Swelling and biocompatibility of sodium alginate/poly(γ‐glutamic acid) hydrogels

Sodium alginate (Alg) hydrogel films were crosslinked with either calcium poly(γ‐glutamate) (Ca‐PGA) or CaCl₂. The hydrophilicity of the resulting hydrogel films was evaluated through swelling tests, water retention capacity tests, and water vapor permeation tests. The swelling ratio, water retention capacity, and the water vapor transmission rate (WVTR) of Alg/Ca‐PGA were higher than those of Ca‐Alg. The swelling ratio of Alg/Ca‐PGA was 651 and 190% at pH 7.4 and pH 1.2, respectively. The tensile strength of Alg/Ca‐PGA hydrogel was lower than that of Ca‐Alg. The results of hemocompatibility test showed that Alg/Ca‐PGA caused shorter activated partial thromboplastin time (APTT) than Ca‐Alg. Both Ca‐Alg and Alg/Ca‐PGA exhibited almost no adsorption of human serum albumin (HSA), whereas the adsorption of human plasma fibrinogen (HPF) of Ca‐Alg was 10 times of that of Alg/Ca‐PGA. In addition, Alg/Ca‐PGA exhibited platelet adhesion higher than Ca‐Alg. Furthermore, both Alg/Ca‐PGA and Ca‐Alg exhibited no cytotoxicity. Copyright © 2009 John Wiley & Sons, Ltd.     

Aminated PCL‐based copolymers by chemical modification of poly(α‐iodo‐ε‐caprolactone‐co‐ε‐caprolactone)

A novel method is proposed to access to new poly(α‐amino‐ε‐caprolactone‐co‐ε‐caprolactone) using poly(α‐iodo‐ε‐caprolactone‐co‐ε‐caprolactone) as polymeric substrate. First, ring‐opening (co)polymerizations of α‐iodo‐ε‐caprolactone (αIεCL) with ε‐caprolactone (εCL) are performed using tin 2‐ethylhexanoate (Sn(Oct)₂) as catalyst. (Co)polymers are fully characterized by ¹H NMR, ¹³C NMR, FTIR, SEC, DSC, and TGA. Then, these iodinated polyesters are used as polymeric substrates to access to poly(α‐amino‐ε‐caprolactone‐co‐ε‐caprolactone) by two different strategies. The first one is the reaction of poly(αIεCL‐co‐εCL) with ammonia, the second one is the reduction of poly(αN₃εCL‐co‐εCL) by hydrogenolysis. This poly(α‐amino‐ε‐caprolactone‐co‐ε‐caprolactone) (F_αNH2εCL < 0.1) opens the way to new cationic and water‐soluble PCL‐based degradable polyesters. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 6104–6115, 2009     

Synthesis and characterization of poly(3,3 bis(azidomethyl)oxetane‐co‐ε‐caprolactone)s

The quasi‐living cationic copolymerization of 3,3‐bis(chloromethyl)oxetane (BCMO) and ε‐caprolactone (ε‐CL), using boron trifluoride etherate as catalyst and 1,4‐butanediol as coinitiator, was investigated in methylene chloride at 0°C. The resulting hydroxyl‐ended copolymers exhibit a narrow molecular weight polydispersity and a functionality of about 2. The reactivity ratios of BCMO (0.26) and ε‐CL (0.47), and the T_g of the copolymers, indicate their statistical character. The synthesis of poly(3,3‐bis(azidomethyl)oxetane‐co‐ε‐caprolactone) from poly(BCMO‐co‐ε‐CL) via the substitution of the chlorine atoms by azide groups, using sodium azide in DMSO at 110°C, occurs without any degradation, but the copolymers decompose at about 240°C. All polymers were characterized by vapor pressure osmometry or steric exclusion chromatography, ¹H‐NMR and FTIR spectroscopies, and DSC. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1027–1039, 1999     

Poly(γ‐benzyl‐L‐glutamate)‐functionalized single‐walled carbon nanotubes from surface‐initiated ring‐opening polymerizations of N‐carboxylanhydride

Single‐walled carbon nanotubes (SWCNTs) have been functionalized with poly(γ‐benzyl‐L ‐glutamate) (PBLG) by ring‐opening polymerizations of γ‐benzyl‐L ‐glutamic acid‐based N‐carboxylanhydrides (NCA‐BLG) using amino‐functionalized SWCNTs (SWCNT‐NH₂) as initiators. The SWCNT functionalization has been verified by FTIR spectroscopy and transmission electron microscopy. The FTIR study reveals that surface‐attached PBLGs adopt random‐coil conformations in contrast to the physically absorbed or bulk PBLGs, which exhibit α‐helical conformations. Raman spectroscopic analysis reveals a significant alteration of the electronic structure of SWCNTs as a result of PBLG functionalization. The PBLG‐functionalized SWCNTs (SWCNT‐PBLG) exhibit enhanced solubility in DMF. Stable DMF solutions of SWCNT‐PBLG/PBLG with a maximum SWCNTs concentration of 259 mg L^?1 can be readily obtained. SWCNT‐PBLG/PBLG solid composites have been characterized by differential scanning calorimetry, thermogravimetric analysis, wide/small‐angle X‐ray scattering (W/SAXS), scanning electron microscopy, and polarized optical microscopy for their thermal or morphological properties. Microfibers containing SWCNT‐PBLG and PBLG can also be prepared via electrospinning. WAXS characterization reveals that SWCNTs are evenly distributed among PBLG rods in solution and in the solid state where PBLGs form a short‐range nematic phase interspersed with amorphous domains. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2340–2350, 2010     

Synthesis of poly[(2‐oxo‐1,3‐dioxolane‐4‐yl) methyl methacrylate‐co‐ethyl acrylate] by incorporation of carbon dioxide into epoxide polymer and the miscibility behavior of its blends with poly(methyl methacrylate) or poly(vinyl chloride)

This study was related to the investigation of the chemical fixation of carbon dioxide to a copolymer bearing epoxide and the application of the cyclic carbonate group containing copolymer‐to‐polymer blends. In the synthesis of poly[(2‐oxo‐1,3‐dioxolane‐4‐yl) methyl methacrylate‐co‐ethyl acrylate] [poly(DOMA‐co‐EA)] from poly(glycidyl methacrylate‐co‐ethyl acrylate) [poly(GMA‐co‐EA)] and CO₂, quaternary ammonium salts showed good catalytic activity. The films of poly(DOMA‐co‐EA) with poly(methyl methacrylate) (PMMA) or poly(vinyl chloride) (PVC) blends were cast from N,N′‐dimethylformamide solution. The miscibility of the blends of poly(DOMA‐co‐EA) with PMMA or PVC have been investigated both by DSC and visual inspection of the blends. The optical clarity test and DSC analysis showed that poly(DOMA‐co‐EA) containing blends were miscible over the whole composition range. The miscibility behaviors were discussed in terms of Fourier transform infrared spectra and interaction parameters based on the binary interaction model. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 1472–1480, 2001     

Influence of multiple processing on selected properties of poly(3‐hydroxybutyrate‐co‐4‐hydroxybutyrate)

The effect of multiple (up to 10 times) injection molding of processed poly(3‐hydroxybutyrate‐co‐4‐hydroxybutyrate) (P(3,4HB)) on its phase transition temperatures, degree of crystallinity, degradation temperature, mass flow rate, mechanical properties, dynamic mechanical properties, and Charpy's impact strength is presented. The studies have shown that the multiple injection lowers the degree of crystallinity and the thermal stability of P(3,4HB). The mass flow rate values increased with increasing the injection number. It was found that the multiple injections had no substantial effect on the tensile strength up to 10 injection cycles and the tensile strength at break, tensile strain at tensile strength, and tensile strain at break up to 6 injection cycles. The maximum value of storage modulus at 30 °C and impact strength were recorded for sample after 4 cycles of injection, while the values of storage modulus at 120 °C increased with increase of the injection cycles. Copyright © 2015 John Wiley & Sons, Ltd.     

Nonisothermal crystallization kinetics of poly(ε‐caprolactone) blocks in double crystalline triblock copolymers containing poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) and poly(ε‐caprolactone) units

The poly(3‐hydroxbutyrate‐co‐3‐hydroxyvalerate)/poly(ε‐caprolactone) block copolymers (PHCLs) with three different weight ratios of PCL blocks (38%, named PHCL‐38; 53%, named PHCL‐53; and 60%, named PHCL‐60) were synthesized by using PHBV with two hydroxyl end groups to initiate ring‐opening polymerization of ε‐caprolactone. During DSC cooling process, melt crystallization of PHCL‐53 at relatively high cooling rates (9, 12, and 15 °C min^?1) and PHCL‐60 at all the selected cooling rates corresponded to PCL blocks so that PHCL‐53 and PHCL‐60 were used to study the nonisothermal crystallization behaviors of PCL blocks. The kinetics of PCL blocks in PHCL‐53 and PHCL‐60 under nonisothermal crystallization conditions were analyzed by Mo equation. Mo equation was successful in describing the nonisothermal crystallization kinetics of PCL blocks in PHCLs. Crystallization activation energy were estimated using Kissinger's method. The results of kinetic parameters showed that both blocks crystallized more difficultly than corresponding homopolymers. With the increase of PCL content, the crystallization rate of PCL block increased gradually. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Electrospun fiber mats of poly(3‐hydroxybutyrate), poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate), and their blends

Electrospinning of poly(3‐hydroxybutyrate) (PHB), poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV), and their blends was first carried out in chloroform at 50 °C on a stationary collector. The average diameter of the as‐spun fiber from PHB and PHBV solutions decreased with increasing collection distance and increased with increasing solution concentration and applied electrical potential. In all of the spinning conditions investigated, the average diameter of the as‐spun pure fibers ranged between 1.6 and 8.8 μm. Electrospinning of PHB, PHBV, and their blends was carried out further at a fixed solution concentration of 14% w/v on a homemade rotating cylindrical collector. Well‐aligned, cross‐sectionally round fibers without beads were obtained. The average diameter of the as‐spun pure and blend fibers ranged between 2.3 and 4.0 μm. The as‐spun fiber mats appeared to be more hydrophobic than the corresponding films and much improvement in the tensile strength and the elongation at break was observed for the blend fiber mats over those of the pure fiber ones. Lastly, indirect cytotoxicity evaluation of the as‐spun pure and blend fiber mats with mouse fibroblasts (L929) indicated that these mats posed no threat to the cells. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2923–2933, 2006     

Miscible blends of poly(ethylene oxide) with brush copolymers of poly(vinyl alcohol)‐graft‐poly(l‐lactide)

Even though poly(ethylene oxide) (PEO) is immiscible with both poly(l ‐lactide) (PLLA) and poly(vinyl alcohol) (PVA), this article shows a working route to obtain miscible blends based on these polymers. The miscibility of these polymers has been analyzed using the solubility parameter approach to choose the proper ratios of the constituents of the blend. Then, PVA has been grafted with l ‐lactide (LLA) through ring‐opening polymerization to obtain a poly(vinyl alcohol)‐graft‐poly(l ‐lactide) (PVA‐g‐PLLA) brush copolymer with 82 mol % LLA according to ¹H and ¹³C NMR spectroscopies. PEO has been blended with the PVA‐g‐PLLA brush copolymer and the miscibility of the system has been analyzed by DSC, FTIR, OM, and SEM. The particular architecture of the blends results in DSC traces lacking clearly distinguishable glass transitions that have been explained considering self‐concentration effects (Lodge and McLeish) and the associated concentration fluctuations. Fortunately, the FTIR analysis is conclusive regarding the miscibility and the specific interactions in these systems. Melting point depression analysis suggests that interactions of intermediate strength and PLOM and SEM reveal homogeneous morphologies for the PEO/PVA‐g‐PLLA blends. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 1217–1226     

Crosslinked copolymer with low dielectric constant and dissipation factor based on poly(2,6‐Dimethylphenol‐co−2,6‐Diphenylphenol) and a crosslinker

The crosslinked poly(2,6‐dimethylphenol (95 mol %)‐co?2,6‐diphenylphenol (5 mol %)) (poly(2,6‐DMP₉₅‐co?2,6‐DPP₅)) was successfully developed as an insulating material separating conducting elements with a low dielectric constant and dissipation factor. The crosslinked poly(2,6‐DMP₉₅‐co?2,6‐DPP₅) was prepared by the oxidative coupling polymerization of 2,6‐DMP with 2,6‐DPP, followed by the reaction with 4,4′‐methylenebis[2,6‐bis(methoxymethyl)]phenol (MBMP) as a crosslinking agent. The crosslinked poly(2,6‐DMP₉₅‐co?2,6‐DPP₅) exhibited a good thermal stability and glass transition temperature. The dielectric constant and dissipation factor of the crosslinked poly(2,6‐DMP₉₅‐co?2,6‐DPP₅) were 2.6 and 0.004 at 10 GHz, respectively. Moreover, a flexible double layer copper clad laminate based on the crosslinked poly(2,6‐DMP₉₅‐co?2,6‐DPP₅) composite was successfully prepared, indicating a useful material for high‐speed and high‐frequency electrical applications. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 3218–3223     

Synthesis and pH‐responsive assembly of methoxy poly(ethylene glycol)‐b‐poly(ε‐caprolactone) with pendant carboxyl groups

pH‐responsive methoxy poly(ethylene glycol)‐b‐poly(ε‐caprolactone) bearing pendant carboxyl groups mPEG‐b‐P(2‐CCL‐co‐6‐CCL) was synthesized based on our newly monomer benzyloxycarbonylmethly functionalized ε‐caprolactone. Their structure was confirmed by ¹H NMR, ¹³C NMR, and Fourier transform infrared spectrum spectra. In addition, SEC results indicated that the copolymers had a relatively narrow polydispersity. WXRD and DSC demonstrated that the introduction of carboxymethyl groups had significant effect on the crystallinity of the copolymers. Furthermore, the solution behavior of mPEG‐b‐P(2‐CCL‐co‐6‐CCL) has been studied by various methods. The results indicated that mPEG‐b‐P(2‐CCL‐co‐6‐CCL) had a rich pH‐responsive behavior and the micelles could be formed by pH induction, and the mPEG‐b‐P(2‐CCL‐co‐6‐CCL) could existed as unimers, micelles or large aggregates in different pH range accordingly. The mechanism of which was supposed to depend on the counteraction between the hydrophobic interaction from PCL and the ionization of the carboxyl groups along the polymer chain. Moreover, the mPEG‐b‐P(2‐CCL‐co‐6‐CCL) copolymers displayed good biocompatibility according to the preliminary cytotoxicity study. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 188–199     

Preparation and characterization of biodegradable poly(lactic acid)‐ block‐poly(ε‐caprolactone) multiblock copolymer

Biodegradable copolymers of poly(lactic acid)‐block‐poly(ε‐caprolactone) (PLA‐b‐PCL) were successfully prepared by two steps. In the first step, lactic acid monomer is oligomerized to low molecular weight prepolymer and copolymerized with the (ε‐caprolactone) diol to prepolymer, and then the molecular weight is raised by joining prepolymer chains together using 1,6‐hexamethylene diisocyanate (HDI) as the chain extender. The polymer was carefully characterized by using ¹H‐NMR analysis, gel permeation chromatography (GPC), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and Fourier transform infrared spectroscopy (FTIR). The results of ¹H‐NMR and TGA indicate PLA‐b‐PCL prepolymer with number average molecular weights (M_n) of 4000–6000 were obtained. When PCL‐diols are 10 wt%, copolymer is better for chain extension reaction to obtain the polymer with high molecular weight. After chain extension, the weight average molecular weight can reach 250,000 g/mol, as determined by GPC, when the molar ratio of –NCO to –OH was 3:1. DSC curve showed that the degree of crystallization of PLA–PCL copolymer was low, even became amorphous after chain extended reaction. The product exhibits superior mechanical properties with elongation at break above 297% that is much higher than that of PLA chain extended products. Copyright © 2009 John Wiley & Sons, Ltd.     

Synthesis and characterization of macroinitiator‐amino terminated PEG and poly(γ‐benzyl‐L‐glutamate)‐PEO‐poly(γ‐benzyl‐L‐glutamate) triblock copolymer

Macroinitiator‐amino terminated poly(ethylene glycol) (PEG) (NH₂‐PEO‐NH₂) was prepared by converting both terminal hydroxyl groups of PEG to more reactive primary amino groups. The synthetic route involved reactions of chloridize, phthalimide and finally hydrazinolysis. Furthermore, poly(γ‐benzyl‐L ‐glutamate)‐poly(ethylene oxide)‐poly(γ‐benzyl‐L ‐glutamate) (PBLG‐PEO‐PBLG) triblock copolymer was synthesized by polymerization of γ‐benzyl‐L ‐glutamate N‐carboxyanhydride (Bz‐L‐GluNCA) using NH₂‐PEO‐NH₂ as macroinitiator. The resultant NH₂‐PEO‐NH₂ and triblock copolymer were characterized by FT‐IR, ¹H‐NMR and gel permeation chromatography (GPC) techniques. The results demonstrated that the degree of amination of the NH₂‐PEO‐NH₂ could be up to 1.95. The molecular weight of the PBLG‐PEO‐PBLG triblock copolymer could be adjusted easily by controlling the molar ratio of Bz‐L ‐Glu NCA to the macroinitiator NH₂‐PEO‐NH₂. Copyright © 2004 John Wiley & Sons, Ltd.     

Blends of poly(3‐hydroxybutyrate)/4,4′‐thiodiphenol and poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate)/ 4,4′‐thiodiphenol: Specific interaction and properties

The specific interaction between poly(3‐hydroxybutyrate) [P(3HB)] and 4,4′‐thiodiphenol (TDP) and between poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) and TDP was investigated by Fourier transform infrared (FTIR) spectroscopy. Interassociated hydrogen bonds were found between the polyester chains and the TDP molecules in the binary blends. The fractions of associated carbonyl groups, F_b 's, in the blends first increased and then decreased as the TDP content increased. The thermal and dynamic mechanical properties of P(3HB)–TDP and PHBV–TDP blends were investigated by differential scanning calorimetry and dynamic mechanical thermal analysis, respectively. Thermal analysis revealed that the P(3HB)–TDP blends possessed eutectic phase behavior. Furthermore, it was found that the thermal and dynamic mechanical properties of P(3HB) and PHBV were greatly modified through blending with TDP. Environmental degradability in river water was evaluated by a biochemical oxygen demand tester, and it was clarified that TDP lowered the degradation rate of P(3HB). The results suggest that TDP is effective in modifying the physical properties as well as the biodegradability of polyesters. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 2891–2900, 2000     

Studies on Binary Blends of Poly(3‐hydroxybutyrate‐co‐3‐hydroxyhexanoate) and Natural Polyphenol Catechin: Specific Interactions and Thermal Properties

The existence of a specific intermolecular hydrogen‐bonding interaction between poly(3‐hydroxybutyrate‐co‐3‐hydroxyhexanoate) [P(3HB‐co‐3HH)] and (+)‐catechin in their blends was demonstrated by Fourier‐transform infrared spectroscopy (FT‐IR). It was found that the experimentally estimated fraction of hydrogen‐bonded carbonyl groups was much lower than the theoretically predicted maximum fraction. Only one glass transition temperature (T_g) occurred in the blends with the compositions detected by differential scanning calorimetry (DSC), being further confirmed by the results of dynamic mechanical thermal analysis (DMTA). The decrease of the melting point (T_m) and the increase of the glass transition temperature of the blends observed by the DSC measurements also suggested the existence of a strong intermolecular interaction. It was interesting to note that, as a low‐molecular‐weight compound, catechin showed a glass transition, which arises from strong self‐association. As expected, the crystalline structure of P(3HB‐co‐3HH) in the blends showed no change, but the crystallinity of the copolymer component in the blends, calculated by wide‐angle X‐ray diffraction, decreased with the increase of catechin weight content. Investigated by tensile experiments, the maximum strength and modulus decreased sharply with the increase of catechin content; on the contrary, the elongation changed slowly.

The FT‐IR spectra in the wave‐number 1 680–1 780 cm^?1 region for blends of P(3HB‐co‐3HH)/catechin. A: HBH; B: HBHC10; C: HBHC20; D: HBHC30; E: HBHC40; F: HBHC50; and G: catechin.     

Synthesis and characterization of poly(vinyl alcohol)‐graft‐[poly(D,L‐lactide)/poly(D,L‐lactide‐co‐glycolide)] hydrogels

Poly(D ,L ‐lactide) and poly(D ,L ‐lactide‐co‐glycolide) with various composition and with one methacrylate and one carboxylate end group were synthesized and grafted onto poly(vinyl alcohol) (PVA) via the carboxylate group. The graft copolymers were crosslinked via the methacrylate groups using a free radical initiator. The polymer networks were characterized by means of NMR and studied qualitatively by means of IR spectroscopy. The influence of the glycolide content in the polyester grafts and of the number of ester units in the grafts on thermal properties and swellability were studied as well. The high swellability in water is characteristic of all hydrogels. Differential scanning calorimetry (DSC) showed a single glass transition temperature that occurs in the range between 51 and 69 °C. Thermogravimetric analysis (TGA) of the networks showed the main loss in weight in the temperature range between 290 and 370 °C. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4536–4544, 2007     

Synthesis of high‐molecular‐weight aliphatic–aromatic copolyesters from poly(ethylene‐co‐1,6‐hexene terephthalate) and poly(L‐lactic acid) by chain extension

A series of aliphatic–aromatic multiblock copolyesters consisting of poly(ethylene‐co‐1,6‐hexene terephthalate) (PEHT) and poly(L ‐lactic acid) (PLLA) were synthesized successfully by chain‐extension reaction of dihydroxyl terminated PEHT‐OH prepolymer and dihydroxyl terminated PLLA‐OH prepolymer using toluene‐2,4‐diisoyanate as a chain extender. PEHT‐OH prepolymers were prepared by two step reactions using dimethyl terephthalate, ethylene glycol, and 1,6‐hexanediol as raw materials. PLLA‐OH prepolymers were prepared by direct polycondensation of L ‐lactic acid in the presence of 1,4‐butanediol. The chemical structures, the molecular weights and the thermal properties of PEHT‐OH, PLLA‐OH prepolymers, and PEHT‐PLLA copolymers were characterized by FTIR, ¹H NMR, GPC, TG, and DSC. This synthetic method has been proved to be very efficient for the synthesis of high‐molecular‐weight copolyesters (say, higher than M_w = 3 × 10⁵ g/mol). Only one glass transition temperature was found in the DSC curves of PEHT‐PLLA copolymers, indicating that the PLLA and PEHT segments had good miscibility. TG curves showed that all the copolyesters had good thermal stabilities. The resulting novel aromatic–aliphatic copolyesters are expected to find a potential application in the area of biodegradable polymer materials. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5898–5907, 2009     

Biodegradable polyester/modified mesoporous silica composites for effective bone repair with self‐reinforced properties

A series novel composites based on poly(_L‐lactide) (PLLA) oligomer modified mesoporous silica (MCM41) homogeneous dispersed into poly(_L‐lactide‐co‐trimethylene carbonate‐co‐glycolide) (PLTG) terpolymer has been successfully prepared. The structure of PLTG terpolymer was characterized by ¹H NMR. The structure and properties of modified and unmodified MCM41 were attested by Fourier transform infrared spectroscopy (FTIR), thermogravimetric analyzer (TGA), X‐ray diffraction (XRD), N₂ adsorption–desorption, scanning electron microscope (SEM), and transmission electron microscope (TEM), which demonstrated that the MCM41 was successfully grafted by the PLLA oligomer. The effect of different concentration of modified MCM41 in PLTG matrix on thermal properties, mechanical properties, and hydrophilicity was investigated by TGA, differential scanning calorimetry (DSC), mechanical testing, contact angle measurement, and SEM. The results of mechanical tests showed that 5 wt% of modified MCM41 nanoparticles gave rise to optimal reinforcing effect. The tensile strength, Young's modulus, and elongation at break of the PLTG/PLLA‐MCM41 (5%) composites were 33.2 Mpa, 1.58 Gpa, and 268.7%, respectively, which were all higher than the PLTG/MCM41 (5%) composites and pristine PLTG matrix, which were due to good interfacial adhesion between the PLTG matrix and MCM41 nanoparticles. TGA and DSC have shown that 5% modified MCM41 in the PLTG increased the temperature of composite degradation and T_g. Water contact angle measurement showed the hydrophilicity of the composites increases with the increase of modified MCM41 content. The live/dead assay showed that the modified MCM41 existing on the PLTG matrix presents very excellent cytocompatibility. Therefore, the novel composite material represents promising way for bone tissue engineering application.     

Composites of poly(L‐lactide‐trimethylene carbonate‐glycolide) and surface modified SBA‐15 as bone repair material

This work aims to develop novel composites from a poly(L ‐lactide‐co‐trimethylene carbonate‐co‐glycolide) (PLTG) terpolymer and mesoporous silica (SBA‐15) nanofillers surface modified by post‐synthetic functionalization. SBA‐15 first reacts with a silane coupling agent, γ‐aminopropyl‐trimethoxysilane to introduce ammonium group. PLLA chains were then grafted on the surface of SBA‐15 through ammonium initiated ring‐opening polymerization of L ‐lactide. Composites were prepared via solution mixing of PLTG terpolymer and surface modified SBA‐15. The structures and properties of pure SBA‐15, γ‐aminopropyl‐trimethoxysilane modified SBA‐15 (H₂N‐SBA‐15), PLLA modified SBA‐15 (PLLA‐NH‐SBA‐15), and PLTG/PLLA‐NH‐SBA‐15 composites were characterized by Fourier transform infrared spectroscopy, thermogravimetric analysis, X‐ray diffraction, scanning electron microscopy, energy‐dispersive X‐ray spectroscopy, transmission electron microscopy, N₂ adsorption‐desorption, differential scanning calorimetry, contact angle measurement, and mechanical testing. The results demonstrated that PLLA chains were successfully grafted onto the surface of SBA‐15 with grafting amounts up to 16 wt.%. The PLTG/PLLA‐NH‐SBA‐15 composites exhibit good mechanical properties. The tensile strength, Young's modulus, and elongation at break of the composite containing 5 wt.% of PLLA‐NH‐SBA‐15 were 39.9 MPa, 1.3 GPa, and 273.6%, respectively, which were all higher than those of neat PLTG or of the composite containing 5 wt.% of pure SBA‐15. Cytocompatibility tests showed that the composites present very low cytotoxicity.     

Synthesis,structural analysis,and visualization of poly(2‐ethynyl‐9‐substituted carbazole)s and poly(3‐ethynyl‐9‐substituted carbazole)s containing chiral and achiral minidendritic substituents

The synthesis of 2‐ethynyl‐9‐substituted carbazole and 3‐ethynyl‐9‐substituted carbazole monomers containing first‐generation chiral and achiral dendritic (i.e., minidendritic) substituents, 2‐ethynyl‐9‐[3,4,5‐tris(dodecan‐1‐yloxy)benzyl]carbazole (2ECz), 3‐ethynyl‐9‐[3,4,5‐tris(dodecan‐1‐yloxy)benzyl]carbazole (3ECz), 2‐ethynyl‐9‐{3,4,5‐tris[(S)‐2‐methylbutan‐1‐yloxy]benzyl}carbazole (2ECz*), and 3‐ethynyl‐9‐{3,4,5‐tris[(S)‐2‐methylbutan‐1‐yloxy]benzyl}carbazole (3ECz*), is presented. All monomers were polymerized and copolymerized by stereospecific polymerization to produce cis‐transoidal soluble stereoisomers. A structural analysis of poly(2ECz), poly(2ECz*), poly(3ECz), poly(3ECz*), poly(2ECz*‐co‐2ECz), and poly(3ECz*‐co‐3ECz) by a combination of techniques, including ¹H NMR, ultraviolet–visible, and circular dichroism spectroscopy, thermal optical polarized microscopy, and X‐ray diffraction experiments, demonstrated that these polymers had a helical conformation that produced cylindrical macromolecules exhibiting chiral and achiral nematic phases. Individual chains of these cylindrical macromolecules were visualized by atomic force microscopy. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3509–3533, 2002