Effect of thermal annealing on the structure and magnetism of Fe-doped ZnO nanocrystals synthesized by solid state reaction

High purity Fe₂O₃/ZnO nanocomposites were annealed in air at different temperatures between 100 and 1200 °C to get Fe-doped ZnO nanocrystals. The structure and grain size of the Fe₂O₃/ZnO nanocomposites were investigated by X-ray diffraction 2θ scans. Annealing induces an increase of the grain size from 25 to 195 nm and appearance of franklinite phase of ZnFe₂O₄. Positron annihilation measurements reveal large number of vacancy defects in the interface region of the Fe₂O₃/ZnO nanocomposites, and they are gradually recovered with increasing annealing temperature. After annealing at temperatures higher than 1000 °C, the number of vacancies decreases to the lower detection limit of positrons. Room temperature ferromagnetism can be observed in Fe-doped ZnO nanocrystals using physical properties measurement system. The ferromagnetism remains after annealing up to 1000 °C, suggesting that it is not related with the interfacial defects.     

Room-temperature ferromagnetism in Zn1−xMnxO

In view of recent controversies on above room-temperature ferromagnetism (RTFM) in transition-metal-doped ZnO, the present paper aims to shed some light on the origin of ferromagnetism by investigating annealing effects on structure and magnetism for polycrystalline Zn_1−xMn_xO powder samples prepared by solid-state reaction method and annealed in air at different temperatures. Magnetic measurements indicate that the samples are ferromagnetic at room temperature (RTFM). Room temperature ferromagnetism has been observed in the sample annealed at a low temperature of 500 °C with a saturated magnetization (M_s) of 0.159 emu/g and a coercive force of 89 Oe. A reduction in RTFM is clearly observed in the sample annealed at 600 °C. Furthermore, the saturation magnetic moment decreases with an increase in grain size, suggesting that ferromagnetism is due to defects and/or oxygen vacancy confined to the surface of the grains. The experimental results indicate that the ferromagnetism observed in Zn_1−xMn_xO samples is intrinsic rather than associated with secondary phases.     

Effects of annealing temperature on YAG:Ce synthesized by spray-drying method

In this report, YAG:Ce phosphors were synthesized by spray-drying method. The effects of annealing temperature on crystal structure, morphology and photoluminescence property (PL) of as-prepared samples were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and spectrofluorometer, respectively. The XRD patterns showed all the samples are in consistence with a single garnet phase, and the location of strongest peak shifts to smaller angle with increasing the annealing temperature. The SEM micrographs revealed the sample annealed at 1200 °C appears to be a spherical polycrystalline aggregate; as the samples were annealed at 1300?1400 °C, spherical grains obviously grow up; but the sample annealed at over 1400 °C forms an irregular bulk. The emission spectra of samples indicated the PL of samples annealed at 1200?1400 °C improve with increasing the annealing temperature because of the diffusion of Si⁴⁺ ions; whereas the PL of sample annealed at the temperature over 1400 °C decreases likely resulting from inflection effects of multiangular shape of grains. Therefore, the samples annealed at 1400 °C are suitable for gaining phosphor with high brightness and good morphology.     

Room temperature photoluminescence mechanism of SiOx film after annealing at different temperatures

SiO_x films were deposited on Si(1 0 0) substrates by evaporation of SiO powder. The samples were annealed from room-temperature (RT) to 1100 °C. After the samples were cooled down to RT, photoluminescence (PL) spectra from these samples were measured. It was found that when the annealing temperature Ta is not higher than 1000 °C, there is a PL centered at 620 nm, and with Ta increasing the intensity increases at first and then decreases when Ta is higher than 500 °C. When Ta is no less than 1000 °C another PL peak located at 720 nm appears. Combined with Raman and XRD spectra, we confirm that the latter PL is from Si nanocrystals that start to form when Ta is higher than 1000 °C. PL spectra for Ta<900 °C were discussed in detail and was attributed to defects in the matrix rather than from Si clusters.     

Thermal evolution of vacancy defects induced in sintered UO2 disks by helium implantation

A slow positron beam coupled with Doppler broadening (DB) spectrometer was used to measure the low- and high-momentum annihilation fractions, S and W, respectively, as a function of positron energy in UO₂ disks implanted with different 1 MeV ³He fluences and annealed in ArH₂ or in vacuum. The S(E) and W(E) behaviors indicate that for fluences in the range from 2 × 10¹⁴ to 2 × 10¹⁶³He cm⁻², the vacancy defects distribution evolves with the annealing temperature in the range from 264 to 700 °C under ArH₂. This evolution is found to be dependent on the ³He fluence implanted in the sintered UO₂ disks. For the lowest fluence of 2 × 10¹⁴³He cm⁻², the S(W) plot with positron energy as the running parameter suggests that only the concentration of vacancy defects decreases when annealing temperature increases. For the highest implantation fluences (from 5 × 10¹⁵ to 2 × 10¹⁶³He cm⁻²) the S(W) plot suggests that the nature of the vacancy defects changes in the annealing temperature range from 260 to 400 °C. Measurements performed in implanted UO₂ disks annealed in vacuum have revealed a partial recovery of the vacancy defects possibly due to their recombination with mobile oxygen interstitials. The role of the hydrogen infusion into the disk is also discussed.     

Evidence of formation of tetravacancies in uniformly oxygen irradiated n-type silicon

High purity n-type silicon single crystal with resistivity in the order of 4000 Ω cm has been irradiated with high-energy oxygen ions at room temperature up to a fluence of 5E15 ions/cm². The energy of the beam was varied from 3 to 140 MeV using a rotating degrader to achieve a depthwise near-uniform implantation profile. Radiation induced defects and their dynamics have been studied using positron annihilation spectroscopy along with isochronal annealing up to 700 °C in steps of 50 °C for 30 min. After annealing the sample at 200 °C for 30 min, formation of silicon tetravacancies has been noticed. The formation of the tetravacancies was found to be due to agglomeration of divacancies present in the irradiated sample. An experimentally obtained positron lifetime value of 338±10 ps has been reported for silicon tetravacancies, which has a very close agreement with the value obtained from recent theoretical calculations. The tetravacancies were found to dissociate into trivacancy clusters upon further annealing. The trivacancies thus obtained were observed to agglomerate beyond 400 °C to form larger defect clusters. Finally, all the defects were found to anneal out after annealing the sample at 650 °C.     

Investigation of microstructure thermal evolution in nanocrystalline Cu

The microstructure of nanocrystalline Cu prepared by compacting nanoparticles (50-60 nm in diameter) under high pressures has been studied by means of positron lifetime spectroscopy and X-ray diffraction. These nanoparticles were produced by two different methods. We found that there are order regions interior to the grains and disorder regions at the grain boundaries with a wide distribution of interatomic distances. The mean grain sizes of the nanocrystalline Cu samples decrease after being annealed at 900 °C and increase during aging at 180 °C, which are observed by X-ray diffraction, revealing that the atoms exchange between the two regions. The positron lifetime results clearly indicate that the vacancy clusters formed in the annealing process are unstable and decomposed at the aging time below 6 hours. In addition, the partially oxidized surfaces of the nanoparticles hinder grain growth when the samples age at 180 °C, and the vacancy clusters inside the disorder regions, which are related to Cu₂O, need longer aging time to decompose. The disorder regions remain after the heat treatment in this work, in spite of the grain growth, which will be good for the samples keeping the properties of nanocrystalline material.     

He离子注入ZnO中缺陷形成的慢正电子束研究

在ZnO单晶样品中注入了能量为20—100keV、总剂量为4.4×10¹⁵cm^-2的He离子.利用基于慢正电子束的多普勒展宽测量研究了离子注入产生的缺陷.结果表明，He离子注入ZnO产生了双空位或更大的空位团.在400℃以下退火后，He开始填充到这些空位团里面，造成空位团的有效体积减少.经过400℃以上升温退火后，这些空位团的尺寸开始增大，但由于有少量的He仍然占据在空位团内，因此直到800℃这些空位团仍保持稳定.高于800℃退火后，由于He的脱附，留下的空位团 关键词： 慢正电子束 ZnO 离子注入 缺陷     

Annealing temperature dependence of Raman scattering in Si/SiO2 superlattice prepared by magnetron sputtering

Si/SiO₂ superlattices were prepared by magnetron sputtering, and the deposition temperature and annealing temperature had a great influence on the superlattice structure. In terms of SEM images, the mean size of Si nanocrystals annealed at 1100 °C is larger than that of nanocrystals annealed at 850 °C. It was found that the films deposited at room temperature are amorphous. With increasing deposition temperature, the amorphous and crystalline phases coexist. With increasing annealing temperature, the Raman intensity of the peak near 470 cm⁻¹ decreases, and the intensity of that at 520 cm⁻¹ increases. Also, on increasing the annealing temperature, the Raman peak near 520 cm⁻¹ shifts and narrows, and asymmetry emerges. A spherical cluster is used to model the nanocrystals in Si/SiO₂ superlattices, and the observed Raman spectra are analyzed by combining the effects of confinement on the phonon frequencies. Raman spectra from a variety of nanocrystalline silicon structures were successfully explained in terms of the phonon confinement effect. The fitted results agreed well with the experimental observations from SEM images.     

Underlayer diffusion-induced enhancement of coercivity in high anisotropy FePt thin films

The L1₀ ordered FePt films have been prepared at 300 °C with a basic structure of CrRu/MgO/FePt, followed by a post-annealing process at temperatures from 200 to 350 °C. The magnetic properties and the microstructure of the films were investigated. It is found that coercivity of FePt films increases greatly from 3.57 to 9.1 kOe with the increasing annealing temperature from 200 to 350 °C. The loop slope of the M–H curves decreases with the increasing annealing temperature, which is due to the grain isolation induced by MgO underlayer diffusion during the annealing process. The underlayer diffusion could be a useful approach to prepare the FePt-based composite films for high-density recording media.     

Influence of high temperature annealing on the structure, hardness and tribological properties of diamond-like carbon and TiAlSiCN nanocomposite coatings

Diamond-like carbon (DLC) and TiAlSiCN nanocomposite coatings were synthesized and annealed at different temperatures in a vacuum environment. The microstructure, hardness and tribological properties of as-deposited and annealed DLC-TiAlSiCN nanocomposite coatings were characterized by X-ray diffraction, X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), Raman spectroscopy, nano-indentation and friction tests. The TEM results reveal that the as-deposited DLC-TiAlSiCN coating has a unique nanocomposite structure consisting of TiCN nanocrystals embedded in an amorphous matrix consisting of a-Si₃N₄, a-SiC, a-CN and DLC, and the structure changed little after annealing at 800 °C. However, XPS and Raman results show that an obvious graphitization of the DLC phase occurred during the annealing process and it worsened with annealing temperature. Because of the graphitization, the hardness of the DLC-TiAlSiCN coating after annealing at 800 °C decreased from 45 to 36 GPa. In addition, the DLC-TiAlSiCN coating after annealing at 800 °C has a similar friction coefficient to the as-deposited coating.     

Comparative study on the effect of annealing treatments on RTL mechanism in natural quartz from different origins

The behaviour of trap centres and luminescence centres has been investigated for fired and unfired natural quartz from bricks and sediments irradiated at 100 Gy and annealed at different temperatures in the range 350-700 °C. The annealing treatment affects thermoluminescence (TL) glow curve as various changes were observed. The higher sensitization occurred for an annealing in the region 550-600 °C. At this annealing temperature, it has been observed the emergence of two peaks arising at 96 and 180 °C. At lower annealing temperatures, these peaks are overlapped by the peaks localized at 90 and 195 °C, respectively. Concerning the fired quartz, the higher sensitization occurred for an annealing in the region 500-550 °C for peak temperature around 200 °C and an unusual desensitization for the peak temperature around 100 °C. The behaviour of the two types of quartz is analyzed regarding to their kinetic parameters and luminescence emission and compared to literature data.     

Structural characterization of supported nanocrystalline ZnO thin films prepared by dip-coating

Nanocrystalline ZnO thin films prepared by the sol-gel dip-coating technique were characterized by grazing incidence X-ray diffraction (GIXD), atomic force microscopy (AFM), X-ray reflectivity (XR) and grazing incidence small-angle X-ray scattering (GISAXS). The structures of several thin films subjected to (i) isochronous annealing at 350, 450 and 550 °C, and (ii) isothermal annealing at 450 °C during different time periods, were characterized. The studied thin films are composed of ZnO nanocrystals as revealed by analysing several GIXD patterns, from which their average sizes were determined. Thin film thickness and roughness were determined from quantitative analyses of AFM images and XR patterns. The analysis of XR patterns also yielded the average density of the studied films. Our GISAXS study indicates that the studied ZnO thin films contain nanopores with an ellipsoidal shape, and flattened along the direction normal to the substrate surface. The thin film annealed at the highest temperature, T = 550 °C, exhibits higher density and lower thickness and nanoporosity volume fraction, than those annealed at 350 and 450 °C. These results indicate that thermal annealing at the highest temperature (550 °C) induces a noticeable compaction effect on the structure of the studied thin films.     

Effects of annealing temperature and method on structural and optical properties of TiO2 films prepared by RF magnetron sputtering at room temperature

TiO₂ thin film was deposited on non-heated Si(1 0 0) substrate by RF magnetron sputtering. The as-deposited films were annealed by a conventional thermal annealing (CTA) and rapid thermal annealing (RTA) at 700 and 800 °C, and the effects of annealing temperature and method on optical properties of studied films were investigated by measuring the optical band gaps and FT-IR spectra. And we also compared the XRD patterns of the studied samples. The as-deposited film showed a mixed structure of anatase and brookite. Only rutile structures were found in samples annealed above 800 °C by CTA, while there are no special peaks except the weak brookite B(2 3 2) peak for the sample annealed at (or above) 800 °C by RTA. FT-IR spectra show the broad peaks due to Ti-O vibration mode in the range of 590-620 cm⁻¹ for the as-deposited film as well as samples annealed by both annealing methods at 700 °C. The studied samples all had the peaks from Si-O vibration mode, which seemed to be due to the reaction between TiO₂ and Si substrate, and the intensities of these peaks increased with increasing of annealing temperature. The optical band gap of the as-deposited film was 3.29 eV but it varied from 3.39 to 3.43 eV as the annealing temperature increased from 700 to 800 °C in the samples annealed by CTA. However, it varied from 3.38 to 3.32 eV as the annealing temperature increased from 700 to 800 °C by RTA.     

Self-implantation of Cz-Si: Clustering and annealing of defects

Observations of vacancy clusters formed in Czochralski (Cz) Si after high energy ion implantation are reported. Vacancy clusters were created by 2 MeV Si ion implantation of 1 × 10¹⁵ ions/cm² and after annealing between 600 and 650 °C. Doppler broadening measurements using a slow positron beam have been performed on the self-implanted Si samples, both as-implanted and after annealing between 200 and 700 °C for time intervals ranging from 15 to 120 min. No change in the S parameter was noted after the thermal treatment up to 500 °C. However, the divacancies (V₂) created as a consequence of the implantation were found to start agglomerating at 600 °C, forming vacancy clusters in two distinct layers below the surface; the first layer is up to 0.5 μm and the second layer is up to 2 μm. The S-W plots of the data suggest that clusters of the size of hexavacancies (V₆) could be formed in both layers after annealing for up to an hour at 600 °C or half an hour at 650 °C. After annealing for longer times, it is expected that vacancies are a mixture of V₆ and V₂, with V₆ most probably dominating in the first layer. Further annealing for longer times or higher temperatures breaks up the vacancy clusters or anneals them away.     

Studying the recovery of as-received industrial Al alloys by positron annihilation spectroscopy

Positron annihilation lifetime (PAL) spectroscopy, Doppler broadening of annihilation radiation (DBAR) spectroscopy and Vickers microhardness (Hv) measurements were performed to study the micro- and macro-structure variations during isochronal annealing from room temperature (RT) to 500 °C of commercial pure Al (1 1 0 0), Al-Mn-Mg (3 0 0 4) and Al-Mg-Si (6 2 0 1) alloys. Three annealing stages of microstructures have been identified as recovery, partial recrystallization and complete recrystallization followed by grain growth. A positive correlation between the macroscopic mechanical properties (Hv) and positron annihilation parameters has been achieved for the three samples under investigation.     

Real time investigation of the growth of silicon carbide nanocrystals on Si(1 0 0) using synchrotron X-ray diffraction

The growth of silicon carbide nanocrystals on Si(1 0 0) is studied by synchrotron surface X-ray diffraction (SXRD) during annealing at high temperature. A chemisorbed methanol monolayer is used as carbon source, allowing to have a fixed amount of carbon atoms to feed the growth. At room temperature, minor changes in the 2 × 1 reconstruction of silicon are observed due to the formation of Si-O-CH₃ and Si-H bonds from methanol molecules. When annealed at 500 °C, carbon incorporation into the silicon leads only to local modifications of the surface structure. Above 600 °C, tri-dimensional silicon carbide nanocrystals growth takes place, together with surface roughening and sharp decrease of domain sizes of the 2 × 1 reconstruction. The different processes taking place at each temperature are clearly distinguished and identified during the real time SXRD measurements.     

Annealing temperature influence on electrical properties of ion beam sputtered Bi2Te3 thin films

Ion beam sputtering process was used to deposit n-type fine-grained Bi₂Te₃ thin films on BK7 glass substrates at room temperature. In order to enhance the thermoelectric properties, thin films are annealed at the temperatures ranging from 100 to 400 °C. X-ray diffraction (XRD) shows that the films have preferred orientations in the c-axis direction. It is confirmed that grain growth and crystallization along the c-axis are enhanced as the annealing temperature increased. However, broad impurity peaks related to some oxygen traces increase when the annealing temperature reached 400 °C. Thermoelectric properties of Bi₂Te₃ thin films were investigated at room temperature. The Bi₂Te₃ thin films, including as-deposited, exhibit the Seebeck coefficients of −90 to −168 μV K⁻¹ and the electrical conductivities of 3.92×10²-7.20×10² S cm⁻¹ after annealing. The Bi₂Te₃ film with a maximum power factor of 1.10×10⁻³ Wm⁻¹ K⁻² is achieved when annealed at 300 °C. As a result, both structural and transport properties have been found to be strongly affected by annealing treatment. It was considered that the annealing conditions reduce the number of potential scattering sites at grain boundaries and defects, thus improving the thermoelectric properties.     

Influence of annealing temperature on structural and optical properties of ZnO: In thin films prepared by ultrasonic spray technique

Transparent conducting indium doped zinc oxide was deposited on glass substrate by ultrasonic spray method. The In doped ZnO samples with indium concentration of 3 wt.% were deposited at 300, 350 and 400 °C with 2 min of deposition time. The effects of substrate temperature and annealing temperature on the structural, electrical and optical properties were examined. The DRX analyses indicated that In doped ZnO films have polycrystalline nature and hexagonal wurtzite structure with (0 0 2) preferential orientation and the maximum average crystallite size of ZnO: In before and annealed at 500 °C were 45.78 and 55.47 nm at a substrate temperature of 350 °C. The crystallinity of the thin films increased by increasing the substrate temperature up 350 °C, the crystallinity improved after annealing temperature at 500 °C. The film annealed at 500 °C and deposited at 350 °C show lower absorption within the visible wavelength region. The band gap energy increased from E_g = 3.25 to 3.36 eV for without annealing and annealed films at 500 °C, respectively, indicating that the increase in the transition tail width. This is due to the increase in the electrical conductivity of the films after annealing temperature.     

Structural and optical properties of Au-implanted ZnO films

The structural and luminescence related optical behaviours of Au ion implanted ZnO films grown by magnetic sputtering and their post implantation annealing behaviours in the temperature range of 100-700 °C have been investigated. Optical absorption and transmittance spectra of the films indicate that band edge of Au-implanted ZnO has shifted to high energy range and optical band gap has increased, because the sharp difference of thermal expansion induces the lattice mismatch between ZnO and SiO₂. PL spectra reveal that UV and visible luminescence bands of ZnO films can be improved after thermal annealing due to recovery of defects and Au ions incorporation. Importantly, green luminescence band of 530 nm has been only observed in the Au-implanted and subsequently annealed ZnO films and it enhances with the increasing annealing temperature, which can be related to Au atoms or clusters in ZnO films. Furthermore, X-ray photoelectron spectroscopy measurements reveal that the Au⁰ is dominant state in Au implanted and annealed ZnO films. Possible mechanisms, such as optical transitions of Au atoms or clusters and deep level luminescence of ZnO, have been proposed for green emission.