleaning application

In this study, TiO_2−xN_x/TiO₂ double layers thin film was deposited on ZnO (80 nm thickness)/soda-lime glass substrate by a dc reactive magnetron sputtering. The TiO₂ film was deposited under different total gas pressures of 1 Pa, 2 Pa, and 4 Pa with constant oxygen flow rate of 0.8 sccm. Then, the deposition was continued with various nitrogen flow rates of 0.4, 0.8, and 1.2 sccm in constant total gas pressure of 4 Pa. Post annealing was performed on as-deposited films at various annealing temperatures of 400, 500, and 600 °C in air atmosphere to achieve films crystallinity. The structure and morphology of deposited films were evaluated by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and atomic force microscopy (AFM). The chemical composition of top layer doped by nitrogen was evaluated by X-ray photoelectron spectroscopy (XPS). Photocatalytic activity of samples was measured by degradation of Methylene Blue (MB) dye. The optical transmittance of the multilayer film was also measured using ultraviolet-visible light (UV-vis) spectrophotometer. The results showed that by nitrogen doping of a fraction (∼1/5) of TiO₂ film thickness, the optical transmittance of TiO_2−xN_x/TiO₂ film was compared with TiO₂ thin film. Deposited films showed also good photocatalytic and hydrophilicity activity at visible light.     

Low temperature synthesis of iodine-doped TiO2 nanocrystallites with enhanced visible-induced photocatalytic activity

Iodine-doped TiO₂ nanocrystallites (denoted as I-TNCs) were prepared via a newly developed triblock copolymer-mediated sol-gel method at a temperature of 393 K. I-doping, crystallization and the formation of porous structure have been simultaneously achieved. The obtained particles were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and UV-vis spectrophotometer. The results indicated that the as-prepared I-TNCs possessed a diameter of ca. 5 nm with anatase crystalline structure and a specific surface area of over 200 m² g⁻¹. The presence of iodine expanded the photoresponse in visible light range, and led to enrich in surface hydroxyl group on the TiO₂ surface. Compared with the commercial photocatalyst P25, the I-TNCs significantly enhanced the photocatalytic efficiency in the degradation of rhodamine B and 2,4-dichlorophenol, and the I-TNCs with 2.5 mol% doping ratio exhibited the best photocatalytic activity.     

Study on the properties and charge generation in dye-sensitized n-TiO2|dye|p-CuI solid state photovoltaic solar cells

Transparent semiconducting copper iodide (CuI) films were prepared by XeCl Excimer laser and their characteristics are investigated. These films exhibited optical transmittance over 80% in the wavelength range from 400 to 900 nm and minimum resistivity of about 2 kΩ cm⁻¹. The optical absorption of the these films shows a remarkable blue shift compared to that of polycrystalline of CuI, which can be explained from the viewpoint formation of ultra fine of CuI grains. The titanium dioxide (TiO₂) films have been prepared by sol-gel method. The properties of pulsed laser deposited CuI and TiO₂ films in power output of n-TiO₂|dye|p-CuI cells is studied. An efficient charge generation is observed through the illumination of TiO₂ layer of the fabricated n-TiO₂|dye|p-CuI solid state photovoltaic solar cells. From the current-voltage characteristics, the fill factor and power conversion efficiency were about of 45 and 3%, respectively. The maximum photo-current of about 12.5 mA/cm² and photo-voltage of 475 mV under AM 1.5 conditions were obtained for the n-TiO₂|dye|p-CuI solid states photovoltaic solar cells with good reproducibility. Adsorbed dye molecules to the TiO₂ surface act as a relay, especially under illumination through TiO₂ layer in the wave range region of 300-400 nm.     

Synthesis and characterization of hydroxyapatite/titania nanocomposites using in situ precipitation technique

Hydroxyapatite/titania nanocomposites were successfully synthesized by in situ precipitation of precursor matters from hydroxyapatite and titania at 70 °C with different hydroxyapatite/titania ratios. X-ray diffraction, Fourier transform infrared spectroscopy, Brunauer–Emmett–Teller surface, scanning and transmission electron microscopes were employed to characterize the prepared nanocomposite powders. X-ray diffraction results indicated that hydroxyapatite and anatase (TiO₂) were the major crystalline phases. By increasing the amount of titania nano-particles, Fourier transform infrared spectroscopy revealed that (PO₄)³⁻ bands at 567, 1033 cm⁻¹ decreased. Brunauer–Emmett–Teller surface results also showed a reduction in surface areas of nanocomposites. Transmission electron microscope observations revealed that the aspect ratio of hydroxyapatite/TiO₂ nanocrystals increased by increasing TiO₂ proportion in nanocomposites. The observed nanorod crystals tended to thin, elongated and plate-like in shape.     

Enhanced photocatalytic activity of TiO2 nano-structured thin film with a silver hierarchical configuration

TiO₂ sol-gels with various Ag/TiO₂ molar ratios from 0 to 0.9% were used to fabricate silver-modified nano-structured TiO₂ thin films using a layer-by-layer dip-coating (LLDC) technique. This technique allows obtaining TiO₂ nano-structured thin films with a silver hierarchical configuration. The coating of pure TiO₂ sol-gel and Ag-modified sol-gel was marked as T and A, respectively. According to the coating order and the nature of the TiO₂ sol-gel, four types of the TiO₂ thin films were constructed, and marked as AT (bottom layer was Ag modified, surface layer was pure TiO₂), TA (bottom layer was pure TiO₂, surface layer was Ag modified), TT (pure TiO₂ thin film) and AA (TiO₂ thin film was uniformly Ag modified). These thin films were characterized by means of linear sweep voltammetry (LSV), X-ray diffraction (XRD), scanning electron microscopy (SEM), electrochemical impedance spectroscopy and transient photocurrent (I_ph). LSV confirmed the existence of Ag⁰ state in the TiO₂ thin film. SEM and XRD experiments indicated that the sizes of the TiO₂ nanoparticles of the resulting films were in the order of TT > AT > TA > AA, suggesting the gradient Ag distribution in the films. The SEM and XRD results also confirmed that Ag had an inhibition effect on the size growth of anatase nanoparticles. Photocatalytic activities of the resulting thin films were also evaluated in the photocatalytic degradation process of methyl orange. The preliminary results demonstrated the sequence of the photocatalytic activity of the resulting films was AT > TA > AA > TT. This suggested that the silver hierarchical configuration can be used to improve the photocatalytic activity of TiO₂ thin film.     

N-doped TiO2 photo-catalyst for the degradation of 1,2-dichloroethane under fluorescent light

The photo-catalytic degradation of 1,2-dichloroethane (1, 2-DCE) using nitrogen-doped TiO₂ photo-catalysts under fluorescent light irradiation was investigated. Highly pure TiO₂ and nitrogen-doped TiO₂ were prepared by a sol-gel method and characterized by thermo-gravimetric/differential-thermal analysis (TG/DTA), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared (FTIR) spectroscopy. The results indicate that the photo-catalysts were mainly nano-size with an anatase-phase structure. The degradation reaction of 1,2-DCE was operated under visible-light irradiation, and the photo-catalytic oxidation was conducted in a batch photo-reactor with various nitrogen doping ratios (N/Ti = 0-25 mol%). The relative humidity (RH) was controlled at 0-20% and the oxygen concentration was controlled at 0-21%. The photo-degradation with nitrogen-doped TiO₂ showed superior photo-catalytic activity compared to that for pure TiO₂. TiO₂ doped with 15 mol% nitrogen exhibited the best photo-catalytic efficiency under the tested conditions. The products from the 1,2-DCE photo-catalytic oxidation were CO₂ and water; the by-products included dichloromethane, methyl chloride, ethyl chloride, carbon monoxide, and hydrogen chloride. The reaction pathway of 1,2-DCE indicates that oxygen molecules are the major factor that causes the degradation of 1,2-DCE in the gas phase.     

Chemical synthesis of spinel nickel ferrite (NiFe2O4) nano-sheets

The present investigation is related to the deposition of single-phase nano-sheets spinel nickel ferrite (NiFe₂O₄) thin films onto glass substrates using a chemical method. Nano-sheets nickel ferrite films were deposited from an alkaline bath containing Ni²⁺ and Fe²⁺ ions. The films were characterized for their structural, surface morphological and electrical properties by means of X-ray diffraction (XRD), transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and two-point probe electrical resistivity techniques. The X-ray diffraction pattern showed that NiFe₂O₄ nano-sheets are oriented along (3 1 1) plane. The FT-IR spectra of NiFe₂O₄ films showed strong absorption peaks around 600 and 400 cm⁻¹ which are typical for cubic spinel crystal structure. Microstructural study of NiFe₂O₄ film revealed nano-sheet like morphology with average sheet thickness of 30 nm. The room temperature electrical resistivity of the NiFe₂O₄ nano-sheets was 10⁷ Ω cm.     

Structural properties of single and multilayer ITO and TiO2 films deposited by reactive pulsed laser ablation deposition technique

Indium tin oxide (ITO) and titanium dioxide (TiO₂) single layer and double layer ITO/TiO₂ films were prepared using reactive pulsed laser ablation deposition (RPLAD) with an ArF excimer laser. The films were deposited on SiO₂ substrates heated at 200 and 400 °C. ITO and TiO₂ films with uniform thicknesses of about 400 and 800 nm, respectively, over large areas were prepared. X-ray diffraction (XRD) analysis revealed that the ITO films are formed of highly orientated nanocrystals with an average particle size of 10-15 nm. Atomic force microscopy (AFM) observations indicate rough ITO films surfaces with average roughness of 26-30 nm. Pores were also observed. TiO₂ films deposited on the prepared ITO films result less crystalline. Annealing at 300 and 500 °C for three consecutive hours promoted formation of TiO₂ anatase phase, with crystal size of ∼6-7 nm. From the scanning transmission electron microscope (STEM) images, it can be seen that the TiO₂ films deposited onto the prepared ITO films present a relatively high pore sizes with an average pore diameter of ∼40 nm and excellent uniformity. In addition, STEM cross-sectional analysis of our films showed a columnar structure but no evidence of voids in the structure. Therefore, films exhibited large surface area, well suited for dye-sensitized solar cells (DSSC) applications.     

Physico-chemical, optical and electrochemical properties of iron oxide thin films prepared by spray pyrolysis

Iron oxide thin films were prepared by spray pyrolysis technique onto glass substrates from iron chloride solution. They were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and (UV-vis) spectroscopy. The films deposited at T_s ≤ 450 °C were amorphous; while those produced at T_sub = 500 °C were polycrystalline α-Fe₂O₃ with a preferential orientation along the (1 0 4) direction. By observing scanning electron microscopy (SEM), it was seen that iron oxide films were relatively homogeneous uniform and had a good adherence to the glass substrates. The grain size was found (by RX) between 19 and 25 nm. The composition of these films was examined by X-ray photoelectron spectroscopy and electron probe microanalysis (EPMA). These films exhibited also a transmittance value about 80% in the visible and infrared range. The cyclic voltammetry study showed that the films of Fe₂O₃ deposited on ITO pre-coated glass substrates were capable of charge insertion/extraction when immersed in an electrolyte of propylene carbonate (PC) with 0.5 M LiCLO₄.     

Influence of Au thickness on the optical and electrical properties of transparent and conducting TiO2/Au/TiO2 multilayer films

Au-intermediate TiO₂/Au/TiO₂ (TAT) multilayer films were deposited by RF magnetron sputtering onto glass substrates. Changes in the optical and electrical properties of the films were investigated with respect to the thickness of the Au interlayer.The observed optical and electrical properties were dependent on the thickness of the Au interlayer. The resistivity decreased to 3.3 × 10⁻⁴ Ω cm for TiO₂ films with a 20 nm-thick Au interlayer and the optical transmittance was also influenced by the Au interlayer. Although optical transmittance deteriorated as Au thickness increased, TiO₂ films with a 5 nm-thick Au interlayer showed a relatively high optical transmittance of 80% at a wavelength of 550 nm. In addition, since a TAT film with a 5 nm-thick Au interlayer showed a relatively high work function value, it is an alternative candidate for use as a transparent anode in OLEDs and flat panel displays.     

Fabrication of hydrophobic surface of titanium dioxide films by successive ionic layer adsorption and reaction (SILAR) method

Titanium dioxide (TiO₂) films were fabricated on fluorine doped tin oxide (FTO) coated glass substrate using successive ionic layer adsorption and reaction (SILAR) method. The X-ray diffraction, scanning electron microscopy, transmission electron microscopy, optical absorption and contact angle measurement were applied to study the structural, surface morphological, optical and surface wettability properties of the as-deposited and annealed TiO₂ films. The X-ray diffraction studies revealed both as-deposited and annealed TiO₂ films are amorphous. Irregular shaped spherical grains of random size and well covered to the fluorine doped tin oxide coated glass substrates were observed from SEM studies with some cracks after annealing. The optical band gap values of virgin TiO_2, annealed, methyl violet and rose bengal sensitized TiO₂ were found to be 3.6, 3.5, 2.87 and 2.95 eV, respectively. Surface wettability studied in contact with liquid interface, showed hydrophobic nature as water contact angles were greater than 90°. The adsorption of dyes, as confirmed by the photographs, is one of the prime requirements for dye sensitized solar cells (DSSC).     

Microstructural, optical and photocatalytic properties of CdS doped TiO2 thin films

CdS doped TiO₂ thin films (with CdS content=0, 3, 6, 9 and 12 at%) were grown on glass substrates. The X-ray diffraction analysis revealed that the films are polycrystalline of monoclinic TiO₂ structure. The microstructure parameters of the films such as crystallite size (D_ν) and microstrain (e) are calculated. Both the crystallites size and the microstrain are decreased with increasing CdS content. The optical constants have been determined in terms of Murmann's exact equations. The refractive index and extinction coefficient are increased with increasing CdS content. The optical band gap is calculated in the strong absorption region. The possible optical transition in these films is found to be an allowed direct transition. The values of E_g^opt are found to decrease as the CdS content increased. The films with 3 at% CdS content have better decomposition efficiency than undoped TiO₂. The films with 6 at% and 9 at% CdS content have decomposition efficiency comparable to that of undoped TiO₂, although they have lower band gap. The CdS doped TiO₂ could have a better impact on the decomposing of organic wastes.