Interaction of Sb ions with Eu ions during the room temperature synthesis of luminescent Sb2O3 nanorods: Probed through Eu luminescence

The interaction of Eu³⁺ with Sb³⁺ ions during the room temperature synthesis of luminescent Sb₂O₃ nanorods is investigated using luminescence and vibrational spectroscopic techniques. Our results demonstrate that well crystalline, oriented Sb₂O₃ nanorods having length of around 3-4 μm, a width of around 100-200 nm and luminescence at around 390 nm can be synthesized at room temperature. Incorporation of Eu³⁺ in these nanorods has been attempted and it is found that Eu³⁺ ions do not have any interaction with nanorods and their orientation. Detailed Eu³⁺ luminescence and XRD studies confirmed that a part of Sb³⁺ ions reacts with Eu³⁺ ions in the presence of hydroxyl ions (present in the medium) to form an amorphous antimony europium hydroxide compound. The amorphous compound on heating at high temperatures leads to its decomposition, giving hydrated Sb(V) oxides and Eu₂O₃ as major phases.     

One-pot synthesis of gold nanorods via autocatalytic growth of sonochemically formed gold seeds: The effect of irradiation time on the formation of seeds and nanorods

A one-pot synthesis for gold nanorods was developed using sonochemical reduction of gold ions in an aqueous solution in the presence of cetyltrimethylammonium bromide, silver nitrate, and ascorbic acid, where we focused on the autocatalytic growth of gold seeds formed by ultrasonic irradiation for short times. In growth experiments with these sonochemically formed gold seeds, sigmoidal shape growth curves were observed, and the induction period before growth began was longer for shorter irradiation times. This result indicated that the number of sonochemically formed gold seeds increased with increasing irradiation time. The average aspect ratio of the gold nanorods produced changed from 2.0 at an irradiation time of 0.5 min to 3.6 at 15 min. The gold nanorods produced were longer and wider when the irradiation time was shorter.     

Low temperature synthesis of hexagonal ZnO nanorods and their hydrogen sensing properties

The growth of hexagonal ZnO nanorods was demonstrated by low temperature chemical synthesis approach. X-ray diffraction (XRD) analysis revealed a wurtzite hexagonal structure of the ZnO nanorods. The optical properties were measured by UV-vis spectrophotometer at room temperature. X-ray photoelectron spectroscopy (XPS) confirmed high purity of the ZnO nanorods. The hydrogen sensor made of the ZnO nanorods showed reversible response. The hydrogen gas tests were carried out in presence of ambient air and the influence of operation temperature on the hydrogen gas sensing property of ZnO nanorods was also investigated.     

Hydrothermal synthesis, characterization and Raman studies of Eu activated Gd2O3 nanorods

Eu³⁺ (8 mol%) activated gadolinium oxide nanorods have been prepared by hydrothermal method without and with surfactant, cityl trimethyl ammonium bromide (CTAB). Powder X-ray diffraction (PXRD) studies reveal that the as-formed product is in hexagonal Gd(OH)₃:Eu phase and subsequent heat treatment at 350 and 600 °C transforms the sample to monoclinic GdOOH:Eu and cubic Gd₂O₃:Eu phases, respectively. The structural data and refinement parameters for cubic Gd₂O₃:Eu nanorods were calculated by the Rietveld refinement. SEM and TEM micrographs show that as-obtained Gd(OH)₃:Eu consists of uniform nanorods in high yield with uniform diameters of about 15 nm and lengths of about 50-150 nm. The temperature dependent morphological evolution of Gd₂O₃:Eu without and with CTAB surfactant was studied. FTIR studies reveal that CTAB surfactant plays an important role in converting cubic Gd₂O₃:Eu to hexagonal Gd(OH)₃:Eu. The strong and intense Raman peak at 489 cm⁻¹ has been assigned to A_g mode, which is attributed to the hexagonal phase of Gd₂O₃. The peak at ∼360 cm⁻¹ has been assigned to the combination of F_g and E_g modes, which is mainly attributed to the cubic Gd₂O₃ phase. The shift in frequency and broadening of the Raman modes have been attributed to the decrease in crystallite dimension to the nanometer scale as a result of phonon confinement.     

Experimental and kinetic modeling study of C2H4 oxidation at high pressure

A detailed chemical kinetic model for oxidation of C₂H₄ in the intermediate temperature range and high pressure has been developed and validated experimentally. New ab initio calculations and RRKM analysis of the important C₂H₃ + O₂ reaction was used to obtain rate coefficients over a wide range of conditions (0.003-100 bar, 200-3000 K). The results indicate that at 60 bar and medium temperatures vinyl peroxide, rather than CH₂O and HCO, is the dominant product. The experiments, involving C₂H₄/O₂ mixtures diluted in N₂, were carried out in a high pressure flow reactor at 600-900 K and 60 bar, varying the reaction stoichiometry from very lean to fuel-rich conditions. Model predictions are generally satisfactory. The governing reaction mechanisms are outlined based on calculations with the kinetic model. Under the investigated conditions the oxidation pathways for C₂H₄ are more complex than those prevailing at higher temperatures and lower pressures. The major differences are the importance of the hydroxyethyl (CH₂CH₂OH) and 2-hydroperoxyethyl (CH₂CH₂OOH) radicals, formed from addition of OH and HO₂ to C₂H₄, and vinyl peroxide, formed from C₂H₃ + O₂. Hydroxyethyl is oxidized through the peroxide HOCH₂CH₂OO (lean conditions) or through ethenol (low O₂ concentration), while 2-hydroperoxyethyl is converted through oxirane.     

同位素示踪法研究铜薄膜在水汽中的氧化传质机理

采用H¹⁶₂O/H¹⁸₂O接续氧化并结合同位素示踪方法,研究了铜薄膜在水汽中氧化的传质机理.将真空热蒸发制备的铜薄膜样品,分别在H¹⁶₂O,H¹⁸₂O中以及H¹⁶₂O/H¹⁸₂O接续进行氧化处理;利用X射线衍射(XRD)研究了氧化产物的形态和结构 关键词： 同位素示踪 短路扩散 铜薄膜 18₂O')" href="#">H¹⁸₂O     

Effect of Eu,Tb codoping on the luminescent properties of Y2O3 nanorods

Red-emitting Y₂O₃:Eu³⁺ and green-emitting Y₂O₃:Tb³⁺ and Y₂O₃:Eu³⁺, Tb³⁺ nanorods were synthesized by hydrothermal method. Their structure and micromorphology have been analyzed by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The photoluminescence (PL) property of Y₂O₃:Eu³⁺,Tb³⁺ phosphor was investigated. In the same host (Y₂O₃), upon excitation with ultraviolet (UV) irradiation, it is shown that there are strong emissions at around 610 and 545 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺ and ⁵D₄-⁷F₅ transition of Tb³⁺, respectively. Different qualities of Eu³⁺and Tb³⁺ ions are induced into the Y₂O₃ lattice. From the excitation spectrum, we speculate that there exists energy transfer from Tb³⁺ to Eu³⁺ ions .The emission color of powders reveals regular change in the separation of light emission. These powders can meet with the request of optical display material for different colors or can be potentially used as labels for biological molecules.     

On the isotope effect of Tc in squaric acid (H2C4O4)

The phase transition mechanism in squaric acid is reviewed from the viewpoint of the pressure dependence of the O—H—O bond length (2R). The two-dimensional pressure effect on T_c is extracted from the hydrostatic pressure behaviour by taking account of the uniaxial stress applied perpendicular to the layer planes. The result shows that if 2R(H₂SQ) is stretched to 2R(D₂SQ) the phase transition temperature 7^H _c of H₂SQ coincides with T^D _c of D₂SQ. This result supports the suggestion that the phase transition mechanism is of the order-disorder type.     

Interfacial reactions and oxidation behavior of Al2O3 and Al2O3/Al coatings on an orthorhombic Ti2AlNb alloy

The uniform and dense Al₂O₃ and Al₂O₃/Al coatings were deposited on an orthorhombic Ti₂AlNb alloy by filtered arc ion plating. The interfacial reactions of the Al₂O₃/Ti₂AlNb and Al₂O₃/Al/Ti₂AlNb specimens after vacuum annealing at 750 °C were studied. In the Al₂O₃/Ti₂AlNb specimens, the Al₂O₃ coating decomposed significantly due to reaction between the Al₂O₃ coating and the O-Ti₂AlNb substrate. In the Al₂O₃/Al/Ti₂AlNb specimens, a γ-TiAl layer and an Nb-rich zone came into being by interdiffusion between the Al layer and the O-Ti₂AlNb substrate. The γ-TiAl layer is chemically compatible with Al₂O₃, with no decomposition of Al₂O₃ being detected. No internal oxidation or oxygen and nitrogen dissolution zone was observed in the O-Ti₂AlNb alloy. The Al₂O₃/Al/Ti₂AlNb specimens exhibited excellent oxidation resistance at 750 °C.     

Hydrothermal synthesis of C-doped Zn3(OH)2V2O7 nanorods and their photocatalytic properties under visible light illumination

A visible light-driven photocatalyst, C-doped Zn₃(OH)₂V₂O₇, prepared by a hydrothermal method was studied. The as-prepared catalyst was characterized by SEM, XRD, DRS, and XPS, and exhibited efficient photocatalytic activity in the degradation of methylene blue (MB) under visible-light irradiation. Besides decoloring, the decomposition of MB was also observed, further demonstrating the performance of the photocatalyst. The carbon existing on the surface of Zn₃(OH)₂V₂O₇ nanorods was free and in carbide form. Dye degradation followed first-order kinetics, and was explained on the basis of the Langmuir-Hinshelwood mechanism.     

Anomalous pressure-induced phase transformation in nano-crystalline erbium sesquioxide (Er2O3): partial amorphization under compression

Nanophase materials have novel physical and chemical properties, differing from bulk materials. It is of exceptional interest to investigate the size effect on structural stability in nanocrystals. Here, we investigated pressure-induced phase transitions in nanosized Er₂O₃ using angle-dispersive synchrotron X-ray diffraction up to 40.6 GPa. Nano-Er₂O₃ has enhanced transition pressure and higher bulk modulus (K₀) than its bulk counterparts. Amorphous Er₂O₃ nanoclusters with traces of monoclinic phase are obtained upon compression. This is the first time that partial amorphous structure under compression was observed in nano-Er₂O₃, indicating a kinetic trapping of partial amorphous Er₂O₃ on pressurizing.     

Theoretical study on the oxidation of zigzag silicon carbide nanotubes (SiCNTs) by singlet O2

Singlet O₂ produced upon photoexcitation is a very important oxidative reagent. The study on its reaction with nanotube might be useful not only to evaluate the stability of the nanotube upon air exposure and sunlight, but also to modify the properties of the nanotube. Considering the unique properties and wide applications of silicon carbide nanotube (SiCNT), in this paper, we performed extensive density functional theory (DFT) calculations to study the oxidation of a series of zigzag (n,0) SiCNTs (n=6 to 12) by singlet O₂. It is found that the reaction process contains two steps, namely, (i) [2+2] cycloaddition of a singlet O₂ to the Si–C bond, followed by (ii) the dissociation of the O–O bond, leading to the formation of an epoxide configuration with a highly exothermicity (>4.00 eV). Compared with pure SiCNT, the cycloaddition of singlet O₂ on tube leads to the decrease of the band gap, while the formation of the stable epoxy structure render band gap increase. Our results indicate that the SiCNT is more prone to be degraded after exposure to air and sunlight.     

FC(O)O2的结构及其自由基与NO反应的微观机理研究

用密度泛函理论(DFT)和哈特里-福克(HF)从头计算方法和半经验势方法等研究了FC(O)O₂ 的结构和振动性质.在DFT中采用B3LYP方法,在6-311G(d)基组上对FC(O)O₂自由基与NO反应的微观过程进行了分析.首先给出了各反应物、中间体、过渡态和生成物的几何构型,然后计算了它们的能量和频率,通过频谱分析得到反应的中间体和过渡态信息,即FC(O)O₂与NO反应为多反应通道,势垒高度和反应速度给出主要通道是FC(O)O₂     

Photoluminescent properties of Y2O3:Eu phosphors prepared via urea precipitation in non-aqueous solution

Europium-doped yttrium oxide phosphors were obtained by firing precursors prepared by urea precipitation in ethanol and ethylenediamine. The precipitation in non-aqueous solution was carried out in an autoclave at 150°C to allow the decomposition of urea. The photoluminescent intensities of the phosphors prepared in ethanol and ethylenediamine increased by about 30% compared to that of the phosphor prepared by the conventional urea homogeneous precipitation in aqueous solution. Amorphous carbonates and amorphous hydroxides/carbonates mixtures were identified as precursors from ethanol and ethylenediamine, respectively. The morphology and particle size were studied by SEM and dynamic laser scattering method.     

Effects of RE2O3 (RE = Tm, Sc, Yb) addition on the superconducting properties of ErBa2Cu3Oy

We investigated the effects of added Tm₂O₃, Sc₂O₃, and Yb₂O₃ on the superconducting properties of sintered Er123 samples. Tm₂O₃ addition caused the least T_c degradation, exhibiting a T_c above 90 K even for 17 vol% addition. Samples with added Sc₂O₃ maintained a T_c at above 90 K up to an addition of 7.2 vol%, while Yb₂O₃-containing samples showed a monotonic decrease in T_c with increased vol% of added Yb₂O₃. Tm₂O₃-containing samples exhibited a slight increase in J_c(0.1 T)/J_c(0) and had constant J_c values even for 17 vol% addition. XRD and SEM results indicate that the Tm₂O₃ is very stable in the superconducting matrix.     

Synthesis of nanorods and mixed shaped copper ferrite and their applications as liquefied petroleum gas sensor

Present paper reports the preparation and characterization of nanorods and mixed shaped (nanospheres/nanocubes) copper ferrite for liquefied petroleum gas (LPG) sensing at room temperature. The structural, surface morphological, optical, electrical as well as LPG sensing properties of the copper ferrite were investigated. Single phase spinel structure of the CuFe₂O₄ was confirmed by XRD data. The minimum crystallite size of copper ferrite was found 25 nm. The stoichiometry was confirmed by elemental analysis and it revealed the presence of oxygen, iron and copper elements with 21.91, 12.39 and 65.70 atomic weight percentages in copper ferrite nanorods. The band gap of copper ferrite was 3.09 and 2.81 eV, respectively for nanospheres/nanocubes and nanorods. The sensing films were made by using screen printing technology and investigated with the exposure of LPG. Our results show that the mixed shaped CuFe₂O₄ had an improved sensing performance over that of the CuFe₂O₄ nanorods, of which a possible sensing mechanism related to a surface reaction process was discussed. Sensor based on mixed shaped copper ferrite is 92% reproducible after one month. The role of PEG in the synthesis for obtaining nanospheres/nanocubes has also been demonstrated.     

Effect of pressure on cubic (C-type) Eu2O3 studied via Eu3+ luminescence

Abstract

Luminescence spectra from Eu³⁺ ion in C-type Eu₂O₃ under high pressures have been obtained. The spectral shifts can be used to study the effect of pressure on the spin-orbit and the Coulomb interactions of the 4f electrons, which are correlated with expansion of the 4f-electron wave functions. This expansion with the application of pressure results in both the variation of the electronegativity and radius of the Eu³⁺ ion and, ultimately, the phase transformation from C-to B-type Eu₂O₃. Therefore, core 4f-electrons can thus be thought of as quasivalence electrons.