Dynamics of ions produced by laser ablation of ceramic Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and Al at 193 nm

We study the dynamics of ions produced upon ablation of Al and ceramic Al₂O₃ targets using nanosecond laser pulses at 193 nm (6.4 eV) as a function of the laser fluence from threshold up to 12 J cm⁻². An electrical (Langmuir) probe located at 40 mm from the target surface has been used for determining the ion yield and calculating the kinetic energy distributions. The results for both targets show the existence of a significant amount of ions having kinetic energies >200 eV (≈20% around threshold fluence), and kinetic energies are up to >1.5 keV. The results are related with the existence of direct photonionization processes caused by the photon energy of the laser being higher than the ionization potential of Al (5.98 eV). Comparison of the ion yield when ablating the two types of targets for fluences above threshold to data reported in the literature suggests that the magnitude of the yield and its threshold are parameters depending on the thermal properties of the target rather than on the laser wavelength. Around threshold, the different behavior of ion yield when ablating Al and Al₂O₃ targets suggests that the threshold for neutral aluminium and ion species in the case of ablation of the Al₂O₃ target must be similar.     

RF-plasma assisted pulsed laser deposition of nitrogen-doped SrTiO3 thin films

Perovskite-type nitrogen substituted SrTiO₃ thin films were deposited with a one-step process by RF-plasma assisted pulsed laser deposition from a SrTiO₃ target using a N₂ plasma, while deposition with a NH₃ plasma yields films with almost no incorporated nitrogen. The deposited films exhibit a cubic perovskite-type crystal structure and reveal oriented growth on MgO(100) substrates. The unit cell parameters of the studied N-doped SrTiO₃ films range within 3.905<a<3.918 Å, which is slightly larger than for SrTiO₃ (a=3.905 Å). The nitrogen content in the deposited films varies from 0.2 to 0.7 atom%. The amount of incorporated nitrogen in the films decreases with increasing RF-power, while the N₂ flow rate does not have any pronounced influence on the N content. Nitrogen incorporation results in an increased optical absorption at 400–600 nm, which is associated with N(2p) energy states that have a higher energy level than the valence band in strontium titanate. The optical band gap energies in the studied N-doped SrTiO₃ films are at 3.2–3.3 eV, which is very similar to that of pure strontium titanate (～3.2 eV). Films deposited with NH₃ for the RF-plasma exhibit a lower degree of crystallinity and reveal almost no nitrogen incorporation into the crystal lattice.     

Production and characterization of Nd,Cr:GSGG thin films on Si(001) grown by pulsed laser ablation

Nd,Cr:Gd₃Sc₂Ga₃O₁₂ (GSGG) thin films have been produced for the first time. They were grown on Si(001) substrates at 650 °C by pulsed laser ablation at 248 nm of a crystalline Nd,Cr:GSGG target rod. The laser plume was analyzed using time-of-flight quadrupole mass spectroscopy, and consisted of elemental and metal oxide fragments with kinetic energies typically in the range 10 to 40 eV, though extending up to 100 eV. Although films deposited in vacuum using laser fluences of 0.8±0.1 J cm⁻² reproduced the Nd,Cr:GSGG bulk stoichiometry, those deposited using fluences above ≈3 J cm⁻² resulted in noncongruent material transfer and were deficient in Ga and Cr. Attempts to grow films using synchronized oxygen or oxygen/argon pulses yielded mixed oxide phases. Under optimal growth conditions, the films were heteroepitaxial, with GSGG(001)[100]∥Si(001)[100], and exhibited Volmer–Weber-type growth. Room-temperature emission spectra of the films suggest efficient non-radiative energy transfer between Cr³⁺ and Nd³⁺ ions, similar to that of the bulk crystal. Received: 1 October 1999 / Accepted: 15 October 1999 / Published online: 23 February 2000     

Hardnes and resistivity of amorphous carbon thin films deposited by laser ablation

Amorphous carbon thin films were deposited by laser ablation of a graphite target, using the fundamental line of a 5 ns Nd:YAG laser. Deposition was carried out as a function of the plasma parameters (mean kinetic ion energy and plasma density), determined by means of a planar probe. In the selected working regimes the optical emission from the plasma is mainly due to atomic species, namely C⁺ (426.5 nm); however, there is also emission from other atomic species and molecular carbon. The hardness and resistivity could be varied in the range between 10 and 25 GPa, and 10⁸ and 10¹¹ Ω cm, respectively. The maximum values were obtained at a 200 eV ion energy and 6×10¹³ cm⁻³ plasma density, where the maximum quantity of C–C sp³ bonds was formed, as confirmed by Raman spectroscopy.     

Structural and electrical properties of lithium manganese oxide thin films grown by pulsed laser deposition

LiMn₂O₄ thin films were deposited by reactive pulsed laser deposition technique and studied the microstructural and electrical properties of the films. The LiMn₂O₄ thin films deposited in an oxygen partial pressure of 100 mTorr and at a substrate temperature of 573 K from a lithium rich target were found to be nearly stoichiometric. The films exhibited predominantly (111) orientation representing the cubic spinel structure with Fd3m symmetry. The intensity of (111) peak increased and a slight shift in the peak position was observed with the increase of substrate temperature. The lattice parameter increased from 8.117 to 8.2417 Å with the increase of substrate temperature from 573 to 873 K. The electrical conductivity of the films is observed to be a strong function of temperature. The evaluated activation energy for the films deposited at 873 K is 0.64 eV.     

Ionized physical vapor deposited Al2O3 films: Does subplantation favor formation of α‐Al2O3?

The broad energy distributions of the condensing particles typically encountered in ion assisted vapor deposition techniques are often a drawback when attempting to understand the effect of the energetic bombardment on the film properties. In the current study, a monoenergetic Al⁺ beam generated by a filtered cathodic arc discharge is employed for the deposition of alumina (Al₂O₃) films at well defined Al⁺ ion energies between 4 eV and 200 eV at a substrate temperature of 720 °C. Structural analysis shows that Al⁺ energies of 40 eV or larger favor the formation of the thermodynamically stable α‐Al₂O₃ phase at the expense of other metastable Al₂O₃ polymorphs. The well defined ion energies are used as input for Monte‐Carlo based simulations of the ion–surface interactions. The results of these simulations reveal that the increase of the Al⁺ ion energy leads to an increase in the fraction of ions subplanted into the growing film. These findings underline the previously not considered role of subsurface processes on the phase formation of ionized physical vapor deposited Al₂O₃ films. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Determining the properties of pulsed laser deposited thin films by controlling the kinetic energy of the film-forming particles

The deposition of Al₂O₃ thin films by pulsed KrF excimer laser radiation (248 nm) on fused silica substrates is investigated as a function of the processing variables: laser fluence, processing gas pressure and target-to-substrate distance. The kinetic energy of the Al species in the laser-generated plasma, as measured by time-of-flight optical emission spectroscopy and time-of-flight quadrupole mass spectrometry, is described as a function of the type and pressure of the processing gas, the distance from target, and the laser fluence. The influence of the kinetic energy of the film-forming particles on the density and the refractive index of the resulting films, determined by ellipsometry, is investigated. The densification of the Al₂O₃ thin films to 94% of the bulk value is achieved by film-forming Al particles impinging on the growing surface with mean kinetic energies of about 25 eV.     

Molecular materials derived from MPc (M=Fe, Pb, Co) and 1,8-dihydroxiantraquinone thin films: Formation, electrical and optical properties

Semiconductor-like thin films were grown using metallic phthalocyanines (MPc) (M=Fe, Pb, Co) and 1,8 dihydroxiantraquinone as initial compounds. The morphology of the deposited films was studied by using scanning electron microscopy and atomic force microscopy. The powder and thin-film samples of the synthesized materials, deposited by vacuum thermal evaporation, showed the same intra-molecular bonds as in IR spectroscopy studies, which suggests that the evaporation process does not alter these bonds. The optical band gap values of C₆₀H₂₈N₈O₈Fe, C₆₀H₂₈N₈O₈Pb and C₆₀H₂₈N₈O₈Co calculated from the absorption coefficient were found to be 1.60, 1.89 and 1.75 eV, respectively, arising from non-direct transitions. The effect of temperature on conductivity was also measured in these samples. It was found that the temperature-dependent electric current in all cases showed a semiconductor behavior with conductivities in the order of 10⁻⁶ Ω⁻¹ cm⁻¹ where the highest value corresponded to the cobalt material. The linear dependence observed in the films implies only one type of conduction mechanism in all cases, with mean activation energies of the order of 1.55, 1.77 and 1.50 eV for iron, lead and cobalt-based thin films, respectively.     

Optical and structural properties of thin films deposited from laser fused Zirconia,Hafnia, and Yttria

The optical and structural properties of films deposited from laser sintered Zirconia (ZrO₂), Hafnia (HfO₂), and Yttria (Y₂O₃) and from the commercially available (unprocessed material) Zirconia, Hafnia and Yttria, were studied and compared. All the films had low absorption. Films deposited from the laser sintered material had very low optical inhomogeneity. ZrO₂ films showed negative inhomogeneity for films deposited from the unprocessed material. The refractive index increased for ZrO₂ films deposited from the laser sintered material. HfO₂ and Y₂O₃ films showed positive inhomogeneity when deposited from the unprocessed material. The refractive index of the films of these materials decreased when deposited from the laser sintered material. The thin films of ZrO₂ and Y₂O₃ prepared from laser sintered material had stable monoclinic and cubic structures respectively while HfO₂ films were found to be amorphous.     

A comparative study of gadolinium gallium garnet growth by femtosecond and nanosecond pulsed laser deposition

The growth of epitaxial Nd:Gd₃Ga₅O₁₂ (GGG) on Y₃Al₅O₁₂ (YAG) by femtosecond pulsed laser deposition is reported. We have used a Ti:sapphire laser at a wavelength of 800 nm and pulse length of 130 fs, operating at a repetition rate of 1 kHz. The film properties have been studied systematically as a function of the deposition parameters of laser fluence, spot-size, oxygen pressure, target-substrate distance and temperature. Scanning electron microscopy, atomic force microscopy and X-ray diffractometry were used to characterise the surface structure and crystallinity of the films. X-ray diffraction analysis shows that epitaxial growth has occurred. A comparison between the ion velocities produced by nanosecond and femtosecond laser ablation of the GGG target material has been investigated by the Langmuir probe technique. The results indicate a large difference in the plasma characteristics between femtosecond and nanosecond ablation, with ion velocities up to eight times faster observed in the femtosecond case.     

Anatase TiO2 films fabricated by pulsed laser deposition using Ti target

TiO₂ films were prepared by pulsed laser deposition using a metallic Ti target in an O₂ gas ambient. The microstructure along with optical and photocatalytic properties of the deposited films were systematically studied by changing the deposition parameters and substrates. It was found that TiO₂ films having nearly pure anatase phase grew effectively in O₂ atmosphere. When the films were fabricated at a substrate temperature of 400°C, their phase structures were greatly affected by the O₂ gas pressure, and nearly pure anatase phase with typical (101) and (004) peaks can be obtained under an O₂ pressure of 15 Pa. For the deposition at 700°C, the crystal structure of the TiO₂ films exhibited a strong anatase (004) peak and was inert to the oxygen pressures. Two modes, namely a substrate-temperature-controlled mode and an oxygen-pressure-controlled mode, were considered for the growth of the anatase TiO₂ films under different substrate temperatures. In addition, the optical and photocatalytic properties were found to be sensitive to both the microstructure and grain size of the TiO₂ films.     

Nanoindentation on carbon thin films obtained from a C60 ion beam

Raman spectra, atomic force microscope (AFM) images, hardness (H) and Young's modulus (E) measurements were carried out in order to characterize carbon thin films obtained from a C₆₀ ion beam on silicon substrates at different deposition energies (from 100 up to 500 eV). The mechanical properties were studied via the nanoindentation technique. It has been observed by Raman spectroscopy and AFM that the microstructure presents significant changes for films deposited at energies close to 300 eV. However, these remarkable changes have not been noticeable on the mechanical properties: apparently H and E increase with higher deposition energy up to ∼11 and ∼116 GPa, respectively. These values are underestimated if the influence of the film roughness is not taken into account.     

Preparation of Co:TiO2 thin films by crossed-beam pulsed laser deposition

Co:TiO₂ thin films were deposited using two interacting plasmas produced from different targets, TiO₂ and cobalt. By keeping constant the laser ablation conditions on the TiO₂ target and changing them on the Co target, it was possible to vary in a controlled way the Co content in the films. The cobalt plasma parameters, such as the ion kinetic energy and plasma density, were determined for each deposition condition in an attempt to correlate them with the material’s properties. The cobalt ion mean kinetic energy was varied from 36 to 789 eV, resulting in films with Co content from 1.2 up to 5.1 at.%, respectively, revealing that the cobalt content can be controlled by the Co⁺ kinetic energy. The study of the optical properties showed that the optical band gap decreased from 2.9 to 2.0 eV as the Co content increased. Raman spectroscopy was used to characterize the microstructure of the deposits, and the obtained results suggest the formation of two coexisting phases: TiO₂ in its rutile phase and CoTiO₃. It was found that as the Co⁺ energy increases, the CoTiO₃ phase develops in a greater quantity. XPS measurements confirm the Raman spectroscopy results.     

多孔TiO2/Al/SiO2纳米复合结构的紫外光吸收特性研究

在SiO₂玻璃衬底上用脉冲激光沉积(PLD)技术,分别沉积Ti和Ti/Al膜,经电化学阳极氧化成功制备了多孔TiO₂/SiO₂和TiO₂/Al/SiO₂纳米复合结构. 其中TiO₂薄膜上的微孔阵列高度有序,分布均匀. 实验研究了Al过渡层对多孔TiO₂薄膜光吸收特性的影响. 结果表明：无Al过渡层的多孔TiO₂薄膜其紫外吸收峰在27 关键词： 2薄膜')" href="#">多孔TiO₂薄膜 阳极氧化 紫外光吸收     

多孔TiO2/Al/SiO2纳米复合结构的紫外光吸收特性研究

在SiO₂玻璃衬底上用脉冲激光沉积(PLD)技术，分别沉积Ti和Ti/Al膜，经电化学阳极氧化成功制备了多孔TiO₂/SiO₂和TiO₂/Al/SiO₂纳米复合结构. 其中TiO₂薄膜上的微孔阵列高度有序，分布均匀. 实验研究了Al过渡层对多孔TiO₂薄膜光吸收特性的影响. 结果表明：无Al过渡层的多孔TiO₂薄膜其紫外吸收峰在27     

Visible-light photocatalysis of nitrogen-doped TiO2 nanoparticulate films prepared by low-energy ion implantation

Nitrogen-doped TiO₂ (N-TiO₂) films were prepared by low-energy implantation of nitrogen ions into pulsed laser deposited anatase TiO₂ films. The anatase phase of the films was not changed by the implantation with very low energy of 200 eV. XPS measurements revealed that the implanted nitrogen species were mainly interstitial ones. The nitrogen concentration was increased with increasing ion flux which could be controlled by adjusting the gas flow rate of the ion source. All the produced N-TiO₂ films exhibited visible-light photocatalytic activities in degradation of methylene blue in aqueous solutions, indicating that interstitial nitrogen could also be responsible for the photocatalysis in visible region. Higher visible-light photocatalytic efficiency was achieved with higher implanted nitrogen concentration.     

Post-annealing effect upon optical properties of electron beam evaporated molybdenum oxide thin films

Molybdenum oxide (MoO₃) thin films were deposited by electron beam evaporation. The chemical composition, microstructure, optical and electrical properties of MoO₃ thin films depend on the annealing temperature and ambient atmosphere. X-ray diffraction (XRD) shows that crystalline MoO₃ films can be obtained at various post-annealing temperatures from 200 to 500 °C in N₂ and O₂. X-ray photoelectron spectroscopy (XPS) results reveal that the O-1s emission peak was shifted slightly toward lower binding energies as the annealing temperature in N₂ was increased. The oxygen vacancies and conductivity of MoO₃ film increased with the annealing temperature. However, when the MoO₃ films were annealed in an atmosphere of O₂, the optical transmission, the O/Mo ratio and the photon energy increased with the annealing temperature. The results differ from those for films annealed in a N₂ atmosphere.     

Preparation and characterization of ferroelectric SrBi2Ta2O9 thin films on Si using Al2O3 buffer layers

SrBi₂Ta₂O₉ (SBT) thin films were prepared on p-type Si(100) substrates with Al₂O₃ buffer layers. Both the SBT films and the Al₂O₃ buffer layers were deposited by a pulsed laser deposition technique using a KrF excimer laser. An Al prelayer was used to prevent Si surface oxidization in the initial growth stage. It is shown that Al₂O₃ buffer layers effectively prevented interdiffusion between SBT and Si substrates. Furthermore, the capacitance–voltage (C-V) characteristics of the SBT/Al₂O₃/Si heterostructures show a hysteresis loop with a clockwise trace, demonstrating the ferroelectric switching properties of SBT films and showing a memory window of 1.6 V at 1 MHz. Received: 17 July 2000 / Accepted: 16 August 2000 / Published online: 30 November 2000     

Microstructure and electrical conductivity of YSZ thin films prepared by pulsed laser deposition

Yttria-stabilized zirconia (YSZ) is the most common solid electrolyte material used e.g. in ceramic fuel cells. Thin films of YSZ were deposited on c-cut sapphire single crystals by pulsed laser deposition using a KrF excimer laser focused on a polycrystalline 8 mol% Y₂O₃-stabilized ZrO₂ target. Depending on the substrate temperature and the oxygen background pressure during deposition, different microstructures are obtained. XRD and high-resolution SEM revealed the formation of dense amorphous films at room temperature. At 600°C preferentially (111) oriented polycrystalline films consisting of densely agglomerated nm-sized grains of the cubic phase resulted. Grain size and surface roughness could be controlled by varying the oxygen background pressure. RBS and PIXE evidenced congruent transfer only for a low number of pulses, indicating a dynamical change of the target stoichiometry during laser irradiation. The in-plane ionic conductivity of the as-deposited crystalline films was comparable to bulk YSZ. The conductivity of initially amorphous YSZ passes a maximum during the crystallization process. However, the relative changes remain small, i.e. no significant enhancement of ionic conductivity related to the formation of a nanocrystalline microstructure is found.     

Effect of 100 MeV O7+ ion beam irradiation on structural,optical and electronic properties of SnO2 thin films

In this paper, we present the impact of swift heavy ion beam irradiation on the structural, optical and electronic properties of SnO₂ thin films. Thin films were deposited using the pulsed laser deposition technique on Al₂O₃ substrates. Atomic force microscopy, X-ray diffraction, UV–visible absorption and temperature-dependent resistivity measurements were performed to explore the morphological, structural, optical and electronic properties of the as-deposited and irradiated samples. The peak intensity of the (200) peak was found to decrease monotonously with increasing irradiation fluence. The band gap energy of the 1×10¹¹ ion/cm² irradiated sample was found to increase. The electrical resistivity of the samples showed a continuous increase with the irradiation fluence.