Microstructure and high-temperature wear resistance of a laser surface alloyed γ-TiAl with carbon

TiC reinforced composite coating on γ-TiAl alloy was successfully fabricated by laser surface alloying with carbon. The fine TiC reinforcing phase had a gradient distribution in the coating, and its growth morphology of TiC in laser surface alloyed coating was in unique faceted platelet-like. The composite coating exhibited high hardness and excellent high-temperature sliding wear resistance.     

激光熔覆TiC陶瓷涂层的组织和摩擦磨损性能研究

采用激光熔覆技术在TC4合金表面上制备了TiC陶瓷涂层,分析了熔覆层的微观组织,测试了熔覆层的硬度和摩擦磨损性能。结果表明:TiC激光熔覆层分为熔覆区和稀释区两个区域,熔覆区未受到基底的稀释,由TiC颗粒和TiC树枝晶组成;稀释区受到了基底的稀释,由TiC树枝晶和钛合金组成;TiC激光熔覆层的显微硬度在HV700~1500之间,明显地改善了TC4合金表面的摩擦和磨损性能。     

Microstructure and wear properties of TiCN/Ti coatings on titanium alloy by laser cladding

Titanium carbide nitride (TiCN) reinforced Ti coating was fabricated on the surface of Ti–6Al–4V alloy by laser cladding method. Microstructure and wear properties at the surface of the coating in atmosphere were investigated. Three zones can be distinguished of the coating: the clad zone (CZ), the heat affected zone (HAZ) and the substrate. The clad zone is composed of TiCN dendrites, TiO₂ and Ti. A metallurgical bonding between the coating and the substrate was obtained. The microhardness and wear resistance of the TiCN/Ti coating are significantly improved. The average hardness of the coating is about 3 to 6 times of that of the substrate. The friction coefficients of the substrate and the coating are 0.48 and 0.34 respectively. The friction coefficient of the Ti–6Al–4V substrate was insensitive to the normal load, while that of the cladded TiCN/Ti coating was very sensitive to the normal load. The wear mass losses of the cladded samples are much lower than that of the substrate whatever the normal load is.     

Influence of temperature on structure as well as adhesion and friction and wear behavior of hydrogenated carbon nitride films prepared on silicon substrate

Hydrogenated-carbon nitride (CN_x:H) films were synthesized on silicon substrate in a large quantity by the pyrolysis of ethylenediamine in a temperature range of 700-950 °C. The influence of temperature on the morphology, structure, adhesion to substrate, and friction and wear behavior of CN_x:H films was investigated. It has been found that CN_x:H films obtained at 700 °C and 800 °C are amorphous, and those prepared at 900 °C and 950 °C consist of carbon nitride nanocrystal. Besides, CN_x:H film sample obtained at 700 °C has the maximum N content of 9.1 at.% but the poorest adhesion to Si substrate, while the one prepared at 900 °C has the lower N content and the highest adhesion to substrate. As a result, nanocrystalline CN_x:H (nc-CN_x:H) film synthesized at 900 °C possesses the best wear resistance when slides against stainless steel counterpart. N atom is incorporated into the graphitic network in three different bonding forms, and their relative content is closely related to temperature, corresponding to different adhesion as well as friction and wear behavior of the films obtained at different temperatures. Furthermore, the friction coefficient and antiwear life of as-deposited CN_x:H films vary with varying deposition temperature and thickness, and the film with thickness of 1.3 μm, obtained at 900 °C, has the longest antiwear life of over 180,000 s.     

Microstructure, microhardness and dry friction behavior of cold-sprayed tin bronze coatings

In this paper, two types of tin bronze coatings (Cu-6 wt.% Sn and Cu-8 wt.% Sn) were prepared by cold spray process. The as-sprayed coatings were subjected to a vacuum heat treatment at 600 °C for 3 h. The coating microstructure, microhardness and tribological performance were characterized. The effects of the tin content and the vacuum heat treatment on the microstructure, microhardness and tribological behavior of the coatings were investigated. It is found that the as-sprayed CuSn6 (As6) and CuSn8 (As8) coatings exhibit practically an identical porosity. Meanwhile, As8 presents a higher microhardness than As6. In addition, the increase of the tin content in the powder feedstock leads to a lower wear rate. After a heat treatment, coating porosities are significantly reduced. However, the coating hardness is significantly decreased and the coating presents a much decreased wear resistance. For the as-sprayed coatings, such factors as ploughing and particle delamination could determine the sliding process. The heat treatment results in a distinct modification of the tribological behavior. For the annealed coatings, the adhesion, between the coating and the counterpart, could play a dominant role in the sliding process.     

Synthesis of Fe-based amorphous composite coatings with low purity materials by laser cladding

Amorphous composite coatings Fe₃₈Ni_30−XSi₁₆B₁₄V₂M_X (X = 0, 1, 2) (M contains Al, Ti, Mo, and C) were prepared with low purity of raw materials by laser cladding. X-ray diffraction and transmission electron microscopy results show that the coating have an amorphous structure with a few crystalline phase on it. The amorphous phase is the primary phase. The glass forming ability as well as the microhardness of the Fe-based alloy made from low purity raw materials can be much enhanced by adding small amount of multi-components. However, the elements addition has its optimal quantity. When X is equal to 1, the microstructure of the coating contains 97.93% amorphous phase and 2.07% crystalline phase on it. As a result, the microhardness of the coating reaches maximum. With further increasing of the additions, the amorphous phase in the coating lessens instead of augment and the crystalline phase begins to accumulate, which result in the decrease of the microhardness.     

激光熔覆NiCrBSi涂层组织及摩擦磨损性能

采用激光熔覆技术在H13钢表面制备了NiCrBSi合金涂层,利用OM,SEM,EDX和XRD等对熔覆层的微观组织进行了分析,测试了熔覆层的显微硬度和摩擦磨损性能。结果表明,激光熔覆层与基体形成了良好的冶金结合,熔覆层的组织主要由γ-Ni,Cr7C3和CrB等相组成。熔覆层显微硬度在650~850HV之间,明显高于H13钢基体的硬度。摩擦磨损实验表明,在相同的条件下,熔覆层的耐磨性比基体有了明显的提高,磨损体积减少了92.4%。通过对磨损后的试样进行粗糙度测试后表明,涂层具有更平滑的表面。     

Investigation of the microstructure and tribological behavior of cold-sprayed tin-bronze-based composite coatings

In this paper, tin-bronze/TiN and tin-bronze/quasicrystal (AlCuFeB) composite coatings were fabricated by cold spray process. Microstructure and microhardness of the prepared coatings were investigated. Ball-on-disc dry sliding wear tests were conducted in an ambient condition to examine the tribological behavior of the composite coatings. The results show that the microhardness and the density of composite coatings increase significantly compared to the pure tin-bronze coating. The friction coefficient of composite coating decreases when reinforcing particles were introduced. Furthermore, the bronze/quasicrystal composite coating has a lower friction coefficient and wear rate than the bronze/TiN coating. Tribological mechanisms of the composite coatings were discussed.     

Microstructure and wear resistance of composite layers on a ductile iron with multicarbide by laser surface alloying

Multicarbide reinforced metal matrix composite (MMC) layers on a ductile iron (QT600-3) were fabricated by laser surface alloying (LSA) using two types of laser: a 5 kW continuous wave (CW) CO₂ laser and a 400 W pulsed Nd:YAG laser, respectively. The research indicated that LSA of the ductile iron with multicarbide reinforced MMC layers demonstrates sound alloying layers free of cracks and porosities. The microstructure, phase structure and wear properties of MMC layers were investigated by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD), as well as dry sliding wear testing. The microstructure of the alloyed layer is composed of pre-eutectic austenite, ledeburite, spherical TiC, Cr₇C₃ and Cr₂₃C₆ with various morphologies. TiC particles are dispersed uniformly in the upper region of MMC layers. The average hardness of LSA layers by CO₂ laser and pulsed Nd:YAG laser is 859 HV_0.2 and 727 HV_0.2, respectively. The dry sliding wear testing shows the wear resistance of ductile iron is significantly improved after LSA with multicarbide.     

Thermal stability of titanium nitride coatings prepared by the mixing technology with laser and plasma

Titanium samples were treated by the mixing technology with laser and plasma (LPN) using different laser power densities. These nitrided samples were then annealed at 473 K, 673 K, 873 K, and 1073 K for 2 h in vacuum, respectively. The samples before and after annealing were characterized at room temperature and compared in terms of microstructure. X-ray diffraction and cross-sectional optical microscopy studies showed that the layer structure of the titanium nitride coating is preserved after annealing at 1073 K when the coating is formed using a laser power density of 8.0 × 10⁵ W/cm². Therefore, titanium nitride coatings produced by LPN demonstrate excellent thermal stability and are potential candidates for high temperature tribological applications.     

Microstructure and corrosion behavior of austenitic stainless steel treated with laser

Surface modification of AISI316 stainless steel by laser melting was investigated experimentally using 2 and 4 kW laser power emitted from a continuous wave CO₂ laser at different specimen scanning speeds ranged from 300 to 1500 mm/min. Also, an investigation is reported of the introduction of carbon into the same material by means of laser surface alloying, which involves pre-coating the specimen surfaces with graphite powder followed by laser melting. The aim of these treatments is to enhance corrosion resistance by the rapid solidification associated with laser melting and also to increase surface hardness without affecting the bulk properties by increasing the carbon concentration near the surface. Different metallurgical techniques such as optical microscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD) were used to characterize the microstructure of the treated zone. The microstructures of the laser melted zones exhibited a dendritic morphology with a very fine scale with a slight increase in hardness from 200 to 230 Hv. However, the laser alloyed samples with carbon showed microstructure consisting of γ dendrite surrounded by a network of eutectic structures (γ+carbide). A significant increase in hardness from 200 to 500 Hv is obtained. Corrosion resistance was improved after laser melting, especially in the samples processed at high laser power (4 kW). There was shift in I_corr and E_corr toward more noble values and a lower passive current density than that of the untreated materials. These improvements in corrosion resistance were attributed to the fine and homogeneous dendritic structure, which was found throughout the melted zones. The corrosion resistance of the carburized sample was lower than the laser melted sample.     

Effects of processing parameters on structure of Ni-based WC composite coatings during laser induction hybrid rapid cladding

The relationships between the processing parameters (i.e. laser specific energy, powder density, preheated temperature of substrate and types of substrate) and the structure characteristics of Ni-based WC composite coatings during laser induction hybrid rapid cladding (LIHRC) were investigated systematically. The results show that laser specific energy, cladding height and contact angle have a linear relation with powder density, as can provide the predictions of laser processing parameters according to the geometrical characteristics of a single laser track (i.e. cladding height, cladding width). Moreover, dilution of composite coating increases with the increasing of laser specific energy and the preheated temperature of substrate, while reduces with the increasing of powder density. The types of substrate also have an important effect on dilution of composite coating, as has a strong dependence on the thermophysical properties of substrate (i.e. melting point, resistivity and permeability).     

Microstructure and wear resistance of laser clad cobalt-based alloy multi-layer coatings

Multi-layer Co-based alloy (HMSP 2537) were deposited on Ni-based superalloy plate with a TJ-TL-T5000 type CO₂ laser. Sections of such coatings were examined to reveal their microstructure and phase composition using optical microscope, scanning electron microscope (SEM), and X-ray diffractometer (XRD). The hardness and wear resistance of the coatings were tested. The results showed that the prime phase (γ-Co dendrite) and other phases, such as CrNi, Co₇W₆, and Cr₂₃C₆ existed in the coatings. Dendrite or cellular microstructures were observed perpendicular to the interface, and coarsening microstructures were obtained as more layers deposited. Dendrite paralleling to laser scan speed was also found near the top surface of the last layer. Fine microstructures of γ-Co dendrite and lamellar eutectic in inter-dendritic regions strengthened the coatings. Microhardness and wear resistance of the coatings were much higher than that of substrate but slightly decreased with layers increased.     

Microstructure of yttric calcium phosphate bioceramic coatings synthesized by laser cladding

The yttric calcium phosphate (CaP) coatings were in situ prepared on pure titanium substrate by laser cladding. The morphologies and phases constitution of CaP coatings were studied by electron probe microanalysis, X-ray diffraction and so on. The bonding state between the coating and the substrate is fine metallurgical combination, and the addition of yttria can fine the structure and increase the tensile strength of the coatings. The X-ray result shows that the coating is composed of the phases of HA, α-Ca₂P₂O₇, β-Ca₂P₂O₇ and CaTiO₃.     

Study on the microstructure and wear resistance of the composite coatings fabricated on Ti-6Al-4V under different processing conditions

Composite coatings mainly containing titanium carbides and borides were produced by laser surface alloying of Ti-6Al-4V with graphite and boron mixed powders. The test results show that the coatings have higher hardness (1600-1700 HV_0.1) and are more resistant to wear than the as-received sample. Laser scanning speed and the content of alloying elements (weight ratio of graphite to boron) have an effect on both the microstructure and the wear resistance of the coatings. TEM results show that strip titanium carbides and borides grow alternately and thus restrain the formation of coarse needle-like TiB and dendritic TiC crystals produced by laser alloying of titanium alloys with boron and graphite separately.     

Investigation on friction and wear behaviors of FeS films on L6 steel surface

Low temperature ion sulfuration technique was utilized to prepare the solid lubrication iron sulfide (FeS) film on the surface of die-steel AISI L6. The friction and wear behaviors of sulfurized L6 steel were investigated on the ring-on-block tester of MM-200 under dry sliding condition. Atomic force microscopy and scanning electron microscopy were adopted to analyze the morphologies and compositions of surfaces and wear scars of the FeS film. X-ray diffractometer was used to study the film phase structure. Scanning Auger microprobe was employed to detect the elements distribution with depth. The results showed that the tribological properties of sulfurized L6 steel were superior to that of the unsulfurized one.     

Electrodeposited nickel-cobalt composite coating containing MoS2

Ni-Co/MoS₂ composite coatings were prepared by electrodeposition in a Ni-Co plating bath containing nano-sized MoS₂ particles to be co-deposited. The polarization behavior of the composite plating bath was examined on a PAR-273A potentiostat/galvanostat device. The friction and wear behaviors of the Ni-Co/MoS₂ composite coatings were evaluated with UMT-2MT test rig in a ball-on-disk contact mode. The morphologies of the original and worn surfaces of the composite coatings were observed on scanning electron microscope (SEM). It was found that the introduction of MoS₂ nano-particulates in the electrolyte caused the shift towards larger negatives of the reduction potential of the Ni-Co alloy coating, and the co-deposited MoS₂ showed no significant effect on the electrodeposition process of the Ni-Co alloy coating. However, the co-deposited MoS₂ led to changes in the surface morphology and structure of the composite coating as well. Namely, the peak width of the Ni-Co solid solution for the composite coating is broader as compared to that of the Ni-Co alloy coating. The co-deposited MoS₂ particulates were uniformly distributed in the Ni-Co matrix and contributed to increase tribological properties of the Ni-Co alloy coating.     

Sliding friction and wear behaviors of surface-coated natural serpentine mineral powders as lubricant additive

This work aims to investigate the friction and wear properties of surface-coated natural serpentine powders (SP) suspended in diesel engine oil using an Optimal SRV oscillating friction and wear tester. The worn surface was characterized by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS). Results indicated that the additives can improve the wear resistance and decrease friction coefficient of carbon steel friction couples. The 0.5 wt% content of serpentine powders is found most efficient in reducing friction and wear at the load of 50 N. The SEM and XPS analysis results demonstrate that a tribofilm forms on the worn surface, which is responsible for the decrease in friction and wear, mainly with iron oxides, silicon oxides, graphite and organic compounds.     

Microstructure and tribological properties of TiAg intermetallic compound coating

TiAg intermetallic compound coating has been in situ synthesized successfully on pure Ti substrate by laser cladding using Ag powder as the precursor. It has been found that the prepared coating mainly comprised TiAg and Ti phases. The high resolution transmission electron microscopy results further conform the existence of TiAg intermetallic compound in the prepared coating. The magnified high resolution transmission electron microscopy images shown that the laser cladding coating contains TiAg nanocrystalline with the size of about 4 nm. Tribological properties of the prepared TiAg intermetallic compound coating were systematically evaluated. It was found that the friction coefficient and wear rate was closely related to the normal load and sliding speed, i.e., the friction coefficient of the prepared TiAg intermetallic compound coating decreased with increasing normal load and sliding speed. The wear rate of the TiAg intermetallic compound coating decreased rapidly with increasing sliding speed, while the wear rate increased as the normal load increased.     

Fretting wear behaviour of microarc oxidation coatings formed on titanium alloy against steel in unlubrication and oil lubrication

Ceramic coatings were formed on Ti6Al4V alloy surface by microarc oxidation (MAO) in a Na₂SiO₃ system solution. Unlubricated, smear oil and oil bath lubricated fretting tests were performed on MAO coatings against 52100 steel on a fretting wear tester. Microstructural investigation of the worn surfaces was performed and the wear mechanisms were studied. The results show that the coatings are mainly composed of rutile and a small amount of anatase TiO₂, both in nano grain structure. Friction coefficient of microarc oxidation coatings under oil bath lubrication was significantly reduced, favorable stable at 0.15, which indicates that the coatings with oil lubricated lowered the shear and adhesive stresses between contact surfaces, consequently alleviating the possibility of initiation and propagation of cracks in the inner layer of the coating or titanium alloy substrate.