Effect of O2 and H2O on the tri-reforming of the simulated biogas to syngas over Ni-based SBA-15 catalysts

A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method. The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a continuous flow fixed-bed micro-reactor. The stability of the catalyst was tested at 800 ℃. The results indicated that 10 wt%Ni/SBA-15 catalyst exhibited the highest catalytic activities for the combined reforming of the simulated biogas to syngas. Under the reaction conditions of the feed gas molar ratios CH4/CO2/O2/H2O = 2/1/0.6/0.6, GHSV = 24000 ml•g{cat}-1\cdoth-1 and the reaction temperatureT = 800 ℃, the conversions of CH4 and CO2 were 92.8% and 76.3%, respectively, and the yields of CO and H2 were 99.0% and 82.0%, respectively. The catalytic activities of the catalyst did not decrease obviously after 100 h reaction time on stream.     

Effect of Cu promoter on Ni-based SBA-15 catalysts for partial oxidation of methane to syngas

A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and H2-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ◦C the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.     

Ni基催化剂上CH~4部分氧化反应的研究

本文研究了NiO/SiO~2, NiO/Al~2O~3, NiO/La~2O~3催化剂的晶相组成及其还原性质。考察了催化剂的活性、选择性、稳定性。讨论了负载型催化剂稳定性较高的原因和发生部分氧化反应时CH~4的活化过程。     

水对SBA-15负载的钴基费-托合成催化剂催化性能的影响

以SBA-15分子筛为载体,采用等体积浸渍法制备了负载量为20%的钴基催化剂,采用TEM、XRD、H2-TPR和N2物理吸附-脱附等方法对催化剂进行了表征,并在浆态床反应器中考察了水的加入对费-托合成反应性能的影响.结果表明,金属钴物种进入到SBA-15载体的孔道中;产物在孔道中的滞留以及水促进的金属钴物种的团聚,引起了催化剂活性的降低;水的加入有利于反应物和产物在孔道中的传输,增加CO的转化率;在SBA-15负载的钴基催化剂中,产物在孔道中的滞留对催化剂活性影响较大,引起的扩散限制是催化剂活性降低的重要原因.     

镍基催化剂上稻草水蒸气重整制富氢合成气

采用浸渍法制备了SiO₂, γ-Al₂O₃, CaO和TiO₂负载的Ni催化剂, 以及不同MgO含量的MgO-7.5%Ni/γ-Al₂O₃催化剂,利用X射线衍射和N₂吸附-脱附技术表征了催化剂的结构,在固定床反应器上评价了它们在稻草水蒸气催化重整制合成气反应中的催化性能,考察了反应条件对催化剂性能的影响.结果表明, 以γ-Al₂O₃为载体时Ni催化剂活性最高,其中7.5%Ni/γ-Al₂O₃催化剂的H₂收率可达1071.3ml/g,H₂:CO的体积比为1.4:1;同时,MgO的添加进一步提高了该催化剂的性能,当MgO含量为1.0%时,H₂收率可达1194.6ml/g,H₂:CO体积比可达3.9:1.可见MgO的加入促进了Ni基催化剂上稻草水蒸气催化重整制合成气反应的进行,同时使得合成气中CO发生水-汽转换反应,从而大大提高了合成气中H₂含量.     

Methanation of syngas over coral reef-like Ni/Al_2O_3 catalysts

Coral reef-like Ni/Al2O3 catalysts were prepared by co-precipitation of nickel acetate and aluminium nitrate with sodium carbonate aqueous solution in the medium of ethylene glycolye.Methanation of syngas was carried out over coral reef-like Ni/Al2O3 catalysts in a continuous flow type fixed-bed reactor.The structure and properties of the fresh and used catalysts were studied by SEM,N2 adsorption-desorption,XRD,H2-TPR,O2-TPO,TG and ICP-AES techniques.The results showed that the coral reef-like Ni/Al2O3 catalysts exhibited better activity than the conventional Ni/Al2O3-H2O catalysts.The activities of coral reef-like catalysts were in the order of Ni/Al2O3-673>Ni/Al2O3-573>Ni/Al2O3- 473>Ni/Al2O3-773.Ni/Al2O3-673-EG catalyst showed not only good activity and improved stability but also superior resistance to carbon deposition,sintering,and Ni loss.Under the reaction conditions of CO/H2(molar ratio)=1:3,593 K,atmospheric pressure and a GHSV of 2500 h-1,CH4 selectivity was 84.7%,and the CO conversion reached 98.2%.     

Effect of MgO promoter on Ni-based SBA-15 catalysts for combined steam and carbon dioxide reforming of methane

A series of Ni/SBA-15 catalysts with Ni contents ranging from 5 wt% to 15 wt%, as well as another series of 10%Ni/MgO/SBA-15 catalysts, in which the range of the MgO content was from 1 wt% to 7 wt%, were prepared, and their catalytic performances for the reaction of combined steam and carbon dioxide reforming of methane were investigated in a continuous flow microreactor. The structures of the catalysts were characterized using the XRD, H2-TPR and CO2-TPD techniques. The results indicated that the CO selectivity for this reaction was very close to 100%, and the H2/CO ratio of the product gas could be controlled by changing the H2O/CO2 molar ratio of the feed gas. The simultaneous and plentiful existing of steam and CO2 had a significant influence on the catalytic performance of the 10%Ni/SBA-15 catalyst without modification. After reacting at 850 °C for 120 h over this catalyst, the CH4 conversion dropped from 98% to 85%, and the CO2 conversion decreased from 86% to 53%. However, the 10%Ni/3%MgO/SBA-15 catalyst exhibited a much better catalytic performance, and after reacting for 620 h, the CO2 conversion over this catalyst dropped from 92% to around 77%, while the CH4 conversion was not decreased. Oxidation of the Ni0 species as well as carbon deposition during the reaction were the main reasons for the deactivation of the catalyst without modification. On the other hand, modification by the MgO promoter improved the dispersion of the Ni0 species, and enhanced the CO2 adsorption affinity which in turn depressed the occurring of carbon deposition, and thus retarded the deactivation process.     

Catalytic steam reforming of biomass over Ni-based catalysts: Conversion from poplar leaves to hydrogen-rich syngas

A series of Ni/SBA-15 catalysts with Ni contents from 5 wt%–20 wt%and CaO-12.5%Ni/SBA-15 catalysts with CaO contents from 1.4 wt%–9.8 wt%have been prepared.The structure of the catalysts was characterized using X-ray diffraction(XRD),N2 adsorption-desorption,transmission electron microscopy(TEM)and X-ray photoelectron spectroscopy(XPS).The performance of catalytic steam reforming of the poplar leaves to the hydrogen-rich syngas was tested in a fixed-bed reactor.The results indicate that the 7.0wt%CaO-12.5wt%Ni/SBA-15 catalyst exhibits the best performance for the catalytic steam reforming of poplar leaves to hydrogen-rich syngas.The ratio of H2:CO can reach ca 5:1 in the hydrogen-rich syngas.The yield of H2 can reach 273.30 mL/g(poplar leaves).In the CaO-Ni/SBA-15 catalyst,Ni active component mainly fills the role of catalytic steam reforming of the poplar leaves,and CaO active component mainly plays the role as water-gas shift and CO2 sorbent.     

气相中H2O2与N2O反应机理的探讨

采用RHF/AM1方法研究了H2O2与N2O的反应机理.计算结果表明,该反应是多步反应,先后通过2个过渡态（TS1,TS3）,1个内旋转位垒（TS2）,2个中间体（IM1,IM2）.其中从反应物Re到TS1为整个反应的决速步骤,速控步骤的活化能为323.04 kJ•mol－1.整个反应为一放热反应,放出的热量为147.67kJ•mol－1.     

还原气氛对CoFe/SBA-15催化剂F-T反应性能的影响

考察了不同还原气氛处理CoFe/SBA-15催化剂对F-T反应性能的影响。结果表明,H2气氛下有利于六方钴的生成;催化剂的活性取决于钴含量,随着钴含量的增加,F-T反应中CO转化率增加,C5+选择性增加。随着铁含量的增加,催化剂表现了较高的CO2选择性。CO还原有利于立方钴的生成,导致催化活性相比H2还原的催化剂活性要低。同时CO还原容易产生积炭使催化剂的钴活性位被覆盖,导致甲烷选择性随着钴含量增加而升高。但碳化铁的生成有利于提高20Fe/SBA-15催化剂的活性,有利于低碳烃生成及C2~4烃烯烷比增加。     

Ni-WO3/SBA-15催化剂上纤维素的水解加氢

采用等体积浸渍法制备了Ni-WO₃/SBA-15催化剂,将其应用于纤维素的水相氢解.考察了温度对纤维素水解和其形貌的影响及Ni、WO₃含量等对纤维素转化行为的影响.XRD表征结果表明,随着温度的升高纤维素颗粒粒径逐渐变小并趋于均一,结晶状态逐渐由晶型变为无定型态.H₂-TPR结果表明,Ni和WO₃间存在较强的相互作用,这种相互作用提高了W物种对C-C键的解离性能,同时,提高了Ni物种的加氢活性,促进了纤维素向乙二醇的转化.在3%Ni-15%WO₃/SBA-15催化剂上,反应条件为230 ℃、6.0 MPa、6.0 h时,纤维素完全转化,乙二醇的产率达到70.7%.     

Synthesis and Structure of Propionate－bridged Mixed－metal Cluster Compound：〔MoW_2O_2（O_2CC_2H_5）_6（H_2O）_3〕ZnBr_4·4H_2O

ＳｙｎｔｈｅｓｉｓａｎｄＳｔｒｕｃｔｕｒｅｏｆＰｒｏｐｉｏｎａｔｅ－ｂｒｉｄｇｅｄＭｉｘｅｄ－ｍｅｔａｌＣｌｕｓｔｅｒＣｏｍｐｏｕｎｄ：〔ＭｏＷ_２Ｏ_２（Ｏ_２ＣＣ_２Ｈ_５）_６（Ｈ_２Ｏ）_３〕ＺｎＢｒ_４·４Ｈ_２Ｏ￥ＬｉｕＨｕａｎｇ；ＸｕＬｉ；Ｈｕａ...     

正已醇氧化成正已醛磷钨杂多酸催化剂的过氧化氢分解活性

详细讨论了磷钨杂多酸催化氧化正已醇生成正已醛反应中,在不同条件下氧化剂过氧化氢的分解活性及其动力学性质。结果表明,反应温度是影响过氧化氢分解的主要因素,温度低于70℃,分解反应进行平缓;温度一旦达到或超过80℃,则过氧化氢的分解速率迅速加快,2h的分解率达95.2%。有机溶剂及反应底物的加入,均对过氧化氢的分解反应始终保持其一级动力学性质。     

K_3H_3[As_2W_(21)O_(69)(H_2O)]·19H_2O的合成及晶体结构(英文)

利用二缺位K14[As2W19O67]·nH2O前驱体在酸性条件下的结构转变得到了饱和的砷钨酸盐K3H3[As2W21O69(H2O)]·19H2O(1),借助傅立叶变换红外光谱和X射线单晶衍射对其结构进行了表征.结果表明,化合物1的多阴离子骨架由两个相同的三缺位[α-AsW9O33]9-片段通过三个W=O基团连接而成.值得提及的是,在化合物1的阴离子骨架中心空腔中存在一个游离的水分子.     

Synthesis and Crystal Structure of [Ni(C_5H_2N_2O_4)(2,2''''bipy)(H_2O)_2]·H_2O

1 INTRODUCTION Orotic acid (H3dtpc), an important pyrimidine derivative as the effective precursor in the biosynthesis of pyrimidine base of nucleic acids in living organisms, plays a unique role in bioinorganic and pharmaceutical. Aside from the biological interest, orotic acid is also interesting in coordination chemistry. Its ketonic and enolic tautomers along with asymmetric geometry make it to be a very good versatile polydentate ligand[1~5]. The incorporation of metals into supram…     

双功能催化剂催化CO2加氢制低碳烯烃反应中In2O3的尺寸效应

CO2催化加氢转化成高附加值化学品如低碳烯烃(C2=–C4=)等是减少碳排放的有效途径之一.采用金属氧化物/分子筛双功能催化剂可以实现CO2加氢直接高选择性合成C2+碳氢化合物.通常认为,金属氧化物组分可以活化CO2转化为甲醇等含氧中间体,该中间体在分子筛孔道内进一步转化为各种烃.氧化铟(In2O3)/SAPO-34双功能催化剂由于具有出色的催化CO2加氢制低碳烯烃反应性能而备受关注,然而,仍需进一步提升催化剂的催化性能以推动该反应的工业应用.目前,氧化物的结构与双功能催化剂性能之间的关系还不明确,这不利于其催化性能的改善.现有关于金属氧化物纳米粒子的尺寸(特别是小于23 nm)效应及其对双功能催化CO2加氢反应的活性和产物分布的影响的报道较少,对此深入理解将有利于设计更高性能的催化剂.本文采用沉淀法,通过控制焙烧温度得到了一系列尺寸为7～28 nm的立方相In2O3,通过多种表征手段探究了In2O3的尺寸对其结构与表面化学性质的影响.结果表明,随着In2O3晶粒尺寸的减小,其氧空位数目、CO2、H2与NH3吸附量以及Lewis较强酸性位比例均逐渐增加.在350oC,3 Mpa,9000 mL·gcat–1·h–1和H2/CO2比为3的反应条件下,研究了In2O3/SAPO-34双功能催化剂中In2O3粒径对其催化CO2加氢制低碳烯烃反应性能的影响.结果表明,随着双功能催化剂中In2O3尺寸的增大,低碳烯烃(尤其是丙烯)选择性、收率及烯烃与烷烃比例均先升高后降低,在尺寸为19 nm的In2O3上达到最大值,分别为76.9％、12.3 mmol goxide–1 h–1和4.8.较小尺寸的In2O3虽然具有较大的比表面积和更多的氧空位,并为CO2和H2的活化提供了更多的活性位,但小于19 nm的颗粒更容易烧结;In2O3的尺寸还会影响其与SAPO-34的协同效应,进而影响双功能催化剂的催化活性.此外,相对于其它尺寸的In2O3,19 nm的In2O3更有利于甲醇中间体的生成.因而19 nm In2O3耦合SAPO-34的双功能催化剂性能最好,其催化CO2转化率最高,为14.1％.综上,适中尺寸的In2O3能够促进In2O3/SAPO-34上CO2加氢制低碳烯烃反应.这些结果为通过平衡结构稳定性和催化性能来设计更有效的催化CO2转化的复合催化剂提供了理论指导.     

Preparation,characterization and hydrodesulfurization performances of Co-Ni_2P/SBA-15 catalysts

A series of Co-Ni2P/SBA-15 catalysts with various Co contents, Ni2P contents and P/Ni molar ratios were prepared by impregnating nickel nitrate, diammonium hydrogen phosphate, and then cobalt nitrate into SBA-15 support followed by temperature-programmed reduction in a H2 flow. The catalyst structure was characterized by X-ray diffraction(XRD), high resolution-transmission electron microscopy(HR-TEM)and N2adsorption-desorption techniques and their catalytic performance of the hydrodesulfurization(HDS) of dibenzothiophene(DBT) was evaluated. The effects of Co contents, Ni2 P contents and P/Ni molar ratios on the catalyst structure and HDS of DBT over the Co-Ni2P/SBA-15 catalyst were investigated. The results indicated that the mesoporous structure was mainly maintained and the nickel phosphides were well dispersed in all of the characterized catalysts. The 4Co-25Ni2P/SBA-15(P/Ni = 0.8) catalyst with the Co and Ni2 P contents of 4 wt% and25 wt%, respectively, and the P/Ni molar ratio of 0.8 showed the highest catalytic performance for HDS of DBT. Under the reaction conditions of 380?C and 3.0 MPa, the DBT conversion can reach 99.62%. The HDS of DBT proceeded mainly via the direct desulfurization(DDS)pathway with biphenyl(BP) as the dominant product on all of the catalysts and the BP selectivity was slightly enhanced after the introduction of Co promoters.     

Hydrothermal Synthesis and Crystal Structure of [H_4As_8V_(14)O_(42)(H_2O)]·6H_2O

1 INTRODUCTION The chemistry of polyoxometalates continues to attract interest as a result of their realized and potential applications in diverse fields, such as cata- lysis, analysis, biochemistry, medicine and material science[1～3]. In the past few …     

Toluene abatement on Ag-CeO2/SBA-15 catalysts: synergistic effect of silver and ceria

As a typical volatile organic compound, toluene is a hazardous material for human health and the environment, and currently, the development of catalysts for its oxidation into CO₂ and water is crucial. The series of Ag-CeO₂/SBA-15 catalysts is synthesized by wetness impregnation techniques and characterized by a number of physical-chemical methods (nitrogen [N₂] physisorption, small angle X-ray scattering [SAXS], transmission electron microscopy [TEM], and temperature-programmed reduction [TPR]). The toluene sorption and catalytic properties in toluene oxidation are studied. Small silver [Ag] and cerium oxide [ceria, CeO_2] particles with sizes below 3 nm are predominantly formed in the ordered structure of Santa Barbara Amorphous-15 [SBA-15]. The interactions between the Ag and CeO₂ nanoparticles are established. Temperature-programmed desorption of toluene [TPD-C₇H₈] analysis shows that physical adsorption of toluene occurs on pristine SBA-15 material, while the introduction of either silver or ceria to SBA-15 leads to the appearance of additional strongly bound chemisorbed toluene on such sites. When both Ag and CeO₂ are introduced, only chemisorbed toluene is formed over the Ag-CeO₂/SBA-15 catalyst, and the highest catalytic activity in toluene oxidation is observed over this catalyst (T_98% = 233 °C, 0.2% C₆H₅CH₃) that is attributed to the synergistic effect of ceria [CeO_2] and silver [Ag].     

CO2氧化丙烷脱氢制丙烯V-Cr/SBA-15催化剂的研究

以介孔分子筛SBA-15为载体,V和Cr为活性组分,采用浸渍法制备了不同V和Cr质量分数的V-Cr/SBA-15催化剂,研究了其对二氧化碳氧化丙烷制丙烯反应的催化性能,采用XRD、BET、TPR等分析测试技术对催化剂的结构进行了表征。结果表明,催化剂中V组分的质量分数较大时以V2O5物相存在,Cr组分以Cr2O3物相存在,它们对SBA-15分子筛的介孔特征影响不大;V、Cr单组分和双组分催化剂都具有较好的CO2氧化丙烷脱氢制丙烯的催化性能,V和Cr质量分数相同的双组分催化剂比单组分催化剂具有更高的催化活性;在V-Cr/SBA-15催化剂中,V和Cr之间存在一定的相互作用,进而改变了催化剂的氧化还原性能,提高了催化剂的催化性能。