W doping-dependent structural and ferroelectric properties of SrBi2Nb2O9 ferroelectric ceramics

The structural and ferroelectric characteristics of SrBi₂(Nb_1−xW_x)₂O₉ (x=0–0.12) ferroelectric ceramics were investigated. SrBi₂(Nb_1−xW_x)₂O₉ ceramics consisted of a single-phase layered perovskite structure when x was less than 0.06. Uniform microstructure and grain size reduction were observed after the introduction of W. The maximum remanent polarization of 16 μC/cm² appeared at x=0.03, and the coercive field decreased with increasing concentration of W. The ferroelectric behavior of SrBi₂(Nb_1−xW_x)₂O₉ ceramics is interpreted based on the Raman measurement.     

Structural and electrical properties of crystalline (1−x)Ta2O5−xTiO2 thin films fabricated by metalorganic decomposition

Polycrystalline (1−x)Ta₂O₅−xTiO₂ thin films were formed on Si by metalorganic decomposition (MOD) and annealed at various temperatures. As-deposited films were in the amorphous state and were completely transformed to crystalline after annealing above 600 °C. During crystallization, a thin interfacial SiO₂ layer was formed at the (1−x)Ta₂O₅−xTiO₂/Si interface. Thin films with 0.92Ta₂O₅–0.08TiO₂ composition exhibited superior insulating properties. The measured dielectric constant and dissipation factor at 1 MHz were 9 and 0.015, respectively, for films annealed at 900 °C. The interface trap density was 2.5×10¹¹ cm⁻² eV⁻¹, and flatband voltage was −0.38 V. A charge storage density of 22.8 fC/μm² was obtained at an applied electric field of 3 MV/cm. The leakage current density was lower than 4×10⁻⁹ A/cm² up to an applied electric field of 6 MV/cm.     

A study on the nonstoichiometry of tin oxides by coulometric titration

In this investigation, nonstoichiometries and defect structures of tin oxides were studied between 694 and 990 K by coulometric titration using solid state electrolyte (YSZ) cells. The relationship between nonstoichiometry of the oxide (x) and equilibrium oxygen partial pressure (P_o2) was expressed by the proportionality: xP_O2^−1/6. An intermediate oxide phase, Sn₃O₄ between Sn and SnO₂ was observed in the temperature range of 696–732 K. The standard Gibbs energy of formation of Sn₃O₄ via the reaction; was found to be ΔG^o_Sn3O4 = −1163960+417.36 T (J/mol). The standard Gibbs energy change for the defect formation reaction in SnO_2−x was calculated to be ΔG^o_SnO2−x = 3.05×10⁵−38.97 T (J/mol)).     

Transient creep of YBa2Cu3O7−x superconductor

Rapid changes of oxygen partial pressure (P_O2) between 10³ and 2.1×10⁴ Pa have been carried out during steady-state plastic deformation of polycrystalline YBa₂Cu₃O_7−x (YBCO) at temperatures between 825 and 900°C. Transient creep was observed after such P_O2 changes. The analysis of these creep transients allowed the determination of the chemical diffusion coefficient for reequilibration, which is identical to that found from thermogravimetry and electrical conductivity experiments for oxygen vacancies.     

Oxygen diffusion and surface exchange in La1−xSrxFe0.8Cr0.2O3−δ (x=0.2, 0.4 and 0.6)

Oxygen tracer diffusion (D*) and surface exchange rate constant (k*) have been measured, using isotopic exchange and depth profiling by secondary ion mass spectrometry (SIMS), in La_1−xSr_xFe_0.8Cr_0.2O_3−δ (x=0.2, 0.4 and 0.6). Measurements were made as a function of temperature (700–1000 °C) and oxygen partial pressure (0.21–10⁻²¹ atm) in dry oxygen, water vapour and water vapour/hydrogen/nitrogen mixtures. At high oxygen activity, D* was found to increase with increasing temperature and Sr content. The activation energies for D* in air are 2.13 eV (x=0.2), 1.53 eV (x=0.4) and 1.21 eV (x=0.6). As the oxygen activity decreases, D* increases as expected qualitatively from the increase in oxygen vacancy concentration. Under strongly reducing conditions, the measured values of D* at 1000 °C range from 10⁻⁸ cm² s⁻¹ for x=0.2 to 10⁻⁷ cm² s⁻¹ for x=0.4 and 0.6. The activation energies determined at constant H₂O/H₂ ratio are 1.21 eV (x=0.2), 1.59 eV (x=0.4) and 0.82 eV (x=0.6).

The surface exchange rate constant of oxygen for the H₂O molecule is similar in magnitude to that for the O₂ molecule and both increase with increasing Sr concentration.     

Improvement of the magnetic properties of low-neodymium magnets by minor addition of titanium

Rapidly solidified nanocomposite Nd₉Fe_77−xB₁₄Ti_x alloys, consisting of magnetic Nd₂Fe₁₄B phase and soft magnetic phases, were investigated. The effect of titanium addition on the structure and magnetic properties was studied. It was found that 2–4 at% Ti addition leads to substantial increase of the coercivity and maximum energy product, maintaining the remanence unchanged. The highest properties: J_r=0.81 T, _JH_c=907 kA/m, (BH)_max=99 kJ/m³, were achieved for the Nd₉Fe₇₃B₁₄Ti₄ alloy. This effect we attribute to the formation of fine and homogeneous grain structure and a change of the phase morphology in the Ti-containing alloys. The initial magnetization curve indicates a change of the coercivity mechanisms giving rise to pinning of domain walls, which is caused by reduction of the crystallite size.     

Very strong interlayer exchange coupling in epitaxial Fe/Fe1−xSix/Fe trilayers (x=0.4–1.0)

Fe/Fe_1−xSi_x/Fe (x=0.4–1.0) wedge-type epitaxial trilayers with improved homogeneity are grown by co-evaporation from two electron-beam sources. The coupling strengths of the bilinear (J₁) and biquadratic (J₂) coupling terms are derived from Brillouin light scattering (BLS) spectra and longitudinal MOKE hysteresis loops. The total coupling strength J=J₁+J₂ increases dramatically with increasing x and reaches values in excess of 6 mJ/m².     

Oxygen tracer diffusion in La1 − xSrxCoO3

Tracer diffusion of ¹⁸O in dense, polycrystalline La_1−xSr_xCoO₃ for x = 0.1 has been measured in the temperature range 400 to 600 °C and at 500 °C for x = 0.2 at an oxygen partial pressure of 1 × 10⁵ Pa. Depth profiles were obtained by secondary ion mass spectrometry. The diffusion coefficient for La_0.9Sr_0.1CoO₃ is given by D = (17–247) exp[(−232 ± 8 kJ/mole)/RT] cm²/s. This value is several orders of magnitude lower than D extrapolated from the results for x = 0.2 measured in the 700–900 °C temperature range. One possible explanation for the discrepancy is that the two measurements reflect different diffusion paths. As expected, La_0.8Sr_0.2CoO₃ exhibits a higher diffusivity at 500 °C than does La_0.9Sr_0.1CoO₃.     

Enhanced magnetic properties of Nd–Fe–B thin films crystallized by heat treatment

Nd₂Fe₁₄B Φ phase crystallites were formed in Nd_16.7Fe_65.5B_17.8 thin films prepared by RF sputtering with subsequent heat treatment. The 2 μm-thick films were deposited onto 0.1 mm Mo sheets at an average substrate temperature (T_s) of 365°C. The enhanced magnetic properties of the magnetically anisotropic thin films were investigated using different heating rates (h_r) of 10°C, 20°C, 50°C and 100°C/min in an annealing experiment. Transformation from the amorphous phase to the crystalline phase is clearly manifested by the formation of fine crystallites embedded as a columnar matrix of Nd₂Fe₁₄B phase. High-resolution scanning electron microscope data of the cross-section of the annealed films show columnar stacking of Nd₂Fe₁₄B crystallites with sizes <500 nm. Transmission electron microscope observations revealed that the microstructure of these films having out-of-plane magnetization consists of uniformly distributed Φ phase with grain size around 400 nm together with small Nd rich particles. This grain size of Φ phase is comparable to the single domain particle diameter of Nd₂Fe₁₄B. Significant change in _iH_c, 4πM_r and 4πM_s with h_r was confirmed. Annealing conditions with a heating rate of 50°C/min to an annealing temperature (T_a) of 650°C for 30 min was consequently found to give optimum properties for the NdFeB thin films. The resulting magnetic properties, considered to be the effect of varying h_r were _iH_c= 1307–1357 kA/m, 4πM_r=0.78–1.06 T and 4πM_s=0.81–1.07 T.     

The relationship between crystal structure and electrical conductivity in the LaY1−xInxO3 (x=0.0–0.7) system

The electrical conductivity of the LaY_1−xIn_xO₃ (x=0.0–0.7) system has been studied from the viewpoint of crystal chemistry. The high temperature form of LaYO₃ (x=0.0) was ascertained to be the Sm₂O₃-type (B-type rare earth) structure, not perovskite-type one. The X-ray diffraction (XRD) experiments revealed that the samples with x=0.05 and 0.10 were the mixed phase of Sm₂O₃-type and perovskite-type structure, and changed to perovskite phase in the range of x0.20. From oxygen partial pressure dependence of the electrical conductivity, it was found that both the Sm₂O₃-type and the perovskite-type single phases showed hole conduction, but the mixed phase did oxide-ion one. The electrical conductivity of the LaY_1−xIn_xO₃ (x=0.0–0.7) system increased with increasing x, and showed the maximum value in the range of x=0.05–0.10, and then decreased with increasing x. The occurrence of oxide-ion conduction was discussed from the viewpoint of lattice distortion in the mixed phase.     

Gas source MBE grown wavelength extended 2.2 and 2.5 μm InGaAs PIN photodetectors

Using homo-junction structure and relative thin linear graded In_xGa_1−xAs as the buffer layer, extended wavelength InGaAs PIN photodetectors with cut-off wavelength of 2.2 and 2.5 μm at room temperature have been grown by using GSMBE, and their performance over a wide temperature range have been extensively investigated. For those 2.2 or 2.5 μm detectors with 100 μm diameter, the typical dark current (V_R = 10 mV) and R₀A are 57 nA/10.3 Ω cm² or 67 nA/12.7 Ω cm² at 290 K, and 84 pA/4.70 kΩ cm² or 161 pA/3.12 kΩ cm² at 210 K respectively. The thermal activation energies of the dark current are 0.447 eV or 0.404 eV for 2.2 or 2.5 μm detectors respectively.     

Structural and optical properties of thermally evaporated Bi2Te3 films

Bi₂Te₃ films were prepared by thermal evaporation technique. X-ray diffraction analysis for as-deposited and annealed films in vacuum at 150 °C were polycrystalline with rhombohedral structure. The crystallite size is found to increase as the film thickness increases and has values in the range 67–162 nm. The optical constants (the refractive index, n, and absorption index, k) were determined using transmittance and reflectance data in the spectral range 2.5–10 μm for Bi₂Te₃ films with different thicknesses (25–99.5 nm). Both n and k are independent on the film thickness in the investigated range. It was also found that Bi₂Te₃ is a high refractive index material (n has values of 4.7–8.8 in the wavelength range 2.5–10 μm). The allowed optical transitions were found to be direct optical transitions with energy gap  eV. The optical conductivities σ₁ = ƒ(hν) and σ₂ = f(hν) show distinct peaks at about 0.13 and 0.3 eV, respectively. These two peaks can be attributed to optical interband transitions.     

Effects of cation- or oxide ion-defect on conductivities of apatite-type La–Ge–O system ceramics

A series of apatite-type La–Ge–O ceramics were prepared and their cation-defect at the 4f+6h sites and oxide ion-defect at 2a site were investigated. In La_xGe₆O_12+1.5x ceramics of x=6–12, the higher conductivities were obtained in the region of apatite composition, La_x(GeO₄)₆O_1.5x−12 (x=8–9.33), and the highest conductivity was achieved for La₉(GeO₄)₆O_1.5 (x=9), where the number of cation (La³⁺) occupying the 4f+6h sites is 9 and the number of oxide ion occupying the 2a site is 1.5. The ceramics with cation- and oxide ion-defects were La_9−0.66xSr_x(GeO₄)₆O_1.5 (x=0–1), La_9−1.33xZr_x(GeO₄)₆O_1.5 (x=0–1), La_9−xSr_x(GeO₄)₆O_1.5−0.5x (x=0–3), La_9−xZr_x(GeO₄)₆O_1.5+0.5x (x=0–1), La_x(GeO₄)_3x−21(AsO₄)_27−3xO_1.5 (x=0–3), La_x(GeO₄)_33−3x(AlO₄)_3x−27O_1.5 (x=0–3), La₉(GeO₄)_6−x (AlO₄)_xO_1.5−0.5x (x=0–3), La₉(GeO₄)_6−x(AsO₄)_xO_1.5+0.5x (x=0–1), La_9.33−xSr_x(GeO₄)₆O_2−0.5x (x=0–1.2) and La_x(GeO₄)_4.5(AlO₄)_1.5O_1.5x−12.75 (x=8.8–9.83), which were prepared by the partial substitution of La³⁺and GeO₄⁴⁻of the basic apatite La₉(GeO₄)₆O_1.5 with Sr²⁺ or Zr⁴⁺ and AlO₄⁵⁻ or AsO₄³⁻. Such substitutions lowered the conductivity of La₉(GeO₄)₆O_1.5. These results were discussed by the electrostatic interaction between Sr²⁺, Zr⁴⁺, AlO₄⁵⁻ or AsO₄³⁻ and oxide ion as a conductive species.     

Lithium insertion to ReO3-type metastable phase in the Nb2O5–WO3 system

Lithium insertion to distorted ReO₃-type metastable solid solution Nb_xW_1−xO_3−x/2 (0≤x<0.25) has been studied by chemical and electrochemical methods. In the course of lithium insertion into tetragonal compounds, transition to a cubic phase was found to occur in the region where values of y (in Li_yNb_xW_1−xO_3−x/2) fall between 0.2 and 0.3, and the phase transition was found to depend on the conditions of the reaction. Changes in OCV and lattice parameters in tetragonal region (y<0.2) were discussed from the viewpoint of the ordering of lithium ions. Also, the component diffusion coefficient of lithium in tetragonal compounds Li_0.1Nb_xW_1−xO_3−x/2 (0≤x≤0.23) was found to increase with niobium content when x≤0.10, and to saturate at 4×10⁻⁹ cm²/s.     

Perpendicular magnetic anisotropy of Fe-Nd alloy thin films

A study of the magnetic properties of Fe_{100 − x}Nd_x (18 x 50) films made by rf sputtering has been carried out. The perpendicularly magentized films were fabricated for compositions in the range from x = 35 to 50 at substrate temperatures between 210 to 290°C. The intrinsic perpendicular magnetic anisotropy constant K_u is maximum at about x = 40 where K_u is about 1 × 10⁷ erg/cm³ at room temperature. The temperature dependence of K_u implies that the origin of the perpendicular magnetic anisotropy may be related to some sort of atomic ordering of crystalline clusters in an amorphous matrix.     

Phase formation and magnetic properties of Nd2Fe14B-type Nd16Co76B8−xCx alloys and their hydrides

An attempt is made to synthesize Nd₂Co₁₄C compound by mechanical alloying Nd₁₆Co₇₆B_8−xC_x (0x8) alloys and subsequent annealing. Phase formation and magnetic properties of Nd₂Fe₁₄B-type Nd₁₆Co₇₆B_8−xC_x alloys and their hydrides are investigated. The Nd₂Co₁₄(B,C) phase with Nd₂Fe₁₄B-type structure is formed for Nd₁₆Co₇₆B_8−xC_x (0x7) alloys, while NdCo₇C_δ phase with TbCu₇-type structure is observed in Nd₁₆Co₇₆C₈ alloy. The lattice parameter c of the Nd₂Co₁₄(B,C) phase decreases with increasing the carbon content. A limit volume of the unit cell to form the Nd₂Fe₁₄B-type structure is estimated to be 0.870 nm³. The spin-reorientation temperature T_SR increases with increasing the carbon content, due to an enhancement of magnetocrystalline anisotropy caused by carbon substitution for boron. After hydrogenation, the lattice expansion is observed for Nd₁₆Co₇₆B_8−xC_x (0x7) alloys. The spin-reorientation temperature of Nd₁₆Co₇₆B_8−xC_xH_y (0x7) is much lower than that of the host alloys. Some structural and magnetic properties of hypothetic Nd₂Co₁₄C and Nd₂Co₁₄CH_y compounds are estimated by extrapolation.     

Effect of Ti and C additions on structural and magnetic properties of (Pr,Nd)–Fe–B nanocrystalline magnetic materials

Effects of titanium carbide (TiC) addition on structural and magnetic properties of isotropic (Pr,Nd)–Fe-B nanocrystalline magnetic materials have been investigated. In this work, we investigate the effect of TiC addition on a (Pr,Nd)-poor and B-rich composition, as well as on a B-poor and (Nd,Pr)-rich composition. Rapidly solidified (Pr,Nd)–Fe–B alloys were prepared by melt-spinning. The compositions studied were (Pr_1−xNd_x)₄Fe₇₈B₁₈ (x=0, 0.5, and 1) with addition of 3 at% TiC. Unlike the (Pr_xNd_1−x)_9.5Fe_84.5B₆ materials that present excellent values for coercive field and energy product, the (Pr,Nd)-poor and B-rich composition alloys with TiC addition present lower values. Rietveld analysis of X-ray data and Mössbauer spectroscopy revealed that samples are predominantly composed of Fe₃B and -Fe. For the RE-rich compositions (Pr_xNd_1−x)_9.5Fe_84.5B₆ (x=0.1, 0.25, 0.5, 0.75, and 1) with the addition of 3 at% TiC, the highest coercive field and energy product (8.4 kOe and 14.4 MGOe, respectively) were obtained for the composition Pr_9.5Fe_84.5B₆.     

Ionic conduction in dilute pseudo-binary systems CuBr–Cu2Se

Ionic conductivity, σ_i, of dilute pseudobinary alloys (CuBr)_1−x(Cu₂Se)_x (x≤0.1) in their γ-phase has been measured by an ac method. The increase of the ionic conductivity propertional to x has been observed, which is attributed to interstitial ions brought by Cu₂Se dissolved in CuBr. It is found that the temperature dependence of mobility of interstitial ions, μ, evaluated by the relation Δσ_i/x=kμ (k is a constant) is bent at the temperature corresponding to the extrinsic–intrinsic transition of the based material CuBr.     

MnO thin film cathode for rechargeable microbatteries

Thin films of MnO were deposited by electron beam evaporation using a MnO or MnO₂ source. The thin films were charaterized by X-ray and electron diffraction. The Coulomb titration curve reveals a potential plateau of 2.9 V over the composition range 0.05<x<2.0. The chemical diffusion coefficient of lithium in thin films at 15°C is 2.7×10⁻¹⁴ cm²/s for 0<x<0.01 and 2.2×10⁻¹⁵ cm²/s for 0.02<x<0.06. Good reversibility for lithium insertion and extraction is demonstrated by cyclic voltammetry.     

Mixed electronic and ionic conductivity of LaCo(M)O3 (M=Ga, Cr, Fe or Ni).: V. Oxygen permeability of Mg-doped La(Ga, Co)O3−δ perovskites

The LaGa_1−x−yCo_xMg_yO_3−δ solid solutions with rhombohedrally-distorted perovskite structure were ascertained to form in the concentration range of 0≤y≤0.10 at x=0.60 and 0≤y≤0.20 at x=0.35–0.40. Increasing cobalt content results in increasing electrical conductivity and thermal expansion of the perovskites. Thermal expansion coefficients of the LaGa_1−x−yCo_xMg_yO_3−δ ceramics were calculated from the dilatometric data to vary in the range of 12.4–19.8×10⁻⁶ K⁻¹ at 300–1100 K. Doping La(Ga,Co)O_3−δ solid solutions with magnesium leads to increasing oxygen nonstoichiometry, electronic and oxygen ionic conductivity. Oxygen permeation fluxes through LaGa_1−x−yCo_xMg_yO_3−δ membranes were found to be limited by the bulk ionic conduction and to increase with magnesium concentration, being essentially independent of cobalt content.